Structural, thermal and morphological properties of aqueous hybrid emulsion of silylated poly (urethane)/organic modified montmorillonite nanocomposites based on a new silicone and imide ring containing vinylic macromonomer

A new silicone and imide ring containing vinylic macromonomer, N-trimethylsiloxyethyltrimellitilimidomethacrylate (TMSETMIM), has been synthesized for the formulation of waterborne polyurethane (PU). A vinyl group containing silicone, the (3-methacryloyloxypropyl) trimethoxysilane (MPTMS) was used for comparison of the effects of silicone type with TMSETMIM on the PU. Then, a series of new siliconized PU hybrid nanocomposites, were successfully synthesized by the emulsion polymerization in the presence of organic modified montmorillonite (OMMT) and an aqueous PU dispersion using ammonium peroxodisulfate (APS) as an initiator. The PU dispersion was synthesized by a polyaddition reaction of hexamethylene diisocyanate (HMDI), on polypropylene glycol (PPG-1000) and dimethylol propionic acid (DMPA) as a chain extender. The obtained NCO chain ends reacted with water (which acts as a further chain extender producing some urea bonds). The structural elucidation of monomer was carried out by FTIR, ¹H-NMR, and ¹³C-NMR spectroscopic techniques. The copolymers were also characterized by using FTIR. Thermal properties of the copolymers were studied by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The morphologies of the copolymers were characterized with scanning electron microscopy (SEM) and transition electron microscopy (TEM) and then the effects of silicone concentrations on the water absorption ratio was examined. The formed film from the hybrid emulsion containing TMSETMIM could provide obviously higher water-resistance property in comparison with MPTMS. Also, the heat stability increases while the T _g decreased.     

Mucin coating on polymeric material surfaces to suppress bacterial adhesion

Mucin, a group of large glycoproteins, constitutes one of the major components of mucous which covers the lumenal surfaces of epithelial organs and serves as a physical barrier between the extracellular milieu and the plasma membrane. The molecules have a generic structure consisting of a thread-like peptide backbone with densely packed carbohydrate side chains. Protein and carbohydrate contents are about 30 and 50%, respectively. On hydrophobic materials in aqueous environments the naked parts of mucin’s protein backbone will adhere due to their hydrophobicity, while the carbohydrate side chains are thought to orient themselves away from the surface. This gives the mucin molecules their unique properties as surfactants, i.e. they tend to adsorb to hydrophobic surfaces via protein-surface interactions while they hold water molecules via their hydrophilic oligosaccharide clusters. In the present work, bovine submaxillary gland mucin (BSM) is purified by SEC and subsequently characterized with PAGE. Four polymeric materials, PMMA, silicone, Tecoflex® polyurethane and polystyrene, are selected as coating targets. Contact angle measurements show significant changes in these materials after coating with BSM. Surface concentrations of adsorbed BSM are determined by amino acid analysis and found to correlate well with observed reductions in contact angle. Both Staphylococcus aureus and CNS S. epidermidis are used to contaminate uncoated and BSM coated surfaces of all four materials, demonstrating a correlation between suppression of bacterial adhesion and surface concentration of BSM. Thus, bacterial counts on the coated PMMA, PS, PU and silicone specimens amount to ≈3, 10, 8 and 30% of the counts found on their uncoated counterparts. These results suggest that mucin coatings could profitably be employed to reduce the risk of microbial infections on polymeric biomaterials.     

Analysis of organosilicone copolymers by gradient polymer elution chromatography with evaporative light scattering detection

Organosilicone copolymers have found numerous applications in the cosmetics, detergent and coating industries. Coupling a polar polymer (like polyglycols) to a non-polar silicone gives anchorage and emulsification capabilities to the polymer. When coupling a silicone polymer to a polyglycol, the copolymer formed differs from the starting polymers by a single bond which is often difficult to evidence using spectroscopic techniques such as NMR or infrared, especially when the polymers have a high molecular mass. Gradient polymer elution chromatography (GPEC) coupled to an evaporative light scattering detector was developed for the characterization of copolymers based on their chemical composition distribution. Different block and graft polyglycol-silicone copolymers were successfully characterized by GPEC and residual homopolymers have been easily quantified.     

