We report on experimental evidence of pronounced global plasticity measured in monolithic Pt57.5Cu14.7Ni5.3P22.5 bulk metallic glass under both bending and unconfined compression loading conditions. A plastic strain of 20% is measured, never before seen in metallic glasses. Also, permanent deformation and a strain exceeding 3% before failure is observed during bending of 4 mm thick samples. To date, no monolithic metallic material has exhibited such a combination of high strength, extensive ductility, and high elastic limit. The large plasticity is reflected in a high Poisson ratio of 0.42, which causes the tip of a shear band to extend rather than initiate a crack. This results in the formation of multiple shear bands and is the origin of the observed large global ductility and very high fracture toughness, approximately 80 MPa m(-1/2).     

Pd-Si binary bulk metallic glass

Pd_80+x Si_20−x (x = 0, 1, and 2) binary metallic glasses with the diameter ranging from 7 to 8 mm were prepared by a combination of fluxing and water quenching or air cooling. Thermal analysis results show that with increasing Si content, the glass transition temperature T _g, the initial crystallization temperature T _x and the onset crystallization temperature T _p of Pd-Si binary glassy alloys increase. Moreover, the supercooled liquid region reaches 61 K. It indicates that Pd-Si binary alloys possess large glass forming ability, which can be greatly improved by fluxing treatment. Supported by the National Basic Research Program of China (Grant No. 2007CB613905) and the National Natural Science Foundation of China (Grant Nos. 50671050 and 50431030)     

Effect of the cooling rate on plastic deformability of a Zr-based bulk metallic glass

The present work found the plastic deformability of Zr65Cu17.5Ni10Al7.5 BMG dependent on the cooling rate during the formation from the molten state alloy. The deformation behavior in the compression test of φ 2 mm Zr65Cu17.5Ni10Al7.5 BMGs as-cast or lathed from different sizes as-cast samples was characterized, and they exhibited different plastic strains. The compressive plastic strain increases with the decreasing diameter of the as-cast specimens, i.e. with increasing the cooling rate. It is suggested that free volume content in the BMGs, which is related to the cooling rate during the rapid solidification, could play an important role in the deformation process of the BMGs.     

"Work-Hardenable" ductile bulk metallic glass

Usually, monolithic bulk metallic glasses undergo inhomogeneous plastic deformation and exhibit poor ductility (< 1%) at room temperature. We present a new class of bulk metallic glass, which exhibits high strength of up to 2265 MPa together with extensive "work hardening" and large ductility of 18%. Significant increase in the flow stress was observed during deformation. The "work-hardening" capability and ductility of this class of metallic glass is attributed to a unique structure correlated with atomic-scale inhomogeneity, leading to an inherent capability of extensive shear band formation, interactions, and multiplication of shear bands.     

Compressive fracture characteristics of Zr-based bulk metallic glass

The compressive fracture characteristics of Zr-based bulk metallic glass under uniaxial compression tests are studied.The zigzag rheological behavior is observed in the compression stress-strain curves of amorphous alloys.At room temperature the uniaxial compression fracture takes place along the plane which is at a 45-degree angle to the direction of the compressive stress.The microstructure of a typical fracture pattern is the vein network.A unique,finger-like vein pattern is found to exist at the fractur...     

Deformation behavior of Fe-based bulk metallic glass during nanoindentation

Fe-based bulk metallic glasses (BMGs) normally exhibit super high strength but significant brittleness at ambient temperature. Therefore, it is difficult to investigate the plastic deformation behavior and mechanism in these alloys through conventional tensile and compressive tests due to lack of distinct macroscopic plastic strain. In this work, the deformation behavior of Fe₅₂Cr₁₅Mo₉Er₃C₁₅B₆ BMG was investigated through instrumented nanoindentation and uniaxial compressive tests. The results show that serrated flow, the typical plastic deformation feature of BMGs, could not be found in as-cast and partially crystallized samples during nanoindentation. In addition, the deformation behavior and mechanical properties of the alloy are insensitive to the applied loading rate. The mechanism for the appearance of the peculiar deformation behavior in the Fe-based BMG is discussed in terms of the temporal and spatial characteristics of shear banding during nanoindentation. Supported by the National Natural Science Foundation of China (Grant Nos 50571109, 10572142 and 56771102) and the National Basic Research Program of China (973 Program)(Grant No 2007CB613900)     

Phase separating bulk metallic glass: a hierarchical composite

Phase separating systems present a unique opportunity for designing composites with hierarchical microstructure at different length scales. We report here our success in synthesizing phase separating metallic glasses exhibiting the entire spectrum of microstructural possibilities expected from a phase separating system. In particular, we report novel core shell and hierarchical structures of spherical glassy droplets, resulting from critical wetting behavior and limited diffusion. We also report synthesis of a bulk phase separating glass in a metallic glass system. The combination of unique core shell and hierarchical structures in metallic glass systems opens a new avenue for the microstructure design of metallic glasses.     

