Contributions of the nanovoid structure to the moisture absorption properties of epoxy resins

Epoxy resins absorb significant quantities of moisture, typically 1 to 7% by weight for various formulations, which can greatly compromise their physical properties. It is known that polarity of the epoxy is a significant factor in determining the ultimate moisture uptake. However, the contribution from molecular topology still remains vague. In this work, the effects of molecular topology are elucidated by synthesizing novel epoxies where the polarity is maintained constant but the topology is systematically altered. The molecular topology is quantified in part via Positron Annihilation Lifetime Spectroscopy (PALS) in terms of the nanometer-sized voids, or nanovoids, that are also commensurate with typical interchain distances. The nanovoids are separated into their absolute zero and thermally fluctuating fractions by performing PALS measurements over a wide range of temperatures. A strong correlation is observed between the absolute zero hole volume fraction and the ultimate moisture uptake. Although the correlation is clear, the absolute zero hole volume fraction alone is not sufficient to predict the ultimate moisture uptake, and network polarity must also be considered. It is surmised that the role of the nanovoids is to open the epoxy matrix and alleviate steric hindrances that may prevent a water molecule from associating with a polar group. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 3035–3048, 1998     

Conformation and luminescence characteristics of nanopoly[2‐metoxy‐5‐(2′‐ethyl‐hexyloxy)‐p‐phenylene vinylene] in two‐dimensional arrays

With anodic alumina with an ordered nanopore array used as a template, poly[2‐metoxy‐5‐(2′‐ethyl‐hexyloxy)‐p‐phenylene vinylene] (MEH–PPV) was embedded into the nanopores, and then two‐dimensional arrays of light‐emitting nanopolymers were prepared. By the measurement and analysis of photoluminescence and photoluminescence excitation spectra of the samples, it was demonstrated that the optical properties of the nano‐MEH–PPV arrays were obviously different from those of MEH–PPV films. The conformations of the MEH–PPV chains in the nanopores, films, and solutions and their effects on the optical properties were examined. It was determined experimentally that the conformations of the MEH–PPV chains in the solutions were maintained in the nano‐MEH–PPV arrays. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3037–3041, 2006     

Effects of water on epoxy cure kinetics and glass transition temperature utilizing molecular dynamics simulations

Effects of water on epoxy cure kinetics are investigated. Experimental tests show that absorbed water in an uncured bisphenol‐F/diethyl‐toluene‐diamine epoxy system causes an increase in cure rate at low degrees of cure and a decrease in cure rate at high degrees of cure. Molecular simulations of the same epoxy system indicate that the initial increase in cure rate is due to an increase in molecular self‐diffusion of the epoxy molecules in the presence of water. Effects of water on the glass transition temperature (T_g) of the crosslinked thermoset are also studied. Both experiments and simulations show that water decreases T_g. Both types of results indicate that T_g effects are small below 1% water by weight, but that T_g depression occurs much quickly with increasing water content above 1%. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017 , 55, 1150–1159     

Effects of Moisture on the Mechanical Properties of Microcrystalline Cellulose and the Mobility of the Water Molecules as Studied by the Hybrid Molecular Mechanics–Molecular Dynamics Simulation Method

A hybrid molecular mechanics–molecular dynamics simulation method has been performed to study the effects of moisture content on the mechanical properties of microcrystalline cellulose (MCC) and the mobility of the water molecules. The specific volume and diffusion coefficient of the water increase with increasing moisture content in the range studied of 1.8–25.5 w/w%, while the Young's modulus decreases. The simulation results are in close agreement with the published experimental data. Both the bound scission and free‐volume mechanisms contribute to the plasticization of MCC by water. The Voronoi volume increases with increasing moisture content. It is related to the free volume and the increase enhances the mobility of the water molecules and thus increases the coefficient of diffusion of the water. Moreover, with increasing moisture content, the hydrogen bonding per water molecule between MCC–water molecules decreases, thus increasing the water mobility and number of free water molecules. © 2019 The Authors. Journal of Polymer Science Part B: Polymer Physics published by Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 454–464     