分子印迹固相萃取-液相色谱质谱联用对4种磺酰脲类除草剂残留的测定

采用苄嘧磺隆分子印迹固相萃取柱(MISPE)对加标大米中的苄嘧磺隆、甲磺隆、苯磺隆和烟嘧磺隆4种磺酰脲类除草剂进行净化和富集预处理,并采用LC-MS方法进行定量分析.质谱条件为:正离子检测模式(M+H),检测质量范围为m/z 200 ～800 ,毛细管电压3.93 kV,锥孔电压20 V,脱溶剂温度250 ℃,辅助气流速4 L/min.4种磺酰脲类除草剂在0.01 ～0.70 mg·L~(-1)范围内线性良好.回收率为68% ～100%,表明样品液中的烟嘧磺隆、甲磺隆、苯磺隆和苄嘧磺隆能直接被分子印迹固相萃取柱中的印迹位点保留,而杂质几乎不被保留.分子印迹固相萃取柱对磺酰脲类除草剂表现出良好的识别性能.     

Chitosan-graft-poly(ϵ-caprolactone)s: An optimized chemical approach leading to a controllable structure and enhanced properties

A novel synthetic approach was developed for the controllable modification of chitosan (CS) with poly(ϵ-caprolactone) (PCL). 6-O-Triphenylmethyl-chitosan (TMCS) was synthesized as a highly soluble intermediate in organic solvents to facilitate an efficient grafting reaction of PCL onto CS in a homogeneous reaction medium. Subsequently, the syntheses of CS-g-PCL copolymers with different degrees of substitution (ds) and various chain lengths of PCL (number-average molecular weight = 1200–11,000) were carried out by a coupling reaction between the carboxylic terminal groups of PCL chains and the amino groups of TMCS. The successful grafting reaction was confirmed by GPC measurements, which indicated that the products were graft copolymers rather than physical blends. The ds, defined as the number of PCL chains per saccharide unit, of the graft copolymers could be adjusted simply by changes in the molar feed ratios of PCL to CS, and graft copolymers with different ds values ranging from 0.28 to 0.49 were synthesized, as calculated by ¹H NMR and elemental analysis. DSC and X-ray measurements showed that the melting temperature and enthalpy of the PCL grafts of these graft copolymers could be adjusted by the ds and the chains length of PCL, respectively. Meanwhile, the CS-g-PCL copolymers exhibited better solubility in various solvents, such as in chloroform for some of the resultant graft copolymers, than the original CS. Finally, nanoparticles of 100–200 nm, having hydrophobic PCL domains and cationic hydrophilic surfaces, were obtained through the self-assembly of the copolymers in selective solvents. These types of graft copolymers have great potential in various applications, such as targeted drug and gene delivery as well as tissue engineering. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2556–2568, 2007     

Investigation of lectinized liposomes as M-cell targeted carrier-adjuvant for mucosal immunization

In the present investigation hepatitis B surface antigen (HBsAg) encapsulated liposomes were developed and coupled with Ulex europaeus agglutinin 1 (UEA-1) to increase transmucosal uptake by M-cells of the Peyer's patches. The liposomes were characterized for shape, size, polydispersity and encapsulation efficiency. Bovine submaxillary mucin (BSM) was used as a biological model for the in vitro determination of lectin activity and specificity. Dual staining technique was used to investigate targeting of lectinized liposomes to the M-cells. Anti-HBsAg IgG response in serum and anti-HBsAg sIgA level in various mucosal fluids was estimated by using ELISA, following oral immunization with lectinized and non-lectinized liposomes in Balb/c mice. Additionally, interleukin-2 (IL-2) and interferon-γ (IFN-γ) level in the spleen homogenates was determined. The results suggest that lectinized liposomes were successfully developed, exhibited increased activity with BSM as compared to non-lectinized liposomes and α-l-fucose specificity of the lectinized liposomes was also maintained. The lectinized liposomes were predominantly targeted to the M-cells. The serum anti-HBsAg IgG titre obtained after 3 consecutive days oral immunizations with HBsAg encapsulated lectinized liposomes and boosting after third week was comparable with the titre recorded after single intramuscular prime and third week boosting with alum-HBsAg. Moreover, lectinized liposomes induced higher sIgA level in mucosal secretions and cytokines level in the spleen homogenates. The results showed that the developed surface modified liposomes could be a potential module for the development of effective mucosal vaccines.     

