Probing multiple melting behaviors in poly(ethylene naphthalene 2,6‐dicarboxylate) with different thermal histories by simultaneous wide‐angle and small‐angle X‐ray scattering

A simultaneous wide‐angle and small‐angle X‐ray scattering study of two poly(ethylene naphthalene 2,6‐dicarboxylate) samples crystallized from the glassy state at different annealing temperatures for different annealing times was carried out with synchrotron radiation. Either single or dual melting was induced in the samples, as confirmed by differential scanning calorimetry (DSC). The correlation function and interface distribution function were calculated to evaluate microstructural parameters such as the long spacing, the thickness of the amorphous and crystalline phases, and the width of the size distributions. The sample with dual melting behavior exhibited an abrupt increase of all microstructural parameters at temperatures above the melting of the lowest endotherm, whereas the sample revealing a single melting endotherm did not show such a sudden change. This finding agrees with the concept that the appearance of two melting peaks in DSC traces can be explained by the dual lamellar stacking model. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 881–894, 2001     

A differential scanning calorimetry study on poly(ethylene terephthalate) isothermally crystallized at stepwise temperatures: multiple melting behavior re-investigated

The multiple melting behavior of poly(ethylene terephthalate) (PET) was investigated with differential scanning calorimetry (DSC) by examining PET samples having been subjected to special schemes of crystallization and annealing treatment at multiple descending temperatures. Upon such step-wise annealing in decreasing temperatures, the existence of doublet melting peaks in addition to a series of multiple minor peaks in the PET has been demonstrated using carefully designed thermal schemes. Using the Hoffman theory, multiple lamellae populations, might be suggested to be simultaneously present in the PET subjected to such thermal treatments. However, direct experimental evidence has yet to be provided. The low-temperature minor crystals simply melt during normal scanning without having time enough to reorganize into higher-melt crystals. Nevertheless, the effect of scanning on non-isothermal crystallization does exist but is primarily confined to the temperature range much below the main melting region where the crystallization of polymer chains can progress at a reasonable rate. At higher temperatures near the main melting region, annealing for extended times is required in order to result in relative changes of the melting endotherms of the upper and lower peaks in the main melting doublet. In all we have shown that interpretations of the multiple melting phenomenon in semicrystalline polymers can be better refined.     

Relaxation behavior of poly(ethylene terephthalate)/poly(ethylene naphthalene 2,6‐dicarboxylate) blends prepared by cryogenic blending

A method including cryogenic grinding, melt pressing from the molten state, and quenching was used to prepare blends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalene 2,6‐dicarboxylate) (PEN) in which the two phases were highly dispersed. The effect of melt‐pressing times on the thermal properties and relaxation behavior of PET/PEN films were characterized with differential scanning calorimetry and dielectric spectroscopy. For short melt‐pressing times, two glass‐transition, two crystallization, and two melting peaks were observed, indicating the presence of PET‐rich and PEN‐rich phases in these blends. Longer melt‐pressing times revealed a single glass transition and a single α‐relaxation process, showing that PET–PEN block copolymers were likely to be formed during the melt pressing. The experimental findings were examined in terms of the transesterification reactions between the blend components, as revealed by ¹H NMR measurements. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2570–2578, 2002     

X‐ray studies on the double melting behavior of poly(butylene terephthalate)

The double melting behavior of poly(butylene terephthalate) (PBT) was studied with differential scanning calorimetry (DSC) and wide‐angle X‐ray analysis. DSC melting curves of melt‐crystallized PBT samples, which we prepared by cooling from the melt (250 °C) at various cooling rates, showed two endothermic peaks and an exothermic peak located between these melting peaks. The cooling rate effect on these peaks was investigated. The melt‐crystallized PBT sample cooled at 24 K min^?1 was heated at a rate of 1 K min^?1, and its diffraction patterns were obtained successively at a rate of one pattern per minute with an X‐ray measurement system equipped with a position‐sensitive proportional counter. The diffraction pattern did not change in the melting process, except for the change in its peak height. This suggests that the double melting behavior does not originate from a change in the crystal structure. The temperature dependence of the diffraction intensity was obtained from the diffraction patterns. With increasing temperature, the intensity decreased gradually in the low‐temperature region and then increased distinctly before a steep decrease due to the final melting. In other words, the temperature‐dependence curve of the diffraction intensity showed a peak that is interpreted as proof of the recrystallization in the melting process. The peak temperature was 216 °C. The temperature‐dependence curve of the enthalpy change obtained by the integration of the DSC curve almost coincided with that of the diffraction intensity. The double melting behavior in the heating process of PBT is concluded to originate from the increase of crystallinity, that is, recrystallization. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2005–2015, 2001     

