Synthesis and magnetic properties of hard/soft SrFe12O19/Ni0.7Zn0.3Fe2O4 nanocomposite magnets

Magnetic nanocomposite SrFe₁₂O₁₉/Ni_0.7Zn_0.3Fe₂O₄ powders with different weight fractions of the Ni_0.7Zn_0.3Fe₂O₄ soft ferrite were synthesized by a combination of the sol–gel self-propagation and glyoxilate precursor methods. The results of magnetic measurements revealed the higher Mr/Ms ratio for the nanocomposites than that for the single phase SrFe₁₂O₁₉ which proves the existence of the intergrain exchange coupling between hard and soft magnetic phases with the exchange spring behavior. The highest Mr/Ms ratio of 0.63 was obtained in the composite consisting of 80 wt% of SrFe₁₂O₁₉ and 20 wt% Ni_0.7Zn_0.3Fe₂O₄. The microstructural studies of this sample exhibited the average dimensions of hard and soft phases about 20 nm and 15 nm, respectively which are small enough for strong exchange coupling according to the theoretical studies. The variations of the reduced remanence (Mr/Ms) with increasing the weight fraction of the soft phase could be also explained by the role of the exchange and dipolar interactions in tuning the magnetic properties of the nanocomposites.     

Structural and magnetic studies on spark plasma sintered SmCo5/Fe bulk nanocomposite magnets

SmCo₅+x wt% Fe (x=0$x=0$, 5 and 10) nanocomposite powders were synthesized by mechanical milling and were consolidated into bulk shape by spark plasma sintering (SPS) technique. The evolution of structure and magnetic properties were systematically investigated in milled powders as well as in SPS samples. A maximum coercivity of 8.9 kOe was achieved in spark plasma sintered SmCo₅+5 wt% Fe sample. The exchange spring interaction between the hard and soft magnetic phases was evaluated using δM–H measurements and the analysis revealed that the SPS sample containing 5 wt% Fe had a stronger exchange coupling between the magnetic phases than that of the sample with10 wt% Fe.     

The magnetization reversal behaviour for SmCo6.8Zr0.2 and SmCo6.8Zr0.2/α-（Fe,Co） nanocrystalline magnets at low temperature

This paper reports that the SmCo 6.8 Zr 0.2 nanocrystalline permanent magnets and SmCo 6.8 Zr 0.2 /α-(Fe,Co) nanocomposite permanent magnets are successfully produced by mechanical alloying and subsequently annealing at 700 C for 10 minutes.The x-ray diffraction results show that the phase structure of SmCo 6.8 Zr 0.2 nanocrystalline permanent magnets is composed of SmCo 7 phase and SmCo 6.8 Zr 0.2 /α-(Fe,Co) nanocomposite permanent magnets is composed of SmCo 7 and α-(Fe,Co) phases.The mechanism of magnetization reversal is mainly controlled by inhomogeneous domain wall pinning in SmCo 6.8 Zr 0.2 and SmCo 6.8 Zr 0.2 /α-(Fe,Co) magnets.The inter-grain exchange interaction at low temperature is investigated,which shows that the inter-grain exchange interaction of SmCo 6.8 Zr 0.2 /α-(Fe,Co) magnets increases greatly by the decrease of the measured temperature.According to Δm irr-H/H cj,Δm rev-H/H cj and χ irr-H/H cj curves at room temperature and 100 K,the changes of irreversible and reversible magnetization behaviours of SmCo 6.8 Zr 0.2 and SmCo 6.8 Zr 0.2 /α-(Fe,Co) magnets with the decreasing temperature are analysed in detail.The magnetic viscosity and the activation volume of SmCo 6.8 Zr 0.2 and SmCo 6.8 Zr 0.2 /α-(Fe,Co) magnets at different temperatures are also studied.     

