Synthesis of Fe-doped NiO nanofibers using electrospinning method and their ferromagnetic properties

To make p-type diluted magnetic semiconductor (DMS), Ni_1−xFe_xO nanofibers with different Fe doping concentrations have been successfully synthesized by electrospinning method using polyvinyl alcohol (PVA) and Ni(CH₃COO)₂·4H₂O as starting materials. The nanofibers were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy, superconductivity quantum interference device (SQUID) and X-ray photoelectron spectroscopy (XPS) test. The results show that Fe doping has no influence on the diameter and surface morphology of NiO nanofibers, and the nanofibers are polycrystalline with NaCl structure. All Fe-doped samples show obvious ferromagnetic properties and the saturation magnetization is enhanced with increase of the doping concentration of Fe, which indicates that the doped Fe has been incorporated into the NiO host and results in room-temperature ferromagnetism in the Ni_1−xFe_xO nanofibers.     

Synthesis and magnetic properties of Li-Mn-Zn spinel oxides

LiMn_2−XZn_XO₄ (X<0.5) compounds were prepared by sol-gel method. The specimens with a large substitution degree (X>0.2) led to symmetry reduction from Fdm to P2₁3 in the spinel oxide, while those with a small substitution degree (X<0.1) had Fdm cubic symmetry. The Zn²⁺-substitution led to the enhancement of the low-temperature magnetic susceptibility and a shift in the Weiss constant from negative to positive, indicating that the dominant exchange interaction changed from antiferromagnetic to ferromagnetic. For the compounds with X=0.5, the spontaneous magnetization was 4.48μ_B and the Curie temperature was approximately 21 K. The experimentally obtained magnetization value was close to the value calculated under the assumption that the spins of the Mn⁴⁺ ions were aligned in ferromagnetic form. In addition, the magnetic properties of Li-Mn-Zn spinel oxides were briefly discussed, and compared with those of Li-Mn-M (M=Ni, Mg) spinel oxides.     

Structure and magnetic properties of Nb-doped FeZrB soft magnetic alloys

Structure and magnetic properties of Nb-doped (FeZrB)_100−xNb_x alloy are investigated by X-ray diffraction (XRD), differential scanning calorimetry and vibrating sample magnetometer. The fully amorphous structure of the as-quenched ribbons is confirmed by the XRD pattern. With increasing Nb, the glass transition temperature and the onset crystallization temperature are increased, indicating increased stability of the amorphous structure. For x=1, the saturation magnetization of the ribbons is 125.7 emu/g and the optimized annealing temperature increases from 550 to 630 °C. The morphology of the crystallized phases is observed by scanning electron microscopy. The results show that nanocrystalline α-Fe grains are dispersed in the amorphous matrix.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

DC current effect on the magnetic phase and transport properties of polycrystalline La0.7Ca0.3MnO3

The influence of DC current on the resistivity and phase transition of polycrystalline La_0.7Ca_0.3MnO₃ has been investigated. The specific heat measurement found that charge carriers and ferromagnetic spin-wave contributions were changed after applied DC current. Applying high electric fields leads to the formation of ferromagnetic regions. The resistivity drops abruptly once the percolating current path is established. As current through the sample disappears, the larger ferromagnetic (FM) clusters, however, remain and are frozen in giving a measurable contribution to the specific heat of the system. The larger clusters should give rise to the value of spin-wave stiffness constant (D), as it is expected to increase the strength of the ferromagnetic coupling. The metallic ferromagnetic regions would make the charge carrier delocalization and attribute to specific heat linear term γ.     

Effect of Sr concentration on microstructure and magnetic properties of (Ba1−xSrx)(Ti0.3Fe0.7)O3 ceramics

Fe-doped (Ba_1−xSr_x)TiO₃ ceramics were prepared by solid-state reaction, and ferromagnetism was realized at room temperature. The microstructure and magnetism were modified by the Sr concentration control (0≤x≤75 at%) at a fixed Fe concentration, and the relevant magnetic exchange mechanism was discussed. All the samples are shown to have a single perovskite structure. When increasing the Sr concentration, the phase structure is transformed from a hexagonal perovskite into a cubic perovskite, with a monotonic decrease in lattice parameters induced by ionic size effect. The room-temperature ferromagnetism is expected to originate from the super-exchange interactions between Fe³⁺ on pentahedral and octahedral Ti sites mediated by the O²⁻ ions. The increase in Sr addition modifies two main influencing factors in magnetic properties: the ratio of pentahedral to octahedral Fe³⁺ and the concentration of oxygen vacancies, leading to a gradually enhanced saturation magnetization. The highest value, obtained for Fe-doped (Ba_0.25Sr_0.75)TiO₃, is an order of magnitude higher than that of the Fe-doped BaTiO₃ system with similar Fe concentration and preparation conditions, which may indicate (Ba_1−xSr_x)TiO₃ as a more suitable matrix material for multiferroic research.     

