Excellent Capacitive Performance of a Three‐Dimensional Hierarchical Porous Graphene/Carbon Composite with a Superhigh Surface Area

Three‐dimensional hierarchical porous graphene/carbon composite was successfully synthesized from a solution of graphene oxide and a phenolic resin by using a facile and efficient method. The morphology, structure, and surface property of the composite were investigated intensively by a variety of means such as scanning electron microscopy (SEM), transmission electron microscopy (TEM), N₂ adsorption, Raman spectroscopy, and Fourier transform infrared spectroscopy (FTIR). It is found that graphene serves as a scaffold to form a hierarchical pore texture in the composite, resulting in its superhigh surface area of 2034 m²g^?1, thin macropore wall, and high conductivity (152 S m^?1). As evidenced by electrochemical measurements in both EMImBF₄ ionic liquid and KOH electrolyte, the composite exhibits ideal capacitive behavior, high capacitance, and excellent rate performance due to its unique structure. In EMImBF₄, the composite has a high energy density of up to 50.1 Wh kg^?1 and also possesses quite stable cycling stability at 100 °C, suggesting its promising application in high‐temperature supercapacitors. In KOH electrolyte, the specific capacitance of this composite can reach up to an unprecedented value of 186.5 F g^?1, even at a very high current density of 50 A g^?1, suggesting its prosperous application in high‐power applications.     

Multifunctional Ag‐Decorated Porous TiO2 Nanofibers in Dye‐Sensitized Solar Cells: Efficient Light Harvesting,Light Scattering,and Electrolyte Contact

Designing the photoanode structure in dye‐sensitized solar cells (DSSCs) is vital to realizing enhanced power conversion efficiency (PCE). Herein, novel multifunctional silver‐decorated porous titanium dioxide nanofibers (Ag/pTiO₂ NFs) made by simple electrospinning, etching, and chemical reduction processes are introduced. The Ag/pTiO₂ NFs with a high surface area of 163 m² g^?1 provided sufficient dye adsorption for light harvesting. Moreover, the approximately 200 nm diameter and rough surface of the Ag/pTiO₂ NFs offered enough light scattering, and the enlarged interpores among the NFs in the photoanode also permitted electrolyte circulation. Ag nanoparticles (NPs) were well dispersed on the surface of the TiO₂ NFs, which prevented aggregation of the Ag NPs after calcination. Furthermore, a localized surface plasmon resonance effect by the Ag NPs served to increase the light absorption at visible wavelengths. The surface area and amount of Ag NPs was optimized. The PCE of pTiO₂ NF‐based DSSCs was 27 % higher (from 6.2 to 7.9 %) than for pure TiO₂ NFs, whereas the PCE of Ag/pTiO₂ NF‐based DSSCs increased by about 12 % (from 7.9 to 8.8 %). Thus, the PCE of the multifunctional pTiO₂ NFs was improved by 42 %, that is, from 6.2 to 8.8 %.     

Triarylboron‐Linked Conjugated Microporous Polymers: Sensing and Removal of Fluoride Ions

A luminescent conjugated microporous polymer (BCMP‐3) has been synthesized in high yield by a carbon–carbon coupling reaction using triarylboron as a building unit. BCMP‐3 was fully characterized by using powder X‐ray diffraction analysis, Fourier transform infrared spectroscopy, ¹³C solid‐state NMR spectroscopy, field emission scanning electron microscopy, thermogravimetric analysis, and nitrogen and carbon dioxide adsorption. The new three‐dimensional conjugated framework possess a high Brunauer–Emmett–Teller (BET) specific surface area up to 950 m² g^?1 with a pore volume of 0.768 cm³ g^?1, good stability, and abundant boron sites in the skeleton. Under excited‐light irradiation, BCMP‐3 exhibits strong fluorescent emission at 488 nm with a high absolute quantum yield of 18 % in the solid state. Polymer BCMP‐3 acts as a colorimetric and fluorescent chemosensor with high sensitivity and selectivity for F^? over other common anions. In addition, the polymer also works as an adsorbent for F^? removal and shows good adsorption capacities of up to 24 mg g^?1 at equilibrium F^? concentrations of 16 mg L^?1 and a temperature of 298 K. The adsorption kinetics and isotherm were analyzed by fitting experimental data with pseudo‐second‐order kinetics and Langmuir equations. Furthermore, we highlight that BCMP‐3 is an adsorbent for fluoride removal that can be efficiently reused many times without loss of adsorption efficiency.     

