Luminescence and thermally stimulated recombination processes in Li<Subscript>6</Subscript>Gd(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>:Ce<Superscript>3+</Superscript> crystals

The luminescence and thermally stimulated recombination processes in lithium borate crystals Li₆Gd(BO₃)₃ and Li₆Gd(BO₃)₃:Ce have been studied. The steady-state luminescence spectra under X-ray excitation (X-ray luminescence), temperature dependences of the intensity of steady-state X-ray luminescence (XL), and thermally stimulated luminescence (TSL) spectra of these compounds have been investigated in the temperature range of 90–500 K. The intrinsic-luminescence 312-nm band, which is due to the ⁶ P _J → ⁸ S _7/2 transitions in Gd³⁺ matrix ions, dominates in the X-ray luminescence spectra of these crystals; in addition, there is a wide complex band at 400–420 nm, which is due to the d → f transitions in Ce³⁺ impurity ions. It is found that the steady-state XL intensity in these bands increases several times upon heating from 100 to 400 K. The possible mechanisms of the observed temperature dependence of the steady-state XL intensity and their correlation with the features of electronic-excitation energy transfer in these crystals are discussed. The main complex TSL peak at 110–160 K and a number of minor peaks, whose composition and structure depend on the crystal type, have been found in all crystals studied. The nature of the shallow traps that are responsible for TSL at temperatures below room temperature and their relation with defects in the lithium cation sublattice are discussed.     

Broadband infrared luminescence from transparent glass–ceramics containing Ni<Superscript>2+</Superscript>-doped <Emphasis Type="BoldItalic">β</Emphasis> -Ga<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocrystals

Transparent Ni²⁺-doped β-Ga₂O₃ glass–ceramics were synthesized. The nanocrystal phase in the glass–ceramics was identified to be β-Ga₂O₃ and its size was about 3.6 nm. It was confirmed from the absorption spectra that the ligand environment of Ni²⁺ ions changed from the trigonal bi-pyramid fivefold sites in the as-cast glass to the octahedral sites in the glass–ceramics. The broadband infrared emission centering at 1270 nm with full width at half maximum (FWHM) of more than 250 nm was observed. The fluorescence lifetime was about 1.1 μs at room temperature. The observed infrared emission could be attributed to the ³ T _2g (³ F )→³ A _2g (³ F ) transition of octahedral Ni²⁺ ions. It is suggested that the Ni²⁺-doped transparent β-Ga₂O₃ glass–ceramics with broad bandwidth and long lifetime have a potential as a broadband amplification medium. PACS 42.70.-a; 42.70.Ce; 81.40.Tv     

Thermal and optical properties of Tm<Superscript>3+</Superscript>:NaLa(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

A Tm³⁺-doped NaLa(WO₄)₂ single crystal with a dimension of Φ20 mm×40 mm was grown by the Czochralski method. Anisotropic thermal expansion coefficients of this crystal were investigated. Polarized absorption spectra, emission spectra and decay curve were recorded at room temperature. The absorption and emission cross-section were presented. Based on the Judd–Ofelt analysis, we obtained the three intensity parameters: Ω₂=10.21×10^-20, Ω₄=2.66×10^-20, and Ω₆=1.46×10^-20 cm². The radiative probabilities, radiative lifetimes, and branch ratios of Tm³⁺:NaLa(WO₄)₂ were calculated, too. Luminescence lifetime of the ³ H ₄ level was measured to be 220 μs. The stimulated emission cross-section for the ³ F ₄→³ H ₆ transition were determined using the reciprocity method, potential laser gain for this transition were also investigated, the gain curves implied that the tunable range is up to 200 nm. PACS 42.70.Hj; 78.20.-e     

Magnetic properties of LiNi<Subscript>0.5</Subscript>Mn<Subscript>0.47</Subscript>Al<Subscript>0.03</Subscript>O<Subscript>2</Subscript> as positive electrode for Li-ion batteries