Complex permittivity, complex permeability and microwave absorption properties of ferrite-paraffin polymer composites

We have investigated the electromagnetic (EM) characteristics of Co_xMn_1−xFe₂O₄ spinel ferrite (where x=0.0, 0.5 and 1.0) nanoparticles (NPs)/paraffin nanocomposite material at 8-20 GHz. Co_xMn_1−xFe₂O₄ NPs have been synthesized by cetyltrimethylammonium assisted hydrothermal route using NaOH. A variation in complex dielectric permittivity and magnetic permeability at room temperature with frequency in the range 8-20 GHz has been studied. Particles showed phase purity and crystallinity in powder X-ray diffraction (XRD) analysis. At the same time, Co_xMn_1−xFe₂O₄ NPs demonstrated a spinel cubic structure from XRD results. A reflection loss of −46.60 dB was found at 10.5 GHz for an absorber thickness of 2 mm. Co_xMn_1−xFe₂O₄ may be attractive candidates for EM wave absorption materials.     

Synthesis and magnetic properties of ordered barium ferrite nanowire arrays in AAO template

BaFe₁₂O₁₉ nanowire arrays having single magnetic domain size (≤460 nm) in anodic aluminum oxide (AAO) templates were prepared by sol-gel and self-propagating high-temperature synthesis techniques. The diameter of the nanowire arrays is approximately 70 nm and the length is about 2-4 μm. The specimens were characterized using X-ray diffraction, vibrating sample magnetometer, field emission scan electron microscope, atomic force microscopy and microwave vector network analyzer. The magnetic properties of BaFe₁₂O₁₉ nanowire arrays embedded in AAO templates were measured by VSM with a field up to 1274 KA/m at room temperature. The results indicate that the nanowire arrays exhibit large saturation magnetization and high coercivity in the range of 6000 Oe and an obvious magnetic anisotropy with the easy magnetizing axis along the length of the nanowire arrays, probably due to the shape anisotropy and magneto-crystalline anisotropy. Finally the microwave absorption properties of the nanowires were discussed.     

Synthesis and magnetic properties of single-crystalline BaFe12O19 nanoparticles

Rod-like and platelet-like nanoparticles of simple-crystalline barium hexaferrite (BaFe₁₂O₁₉) have been synthesized by the molten salt method. Both particle size and morphology change with the reaction temperature and time. The easy magnetization direction (0 0 l) of the BaFe₁₂O₁₉ nanoparticles has been observed directly by performing X-ray diffraction on powders aligned at 0.5 T magnetic field. The magnetic properties of the BaFe₁₂O₁₉ magnet were investigated with various sintering temperatures. The maximum values of saturation magnetization (σ_s=65.8 emu/g), remanent magnetization (σ_r=56 emu/g) and coercivity field (H_ic=5251 Oe) of the aligned samples occurred at the sintering temperatures of 1100 °C. These results indicate that BaFe₁₂O₁₉ nanoparticles synthesized by the molten salt method should enable detailed investigation of the size-dependent evolution of magnetism, microwave absorption, and realization of a nanodevice of magnetic media.     

Synthesis and luminescence properties of europium doped YBa3B9O18

Europium (Eu³⁺) doped YBa₃B₉O₁₈ were synthesized by conventional solid state solidification methods. (Y_1−xEu_x)Ba₃B₉O₁₈ formed solid solutions in the range of x=0–1.0. The luminescence property measurements upon excitation in ultraviolet–visible range show well-known Eu³⁺ excitation and emission. The charge transfer excitation band of Eu³⁺ dominates the excitation spectra. The emission spectrum of Eu³⁺ ions consists mainly of several groups of lines in the 550–720 nm region, due to the transitions from the ⁵D₀ level to the levels ⁷F_J (J=0, 1, 2, 3, 4) of Eu³⁺ ions. The dependence of luminescence intensity on Eu³⁺ concentration shows no concentration quenching for fully concentrated EuBa₃B₉O₁₈. Eu³⁺ doped YBa₃B₉O₁₈ are promising phosphors for applications in displays and optical devices.     