Heat‐Treated Aerogel as a Catalyst for the Oxygen Reduction Reaction

Aerogels are fascinating materials that can be used for a wide range of applications, one of which is electrocatalysis of the important oxygen reduction reaction. In their inorganic form, aerogels can have ultrahigh catalytic site density, high surface area, and tunable physical properties and chemical structures—important features in heterogeneous catalysis. Herein, we report on the synthesis and electrocatalytic properties of an iron–porphyrin aerogel. 5,10,15,20‐(Tetra‐4‐aminophenyl)porphyrin (H₂TAPP) and Fe^II were used as building blocks of the aerogel, which was later heat‐treated at 600 °C to enhance electronic conductivity and catalytic activity, while preserving its macrostructure. The resulting material has a very high concentration of atomically dispersed catalytic sites (9.7×10²⁰ sites g^?1) capable of catalyzing the oxygen reduction reaction in alkaline solution (E_onset=0.92 V vs. RHE, TOF=0.25 e^? site^?1 s^?1 at 0.80 V vs. RHE).     

One‐Pot Synthesis of Pomegranate‐Structured Fe3O4/Carbon Nanospheres‐Doped Graphene Aerogel for High‐Rate Lithium Ion Batteries

A unique hierarchically nanostructured composite of iron oxide/carbon (Fe₃O₄/C) nanospheres‐doped three‐dimensional (3D) graphene aerogel has been fabricated by a one‐pot hydrothermal strategy. In this novel nanostructured composite aerogel, uniform Fe₃O₄ nanocrystals (5–10 nm) are individually embedded in carbon nanospheres (ca. 50 nm) forming a pomegranate‐like structure. The carbon matrix suppresses the aggregation of Fe₃O₄ nanocrystals, avoids direct exposure of the encapsulated Fe₃O₄ to the electrolyte, and buffers the volume expansion. Meanwhile, the interconnected 3D graphene aerogel further serves to reinforce the structure of the Fe₃O₄/C nanospheres and enhances the electrical conductivity of the overall electrode. Therefore, the carbon matrix and the interconnected graphene network entrap the Fe₃O₄ nanocrystals such that their electrochemical function is retained even after fracture. This novel hierarchical aerogel structure delivers a long‐term stability of 634 mA h g^?1 over 1000 cycles at a high current density of 6 A g^?1 (7 C), and an excellent rate capability of 413 mA h g^?1 at 10 A g^?1 (11 C), thus exhibiting great potential as an anode composite structure for durable high‐rate lithium‐ion batteries.     

Preparation and characterization of a nitrogen-doped mesoporous carbon aerogel and its polymer precursor

Nitrogen-containing carbon aerogel was prepared from resorcinol–melamine–formaldehyde (R–M–F) polymer gel precursor. The polymer gel was supercritically dried with CO₂, and the carbonization of the resulting polymer aerogel under nitrogen atmosphere at 900 °C yielded the carbon aerogel. The polymer and carbon aerogels were characterized with TG/DTA–MS, low-temperature nitrogen adsorption/desorption (??196 °C), FTIR, Raman, powder XRD and SEM–EDX techniques. The thermal decomposition of the polymer aerogel had two major steps. The first step was at 150 °C, where the unreacted monomers and the residual solvent were released, and the second one at 300 °C, where the species belonging to the polymer network decomposition could be detected. The pyrolytic conversion of the polymer aerogel was successful, as 0.89 at.% nitrogen was retained in the carbon matrix. The nitrogen-doped carbon aerogel was amorphous and possessed a hierarchical porous structure. It had a significant specific surface area (890 m² g^?1) and pore volume (4.7 cm³ g^?1). TG/DTA–MS measurement revealed that during storage in ambient conditions surface functional groups formed, which were released upon annealing.     

One‐stage Template‐free KOH Activation for Mesopore‐enriched Carbons and Their Application in CO2 Capture

Activated carbons with a high mesoporous structure were prepared by a one‐stage KOH activation process without the assistance of templates and further used as adsorbents for CO₂ capture. The physical and chemical properties as well as the pore structures of the resulting mesoporous carbons were characterized by N₂ adsorption isotherms, scanning electron microscopy (SEM ), X‐ray diffraction (XRD ), Raman spectroscopy, and Fourier transform infrared (FTIR ) spectroscopy. The activated carbon showed greater specific surface area and mesopore volume as the activation temperature was increased up to 600°C, showing a uniform pore structure, great surface area (up to ~815 m²/g), and high mesopore ratio (~55%). The activated sample exhibited competitive CO₂ adsorption capacities at 1 atm pressure, reaching 2.29 and 3.4 mmol/g at 25 and 0°C, respectively. This study highlights the potential of well‐designed mesoporous carbon as an adsorbent for CO₂ removal and widespread gas adsorption applications.     