Wide‐angle X‐ray diffraction and differential scanning calorimetry study of the crystallization of poly(ethylene naphthalate), poly(butylene naphthalate), and their copolymers

The crystallization behavior of a series of poly(ethylene‐co‐butylene naphthalate) (PEBN) random copolymers was studied. Wide‐angle X‐ray diffraction (WAXD) patterns showed that the crystallization of these copolymers could occur over the entire range of compositions. This resulted in the formation of poly(ethylene naphthalate) or poly(butylene naphthalate) crystals, depending on the composition of the copolymers. Sharp diffraction peaks were observed, except for 50/50 PEBN. Eutectic behavior was also observed. This showed isodimorphic cocrystallization of the PEBN copolymers. The variation of the enthalpy of fusion of the copolymers with the composition was estimated. The isothermal and nonisothermal crystallization kinetics were studied. The crystallization rates were found to decrease as the comonomer unit content increased. The tensile properties were also measured and were found to decrease as the butylene naphthalate content of the copolymers increased. For initially amorphous specimens, orientation was proved by WAXD patterns after drawing, but no crystalline reflections were observed. However, the fast crystallization of drawn specimens occurred when they were heated above the glass‐transition temperature. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 843–860, 2004     

Small‐angle X‐ray scattering and polymer melting: A model study

Small‐angle X‐ray scattering (SAXS) gives information on lamellar stacks in semicrystalline polymers. SAXS experiments have been used to follow the melting transition that occurs over a temperature range of 10 °C or more. One common feature is the increase in the average period by 50–100% during the melting process, a change that is often attributed to sequential melting of crystals in the lamellar stack. A quantitative treatment shows that the scattering experiment indicates only the original period, not the average period that increases throughout sequential melting. With this model, I discuss the relation between structural parameters of the melting structure and quantities derived from the SAXS intensity, the correlation function, and the interface distribution function. Uncertainties persist in our understanding of polymer melting. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2454–2460, 2001     

Temperature‐modulated differential scanning calorimetry studies on the origin of double melting peaks in isothermally melt‐crystallized poly(L‐lactic acid)

In this work, the melting behaviors of nonisothermally and isothermally melt‐crystallized poly(L ‐lactic acid) (PLLA) from the melt were investigated with differential scanning calorimetry (DSC) and temperature‐modulated differential scanning calorimetry (TMDSC). The isothermal melt crystallizations of PLLA at a temperature in the range of 100–110 °C for 120 min or at 110 °C for a time in the range of 10–180 min appeared to exhibit double melting peaks in the DSC heating curves of 10 °C/min. TMDSC analysis revealed that the melting–recrystallization mechanism dominated the formation of the double melting peaks in PLLA samples following melt crystallizations at 110 °C for a shorter time (≤30 min) or at a lower temperature (100, 103, or 105 °C) for 120 min, whereas the double lamellar thickness model dominated the formation of the double melting peaks in those PLLA samples crystallized at a higher temperature (108 or 110 °C) for 120 min or at 110 °C for a longer time (≥45 min). © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 466–474, 2007     

Influence of additives on the crystal structure and melting behavior of poly(ethylene‐2,6‐naphthalene dicarboxylate)

The influence of additives on the crystal modification and melting behavior of poly(ethylene‐2,6‐naphthalene dicarboxylate) (PEN) was investigated with wide‐angle X‐ray diffraction and differential scanning calorimetry (DSC). The addition of a nucleating promoter, Ceraflour 993, had no effect on the crystal modification and melting behavior of PEN crystallized under all chosen experimental conditions. However, the addition of a nucleating agent, sodium benzoate (SB), did affect the crystal modification and melting behavior of PEN when PEN/SB was crystallized at a higher temperature, but not at a lower temperature. A mixture of α and β modifications of PEN was obtained, and an overlapped dual melting peak was observed in DSC curves when PEN was crystallized at a higher temperature in the presence of SB, instead of a single crystal form and a single melting peak for the crystallization of pure PEN. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 296–301, 2004     

