Preparation and properties of new poly(amide‐imide)s based on 1,4‐bis(4‐trimellitimidophenoxy)naphthalene and aromatic diamines

A diimide dicarboxylic acid, 1,4‐bis(4‐trimellitimidophenoxy)naphthalene (1,4‐BTMPN), was prepared by condensation of 1,4‐bis(4‐aminophenoxy)naphthalene and trimellitic anhydride at a 1 : 2 molar ratio. A series of novel poly(amide‐imide)s (IIa–k) with inherent viscosities of 0.72 to 1.59 dL/g were prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid 1,4‐BTMPN with various aromatic diamines (Ia–k) in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. The poly(amide‐imide)s showed good solubility in NMP, N,N‐dimethylacetamide, and N,N‐dimethylformamide. The thermal properties of the obtained poly(amide‐imide)s were examined with differential scanning calorimetry and thermogravimetry analysis. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures in the range of 215 to 263°C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses at temperatures in the range of 538 to 569°C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s also is presented. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1–8, 2000     

Synthesis and characterization of poly(aryl amide imide)s derived from diphenyltrimellitic anhydride

The synthesis and characterization of a series of novel poly(aryl amide imide)s based on diphenyltrimellitic anhydride are described. The poly(aryl amide imide)s, having inherent viscosities of 0.39–1.43 dL/g in N-methyl-2-pyrrolidinone at 30°C, were prepared by polymerization with aromatic diamines in N,N-dimethylacetamide and subsequent chemical imidization. All the polymers were amorphous, readily soluble in aprotic polar solvents such as DMAC, NMP, dimethylsulfoxide, N,N-dimethylformamide, and m-cresol, and could be cast to form flexible and tough films. The glass transition temperatures were in the range of 284–366°C, and the temperatures for 5% weight loss in nitrogen were above 468°C. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 4541–4545, 1999     

Fluorinated polyamides and poly(amide imide)s based on 1,4‐bis(4‐amino‐2‐trifluromethylphenoxy)benzene,aromatic dicarboxylic acids,and various monotrimellitimides and bistrimellitimides: Syntheses and properties

A CF₃‐containing diamine, 1,4‐bis(4‐amino‐2‐trifluromethylphenoxy) benzene ( I ), was prepared from hydroquinone and 2‐chloro‐5‐nitrobenzotrifluoride. Imide‐containing diacids ( V _a–h and VI _a,b ) were prepared through the condensation reaction of amino acids, aromatic diamines, and trimellitic anhydride. Then, a series of soluble fluorinated polyamides ( VII _a–h ) and poly(amide imide)s ( VIII _a–h and X _a,b ) were synthesized from I with various aromatic diacids ( II _a–h ) and imide‐containing diacids ( V _a–h and VI _a,b ) via direct polycondensation with triphenyl phosphate and pyridine. The polyamides and poly(amide imide)s had inherent viscosities of 1.00–1.70 and 0.79–1.34 dL/g, respectively. All the synthesized polymers showed excellent solubility in amide‐type solvents such as N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide, and N‐dimethylformamide and afforded transparent and tough films via solvent casting. Polymer films of VII _a–h , VIII _a–h , and X _a,b had tensile strengths of 91–113 MPa, elongations to break of 8–40%, and initial moduli of 2.1–2.8 GPa. The glass‐transition temperatures of the polyamides and poly(amide imide)s were 254–276 and 255–292 °C, respectively, and the imide‐containing poly(amide imide)s had better thermal stability than the polyamides. The polyamides showed higher transparency and were much lighter in color than the poly(amide imide)s, and their cutoff wave numbers were below 400 nm. In comparison with isomeric IX _{c – h} , poly(amide imide)s VIII _c–h exhibited less coloring and showed lower yellowness indices. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3116–3129, 2004     

Influence of multiple stimuli on the lower critical solution temperature of new cationic poly(N‐acryloyl‐N′‐ethylpiperazine‐co‐N‐isopropylacrylamide) solutions

