Adsorption and inhibitive properties of aminobiphenyl and its Schiff base on mild steel corrosion in 0.5 M HCl medium

Electrochemical measurements were performed to investigate the effectiveness and adsorption behaviour of aminobiphenyl (Aph) and 2-(3-hydroxybenzylideneamino)biphenyl (Aph-S), as corrosion inhibitors for mild steel (MS) in 0.5 M HCl solution. Potentiodynamic polarization, linear polarization resistance (LP) and electrochemical impedance spectroscopy (EIS) techniques were applied to study the metal corrosion behaviour in the absence and presence of different concentrations of Aph and Aph-S. In order to gain more information about adsorption mechanism the AC impedance technique was used to evaluate the potential of zero charge (PZC) from polarization resistance (R_p) versus voltage (E) plot. Potentiodynamic polarization measurements showed that Aph act as cathodic type inhibitor where as Aph-S act mixed type. The inhibition efficiency (IE%) increases with increasing concentration of compounds and reached 92.6% for Aph and 97.2% for Aph-S at 5 × 10⁻³ M. Double layer capacitance (C_dl) and polarization resistance (R_p) values are derived from Nyquist plots obtained from AC impedance studies. The experimental data fit Langmuir isotherm for both Aph and Aph-S, and from the adsorption isotherm some thermodynamic data for the adsorption processes are calculated and discussed. The effect of exposure time on the corrosion behaviour of mild steel in the absence and presence of inhibitor over 168 h was also studied.     

Inhibition effect of environmentally benign Karanj (Pongamia pinnata) seed extract on corrosion of mild steel in hydrochloric acid solution

The inhibition of the corrosion of mild steel in hydrochloric acid solution by the seed extract of Karanj (Pongamia pinnata) has been studied using weight loss, electrochemical impedance spectroscopy, potentiodynamic polarization, and linear polarization techniques. Inhibition was found to increase with increasing concentration of the extract. The effect of temperature, immersion time, and acid concentration on the corrosion behavior of mild steel in 1 M HCl with addition of extract was also studied. The adsorption of the extract on the mild steel surface obeyed the Langmuir adsorption isotherm. Values of inhibition efficiency calculated from weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopy are in good agreement. Polarization curves showed that Karanj (P. pinnata) seed extract behaves as a mixed-type inhibitor in hydrochloric acid. The activation energy as well as other thermodynamic parameters for the inhibition process was calculated. The adsorbed film on mild steel surface containing Karanj (P. pinnata) seed extract inhibitor was also measured by Fourier transform infrared spectroscopy. The results obtained showed that the seed extract of Karanj (P. pinnata) could serve as an effective inhibitor of the corrosion of mild steel in hydrochloric acid media.     

1,7′-dimethyl-2′-propyl-1<Emphasis Type="Italic">H</Emphasis>,3′<Emphasis Type="Italic">H</Emphasis>-2,5′-bibenzo[<Emphasis Type="Italic">d</Emphasis>]imidazole as a corrosion inhibitor of mild steel in 1 M HCl

Inhibition effect of imidazole derivative 1,7′-dimethyl-2′-propyl-1H,3′H-2,5′-bibenzo[d]imidazole (DPBI) against mild steel corrosion in 1 M HCl solutions was evaluated using the conventional mass loss method, potentiodynamic polarization, linear polarization, and electrochemical impedance spectroscopy. The mass loss results showed that DPBI is an excellent corrosion inhibitor; electrochemical polarizations data revealed the mixed mode of inhibition; and the results of electrochemical impedance spectroscopy showed that the change in the impedance parameters, charge transfer resistance, and double layer capacitance with the change in the concentration of the inhibitor is due to the adsorption of the molecule leading to the formation of a protective layer on the surface of mild steel. The inhibition action of this compound was assumed to occur via adsorption on the steel surface through the active centers of the molecule.     

Inhibitory effects of Murraya koenigii (curry leaf) leaf extract on the corrosion of mild steel in 1 M HCl

Abstract

The inhibitive effect of the Murraya koenigii (curry leaf) leaf extract on the corrosion of mild steel in 1 M HCl was investigated by using weight loss, open circuit potential measurements, potentiostatic polarization techniques, and impedance analysis. The results show that Murraya koenigii extract is an effective corrosion inhibitor for protecting the corrosion of mild steel in 1 M HCl medium even at stimulated conditions. The inhibition efficiency increases with increasing the concentration of the inhibitor in the medium. The percentage inhibitor efficiency under stagnant condition calculated based on weight loss method is found to be above 94.5% when the medium contains 1000 ppm of the inhibitor.     

