Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

High quality nitrogen-doped zinc oxide thin films grown on ITO by sol–gel method

Highly transparent N-doped ZnO thin films were deposited on ITO coated corning glass substrate by sol–gel method. Ammonium nitrate was used as a dopant source of N with varying the doping concentration 0, 0.5, 1.0, 2.0 and 3.0 at%. The DSC analysis of prepared NZO sols is observed a phase transition at 150 °C. X-ray diffraction pattern showed the preferred (002) peak of ZnO, which was deteriorated with increased N concentrations. The transmittance of NZO thin films was observed to be ~88%. The bandgap of NZO thin films increased from 3.28 to 3.70 eV with increased N concentration from 0 to 3 at%. The maximum carrier concentration 8.36×10¹⁷ cm⁻³ and minimum resistivity 1.64 Ω cm was observed for 3 at% N doped ZnO thin films deposited on glass substrate. These highly transparent ZnO thin films can be used as a window layer in solar cells and optoelectronic devices.     

Structural and optical properties of Mn-doped ZnO nanocrystalline thin films with the different dopant concentrations

The transparent nanocrystalline thin films of undoped zinc oxide and Mn-doped (Zn_1−xMn_xO) have been deposited on glass substrates via the sol–gel technique using zinc acetate dehydrate and manganese chloride as precursor. The as-deposited films with the different manganese compositions in the range of 2.5–20 at% were pre-heated at 100 °C for 1 h and 200 °C for 2 h, respectively, and then crystallized in air at 560 °C for 2 h. The structural properties and morphologies of the undoped and doped ZnO thin films have been investigated. X-ray diffraction (XRD) spectra, scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS) were used to examine the morphology and microstructure of the thin films. Optical properties of the thin films were determined by photoluminescence (PL) and UV/Vis spectroscopy. The analyzed results indicates that the obtained films are of good crystal quality and have smooth surfaces, which have a pure hexagonal wurtzite ZnO structure without any Mn related phases. Room temperature photoluminescence is observed for the ZnO and Mn-doped ZnO thin films.     

Investigation of reduced graphene oxide effects on ultra-violet detection of ZnO thin film

The reduced graphene oxide (rGO) incorporated ZnO thin films were fabricated by dip-coating method. The Raman and FT-IR spectra of 0.075 wt% incorporated composite film showed reduction of GO in composite film. The transmittanceProd. Type: FTP spectra have shown that rGO incorporation increase the visible light absorption of ZnO thin film while the calculated band gaps of samples were decreased from 3.28 to 3.25 eV by increasing the rGO content. The linear trend of I–V curve suggests an ohmic contact between ZnO and rGO. Besides, it was found that by increasing the rGO content, the electrical resistivity was decreased from 4.32×10² Ω cm for pure ZnO film to 2.4×10¹ Ω cm for 0.225 wt% rGO incorporated composite film. The composite photodetectors not only possessed a desirable UV photosensitivity, but also the response time of optimum sample containing 0.075 wt% rGO was reduced to about one-half of pure ZnO thin film. Also, the calculated signal to noise (SNR) showed that highly conductive rGO in composite thin films facilitate the carrier transportation by removing the trapping centers. The mechanism of photoresponsivity improvement of composite thin films was proposed by carrier transportation process.     

Carbon nanotube–ZnO nanocomposite electrodes for supercapacitors

Carbon nanotube (CNT)–zinc oxide (ZnO) nanocomposite and gel poly(vinyl alcohol)–phosphomolybdic acid were employed as the electrode and electrolyte of the experimental supercapacitor cell, respectively. The ZnO nanodots were deposited onto CNT films by ultrasonic spray pyrolysis in different times. The results of electrochemical measurements showed that the electrode with ZnO deposited in 5 min had the optimal capacitive properties among the experimental series, with a lowest interfacial electron transfer resistance, a very high capacitance of 323.9 F/g and good reversibility in the repetitive charge/discharge cycling test.     

Photoluminescence of chemical solution-derived amorphous ZnO layers prepared by low-temperature process

Growth characteristic and optical properties of the amorphous ZnO thin films prepared on soda-lime–silica glass substrates by chemical solution process at 100 and 200 °C were investigated by using X-ray diffraction analysis, scanning probe microscope, ultraviolet spectrophotometer, and photoluminescence. The films exhibited an amorphous pattern even when finally heat treated at 100–200 °C for 60 min. The photoluminescence spectrum of amorphous ZnO films shows a strong near-band-edge emission, while the visible emission is nearly quenched.     