Thermal transitions and structure of epoxy networks based on α, ω‐diamino terminated poly(propylene oxide)‐block‐poly(ethylene oxide)‐block‐poly(propylene oxide) swollen in water

Thermal transitions in epoxy networks prepared by reaction of α, ω‐diamino terminated poly(propylene oxide)‐block‐poly(ethylene oxide)‐block‐poly(propylene oxide) and diglycidyl ether of brominated Bisphenol A, swollen in water, were studied by differential scanning calorimetry (DSC) in a broad temperature range (from ?100 °C to 20 °C). Networks of two different values of initial molar ratio of amino and epoxy groups were prepared, r (r = 1.00, 2.00), and swollen with different amounts of water up to equilibrium concentration values. The qualitatively different kinds of experimental thermograms have been obtained for two networks and classified according to the amount of water in the sample on the basis of the phase diagram of the system. Also, the concentration dependence of the curves in this diagram (glass transition, melting, and crystallization) as well as the fraction of noncrystallizable water supply some information about the morphology of the system. In this sense, the existence of a microphase separated structure of swollen networks is suggested. The structure consists of hydrophilic and hydrophobic domains and depends on the initial molar ratio of the reactive groups. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 699–708, 2005     

Probing the molecular interactions in the diffusion of water through epoxy and epoxy–bismaleimide networks

Fourier transform infrared spectroscopy in the near‐infrared (NIR) frequency range was used to investigate the molecular interactions occurring between absorbed water molecules and networks based on a tetrafunctional epoxy resin. One of these networks was a typical formulation containing 4,4′‐diamino diphenylsulfone as a hardener, and the other was a modified resin containing 4,4′‐bismaleimide‐diphenylmethane (BMI) as a coreactive monomer. Molecular spectroscopy analysis confirmed the existence of mobile water localized into network defects (microvoids) that did not interact with the networks and water molecules bound to the networks through hydrogen‐bonding interactions. In the BMI‐containing system, the fraction of bound water decreased significantly with respect to the unmodified epoxy resin. This was a relevant result because the bound water was primarily responsible for the plasticization of the network and for the consequent worsening of mechanical performance. Water diffusion was investigated with gravimetric sorption measurements and time‐resolved Fourier transform NIR spectroscopy measurements. These showed that the presence of BMI decreased the water uptake at equilibrium, enhanced the diffusivity, and reduced the activation energy for diffusion. A dual‐mode model for diffusion was found to be suitable for accurately describing the mass‐transport process in both investigated systems. The results of the model simulations allowed us to estimate the ratio of free and bound water, which was in good agreement with that obtained from the spectroscopic analysis. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 922–938, 2002     

Study of the photodegradation of epoxy polymers with slow positron annihilation spectroscopy

The photodegradation of an amine‐cured epoxy coating after exposure to accelerated UV‐340 and UV‐313 irradiation was investigated with an atomic‐level technique, positron annihilation spectroscopy (PAS), which detected and characterized the free volumes and defects as a function of the depth. Significant changes in the subnanometer defect parameters S and W were observed as a function of the exposure time near the surface. This was interpreted as due to a loss of the free volume and hole fraction resulting from photodegradation. A dead layer near the surface, resulting from UV irradiation from the surface up to a thickness of 0.4 μm, at which there was nearly no positronium formation, was observed. Correlations between physical defects from PAS in terms of the free volumes and chemical defects from electron spin resonance spectroscopy in terms of free radicals and chemical structural changes measured by ultraviolet–visible and Fourier transform infrared spectroscopy were established. A high sensitivity of PAS for detecting the early stage of degradation, on the order of hours for UV‐313 and on the order of days for UV‐340 irradiation, was observed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2441–2459, 2004     