Study on the Inhibition of Mild Steel Corrosion by Cationic Gemini Surfactant in 1 M HCl

The cationic gemini surfactant 1,2-bis(N-tetradecyl-N,N-dimethylammonium)ethane dibromide (14-2-14) was synthesized using a previously described method. The surfactant was characterized using ¹H NMR. The corrosion inhibition effect of 14-2-14 on mild steel in 1 M HCl at temperatures 30–60°C was studied using weight loss measurements, potentiodynamic polarization measurements and electrochemical impedance spectroscopy. Morphology of the corroded mild steel specimens was examined using scanning electron microscopy (SEM). The results of the studies show that gemini surfactant is an efficient inhibitor for mild steel corrosion in 1 M HCl; the maximum inhibition efficiency (IE) of 98.06% is observed at surfactant concentration of 100 ppm at 60°C. The %IE increases with the increasing inhibitor concentration and temperature. The adsorption of inhibitor on the mild steel surface obeys Langmuir adsorption isotherm. SEM studies confirmed smoother surface for inhibited mild steel specimen.     

Adsorption Behavior and Inhibition Corrosion Effect of Sodium Carboxymethyl Cellulose on Mild Steel in Acidic Medium

The effect of sodium carboxymethyl cellulose (Na-CMC) on the corrosion behavior of mild steel in 1.0 mol·L⁻¹ HCl solution has been investigated by using weight loss (WL) measurement, potentiodynamic polarization, linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS) methods. These results showed that the inhibition efficiency of Na-CMC increased with increasing the inhibitor concentration. Potentiodynamic polarization studies revealed that the Na-CMC was a mixed type inhibitor in 1.0 mol·L⁻¹ HCl. The adsorption of the inhibitor on mild steel surface has been found to obey the Langmuir isotherm. The effect of temperature on the corrosion behavior of mild steel in 1.0 mol·L⁻¹ HCl with addition of 0.04% of Na-CMC has been studied in the temperature range of 298–328 K. The associated apparent activation energy (E^*_a) of corrosion reaction has been determined. Scanning electron microscopy (SEM) has been applied to investigate the surface morphology of mild steel in the absence and presence of the inhibitor molecules.     

酸性介质中羧甲基纤维素钠在低碳钢表面的吸附和缓蚀作用

The effect of sodiumcarboxymethyl cellulose (Na-CMC) on the corrosion behavior of mild steel in 1.0 mol·L-1 HCl solution has been investigated by using weight loss (WL) measurement, potentiodynamic polarization, linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS) methods. These results showed that the inhibition efficiency of Na-CMC increased with increasing the inhibitor concentration. Potentiodynamic polarization studies revealed that the Na-CMC was a mixed type inhibitor in 1.0 mol·L-1 HCl. The adsorption of the inhibitor on mild steel surface has been found to obey the Langmuir isotherm. The effect of temperature on the corrosion behavior of mild steel in 1.0 mol·L -1 HCl with addition of 0.04% of Na-CMC has been studied in the temperature range of 298-328 K. The associated apparent activation energy (E*a) of corrosion reaction has been determined. Scanning electron microscopy (SEM) has been applied to investigate the surface morphology of mild steel in the absence and presence of the inhibitor molecules.     

The inhibition behavior of two pyrimidine-pyrazole derivatives against corrosion in hydrochloric solution: Experimental,surface analysis and in silico approach studies

Two pyrimidine-pyrazole derivatives have been investigated as corrosion inhibitors for mild steel in acidic medium using weight loss measurement, polarization curve and electrochemical impedance spectroscopy (EIS). The results obtained reveal that these compounds perform as corrosion inhibitors for mild steel in 1 M HCl. The values of inhibition efficiency calculated from three experimental techniques are reasonably in good agreement. The adsorption process of these compounds on surface of mild steel obeys to El Awady isotherm. Also, the adsorption process of inhibitors studied explaining by surface analysis (EDX). This work followed by in silico approach studies. Firstly, we used Marvinsketch.18 program in order to detect predominant form of inhibitors in electrolytic solution and then computed by Gaussian 09 based on the DFT method at B3LYP/6-31G (d,p).The results obtained theoretically are in good correlation with those obtained experimentally.     

Electrochemical investigation of corrosion and corrosion inhibition of iron in hydrochloric acid solutions

The inhibition effect of 1-methyl pyrazole (MPA) on the acidic corrosion of iron in 1.0 M HCl was studied at different concentrations (10^?3–10^?2 M) by potentiodynamic polarization and electrochemical impedance spectroscopy, and EIS measurements. It is found from the polarization studies that methyl pyrazole (MPA) behaves mainly as anodic inhibitor in HCl. Values of polarization resistance (R_p) and double layer capacitance (C_dl) in the absence and presence of MPA in 1.0 M HCl are determined. The adsorption of MPA on iron surface from HCl is found to obey Temkin adsorption isotherm.     