High c-axis preferred orientation ZnO thin films prepared by oxidation of metallic zinc

Thin films of zinc oxide were grown on glass substrates by thermal oxidation. The metallic zinc films were thermally oxidized at different temperatures ranging from 300 to 600 °C to yield ZnO thin films. The structural property of the thin films was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The X-ray diffraction measurements showed that the films oxidized at 300 °C were not oxidized entirely, and the films deposited at 600 °C had better crystalline quality than the rest. When the oxidation temperature increased above 400 °C, the films exhibited preferred orientation along (002) and high transmittance ranging from 85% to 98% in vis–near-infrared band. Meanwhile, the films showed a UV emission at about 377 nm and green emission. With the increasing of oxidation temperature, the intensity of green emission peak was enhanced, and then decreased, disappearing at 600 °C, and the case of UV emission increased. Furthermore, a strong green emission was observed in the film sintered in pure oxygen atmosphere.     

Comparative study on structural and optical properties of ZnO thin films prepared by PLD using ZnO powder target and ceramic target

Zinc oxide thin films have been obtained in O₂ ambient at a pressure of 1.3 Pa by pulsed laser deposition (PLD) using ZnO powder target and ceramic target. The effect of temperature on structural and optical properties of ZnO thin films was investigated systematically by XRD, SEM, FTIR and PL spectra. The results show that the best structural and optical properties can be achieved for ZnO thin film fabricated at 700 °C using powder target and at 400 °C using ceramic target, respectively. The PL spectrum reveals that the efficiency of UV emission of ZnO thin film fabricated by using powder target is low, and the defect emission of ZnO thin film derived from Zn_i and O_i is high.     

Epitaxial ZnO thin films grown by pulsed electron beam deposition

In this work, the pulsed electron beam deposition method (PED) is evaluated by studying the properties of ZnO thin films grown on c-cut sapphire substrates. The film composition, structure and surface morphology were investigated by means of Rutherford backscattering spectrometry, X-ray diffraction and atomic force microscopy. Optical absorption, resistivity and Hall effect measurements were performed in order to obtain the optical and electronic properties of the ZnO films. By a fine tuning of the deposition conditions, smooth, dense, stoichiometric and textured hexagonal ZnO films were epitaxially grown on (0001) sapphire at 700 °C with a 30° rotation of the ZnO basal plane with respect to the sapphire substrate. The average transmittance of the films reaches 90% in the visible range with an optical band gap of 3.28 eV. Electrical characterization reveals a high density of charge carrier of 3.4 × 10¹⁹ cm^?3 along with a mobility of 11.53 cm²/Vs. The electrical and optical properties are discussed and compared to ZnO thin films prepared by the similar and most well-known pulsed laser deposition method.     

Nonlinear optical properties of erbium doped zinc oxide (EZO) thin films

Undoped and Erbium (Er) doped zinc oxide (EZO) thin films were deposited on glass substrate by sol–gel method using spin coating technique with different doping concentration. EZO films were characterized using X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), UV–VIS-NIR transmission and single beam z scan method under illumination of frequency doubled Nd:YAG laser. The deposited films were found to be well crystallized with hexagonal wurtzite structure having a preferential growth orientation along the ZnO (002) plane. A blue-shift was observed in the band gap of EZO films with increasing Er concentration. All the films exhibited a negative value of nonlinear refractive index (n₂) at 532 nm which is attributed to the two photon absorption and weak free carrier absorption. Third order nonlinear optical susceptibility, χ⁽³⁾ values of EZO films were observed in the remarkable range of 10^? 6 esu. EZO (0.4 at.%) sample was found to be the best optical limiter with limiting threshold of 1.95 KJ/cm².     

Effect of annealing temperature on the characteristics of ZnO thin films

Effect of annealing temperature on characteristics of sol–gel driven ZnO thin film spin-coated on Si substrate was studied. The UV–visible transmittance of the sol decreased with the increase of the aging time and drastically reduced after 20 days aging time. Granular shape of ZnO crystallites was observed on the surface of the films annealed at 550, 650, and 750 °C, and the crystallite size increased with the increase of the annealing temperature. Consequently nodular shape of crystallites was formed upon increasing the annealing temperature to 850 °C and above. The current–voltage characteristics of the Schottky diodes fabricated with ZnO thin films with various annealing temperatures were measured and analyzed. It is found that, ZnO films showed the Schottky characteristics up to 750 °C annealing temperature. The Schottky diode characteristics were diminished upon increasing the annealing temperature above 850 °C. XPS analysis suggested that the absence of oxygen atoms in its oxidized state in stoichiometric surrounding, might be responsible for the diminished forward current of the Schottky diode when annealed above 850 °C.     