Differential scanning calorimetry,small‐angle X‐ray scattering,and wide‐angle X‐ray scattering on homogeneous and heterogeneous ethylene‐α‐copolymers

The objective of this work was to use both X‐ray and differential scanning calorimetry techniques in a comparative study of the lamellar and crystalline structures of heterogeneous and homogeneous ethylene‐α‐copolymers. The samples differed in the comonomer type (1‐butene, 1‐hexene, 1‐octene, and hexadecene), comonomer content, and catalyst used in the polymerizations. Step crystallizations were performed with differential scanning calorimetry, and the crystallinity and lamellar thicknesses of the different crystal populations were determined. Wide‐angle X‐ray scattering was used to determine crystallinities, average sizes of the crystallites, and dimensions of the orthorhombic unit cell. The average thickness, separation of the lamellae, and volume fractions of the crystalline phase were determined by small‐angle X‐ray scattering (SAXS). The results revealed that at densities below 900 kg/m³, polymers were organized as poorly organized crystal bundles. The lamellar distances were smaller and the lamellar thickness distributions were narrower for the homogeneous ethylene copolymers than for the heterogeneous ones. Step‐crystallization experiments by SAXS demonstrated that the long period increased after annealing. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 1860–1875, 2001     

Phase behavior and structure development in extruded poly(ethylene terephthalate)/poly(ethylene‐2,6‐naphthalate) blend

Liquid–liquid phase separation and subsequent homogenization during annealing in an extruded poly(ethylene terephthalate) (PET)/poly(ethylene‐2,6‐naphthalate) (PEN) blend were investigated with time‐resolved light scattering and optical microscopy. In the initial stage, the domain structure was developed by demixing via spinodal decomposition. In the later stage, the blend was homogenized by transesterification between the two polyesters. The crystallization rate depended on the sequence distribution of polymer chains, which was determined by the level of transesterification rather than the composition change of separated phases. When the crystallization of PEN preceded that of PET, PEN showed a higher melting point. However, when the crystallization rate of PEN was slower than that of PET, the previously formed PET crystals suppressed the crystallization of PEN, causing the coarse crystalline structure of PEN to have a lower melting point. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2625–2633, 2000     

Thermal analysis of the multiple melting behavior of poly(butylene succinate‐co‐adipate)

The melting behavior of poly(butylene succinate‐co‐adipate) (PBSA) isothermally crystallized from the melt was investigated by differential scanning calorimetry. Triple, double, or single melting endotherms were observed in subsequent heating scan for the samples isothermally crystallized at different temperatures. These endothermic peaks were labeled as I, II, and III for low‐, middle‐, and high‐temperature melting endotherms, respectively. The independence of endotherm III to the crystallization temperature, the existence of an exothermic crystallization peak just below the endotherm III, and the heating rate dependence of endotherm III indicated that endotherm III was due to the remelting of recrystallized lamellar during a heating scan. The influence of crystallization time on the melting behavior of PBSA showed that endotherms II and III developed prior to endotherm I; endotherm III developed rather simultaneously with endotherm II. Further investigation showed that the peak temperature of endotherm I increased linearly with the logarithm of the crystallization time. It suggested that endotherm II was attributed to the melting of the primary lamellae, while endotherm I was due to the melting of secondary lamellae. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 3077–3082, 2005     

Thermal memory of poly(3‐hydroxybutyrate) using temperature‐modulated differential scanning calorimetry