Interaction of water‐soluble tetrakis‐(1‐methyl‐4‐pyridiniyl)‐porphyrin and CdS naonoparticles

The interaction between positively charged porphyrin TMPyP(4) (tetrakis‐(1‐methyl‐4‐pyridiniyl) porphyrin) and negatively charged surface of colloidal CdS nanoparticles has been studied by absorption spectrum, fluorescence spectroscopy, and time‐correlated single‐photon‐counting methods. Addition of CdS colloid to a TMPyP(4) solution leads to TMPyP(4) adsorption onto the surface of CdS colloid with an apparent association constant of 4643 L/mol. This adsorption results in distinct changes in absorption spectrum of TMPyP (4) and the quenching of its′ fluorescence, but the biexponential fluorescence decay changes hardly. Nearly 90% of the fluorescence of 5 × 10^?6 mol/L TMPyP(4) can be quenched with 1.5 × 10^?4 mol/L CdS colloid. These spectral changes are attributed to the formation of a certain form complex TMPyP(4)‐CdS.     

Synthesis of High‐Surface‐Area Nitrogen‐Doped Porous Carbon Microflowers and Their Efficient Carbon Dioxide Capture Performance

Sustainable carbon materials have received particular attention in CO₂ capture and storage owing to their abundant pore structures and controllable pore parameters. Here, we report high‐surface‐area hierarchically porous N‐doped carbon microflowers, which were assembled from porous nanosheets by a three‐step route: soft‐template‐assisted self‐assembly, thermal decomposition, and KOH activation. The hydrazine hydrate used in our experiment serves as not only a nitrogen source, but also a structure‐directing agent. The activation process was carried out under low (KOH/carbon=2), mild (KOH/carbon=4) and severe (KOH/carbon=6) activation conditions. The mild activated N‐doped carbon microflowers (A‐NCF‐4) have a hierarchically porous structure, high specific surface area (2309 m² g^?1), desirable micropore size below 1 nm, and importantly large micropore volume (0.95 cm³ g^?1). The remarkably high CO₂ adsorption capacities of 6.52 and 19.32 mmol g^?1 were achieved with this sample at 0 °C (273 K) and two pressures, 1 bar and 20 bar, respectively. Furthermore, this sample also exhibits excellent stability during cyclic operations and good separation selectivity for CO₂ over N₂.     

Infrared Spectroscopic Studies on the Surface Chemistry of High‐Surface‐Area Gallia Polymorphs

Polymorphs α, β, and γ of Ga₂O₃ having hexagonal (corundum‐type), monoclinic and cubic (spinel‐type) structure, respectively, were prepared in a high‐surface‐area form, and characterized by powder X‐ray diffraction. Nitrogen adsorption at 77 K showed these gallia samples to have specific surface areas of 77 (α‐Ga₂O₃), 40 (β‐Ga₂O₃) and 120 m² g^?1 (γ‐Ga₂O₃). Fourier transform infrared spectroscopy of adsorbed carbon monoxide (at 77 K) and pyridine (at room temperature) showed that the three gallia polymorphs have a very similar surface Lewis acidity, regardless of their different crystal structures. This Lewis acidity was assigned, mainly, to coordinatively unsaturated tetrahedral Ga³⁺ ions situated on the surface of the small crystallites which constitute the different metal oxide varieties. Ga³⁺···CO adducts formed after CO adsorption gave (in all cases) a characteristic C–O stretching band at 2195–2200 cm^?1, while Lewis‐type adducts formed with adsorbed pyridine were characterized by IR absorption bands at 1610–1612 and 1446–1450 cm^?1. The three (partially hydroxylated) gallia polymorphs showed also a very weak Brønsted acidity, which they manifested by forming hydrogen‐bonded adducts with both CO and pyridine; however no protonation of adsorbed pyridine occurred.     

Carbon‐Dot‐Sensitized,Nitrogen‐Doped TiO2 in Mesoporous Silica for Water Decontamination through Nonhydrophobic Enrichment–Degradation Mode

