High magnetostriction at low fields of (Tb1−xDyx)0.2Pr0.8(Fe0.4Co0.6)1.88C0.05 intermetallic compounds

The structure and magnetostriction of the (Tb_1−xDy_x)_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 intermetallic compounds (0≤x≤1) were studied by X-ray diffraction and magnetic measurements. The formation of an approximate single Laves phase with a MgCu2-type cubic structure was observed in this series of compounds. It was found that the Curie temperature and the saturation magnetization of the compounds would decrease with increase in the Dy content up to x=1. The magnetostriction λ_a (λ_a=λ_‖-λ_⊥) gently rises when x≤0.6, and follows with a precipitous fall when x exceeds 0.6, with the highest value of λ_a being reached in the compounds with x=0.6. The magnetostriction of all the samples was observed to approach their own saturation in the magnetic fields higher than 4 kOe. This indicates that the addition of a small amount of Dy could effectively improve the low-field magnetostriction of the Tb_0.2Pr_0.8(Fe_0.4Co_0.6)_1.88C_0.05 compounds, which could become a kind of promising magnetostrictive material.     

Magnetic transitions and magnetostrictive properties of Laves compounds Sm0.88Nd0.12(Fe1−xCox)1.93

The structure, magnetic and magnetostrictive properties of Sm_0.88Nd_0.12(Fe_1−xCo_x)_1.93 (0≤x≤1.0) alloys have been investigated. The alloys have the cubic MgCu₂ structure over the whole composition range and the lattice parameter a decreases with increasing x. For 0≤x≤0.2, substitution of Co for Fe slightly increases the saturation magnetization M_s and Curie temperature T_c, while further substitution causes a decrease in both M_s and T_c. The spin reorientation is observed, and a phase diagram for the spin configurations of the Sm_0.88Nd_0.12(Fe_1−xCo_x)_1.93 system is determined. The spontaneous magnetostriction λ₁₁₁ increases as x is increased, while a monotonic decrease of the saturation magnetostriction λ_s with x originates from the increase of λ₁₀₀ with opposite sign to that of λ₁₁₁, which may be caused by the filling of the d band due to Co substitution.     

Magnetic properties and room-temperature magnetocaloric effect in the doped antipervoskite compounds Ga1−xAlxCMn3 (0≤x≤0.15)

We report the effects of Al doping on the structure, magnetic properties, and magnetocaloric effect of antiperovskite compounds Ga_1−xAl_xCMn₃ (0≤x≤0.15). Partial substitutions of Al for Ga enhance the Curie temperature (from 250 K for x=0.0 to 312 K for x=0.15) and the saturation magnetization. On increasing the doping level x, the maximum values of the magnetic entropy change (−ΔS_M) decreases while the temperature span of −ΔS_M vs. T plot broadens. Furthermore, the relative cooling power (RCP) is also studied. For 20 kOe, the RCP value tends to saturate at a high doping level (for x=0.12, 119 J/kg at 296 K). However, at 45 kOe, the RCP value increases quickly with increasing x (for x=0.15, 293 J/kg at 312 K). Considering the relatively large RCP and inexpensive raw materials, Ga_1−xAl_xCMn₃ may be alternative candidates for room-temperature magnetic refrigeration.     

The structural and magnetic properties of Ni2Mn1−xBxGa Heusler alloys

The influence of the substitution of manganese by boron on the crystal structure and magnetic properties of Ni₂Mn_1−xB_xGa Heusler alloys with 0?x?0.5 has been investigated using X-ray diffraction, thermal expansion, resistivity, and magnetization measurements. The samples with concentrations x<0.25 were found to be of single phase and belonged to the cubic L2₁ crystal structure at room temperature. Crystal cell parameters of the alloys decreased from 5.830 to 5.825 Å with increasing boron concentration (x) from 0 to 0.25. The alloys were ferromagnetically ordered at 5 K and the saturation magnetization decreased with increasing boron concentration. The ferromagnetic ordering and structural transition temperatures for 0?x?0.3 have been observed and the phase (x−T) diagram of the Ni₂Mn_1−xB_xGa system was constructed. The phase (x−T) diagram indicates that the ground state of Ni₂Mn_1−xB_xGa alloys belongs to ferromagnetic martensitic, premartensitic, and austenitic phases in x?0.12, 0.12<x?0.18, and 0.18<x?0.3, respectively. The relative influence of cell parameters and electron concentrations on the phase diagram is discussed.     