Shear band formation and ductility in bulk metallic glass

The variations in the chemical compositions of the metallic glasses reported in the literature, as well as the overall lack of experimental data concerning the inhomogeneous deformation behaviour of metallic glass, make the evaluation of the effects of shear band/fracture behaviour on the mechanical properties of metallic glasses difficult. Isolating the effect of local shear band formation on bulk inhomogeneous flow would appear to be a first step in approaching this problem. The mechanical behaviour of Vitreloy metallic glass at room temperature and at various strain rates in tension and compression was investigated. The formation of multiple shear bands was observed at high strain rates. An increase in strain rate leads to enhanced ductility in tension and compression. Some aspects of the deformation processes in tension and compression are discussed.     

新型Pr基大块非晶及其特性研究

用铜模吸铸法获得了直径为5mm的一种新的Pr基大块非晶.与以往其他稀土-过渡金属(RE-TM)大块非晶不同的是，这种新的Pr基大块非晶具有明显的玻璃转变和稳定的过冷液相区，且其玻璃转变温度在目前已知的大块非晶中是最低的，T_g=409K.研究了该大块非晶的玻璃转变动力学，并给出了Kauzmann温度T_k、Vogel-Fulcher温度T⁰_g及脆性参数m等重要参数. 关键词： 大块非晶 玻璃转变 脆性参数m     

Irreversible structural relaxation in a bulk Pd-Cu-Ni-P metallic glass

The evolution of the shear modulus and the damping decrement during irreversible structural relaxation in a bulk Pd₄₀Cu₃₀Ni₁₀P₂₀ metallic glass in a temperature range below the glass transition temperature has been studied with an inverse torsion pendulum at a frequency of ～25 Hz. It is shown that the irreversible relaxation can be recovered via quenching from temperatures above the glass transition temperature. The spectrum shape, the characteristic activation energies, and the attempt frequencies of the irreversible structural relaxation are estimated.     

Fracture characteristics of bulk metallic glass under high speed impact

High speed impact experiments of rectangular plate-shaped Zr₄₁Ti₁₄Cu_12.5Ni₁₀Be_22.5 bulk metallic glass (BMG) were performed using a two-stage light gas gun. Under spherical shock waves with impact velocities ranging from 0.503 km/s to 4.917 km/s, obvious traces of laminated spallation at the back (free) surface and melting (liquid droplets) at the impact point were observed. The angles about 0?, 17?, 36?, and 90? to the shocking direction were shown in the internal samples because of the interaction between the compressive shock waves and the rarefaction waves. The compressive normal stress was found to induce the consequent temperature rise in the core of the shear band.     

Spin-glass behavior and magnetocaloric effect in Tb-based bulk metallic glass

A noncollinear-ferromagnetic spin-glass-like state was observed in Tb₅₅Co₂₀Al₂₅ bulk metallic glass due to the strong random magnetic anisotropy. Associated with this behavior, we observed a comparatively large magnetic entropy change (ΔS_m is 9.75 J K⁻¹ kg⁻¹) in a field change of 7 T and a correspondingly high value of the magnetic refrigeration capacity (RC is 540 J kg⁻¹) with almost no hysteresis loss in the vicinity of the so-called Curie temperature. This opens the possibility of using this material for magnetic cooling purposes.     

Numerical study of pile-up in bulk metallic glass during spherical indentation

Pile-up around indenter is usually observed during instrumented indentation tests on bulk metallic glass. Neglecting the pile-up effect may lead to errors in evaluating hardness, Young’s modulus, stress-strain response, etc. Finite element analysis was employed to implement numerical simulation of spherical indentation tests on bulk metallic glass. A new model was proposed to describe the pile-up effect. By using this new model, the contact radius and hardness of Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 bulk metallic glass were obtained under several different indenter loads with pile-up, and the results agree well with the data generated by numerical simulation. Supported by the National Natural Science Foundation of China (Grant Nos 10725211, 10721202 and 10472119) and the Key Project of Chinese Academy of Sciences (Grant Nos KJCX2-YW-M04 and KJCX-SW-L08)     

Tribological characterisation of Zr-based bulk metallic glass in simulated physiological media

Due to their excellent wear resistant properties and high strength, as well as a low Young's modulus, Zr-based bulk metallic glasses (BMGs) are potentially suitable biomaterials for low-friction arthroplasty. The wear characteristics of the Zr_60.14Cu_22.31Fe_4.85Al_9.7Ag₃ bulk amorphous alloy against ultra-high-molecular-weight polyethylene (UHMWPE) compared to a CoCrMo/UHMWPE combination were investigated in two different wear screening test devices, reciprocating and unidirectional. Hank's solution and sterile calf bovine serum were selected as the lubricant fluid media. It was found that different fluid media had insignificant effect on polyethylene wear against BMG counterfaces. The wear behaviour obtained on both test devices demonstrated that Zr-based BMG achieved UHMWPE counterface wear rates superior to conventional cast CoCrMo alloy, where the wear rate of UHMWPE is decreased by over 20 times. The tribological performance of these joints is superior to that of conventional metal-on-polymer designs. Contact angle measurements suggested that the advantage of BMG over a CoCrMo alloy counterface is attributed to its highly hydrophilic surfaces.     