The layered LiNi_0.5Mn_0.47Al_0.03O₂ was synthesized by wet chemical method and characterized by X-ray diffraction and analysis of magnetic measurements. The powders adopted the α-NaFeO₂ structure. This substitution of Al for Mn promotes the formation of Li(Ni_0.47²⁺Ni_0.03³⁺Mn_0.47⁴⁺Al_0.03³⁺)O₂ structures and induces an increase in the average oxidation state of Ni, thereby leading to the shrinkage of the lattice unit cell. The concentration of antisite defects in which Ni²⁺ occupies the (3a) Li lattice sites in the Wyckoff notation has been estimated from the ferromagnetic Ni²⁺(3a)–Mn⁴⁺(3b) pairing observed below 140 K. The substitution of 3% Al for Mn reduces the amount of antisite defects from 7% to 6.4–6.5%. The analysis of the magnetic properties in the paramagnetic phase in the framework of the Curie–Weiss law agrees well with the combination of Ni²⁺ (S = 1), Ni³⁺ (S = 1/2) and Mn⁴⁺ (S = 3/2) spin-only values. Delithiation has been made by the use of K₂S₂O₈. According to this process, known to be softer than the electrochemical one, the nickel ions in the (3b) sites are converted into Ni⁴⁺ in the high spin configuration, while Ni²⁺(3a)–Mn⁴⁺(3b) ferromagnetic pairs remain, as the Li⁺(3b) ions linked to the Ni²⁺(3a) ions in the antisite defects are not removed. The results show that the antisite defect is surrounded by Mn⁴⁺ ions, implying the nonuniform distribution of the cations in agreement with previous NMR and neutron experiments.     

Fragmentation of sputtered Si<Subscript><Emphasis Type="Italic">n</Emphasis></Subscript>O<Stack><Subscript><Emphasis Type="Italic">m</Emphasis></Subscript><Superscript>+</Superscript></Stack> clusters: Release kinetic and dissociation energies

The spectra of kinetic energies of positive Si _n O _m ⁺ cluster ions (n = 2–5, m = 2–7) have been measured using a double focusing ion microanalyzer with reverse geometry at instants 10⁻⁵ to 10⁻⁴ s after emission. The dissociation energies have been determined within the evaporative ensemble model and the theory of unimolecular decay reactions. The results obtained are compared with the binding energies of neutral Si _n O _m clusters.     

Sensitizer-dependent up-conversion of Ho<Superscript>3+</Superscript> in nanocrystalline Y<Subscript>2</Subscript>O<Subscript>3</Subscript>

Ho³⁺–Yb³⁺ co-doped Y₂O₃ nanocrystals were synthesized by firing hydroxy carbonate precursors. Yb³⁺-concentration-dependent up-conversion properties of Ho³⁺ in Y₂O₃ nanocrystals have been investigated. The relative intensity of up-converted red emission increases more quickly than that of the green and the near-infrared ones with the enhancement of the concentration of Yb³⁺. It is believed that the energy process ⁵ S ₂ (⁵F₄) (Ho) + ⁵ I ₇ (Ho) →⁵ I ₆ (Ho)+⁵ F ₅ (Ho) plays an important role in the population of the ⁵ F ₅ level of Ho³⁺. The result indicates that the intensity ratio of the green emission to the red one can be tuned by changing the sensitizer concentration. PACS 78.55.-m     

Superhyperfine Structure of EPR Spectra in LiLuF<Subscript>4</Subscript>:U<Superscript>3+</Superscript> and LiYF<Subscript>4</Subscript>:Yb<Superscript>3+</Superscript> Single Crystals

Electron paramagnetic resonance (EPR) spectra of doped paramagnetic crystals LiLuF₄:U³⁺ and LiYF₄:Yb³⁺ have been investigated at a frequency of about 9.42 GHz in the temperature range of 10–20 K. The U³⁺ ion spectrum is characterized by g-factors g _∥ = 1.228 and g _⊥ = 2.516, and contains the hyperfine structure due to the ²³⁵U isotope with nuclear spin I = 7/2 and natural abundance of 0.71%. The observed hyperfine interaction constants are A _∥ = 81 G and A _⊥ = 83.8 G. Moreover, the spectrum reveals the well-resolved superhyperfine structure (SHFS) due to two groups of four fluorine ions forming the nearest surrounding of the U³⁺ ion. This SHFS contains up to nine components with the spacing between components being about 12.7 G. The SHFS is observed also in the EPR spectrum of the LiYF₄:Yb³⁺ crystal; up to 17 components with spacing of about 3.7 G may be traced. Some parameters of the effective Hamiltonian of the SHF interaction are estimated, the contribution of covalent bonding of f-electrons with ligands into these parameters is discussed. Authors' address: Igor N. Kurkin, Kazan State University, Kremlevskaya ulitsa 18, Kazan 420008, Russian Federation     

