MOCVD法制备Cu掺杂ZnO薄膜

通过金属有机物化学气相沉积(MOCVD)设备,在c-Al2 03衬底上生长本征和Cu掺杂ZnO( ZnO∶ Cu)薄膜.X射线衍射(XRD)谱观察到未掺杂的ZnO和ZnO∶ Cu样品都呈现出较好的c轴择优取向生长.X射线光电子能谱(XPS)表明Cu已掺入到ZnO薄膜中.利用光致发光(PL)测试对本征ZnO和ZnO∶ C...     

PLD制备的Cu掺杂SnS薄膜的结构和光学特性

利用脉冲激光沉积(PLD)在玻璃衬底上制备了Cu掺杂SnS薄膜.靶材是由SnS和Cu₂S粉末混合压制而成(Cu和Sn的量比分别为0%、2.5%、5%、7.5%和10%).利用X射线衍射(XRD)、拉曼光谱仪(Raman)、原子力显微镜(AFM)、紫外-可见-近红外分光光度计(UV-Vis-NIR)、Keithley 4200-SCS半导体参数分析仪研究了Cu掺杂量对SnS薄膜的晶体结构、表面形貌、光学性质和电学性能的影响.结果表明:所制备的SnS薄膜样品沿(111)晶面择优取向生长, SnS :5%Cu薄膜的结晶质量最好且具有SnS特征拉曼峰.随着Cu掺杂量的增大, 平均颗粒尺寸逐渐增大.不同Cu掺杂量的薄膜在可见光范围内的吸收系数均为10⁵ cm^-1数 量级.SnS :5%Cu薄膜的禁带宽度E_g为2.23 eV, 光暗电导率比值为2.59.同时, 在玻璃衬底上制备了p-SnS :Cu/n-ZnS 异质结器件, 器件在暗态及光照的条件下均有良好的整流特性, 并具有较弱的光伏特性.     

(Cu,N)共掺杂TiO2/MoS2异质结的电子和光学性能:杂化泛函HSE06

在密度泛函理论的基础上,系统地研究了Cu/N（共）掺杂的TiO₂/MoS₂异质结体系的几何结构、电子结构和光学性质.计算发现,TiO₂/MoS₂异质结的带隙相比于纯的TiO₂（101）表面明显变小,Cu/N（共）掺杂TiO₂/MoS₂异质结体系的禁带宽度也明显地减小,这导致光子激发能量的降低和光吸收能力的提高.通过计算Cu/N（共）掺杂TiO₂/MoS₂的差分电荷密度,发现光生电子与空穴积累在掺杂后的TiO₂（101）表面和单层MoS₂之间,这表明掺杂杂质体系可以有效地抑制光生电子-空穴对的复合.此外,我们计算了在不同压力下TiO₂/MoS₂异质结的几何、电子和光学性质,发现适当增加压力可以有效提高异质结的光吸收性能.本文结果表明,Cu/N（共）掺杂TiO₂/MoS₂异质结和对TiO₂/MoS₂异质结加压都能有效地提高材料的光学性能.     

In掺杂氮化亚铜薄膜的电学、光学和结构特性研究

采用射频磁控溅射方法, 在低功率和低温条件下利用纯氮气作为反应溅射气体制 备出不同In含量的三元氮化物Cu_xIn_yN薄膜. 研究发现In掺杂浓度对薄膜微结构、形貌、表面化学态以及光学特性有灵敏的调节作用. 光电子峰、俄歇峰、俄歇参数的化学位移变化从不同角度揭示了不同含量In掺杂引 起的原子结合情况的变化. XPS结果显示In含量小于8.2 at.%的样品形成了Cu-In-N键. 对In含量为4.6 at.%的样品进行XRD和TEM结构测试, 实验结果肯定了In原子填充到Cu₃N的反ReO₃结构的体心位置. 并且当In含量增至10.7 at.%时, 薄膜生长的择优取向从之前占主导地位的(001)方向转变为(111)方向. 此外, 随着In含量的增加, 薄膜的R-T曲线从指数形式变为线性. 当In含量为47.9 at.%时, 薄膜趋于大温区恒电阻率材料, 电阻温度系数TCR仅为-6/10000. 光谱测量结果显示In摻杂使得氮化亚铜掺杂薄膜的光学帯隙从间接帯隙变为直接帯隙. 由于Burstein-Moss效应, 帯隙发生蓝移, 从1.02 eV 到2.51 eV, 实现了帯隙连续可调. 关键词： 三元氮化物 薄膜 光学特性 氮化亚铜     