Mesoporous silica synthesized from the cocondensation of tetraethoxysilane and silylated carbon dots containing an amide group has been adopted as the carrier for the in situ growth of TiO₂ through an impregnation–hydrothermal crystallization process. Benefitting from initial complexation between the titania precursor and carbon dot, highly dispersed anatase TiO₂ nanoparticles can be formed inside the mesoporous channel. The hybrid material possesses an ordered hexagonal mesostructure with p6mm symmetry, a high specific surface area (446.27 m² g^?1), large pore volume (0.57 cm³ g^?1), uniform pore size (5.11 nm), and a wide absorption band between λ=300 and 550 nm. TiO₂ nanocrystals are anchored to the carbon dot through Ti?O?N and Ti?O?C bonds, as revealed by X‐ray photoelectron spectroscopy. Moreover, the nitrogen doping of TiO₂ is also verified by the formation of the Ti?N bond. This composite shows excellent adsorption capabilities for 2,4‐dichlorophenol and acid orange 7, with an electron‐deficient aromatic ring, through electron donor–acceptor interactions between the carbon dot and organic compounds instead of the hydrophobic effect, as analyzed by the contact angle analysis. The composite can be photocatalytically recycled through visible‐light irradiation after adsorption. The narrowed band gap, as a result of nitrogen doping, and the photosensitization effect of carbon dots are revealed to be coresponsible for the visible‐light activity of TiO₂. The adsorption capacity does not suffer any clear losses after being recycled three times.     

Large‐Scale Synthesis of MOF‐Derived Superporous Carbon Aerogels with Extraordinary Adsorption Capacity for Organic Solvents

Carbon aerogels (CAs) with 3D interconnected networks hold promise for application in areas such as pollutant treatment, energy storage, and electrocatalysis. In spite of this, it remains challenging to synthesize high‐performance CAs on a large scale in a simple and sustainable manner. We report an eco‐friendly method for the scalable synthesis of ultralight and superporous CAs by using cheap and widely available agarose (AG) biomass as the carbon precursor. Zeolitic imidazolate framework‐8 (ZIF‐8) with high porosity is introduced into the AG aerogels to increase the specific surface area and enable heteroatom doping. After pyrolysis under inert atmosphere, the ZIF‐8/AG‐derived nitrogen‐doped CAs show a highly interconnected porous mazelike structure with a low density of 24 mg cm^?3, a high specific surface area of 516 m² g^?1, and a large pore volume of 0.58 cm^?3 g^?1. The resulting CAs exhibit significant potential for application in the adsorption of organic pollutants.     

Effective removal of 2,4,6‐trinitrophenol over hexagonal metal–organic framework NH2‐MIL‐88B(Fe)

A nanostructured organic–inorganic framework, hexagonal NH₂‐MIL‐88B, has been prepared through a facile one‐pot reflux reaction and then it was characterized using various techniques. The as‐prepared sample with high specific surface area (414 m² g^?1) showed excellent adsorption for 2,4,6‐trinitrophenol (TNP) in the liquid phase. Detailed studies of the adsorption kinetics, adsorption mechanism, adsorption isotherm, activation energy and various thermodynamic parameters were conducted. The adsorption mechanism of NH₂‐MIL‐88B for TNP may be ascribed to hydrogen bond interaction, and the complexation between ─OH in TNP and unsaturated Fe(III) on the surface of NH₂‐MIL‐88B. The maximum adsorption capacity of NH₂‐MIL‐88B for TNP based on the Langmuir isotherm was 163.66 mg g^?1. The as‐prepared NH₂‐MIL‐88B adsorbent seems to be a promising material in practice for TNP removal from aqueous solution.     

氧化硅-石墨烯气凝胶介孔复合材料的合成及其对苯的吸附性能

采用水热法快速合成了一种新型介孔氧化硅-石墨烯气凝胶复合吸附材料(MSGA)。通过X射线衍射、扫描电镜等方法对MSGA进行表征。结果表明,经过水热反应和冻干处理后的MSGA材料的介孔结构保持完好,介孔氧化硅在MSGA中的分散具有高度均一性。当介孔氧化硅的含量达到88.2(wt)%时,MSGA的比表面积可达395.5m~2/g。MSGA材料对苯蒸汽的常温常压吸附量为10.77mL/g,是石墨烯气凝胶的13倍,吸附穿透时间达到石墨烯气凝胶的34.4倍。在0.8%的环境湿度下,由于材料表面羟基的亲和性,进一步提升了对苯的吸附。得益于超低密度和丰富的内部孔隙结构,MSGA能够适应高达500mL/min的气流量。上述结果表明,该复合材料在VOCs消除领域具有广阔的应用前景。     

Polymerization under Hypersaline Conditions: A Robust Route to Phenolic Polymer‐Derived Carbon Aerogels

Polymer‐derived carbon aerogels can be obtained by direct polymerization of monomers under hypersaline conditions using inorganic salts. This allows for significantly increased mechanical robustness and avoiding special drying processes. This concept was realized by conducting the polymerization of phenol–formaldehyde (PF) in the presence of ZnCl₂ salt. Afterwards, the simultaneous carbonization and foaming process conveniently converts the PF monolith into a foam‐like carbon aerogel. ZnCl₂ plays a key role, serving as dehydration agent, foaming agent, and porogen. The carbon aerogels thus obtained are of very low density (25 mg cm^?3), high specific surface area (1340 m² g^?1), and have a large micro‐ and mesopore volume (0.75 cm³ g^?1). The carbon aerogels show very promising potential in the separation/extraction of organic pollutants and for energy storage.     