Transport properties of small molecules in zwitterionic polymers

Despite great interests in using zwitterionic polymers for membrane surface modification to enhance antifouling properties, there lacks fundamental understanding of the relationship between polymer structure and water/salt separation properties. In this study, two series of zwitterionic polymers were prepared from sulfobetaine methacrylate and 2‐methacryloyloxyethyl phosphorylcholine. Both are crosslinked by poly(ethylene glycol) diacrylate (PEGDA). These copolymers were thoroughly characterized in terms of sol‐gel fraction, density, glass transition temperature, contact angle, water and salt transport properties, and pure‐gas permeability. Interestingly, the zwitterionic polymers exhibit water sorption and permeability similar to noncharged poly(ethylene glycol)‐based materials. These zwitterionic polymers exhibit lower NaCl diffusivity and permeability and thus higher water/NaCl selectivity than the non‐charged PEG‐based materials at similar water volume fractions, demonstrating their promise for membrane surface modification for desalination and wastewater treatment. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 1924–1934     

Contributions of side groups to the water diffusion in cured epoxy resins (2) study on physical aging

Novolac epoxy resins cured with novolac resin, novolac acetate resin, novolac butyrate resin, and novolac phenylacetate resin named as EP, EPA, EPB, and EPP, respectively, were prepared. Their physical aging behavior at a T_g‐30 °C (30 °C below glass‐transition temperature) was examined by positron annihilation lifetime spectroscopy and differential scanning calorimetry. The ortho‐positronium annihilation lifetime τ₃ variation extent of EP is less apparent than that of the other three esterified samples during physical aging. The time dependence of ops intensity I₃ agreed with the Kohlrausch‐Williams‐Watts (KWW) equation. The relaxation time (τ₀) and nonexponential parameter were calculated. The free volume and enthalpy relaxation rate characterized by the reciprocal of τ₀ and ?ΔH/?logt, respectively, exhibit the same order—EPP > EPB > EPA > EP. These results suggest that the extend and rate of relaxation are not only related to the frozen free volume produced by quenching but also significantly influenced by segmental mobility of the network that attributed to the side‐group flexibility and their interaction with networks. This work also supports the fact that side‐group flexibility and the free‐volume fraction and distribution act in concert to control the water‐diffusion behavior in epoxy networks. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1135–1142, 2003     

Preparation,thermal properties,and flame retardance of epoxy–silica hybrid resins

A novel epoxy system was developed through the in situ curing of bisphenol A type epoxy and 4,4′‐diaminodiphenylmethane with the sol–gel reaction of a phosphorus‐containing trimethoxysilane (DOPO–GPTMS), which was prepared from the reaction of 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO) with 3‐glycidoxypropyltrimethoxysilane (GPTMS). The preparation of DOPO–GPTMS was confirmed with Fourier transform infrared, ¹H and ³¹P NMR, and elemental analysis. The resulting organic–inorganic hybrid epoxy resins exhibited a high glass‐transition temperature (167 °C), good thermal stability over 320 °C, and a high limited oxygen index of 28.5. The synergism of phosphorus and silicon on flame retardance was observed. Moreover, the kinetics of the thermal oxidative degradation of the hybrid epoxy resins were studied. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2354–2367, 2003     

Micellar structure and mechanical properties of block copolymer‐modified epoxies

Amphiphilic block copolymers provide a unique means for toughening epoxy resins because they can self‐assemble into different inclusion shapes before epoxy curing. The two examples reported here are spherical micelles and vesicles, which form in blends containing epoxy and symmetric or asymmetric poly(ethylene oxide)–poly(ethylene‐alt‐propylene) (PEO–PEP) block copolymer with PEO volume fractions of 0.5 and 0.26, respectively. The vesicles and spherical micelles were characterized by transmission electron microscopy and small‐angle X‐ray scattering (SAXS), respectively. SAXS data from the spherical micelles were fit to the Percus–Yevick model for a liquid‐like packing of spheres with hard‐core interactions. Mechanical properties of spherical‐micelle‐modified and vesicle‐modified epoxies in the dilute limit are compared. The glass‐transition temperature and Young's (storage) modulus were tested with dynamic mechanical spectroscopy, and compact‐tension experiments were performed to determine the critical plane‐strain energy release rate for fracture. Vesicles were most effective in improving the epoxy fracture resistance. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2996–3010, 2001     