New multi‐stimuli responsive cationic copolymers based on N‐acryloyl‐N′‐ethyl piperazine (AcrNEP) and N‐isopropylacrylamide (NIPAM) were prepared by thermal free‐radical solution polymerization in dioxane at 75 °C. The chemical composition of the copolymers was determined by ¹H NMR spectroscopy and was found that the copolymers were slightly rich in NIPAM content than that of AcrNEP. The reactivity of the two monomers for the copolymerization reaction was evaluated by the extended Kelen‐Tüdös method. The distribution of monomer sequence in the copolymer chain was estimated using the terminal copolymerization model. The maximum tendency to alternation (～ 70%) was at 60 mol % of AcrNEP in the monomer feed. The copolymers were readily soluble in water at room temperature at all compositions and exhibited well‐defined lower critical solution temperature (LCST) phenomenon. The influence of various stimuli such as pH, temperature, simple inorganic salts, and surfactants on the LCST of the copolymers was studied in detail. Simple inorganic salts such as sodium chloride, sodium bromide, and sodium sulfate showed a salting‐out effect while sodium iodide showed a salting‐in effect. The salting‐out coefficient of the salts were calculated using the Sestchenow method, and the salting trend followed the order SO₄^2? > Cl^? > Br^? > I^?. The divalent salt was more effective in lowering the LCST than the monovalent salts. The cationic surfactant hexadecyl trimethylammonium bromide at concentrations above the critical micelle concentration caused a gradual increase in the LCST of the copolymer solutions. The intrinsic viscosity and light scattering behavior of the copolymers in water and in sodium chloride solutions were studied in detail. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 1175–1183     

Polymerization of 4,4′‐(hexafluoroisopropylidene)‐N,N′‐bis(phthaloyl‐L‐leucine) diacid chloride with aromatic diamines by microwave irradiation

A new facile and rapid polycondensation reaction of 4,4′‐(hexafluoroisopropylidene)‐N,N′‐bis(phthaloyl‐L‐leucine) diacid chloride (1) with several aromatic diamines, including benzidine (2a), 4,4′‐diaminodiphenyl methane (2b), 1,5‐diaminoanthraquinone (2c), 4,4′‐sulfonyldianiline (2d), 3,3′‐diaminobenzophenone (2e), P‐phenylenediamine (2f), 2,6‐diaminopyridine (2g), 4,4′‐diaminobenzophenone (2h), 2,4‐diaminotoluene (2i), and 4,4′‐diaminodiphenylether (2j), was developed with a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions proceeded rapidly compared to conventional solution polycondensation and finished within 12 min, producing a series of optically active poly(amide‐imide)s with quantitative yields and high inherent viscosities of 0.50–1.93 dL/g. All of the polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(amide‐imide)s are reported. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1154–1160, 2000     

New poly(amide–imide)s syntheses. XXIII. Synthesis and properties of poly(amide–imide)s derived from 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline and various bis(trimellitimide)s

A series of poly(amide–imide)s III_a–m containing flexible isopropylidene and ether groups in the backbone were synthesized by the direct polycondensation of 4,4′‐[1,4‐phenylenebis(isopropylidene‐1,4‐phenyleneoxy)]dianiline (PIDA) with various bis(trimellitimide)s II_a–m in N‐methyl‐2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents. The resulting poly(amide–imide)s had inherent viscosities in the range of 0.80–1.36 dL/g. Except for those from the bis(trimellitimide)s of p‐phenylenediamine and benzidine, all the polymers could be cast from DMAc into transparent and tough films. They exhibited excellent solubility in polar solvents. The 10% weight loss temperatures of the polymers in air and in nitrogen were all above 495°C, and their T_g values were in the range of 201–252°C. Some properties of poly(amide–imide)s III were compared with those of the corresponding poly(amide–imide)s V prepared from the bis(trimellitimide) of diamine PIDA and various aromatic diamines. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 69–76, 1999     

Synthesis of optically active poly(amide‐imide)s derived from N,N′‐(4,4′‐carbonyldiphthaloyl)‐bis‐L‐leucine diacid chloride and aromatic diamines by microwave radiation