晶粒易轴取向度对纳米晶永磁Pr2Fe14B磁性的影响

构造了立方和不规则形状晶粒的各向异性纳米晶单相Pr₂Fe₁₄B磁体 .利用微磁学的有限元法，模拟计算了样品的磁滞回线.计算结果表明，随着磁体晶粒易轴取向度的变差， 磁体的剩磁、矫顽力均随之下降.不同晶粒尺寸的纳米晶单相Pr₂Fe_{14B磁体，其磁 性能随取向度的变化快慢不同，原因在于磁体中的晶间交换作用 (IGEC) 的强弱不同.随着 晶粒取向度的提高，纳米晶单相磁体的矫顽力逐渐增加，这完全不同于烧结磁体. 关键词： 纳米晶磁体 矫顽力 剩磁}     

高性能纳米复合永磁材料的模拟计算研究

构造了在软磁相基体中析出规则形状硬磁相的各向同性和各向异性纳米复合永磁材料Pr2Fe14Bα-Fe.利用微磁学的有限元法，模拟计算了样品的磁滞回线.通过对剩磁、矫顽力和最大磁能积与软磁相厚度的关系分析，发现在软磁相厚度为0—12nm的范围内，复合磁体的矫顽力随软磁相厚度的增加而单调下降，而最大磁能积则是在适当的矫顽力和剩磁下达到最高.预计纳米复合Pr2(Fe,Co)14Bα-(Fe,Co)的各向同性磁体的最大磁能积最高可达248kJ/m3，而各向异性磁体则高达784kJ/m3. 关键词： 纳米复合永磁 矫顽力 剩磁 磁能积     

Magnetic anisotropy,exchange coupling and Dzyaloshinskii–Moriya interaction of two-dimensional magnets

The two-dimensional (2D) magnets provide novel opportunities for understanding magnetism and investigating spin related phenomena in several atomic thickness. Multiple features of 2D magnets, such as critical temperatures, magnetoelectric/magneto-optic responses, and spin configurations, depend on the basic magnetic terms that describe various spins interactions and cooperatively determine the spin Hamiltonian of studied systems. In this review, we present a comprehensive survey of three types of basic terms, including magnetic anisotropy that is intimately related with long-range magnetic order, exchange coupling that normally dominates the spin interactions, and Dzyaloshinskii−Moriya interaction (DMI) that favors the noncollinear spin configurations, from the theoretical aspect. We introduce not only the physical features and origin of these crucial terms in 2D magnets but also many correlated phenomena, which may lead to the advance of 2D spintronics.     

Correlation between microstructure and first-order magnetization reversal in the SmCo5/α-Fe nanocomposite magnets

SmCo₅/α-Fe nanocomposite magnets with different morphology have been fabricated by ball milling of the micrometer sized SmCo₅ and α-Fe powders. The α-Fe grains vary from elongated nano-strips to spherical nanoparticles with increasing milling time. The inter-phase exchange coupling is enhanced with increasing milling time due to reduced grain size. The first-order reversal curves (FORCs) are taken to identify optimal conditions for exchange coupling. It has been found that the stripped morphology results in weak inter-phase exchange coupling, while enhanced exchange coupling is observed with further reduction of the soft-phase grain size. Compared with the measurement of demagnetization curves, FORC analysis provides more information on the magnetostatic as well as the exchange interactions.     

Nd-Fe-B/FeCo多层纳米复合膜的结构和磁性

制备了Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀多层纳米复合磁性薄膜，对溅射态和650℃退火处理15 min试样的相成分分析和微结构的观察显示，溅射态薄膜呈非晶态，经650℃退火处理15 min后，薄膜主要相成分为硬磁性Nd₂Fe₁₄B相和软磁性相FeCo(110)相.Nd₂Fe₁₄B相呈柱状，其易磁化c轴垂直于膜面，尺寸约10 nm.在硬磁性相和软磁性相之间存在少量富Nd相和非晶态，富Nd相大小约7 nm.磁性测量和分析表明，1)该系列薄膜退火态具有垂直于膜面的磁晶各向异性.2)对于固定厚度(10 nm)层Nd-Fe-B和不同厚度(t_FeCo=1—100 nm)层FeCo多层纳米复合膜,剩磁随软磁相FeCo 厚度的增加快速增加，而矫顽力则减小.当t_FeCo=5 nm时，最大磁能积达到200 kJ/m³. 3)硬磁相Nd-Fe-B层和软磁相FeCo层之间交换耦合导致剩磁和磁能积增强. 关键词： Nd-Fe-B/FeCo多层纳米复合膜 交换耦合 磁各向异性     

