Low-temperature growth of ZnO nanorods by chemical bath deposition

Aligned ZnO nanorod arrays were synthesized using a chemical bath deposition method at normal atmospheric pressure without any metal catalyst. A simple two-step process was developed for growing ZnO nanorods on a PET substrate at 90-95 degrees C. The ZnO seed precursor was prepared by a sol-gel reaction. ZnO nanorod arrays were fabricated on ZnO-seed-coated substrate. The ZnO seeds were indispensable for the aligned growth of ZnO nanorods. The ZnO nanorods had a length of 400-500 nm and a diameter of 25-50 nm. HR-TEM and XRD analysis confirmed that the ZnO nanorod is a single crystal with a wurtzite structure and its growth direction is [0001] (the c-axis). Photoluminescence measurements of ZnO nanorods revealed an intense ultraviolet peak at 378.3 nm (3.27 eV) at room temperature.     

均匀沉淀法制备氧化锌纳米棒

采用均匀沉淀法制备了氧化锌纳米棒,用XRD,TEM,PL等检测手段对样品进行了表征.结果表明:所得样品为长约100 nm,宽约30 nm的纤锌矿结构氧化锌纳米棒,颗粒分布均匀.其在可见光区比紫外区的荧光发射显著增强.     

微波固相合成氧化锌纳米棒

通过前驱体的微波固相热分解法快速合成了氧化锌纳米棒, 其直径在60～385 nm之间, 长可达数微米. 前驱体则通过一步室温固相反应制备. 用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、能量色散X射线分析(EDX)和透射电子显微镜(TEM)对产物的结构和形貌进行了表征. 同时, 对氧化锌纳米棒的光致发光(PL)性能作了测试, 结果表明在355 nm处有一个明显的近带隙发射峰. 另外, 对比实验表明, 微波辐射在氧化锌纳米棒的形成过程中起了关键性作用, 并对其形成机理进行了初步探讨.     

Soft template synthesis of ZnO nanorods and their optical properties

A simple solution route was developed to fabricate monodisperse wurtzite ZnO nanorods. The as-prepared samples were 5 ??m in length and 70?C100 nm in diameter. The crystallinity, morphology, and structure of the rod-like ZnO microcrystals were examined. The crystal phases and the microstructure of the nanorods were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Room- and low-temperature photoluminescence (PL) and Raman spectra were employed to investigate the surface states of the samples. The deep-level emission band was barely observable at both room and cryogenic temperatures.     

常温直接沉淀法制备ZnO纳米棒

在常温下, 以PEG-400(聚乙二醇400)为表面活性剂, 采用直接沉淀法合成了ZnO纳米棒. 产物用XRD, TEM, SAED和 HRTEM等进行了表征. 结果表明, 所得ZnO为一维的纳米棒, 属于六方纤维矿的单晶结构. ZnO纳米棒的直径在20~40 nm之间, 长度在300~800 nm范围. (0001)面为ZnO纳米棒的生长方向. 讨论了ZnO相的生成和ZnO纳米棒的形成机理以及PEG-400在其形成过程中的作用.     

水热法制备高度取向的氧化锌纳米棒阵列

氧化锌的激子结合能(60meV)及光增益系数(300cm^-1)比GaN的(25meV,100cm^-1)还高,这一特点使它成为紫外半导体激光发射材料的研究热点。最近,Yang等成功地观测到规则的ZnO纳米线阵列的激光发射现象,更加激起了人们合成一维高度有序ZnO纳米结构的热情,由于一维ZnO     

化学溶液沉积法制备单分散氧化锌纳米棒阵列

在由溶胶凝胶法制备的纳米ZnO薄膜基底上, 采用化学溶液沉积法制备了单分散、高度取向的ZnO纳米棒阵列膜. 通过控制纳米ZnO薄膜的制备工艺, 可以调节氧化锌纳米棒的直径. 利用FESEM, TEM, HRTEM, SAED和XRD表征了氧化锌纳米棒阵列的形貌和晶体结构. ZnO纳米棒的室温PL谱具有很高的紫外带边发射峰, 在可见光波段无发射峰, 表明该方法制备的ZnO纳米棒晶体结构完整, 晶体中O空位的浓度很低.     

