Er3+及Er3+/Yb3+共掺铋酸盐玻璃光谱性质研究

制备了Er³⁺及Er³⁺/Yb³⁺共掺铋酸盐玻璃，测试了样品的吸收光谱、荧光光谱.应用Judd-Oflet理论计算了Er³⁺在铋酸盐玻璃中的光谱强度参数，分别为Ω₂=(5.47—2.92)×10^-20cm²，Ω₄=(2.16—1.22)×10^-20cm², 关键词： 3+')" href="#">Er³⁺ 铋酸盐玻璃 3+/Yb³⁺共掺')" href="#">Er³⁺/Yb³⁺共掺 光谱性质     

Yb3+/Er3+共掺杂TeO2-WO3-ZnO玻璃的光谱性质

制备了Yb³⁺/Er³⁺共掺杂的TeO₂-WO₃-ZnO玻璃,测量了Er³⁺在玻璃中的吸收光谱和970nmLD激发下的荧光光谱、荧光寿命和上转换光谱.计算了Yb³⁺/Er³⁺间的能量传递效率和Er³⁺离子1.5μm波段的吸收截面、发射截面,并研究了其荧光强度和上转换发光与Yb³⁺掺杂浓度间的关系.结果表明,Yb³⁺共掺杂可明显提高Er³⁺离子1.5μm发射的荧光强度,实验所得Yb³⁺离子的最佳掺杂浓度为Er³⁺离子浓度的3倍,在7.28×1020ions/cm³左右.Er³⁺离子1.5μm发射的荧光半峰全宽为67～72nm;上转换红、绿光均为双光子过程,随Yb³⁺掺杂浓度的增加,上转换红、绿光强度均增强.     

Er3+/Yb3+共掺NaYF4/LiYF4微米晶体的上转换荧光特性

采用水热法成功制备了Er³⁺/Yb³⁺共掺杂的NaYF₄和LiYF₄微米晶体. 通过X射线衍射仪和环境扫描电子显微镜对样品的晶体结构及形貌进行表征. 实验结果表明: 六方相NaYF₄微米晶体为棒状结构, 而四方相LiYF₄微米晶体则为八面体结构. 在近红外光980 nm激发下, NaYF₄:Yb³⁺/Er³⁺和LiYF₄:Yb³⁺/Er³⁺ 微米晶体均展现出很强上转换荧光发射. 且NaYF₄:Yb³⁺/Er³⁺微米晶体的荧光发射强度大约是LiYF₄:Yb³⁺/Er³⁺微米晶体的2倍, 但红绿比明显较低. 根据荧光光谱, 并借助激光光谱学及发光动力学深入探讨基质变化及表面修饰剂乙二胺四乙二酸(EDTA)对荧光特性的影响. 实验结果发现: 影响荧光强度的主要因素是基质环境的局域对称性, 而导致不同红绿比则是由于样品表面较多的EDTA分子所引起. Er³⁺掺杂的NaYF₄和LiYF₄ 微米晶体呈现出很强的绿光发射可被应用于全色显示, 荧光粉和微光电子器件中.     

高Yb3+/Er3+掺杂的磷基有源光纤材料的光谱性质

研究了Yb³⁺/Er³⁺共掺60P₂O₅-15BaO-10Al₂O₃-5ZnO-10R₂O（R=Na,K）以P₂O₅为主体的磷基有源光纤材料的光谱性质,以及不同Yb³⁺/Er³⁺掺杂浓度对光谱性质的影响规律。当Er³⁺浓度为9.100×10¹⁹/cm³、Yb³⁺的掺杂浓度为5.407×10²⁰/cm³、Yb³⁺/Er³⁺浓度比为6：1时,玻璃样品在1 531 nm处的受激发射截面最大,为6.17×10^-21 cm²。同时,其荧光寿命为9.73 ms,荧光半高宽为53.16 nm,发射截面与半高宽的乘积为3.28×10^-32 m³,综合性能最佳。     

Er3+/Yb3+共掺TeO2-WO3-Bi2O3玻璃的光谱性质和上转换发光

本文制备了Er³⁺/Yb³⁺共掺TeO₂-WO₃-Bi₂O₃(TWB)玻璃. 测试和分析了样品的吸收光谱、荧光光谱及上转换发光. 用Judd-Oflet(J-O)理论计算了Er³⁺在玻璃样品中的光谱强度参数,随着Bi₂O₃含量的增加,Ω₂增加,Ω₄ 关键词： 碲酸盐玻璃 光谱性质 上转换     