纳米复合永磁材料的有效各向异性与矫顽力

研究了纳米Nd2Fe14B/α-Fe复合永磁材料中晶粒交换耦合相互作用对有效各向异性的影响和变化规律.结果表明：晶粒之间的交换耦合作用使材料的有效各向异性Keff随晶粒尺寸的减小而下降、随软磁性相成分的增加而降低. 当晶粒尺寸 减小到4nm时，Keff值减小为其各自通常各向异性常数值的1/3—1/4.有效各向异性的变化特点与矫顽力的变化规律基本相同.纳米复合永磁材料矫顽力的降低主要由于有效各向异性的减小而引起. 关键词： 纳米复合永磁材料 交换耦合相互作用 有效各向异性 矫顽力     

NdFeB纳米复合永磁材料的交换耦合相互作用和有效各向异性

以Nd₂Fe₁₄B/αFe为例，采用立方体晶粒结构模型，研究了纳米复合永磁材料中不同磁性晶粒间的交换耦合相互作用和有效各向异性.纳米复合永磁材料的有效各向异性Keff等于软、硬磁性相各向异性的统计平均值，每个晶粒的各向异性由晶粒表面交换耦合部分和晶粒内部未交换耦合部分的各向异性共同确定.计算结果表明，软、硬磁性相晶粒尺寸分布显著地影响有效各向异性Keff的值.当软、硬磁性晶粒尺寸D相同时，Keff随晶粒尺寸和硬磁性相体积分数的降低而减小, 当D<20nm 时，K 关键词： 纳米复合永磁材料 交换耦合相互作用 有效各向异性 晶粒尺寸     

相分布和晶粒尺寸对Nd2Fe14B/ɑ-Fe纳米复合永磁材料矫顽力的影响

本文采用统计平均方法研究了软、硬磁性晶粒尺寸及相分布对Nd2Fe14B/α-Fe纳米复合永磁材料矫顽力的影响。计算结果表明：对于单相纳米硬磁材料，磁体矫顽力随着硬磁性晶粒尺寸的减小而降低；对于软、硬两磁性相组成的Nd2Fe14B/a-Fe纳米复合永磁材料，两相的随机分布将导致磁体矫顽力随硬磁性晶粒尺寸的减小呈现极大值。本文的计算结果还表明当硬磁性晶粒尺寸大于软磁性晶粒的最佳尺寸时(15nm)，具有多层膜结构的Nd2Fe14B/a-Fe纳米复合永磁材料将比两相随机分布时具有更大的矫顽力。     

Effects of spacer layers on magnetic properties and exchange couplings of Nd-Fe-B/Nd-Ce-Fe-B multilayer films

The influences of the spacer-layer Ta on the structures and magnetic properties of Nd Fe B/Nd Ce Fe B multilayer films are investigated via DC sputtering under an Ar pressure of 1.2 Pa. An obvious(00l) texture of the hard phase is observed in each of the films, which indicates that the main phase of the film does not significantly change with Ta spacer-layer thickness. As a result, both the remanence and the saturation magnetization of the magnet first increase and then decrease,and the maximum values of 4πM_r and H_(cj) are 10.4 k Gs(1 Gs = 10_(-4)T) and 15.0 kOe(1 Oe = 79.5775 A·m_(-1)) for the film with a 2-nm-thick Ta spacer-layer, respectively, where the crystalline structures are columnar shape particles. The measured relationship between irreversible portion D(H) =-?M_(irr)/2 M_r and H indicates that the nucleation field of the film decreases with spacer layer thickness increasing, owing to slightly disordered grains near the interface between different magnetic layers.     