Microstructure and electro-optical properties of sol–gel derived Cd-doped ZnO films

The microstructure, and the electrical and optical properties of undoped zinc oxide (ZnO) and cadmium-doped ZnO (CZO) films deposited by a sol–gel method have been investigated. The films have a polycrystalline structure with hexagonal wurtzite ZnO. Scanning electron microscopy (SEM) images indicated that the films have a wrinkle network with uniform size distributions. The elemental analyses of the CZO films were carried out by energy dispersive X-ray analysis. The fundamental absorption edge changed with doping. The optical band gap of the films decreased with Cd dopant. The optical constants of the films such as refractive index, extinction coefficient and dielectric constants changed with Cd dopant. A two-probe method was used to investigate the electrical properties, and the effect of Cd content on the electrical properties was investigated. The electrical conductivity of the films was improved by incorporation of Cd in the ZnO film.     

Optoelectronic properties of SnO_2 thin films sprayed at different deposition times

This article presents the elaboration of tin oxide(SnO_2) thin films on glass substrates by using a home-made spray pyrolysis system. Effects of film thickness on the structural, optical, and electrical film properties are investigated. The films are characterized by several techniques such as x-ray diffraction(XRD), atomic force microscopy(AFM), ultravioletvisible(UV–Vis) transmission, and four-probe point measurements, and the results suggest that the prepared films are uniform and well adherent to the substrates. X-ray diffraction(XRD) patterns show that SnO_2 film is of polycrystal with cassiterite tetragonal crystal structure and a preferential orientation along the(110) plane. The calculated grain sizes are in a range from 32.93 nm to 56.88 nm. Optical transmittance spectra of the films show that their high transparency average transmittances are greater than 65% in the visible region. The optical gaps of SnO_2 thin films are found to be in a range of 3.64 e V–3.94 e V. Figures of merit for SnO_2 thin films reveal that their maximum value is about 1.15 × 10-4-1?atλ = 550 nm. Moreover, the measured electrical resistivity at room temperature is on the order of 10-2?·cm.     

Bismuth oxide thin films prepared by chemical bath deposition (CBD) method: annealing effect

Bismuth oxide thin films have been deposited by room temperature chemical bath deposition (CBD) method and annealed at 623 K in air. They were characterized for structural, surface morphological, optical and electrical properties. From the X-ray diffraction patterns, it was found that after annealing a non-stoichiometric phase, Bi₂O_2.33, was removed and phase pure monoclinic Bi₂O₃ was obtained. Surface morphology of Bi₂O₃ film at lower magnification SEM showed rod-like structure, however, higher magnification showed a rectangular slice-like structure perpendicular to substrate, giving rise to microrods on the surface. The optical studies showed the decrease in band gap by 0.3 eV after annealing. The electrical resistivity variation showed semiconductor behavior and from thermoemf measurements, the electrical conductivity was found to be of n-type.     

不同Sb含量p-SnO2薄膜的制备和特性

采用化学气相沉积方法, 利用Sb₂O₃/SnO作为源材料, 在蓝宝石衬底上制备出不同Sb掺杂量的SnO₂薄膜, 并在此基础上制作出p-SnO₂:Sb/n-SnO₂同质p-n 结器件. 研究表明, 随着Sb含量的增加, 样品表面变得平滑, 晶粒尺寸逐渐增大, 且晶体质量有所改善, 发现少量Sb的掺入可以起到表面活化剂的作用. Hall测量结果证实适量Sb的掺杂可以使SnO₂呈现p型导电特性, 当Sb₂O₃/SnO的质量比为1:5时, 其电学参数为最佳值. 此外, p-SnO₂:Sb/n-SnO₂同质p-n结器件展现出良好的整流特性, 其正向开启电压为3.4 V.     