An experimental and theoretical investigation on adsorption properties of some diphenolic Schiff bases as corrosion inhibitors at acidic solution/mild steel interface

The effect of novel synthesized three Schiff bases, namely, 1,3-bis[2-(2-hydroxy benzylidenamino) phenoxy] propane (P1), 1,3-bis[2-(5-chloro-2-hydroxybenzylidenamino) phenoxy] propane (P2), and 1,3-bis[2-(5-bromo-2-hydroxybenzylidenamino) phenoxy] propane (P3), on the corrosion of mild steel in 0.1 M HCl was investigated using potentiodynamic polarization and electrochemical impedance spectroscopy methods. Polarization measurements suggest that P1 acts as mixed type inhibitor while P2 and P3 behave as mainly cathodic inhibitors for acidic corrosion of steel. All electrochemical measurements show that inhibition efficiencies increase with increase in inhibitor concentration. This reveals that inhibitive actions of inhibitors were mainly due to adsorption on steel surface. Adsorption of these inhibitors follows Temkin adsorption isotherm. The correlation between the adsorption ability of inhibitors and their molecular structures has been investigated using quantum chemical parameters obtained by MNDO semi-empirical method. Calculated quantum chemical parameters indicate that Schiff bases adsorbed on steel surface by chemical mechanism.     

Corrosion prevention of mild steel in acidic medium by 2-Pyrrolidin-1-yl-1,3-thiazole-5-carboxylic acid: Theoretical and experimental approach

The inhibition efficiency of 2-Pyrrolidin-1-yl-1,3-thiazole-5-carboxylic acid (PTCA) against mild steel (MS) corrosion was investigated in acidic solution by using quantum chemical calculations based on Density Functional Theory (DFT) method and electrochemical measurements. The electrochemical impedance spectroscopy (EIS), potentiodynamic, potential zero charge (pzc) analysis and electrochemical noise (EN) measurements at various concentrations (from 0.1 to 10 mM) and immersion times were utilized in experimental part. The surface analysis was achieved scanning electron microscope (SEM) and contact angle measurements in the absence and presence of 10 mM PTCA. According to DFT results, PTCA exhibited 3.737 eV band gap and 8.130 Debye dipole moment which were a signal of potentially convenient corrosion inhibitor properties. PTCA has a remarkable corrosion inhibition capability to mild steel, which inhibited both anodic and cathodic corrosion rates, relying on it's physically adsorption on the metal solution interface and protection ability was increased with increasing PTCA concentration. The obtained adsorption equilibrium constant was 11.11 × 10³ M^-1 and calculated standard free energy of adsorption was ?33.03 kJ mol^?1. The determined activation energy values were 55.58 kJ mol^?1 and 96.86 kJ mol^?1 in 0.5 M HCl in the absence and presence of 10 mM PTCA, respectively. PTCA demonstrated a strong inhibition efficiency of 98.3%, after 168 h immersion, according to the EIS results. As a consequently, we recommend that PTCA is a convenient inhibitor in 0.1 M HCl for mild steel protection against corrosion.     

Polyvinyl alcohol–sulphanilic acid water soluble composite as corrosion inhibitor for mild steel in hydrochloric acid medium

The inhibitive action of synthesised polyvinyl alcohol–sulphanilic acid (PVASA) composite on the corrosion of commercial mild steel in 1 M HCl medium has been investigated by weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopic (EIS) methods. Characterization of PVASA composite has been carried out using Fourier transform infrared spectroscopy (FTIR). Experimental results reveal that PVASA composite acts as an inhibitor in the acid environment. The inhibition efficiency increases with an increase in the concentration of the inhibitor. Maximum inhibition efficiency of PVASA composite was found to be 84% at 6000 ppm. Thermodynamic and kinetic parameters have been obtained from temperature studies. Electrochemical measurement reveals that PVASA composite acts as a mixed inhibitor and the adsorption follows Langmuir adsorption isotherm.     

Sildenafil citrate (Viagra) as a corrosion inhibitor for carbon steel in hydrochloric acid solutions

Abstract  

The inhibition effect of sildenafil citrate (Viagra) on the corrosion of carbon steel in 1 M HCl was studied by weight loss, polarization, electrochemical impedance spectroscopy, and UV–Vis spectrophotometry. The results showed that sildenafil citrate is a good corrosion inhibitor for carbon steel in acidic media and acts as mixed type (cathodic/anodic) inhibitor. The adsorption of the inhibitor was well described by the Langmuir adsorption isotherm. Some thermodynamic parameters such as adsorption heat, adsorption entropy, and adsorption free energy were calculated. Kinetic parameters such as the apparent activation energy and pre-exponential factor were calculated and discussed.     