Room temperature solution synthesis of monodispersed single-crystalline ZnO nanorods and derived hierarchical nanostructures

In this work, we report a room temperature wet-chemical approach to synthesize highly regulated, monodispersed ZnO nanorods and derived hierarchical nanostructures. In particular, ZnO has been prepared into single-crystalline conical or prismatic nanorods, and various hierarchical structures such as hexagonally branched, reversed umbrella-type, and cactus-like ZnO nanostructures comprising individual c-oriented nanorods. Depending on the synthetic conditions used, the diameter of nanorods can be controlled with a size down to 10-30 nm, while the aspect ratio can be controlled up to 50-100. Various preparative parameters, such as initial reactant concentrations, solvents, ligands, surfactants, precursor salts, and reaction time, have been systematically examined. Due to slow reactions at room temperature, excellent crystallinity and high morphological yield (100% in most cases) have been achieved via tuning the synthetic parameters. Our photoluminescence and UV measurements also confirm the attained crystal perfection and size uniformity.     

Large-scale synthesis of TiO2 nanorods via nonhydrolytic sol-gel ester elimination reaction and their application to photocatalytic inactivation of E. coli

A simple method of synthesizing a large quantity of TiO(2) nanorods was developed. A nonhydrolytic sol-gel reaction between titanium(IV) isopropoxide and oleic acid at 270 degrees C generated 3.4 nm (diameter) x 38 nm (length) sized TiO(2) nanocrystals. The transmission electron microscopic image showed that the particles have a uniform diameter distribution. X-ray diffraction and selected-area electron diffraction patterns combined with high-resolution transmission electron microscopic image showed that the TiO(2) nanorods are highly crystalline anatase crystal structure grown along the [001] direction. The diameters of the TiO(2) nanorods were controlled by adding 1-hexadecylamine to the reaction mixture as a cosurfactant. TiO(2) nanorods with average sizes of 2.7 nm x 28 nm, 2.2 nm x 32 nm, and 2.0 nm x 39 nm were obtained using 1, 5, and 10 mmol of 1-hexadecylamine, respectively. The optical absorption spectrum of the TiO(2) nanorods exhibited that the band gap of the nanorods was 3.33 eV at room temperature, which is 130 meV larger than that of bulk anatase (3.2 eV), demonstrating the quantum confinement effect. Oleic acid coordinated on the nanorod surface was removed by the reduction of the carboxyl group of oleic acid, and the Brunauer-Emmett-Teller surface area of the resulting naked TiO(2) nanorods was 198 m(2)/g. The naked TiO(2) nanorods exhibited higher photocatalytic activity than the P-25 photocatalyst for the photocatalytic inactivation of E. coli.     

Growth and Characterization of [001] ZnO Nanorod Array on ITO Substrate with Electric Field Assisted Nucleation

This paper reports direct growth of [001] ZnO nanorod arrays on ITO substrate from aqueous solution with electric field assisted nucleation, followed with thermal annealing. X-ray diffraction analyses revealed that nanorods have wurtzite crystal structure. The diameter of ZnO nanorods was 60–300 nm and the length was up to 2.5 μm depending on the growth condition. Photoluminescence spectra showed a broad emission band spreading from 500 to 870 nm, which suggests that ZnO nanorods have a high density of oxygen interstitials. Low and nonlinear electrical conductivity of ZnO nanorod array was observed, which was ascribed to non-ohmic contact between top electrode and ZnO nanorods and the low concentration of oxygen vacancies.     

Synthesis and magnetic properties of hexagonally packed ZnO nanorods

Large-scale uniform aligned ZnO nanorods with a hexagonal tip were successfully synthesized via a facile process at low temperature of (～140 °C) without using any additives and substrate. The process is based on a simple reaction of zinc powder and de-ionized water. The results reveal that the as-prepared ZnO products have an average length of 10 μm and a diameter in the range of 50–260 nm, possessing a single crystal wurtzite structure. The structure and morphology of the ZnO products are characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and energy dispersive X-ray spectrometer (EDX). The possible formation mechanism of nanorods is proposed in brief. The optical properties of grown products were characterized by room-temperature. The magnetic property was tested with a vibrating sample magnetometer at room temperature and revealed a high hysteresis loop indicating a strong ferromagnetic nature of as synthesized ZnO nanorods. The yield producing nanorods with this method includes ease, flexibility, fast being low cost and ineffective on environment free.     