The influence of thermal history on morphology, melting, and crystallization behavior of bacterial poly(3‐hydroxybutyrate) (PHB) has been investigated using temperature‐modulated DSC (TMDSC), wide‐angle X‐ray diffraction (WAXRD) and polarized optical microscopy (POM). Various thermal histories were imparted by crystallization with continuous and different modulated cooling programs that involved isoscan and cool–heat segments. The subsequent melting behavior revealed that PHB experienced secondary crystallization during heating and the extent of secondary crystallization varied with the cooling treatment. PHB crystallized under slow, continuous, and moderate cooling rates were found to exhibit double melting behavior due to melting of TMDSC scan‐induced secondary crystals. PHB underwent considerable secondary crystallization/annealing that took place under modulated cooling conditions. The overall melting behavior was interpreted in terms of recrystallization and/or annealing of crystals. Interestingly, the PHB analyzed by temperature modulation programs showed a broad exotherm before the melting peak in the nonreversing heat capacity curve and a multiple melting reversing curve, verifying that the melting–recrystallization and remelting process was operative. WAXRD and POM studies supported the correlations from DSC and TMDSC results. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 70–78, 2006     

Simultaneous wide‐angle X‐ray diffraction and differential scanning calorimetry analysis of the melting and recrystallization behavior of polyethylene and isotactic polypropylene containing cyclopentane units in the main chain

The melting and crystallization behavior of polyethylene and isotactic polypropylene containing 1,2‐ or 1,3‐disubstituted cyclopentane units in the main chain has been studied with simultaneous wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry. For the ethylene‐based copolymers, the position of a reflection peak in the WAXD patterns shifts to a low angle with the increasing acquired temperature. The temperature dependence on the axial length of the crystal lattice is more marked in the copolymers forming orthorhombic crystals (containing 1,2‐cyclopentane or 5.6 mol % 1,3‐cyclopentane units) than in those forming hexagonal crystals (containing 8.1 mol % 1,3‐cyclopentane units). For the isotactic propylene‐based copolymers, the position of the reflection peaks in the WAXD patterns is independent of the acquired temperature. The proportion of the γ form in the copolymer containing the 1,2‐cyclopentane units is higher than that in the copolymers containing the 1,3‐cyclopentane units. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1457–1465, 2004     

Enthalpy of fusion of poly(3‐hexylthiophene) by differential scanning calorimetry

The enthalpy of fusion for a perfect, infinite poly(3‐hexylthiophene) (P3HT) crystal () must be known to evaluate the absolute crystallinity of P3HT. This value, however, is still ambiguous as different values have been reported using various experimental techniques. Here, we extrapolate the enthalpy of fusion for extended chain crystals of oligomeric P3HT to infinite molecular weight and obtain a value of 42.9 ± 2 J/g employing differential scanning calorimetry with a correction based on grazing incidence small angle X‐ray scattering data. Also, we define the onset of chain folding within P3HT crystallites at a chain length of 5 Kuhn segments. Knowledge of allows calculation of P3HT percent crystallinity in thin films for applications such as organic field effect transistors and solar cells. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 1469–1475     

Differential scanning calorimetry study on thermal behaviors of freeze‐dried poly(L‐lactide) from dilute solutions

Glass transition, cold crystallization, and melting of freeze‐dried poly(L‐lactide) (PLLA) prepared from dilute 1,4‐dioxane solutions were investigated by differential scanning calorimetry (DSC). Conventional DSC measurements of heating scans revealed that freeze‐dried PLLA prepared from a 0.07 wt % solution undergoes a two‐step cold crystallization (or reorganization) with a lower exotherm appearing at about 78 °C and with a higher broad exotherm between 110–155 °C. The peak temperature of the former exotherm is about 50 K lower than that observed for a reference bulk sample. Step‐scan mode DSC, which provides information essentially equivalent to that obtained from the temperature‐modulated DSC, revealed that the glass‐transition temperature is about 6 K lower than that of the reference bulk. These findings suggest enhanced chain mobility for freeze‐dried PLLA. Freeze‐dried PLLA that crystallized at 80 °C for 40 min was revealed to contain a rather large amount of rigid amorphous material (42%). © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 115–124, 2005     

Real‐time SAXS and WAXS study of the multiple melting behavior of poly(ε‐caprolactone)