Effects of different sintering temperature and Nb2O5 content on structural and magnetic properties of Z-type hexaferrites

Nb-doped Z-type hexaferrites (Ba₃(Co_0.4Zn_0.6)₂Fe₂₄O₄₁) with composition of Ba₃(Co_0.4Zn_0.6)₂Fe₂₄O₄₁+x Nb₂O₅ (where x=0.0, 0.1, 0.2, 0.4, 0.6, 0.8, 1.2, 1.6 and 2.0 wt%) were prepared by a solid-state reaction method. The effects of different sintering temperature (T_s) and Nb₂O₅ content on the sintering behaviors, phase composing, microstructure, and magnetic properties of the samples were investigated. The results from X-ray diffraction and scanning electron microscopy show that as the amount of Nb₂O₅ additive increases, the major phase changes to Z-phase, Simultaneously, M-phase and a small amount of niobate phase appear. The Nb₂O₅ additive promotes the grain growth as reaction center at lower sintering temperature (1220 °C), but at higher temperature (1260 °C), niobate phase separated out in grain boundaries as secondary phase will restrain abnormal grain growth, so closed pores in grains are not formed. The Nb₂O₅ additive can enhance densification, improve initial permeability of hexaferrites by increasing the grain growth of hexaferrite and the displacement of ions in the sintering process due to the aberration and activation of crystal lattice, which is accompanied by the solubility of Nb⁵⁺ in the hexaferrites. A relative density of 96%, maximum initial permeability (32–33), minimum coercivity (454–455 A/m) and resonance frequency above 400 MHz were obtained for the sample with 0.8 wt% Nb₂O₅ sintered at 1260 °C for 6 h.     

Magnetic properties of YFe12−xMox compounds and magnetocaloric effect of YFe9.5Mo2.5

The characterization and magnetic properties of YFe_12−xMo_x (x=2.0, 2.5 and 3.0) with the ThMn₁₂-type structure, and the magnetocaloric effect of YFe_9.5Mo_2.5 were investigated. A directional growth was observed in YFe₁₀Mo₂ alloy. A broad peak in the zero-field-cooling (ZFC) magnetization curve of the YFe_12−xMo_x compounds is ascribed to the existence of ferromagnetic clusters with different site moments and scattered orientations of the moments. The broad range of the peak is reduced with increasing Mo content. A weak peak is observed near 190 K in the ZFC curve of YFe₉Mo₃, which is associated with the 8i sites being mostly occupied by Mo atoms. YFe_9.5Mo_2.5 has a magnetic entropy change of −1.09 J/kg K for a field change of 5 T at 277 K.     

Reverse micelle synthesis of perovskite oxide nanoparticles

La_0.6Sr_0.4Co_xFe_1−xO_3−δ (LSCF), La_0.6Sr_0.4Cu_0.2Fe_0.8O_3−δ, Ba_0.5Sr_0.4Co_0.8Fe_0.2O_3−δ and LaFeO_3−δ nanoparticles were synthesized by a reverse micelle procedure. Controlling the size of the micelles through the water:oil phase ratio enabled synthesis of phase pure perovskite particles with average sizes from 14 nm to 50 nm. Small amounts of an impurity phase, likely cobalt oxide, were detected in the XRD spectrum of high cobalt content samples of LSCF (x = 0.8). La_0.6Sr_0.4Co_0.2Fe_0.8O_3−δ nanoparticles were utilized to coat the surface of a dense thin-film La_0.6Sr_0.4Co_0.2Fe_0.8O_3−δ solid oxide fuel cell cathode. The polarization resistance of the nanoparticle coated electrode, measured at open circuit in air at 973 K, was 20% lower than an equivalent un-coated electrode.     

The structural and magnetic properties of Ni2Mn1−xBxGa Heusler alloys

The influence of the substitution of manganese by boron on the crystal structure and magnetic properties of Ni₂Mn_1−xB_xGa Heusler alloys with 0?x?0.5 has been investigated using X-ray diffraction, thermal expansion, resistivity, and magnetization measurements. The samples with concentrations x<0.25 were found to be of single phase and belonged to the cubic L2₁ crystal structure at room temperature. Crystal cell parameters of the alloys decreased from 5.830 to 5.825 Å with increasing boron concentration (x) from 0 to 0.25. The alloys were ferromagnetically ordered at 5 K and the saturation magnetization decreased with increasing boron concentration. The ferromagnetic ordering and structural transition temperatures for 0?x?0.3 have been observed and the phase (x−T) diagram of the Ni₂Mn_1−xB_xGa system was constructed. The phase (x−T) diagram indicates that the ground state of Ni₂Mn_1−xB_xGa alloys belongs to ferromagnetic martensitic, premartensitic, and austenitic phases in x?0.12, 0.12<x?0.18, and 0.18<x?0.3, respectively. The relative influence of cell parameters and electron concentrations on the phase diagram is discussed.     