The effect of 2-aminoquinoline-6-carboxylic acid on the corrosion behavior of mild steel in hydrochloric acid

The inhibitive effect of 2-aminoquinoline-6-carboxylic acid (AQC) against mild steel corrosion in 1?M HCl solutions was investigated using conventional weight loss, potentiodynamic polarization, linear polarization and electrochemical impedance spectroscopy methods. The weight loss results showed that AQC is an excellent corrosion inhibitor since its efficiency increased with the concentration to attain 91.8?% at 500?mg?l^?1. Electrochemical polarization measurements revealed that AQC acted as a mixed-type inhibitor and the results of electrochemical impedance spectroscopy have shown that the change in the impedance parameters, charge transfer resistance and double layer capacitance, with the change in concentration of the inhibitor is due to the adsorption of the molecule leading to the formation of a protective layer on the surface of mild steel. The adsorption was assumed to occur on the steel surface through the active centers of the molecule. The inhibition action of AQC was discussed in view of Langmuir adsorption isotherm. Density functional theory calculations of quantum parameters were used to explain efficiency in relation with molecular structure.     

Corrosion inhibition of mild steel by highly stable polydentate schiff base derived from 1,3- propanediamine in aqueous acidic solution

Recently, the hydrolysis of Schiff bases under experimental conditions gives suspicion for their corrosion inhibition performance. The current study employs a stable Schiff base namely, 2,2′-{propane-1,3-diylbis[azanylylidene (E) methanylylidene]}bis(6-methoxyphenol) (LPD) as corrosion inhibitor for mild steel (MS) in 1 M HCl solution. The presence of the characteristic peak of the imine group in UV-visible spectra was taken as an indicator for LPD stability in acidic media. The inhibition action was examined using electrochemical techniques including potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) besides gravimetric measurement. The inhibition efficiency reached 95.93 % for 0.75 mM LPD after 24 h of immersion at 25 °C. This high efficiency is owing to the presence of the characteristic imine group and other heteroatoms and π- electrons of the aromatic benzene rings. The mechanism of inhibition depends on adsorption phenomena on mild steel surface which obeys Langmuir isotherm model. The calculated values of adsorption equilibrium constant (K_ads), adsorption free energy ΔG_ads, adsorption enthalpy ΔH_ads and adsorption entropy ΔS_ads indicated spontaneous exothermic adsorption process of both physical and chemical nature. By rising temperature, the inhibition efficiency of LPD was decreased. The calculated activation energy was increased as the concentration of LPD increased. LPD was considered as a mixed-type inhibitor as indicated from PDP measurements. The obtained surface morphology and composition analysis using SEM/EDS, AFM and FTIR techniques ensures the high efficiency of LPD as corrosion inhibitor.     

The effect of 1′,3,5,5′-tetramethyl-1′<Emphasis Type="Italic">H</Emphasis>-1,3′-bipyrazole on the corrosion of steel in 1.0 <Emphasis Type="SmallCaps">M</Emphasis> hydrochloric acid

The effect of some prepared compounds, namely 3,5-dimethyl-1H-pyrazole (P1), 3(5)-amino-5(3)-methylpyrazole (P2), and 1′,3,5,5′-tetramethyl-1′H-1,3′-bipyrazole (P3), on the corrosion behaviour of steel in 1.0 M hydrochloric acid solution as corrosive medium has been investigated at 308 K using weight-loss measurement, potentiodynamic polarisation, linear polarisation, and impedance spectroscopy (EIS). Generally, inhibition efficiency of the investigated compounds was found to depend on the concentration and nature of the inhibitor. P3 was a better inhibitor than P1 and P2, and its inhibition efficiency increased with increasing concentration of inhibitor, attaining 94% above 10⁻³  M. Potentiodynamic polarisation studies clearly reveal that P3 acts essentially as a cathodic inhibitor. E (%) values obtained from different methods are in reasonably good agreement. EIS measurements show an increase of transfer resistance with inhibitor concentration. Partial π-charge on atoms was calculated. Correlation between the highest occupied molecular orbital energy E _HOMO and inhibition efficiencies was sought. The temperature effect on the corrosion behaviour of steel in 1.0 M HCl without and with different concentrations of inhibitor P3 was studied in the temperature range 308 to 343 K. Thermodynamic data, for example heat of adsorption ( \Updelta H_\textads^° \Updelta H_{\text{ads}}^{^\circ } ), entropy of adsorption ( \Updelta S_\textads^° \Updelta S_{\text{ads}}^{^\circ } ) and free energy of adsorption ( \Updelta G_\textads^° \Updelta G_{\text{ads}}^{^\circ } ) were calculated by use of thermodynamic equations. Kinetic activation data, for example E _a, ΔH*, ΔS* and pre-exponential factor, were calculated, and are discussed. The inhibiting action of P3 on the corrosion of steel in 1–10 M hydrochloric acid was also studied by weight-loss measurement. The rate constant and reaction constant were calculated for the corrosion reactions. Adsorption of P3 on the steel surface in 1.0 M HCl follows the Langmuir isotherm model.     

