Li3V2(PO4)3/C和Li2.5Na0.5V2(PO4)3/C的结构和电化学性能的比较研究

采用溶胶-凝胶法合成了锂离子正极材料Li3V2(PO4)3/C(LVP/C)及Li2.5Na0.5V2(PO4)3/C,并用XRD、循环伏安及交流阻抗等方法,研究了大量Na+掺杂对材料结构和电化学性能影响。结果表明,大量钠离子的掺杂会使LVP结构由单斜向菱方转变。掺杂化合物Li2.5Na0.5V2(PO4)3/C在0.5 C充电1 C放电时,首次放电容量为118 mAh.g-1,50次循环后容量保持率为92.4%,并发现与单斜LVP存在多个放电平台不同,Li2.5Na0.5V2(PO4)3/C仅在3.7 V处有一个放电平台。     

电池正极材料Li3V2(PO4)3/C的水热合成和性能

以LiOH·H2O, NH4VO3, NH4H2PO4 和麦芽糖等为原料, 采用水热法合成了碳包覆的磷酸钒锂化合物, 考察了碳含量对材料电化学性能的影响. 利用XRD, TEM, SEM和恒流充放电测试等手段对产物的结构、 形貌和电化学性能进行表征. 结果表明, 在650℃煅烧的样品为单一纯相的单斜晶体结构. 晶体颗粒分布为100~300 nm, 粒度分散均匀, 分散性良好, 无团聚现象, 且在颗粒表面包覆了一层无定形碳, 这有利于改善材料的导电率. 含碳量为10.23%的样品, 在倍率1.0C的电流密度下, 在3.0~4.3 V电压范围内, 样品的首次放电比容量高达118.8 mA·h/g, 循环15圈后放电比容量为115.1 mA·h/g, 容量保持率为96.88%.     

碳包覆Li3V2(PO4)3:溶胶-凝胶法合成及性能

利用V₂O₅、LiOH·H₂O、H₂O₂、NH₄H₂PO₄与柠檬酸为原料,通过溶胶-凝胶法合成了碳包覆的Li₃V₂(PO₄)₃复合正极材料。采用XPS、XRD、SEM、TEM、拉曼光谱和电化学方法对材料的性能进行了研究。还研究了其结构与焙烧温度、样品电导率和电化学性能的关系。研究表明复合材料具有空间群为P2₁/n的单斜结构,表面包覆粗糙多孔的碳层。在800 ℃下制备的碳包覆样品的电子导电率高达9.81×10^-5 S·cm^-1,约为高温固相氢气还原法制备的未包覆碳Li₃V₂(PO₄)₃的10000倍。测试结果表明碳包覆Li₃V₂(PO₄)₃的电化学性能远优于未包覆碳的样品。在3.0～4.3 V电压范围内,以0.1C和2C倍率充放电时,碳包覆的Li₃V₂(PO₄)₃具有高比容量(分别为128和109 mAh·g^-1)和优异的循环性能。     

钼掺杂Li3V2（PO4）3/C正极材料的制备及其电化学性能研究

以Li2CO3、NH4H2PO4、V2O5和MoO3为原料,柠檬酸为络合剂和碳源,采用溶胶-凝胶法制备了锂离子正极材料Li3MoxV2-x(PO4)3/C(x=0.01,0.02,0.03).X射线衍射(XRD)表明,合成的材料具有单一的单斜晶系结构,空间群为P21/n.扫描电镜(SEM)显示Li3Mo0.02V1.98(PO4)3/C具有均一的表面形貌.恒流充放电测试表明,当x=0.02时,掺杂后的Li3Mo0.02V1.98(PO4)3具有最佳的电化学性能.在1C倍率下,3.0～4.3 V电位区间,Li3Mo0.02V1.98(PO4)3/C的首次放电比容量达到122.3 mAh.g-1,循环50周之后,容量没有衰减的迹象;而当x=0、0.01和0.03时,首次放电比容量仅分别为117.1、115.1和116.0 mAh.g-1.在3C和5C倍率下,样品Li3Mo0.02V1.98(PO4)3/C仍能保持优异的循环稳定性.     