Spectroscopic properties of Nd<Superscript>3+</Superscript>:CaNb<Subscript>2</Subscript>O<Subscript>6</Subscript> crystal

The absorption spectra, fluorescence spectrum and fluorescence decay curve of Nd³⁺ ions in CaNb₂O₆ crystal were measured at room temperature. The peak absorption cross section was calculated to be 6.202×10⁻²⁰ cm² with a broad FWHM of 7 nm at 808 nm for E//a light polarization. The spectroscopic parameters of Nd³⁺ ions in CaNb₂O₆ crystal have been investigated based on Judd-Ofelt theory. The parameters of the line strengths Ω _t are Ω ₂=5.321×10⁻²⁰ cm²,Ω ₄=1.734×10⁻²⁰ cm²,Ω ₆=2.889×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 167 μs, 152 μs and 91%, respectively. The fluorescence branch ratios are calculated to be β ₁=36.03%,β ₂=52.29%,β ₃=11.15%,β ₄=0.533%. The emission cross section at 1062 nm is 9.87×10⁻²⁰ cm².     

Electrical characterization of the [N(CH<Subscript>3</Subscript>)<Subscript>4</Subscript>][N(C<Subscript>2</Subscript>H<Subscript>5</Subscript>)<Subscript>4</Subscript>]ZnCl<Subscript>4</Subscript> compound

The [N(CH₃)₄][N(C₂H₅)₄]ZnCl₄ compound has been synthesized by a solution-based chemical method. The X-ray diffraction study at room temperature revealed an orthorhombic system with P2₁2₁2 space group. The complex impedance has been investigated in the temperature and frequency ranges 420–520 K and 200 Hz–5 MHz, respectively. The grain interior and grain boundary contribution to the electrical response in the material have been identified. Dielectric data were analyzed using the complex electrical modulus M ^* for the sample at various temperature. The modulus plots can be characterized by full width at half height or in terms of a non-exponential decay function ϕ(t) = exp[(−t/τ) ^β ]. The detailed conductivity study indicated that the electrical conduction in the material is a thermally activated process. The variation of the AC conductivity with frequency at different temperatures obeys the Almond and West universal law.     

Luminescence of CaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript>:Eu crystals

We have studied photoluminescence and thermoluminescence (PL and TL) in CaGa₂Se₄:Eu crystals in the temperature range 77–400 K. We have established that broadband photoluminescence with maximum at 571 nm is due to intracenter transitions 4f⁶ 5d–4f⁷ (⁸S_7/2) of the Eu²⁺ ions. From the temperature dependence of the intensity (log I–10³/T), we determined the activation energy (E _a = 0.04 eV) for thermal quenching of photoluminescence. From the thermoluminescence spectra, we determined the trap depths: 0.31, 0.44, 0.53, 0.59 eV. The lifetime of the excited state 4f6 5d of the Eu²⁺ ions in the CaGa₂Se₄ crystal found from the luminescence decay kinetics is 3.8 μsec. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 76, No. 1, pp. 112–116, January–February, 2009.     

Polarized spectral properties of Er<Superscript>3+</Superscript> ions in NaGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

Polarized spectral properties of Er³⁺:NaGd(WO₄)₂ single crystal are reported. The crystal was grown by the Czochralski method. The Judd–Ofelt theory was applied to analyze the polarized absorption spectra and then calculate the spontaneous emission probabilities, radiative lifetimes, and branching ratios. Fluorescence decay curves of the ⁴ I _13/2, ⁴ I _11/2, and ⁴ S _3/2 multiplets for the Er³⁺ ions were measured. Stimulated emission cross-sections of the ⁴ I _13/2→⁴ I _15/2 transition obtained by the Fuchtbauer–Ladenberg formula and the reciprocity method were compared. Multi-phonon relaxation rates of the crystal were estimated. Green up-conversion fluorescence around 531 and 552 nm was observed, and the possible up-conversion mechanisms were proposed. PACS 78.20.-e; 42.70.Hj     

The effect of temperature and pressure on the heat conductivity of TlSbC<Stack><Subscript>2</Subscript><Superscript>VI</Superscript></Stack> (<Emphasis Type="Italic">C</Emphasis><Superscript>VI</Superscript> → S,Se, Te)

The effect of temperature and pressure on heat conductivity of ternary compounds TiSbC ₂^VI (C ^VI → S, Se, Te) in the solid and liquid states in a temperature range of 300–800 K, as well as under the pressure up to 0.35 GPa in a temperature range of 275–450 K, is studied. The dependence of heat conductivity on average atomic weight under the S → Se → Te transition is found. Analysis of the experimental data makes it possible to attribute TlSbS₂ to the class of substances exhibiting semiconductor-semiconductor melting behavior.     