Water‐Stable Zirconium‐Based Metal–Organic Framework Material with High‐Surface Area and Gas‐Storage Capacities

We designed, synthesized, and characterized a new Zr‐based metal–organic framework material, NU‐1100 , with a pore volume of 1.53 ccg^?1 and Brunauer–Emmett–Teller (BET) surface area of 4020 m²g^?1; to our knowledge, currently the highest published for Zr‐based MOFs. CH₄/CO₂/H₂ adsorption isotherms were obtained over a broad range of pressures and temperatures and are in excellent agreement with the computational predictions. The total hydrogen adsorption at 65 bar and 77 K is 0.092 g g^?1, which corresponds to 43 g L^?1. The volumetric and gravimetric methane‐storage capacities at 65 bar and 298 K are approximately 180 v_STP/v and 0.27 g g^?1, respectively.     

Porphyrin‐based covalent triazine frameworks: Porosity,adsorption performance,and drug delivery

Two porous porphyrin‐based covalent triazine frameworks (PCTFs), in which porphyrin is incorporated as building block, have been synthesized by the Friedel–Crafts reaction. The copolymer PCTFs show large Brunauer–Emmett–Teller specific surface area of up to 1089 m² g^?1, high CO₂ uptake capacity reaching 139.9 mg g^?1 at 273 K/1.0 bar, and good selectivity for CO₂/CH₄ adsorption attaining 6.1 at 273 K/1.0 bar. The resulting porous solids also can be used as matrices for drug delivery of ibuprofen in vitro. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 2594–2600     

Copper nanoparticles incorporated on a mesoporous carbon nitride,an excellent catalyst in the Huisgen 1,3‐dipolar cycloaddition and N‐arylation of N‐heterocycles

Cu nanoparticles with average particles size around 10 nm were incorporated on the surface of a mesoporous carbon nitride support. The XRD and N₂ adsorption isotherms show that it maintains a hexagonal mesoporous structure with a high surface area (600.03 m² g^?1). The embedded Cu nanoparticles exhibit extremely high catalytic performance in two different kinds of organic reactions. The Huisgen 1,3‐dipolar cycloaddition and N‐arylation of N‐heterocycles were all accomplished.     

Thiophene-based conjugated microporous polymers: synthesis,characterization and efficient gas storage

A series of thiophene-based conjugated microporous polymers(ThPOPs) have been synthesized on the basis of ferric chloride-catalyzed oxidative coupling polymerization of multi-thienyl monomers. The structures of ThPOPs were confirmed via solid-state 13 C CP/MAS NMR spectroscopy and Fourier-transform infrared spectroscopy. The ThPOPs possess high porosities and their high Brunauer-Emmett-Teller specific surface area results vary between 350 and 1320 m~2 g~(-1). The presence of abundant ultra-micropores at 0.50–0.63 nm allows ThPOPs efficient gas(carbon dioxide, methane, and hydrogen) adsorption.     

Synthesis of Ti‐MCM‐41 directly from silatrane and titanium glycolate and its catalytic activity1

Titanium is successfully incorporated in hexagonal mesoporous silica to form Ti‐MCM41 at low temperature. Silatrane and titanium glycolate synthesized from the oxide one‐pot synthesis process are used as the precursors. Using the cationic surfactant cetyltrimethylammonium bromide as a template, the resulting meso‐structure mimics the liquid‐crystal phase. The percentage of titanium loading is varied in the range 1–35%. The temperatures used in the preparation are 60 °C and 80 °C. After heat treatment, very high surface area mesoporous silica was obtained and characterized using diffuse reflectance UV (DRUV) spectroscopy, X‐ray diffraction (XRD), BET surface area, X‐ray fluorescence, energy dispersive spectroscopy and transmission electron microscopy (TEM). At 35% titanium, the titanium atom is also in the framework showing the pattern of hexagonal mesostructure, as shown by DRUV, XRD and TEM results. The surface area is extraordinarily high, up to more than 2300 m² g^?1, and the pore volume is as high as 1.3 cm³ g^?1 for a titanium loading range of 1–5%. Oxidative bromination reaction using Ti‐MCM‐41 as catalyst showed impressive results, with the 60 °C catalysts having higher activity. Copyright © 2005 John Wiley & Sons, Ltd.