表面包覆保护的新型正极材料LiFeBO3电化学性能

以偏硼酸锂和草酸亚铁为原料,采用固相反应,合成了用于动力锂离子电池新型正极材料LiFeBO3,并用乙丙共聚物（EPM）对该材料进行包覆保护处理;采用XRD、SEM和元素分析等测试技术对样品进行表征。 实验表明,LiFeBO3具有较高的放电重量比容量,而且包覆EPM后的硼酸铁锂具有更好的电化学性能,5%EPM包覆的硼酸锂首次放电容量达190 mA·h/g,0.5 C下充放电循环50次后容量衰减只有4.2%。     

Li4Mn5O12包覆对三元正极材料结构和性能的影响

LiNi_1/3Mn_1/3Co_1/3O₂具有很高的理论比容量,但是三元正极材料在高电压下长循环时,其表面结构发生较大的衰退,导致电池的循环性能和倍率性能变差。本文采用耐高电压且结构稳定的富锂尖晶石Li₄Mn₅O₁₂包覆LiNi_1/3Mn_1/3Co_1/3O₂可以有效改善材料的电化学性能。通过XRD、SEM、XPS和TEM等手段对包覆后的材料进行分析,证实了在LiNi_1/3Mn_1/3Co_1/3O₂的表面形成了10nm厚的均匀Li₄Mn₅O₁₂的包覆层;在循环100圈后,包覆后的LiNi_1/3Mn_1/3Co_1/3O₂仍...     

锂离子电池正极材料Li3V2(PO4)3/C的制备及电化学性能

以球磨结合焙烧的方法制备锂离子电池正极材料Li3V2(PO4)3/C.XRD、EIS表征及以该材料作正极的恒电流循环测试表明,所得产物为晶体结构发育良好的单斜晶系Li3V2(PO4)3.在0.1C、0.25C和0.5C倍率下,首次放电比容量分别为150.6、134.1和107.1mAh·g-1.0.25C循环130周后容量保持率为87.3%,而0.5C循环105周后容量保持率仍达到87.2%.锂离子在材料中的嵌入、脱出伴随明显的两相转变过程.电荷传递阻抗和SEI膜阻抗是影响材料倍率性能的主要因素.     

低温固相反应合成Li3V2(PO4)3正极材料及其性能

利用V₂O₅·nH₂O湿凝胶，LiOH·H₂O，NH₄H₂PO₄和C等作原料，通过低温固相还原反应在550 ℃焙烧12 h制备出Li₃V₂(PO₄)₃正极材料。采用XRD，SEM和电化学测试对Li₃V₂(PO₄)₃样品性能进行研究。XRD研究表明本法所合成的Li₃V₂(PO₄)₃同传统的高温固相反应法所合成的Li₃V₂(PO₄)₃一样同属于单斜晶系结构。SEM测试表明所合成的样品平均粒径大小约为0.5 μm且粒径分布较窄。电化学测试表明以0.2 C的倍率放电时，样品的首次放电容量为130 mAh·g^-1，室温下循环30次后其比容量为124 mAh·g^-1。     

Mg^2＋掺杂对锂离子正极材料Li3V2（PO4）3的影响

随着市场对锂离子电池(LIB)需求的日趋增长,对电极活性物质的要求也在朝着高能量密度、低成本、安全稳定、环境友好的方向努力,其中正极材料相对负极材料的发展较为缓慢,成为制约LIB发展的瓶颈。NASICON结构的Li3V2(PO4)3属于单斜晶系,相对金属锂具有很高的电势,理论容量高达19     

YF3包覆Li(Li0.22Ni0.17Mn0.61)O2正极材料的性能

富锂层状氧化物作为锂离子电池正极材料具有高比容量优势.采用草酸盐共沉淀法制备Li(Li0.22Ni0.17Mn0.61)O2,并用YF3包覆电极.采用X射线衍射(XRD)、扫描电子显微镜(SEM)和X射线能谱分析(EDS)表征材料结构、观察材料形貌.结果表明,材料颗粒尺寸在100～200 nm范围,YF3包覆不会改变材料结构和形貌.电化学恒流充放电测试表明,YF3包覆Li(Li0.22Ni0.17Mn0.61)O2电极的比容量,尤其倍率比容量明显提高.60 mA·g-1电流密度下包覆电极材料30周循环后其比容量保持在220 mAh·g-1以上,1500 mA·g-1电流密度下其比容量仍可达150 mAh·g-1.电化学阻抗谱(EIS)测试结果表明,YF3包覆电极电荷转移电阻和扩散阻抗均明显降低,有利于电化学性能改善.     