Time growing comparison for ZnO nanorod by using microwave irradiation method

In this study, zinc oxide (ZnO) nanorod were successfully prepared at different growth times (15, 30 and 60 min) using the microwave irradiation method. The ZnO nanorods were simply synthesized at a low temperature (90 °C) with low power microwave assisted heating (about 100 W) and a subsequent ageing process. The synthesized nanorod were characterized using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), energy dispersive X-ray (EDX) and Ultraviolet–Visible spectroscopy (UV–Vis). The FESEM images showed nanorods with diameter ranging between 50 and 150 nm, and length of 150–550 nm. The XRD results indicate that ZnO nanorods of different time of growth exhibits pure wurtzite structure with lattice parameters of 3.2568 and 5.2125 Å. UV–Vis characterization showed that energy gap decreases with increase in time. The result also shows that growth of ZnO at 60 min produces an energy band gap of 3.15 eV. In general, the results of the study confirm that the microwave irradiation method is a promising low temperature, cheap and fast method for the production of ZnO nanostructures.     

氧化锌纳米棒的水热合成及其光催化性能

以分析纯ZnO作为锌源、NaOH为矿化剂、盐酸为反应溶液pH调节剂,利用水热反应制备了花状ZnO纳米棒;采用扫描电子显微镜和X射线衍射仪分析了产物的形貌和结构,考察了水热温度以及Zn2+和OH-浓度比对产物形貌的影响;以甲基橙为目标降解物,采用紫外-可见分光光度计研究了ZnO纳米棒的光催化性能.结果表明,在水热反应温度80℃、Zn2+/OH-浓度比1∶7.5条件下所得ZnO纳米棒呈花状聚合,直径约为200nm,长度约为2μm,具有六方纤锌矿结构.当甲基橙初始浓度为30 mg.L-1、ZnO纳米棒的投放量为1.5g.L-1时,以300W紫外灯照射150min,甲基橙的降解率可达90%.     

Synthesis of cobalt-doped ZnO/rGO nanoparticles with visible-light photocatalytic activity through a cobalt-induced electrochemical method

ZnO is a semiconductor photocatalyst widely applied in photodegradation of organic pollutants and in photoelectric conversion. ZnO exhibits low photocatalytic activity due to poor absorption in the visible region. In this work, a novel cobalt-induced electrochemical growth method was developed to synthesize cobalt-doped ZnO/rGO nanoparticles in an aqueous solution at room temperature. Cobalt-doped ZnO/rGO nanoparticles exhibited wider visible-light absorption band ranging from 400 nm to 700 nm due to cobalt doping. The surface structure of ZnO formed by the cobalt-induced electrochemical method without other ions is suitable for photocatalytic reactions. The cobalt-doped ZnO/rGO nanoparticles were found to exhibit in photodegradation and photo-electrochemical measurements and exhibited enhanced photocatalytic activity under visible-light irradiation.     

Simple solvothermal route to synthesize ZnO nanosheets, nanonails, and well-aligned nanorod arrays

ZnO nanosheets, nanonails, and well-aligned nanorods were fabricated on Zn foils by a solvothermal approach using ethanol as the solvent. A lower synthesis temperature and a shorter time period favor the formation of nanosheets. By optimizing the synthesis temperature and time period, ZnO nanonails with a hexagonal cap and a long stem could be produced. A higher temperature was not favorable to produce uniform and smooth nanorods. Well-aligned ZnO nanorod arrays were produced with diameters within 100-250 nm and lengths up to approximately 6 microm when NaOH was added to the solvent. By optimizing the reaction parameters, the morphology, size, and orientation of the nanoforms could be tailored. The ZnO nanorods exhibit an excitonic strong UV emission and a defect-related broad green emission at room temperature. The defect-related green emission band decreased with the improvement of the degree of alignment of the nanorods.     

Straight and thin ZnO nanorods: hectogram-scale synthesis at low temperature and cathodoluminescence

A novel seed-assisted chemical reaction at 95 degrees C has been employed to synthesize uniform, straight, thin, and single-crystalline ZnO nanorods on a hectogram scale. The molar ratio of ZnO seed and zinc source plays a critical role in the preparation of thin ZnO nanorods. At a low molar ratio of ZnO seed and zinc source, javelin-like ZnO nanorods consisting of thin ZnO nanorods with a diameter of 100 nm and thick ZnO nanorods with a diameter of 200 nm have been obtained. In contrast, straight ZnO nanorods with a diameter of about 20 nm have been prepared. Dispersants such as poly(vinyl alcohol) act spatial obstructors to control the length of ZnO nanorods. The morphology, structure, and optical property of the ZnO nanostructures prepared under different conditions have been characterized by transmission electron microscopy, field emission scanning electron microscopy, X-ray powder diffraction, high-resolution transmission electron microscopy, and cathodoluminescence. The formation mechanisms for the synthesized nanostructures with different morphologies have been phenomenologically presented.     