镧掺杂BaSnO3薄膜的电学和光学特性

利用射频磁控溅射法在(LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (001)单晶基底上生长了镧掺杂BaSnO₃外延薄膜. 通过Hall效应和热电势测量证实了镧掺杂BaSnO₃薄膜具有n型简并半导体特征, 并且基于载流子浓度和Seebeck系数计算出电子的有效质量为0.31m₀ (m₀为自由电子质量). 镧掺杂BaSnO₃薄膜在可见波段具有良好的透明性(透过率大于73%). 基于介电模型对薄膜的透过率曲线进行拟合, 从拟合结果中不仅得到了薄膜的厚度为781.2 nm, 能带宽度为3.43 eV、 带尾宽度为0.27 eV和复光学介电常数随波长的变化规律, 而且也强力地支持了基于电学参数计算电子有效质量的正确性.     

过渡金属与F共掺杂ZnO薄膜结构及磁、光特性

采用溶胶-凝胶法在玻璃衬底上制备了过渡金属元素与F共掺杂Zn_0.98-xTM_xF_0.02O (TM_x=Cu_0.02, Ni_0.01, Mn_0.05, Fe_0.02, Co_0.05)薄膜, 进而利用X射线衍射仪、扫描电子显微镜、紫外-可见透过谱、光致发光及振动样品磁强计等研究了薄膜的表面形貌、微结构、禁带宽度及光致发光(PL)和室温磁学特性. 研究表明: 掺杂离子都以替位的方式进入了ZnO晶格, 掺杂不会破坏ZnO的纤锌矿结构. 其中Zn_0.93Co_0.05F_0.02O薄膜样品的颗粒尺寸最大, 薄膜的结晶度最好且c轴择优取向明显; Zn_0.93Mn_0.05F_0.02O薄膜样品的颗粒尺寸最小, 薄膜结晶度最差且无明显的c轴择优取; Cu, Ni, Fe与F共掺杂样品的颗粒尺寸大小几乎相同. TM掺杂样品均表现出很高的透过率, 同时掺杂后的薄膜样品的禁带宽度都有不同程度的红移. PL谱观察到Zn_0.98-xTM_xF_0.02O薄膜的发射峰主要由较强的紫外发射峰和较弱的蓝光发射峰组成. Zn_0.93Mn_0.05F_0.02O薄膜样品的紫外发光峰最弱, 蓝光发射最强, 饱和磁化强度最大; 与之相反的是Zn_0.96Cu_0.02F_0.02O薄膜, 其紫外发光峰最强, 蓝光发射最弱, 饱和磁化强度最小. 结合微结构和光学性质对Zn_0.98-xTM_xF_0.02O薄膜的磁学性质进行了讨论.     

氧化镓薄膜的制备及其日盲紫外探测性能研究

采用射频磁控溅射方法在蓝宝石单晶衬底上沉积氧化镓(Ga2O3)薄膜,并通过光刻剥离工艺(Lift-off)制备了金属-半导体-金属结构的Ga2O3日盲紫外探测器。对不同温度下沉积的Ga2O3薄膜分析表明,在800℃下获得的薄膜结晶质量最好,薄膜的导电性则随着沉积温度的上升先增大后减小。在800℃制备的β-Ga2O3薄膜的可见光透光率大于90%,光学吸收边在255 nm附近。在10 V偏压下,探测器的暗电流约为1n A,光电流达800 n A,对紫外光响应迅速。器件的响应度达到0.3 A/W,260 nm波长处的响应度是290 nm波长对应响应度的40倍,可实现日盲紫外波段的探测。     

Electrical conductivity, optical and metal–semiconductor contact properties of organic semiconductor based on MEH-PPV/fullerene blend

The electrical conductivity, optical and metal–semiconductor contact properties of the MEH-PPV:C₇₀ organic semiconductor have been investigated. The electrical conductivity results show that the MEH-PPV:C₇₀ film is an organic semiconductor. The optical band gap of the film was found to be 2.06 eV and the fundamental absorption edge in the film is formed by the direct allowed transitions. The refractive index dispersion curve of the film obeys the single oscillator model and E_d and E_o dispersion parameters were found to be 10.61 and 3.89 eV, respectively. The electrical characterization of the ITO/MEH-PPV:C₇₀ diode have been investigated by current–voltage characteristics. ITO/MEH-PPV:C₇₀ diode indicates a non-ideal current–voltage behavior with ideality factor n (2.50) and barrier height φ_B (0.90 eV) values.     