Softening caused by profuse shear banding in a bulk metallic glass

By controlling the specimen aspect ratio and strain rate, compressive strains as high as 80% were obtained in an otherwise brittle metallic glass. Physical and mechanical properties were measured after deformation, and a systematic strain-induced softening was observed which contrasts sharply with the hardening typically observed in crystalline metals. If the deformed glass is treated as a composite of hard amorphous grains surrounded by soft shear-band boundaries, analogous to nanocrystalline materials that exhibit inverse Hall-Petch behavior, the correct functional form for the dependence of hardness on shear-band spacing is obtained. Deformation-induced softening leads naturally to shear localization and brittle fracture.     

Dynamic strength behavior of a Zr-based bulk metallic glass under shock loading

Dynamic strength behavior of Zr51Ti5Ni10Cu25Al9 bulk metallic glass(BMG) up to 66 GPa was investigated in a series of plate impact shock-release and shock-reload experiments.Particle velocity profiles measured at the sample/Li F window interface were used to estimate the shear stress,shear modulus,and yield stress in shocked BMG.Beyond confirming the previously reported strain-softening of shear stress during the shock loading process for BMGs,it is also shown that the softened Zr-BMG still has a high shear modulus and can support large yield stress when released or reloaded from the shocked state,and both the shear modulus and the yield stress appear as strain-hardening behaviors.The work provides a much clearer picture of the strength behavior of BMGs under shock loading,which is useful to comprehensively understand the plastic deformation mechanisms of BMGs.     

Microstructure and mechanical properties of a partially crystallized La-based bulk metallic glass

The evolution of microstructure upon partial crystallization and its influence on the mechanical properties such as hardness, elastic modulus and viscosity in a La 55 Al 25 Cu 10 Ni 5 Co 5 bulk metallic glass alloy are studied. Specimens with various volume fractions of crystalline phases were obtained by annealing the as-cast amorphous alloy above its glass transition temperature and were characterized by transmission electron microscopy. Microscopic examination of the heat-treated samples shows short-range-ordered domains prior to nanocrystallization within the amorphous matrix, followed by the growth and impingement of the crystallites. Whereas the hardness of the annealed samples increases linearly with increasing crystallinity, the elastic modulus and the viscosity both increase abruptly when the crystalline volume fraction is about 40 vol.%, with a only minor variation on either side of this range. The sudden rises in the modulus and viscosity are similar to those in the literature data on the fracture strength of partially crystallized bulk amorphous alloys that shows a steep drop in strength at 30-50 vol.% crystallinity. On the basis of the microscopic observations, it is suggested that the interaction and formation of rigid networks of crystalline phases upon the attainment of a critical second-phase volume fraction may be the possible reason for the sudden change in mechanical properties. Percolation theory is utilized in further substantiating this hypothesis.     

Zr48Cu45Al7大块金属玻璃的原子结构研究

应用同步辐射X射线衍射(XRD)和广延X射线吸收精细结构边方法(EXAFS),结合反蒙特卡罗(RMC)拟合、Voronoi分形技术等对Zr₅₀Cu₅₀二元和Zr₄₈Cu₄₅Al₇三元金属玻璃材料的微观结构进行了系统的研究.结果表明:ZrCuAl三元金属玻璃中Al原子与Zr原子、Cu原子之间存在强相互作用,表现为键长的明显缩短,导致其微观结构中的Voronoi团簇体积普遍小于Zr_{50关键词： 大块金属玻璃 原子结构 玻璃形成能力 同步辐射技术}     

In-situ neutron scattering study of crystallization in a Zr-based bulk metallic glass

In this paper, we report the structure, optical, and gas-sensing properties of Co-doped ZnO nanocrystals prepared by a simple solvothermal route. The red-shift of the band-gap edge is attributed to a merging of donor and conduction bands due to Co doping. Photoluminescence (PL) spectra were used to study the dependence of doping on the deep-level emission, which show obvious enhanced blue-green emission after Co doping. Gas sensors were prepared and tested for the detection of C₂H₅OH in air. It is found that the Co-doped nanocrystals have a significantly better sensing performance than pure ZnO, which is comparable to the Au-functionalized ZnO sensors. We provide a possible explanation in terms of the sensing mechanism of the surface reaction process.     

Computer simulation of the matrix-inclusion interphase in bulk metallic glass based nanocomposites

Atomistic models for matrix-inclusion systems are generated. Analyses of the systems show that interphase layers of finite thickness appear interlinking the surface of the nanocrystalline inclusion and the embedding amorphous matrix. In a first approximation, the interphase is characterized as an amorphous structure with a density slightly reduced compared to that of the matrix. This result holds for both monatomic hard sphere systems and a Cu(47.5)Zr(47.5)Al(5) alloy simulated by molecular dynamics (MD). The elastic shear and bulk modulus of the interphase are calculated by simulated deformation of the MD systems. Both moduli diminish with decreasing density but the shear modulus is more sensitive against density reduction by one order of magnitude. This result explains recent observations of shear band initiation at the amorphous-crystalline interface during plastic deformation.