Leading-order 2πγ exchange NN interaction: Central potentials proportional to g<Subscript>A</Subscript><Superscript>0</Superscript> and g<Subscript>A</Subscript><Superscript>2</Superscript>

We calculate at two-loop order in chiral perturbation theory the electromagnetic corrections to the leading-order 2π exchange NN interaction proportional to g _A ⁰ and g _A ². The resulting 2πγ exchange potential contains isospin-breaking components which reach up to about -2% of the corresponding isovector 2π exchange potential. With a value of only -17keV at r = m _π ^-1 = 1.4fm the charge-independence breaking central potential obtained here is negligibly small in comparison to the one generated by the isoscalar c₃ contact vertex. Our calculation confirms that the largest long-range isospin-violating NN potentials arise from the 2πγ exchange diagrams involving the large low-energy constants c ₄ ≃ - c ₃ ≃ 3.3GeV^-1 representing the important Δ(1232) dynamics.     

Luminescence and electronic excitations in Li<Subscript>6</Subscript>Gd(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>: Ce<Superscript>3+</Superscript> crystals

This paper reports on a study of the luminescence emitted by Li₆Gd(BO₃)₃: Ce³⁺ crystals under selective photoexcitation to lower excited states of the host ion Gd³⁺ and impurity ion Ce³⁺ within the 100–500-K temperature interval, where the mechanisms of migration and relaxation of electronic excitation energy have been shown to undergo noticeable changes. The monotonic 10–15-fold increase in intensity of the luminescence band at 3.97 eV has been explained within a model describing two competing processes, namely, migration of electronic excitation energy over chains of Gd³⁺ ions and vibrational energy relaxation between the ⁶ I _j and ⁶ P _j levels. It has been shown that radiative transitions in Ce³⁺ ions from the lower excited state 5d ¹ to ² F _5/2 and ² F _7/2 levels of the ground state produce two photoluminescence bands, at 2.08 and 2.38 eV (Ce1 center) and 2.88 and 3.13 eV (Ce2 center). Possible models of the Ce1 and Ce2 luminescence centers have been discussed.     

Synthesis and luminescent properties of Eu<Superscript>3+</Superscript>- and Eu<Superscript>2+</Superscript>-activated sodium pyrophosphate Na<Subscript>4</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

The luminescent properties of Eu³⁺ and Eu²⁺ ions in sodium pyrophosphate, Na₄P₂O₇, have been studied. The excitation spectrum of the Eu³⁺ emission in Na₄P₂O₇ consists of several sets of bands in the range 280–535 nm due to 4f–4f transitions of Eu³⁺ ions and a broad band with a maximum at about 240 nm interpreted to be due to a charge transfer (CT) transition from oxygen 2p states to empty states of the Eu³⁺ 4f⁶-configuration. Although the CT band energy is large enough, the quantum efficiency (η) of the Eu³⁺ emission in Na₄P₂O₇ under CT excitation was estimated to be very low (η ≤ 0.01). In terms of a configurational coordinate model, this fact is interpreted as a result of the high efficiency of a radiationless relaxation from the CT state to the ⁷F₀ ground state of Eu³⁺ ions occupying sodium sites in Na₄P₂O₇. A strong reducing agent is required in order to stabilize Eu²⁺ ions in Na₄P₂O₇ during the synthesis. Several nonequivalent Eu²⁺ luminescence centers in Na₄P₂O₇ were found.     

Optical spectra and excited state relaxation dynamics of Sm<Superscript>3+</Superscript> in Gd<Subscript>2</Subscript>SiO<Subscript>5</Subscript> single crystal