Probing the effect of nitrogen gas on electrical conduction phenomena of ZnO and Cu-doped ZnO thin films prepared by spray pyrolysis

Zinc oxide (ZnO) and Cu-doped ZnO (CZO) thin films were prepared on borosilicate glass substrates by spray pyrolysis technique. The X-ray diffraction study revealed that Cu doping caused a reduction in crystallite size. AFM study showed an increase in roughness with doping. This is attributed to the aggregation of particles to form clusters. From transmission electron microscopy analysis, the particle size is measured to be in the range 30–65 nm (average particle size 48 nm) for undoped ZnO, whereas it is in the range 24–56 nm (average particle size 40 nm) for CZO film. The electrical resistivity of the thin films was investigated in the presence of air as well as N₂ mixed air at different temperatures in the range 30–270 °C. The change in resistivity properties was explained on the basis of conduction phenomena within the grain along with the grain boundaries as well as Cu- and N₂-induced defect states. The thermal activation energy of ZnO was found to be in the range 0.04–0.7 eV and dependent on Cu doping and N₂ level in air.     

带隙可调的Al，Mg掺杂ZnO薄膜的制备

利用射频磁控溅射（RF-MS）方法,固定Al₂O₃掺杂量2 wt%,Mg掺杂量分别为1 wt%,3 wt%和5 wt%,在玻璃基底上制备了Al掺杂和Al,Mg共掺杂的ZnO薄膜,在500 ℃空气中退火2 h后,测量并比较了它们的光学和电学性质．结果表明,Al,Mg共掺杂的ZnO薄膜结晶质量良好,具有ZnO纤锌矿结构,具有较强的（002）面衍射峰,表明薄膜晶体沿c轴优先生长;与Al掺杂ZnO薄膜相比蓝端光透射率增加,1 wt%和3 wt% Mg掺杂薄 关键词： 射频磁控溅射 ZnO薄膜 Al Mg共掺杂     

过渡区p型氢化硅氧薄膜结构和光电特性的研究

采用射频等离子体增强化学气相沉积技术,利用二氧化碳(CO_2)、氢气(H_2)、硅烷(SiH_4)和乙硼烷(B_2H_6)作为气源,制备出一系列p型氢化硅氧薄膜.利用拉曼光谱、傅里叶变换红外光谱和暗电导测试,研究了不同二氧化碳流量对薄膜材料结构和光电特性的影响,获得了从纳米晶相向非晶相转变的过渡区P层.研究表明:随着二氧化碳流量从0增加到1.2 cm~3·min~(-1),拉曼光谱的峰值位置从520 cm~(-1)逐渐移至480 cm~(-1).材料红外光谱表明,随着二氧化碳流量的增加,薄膜中的氧含量逐渐增加,氢键配置逐渐由硅单氢键转换为硅双氢键.P层SiO:H薄膜电导率从3S/cm降为8.3×10~(-6)S/cm.所有p型SiO:H薄膜的光学带隙(Eopt)都在1.82—2.13 eV之间变化.在不加背反射电极的条件下,利用从纳米晶相向非晶相转变的过渡区P层作为电池的窗口层,且在P层和I层之间插入一定厚度的缓冲层,制备出效率为8.27%的非晶硅薄膜电池.     

Synthesis and physical behaviour of In2S3 films

In₂S₃ layers have been grown by close-spaced evaporation of pre-synthesized In₂S₃ powder from its constituent elements. The layers were deposited on glass substrates at temperatures in the range, 200–350 °C. The effect of substrate temperature on composition, structure, morphology, electrical and optical properties of the as-grown indium sulfide films has been studied. The synthesized powder exhibited cubic structure with a grain size of 63.92 nm and S/In ratio of 1.01. The films grown at 200 °C were amorphous in nature while its crystallinity increased with the increase of substrate temperature to 300 °C. The films exhibited pure tetragonal β-In₂S₃ phase at the substrate temperature of 350 °C. The surface morphological analysis revealed that the films grown at 300 °C had an average roughness of 1.43 nm. These films showed a S/In ratio of 0.98 and a lower electrical resistivity of 1.28 × 10³ Ω cm. The optical band gap was found to be direct and the layers grown at 300 °C showed a higher optical transmittance of 78% and an energy band gap of 2.49 eV.     