Nitrogen-doped Carbon Coated Na3V2(PO4)3 with Superior Sodium Storage Capability

Cathodes with high cycling stability and rate capability are required for ambient temperature sodium ion batteries in renewable energy storage application. Na₃V₂(PO₄)₃ is an attractive cathode material with excellent electrochemical stability and fast ion diffusion coefficient within the 3D NASICON structure. Nevertheless, the practical application of Na₃V₂(PO₄)₃ is seriously hindered by its intrinsically poor electronic conductivity. Herein, solvent evaporation method is presented to obtain the nitrogen-doped carbon coated Na₃V₂(PO₄)₃ cathode material, delivering enhanced electrochemical performances. N-Doped carbon layer coating serves as a highly conducting pathway, and creates numerous extrinsic defects and active sites, which can facilitate the storage and diffusion of Na⁺. Moreover, the N-doped carbon layer can provide a stable framework to accommodate the agglomeration of the electrode upon electrode cycling. N-Doped carbon coated Na₃V₂(PO₄)₃(NC-NVP) exhibits excellent long cycling life and superior rate performances than bare Na₃V₂(PO₄)₃ without carbon coating. NC-NVP delivers a stable capacity of 95.9 mA·h/g after 500 cycles at 1 C rate, which corresponds to high capacity retention(94.6%) with respect to the initial capacity(101.4 mA·h/g). Over 91.3% of the initial capacity is retained after 500 cycles at 5 C, and the capacity can reach 85 mA·h/g at 30 C rate.     

Li3Fe2(PO4)3/C正极材料的电化学性能及其反应机理研究

采用溶胶凝胶及高能球磨制得Li₃Fe₂(PO₄)₃/C材料,利用多种物理及其电化学技术观察材料形貌,表征材料结构及电化学性能,用电化学原位XAFS等初步研究Li₃Fe₂(PO₄)₃/C超理论容量电化学反应机理. 结果显示,Li₃Fe₂(PO₄)₃/C的结构为单斜晶系,空间群P21/n. 2.0 ~ 4.0 V电位区间,10 mAh·g^-1电流密度,Li₃Fe₂(PO₄)₃/C电极的首周期放电比容量为129 mAh·g^-1,达到其理论容量. 若电位区间拓宽至2.0 ~ 4.95 V,其首周期放电比容量高达165 mAh·g^-1,超出理论的“额外”容量30%. 电化学原位XAFS测试未观察到明显的Fe³⁺/Fe⁴⁺氧化还原对参与电化学反应,初步推测“额外”容量可能来自于该复合材料的高浓度表面缺陷.     

快离子导体Li3V2(PO4)3包覆LiFePO4的结构和性能

通过机械活化将快离子导体Li3 V2(PO4)3包覆在LiFePO4 表面, 制备了性能优异的复合正极材料9LiFePO4@Li3 V2(PO4)3. 用XRD, SEM, HRTEM, EDS和电化学测试等手段研究了材料的物理化学性能. 结果表明, 包覆后的材料含有橄榄石结构的LiFePO4、单斜晶系的Li3 V2(PO4)3 和正交晶系的Li3 PO4; LiFePO4颗粒表面包覆了一层Li3 V2(PO4)3, 且部分V3+进入LiFePO4晶格内部, 使其晶格参数减小, 包覆后的LiFePO4的交换电流密度和锂离子扩散系数均提高了1个数量级. 电化学测试结果表明, 包覆后的LiFePO4的倍率性能及循环性能都得到显著改善, 在1C和2C倍率下, 包覆后的LiFePO4的首次放电比容量较包覆前分别提高了34.09%和78.97%, 经150次循环后容量保持率分别提高了27.77%和65.54%; 并且5C时容量为121.379 mA·h/g(包覆前LiFePO4在5C下几乎没有容量), 循环350次后的容量保持率高达94.03%.     

Conducting Graphene Decorated Li3V2(PO4)3/C for Lithium‐Ion Battery Cathode with Superior Rate Capability and Cycling Stability

In this study, core‐shell structured Li₃V₂(PO₄)₃/C wrapped in graphene nanosheets has been successfully prepared. The reduction of graphene oxide and the synthesis of Li₃V₂(PO₄)₃/C are carried out simultaneously using a chemical route followed by a solid‐state reaction. The effects of conducting graphene are studied by X‐ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectra and electrochemical measurements. The results reveal that the graphene sheets not only form a compact and uniform coating layer throughout the Li₃V₂(PO₄)₃/C, but also stretch out and cross‐link into a conducting network around the Li₃V₂(PO₄)₃/C particles. Thus, the graphene decorated Li₃V₂(PO₄)₃/C electrode exhibits superior high‐rate capability and long‐cycle stability. It delivers a reversible discharge capacity of 178.2 mAh·g^?1 after 60 cycles at a current density of 0.1 C, and the rate performances of 176, 169.3, 156.1 and 135.7 mAh·g^?1 at 1, 2, 5 and 10 C, respectively. The superior electrochemical properties make the graphene decorated Li₃V₂(PO₄)₃/C composite a promising cathode material for high‐performance lithium‐ion battery.     