Block copolymers derived from azobiscyanopentanoic acid. X. Synthesis of silicone–vinyl block copolymers via polysiloxane(azobiscyanopentanamide)s

The synthesis of silicone–vinyl block copolymers has been studied by the use of poly(azo-containing siloxaneamide)s (abbreviated as PASAs), i.e., polysiloxane (azobiscyanopentanamide)s as macroazoinitiators. PASAs with number-average molecular weight of 12000–31000 and with siloxane chain lengths of 250–9800 were prepared by the condensation of azobiscyanopentanoyl chloride and α,ω-bis(3-aminopropyldimethyl)polysiloxanes in equimolar feeds. Several kinds of silicone–vinyl block copolymers were synthesized by radical polymerization of vinyl monomers such as methyl methacrylate, styrene, and vinyl acetate, in the presence of PASA in homogeneous media. The block copolymers with siloxane contents up to 30 mol % were then characterized on the basis of infrared absorption, proton NMR spectra, and gel permeation chromatography.     

Homogeneous time-resolved fluoroimmunoassay of bensulfuron-methyl by using terbium fluorescence energy transfer

A sensitive homogenous time-resolved fluoroimmunoassay (TR-FIA) method for bensulfuron-methyl (BSM) based on fluorescence resonance energy transfer (FRET) from a Tb(3+) fluorescent chelate with N,N,N('),N(')-[2,6-bis(3'-aminomethyl-1'-pyrazoly)-4-phenylpyridine] tetrakis(acetic acid) (BPTA-Tb(3+)) to organic dye, Cy3 or Cy3.5 has been developed. New method combined the use of BPTA-Tb(3+) labeled streptavidin, Cy3 or Cy3.5 labeled anti-BSM monoclonal antibody and biotinylated BSM-BSA conjugate (BSA is bovine serum albumin) for competitive-type immunoassay. After BPTA-Tb(3+) labeled streptavidin was reacted with a competitive immune reaction solution containing biotinylated BSM-BSA, BSM sample and Cy3 or Cy3.5 labeled anti-BSM monoclonal antibody, the sensitized and long-lived emission of Cy3 or Cy3.5 derived from FRET was measured, and thus the concentration of BSM in sample was calculated. The present method has the advantages of rapidity, simplicity and high sensitivity since the B/F (bound reagent/free reagent) separation steps and the solid-phase carrier are not necessary. The method gives the detection limit of 2.10 ngml(-1). The coefficient variations of the method are less than 1.5% and the recoveries are in the range of 95-105% for BSM water sample measurement.     

原子转移自由基聚合及可控自由基聚合

以作者在原子转移自由基聚合领域的研究成果为主导,结合国内外文献,对近年来出现的颇具影响的可控自由基聚合体系与进行了评述与展望。     

A polarity‐activation strategy for the high incorporation of 1‐alkenes into functional copolymers via RAFT copolymerization

A new synthetic methodology for the preparation of copolymers having high incorporation of 1‐alkene together with multifunctionalities has been developed by polarity‐activated reversible addition‐fragmentation chain transfer (RAFT) copolymerization. This approach provides well‐defined alternating poly(1‐decene‐alt‐maleic anhydride), expanding the monomer types for living copolymerizations. Although neither 1‐decene (DE) nor maleic anhydride (MAn) has significant reactivity in RAFT homopolymerization, their copolymers have been synthesized by RAFT copolymerizations. The controlled characteristics of DE‐MAn copolymerizations were verified by increased copolymer molecular weights during the copolymerization process. Ternary copolymers of DE and MAn, with high conversion of DE, could be obtained by using additive amounts (5 mol %) of vinyl acetate or styrene (ST), demonstrating further enhanced monomer reactivities and complex chain structures. When ST was selected as the third monomer, copolymers with block structures were obtained, because of fast consumption of ST in the copolymerization. Moreover, a wide variety of well‐defined multifunctional copolymers were prepared by RAFT copolymerizations of various functional 1‐alkenes with MAn. For each copolymerization, gel permeation chromatography analysis showed that the resulting copolymer had well‐controlled M_n values and fairly low polydispersities (PDI = 1.3–1.4), and ¹H and ¹³C NMR spectroscopies indicated strong alternating tendency during copolymerization with high incorporation of 1‐alkene units, up to 50 mol %. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3488–3498, 2008     

Investigation of ethylene-vinyl alcohol copolymers for surface modification of contact lenses