3,3′,4,4′‐benzophenonetetracarboxylic dianhydride (4,4′‐carbonyldiphathalic anhydride) was reacted with L ‐leucine in a mixture of acetic acid and pyridine (3 : 2), and the resulting imide‐acid [N,N′‐(4,4′‐carbonyldiphthaloyl)‐bis‐L ‐leucine diacid] was obtained in quantitative yield. The compound was converted to the N,N′‐(4,4′‐carbonyldiphthaloyl)‐bis‐L ‐leucine diacid chloride by reaction with thionyl chloride. A new facile and rapid polycondensation reaction of this diacid chloride with several aromatic diamines such as 4,4′‐diaminodiphenyl methane, 2,4‐diaminotoluene, 4,4′‐sulfonyldianiline, p‐phenylenedi‐amine, 4,4′‐diaminodiphenylether, and m‐phenylenediamine was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as O‐cresol. The polymerization reactions proceeded rapidly compared with the conventional solution polycondensation and were completed within 6 min, producing a series of optically active poly(amide‐imide)s with a high yield and an inherent viscosity of 0.37–0.57 dL/g. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(amide‐imide)s are reported. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 177–186, 2001     

Synthesis and properties of organosoluble poly(amide‐imide)s with propeller‐shaped 1,1,1‐triphenylethane units in the main chain

A dicarboxylic acid {1,1‐bis[4‐(4‐trimellitimidophenoxy)phenyl]‐1‐phenylethane ( II )} bearing two performed imide rings was prepared from the condensation of 1,1‐bis[4‐(4‐aminophenoxy)phenyl]‐1‐phenylethane and trimellitic anhydride in a 1/2 molar ratio. A novel family of poly(amide‐imide)s with inherent viscosities of 0.83–1.51 dL/g was prepared by triphenyl phosphite‐activated polycondensation from the diimide‐diacid II with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidinone (NMP), pyridine, and calcium chloride. Because the 1,1,1‐triphenylethane group of II was unsymmetrical, most of the resulting polymers showed an amorphous nature and were readily soluble in polar solvents such as NMP and N,N‐dimethylacetamide. All the soluble poly(amide‐imide)s afforded tough, transparent, and flexible films, which had tensile strengths ranging from 88 to 102 MPa, elongations at break from 6 to 11%, and initial moduli from 2.23 to 2.71 GPa. The synthesized poly(amide‐imide)s possessed glass‐transition temperatures from 250 to 287 °C. The poly(amide‐imide)s exhibited excellent thermal stabilities and had 10% weight losses from 501 to 534 °C under a nitrogen atmosphere. A comparative study of some corresponding poly(amide‐imide)s is also presented. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 775–787, 2001     

Microwave‐assisted synthesis of optically active poly(amide imide)s derived from diacid chloride containing epiclon and L‐leucine with aromatic diamines

Epiclon [3a,4,5,7a‐tetrahydro‐7‐methyl‐5‐(tetrahydro‐2,5‐dioxo‐3‐furanyl)‐1,3‐isobenzofurandione or 5‐(2,5‐dioxotetrahydrofurfuryl)‐3‐methyl‐3‐cyclohexyl‐1,2‐dicarboxylic acid anhydride] was reacted with L ‐leucine in acetic acid, and the resulting imide acid ( 3 ) was obtained in a high yield. The diacid chloride ( 4 ) was obtained from its diacid derivative 3 by a reaction with oxalyl chloride in dry carbon tetrachloride. The polycondensation reaction of 4 with several aromatic diamines, such as 4,4′‐sulfonyldianiline, 4,4′‐diaminodiphenylmethane, 4,4′‐diaminodiphenylether, p‐phenylenediamine, m‐phenylenediamine, 2,4‐diaminotoluene, and 1,5‐diaminonaphthalene, was developed with a domestic microwave oven in the presence of a small amount of a polar organic medium such as N‐methylpyrrolidone. The polymerization reactions were also performed with two other methods: low‐temperature solution polycondensation in the presence of trimethylsilyl chloride and reflux conditions. A series of optically active poly(amide imide)s with moderate yields and inherent viscosities of 0.12–0.19 dL/g were obtained. All of these polymers were fully characterized by IR, elemental analysis, and specific rotation techniques. Some structural characterizations and physical properties of these optically active poly(amide imide)s are reported. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1077–1090, 2003     