The multiple melting behavior of poly(ε‐caprolactone) (PCL) was investigated by real‐time small angle X‐ray scattering (SAXS) and wide angle X‐ray scattering (WAXS) measurements coupling with differential scanning calorimetry (DSC). Semicrystalline specimens prepared by a continuous cooling process showed lengthening of the Bragg period during the progress of double melting. A model of variable thickness of lamella was proposed to fit to the SAXS patterns and revealed that both the crystalline lamella and the amorphous layer contributed to the increase in Bragg period while the later dominated the contribution. The model of variable thickness although satisfied the SAXS data was unable to compromise the data from other probing tools. A modification of the model proposed that each lamella piling up to construct the stacks in the crystallites was itself nonuniform in thickness. The modification with the parallel occurrence of the mechanism of surface melting and crystallization successfully compromised the observations from SAXS, DSC, and optical microscopy and provided a new perspective for the explanation to lengthening of the Bragg period related to multiple melting behavior. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1777–1785, 2010     

Cocrystallization phenomena in piperazine‐based copolyamides as examined by differential scanning calorimetry,wide‐angle X‐ray diffraction,and solid‐state NMR

Copolyamides 2.14/piperazine.14 with variable built‐in ratios of 1,2‐ethylenediamine (1,2‐EDA) and piperazine (pip) were synthesized by solution polycondensation. The built‐in ratio of both diamine comonomers was determined with solution ¹³C NMR analysis. The gradual replacement of 1,2‐EDA units by cycloaliphatic pip units in polyamide 2.14 resulted in a progressively decreased melting (T_m) and crystallization temperature of the obtained copolyamides. Apparently, the T_m raising effect of the incorporation of rigid cycloaliphatic moieties is overruled by the simultaneous T_m reduction caused by a decreasing hydrogen‐bond density. Indications for cocrystallization of 2.14 and pip.14 repeating units were obtained by the thermal analysis of copolyamides 2.14/pip.14 and of a blend of both homopolyamides. A preliminary wide‐angle X‐ray diffraction study pointed to the same conclusion. Solid‐state NMR spectroscopy was used to investigate the influence of the composition on the percentage of the rigid phase of the copolyamides and delivered additional indications for cocrystallization. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2082–2094, 2003     

Online wide‐angle X‐ray diffraction/small‐angle X‐ray scattering measurements for the CO2‐laser‐heated drawing of poly(ethylene terephthalate) fiber

Fiber‐structure‐development in the poly(ethylene terephthalate) fiber drawing process was investigated with online measurements of wide‐angle and small‐angle X‐ray scattering with both a high‐luminance X‐ray source and a CO₂‐laser‐heated drawing system. The intensity profile of the transmitted X‐ray confirmed the location of the neck‐drawing point. The diffraction images had a time resolution of several milliseconds, and this still left much room for improvement. Crystal diffraction appeared in the wide‐angle X‐ray images almost instantaneously about 20 ms after necking, whereas a four‐point small‐angle X‐ray scattering pattern appeared immediately after necking. With the elapse of time after necking, the four‐point scattering pattern changed into a meridional two‐point shape. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 1090–1099, 2005     

Small‐angle x‐ray scattering study of thermoreversible poly(vinyl chloride) gels

Poly(vinyl chloride) (PVC)/bis(2‐ethylhexyl)phthalate (DOP) gels were prepared at room temperature from tetrahydrofuran solutions of PVC and DOP. PVC/DOP gels of different molecular weights at various PVC concentrations (c) were investigated with small‐angle X‐ray scattering (SAXS). The mean distance between two neighboring inhomogeneities (D) and two characteristic lengths, the intrainhomogeneity distance (d₁) and interinhomogeneity distance (d₂), were evaluated from Bragg's law and the distance distribution function, respectively. Both D and d₂ can be expressed by a power‐law relation (e.g., D and d₂ ∝ c^?0.5). After a period of rapid cooling to 25 °C from the sol state, the structural evolution was examined with time‐resolved SAXS measurements. An Avrami analysis with the SAXS invariant data revealed that the growth kinetics of PVC/DOP gels was one‐dimensional growth from predetermined nuclei, regardless of c. These results suggest that the PVC/DOP gels are constructed from a fibrillar structure that forms gel structures at high concentrations or low temperatures. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2340–2350, 2001