Li3V2（PO4）3/C正极材料在不同电压区间的电化学行为及容量衰减原因

采用溶胶-凝胶法制备锂离子电池正极材料Li3V2(PO4)3/C.通过恒电流充放电测试、循环伏安(CV)、电化学阻抗谱(EIS)等方法,研究了Li3V2(PO4)3/C在不同电压区间的电化学行为(3.0-4.5 V和3.0-4.8 V).结果表明,3.0-4.8 V电压区间的循环性能和倍率性能均不及3.0-4.5 V电压区间的.3.0-4.5 V区间0.1C (1C=150 mA?g-1)倍率首次放电比容量为127.0 mAh?g-1,循环50次后容量保持率为99.5%,而3.0-4.8 V区间的分别为168.2 mAh?g-1和78.5%.经过高倍率测试后再回到0.1C倍率充放电,3.0-4.5 V和3.0-4.8 V的放电比容量分别为初始0.1C倍率的99.0%和80.7%.经过3.0-4.8 V电压区间测试后,少部分第三个锂离子能够在低于4.5 V的电压脱出,使3.0-4.5 V电压区间的放电比容量提升了7.4%. CV结果表明3.0-4.8 V区间的容量损失主要表现为第一个锂离子的不可逆损失.极片的X射线衍射(XRD)和X射线光电子能谱(XPS)分析测试结果表明经过3.0-4.8 V测试后, Li3V2(PO4)3的结构发生了轻微的改变.电感耦合等离子体(ICP)测试结果表明循环后的电解液中含有少量的V.结构变形和V溶解可能是Li3V2(PO4)3在3.0-4.8 V区间容量衰减的主要原因.     

Ti4+离子掺杂对Li3V2(PO4)3晶体结构与性能的影响

采用溶胶凝胶/碳热还原法合成了锂离子电池正极材料Li3V2(PO4)3及其掺Ti化合物Li3-2x(V1-xTix)2-(PO4)3. 电化学测试结果表明, 经Ti4+离子掺杂后材料的充放电性能及循环性能明显提高. 与纯相Li3V2(PO4)3在3.58、3.67和4.08 V出现三个平台相比, 掺杂后材料的前两个平台发生简并且平台趋于模糊的倾斜状态. 这种趋势随掺杂量的增大而增强. 差热分析(DTA)表明掺杂生成了稳定的酌相产物. 采用X射线衍射和Rietveld方法表征了化合物的晶体结构, 结果表明, 三个不同位置Li的不完全占据导致晶体中产生阳离子空穴, 使材料在常温下的离子电导率提高了3个数量级. 锂离子混排提高了样品的电导率和充放电比容量.     

Li3V2(PO4)3/C正极材料在不同电压区间的电化学行为及容量衰减原因

采用溶胶-凝胶法制备锂离子电池正极材料Li₃V₂(PO₄)₃/C. 通过恒电流充放电测试、循环伏安(CV)、电化学阻抗谱(EIS)等方法, 研究了Li₃V₂(PO₄)₃/C 在不同电压区间的电化学行为(3.0-4.5 V和3.0-4.8 V). 结果表明, 3.0-4.8 V电压区间的循环性能和倍率性能均不及3.0-4.5 V电压区间的. 3.0-4.5 V区间0.1C (1C=150mA·g^-1)倍率首次放电比容量为127.0 mAh·g^-1, 循环50次后容量保持率为99.5%, 而3.0-4.8 V区间的分别为168.2 mAh·g^-1和78.5%. 经过高倍率测试后再回到0.1C倍率充放电, 3.0-4.5 V和3.0-4.8 V的放电比容量分别为初始0.1C倍率的99.0%和80.7%. 经过3.0-4.8 V电压区间测试后, 少部分第三个锂离子能够在低于4.5V的电压脱出, 使3.0-4.5 V电压区间的放电比容量提升了7.4%. CV结果表明3.0-4.8 V区间的容量损失主要表现为第一个锂离子的不可逆损失. 极片的X射线衍射(XRD)和X射线光电子能谱(XPS)分析测试结果表明经过3.0-4.8 V测试后, Li₃V₂(PO₄)₃的结构发生了轻微的改变. 电感耦合等离子体(ICP)测试结果表明循环后的电解液中含有少量的V. 结构变形和V溶解可能是Li₃V₂(PO₄)₃在3.0-4.8 V区间容量衰减的主要原因.     