Schiff’s base derived from the pharmaceutical drug Dapsone (DS) as a new and effective corrosion inhibitor for mild steel in hydrochloric acid

The inhibition ability of Dapsone’s Schiff’s base with salicylaldehyde (1:2) for mild steel corrosion in 1 M HCl solution at 308 K was studied by means of potentiodynamic polarization, electrochemical impedance spectroscopy techniques, and gravimetric analysis. Results showed that Dapsone salicylaldehyde performed well as a good inhibitor for mild steel in 1 M HCl solution with maximum inhibition efficiency of 95 % at 500 ppm. The adsorption isotherm of the inhibitor followed the Langmuir adsorption. The value of free energy of adsorption showed that it is a spontaneous process and followed typical physical adsorption.     

Gravimetric,electrochemical, and morphological studies of an isoxazole derivative as corrosion inhibitor for mild steel in 1M HCl

In present study, an isoxazole derivative, namely, (Z)-4-(4-hydroxy-3-methoxybenzylidene)-3-methylisoxazol-5(4H)-one referred here as (IOD) has been studied as an environment-friendly corrosion inhibitor for mild steel (MS) in acidic medium (1 M HCl). The present work was investigated by gravimetric, electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PDP), fourier-transform infrared (FT-IR) spectroscopy techniques. Atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS) confirmed the surface morphologies of the MS surface with and without IOD in the acid medium. The inhibition efficiency (I.E.) of IOD was increased by rising its concentration attaining maximum value (96.6%) at 300 ppm at 30 °C and decreases with increasing temperature from 30 °C to 60 °C. The adsorption of studied inhibitor followed Langmuir adsorption isotherm model. The PDP study revealed that the IOD acts as a mixed-type inhibitor with predominating anodic effect. The EIS study confirmed that increasing IOD concentration enhances the charge transfer resistance (R_ct) and then reduces the double layer capacitance (C_dl) owing to the development of a protective layer on the MS surface.     

Poly (vinyl alcohol – aniline) water soluble composite as corrosion inhibitor for mild steel in 1 M HCl

Poly (vinyl alcohol – aniline) PVAA composite was tested for its performance in protecting mild steel MS against corrosion in 1 M HCl. The inhibitive parameters were evaluated by means of weight loss, electrochemical polarization and impedance methods. Results indicated that the addition of PVAA to the acid reduces the corrosion of the metal. Inhibition efficiency increases with increase in inhibitor concentration. The results further revealed that PVAA at a concentration of 2000 ppm furnishes a maximum of 92% inhibition efficiency. Thermodynamic parameters such as free energy of adsorption, heat of adsorption, etc., had been evaluated from temperature studies. The adsorption of PVAA followed Langmuir and Temkin adsorption isotherms. Polarization curves revealed that PVAA is a mixed inhibitor.     

Aqueous extract of Acacia cyanophylla leaves as environmentally friendly inhibitor for mild steel corrosion in 1 M H2SO4 solution

The efficiency of Acacia cyanophylla leaves extract as an environmentally friendly inhibitor for mild steel in aerated aqueous 1 M H₂SO₄ solution has been investigated by potentiodynamic polarization measurements and electrochemical impedance spectroscopy techniques. Addition of inhibitor decreases the corrosion current whereas the corrosion potential values show slight shifts in positive directions. Inhibition efficiency was found to be about 93% (the maximum value was determined from the polarization curve). Efficiencies obtained from both electrochemical techniques are in good agreement. Adsorption of Acacia cyanophylla leaves extract on mild steel surface in 1 M H₂SO₄ solution obeys Langmuir adsorption isotherm. Polarization curves were also obtained at different temperatures in order to measure changes of corrosion rate. Corrosion current increases and inhibition efficiency decreases with temperature increasing in H₂SO₄ solutions with and without Acacia cyanophylla extract. Corrosion parameters also changed with exposure time. Copyright © 2010 John Wiley & Sons, Ltd.