Ethylene-vinyl alcohol copolymers from 0 to 57 mol % of vinyl alcohol were investigated for potential contact lens surface modification. Films of the ethylene-vinyl alcohol copolymers made by solution casting, showed that the copolymers with a high percentage of vinyl alcohol groups possessed excellent surface properties such as good wettability, low protein (albumin) and lipid adsorption, and no conformational change of the adsorbed protein. Utilizing the Langmuir-Blodgett dipping technique, an ultrathin layer of ethylene-vinyl alcohol copolymer was deposited on a silicone rubber substrate. This initial results confirm that wettability was improved and the amount of protein adsorbed was reduced significantly after only one deposition trip.     

Synthesis of silicone–acrylate copolymer latexes and their film properties

Emulsion copolymerization of silicones (octomethyl tetracyclosiloxane, D₄ and methacryloxypropyl trimethoxy silane, MATS) and acrylics was carried out using three different polymerization processes: semicontinuous monomer emulsion addition, batch and initiator solution addition. Results showed that only the semicontinuous process led to a stable latex with monodisperse particles. Various polymerizations were carried out through this process with varying silicone/acrylic ratios and MATS content. Films were obtained from different latexes: their properties are significantly influenced by silicone and MATS contents in copolymers.     

Synthesis of 2-phenoxy-2-phenylethyl acrylate and copolymerization with 2-phenylethyl acrylate: Estimation of monomer reactivity ratios,thermal and optical properties

A new aromatic based monomer 2-phenoxy-2-phenylethyl acrylate (PPEA) was synthesized. Copolymers of PPEA with 2-phenylethyl acrylate (PEA) were prepared by free radical polymerization. The reactivity ratios were estimated using various graphical methods. Structural parameters of the copolymers were obtained by calculating the dyad monomer sequence fractions and the mean sequence length. Optical properties of polymers such as refractive indices and UV-Visible absorption were investigated. The glass transition temperature and thermal degradation behavior of the copolymers were studied. Combined with the RI, transparency and thermal properties, prepared copolymers hold great promise as materials for intraocular lens applications.     

Light‐emitting copolymers based on fluorene and selenophene—Comparative studies with its sulfur analogue: Poly(fluorene‐co‐thiophene)

A series of soluble conjugated copolymers derived from 9,9‐dioctylfluorene (FO) and selenophene (SeH) was synthesized by a palladium‐catalyzed Suzuki coupling reaction with various feed ratios of SeH to FO less than or equal to 50%. The efficient energy transfer from fluorene segments to narrow band‐gap selenophene sites was observed. In comparison with the very well studied copolymer poly(fluorene‐co‐thiophene), poly(9,9‐dioctylfluorene‐co‐selenophene) (PFO‐SeH) shows redshifted photoluminescence (PL) and electroluminescence (EL) emission. PL spectra of the PFO‐SeH copolymers show a significant redshift along with increasing selenophene content in the copolymers and also with increasing polymer concentration in solution. PL quantum efficiency of the selenophene‐containing PFO copolymer is much lower than that of corresponding PFO‐thiophene (Th) copolymers. All these features of PFO‐SeH copolymers can be explained by the difference in aromaticity of selenophene and thiophene heterocycles and the heavy atom effect of Se in comparison with S‐atoms. The device fabricated with PFO‐SeH15 as the emissive layer exhibited high external quantum efficiency (0.51%) at a luminance of 1570 cd/m². Device performance is limited by electron injection and the strong quenching effect of Se atoms. Devices with PFO‐SeH copolymers blended into PFO homopolymers show significant improvement in device performance. External quantum efficiency as high as 1.7% can be obtained for PFO‐SeH30/PFO blend devices. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 823–836, 2005     

Mn2+ alters peroxidase profiles and lignin degradation by the white-rot fungus Pleurotus ostreatus under different nutritional and growth conditions