Yb3+,Er3+:YAG透明陶瓷的制备和1.5 μm波段光谱性能研究

采用固相法和真空烧结技术制备了5at%Yb³⁺,2at％Er³⁺:YAG透明陶瓷.在1760 ℃真空烧结30 h后, 陶瓷样品具有较高透过率.SEM观察表明制备的透明陶瓷在晶粒和晶界处无气孔、第二相的存在.样品的吸收光谱和荧光光谱的测试结果表明: Yb³⁺在940nm波长处有具有较强的吸收系数.样品在1030nm波长的荧光寿命仅为0.274 ms,以及在1.5μm波段的荧光衰减寿命曲线中,初始的荧光强度呈上升趋势,这些表明了Yb,Er:YA 关键词： Er Yb:YAG透明陶瓷 1.5 μm荧光光谱 Judd-Ofelt理论     

Ba5SiO4Cl6: Yb3+, Er3+, Li+荧光粉的制备及上转换发光性质研究

本文采用高温固相反应法制备了Ba₅SiO₄Cl₆: Yb³⁺, Er³⁺, Li⁺ 荧光粉, 并对其上转换发光性质及其发光机理进行了研究. 在980 nm 激光的激发下, Ba₅SiO₄Cl₆: Yb³⁺, Er³⁺ 荧光粉呈现较强的红色(662 nm) 和较弱的绿色(550 nm) 的上转换发光, 红色和绿色的上转换发光分别对应于Er³⁺ 离子的⁴S_3/2/²H_11/2→⁴I_15/2 和⁴F_9/2→⁴I_15/2 跃迁, 且随着掺杂的Er³⁺ 和Yb³⁺ 离子浓度增加, 样品的上转换发光强度增加, 这是因为Yb³⁺ 离子和Er³⁺ 离子之间的能量传递效率增加引起的. 在0.5—0.8 W 功率激发下,样品属于双光子发射, 而在0.9—1.2 W 功率激发下样品具有新的上转换发光机理——光子雪崩效应. 探讨了Li⁺ 掺杂对Ba₅SiO₄Cl₆: Yb³⁺, Er³⁺ 样品的上转换发光性质的影响, Li⁺ 离子的掺杂引起Ba₅SiO₄Cl₆:Yb³⁺, Er³⁺ 上转换发光强度增加, 这是由于Li⁺ 离子的掺入降低了晶体场的对称性引起的.     

共沉淀法制备Y2SiO5∶Er3+ ,Yb3+ ,Tm3+及其上转换发光性能研究

采用化学共沉淀法制备了系列Y_1.98-2xYb_2x Er_0.02SiO₅(0.00≤x≤0.15)以及Y_1.736Yb_0.24Er_0.02Tm_0.004SiO₅上转换发光材料,比较了室温下Y_1.98-2xYb_2x Er_0.02 SiO₅ (x=0.00,0.08)样品在400—1600 nm范围内的吸收光谱,测量了所有样品在976 nm OPO激光器激发下的上转换发射光谱,以及Er³⁺离子⁴S_3/2(⁴F_9/2)→⁴I_15/2,Tm³⁺离子¹G₄→³H₆荧光衰减曲线和不同激发功率下的上转换蓝光发射强度,从而分析讨论了Er³⁺,Tm³⁺在Y₂SiO₅中的上转换发光机理.研究结果表明:在1250 ℃相对较低的温度下合成了X2型单斜晶系Y₂SiO₅ ∶Ln³⁺(Ln³⁺=Er³⁺,Yb³⁺,Tm³⁺),Yb³⁺的敏化显著增强了样品在976 nm附近的吸收能力,并大幅度加宽了该处的吸收带.分析上转换发射光谱发现:上转换绿光和红光强度都随着Yb³⁺浓度的增加先增强后减弱,但红光的猝灭浓度较高,归因于Er³⁺→Yb³⁺反向能量传递ETU4和Yb³⁺→Er³⁺正向能量传递ETU3过程的发生;上转换蓝光发射是三光子吸收过程,是通过Yb³⁺,Tm³⁺之间三次声子辅助的能量转移方式实现的. 关键词： 上转换 共沉淀 2SiO₅∶Er³⁺')" href="#">Y₂SiO₅∶Er³⁺ 3+')" href="#">Yb³⁺ 3+')" href="#">Tm³⁺     