Field and temperature induced colossal strain in Gd5(SixGe1−x)4

Gd₅(Si_xGe_1−x)₄, known for its giant magnetocaloric effect, also exhibits a colossal strain of the order of 10,000 ppm for a single crystal near its coupled first-order magnetic-structural phase transition, which occurs near room temperature for the compositions 0.41≤x≤0.575. Such colossal strain can be utilised for both magnetic sensor and actuator applications. In this study, various measurements have been carried out on strain as a function of magnetic field strength and as a function of temperature on single crystal Gd₅Si₂Ge₂ (x=0.5), and polycrystalline Gd₅Si_1.95Ge_2.05 (x=0.487) and Gd₅Si_2.09Ge_1.91 (x=0.52). Additionally a giant magnetostriction/thermally induced strain of the order of 1800 ppm in polycrystalline Gd₅Si_2.09Ge_1.91 was observed at its first order phase transition on varying temperature using a Peltier cell without the use of bulky equipment such as cryostat or superconducting magnet.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Influence of low Co substitution on magnetoelastic properties of HoFe11Ti intermetallic compound

The thermal expansion and magnetostriction of HoFe_11−xCo_xTi (x=0, 0.3, 0.7 and 1) intermetallic compounds were measured, using the strain gauge method in the temperature range 77–590 K under applied magnetic fields up to 1.5 T. Results show that for samples with x=0 and 0.3, both linear thermal expansion and linear thermal expansion coefficient exhibit anomalies below the Curie temperature. Below room temperature, the spontaneous volume magnetostriction decreases with Co content. For all compounds studied, the anisotropic magnetostriction shows similar behaviour in the measured temperature range. The magnetostriction compensation occurs above room temperature in all samples. The volume magnetostriction shows a linear dependence on the applied field and by approaching the Curie temperature this trend changes to parastrictive behaviour. The results of the spontaneous magnetostriction are discussed based on the local magnetic moment model. The contribution of magnetostriction attributed to the magnetic sublattices R and T (Fe or Co) is discussed.     

Magnetoelastic properties of Nd6Fe13Cu intermetallic compound

Magnetoelastic properties of Nd₆Fe₁₃Cu intermetallic compound are reported. To study the magnetoelastic behaviour of this compound, the thermal expansion as well as the longitudinal (λ_l) and transverse (λ_t) magnetostriction were measured by using the strain gauge method in the selected temperature range of 80-500 K under applied magnetic fields up to 1.5 T. An anomaly and invar-type effects are observed in the linear thermal expansion and α(T) curves at the Néel temperature. The linear spontaneous magnetostriction decreases sharply by approaching the Néel temperature and also shows the short-range magnetic ordering effects when antiferromagnetic-paramagnetic transition occurs. In the low field region, the absolute values of the anisotropic magnetostriction are small and then start to increase with applied magnetic field. Each isofield curve of the anisotropic magnetostriction passes through a minimum and then approaches to zero with increasing temperature. This magnetostriction compensation arises from the difference in the magnetoelastic coupling constants of the sublattices in this compound.     

Magnetic entropy change and magnetic phase transition of LaFe11.4Al1.6Cx （x=0-0.8） compounds

The unit cell volume and phase transition temperature of LaFe11.4Al1.6Cx compounds have been studied. The magnetic entropy change, refrigerant capacity and the type of magnetic phase transition are investigated in detail for LaFe11.4Al1.6Cx with x=0.1, All the LaFe11.4Al1.6Cx （x=0-0.8） compounds have the cubic NaZn13-type structure. The addition of carbon atoms brings about a considerable increase in the lattice parameter. The bulk expansion results in the change of phase transition temperature （Tc）, Tc increases from 187K to 269 K with x varying from 0.1 to 0.8, Meanwhile an increase in the lattice parameter can also cause a change of the magnetic ground state from antiferromagnetic to ferromagnetic. Large magnetic entropy change IASI is found over a large temperature range around Tc and the refrigerant capacity is about 322J/kg for LaFe11.4Al1.6C0.1. The magnetic phase transition belongs in weakly first-order one for x=0.1.     