Effect of Fe/Sr mole ratios on the formation and magnetic properties of SrFe12O19 microtubules prepared by sol-gel method

The sol was obtained by sol-gel method. Then, the sol was dripped onto the absorbent cotton template. The gel was obtained after the evaporation of water. Strontium ferrite microtubules were prepared after carrying out calcination process at different temperatures. The phase, morphology and particle diameter and the magnetic properties of samples were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM), respectively. The effects of Fe³⁺/Sr²⁺ mole ratio and calcination temperature on the crystal structure, morphology and magnetic properties of ferrite microtubules were studied. The external diameters of obtained SrFe₁₂O₁₉ microtubules were found to range between 8 and 13 μm; the wall thicknesses ranged between 1 and 2 μm. When the Fe³⁺/Sr²⁺ mole ratio and the calcination temperature were 11.5 and 850 °C, respectively, the coercivity, saturation magnetization and remanent magnetization for the samples were 7115.1 Oe, 70.1 and 42.4 emu/g, respectively. The mechanism of the formation and variation in magnetic properties of the microtubules were explained.     

The magnetic properties of oxide spinel Li0.5Fe2.5−2xAlxCrxO4 solid solutions

The exchange interactions (J_BB and J_AB are the intra and the inter-sublattice exchange interactions between neighbouring spins, respectively) are obtained by using the general expressions of canting angle and critical temperature obtained by mean field theory of Li_0.5Fe_2.5−2xAl_xCr_xO₄. The expression of magnetic energy of Li_0.5Fe_2.5−2xAl_xCr_xO₄ is obtained for different spin configurations and dilution x. The saturation magnetisation of Li_0.5Fe_2.5-2xAl_xCr_xO₄ is obtained with different values of dilution x. The magnetic phase diagram of Li_0.5Fe_2.5-2xAl_xCr_xO₄ materials is obtained by high temperature series expansions (HTSEs). The critical exponent associated with the magnetic susceptibility of Li_0.5Fe_2.5−2xAl_xCr_xO₄ is deduced.     

Short-range order analysis and some physical properties of InxSe1−x glasses

Bulk In_xSe_1−x (with x=5-25 at%) glasses were prepared using the melt-quench technique. Short range order(SRO) was examined by the X-ray diffraction using Cu(k_α) radiation in the wave vector interval 0.28≤k≤6.5 A⁰⁻¹.The SRO parameters have been obtained from the radial distribution function. The inter-atomic distance obtained from the first and second peak are r₁=0.263 and r₂=0.460 nm, which is equivalent In-Se and Se-Se bond length. The fundamental structural unit for the studied glasses is In₂Se₃ pyramid. Using the differential scanning calorimetry (DSC), the crystallization mechanism of In_xSe_1−x chalcogenide glass has been studied. The glass transition activation energy (E_g) is 289±0.3 kj/mol.There is a correlation amongst the glass forming ability, bond strength and the number of lone pair electrons. The utility of the Gibbs-Di Marzio relation was achieved by estimating T_g theoretically.     

Synthesis and magnetic properties of Fe100-xMox alloy nanowire arrays

The Fe100-xMox(13≤x≤25) alloy nanowire arrays are synthesized by electrodeposition of Fe 2+ and Mo 2+ with different ionic ratios into the anodic aluminum oxide templates.The crystals of Fe100-xMox alloy nanowires gradually change from polycrystalline phase to amorphous phase with the increase of the Mo content and the nanowires are of amorphous structure when the Mo content reaches 25 at%,which are revealed by the X-ray diffraction and the selected area electron diffraction patterns.As the Mo content increases,the magnetic hysteresis loops of Fe100-xMox alloy nanowires in parallel to the nanowire axis are not rectangular and the slopes of magnetic hysteresis loops increase.Those results indicate that the magnetostatic interactions between nanowires and the magnetocrystalline anisotropy both have significant influences on the magnetization reversal process of the nanowire arrays.     

Optoelectronic properties of GaAs1−xPx alloys under the influence of temperature and pressure

This work is concerned with the dependence of the electronic energy band structures for GaAs_1−xP_x alloys on temperature and pressure that is based on local empirical pseudo-potential method. The band structures of GaAs_1−xP_x alloys were calculated in the virtual crystal approximation using the EPM which incorporates compositional disorder as an effective potential.