Er3+/Yb3+共掺杂铋酸盐玻璃的上转换发光和能量传递

用高温熔融法制备了Er³⁺/Yb³⁺共掺杂的45Bi₂O₃-45GeO₂-10PbO玻璃,对玻璃样品进行了光谱测试,分析了上转换发光机制和Yb³⁺→Er³⁺的能量传递效率。通过Yb³⁺离子浓度对Er³⁺离子在铋酸盐玻璃中的上转换荧光强度影响的研究,得到Er³⁺质量分数为0.5%以及Yb³⁺质量分数为2.5%时上转换发光强度最大。研究结果表明,在970nm泵浦激发下,Er³⁺/Yb³⁺共掺杂B₄₅G₄₅P₁₀玻璃在532,545,673nm处产生较强的上转换绿光和红光,是一种较为理想的上转换发光基质材料。     

Ce3+对Er3+/Yb3+共掺TeO2-WO3-ZnO玻璃发光性能的影响

在Er³⁺/Yb³⁺共掺TeO₂-WO₃-ZnO玻璃中引入Ce³⁺，研究了Ce³⁺对Er³⁺1.5μm发射性能及其上转换发光性能的影响。结果表明，随Ce³⁺浓度的增加Er³⁺1.5μm波段的荧光强度先增强后降低，优化的Ce³⁺掺杂浓度在2.07×10²⁰/cm³左右；1.5μm波段的荧光寿命则随Ce³⁺浓度的增加有轻微降低，从3.4ms降到3.0ms，但Ce³⁺浓度的增加对1.5μm波段的荧光半高宽基本无影响；Er³⁺/Ce³⁺间的交叉弛豫Er³⁺(⁴I_11/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_13/2)+Ce³⁺(²F_7/2)使玻璃的上转换发光强度大大降低，但在过高的Ce³⁺浓度下，Er³⁺/Ce³⁺间的另一交叉弛豫Er³⁺(⁴I_13/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_15/2)+Ce³⁺(²F_7/2)则使Er³⁺⁴I_13/2能级粒子数减少，导致1.5μm波段荧光强度和荧光寿命降低. 关键词： 碲钨酸盐玻璃 发光性能 3+离子')" href="#">Er³⁺离子 3+离子')" href="#">Ce³⁺离子 交叉弛豫     

Spectroscopic properties in Er Er3+/Yb3+Co-doped fluorophosphate glass

Using the technique of high-temperature melting, a new Er³⁺/Yb³⁺ co-doped fluorophosphate glass was prepared. The absorption and fluorescence spectra were investigated in depth. The effect of Er³⁺ and Yb³⁺ concentration on the spectroscopic properties of the glass sample was also discussed. According to the Judd-Ofelt theory, the oscillator strength was computed. The lifetime of ⁴I_13/2 level (τ_m) of Er³⁺ ions was 8.23 ms, and the full width at half maximum of the dominating emission peak was 68 nm at 1.53 τ_m. The large stimulated emission cross section of the Er³⁺ was calculated by the McCumber theory. The spectroscopic properties of Er³⁺ ion were compared with those in different glasses. The full width at half maximum and σ_e are larger than those of other glass hosts, indicating this studied glass may be a potentially useful candidate for high-gain erbium-doped fiber amplifier.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Ce3+对Er3+/Yb3+共掺氟磷酸盐玻璃光谱性质的影响

研究了能量接受离子Ce³⁺对Er³⁺上转换发光强度以及Er³⁺在1.5μm附近波段发光性能参数的影响，并从能量匹配及能级结构角度出发对Er³⁺/Ce³⁺间的能量转移机制进行了分析.分析认为，⁴I_11/2能级的Er³⁺通过无辐射能量转移把能量传递给²F_5/2能级的Ce³⁺关键词： 氟磷酸盐玻璃 光谱性质 光纤放大器 3+和Ce³⁺')" href="#">Er³⁺和Ce³⁺     