The white-rot fungus Pleurotus ostreatus produces two types of extracellular peroxidases: manganese-dependent peroxidase (MnP) and versatile peroxidase (VP). The effect of Mn²⁺ on fungal growth, peroxidase activity profiles, and lignin degradation by P. ostreatus was studied in liquid culture and under solid-state fermentation conditions on perlite, the latter resembling the natural growth conditions of this fungus. The fungus was grown in either a defined asparagine-containing basidiomycete selective medium (BSM) or in a rich peptone medium (PM). Biomass production, as determined by respiration experiments in solid-state fermentation and liquid cultures and fungal growth on Petri dishes, was higher in the PM than in the BSM. Mn²⁺ affected biomass production only in the PM on Petri dishes. In the nonamended PM, high levels of MnP and VP activity were detected relative to the nonamended BSM. Nevertheless, a higher rate of ¹⁴C-lignin mineralization was measured in the Mn²⁺-amended BSM, as determined during the course of 47 d of fermentation. Mn²⁺ amendment of the PM increased mineralization rate to that obtained in the Mn²⁺-amended BSM. The enzyme activity profiles of MnP and VP were studied in the BSM using anion-exchange chromatography. In the nonamended BSM, only minute levels of MnP and VP were detected. On Mn²⁺ amendment, two MnP isoenzymes (B1 and B2) appeared. Isoenzyme B2 was purified and showed 100% identity with the MnP isoenzyme purified in our previous study from PM-solid-state fermentation (P6). P6 was found to be the dominant isoenzyme in terms of activity level and gene expression compared with the VP isoenzymes. Based on these results, we concluded that Mn²⁺ plays a key role in lignin degradation under different nutritional and growth conditions, since it is required for the production of MnP in P. ostreatus.     

Combining atom‐transfer radical polymerization and ring‐opening polymerization through bifunctional initiators derived from hydroxy benzyl alcohol—Preparation and characterization of initiators,macroinitiators, and block copolymers

A simple, one‐step procedure has been developed for the preparation of bifunctional initiators capable of polymerizing monomers suitable for atom‐transfer radical polymerization (ATRP) and ring‐opening polymerization (ROP). These bifunctional initiators were employed for making narrow disperse poly(styrene) macroinitiators, which were subsequently used for the ROP of various lactides to yield poly(styrene‐block‐lactide) copolymers. Thermogravimetric analysis (TGA) of these block copolymers are interesting in that it shows a two‐step degradation curve with the first step corresponding to the degradation of poly(lactide) segment and the second step associated with the poly(styrene) segment of the block copolymer. This nature of the block copolymer makes it possible to estimate the block copolymer content by TGA in addition to the ¹H NMR spectroscopic analysis. Thus, this study for the first time highlights the possibility of making porous materials by thermal means which are otherwise obtained by base hydrolysis. The bifunctional initiators were prepared by the esterification of 3‐hydroxy, 4‐hydroxy, and 3,5‐dihydroxy benzyl alcohols with α‐bromoisobutyryl bromide and 2‐bromobutyryl bromide. A mixture of products was obtained, which were purified by column chromatography. The esterified benzyl alcohols were employed in the polymerization of styrene under copper (Cu)‐catalyzed ATRP conditions to yield macroinitiators with low polydispersity. These macroinitiators were subsequently used in the ROP of L ‐, DL ‐, and mixture of lactides. The formation of block copolymers was confirmed by gel permeation chromatography (GPC), spectroscopic and thermal characterizations. The molecular weight of the block copolymers was always higher than the macroinitiator, and the GPC chromatogram was symmetrical indicating the uniform initiation of ROP by the macroinitiators. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 102–116, 2008     

Influence of chain microstructure on the hydrolytic degradation of copolymers from 1,3‐trimethylene carbonate and L‐lactide

Ring‐opening copolymerization of L ‐lactide (LLA) and 1,3‐trimethylene carbonate (TMC) blends with LLA/TMC feed ratios from 90/10 to 50/50 was realized at 110 or at 180 °C for various time periods, using low toxic zirconium (IV) acetylacetonate (Zr(Acac)₄) as initiator. The resulting copolymers exhibit different chain microstructures. Copolymers obtained at 110 °C exhibit a gradient chain structure with the presence of lactidyl sequences next to very short ones, and are semicrystalline. In contrast, copolymers obtained at 180 °C are amorphous because of a more random chain microstructure with the presence of larger amounts of medium sequences. Degradation of the copolymers was carried out in pH 7.4 phosphate buffer at 37 °C. Analytical techniques such as ¹H NMR, DSC, GPC, and XRD were used to monitor the degradation. Initially amorphous copolymers can remain amorphous during degradation because of the highly random unit's distribution, and equivalent LLA and TMC contents. However, initially amorphous copolymers containing larger amounts of lactidyl units are able to crystallize during degradation because of the presence of relatively long LLA blocks. Insofar, as initially semicrystalline copolymers are concerned, degradation occurs preferentially in the amorphous zones. Therefore, various degradation behaviors and degradation rates can be obtained by varying the chemical composition, chain microstructure, and morphology of PLLA‐PTMC copolymers. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3869–3879, 2009     