Mild benzene-thermal route to GaP nanorods and nanospheres

GaP nanorods and nanospheres were synthesized from a mild benzene-thermal route at 240 and 300 degrees C, respectively, using Na, P, and GaCl(3) as the starting materials. The structure of the products was identified as zinc blende phase by X-ray powder diffraction (XRD). Transmission electron microscopy (TEM) images showed that, when the reaction temperature was 240 degrees C, the products were nanorods with widths of 20-40 nm and lengths of 200-500 nm and nanospheres with diameters of 20-40 nm. However, when the reaction temperature was increased to 300 degrees C, the products were only nanospheres, and the diameters increased to 40-60 nm. The reaction proceeded through a metallic gallium intermediate, and a solution-liquid-solid (SLS) mechanism was proposed for the one-dimensional growth. The products were also investigated by UV-vis absorption and X-ray photoelectron spectroscopy.     

ZnO纳米棒阵列在TiO2介孔薄膜上的生长及其表征

通过低温水热法成功地将ZnO纳米棒阵列定向生长在了介孔锐钛矿TiO2纳米晶薄膜上,并主要利用X射线衍射、场发射扫描电子显微镜和光致发光光谱等对其进行了表征。所制备的纳米棒具有六边形的端面,纳米棒的尺寸及端面边长分布范围窄,并且沿c轴方向(002)表现出了明显的择优化生长。此外,相比于玻璃基底或TiO2纳米颗粒薄膜,生长在介孔TiO2薄膜上的ZnO纳米棒阵列表现出了较好的取向生长,表明基底的表面结构和组成对ZnO纳米棒阵列的生长有显著的影响。根据基底有序的多孔结构,讨论了纳米棒阵列可能的生长机理。所得到的ZnO纳米棒阵列在室温下分别表现出了以370 nm为中心的强近紫外光和以530 nm为中心的弱绿光两条荧光谱带。     

Well Oriented ZnO Nanorods Array: Negative Resistance and Optical Switching

Well‐oriented ZnO nanorods (NRs) arrays were grown on Si, alumina, quartz, and FTO substrates through a ZnO seed layer followed by low temperature wet chemical process. The influence of sputtered ZnO seed layer thickness (100, 50, 32, and 16 nm), annealing temperature and CuO_x coverage on the characteristics of ZnO NRs were investigated in this study. The crystalline structural, chemical, morphological, optical, and electrical properties of ZnO NRs arrays were studied by X‐ray diffraction (XRD), field emission‐ scanning electron microscopy equipped by energy dispersive X‐ray spectroscopy (FE‐SEM/EDX), Raman scattering, UV/Vis ‐ near IR absorption spectroscopy and current‐voltage characteristic. XRD and Raman spectra measurement revealed that the synthesize ZnO displayed hexagonal wurtzite structure. The individual rod diameter, density, and orientation can be controlled by varying the seed layer thickness. The mean diameter and maximum length of ZnO NRs are around 55–66 nm and 282 nm, respectively. ZnO NRs/ ZnO thin film structure shows optical switching and negative differential resistance behavior as applicable to ON/OFF gate and memory devices.     

均相沉淀法合成纳米ZnO及其光催化性能研究

以ZnSO_4、尿素为原料,采用均相沉淀法在90 ℃合成出了纳米ZnO,并就反应 温度、反应时间、反应物浓度及物料配比等条件对产物的影响进行了探讨。XRD物 相分析,产物为六方晶系;TEM形貌观察,粒子基本为球形,平均粒径20 nm;并用 IR,TG-DTA等测试手段对其进行了表征。利用紫外-可见分光光度计测试了光吸收 性能,发现纳米氧化锌对200～380 nm波长范围的光有很强吸收性,在可见光范围 内,也有较强的吸收。利用纳米氧化锌作为光催化剂对有机染料溶液进行了降解实 验,发现在日光照射60 min后,对酸性大红4BE的降解率可达100%。