Effect of Sr concentration on microstructure and magnetic properties of (Ba1−xSrx)(Ti0.3Fe0.7)O3 ceramics

Fe-doped (Ba_1−xSr_x)TiO₃ ceramics were prepared by solid-state reaction, and ferromagnetism was realized at room temperature. The microstructure and magnetism were modified by the Sr concentration control (0≤x≤75 at%) at a fixed Fe concentration, and the relevant magnetic exchange mechanism was discussed. All the samples are shown to have a single perovskite structure. When increasing the Sr concentration, the phase structure is transformed from a hexagonal perovskite into a cubic perovskite, with a monotonic decrease in lattice parameters induced by ionic size effect. The room-temperature ferromagnetism is expected to originate from the super-exchange interactions between Fe³⁺ on pentahedral and octahedral Ti sites mediated by the O²⁻ ions. The increase in Sr addition modifies two main influencing factors in magnetic properties: the ratio of pentahedral to octahedral Fe³⁺ and the concentration of oxygen vacancies, leading to a gradually enhanced saturation magnetization. The highest value, obtained for Fe-doped (Ba_0.25Sr_0.75)TiO₃, is an order of magnitude higher than that of the Fe-doped BaTiO₃ system with similar Fe concentration and preparation conditions, which may indicate (Ba_1−xSr_x)TiO₃ as a more suitable matrix material for multiferroic research.     

Structural, magnetic properties and magnetostriction studies of Sm1−xNdxFe1.55 alloys

Structural, magnetic properties and magnetostriction studies of Sm_1−xNd_xFe_1.55 (0≤x≤0.56) alloys have been performed. X-ray diffraction analysis confirms the presence of single cubic Laves phase in Sm_1-xNd_xFe_1.55 alloys with 0≤x≤0.48. The lattice parameter of alloys increases linearly with increase in Nd content while the Curie temperature behaves in the opposite way. The alloy x=0.08 exhibits a giant magnetostriction value (λ_∥-λ_⊥) of −2187 ppm at a magnetic field of 12 kOe due to the anisotropy compensation between Sm³⁺ and Nd³⁺ ions.     

Effect of sintering atmosphere on the electrical and optical properties of (ZnO)1−x(MnO2)x NTCR ceramics

Nominal composition of (ZnO)_1−x(MnO₂)_x (0.005≤x≤0.2) ceramics have been prepared by the standard solid-state reaction method in three different sintering atmospheres: Ar, air, and reductive atmosphere. The effect of sintering atmosphere on the electron spin resonance (ESR), negative temperature coefficient of resistivity (NTCR), and photoluminescence (PL) properties of (ZnO)_1−x(MnO₂)_x ceramics has been investigated in detail. The results demonstrate that the sintering atmosphere has significant effects on the ESR signals of (ZnO)_1−x(MnO₂)_x; the NTCR of the samples sintered in air is larger than those sintering in Ar and reductive atmosphere; the deep-level PL related to oxygen vacancy increases when sintered in the reductive atmosphere.     

La0.1Bi0.9-xEuxFeO3化合物的结构与性能研究

利用固相反应烧结技术制备La_0.1Bi_0.9-xEu_xFeO₃系列化合物. 利用X射线粉末衍射进行物相鉴定和结构分析,确定了材料的相关系：x≤0.05,材料为R3c结构相;0.08≤x≤0.12,材料为赝R3c结构相;x≥0.15是Pbnm相,其中0.15≤x≤0.20区域Pbnm相存在畸变. 磁测量结果表明,材料具有弱铁磁性,对于x≤0.20材料,磁矩在x=0.12成分存在极值. 利用阻抗分析仪测量了室温介电常数随成分的变化关系.讨论了材料的结构与弱铁磁性和室温介电常数间的关系. 关键词： 0.1Bi_0.9-xEu_xFeO₃')" href="#">La_0.1Bi_0.9-xEu_xFeO₃ X射线衍射 磁性 介电常数     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.     

Abnormal positive thermal expansion in Mo substituted ZrW2O8

ZrW₂O₈ displays the unusual property of an isotropic bulk contraction in volume as a function of temperature. We report here on the positive thermal expansion (PTE) property caused by substituting Mo for W sites in ZrW₂O₈ at room temperature. The room temperature crystal structure of ZrW_2−xMo_xO₈ compounds, which were synthesized using a low temperature route, could be divided into ordered phase with α-ZrW₂O₈ structure (0≤x≤0.5) and disordered phase with β-ZrW₂O₈ (0.5<x≤1.5) and c-ZrMo₂O₈ structure (1.5<x≤2). ZrW_2−xMo_xO₈ adopting β-ZrW₂O₈ structure shows abnormal PTE property at room temperature due to the existence of water molecules, while ZrW_2−xMo_xO₈ adopting the other two structures (α-ZrW₂O₈ and c-ZrMo₂O₈) shows negative thermal expansion (NTE) property from room temperature until decomposition for α-ZrW₂O₈ structure or trigonal phase transition for c-ZrMo₂O₈ structure. The reason lies in the fact that the oxygen migration caused by the Mo substitution leads to the re-arrangement of W(Mo)O₄ tetrahedra lying along the 3-fold axis, only particular W/Mo ratio (0.5<x≤1.5) produces a special crystal structure, which allows the entrance of water molecules.     