锂离子电池复合正极材料xLiFePO4·yLi3V2(PO4)3的复合机制

以FePO4·xH2O、V2O5、NH4H2PO4和Li2CO3为原料, 以乙二酸为还原剂, 通过湿化学还原-低温热处理方法制备出锂离子复合正极材料xLiFePO4·yLi3V2(PO4)3. X射线衍射(XRD)结果表明, 合成的材料中橄榄石结构的LiFePO4和单斜晶系的Li3V2(PO4)3两相共存; 从复合材料中LiFePO4、Li3V2(PO4)3相对于相同条件下制备的纯相LiFePO4和Li3V2(PO4)3的晶格常数变化以及结合高分辨透射电子显微镜(HRTEM)、能量散射X射线(EDAX)的结果可以看出, 在复合材料xLiFePO4·yLi3V2(PO4)3中存在部分V和Fe, 分别掺杂在LiFePO4和Li3V2(PO4)3中, 并形成固溶体; X射线光电子能谱(XPS)结果表明, Fe/V在复合材料中的价态与各自在LiFePO4和Li3V2(PO4)3中的价态保持一致, 分别为+2 和+3价. 充放电测试表明, 制备出的复合正极材料电化学性能明显优于单一的LiFePO4和Li3V2(PO4)3; 循环伏安测试表明, 复合正极材料具有优良的脱/嵌锂性能.     

流变相法制备海藻酸基碳包覆Li3V2(PO4)3材料的电化学性能

Li₃V₂(PO₄)₃/C (LVP/C) cathode materials were successfully prepared by a rheological phase method using alginic acid as the carbon source. The X-ray diffraction (XRD) patterns demonstrate that all the samples contain pure LVP with the same monoclinic structure. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images show that LVP/C materials have a uniform particle size. The LVP/C sample with 10% (w) alginic acid shows the best cycling stability. It delivers a discharge capacity of 117.5 mAh·g^-1 (3.0-4.3 V), which can be maintained at 116.5 mAh·g^-1 after 50 cycles at a rate of 0.1C. Its capacity retentions of 99.1% (3.0-4.3 V) and 76.8% (3.0-4.8 V) after 50 cycles are prominently higher than those of pristine Li₃V₂(PO₄)₃, which are 89.7% (3.0-4.3 V) and 62.39% (3.0-4.8 V). These outstanding electrochemical performances are mainly attributed to the alginic acid-based carbon coating, which can increase the electronic conductivity of materials and buffer the mechanical damage of the active materials during the Li ion insertion/extraction process, thus improving the electrochemical performance of the LVP/C samples.     

Design and Construction of 3D Porous Na3V2(PO4)3/C as High Performance Cathode for Sodium Ion Batteries

An easy and delicate approach using cheap carbon source as conductive materials to construct 3D sequential porous structural Na3V2(PO4)3/C(NVP/C)with high performance for cathode materials of sodium ion battery is highly desired.In this paper,the NVP/C with 3D sequential porous structure is constructed by a delicate approach named as“cooking porridge”including evaporation and calcination stages.Especially,during evaporation,the viscosity of NVP/C precursor is optimized by controlling the adding quantity of citric acid,thus leading to a 3D sequential porous structure with a high specific surface area.Furthermore,the NVP/C with a 3D sequential porous structure enables the electrolyte to interior easily,providing more active sites for redox reaction and shortening the diffusion path of electron and sodium ion.Therefore,benefited from its unique structure,as cathode material of sodium ion batteries,the 3D sequential porous structural NVP/C exhibits high specific capacities(115.7,88.9 and 74.4 mA·h/g at current rates of 1,20 and 50 C,respectively)and excellent cycling stability(107.5 and 80.4 mA·h/g are remained at a current density of 1 C after 500 cycles and at a current density of 20 C after 2200 cycles,respectively).