Study of thermal stability of ZnO:B films grown by LPCVD technique

Zinc oxide thin films with different boron doping levels (ZnO:B) are prepared by low pressure chemical vapor deposition (LPCVD) technique. All films here exhibit a pyramid-like surface texture. Stability of the ZnO:B films is systematically investigated through a post heat treatment at ambient temperatures of 300 °C and 250 °C for different durations. It is found that total transmission (TT) of these films at near infrared (NIR) wavelength range increases with the enhanced thermal treating intensity, which could be attributed to decrease of free carrier concentration inside the films. Moreover, light absorption in NIR wavelength range decreases profoundly with the increasing carrier concentration after a post thermal treatment in particular for highly doped ZnO:B films. However, morphology of these ZnO:B films does not vary after the thermal treatment and thus the corresponding light scattering properties do not change as well. Therefore, the thermally treated ZnO:B films may lead to an increase in light-generated current and resulting a higher cell efficiency due to the enhancement of TT when they work as front contact in silicon thin film solar cells.     

Optical properties and structural characteristics of ZnO thin films grown on a-plane sapphire substrates by plasma-assisted molecular beam epitaxy

We investigated structural and optical properties of ZnO thin films grown on (112?0) a-plane sapphire substrates using plasma-assisted molecular beam epitaxy. Negligible biaxial stress in ZnO thin films is due to the use of (112?0) a-plane sapphire substrates and slow substrate cooling. The 14 K photoluminescence spectrum shows a blueshift of energy positions compared with ZnO single crystal. A donor with binding energy of 43 meV and an acceptor with binding energy of ～170 meV are identified by well-resolved photoluminescence spectra. A characteristic emission band at 3.320 eV (so-called A-line) is studied. Based on analysis from photoluminescence spectra, the origin of the A-line, it seems, is more likely an (e, A°) transition, in which defect behaves as an acceptor. The room-temperature photoluminescence is dominated by the FX at 3.307 eV, which is an indication of strongly reduced defect density in ZnO thin films.     

The growth of ZnO:Ga:Cu as new TCO film of advanced electrical,optical and structural quality

Because of having similarities in many physical as well as chemical properties to those of Zn, Cu has been strategically used as an effective dopant e.g., Al, Ga, F, etc., to change the optical, electrical and the micro-structural properties of ZnO thin films for obtaining its favorable opto-electronic performance as a transparent conducting oxide suitable for devices. Present study demonstrates the growth of transparent conducting ZnO:Ga:Cu thin films, by low power RF magnetron sputtering at a low substrate temperature (100 °C). Highly crystalline ZnO:Ga:Cu film with preferred c-axis orientation has been obtained demonstrating a high magnitude of transmission ~85% in the visible range and a high electrical conductivity ~40 S cm^–1, facilitated by large crystallite size (~29 nm), introducing reduced grain boundary scattering. XPS O 1S spectrum reveals the presence of a significant fraction of oxygen atoms effectively increasing the optical transparency. Incorporation of Ga and Cu ions into the ZnO matrix promotes violation of the local translational symmetry as suggested by the relaxation of Raman selection rules for the network, evident by the presence of strong (B₁^high–B₁^low) modes which are typically Raman inactive. The consequences of Cu doping has been compared with identically prepared ZnO and ZnO:Ga films.     

Synthesis of superhydrophobic PTFE-like thin films by self-nanostructuration in a hybrid plasma process

Superhydrophobic poly(tetrafluoro-ethylene) (PTFE) like thin films were grown on silicon wafers using a plasma-based hybrid process consisting on sputtering a carbon target in an Ar/CF₄ atmosphere. The influence of the bias voltage applied to the substrate (V_Bias) as well as of the gas mixture composition (%CF₄) on the chemical composition, the wettability and the morphology of the deposited thin films were evaluated.The chemical composition measured by X-ray Photoelectron Spectroscopy (XPS) has revealed that the F/C atomic ratio is always lower than for conventional PTFE (F/C = 2) and that it decreases when V_Bias increases (from F/C = 1 for V_Bias = ? 100 V to F/C = 0.75 for V_Bias = ? 200 V). This behavior is associated with the preferential sputtering of the fluorine atoms during the plasma-assisted growth of the films. Consecutively, a self-nanostructuration enhanced when increasing V_Bias is observed. As a consequence, the water contact angle (WCA) measurements range from 70° up to 150° depending on (i) the fluorine concentration and (ii) on the magnitude of the nanostructuration. In addition, for the films presenting the highest WCAs, a small hysteresis between the advancing and receding WCAs is observed (< 10°) allowing these films to fulfill completely the requirements of superhydrophobicity. The nanostructuration is probably due to the chemical etching by fluorine atoms of the fluorinated group.In order to get more understanding on the wettability mechanisms of these surfaces, the topography of the films has been evaluated by atomic force microscopy (AFM). The data have revealed, for all films, a dense and regular structure composed by conic objects (A_vH is their average height and A_vD is the average distance between them) for which the dimensions increase with V_Bias. A correlation between A_vH/A_vD, defined as the “morphological ratio”, with the WCA was established. Theoretical evaluations of the WCA using the Wenzel and Cassie equations with, as inputs, the features of the deposited thin film surfaces measured by AFM suggest that the wetting regime is intermediate between these two ideal situations.     