Structural data on the packing of poly(ester amide)s derived from glycine,hexanediol, and odd‐numbered dicarboxylic acids

The crystalline structure of a series of Poly(ester amide)s derived from glycine, hexanediol, and odd‐numbered dicarboxylic acids has been studied using transmission electron microscopy and X‐ray diffraction. Polymers crystallize in an orthorhombic lattice with parameters a = 4.80 Å, b = 22.68 Å, and c in the 45–55 Å interval, depending on the number of methylenes of the chemical repeat unit. The structure of the glutaric derivative can be interpreted as a singular packing of six hydrogen‐bonded sheets. Amide and ester interactions between neighboring layers favor two different sheet arrangements that give rise to the observed superstructure. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2521–2533, 1999     

An infrared study of the effects of hydration on cation‐loaded nafion thin films

We explore the effects of hydration on the vibrational spectra of cation‐exchanged Nafion thin films. In addition to the initial H⁺ form of the membrane, the cations selected for study include: Na⁺, NH, tetramethylammonium, tetrabutylammonium, hexadecyltrimethylammonium, and tris(2,2′‐bipyridine)osmium(II). A flow cell is used to follow the changes occurring in a 1000‐Å film in response to variations in the humidity of a nitrogen purge gas flowing through the cell. The structural changes occurring due to the binding of water to these cation‐exchanged membranes is followed across a broad range of water contents with IR difference spectroscopy. Our results demonstrate a complex role for water in mediating the polyanion–cation interactions. Side‐chain reconstructions may play an important role in the ion‐binding and transport properties of the ionomer domains. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1512–1520, 2000     

Measurement and prediction of solubilities and diffusion coefficients of carbon dioxide in starch–water mixtures at elevated pressures

The solubility and diffusion coefficient of carbon dioxide in intermediate‐moisture starch–water mixtures were determined both experimentally and theoretically at elevated pressures up to 16 MPa at 50 °C. A high‐pressure decay sorption system was assembled to measure the equilibrium CO₂ mass uptake by the starch–water system. The experimentally measured solubilities accounted for the estimated swollen volume by Sanchez–Lacombe equation of state (S‐L EOS) were found to increase almost linearly with pressure, yielding 4.0 g CO₂/g starch–water system at 16 MPa. Moreover, CO₂ solubilities above 5 MPa displayed a solubility increase, which was not contributed by the water fraction in the starch–water mixture. The solubilities, however, showed no dependence on the degree of gelatinization (DG) of starch. The diffusion coefficient of CO₂ was found to increase with concentration of dissolved CO₂, which is pressure‐dependent, and decrease with increasing DG in the range of 50–100%. A free‐volume‐based diffusion model proposed by Areerat was employed to predict the CO₂ diffusivity in terms of pressure, temperature, and the concentration of dissolved CO₂. S‐L EOS was once more used to determine the specific free volume of the mixture system. The predicted diffusion coefficients showed to correlate well with the measured values for all starch–water mixtures. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 607–621, 2006     

Intermolecular interactions on amine‐cured epoxy matrices with different crosslink densities. Influence on the hole and specific volumes and the mechanical behavior