Biodegradation behaviour of poly(lactic acid) and (lactic acid-ethylene glycol-malonic or succinic acid) copolymers under controlled composting conditions in a laboratory test system

(Lactic acid, ethylene glycol, malonic or succinic acid) copolymers [(LA-EG-MA) and (LA-EG-SA) copolymers] were synthesized with different monomer feed ratios by direct polycondensation. The copolymers were characterized in terms of various properties such as acid value and number average molecular weight. The aerobic biodegradation under controlled composting conditions of commercially available and laboratory synthesized poly(l-lactic acid) (PLA) and synthesized copolymers was carried out according to ISO 14855-1:2005. The biodegradability of tested materials was found to be strongly dependent on the lactic acid content, ranging from 94% (method A) and 104% (method B) to 43% (method A) and 46% (method B) over the 110-days of the 50 °C composting.     

Preparation and properties of Si-containing copolymer for near-UV resist. I. Poly(N-(4-hydroxyphenyl) maleimidealt-p-trimethylisilylstyrene)

A new negative near-UV photoresist consisting of poly(N-(4-hydroxyphenyl) maleimidealt-p-trimethylisilylstyrene) (PHMS) and a naphthoquinonediazide ester was developed. PHMS was synthesized by solution free-radical polymerization of the comonomers with azobisisobutyronitrile (AIBN) in 1,4-dioxane at 60°C. The preparation of PHMS in terms of reaction time, thermal initiator, and solvent was evaluated; and a series of different molecular weight copolymers were prepared. PHMS was 1: 1 in composition and was predominantly alternating. These copolymers dissolved in a wide range of solvents (including 5% tetramethylammonium hydroxide). The thermal properties of these copolymers were investigated by DSC and TGA. The chain-stiffening effect of the maleimide group played an important role in effecting high thermal resistance. Near-UV exposure was carried out using a Canon PLA-501F contact printer. High resolution negative images were obtained which had resistance to thermal deformation at 330°C and above. The developed patterns exhibited good adhesion to the silicon substrates without the use of an adhesion promoter. The lithographic applications of a bilayer photoresist system in which the prepared resist was used as the top imaging layer were examined. It is supposed that if PHMS was used as a binder for a diazonaphthoquions sulfonate (NDS) photochemically, positive images would be obtained; however, on the contrary, negative images were observed. It is proposed that photocrosslinking occurred in the PHMS main chain.     

Simultaneous determination of the styrene unit content and assessment of molecular weight of triblock copolymers in adhesives by a size exclusion chromatography method

The content of styrene units in nonhydrogenated and hydrogenated styrene‐butadiene‐styrene and styrene‐isoprene‐styrene triblock copolymers significantly influences product performance. A size exclusion chromatography method was developed to determine the average styrene content of triblock copolymers blended with tackifier in adhesives. A complete separation of the triblock copolymer from the other additives was realized with size exclusion chromatography. The peak area ratio of the UV and refraction index signals of the copolymers at the same effective elution volume was correlated to the average styrene unit content using nuclear magnetic resonance spectroscopy with commercial copolymers as standards. The obtained calibration curves showed good linearity for both the hydrogenated and nonhydrogenated styrene‐butadiene‐styrene and styrene‐isoprene‐styrene triblock copolymers (r  = 0.974 for styrene contents of 19.3–46.3% for nonhydrogenated ones and r  = 0.970 for the styrene contents of 23–58.2% for hydrogenated ones). For copolymer blends, the developed method provided more accurate average styrene unit contents than nuclear magnetic resonance spectroscopy provided. These results were validated using two known copolymer blends consisting of either styrene‐isoprene‐styrene or hydrogenated styrene‐butadiene‐styrene and a hydrocarbon tackifying resin as well as an unknown adhesive with styrene‐butadiene‐styrene and an aromatic tackifying resin. The methodology can be readily applied to styrene‐containing polymers in blends such as poly(acrylonitrile‐butadiene styrene).