Effect of microstructure on the coercivity of HDDR Nd-Fe-B permanent magnetic alloy

The effect of the grain boundary microstructure on the anisotropy and coercivity was investigated in an HDDR Nd-Fe-B permanent magnetic alloy. Considering the special microstructure of its magnetic powder grain, an anisotropic theoretical model influenced simultaneously by the structure defect at the grain boundary and the exchange coupling interaction was put forward. The variations of the structure defect factors based on the nucleation and pinning mechanism with 2r ₀/lex (where r ₀ and lex are the defect thickness and the length of exchange coupling, respectively) were calculated. The results show that the coercivity mechanism of an HDDR Nd-Fe-B permanent magnetic alloy is greatly related to its microstructure defect at the grain boundary. For a fixed lex, when 2r ₀/lex < 1.67, the coercivity is controlled by the pinning mechanism; when 2r ₀/lex > 1.67, it is determined by the nucleation mechanism. The coercivity reaches the maximum when 2r ₀/lex = 1.67. The calculation result is consistent well with the experimental result given by Morimoto et al. Supported by the National Natural Science Foundation of China (Grant No. 50671055)     

Pt插层对Co/FeMn界面的影响

采用磁控溅射的方法制备了Co/FeMn/Co多层膜,研究了Co（底部）/FeMn和FeMn/Co（顶部）界面插入Pt层后磁矩的变化情况．通过测量磁滞回线可知,Co（底部）/FeMn界面的Pt插层改变了体系的饱和磁化强度Ｍ_s,随着Co层厚度（t_Co）的增加Ｍ_s不断趋近于Co块体结构理论值1440 kA/m．这是因为Co（底部）/FeMn界面产生了净磁矩,而界面处的Pt插层可以减少这种净磁矩的产生．但是 关键词： 磁性多层膜 垂直磁各向异性 交换耦合     

Sm(CobalFe0.1Cu0.1Zr0.033)6.9高温永磁合金的矫顽力

对Sm(Co_balFe_0.1Cu_0.1Zr_0.033)_6.9合金, 经810℃等温时效后以0.5℃/min逐渐冷却, 在600℃-400℃温度区间淬火, 研究了不同淬火温度下的磁滞回线、磁畴和矫顽力温度系数β. 发现时效600℃淬火后磁滞回线出现台阶状, 说明畴壁中应存在两处钉扎. 随淬火温度的降低, 合金的室温矫顽力显著增加, 磁滞回线的台阶消失. 通过磁畴形貌发现时效600℃淬火后的磁畴接近条形畴, 1:5相中Cu分布相对均匀, 形成的畴壁钉扎较弱, 从而使磁滞回线出现台阶, 决定矫顽力的畴壁钉扎位于两相界面处; 随时效淬火温度的降低, 磁畴逐渐细化, 畴壁1:5相中的畴壁能降低, 形成了较强的内禀钉扎, 并决定材料的矫顽力, 两相界面处的畴壁钉扎被掩盖. 对不同温度淬火合金的高温矫顽力研究表明, 最强的畴壁钉扎位于两相界面处时, 矫顽力随温度升高逐渐增加, 矫顽力出现温度反常现象; 最强的畴壁钉扎位于1:5相中心时, 矫顽力随温度升高逐渐衰减. 当测试温度达到500℃后不同淬火温度样品的矫顽力几乎相同, 此时最强畴壁钉扎均在两相界面处.     