Synthesis and characterization of fluorinated poly(amide imide)s derived from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and aromatic diamines

A series of fluorinated poly(amide imide)s were prepared from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and various aromatic diamines [3,3′,5,5′‐tetramethyl‐4,4′‐diaminediphenylmethane, α,α‐bis(4‐amino‐3,5‐dimethyl phenyl)‐3′‐trifluoromethylphenylmethane, 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene, 4‐(3′‐trifluoromethylphenyl)‐2,6‐bis(3′‐aminophenyl)pyridine, and 1,1‐bis(4′‐aminophenyl)‐1‐(3′‐trifluoromethylphenyl)‐2,2,2‐trifluoroethane]. The fluorinated poly(amide imide)s, prepared by a one‐step polycondensation procedure, had good solubility both in strong aprotic solvents, such as N‐methyl‐2‐pyrrolidinone, dimethylacetamide, dimethylformamide, dimethyl sulfoxide, and cyclopentanone, and in common organic solvents, such as tetrahydrofuran and m‐cresol. Strong and flexible polymer films with tensile strengths of 84–99 MPa and ultimate elongation values of 6–9% were prepared by the casting of polymer solutions onto glass substrates, followed by thermal baking. The poly(amide imide) films exhibited high thermal stability, with glass‐transition temperatures of 257–266 °C and initial thermal decomposition temperatures of greater than 540 °C. The polymer films also had good dielectric properties, with dielectric constants of 3.26–3.52 and dissipation factors of 3.0–7.7 × 10^?3, and acceptable electrical insulating properties. The balance of excellent solubility and thermal stability associated with good mechanical and electrical properties made the poly(amide imide)s potential candidates for practical applications in the microelectronics industry and other related fields. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1831–1840, 2003     

Synthesis and characterization of new soluble poly(amide‐imide)s derived from 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane

A series of new soluble poly(amide‐imide)s were prepared from the diimide‐dicarboxylic acid 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane with various diamines by direct polycondensation in N‐methyl‐2‐pyrrolidinone containing CaCl₂ with triphenyl phosphite and pyridine as condensing agents. All the polymers were obtained in quantitative yields with inherent viscosities of 0.52–0.86 dL · g^?1. The poly(amide‐imide)s showed an amorphous nature and were readily soluble in various solvents, such as N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide (DMAc), N,N‐dimethylformamide, pyridine, and cyclohexanone. Tough and flexible films were obtained through casting from DMAc solutions. These polymer films had tensile strengths of 71–107 MPa and a tensile modulus range of 1.6–2.7 GPa. The glass‐transition temperatures of the polymers were determined by a differential scanning calorimetry method, and they ranged from 242 to 279 °C. These polymers were fairly stable up to a temperature around or above 400 °C, and they lost 10% of their weight from 480 to 536 °C and 486 to 537 °C in nitrogen and air, respectively. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3498–3504, 2001     

Synthesis and characterization of new type soluble poly(amide–imide)s based on 6FDA imide modified polyterephthalamides

A series of new poly(amide–imide)s (PAIs, series III ) with good processability and characteristics was synthesized by utilizing organosoluble polyimide (PI, 6FDA–PI series) to improve poor‐solubility polyamide (PA, PTPA series), which used terephthalic acid (TPA) as a monomer. The III series PAIs were synthesized starting from the 2 : 1 molar ratio of aromatic diamines ( I ) and 6FDA to prepare imide ring‐preformed diamines ( II ) and then reacted with equimolar amount of TPA by direct polycondensation. Furthermore, by adjustment of the stoichiometry of the I , II, and TPA monomers, PAIs IV having various components were prepared. Most of the resulting PAIs having inherent viscosities between 0.70 and 1.74 dL/g were obtained in quantitative yields, and they were readily soluble in polar solvents such as N,N‐dimethylacetamide, N‐methyl‐2‐pyrrolidone, dimethylformamide, and dimethyl sulfoxide. All of the soluble PAIs afforded transparent, flexible, and tough films. The glass‐transition temperatures of PAIs III were in the range of 236–256 °C, and the 10% weight loss temperatures were recorded at 522–553 °C in nitrogen. The char yields of the III series polymers in nitrogen atmosphere were all higher than 56% even at 800 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 93–104, 2001     