The architecture of an epoxy matrix was modified by curing the resin with mono‐/diamine mixtures having identical chemical structures. Both hole volume and specific volume variations were studied by positron annihilation lifetime spectroscopy and pressure‐volume‐temperature/density measurements, respectively. The average hole volume of the networks at room temperature slightly increased when the monoaminic chain extender content increased. The increment in the intermolecular interactions between functional groups of the networks chains, due to the less hindered nitrogen introduced by the monoamine, appears to be the responsible for the observed behavior. Besides, only small variations on the specific volume were observed on increasing the monoamine content, which points out that for a cured epoxy system, the chemical structure of the curing agent is mainly responsible for chain packing in the networks. On the other hand, intermolecular interactions between chains were considered as the key factor for fixing stiffness and strength. Thus, it was observed that the increase of the intermolecular interactions with the monoamine content produced a decrease in the sub‐T_g small‐range cooperative motions, which increased the low‐deformation mechanical properties at temperatures between β and α relaxations. This conclusion could be applied to previous investigations with epoxy matrices not fully crosslinked (nonstoichiometric or noncompletely cured formulations). Finally, it was found that fracture properties do not significantly depend either on the hole volume or on the intermolecular interactions. Fracture properties are more dependent on the crosslink density and the glass transition temperature. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1240–1252, 2009     

Current Rectification in Temperature‐Responsive Single Nanopores

Herein we demonstrate a fully abiotic smart single‐nanopore device that rectifies ionic current in response to the temperature. The temperature‐responsive nanopore ionic rectifier can be switched between a rectifying state below 34 °C and a non‐rectifying state above 38 °C actuated by the phase transition of the poly(N‐isopropylacrylamide) [PNIPAM] brushes. On the rectifying state, the rectifying efficiency can be enhanced by the dehydration of the attached PNIPAM brushes below the LCST. When the PNIPAM brushes have sufficiently collapsed, the nanopore switches to the non‐rectifying state. The concept of the temperature‐responsive current rectification in chemically‐modified nanopores paves a new way for controlling the preferential direction of the ion transport in nanofluidics by modulating the temperature, which has the potential to build novel nanomachines with smart fluidic communication functions for future lab‐on‐chip devices.     

A convection–diffusion porous media model for moisture transport in polymer composites: Model development and validation

Moisture may cause many detrimental effects to polymers and their composites, thus inhibiting the applications of polymeric materials in hot and humid environments. In this article, a convection–diffusion porous media model is derived to better characterize rapid moisture transport in polymer composites at high temperatures. The model considers both continuum diffusion in solid and high‐pressure convection taking place in the pore network. Coupling of convection and diffusion is achieved by combining the law of conservation of mass, Darcy's law, the liquid–vapor chemical equilibrium, and the ideal gas law. The presented model is validated by conducting experimental tests on an epoxy compound. It is found that the proposed convection–diffusion model is more effective than diffusion‐only and convection‐only models for interpreting rapid desorption tests at high temperatures. A numerical study is also performed to predict maximum vapor pressure during a rapid heating process. Vapor pressure is found to be as high as 6.5 MPa at a heating rate of 10 K/s. It is concluded that the convection–diffusion model is able to capture both vapor dynamics and diffusion mechanism in porous polymeric materials, and can be potentially used to further investigate polymer‐moisture interactions. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1440–1449     

Nanostructured epoxy thermoset templated by an amphiphilic PCL‐b‐PES‐b‐PCL triblock copolymer

The PCL‐b‐PES‐b‐PCL triblock copolymer is used to incorporate into epoxy resin when the blends are cured with 4,4'‐diaminodiphenylsulfone (DDS) to afford the nanostructured epoxy thermosets. The differential scanning calorimetry (DSC) and Fourier transform‐infrared spectroscopy (FT‐IR) show that the nanostructured PCL‐b‐PES‐b‐PCL thermosets are accessed through the formation of the intermolecular hydrogen bonding interactions. The nanostructures are further evidenced by means of small‐angle X‐ray scattering (SAXS) and transmission electron microscopy (TEM). By considering the miscibility of the subchains of block copolymer with epoxy before and after the curing reaction, it is judged that the formation of the nanostructures follows the mechanism of reaction‐induced microphase separation. It is noted that the epoxy resin is significantly toughened in terms of the measurement of critical stress field intensity factor (K_IC). © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 424–432