Structural, optical and electrical studies on pulse electrodeposited CdIn2S4 thin films

CdIn₂S₄ thin films were prepared by pulse electrodeposition technique over F:SnO₂ glass and stainless steel substrates in galvanostatic mode from an aqueous acidic bath containing CdSO₄, InCl₃ and Na₂S₂O₃. The growth kinetics of the film has been studied and the deposition parameters such as electrolyte bath concentration, bath temperature, time of deposition, deposition current and pH of the bath are optimized. X-ray diffraction (XRD) analysis of the as deposited and annealed films shows polycrystalline nature. Energy dispersive analysis by X-ray (EDAX) confirms nearly stoichiometric CdIn₂S₄ nature of the film. Scanning electron microscope (SEM) studies show that, the deposited films are well adherent and grains are uniformly distributed over the surface of the substrate. The optical transmission spectra show a direct band gap of 2.16 eV. Conductivity measurements have been carried out at different temperatures and electrical parameters such as activation energy, trapped energy state and barrier heights etc. have been determined.     

Effect of substrate bias on SE, XPS and XAES studies of diamond-like carbon films deposited by saddle field fast atom beam source

This paper reports the effect of positive substrate bias (V_s) varying from 0 to 180 V on the spectroscopic ellipsometry (SE), X-ray photoelectron spectroscopy (XPS) and X-ray Auger electron spectroscopy (XAES) studies of diamond-like carbon (DLC) films deposited using CH₄ gas as a feedstock into a saddle field fast atom beam (FAB) source. The values of optical constants like refractive index (n) and extinction coefficient (k) of the deposited DLC films were determined using a two phase model. The values of ‘n’ were found to fall in the range from 1.505 to 1.720 and ‘k’ from 0.03 to 0.125 by application of different values of V_s. Value of these optical constants were found to decrease with the increase of substrate bias up to 90 V and then increase beyond this value. Position of C 1s peak evaluated from XPS data was found to occur at 286.09±0.18 eV in DLC films deposited by application of different values of V_s. Observation of full width at half maximum (FWHM) (τ) value (1.928 eV at V_s=0 V, 2.0 eV at V_s=90 V and 1.89 eV at V_s=180 V) clearly hinted the existence of a point of inflection in the properties of DLC films deposited using FAB source this way. A parameter ‘D’ defined as the distance between the maximum of positive going excursion and the minimum of negative going excursion was calculated in the derivative XAES spectra. The values of ‘D’ evaluated from XAES data for DLC films were found to be 14.8, 14.5 and 15.2 at V_s=0, 90 and 180 V, respectively. The sp² percentage was calculated for samples deposited this way and was found to be low and lie approximately at 5.6, 2.8, 2.3, 5.7 and 11.5 for different values of V_s=0, 50, 90, 150 and 180 V. The sp³ content percentage and sp³/sp² ratio was found to be 94.4 and 16.7, 97.7 and 42.5 at V_s=0 and 90 V, respectively. Beyond V_s=90 V these values started decreasing. Mainly, a point of inflection in all the properties of DLC films studied over here at around 90 V of applied substrate bias has been observed, which has been explained on the basis of existing theories in the literature.     

Structural, optical and electrical properties of molybdenum-doped cadmium oxide thin films prepared by spray pyrolysis method

Molybdenum-doped cadmium oxide films were prepared by a spray pyrolysis technique at a substrate temperature of 300?°C. The effect of doping on structural, electrical and optical properties were studied. X-ray analysis shows that the undoped CdO films are preferentially oriented along the (111) crystallographic direction. Molybdenum doping concentration increases the films?? packing density and reorients the crystallites along the (200) plane. A?minimum resistivity of 4.68×10^?4????cm with a maximum mobility of 75?cm²?V^?1?s^?1 is achieved when the CdO film is doped with 0.5?wt.% Mo. The band-gap value is found to increase with doping and reaches a maximum of 2.56?eV for 0.75?wt.% as compared to undoped films of 2.2?eV.     

利用MOCVD技术生长As掺杂的p-ZnMgO薄膜

利用GaAs夹层掺杂的新方法,采用金属有机化学气相沉积(MOVCD)技术,通过控制生长温度,在蓝宝石衬底上成功制备出As掺杂的p型ZnMgO薄膜.利用X射线衍射分析(XRD)、霍尔效应测试和光致发光(PL)谱等表征方法对薄膜的晶体结构、电学性能和光学特性进行分析.结果表明:高温生长的ZnMgO薄膜具有良好的c轴取向性;...