Synthesis and properties of soluble and light‐colored poly(amide‐imide‐imide)s on the basis of tetraimide‐dicarboxylic acid condensed from 4,4′‐oxydiphthalic anhydride, 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane,and m‐aminobenzoic acid,and various aromatic diamines

A new type of tetraimide‐dicarboxylic acid ( I ) was synthesized starting from the ring‐opening addition of m‐aminobenzoic acid, 4,4′‐oxydiphthalic anhydride, and 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane at a 2:2:1 molar ratio in N‐methyl‐2‐pyrrolidone (NMP), followed by cyclodehydration to the diacid I . A series of soluble and light‐colored poly(amide‐imide‐imide)s ( III _a–j) was prepared by triphenyl phosphite‐activated polycondensation from I with various aromatic diamines ( II _a–j). All films cast from N,N‐dimethylacetamide (DMAc) had cutoff wavelengths shorter than 390 nm (374–390 nm) and b* values between 25.26 and 43.61; these polymers were much lighter in color than the alternating trimellitimide series. All of the polymers were readily soluble in a variety of organic solvents such as NMP, DMAc, N,N‐dimethylformamide, dimethyl sulfoxide, and even in less polar m‐cresol and pyridine. Polymers III _a–j afforded tough, transparent, and flexible films that had tensile strengths ranging from 96 to 118 MPa, elongations at break from 9 to 11%, and initial moduli from 2.0 to 2.5 GPa. The glass‐transition temperatures of the polymers were recorded at 240–268 °C. They had 10% weight loss at a temperature above 540 °C and left more than 55% residue even at 800 °C in nitrogen. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 707–718, 2002; DOI 10.1002/pola.10153     

Synthesis and characterization of novel,optically active poly(amide‐imide)s from N,N′‐(4,4′‐sulfonediphthaloyl)‐bis‐L‐phenylalanine diacid chloride and aromatic diamines under microwave irradiation

3,3′,4,4′‐Diphenylsulfonetetracarboxylic dianhydride was reacted with L ‐phenylalanine in acetic acid, and the resulting imide acid ( 3 ) was obtained in high yield. The diacid chloride ( 4 ) was obtained from its diacid derivative ( 3 ) by reaction with thionyl chloride. The polycondensation reaction of 4 with several aromatic diamines such as 4,4′‐sulfonyldianiline, 4,4′‐diaminodiphenyl methane, 4,4′‐diaminodiphenylether, p‐phenylenediamine, m‐phenylenediamine, 2,4‐diaminotoluene, and 1,5‐diaminonaphthalene was developed with a domestic microwave oven in the presence of trimethylsilyl chloride and a small amount of a polar organic medium such as o‐cresol. The polymerization reactions were also performed with two other methods: low‐temperature solution polycondensation in the presence of trimethylsilyl chloride and reflux conditions. A series of optically active poly(amide‐imide)s with moderate inherent viscosities of 0.21–0.42 dL/g were obtained in high yield. All of the aforementioned polymers were fully characterized by IR, ¹H NMR elemental analyses, and specific rotation techniques. Some structural characterizations and physical properties of these optically active poly(amide‐imide) s are reported. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3974–3988, 2003     