Ga30Sb70/Sb80Te20纳米复合多层薄膜的相变特性研究

采用磁控二靶(Ga₃₀Sb₇₀和Sb₈₀Te₂₀)交替溅射方法制备了新型Ga₃₀Sb₇₀/Sb₈₀Te₂₀纳米复合多层薄膜, 对多层薄膜周期中Ga₃₀Sb₇₀层厚度对相变特性的影响进行了研究. 结果表明, 多层薄膜的结晶温度可以通过周期中Ga₃₀Sb₇₀层厚度进行调节, 且随着Ga₃₀Sb₇₀层厚度的增加而升高. Ga₃₀Sb₇₀/Sb₈₀Te₂₀纳米复合多层薄膜的光学带隙随Ga₃₀Sb₇₀层厚度的增加而增大. 采用皮秒激光脉冲抽运光探测技术研究了多层薄膜的瞬态结晶动力学过程, 利用不同能量密度的皮秒激光脉冲可以实现Ga₃₀Sb₇₀/Sb₈₀Te₂₀多层薄膜非晶态和晶态的可逆转变.     

纳米晶永磁材料晶间交换耦合作用的模拟计算研究

利用微磁学有限元法，模拟计算了单相和复相各向同性纳米晶磁体的起始磁化曲线、退磁曲线和回复曲线.验证了用δm(H)曲线的正峰值来衡量纳米晶磁体晶间交换耦合作用的有效性.计算 结果表明，纳米晶单相和复相磁体的晶间交换耦合作用都随晶粒尺寸的增加而降低，当晶粒尺寸过大时 复相磁体表现出两相行为，其δm(H)曲线出现了两个正峰值.分析表明，外场较小的正峰值是软磁相与硬磁相晶粒之间交换耦合作用的结果，而外场较大的正峰值是硬磁相晶粒之间交换耦合作用的结果. 关键词： 纳米晶永磁 晶间交换耦合 δm(H)曲线     

纳米晶复合Pr2Fe14B/α-Fe永磁材料磁性的研究

采用熔体快淬的方法制备Pr₂Fe₁₄B/α-Fe纳米晶复合永磁材料.使用振动样品磁强计(VSM)测量样品的室温磁性能.实验合金成分为(Pr_xFe_94.3-xB_5.7)_0.99Zr₁(其中x＝8.2，8.6，9.0，9.4，9.8，10.2，10.6，11.0，11.4(原子分数，%)).系统地研究了辊速及合金成分对快淬带磁性能的影响，当Pr原子分数由8. 关键词： 纳米复合永磁材料 熔体快淬 2Fe₁₄B/α-Fe')" href="#">Pr₂Fe₁₄B/α-Fe 磁性     

Flexible tuning microwave permeability spectrum in [ferromagnet/antiferromagnet]_n exchange-biased multilayer stack structure

NiFe/[IrMn/NiFe/IrMn] 5 /[NiFe/IrMn] 4 /NiFe structured exchange-biased multilayer films are designed and prepared by magnetron sputtering. The static and the microwave magnetic properties are systematically investigated. The results reveal that adding a partially pinned ferromagnetic layer can effectively broaden the ferromagnetic resonance linewidth toward the low frequency domain. Moreover, a wideband multi-peak permeability spectrum with a 3.1-GHz linewidth is obtained by overlapping the spectra of different partially pinned ferromagnetic layers and [antiferromagnet/ferromagnet/antiferromagnet] n stacks. Our results show that the linewidth of the sample can be feasibly tuned through controlling the proper exchange bias fields of different stacks. The designed multilayered thin films have potential application for a tunable wideband high frequency noise filter.     

纳米晶复合永磁材料的交换耦合相互作用和磁性能

本介绍了纳米磁性材料晶粒交换耦合相互作用的有关理论。采用不同模型讨论了晶粒交换耦合相互作用对纳米单相软磁材料、永磁材料及双相复合永磁材料磁性能的影响。简述了用δM（H）曲线和不可逆磁导率的变化研究晶粒交换耦合相互作用及反磁化过程的方法。讨论了合金分配比、添加元素、制备及热处理工艺对磁体硬磁性能的影响。从理论和实验两方面分析、研究了纳米复合永磁材料的反磁化过程和矫顽力机制。