TeO2-ZnO-Na2O-K2O玻璃中Er3+离子掺杂浓度对其发光及荧光寿命的影响

测量了不同掺杂浓度下Er³⁺离子在碲酸盐玻璃中的吸收光谱、发射光谱和Er3+离子的荧光寿命，计算了Er³⁺离子的发射截面σ_e,分析 了Er ³⁺离子掺杂浓度对其发光强度和荧光寿命的影响.结果表明，Er³⁺离子掺 杂浓度较低时，对其荧光强度和荧光寿命没有显著的影响；掺杂浓度高时，出现了浓度猝灭 效应，使Er³⁺离 子荧光光强度降低，荧光寿命下降.实验确定了掺杂浓度最优值，同时对浓度猝灭机制进行 了分析. 关键词： 碲锌碱玻璃 3+离子')" href="#">Er³⁺离子 掺杂浓度 发光和荧光寿命     

Er3+，Er3+/Yb3+掺杂氟化镧超微材料的光谱特性与上转换发光

采用共沉淀法制备了Er³⁺掺杂和Er³⁺/Yb³⁺共掺杂LaF₃超微材料,所制备的样品的颗粒呈球形,尺寸为250nm左右.计算得到Er³⁺单掺杂样品中对应着⁴S_3/2和⁴F_9/2能级的发光量子效率分别为67.0%和71.9%.研究发现,随着Yb³⁺离子浓度的增加 关键词： 3+')" href="#">Er³⁺ 3+')" href="#">Yb³⁺ 发光 能量传递     

荧光捕获效应对Yb3+磷酸盐玻璃光谱性质的影响

测试了不同掺杂浓度和不同厚度下Yb³⁺磷酸盐玻璃的吸收光谱、荧光光谱和荧 光寿命，计算了积分吸收截面、吸收截面、受激发射截面、自发辐射寿命以及荧光有效线宽等光谱参数，讨论了荧光俘获效应对Yb³⁺磷酸盐玻璃光谱性质的影响.结果表明荧光俘 获效应随样品厚度和掺杂浓度的增加而增大.由于荧光俘获效应的存在使得测量的Yb^{3+磷酸盐玻璃荧光寿命明显长于计算的荧光寿命，在0.2mol%Yb₂O₃低掺 杂浓度下 关键词： 荧光俘获 掺镱磷酸盐玻璃 荧光光谱}     

Er3+单掺及Er3+/Yb3+共掺SiO2-Al2O3-La2O3玻璃光谱性质研究

研究了单掺Er³⁺及Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃的光谱性质随稀土离子浓度变化规律,应用McCumber理论计算了玻璃在1.53 μm的发射截面及积分吸收截面.结果表明:在Er³⁺离子掺杂浓度相同时,玻璃在980 nm吸收截面与Yb³⁺掺杂浓度成反比;当样品中Yb³⁺离子掺杂浓度为3.94×10²⁰ cm^-3时,玻璃在1.53 μm的吸收截面和发射截面最大,在1.40～1.60 μm积分吸收截面也最大;Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃在1.53 μm的荧光半高宽随Er³⁺掺杂浓度升高而增加,当Er³⁺离子掺杂浓度为2.41×10²⁰ cm^-3时,玻璃的荧光半高宽(FWHM)达到52.5 nm.     

FLUORESCENCE MECHANISMS OF Tm3+- AND Yb3+/Tm3+ DOPED AlF3-BASED FLUORIDE GLASS

A complete set of spectroscopic parameters, including Judd-Ofelt parameters, radiative transition probabilities, radiative lifetime, branching ratios and integrated absorption cross section, have been calculated for Tm³⁺- doped fluoroaluminate (AYF) glass, based on the measured absorption spectra. The mechanism of Tm³⁺→Tm³⁺ and Yb³⁺\Leftrightarrow Tm³⁺ energy transfers and fluorescence properties have been investigated in both Tm³⁺ single-doped and Yb³⁺/Tm³⁺ double-doped AYF glasses. The cross-relaxation process, ³F₄+³H₆→2³H₄, is proved, which makes the optimum Tm³⁺ concentration of 1.77μm fluorescence (³H₄→³H₆) much higher than 1.45μm fluorescence (³F₄→³3H₄) in Tm³⁺:AYF glasses. In Yb³⁺/Tm³⁺:AYF glasses, a stronger concentration quenching is found for the 476nm emission than that for the 797nm emission, and is discussed under the 970nm-excitation.