Single crystals of gadolinium orthosilicate Gd₂SiO₅ containing 0.5 at% and 5 at% of Sm³⁺ were grown by the Czochralski method. Optical absorption spectra, luminescence spectra and luminescence decay curves were recorded for these systems at 10 K and at room temperature. Comparison of optical spectra recorded in polarized light revealed that the anisotropy of this optically biaxial host affects the intensity distribution within absorption and emission bands related to transitions between multiplets rather than the overall band intensity. It has been found that among four bands of luminescence related to the ⁴G_5/2→⁶H_J (J=5/2–11/2) transitions of Sm³⁺ in the visible and near infrared region the ⁴G_5/2 →⁶H_7/2 one has the highest intensity with a peak emission cross section of 3.54×10⁻²¹ cm² at 601 nm for light polarized parallel to the crystallographic axis c of the crystal. The luminescence decay curve recorded for Gd₂SiO₅:0.5 at% Sm³⁺ follows a single exponential time dependence with a lifetime 1.74 ms, in good agreement with the ⁴G_5/2 radiative lifetime τ _rad=1.78 ms calculated in the framework of Judd-Ofelt theory. Considerably faster and non-exponential luminescence decay recorded for Gd₂SiO₅:5 at% Sm³⁺ sample was fitted to that predicted by the Inokuti-Hirayama theory yielding the microparameter of Sm³⁺–Sm³⁺ energy transfer C _da=1.264×10⁻⁵² cm⁶×s⁻¹.     

Defect Structure and Up-conversion Luminescence Properties of ZrO<Subscript>2</Subscript>:Yb<Superscript>3+</Superscript>,Er<Superscript>3+</Superscript> Nanomaterials

The up-converting ZrO₂:Yb³⁺,Er³⁺ nanomaterials were prepared with the combustion and sol–gel methods. FT-IR spectroscopy was used for analyzing the impurities. The crystal structures were characterized with X-ray powder diffraction and the mean crystallite sizes were estimated with the Scherrer formula. Up-conversion luminescence measurements were made at room temperature with IR-laser excitation at 977 nm. The IR spectra revealed the conventional and OH⁻ impurities for the combustion synthesis products. The structure of the ZrO₂:Yb³⁺, Er³⁺ nanomaterials was cubic except for the minor monoclinic and tetragonal impurities obtained with the sol–gel method. The materials showed red (650–700 nm) and green (520–560 nm) up-conversion luminescence due to the ⁴F_9/2→⁴I_15/2 and (²H_11/2, ⁴S_3/2)→⁴I_15/2 transitions of Er³⁺, respectively. The products obtained with the combustion synthesis exhibited the most intense luminescence intensity and showed considerable afterglow.     

Photoluminescence of nanoparticles of (Ga<Subscript>2</Subscript>S<Subscript>3</Subscript>)<Subscript>0.95</Subscript>(Eu<Subscript>2</Subscript>O<Subscript>3</Subscript>)<Subscript>0.05</Subscript> solid solution

We have ground bulk samples to obtain nanoparticles of (Ga₂S₃)_1–x (Eu₂O₃) _x solid solutions, the sizes of which were determined using an atomic force microscope. The photoluminescence spectra of the nanoparticles were studied in the temperature interval 77–300 K. We have established the mechanisms for emission and transfer of energy from the matrix to the rare-earth ion, and we determined the Stokes shift (ΔS = 0.7 eV), the Huang–Rhys parameter (S = 16), and the optical phonon energy (ħ−ω = 23 meV).     

Influence of magnetic ordering on electronic structure of Tb<Superscript>3+</Superscript> ion in TbFe<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript> crystal

Optical absorption spectra of trigonal crystal TbFe₃(BO₃)₄ have been studied in the region of ⁷F₆ → ⁵D₄ transition in Tb³⁺ ion depending on temperature (2–220 K) and on magnetic field (0–60 kOe). Splitting of the Tb³⁺ excited states, both under the influence of the external magnetic field and effective exchange field of the Fe-sublattice, have been determined. Landé factors of the excited states have been found. Stepwise splitting of one of the absorption lines has been discovered in the region of the Fe-sublattice magnetic ordering temperature. This is shown to be due to the abrupt change of equilibrium geometry of the local Tb³⁺ ion environment only in the excited state of the Tb³⁺ ion. In general, the magnetic ordering is accompanied by temperature variations of the Tb³⁺ local environment in the excited states. The crystal field splitting components have been identified. In particular, it has been shown that the ground state (in D ₃ symmetry approximation) consists of two close singlet states of A ₁ and A ₂ type, which are split and magnetized by effective exchange field of the Fe-sublattice. Orientations of magnetic moments of the excited electronic states relative to that of the ground state have been experimentally determined in the magnetically ordered state of the crystal. A pronounced shift of one of absorption lines has been observed in the vicinity of the TbFe₃(BO₃)₄ structural phase transition. The temperature interval of coexistence of the phases is about 3 K.