Optical properties of PMN–PT thin films prepared using pulsed laser deposition

(1 ? x)Pb(Mg_1/3Nb_2/3)O₃–xPbTiO₃ (PMN–PT) thin films have been deposited on quartz substrates using pulsed laser deposition (PLD). Crystalline microstructure of the deposited PMN–PT thin films has been investigated with X-ray diffraction (XRD). Optical transmission spectroscopy and Raman spectroscopy are used to characterize optical properties of the deposited PMN–PT thin films. The results show that the PMN–PT thin films of perovskite structure have been formed, and the crystalline and optical properties of the PMN–PT thin films can be improved as increasing the annealing temperature to 750 °C, but further increasing the annealing temperature to 950 °C may lead to a degradation of the crystallinity and the optical properties of the PMN–PT thin films. In addition, a weak second harmonic intensity (SHG) has been observed for the PMN–PT thin film formed at the optimum annealing temperature of 750 °C according to Maker fringe method. All these suggest that the annealing temperature has significant effect on the structural and optical properties of the PMN–PT thin films.     

Properties of nano-ZnO/poly(vinyl alcohol)/poly(ethylene oxide) composite thin films

A series of poly(vinyl alcohol)/nano-ZnO composites were prepared by dispersing nano-ZnO in aqueous solutions containing mixtures of the biodegradable polymers poly(vinyl alcohol) (PVA) and poly(ethylene oxide) (PEO), and composite thin films were prepared by casting. The introduction of nano-ZnO into PVA/PEO mixed solutions significantly decreased the resistivity of the solutions. Ultraviolet absorption, thermal behaviour and visco-elastic properties of the thin films were determined as a function of nano-ZnO content up to 15 wt%. Optimum film properties were obtained with 1 wt% nano-ZnO, higher proportions of nano-ZnO resulting in agglomeration of ZnO particles and deterioration in film properties. The Forouhi and Bloomer model was used for the modelling of ZnO thin films.     

Chemical solution processing and properties of Sr2FeMoO6 thin films

Crack-free and oriented Sr₂FeMoO₆ (SFMO) thin film with double perovskite structure has been fabricated by the chemical solution deposition (CSD) method. A homogeneous and stable SFMO precursor solution was successfully prepared by controlling the reaction of starting metal-organic compounds in a mixture solvent of 1-propanol and 2-methoxyethanol. SFMO thin films with c-axis preferred orientation could successfully be synthesized on MgO (0 0 1) and SrTiO₃ (0 0 1) substrates by optimizing the several processing conditions. SFMO thin film prepared on SrTiO₃ (0 0 1) showed a magnetoresistance effect at a low magnetic field.     

Temperature coefficient of resistance and thermal conductivity of Vanadium oxide ‘Big Mac’ sandwich structure

In this paper, we synthesize and characterize a thin film thermometer structure for infrared microbolometers. The structure is composed of alternating multilayers of Vanadium pentoxide (V₂O₅), 25 nm, and Vanadium (V), 5 nm, thin films deposited by rf magnetron and dc magnetron sputtering respectively and annealed for 20, 30 and 40 min at 300 °C in Nitrogen (N₂) atmosphere. The best achieved temperature coefficient of resistance (TCR) was found to be −2.57%/K for 40 min annealed samples. Moreover, we apply, for the first time, the photo-thermal deflection (PTD) technique for measuring the thermal conductivity of the synthesized thin films. The thermal conductivity of the developed thin films reveals an increase in thermal conductivity from 2 W/m K to 5.8 W/m K for as grown and 40 min annealed samples respectively.     

A competition between (0 0 1) and (0 1 1) alignments in yttria stabilized zirconia thin films fabricated by ion beam assisted deposition

Biaxially textured yttria stabilized zirconia (YSZ) thin films, were deposited on glass substrates by ion beam assisted deposition method with different deposition time. As contrasts, films were also fabricated without assisting ion beam. The orientation properties of the films were characterized by X-ray diffraction. A comparative study shows that there is a competition between (0 0 1) and (0 1 1) alignments during the growth process. Assisting ions make the films (0 0 1)-advantaged and biaxially textured. The competitive growth and the orientation development are explained by selective resputtering and anisotropic damage on growing films induced by assisting ions.