Synthesis and characterization of novel heat resistant poly(amide imide)s

A series of new poly(amide imide)s was prepared from new diacid containing sulfone, ether, amide and imide groups with various aromatic diamines. The diacid was synthesized via four steps, starting from reaction of 4-aminophenol with 4-nitrobenzoyl chloride in the presence of propylene oxide afforded N-(4-hydroxy phenyl)-4-nitrobenzamide. In the second step, reduction of nitro group resulted in preparation of 4-amino-N-(4-hydroxy phenyl) benzamide. In the next step for the preparation of diamine, the reaction of 4-amino-N-(4-hydroxy phenyl) benzamide with bis-(4-chlorophenyl) sulfone in the presence of K₂CO₃ was achieved. The prepared sulfone ether amide diamine was reacted with two moles of trimellitic anhydride to synthesize related sulfone ether amide imide diacid. The precursors and final monomer were characterized by FT-IR, H-NMR and elemental analysis. Direct polycondensation reaction of the sulfone ether amide imide diacid with different diamines in the presence of triphenyl phosphite afforded five different poly (sulfone ether amide imide amide)s. The obtained polymers were fully characterized and their physical properties including thermal behavior, thermal stability, solubility, and inherent viscosity were studied.     

Partially bio‐based poly(amide imide)s by polycondensation of aromatic diacylhydrazides based on lignin‐derived phenolic acids and aromatic dianhydrides: Synthesis,characterization, and computational studies

Two new bio‐based diacylhydrazide monomers, namely, 4,4′‐(propane‐1,3‐diylbis(oxy))bis(3‐methoxybenzohydrazide) and 4,4′‐(propane‐1,3‐diylbis(oxy))bis(3,5‐dimethoxybenzohydrazide) were synthesized starting from lignin‐derived phenolic acids, namely, vanillic acid and syringic acid. A series of poly(amide imide)s was synthesized by polycondensation of these diacylhydrazide monomers with commercially available aromatic dianhydrides. Poly(amide imide)s showed inherent viscosity in the range 0.44–0.56 dL g^?1 and exhibited good solubility in organic solvents. Poly(amide imide)s could be cast into transparent, flexible, and tough films from their N ,N‐dimethylacetamide solutions. Poly(amide imide)s showed 10% weight loss in the temperature range 340–364 °C indicating their good thermal stability. Glass transition temperature (T _g) of poly(amide imides)s were measured by DSC and DMA which were in the range 201–223 °C and 214–248 °C, respectively. The T _g values of poly(amide imide)s were dependent on the number methoxy substituents on aromatic rings of diacylhydrazide monomers. Molecular dynamics simulation studies revealed that chain rigidity is the dominant factor for observed trends in T _g. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 3636–3645     

Synthesis and properties of new soluble aromatic polyamides and polyimides on the basis of N,N′‐bis(3‐aminobenzoyl)‐N,N′‐diphenyl‐1,4‐phenylenediamine

A new N‐phenylated amide (N‐phenylamide) unit containing aromatic diamine, N,N′‐bis(3‐aminobenzoyl)‐N,N′‐diphenyl‐1,4‐phenylenediamine, was prepared by the condensation of N,N′‐diphenyl‐1,4‐phenylenediamine with 3‐nitrobenzoyl chloride, followed by catalytic reduction. Two series of organosoluble aromatic poly(N‐phenylamide‐imide)s and poly(N‐phenylamide‐amide)s with inherent viscosities of 0.58–0.82 and 0.56–1.21 dL/g were prepared by a conventional two‐stage method and the direct phosphorylation polycondensation, respectively, from the diamine with various aromatic dianhydrides and aromatic dicarboxylic acids. All polyimides and polyamides are amorphous and readily soluble in many organic solvents such as N,N‐dimethylacetamide and N‐methyl‐2‐pyrrolidone. These polymers could be solution cast into transparent, tough, and flexible films with high tensile strengths. These polyimides and polyamides had glass‐transition temperatures in the ranges of 230–258 and 196–229 °C, respectively. Decomposition temperatures of the polyimides for 10% weight loss all occurred above 500 °C in both nitrogen and air atmospheres. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2564–2574, 2002     

Synthesis and properties of poly(imide‐hydrazide)s and poly(amide‐imide‐hydrazide)s from N‐[p‐(or m‐)carboxyphenyl]trimellitimide and aromatic dihydrazides or p‐aminobenzhydrazide via the phosphorylation reaction