Influence of boron on the giant magnetocaloric effect of La(Fe0.9Si0.1)13

The influences of boron addition on the phase formation, Curie temperature and magnetic entropy change of the NaZn₁₃-type La(Fe_0.9Si_0.1)₁₃ compound have been investigated. Eight boron containing La(Fe_0.9Si_0.1)₁₃B_x samples were prepared with x=0, 0.03, 0.06, 0.1, 0.2, 0.3, 0.5 and 0.6, respectively. Experimental results show that a small amount of B addition in La(Fe_0.9Si_0.1)₁₃ forms the solid solution NaZn₁₃-type structure phase by substituting B for Si or doping B into interstitial position of the lattice, preserves its giant magnetocaloric effects due to their first-order structural/magnetic transition, as well as increase its Curie temperature T_c slightly. The maximum magnetic entropy changes in the magnetic field change of 0–1.6 T are around 20 J kg^–1 K^–1 for the samples with Boron addition less than 0.3, while improving the Curie temperatures by 2 K.     

Structure,magnetic properties and magnetostriction of laves compounds Nd1−xPrx(Fe0.35Co0.55B0.1)2

The C15 Laves phases with composition Nd_1−xPr_x(Fe_0.35Co_0.55B_0.1)₂ (0?x?1) have been synthesized by arc melting and subsequent annealing. The Curie temperature T_c and the saturation magnetizations M_s at 5 and 295 K decrease with increasing Pr content. The linear anisotropic magnetostriction λ_a=λ_∥−λ_⊥ at room temperature for Nd_1−xPr_x(Fe_0.35Co_0.55B_0.1)₂ alloys with 0?x?0.4 initially reaches a negative minimum, then increases and changes its sign with increasing magnetic field H, and the λ_a for the alloys with x?0.6 is positive and increases as magnetic field H increases.     

Magnetic phase transitions of antiperovskite Mn3−xFexSnC (0.5≤x≤1.3)

The magnetization and electrical resistivity of Mn_3−xFe_xSnC (0.5≤x≤1.3) were measured to investigate the behavior of the complicated magnetic phase transitions and electronic transport properties from 5 to 300 K. The results obtained demonstrate that Fe doping at the Mn sites of Mn₃SnC induces a more complicated magnetic phase transition than that in its parent phase Mn₃SnC from a paramagnetic (PM) state to a ferrimagnetic (FI) state consisting of antiferromagnetic (AFM) and ferromagnetic (FM) components, while, with the change of Fe-doped content and magnetic field, there is a competition between the AFM component and FM component in the FI state. Both the Curie temperature (T_C) and the saturated magnetization M_s increase with increasing x. The FM component region becomes broader with further increasing Fe-doped content x. The external magnetic field easily creates a saturated FM state (and increased T_C) when . Fe doping quenches the negative thermal expansion (NTE) behavior from 200 to 250 K reported in Mn₃SnC.     

Luminescent properties of KGd1−x(WO4)2:Eux and KGd1−x(WO4)2−y(MoO4)y:Eux phosphors in UV-VUV regions

KGd_1−x(WO₄)_2−y(MoO₄)_y:Eu³⁺_x(0.1?x?0.75, y=0 and 0.2) phosphors are synthesized through traditional solid-state reaction and their luminescent properties in ultraviolet (UV) and vacuum ultraviolet (VUV) regions are investigated. Under 147 nm excitation, these phosphors show characteristic red emission with good color purity. In order to improve their emission intensity, the MoO₄²⁻ (20 wt%) is introduced into the anion of KGd_1−x(WO₄):Eu³⁺_x. The Mo⁶⁺ and Eu³⁺ co-doped KGd(WO₄)₂ phosphors show higher emission intensity in comparison with the singly Eu³⁺-doped KGd(WO₄)₂ in VUV region. The chromaticity coordination of KGd_0.45(WO₄):Eu³⁺_0.55 is (x=0.669, y=0.331), while that of KGd_0.45(WO₄)_1.8(MoO₄)_0.2:Eu³⁺_0.55 is (x=0.666, y=0.334) in VUV region.