A series of new poly(imide‐hydrazide)s and poly(amide‐imide‐hydrazide)s were obtained by the direct polycondensation of N‐[p‐(or m‐)carboxyphenyl]trimellitimide (p‐ or m‐CPTMI) with terephthalic dihydrazide (TPH), isophthalic dihydrazide (IPH), and p‐aminobenzhydrazide (p‐ABH) by means of diphenyl phosphite and pyridine in the N‐methyl‐2‐pyrrolidone (NMP) solutions containing dissolved CaCl₂. The resulting hydrazide‐containing polymers exhibited inherent viscosities in the 0.15–0.96 dL/g range. Except for that derived from p‐CPTMI with TPH or p‐ABH, the other hydrazide copolymers were readily soluble in polar solvents such as NMP and dimethyl sulfoxide (DMSO). As evidenced by X‐ray diffraction patterns, the hydrazide copolymer obtained from TPH showed a moderate level of crystallinity, whereas the others were amorphous in nature. Most of the amorphous hydrazide copolymers formed flexible and tough films by solvent casting. The amorphous hydrazide copolymers had glass‐transition temperatures (T_g) between 187 and 233 °C. All hydrazide copolymers could be thermally converted into the corresponding oxadiazole copolymers approximately in the region of 250–400 °C, as evidenced by the DSC thermograms. The oxadiazole copolymers showed a significantly decreased solubility when compared to their respective hydrazide precursors. They exhibited T_g's of 264–302 °C and did not show dramatic weight loss before 400 °C in air or nitrogen. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1599–1608, 2000     

Synthesis and properties of organosoluble poly(amide imide imide)s based on tetraimide dicarboxylic acid condensed from 4,4′‐(hexafluoroisopropylidene)diphthalic anhydride, 4,4′‐oxydianiline,and trimellitic anhydride and various aromatic diamines

A novel tetraimide dicarboxylic acid was synthesized with the ring‐opening addition of 4,4′‐(hexafluoroisopropylidene)diphthalic anhydride, 4,4′‐oxydianiline, and trimellitic anhydride in a 1/2/2 molar ratio in N‐methyl‐2‐pyrrolidone followed by azeotropic condensation to tetraimide dicarboxylic acid. A series of poly(amide imide imide)s (PAIIs) with inherent viscosities of 0.8–1.1 dL/g were prepared from tetraimide dicarboxylic acid with various aromatic diamines by direct polycondensation. Most of the PAIIs were readily soluble in a variety of amide polar solvents and even in less polar m‐cresol and pyridine. Solvent‐cast films had tensile strengths ranging from 99 to 106 MPa, elongations at break ranging from 8 to 13%, and initial moduli ranging from 2.0 to 2.3 GPa. The glass‐transition temperatures of these PAIIs were recorded at 244–276 °C. They had 10% weight losses at temperatures above 520 °C in air or nitrogen atmospheres. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1092–1102, 2002     

Microwave‐assisted synthesis and characterization of heterocyclic,and optically active poly(amide‐imide)s incorporating L‐amino acids

N,N′‐Pyromelliticdiimido‐di‐L ‐alanine ( 1 ), N,N′‐pyromelliticdiimido‐di‐L ‐phenylalanine ( 2 ), and N,N′‐pyromelliticdiimido‐di‐L ‐leucine ( 3 ) were prepared from the reaction of pyromellitic dianhydride with corresponding L ‐amino acids in a mixture of glacial acetic acid and pyridine solution (3/2 ratio) under refluxing conditions. The microwave‐assisted polycondensation of the corresponding diimide‐diacyl chloride monomers ( 5–7 ) with 4‐phenyl‐2,6‐bis(4‐aminophenyl) pyridine ( 10 ) or 4‐(p‐methylthiophenyl)‐2,6‐bis(4‐aminophenyl) pyridine ( 12 ) were carried out in a laboratory microwave oven. The resulting poly(amide‐imide)s were obtained in quantitative yields, and they showed admirable inherent viscosities (0.12–0.55 dlg^?1), were soluble in polar aprotic solvents, showed good thermal stability and high optical purity. The synthetic compounds were characterized by IR, MS, ¹H NMR, and ¹³C NMR spectroscopy, elemental analysis, and specific rotation. Copyright © 2008 John Wiley & Sons, Ltd.