Effects of the Calcination and Reduction Conditions on a Cu/ZnO Methanol Synthesis Catalyst

The CuO crystallite size of the catalysts obtained from aurichalcite greatly depends on the heating rate of calcination for highly active and selective Cu/ZnO catalyst was prepared by reduction with methanol at 443 K for 17 h.     

高活性铜催化剂无受体乙醇催化脱氢制乙醛研究

相较于Wacker工艺进行乙醛工业化生产,发展多相催化体系实现乙醇直接无氧催化脱氢制乙醛和副产氢气,从生产工艺和经济价值方面无疑是一条更加安全高效的路线.在此,我们发展了一种高效、稳固的Cu/SiO₂催化剂,用于乙醇的无受体催化脱氢.通过氨蒸发法制备得到高度分散的Cu颗粒,在没有任何平衡气体的纯乙醇进料条件下,显示出超强的热稳定性.活性组分Cu和载体SiO₂之间的强相互作用,使其具有优异的催化性能.通过反应条件优化,在250℃下实现了较高的乙醇转化率(>40%)和乙醛选择性(>95%),且催化剂在固定床连续反应过程中可稳定运行超过400 h.     

EXAFS研究合成甲醇催化剂Cu／ZnO／MxOy

有关CO。＋H。合成甲醇催化剂的研究已有许多报道［‘－’j，但目前对活性中心及反应机理的认识仍不～致，其中对活性中心的看法归纳起来有3种：（1）Cll为活性中心“‘；（2）Cll”为活性中心［’j；（3）Cll－CtJ”为活性中心［‘1．研究发现，第三组分（如AI刀。）的加入可防止Cu粒子的烧结［’］，使Cu产生无序及缺陷结构，有利于CO。的吸附、活化［‘j及起到高分散Cu／Zno的稳定剂的作用［’j．由于三组分催化剂结构的多相性和准非晶态性，通常的XRD方法难以明确了解其结构，而EXAFS方法对研究局部有序结构特别有效．本文以Z…     

Stabilization of Cu/ZnO Based Catalysts by Nickel Additive in Methanol Decomposition

A series of Cu/Zn based catalysts with and without Ni, prepared by the co-precipitation method, has been studied for methanol decomposition. CO and H2 are the major products. The Cu/Zn catalysts show a low initial activity and a poor stability. The formation of the CuZn alloys was observed in the deactivated Cu/Zn catalysts which were used for methanol decomposition at 250 . When small amounts of Ni were added in the catalyst, the Cu/Zn/Ni(molar ratio 5/4/ x) catalysts showed a high activity at a low temperature. The activity and the stability of the catalyst depend on the nickel content. The activity of the Cu/Zn/Ni catalysts was maintained at a. relatively stable value of 78% conversion of methanol with 95% selectivity of H2, 93% selectivity of CO, and a more than 70% yield of hydrogen was obtained at 250 C when x >1. The stability of the Cu/Zn/Ni (molar ratio 5/4/x) catalysts showed the maximum (ca 88%) when x=1. The stabilization effect of nickel on the Cu/Zn based catalysts may lead to the increasin     

焙烧温度对Cu/ZnO水煤气变换催化剂开停循环性能的影响

采用共沉淀法制备了Cu/Zn物质的量的比为1∶1的Cu/ZnO催化剂, 考察了不同焙烧温度对催化剂的水煤气变换反应活性和开停循环稳定性的影响. 研究发现350 ℃焙烧得到的Cu/ZnO催化剂有最高的反应活性, 在反应温度为200 ℃时, CO转化速率即可达2080 cm³•g_cat^－1•h^－1. 在开停循环性能评价中, Cu/ZnO催化剂表现出了良好的稳定性, 明显优于CeO₂负载的贵金属催化剂, 其中焙烧温度为550 ℃的Cu/ZnO催化剂在一次开停循环操作后活性有明显的提高.     

纳米Ce1—xMnxO2催化剂上乙醇催化氧化发光研究

研究了纳米Ce_1—xMn_xO₂上乙醇催化氧化发光特性, 重点考察了反应温度和催化剂组成(Ce/Mn比)对发光强度的影响规律. 为研究催化发光机理, 在相近的反应条件下考察了纳米Ce_1—xMn_xO₂上乙醇催化氧化反应的活性和选择性. 结果表明: 催化发光强度与催化反应中生成CH₃CHO的产率有很好的顺变关系, 表明CH₃CHO是导致C₂H₅OH分子在纳米Ce_1—xMn_xO₂催化剂上氧化发光的“活性分子”.     

甲醇水蒸气重整制氢的高效碳纳米管改性Cu/ZnO/Al2O3催化剂

以碳纳米管为助剂,制备用于甲醇水蒸气重整制氢的新型高效Cu/ZnO/Al₂O₃催化剂,并与传统Cu/ZnO/Al₂O₃催化剂在相同条件下的催化性能进行了比较.结果表明,添加适量碳纳米管可显著提高催化剂的低温催化活性和选择性,在大幅度提高产氢速率的同时有效降低了重整产气中CO的含量.SEM和XRD分析证实适量碳纳米管的添加有效促进了Cu/ZnO/Al₂O₃催化剂结构特性的改善,有利于活性铜物种的分散,从而显著提高了催化剂的低温催化性能.     

微波辐照促进的甲醇水蒸汽重整制氢Cu/ZnO/Al2O3催化剂

微波介电加热具有高效和节能等特点,近年来利用其独特的“体相加热”效应制备结构特异及性能优越的催化材料在多相催化领域中已引起关注,本文报道微波辐照处理对传统Cu／ZnO／Al2O3催化剂在甲醇水蒸汽重整制氢反应中的促进作用,研究结果表明,微波辐照处理对传统Cu／ZnO／Al2O3催化剂的微结构性质具有调控作用,可大大改善其低温催化活性及制氢选择性。     

乙醇一步法合成乙酸乙酯的Cu／ZnO／CoO／Al2O3／TiO2催化剂

乙醇一步法合成乙酸乙酯的Ｃｕ／ＺｎＯ／ＣｏＯ／Ａｌ２Ｏ３／ＴｉＯ２催化剂郑荣辉曾金龙（厦门大学化工系、物理化学研究所厦门３６１００５）关键词乙酸乙酯合成一步法双功能催化剂中图分类号Ｏ６２３．６２４．１乙醇为单一原料直接合成乙酸乙酯的新方法，克服了以浓...     

乙烷氧化脱氢制乙烯反应中制备方法及助剂对镍基催化剂性能的影响

采用不同方法制备了镍基催化剂,并考察了乙烷氧化脱氢制乙烯(ODE)的反应活性,结果表明,在3种不同制备方法的催化剂上,ODE反应的活性及产物选择性存在明显差异,浸渍法制备的催化剂性能最佳.在相同的条件下,以共浸渍法引入CeO2助剂后,N iO/-γA l2O3催化剂上的低温选择氧化活性显著提高,而目的产物C2H4的选择性变化不大.XRD,还原TG和XPS对催化剂进行表征的结果显示:反应的活性物相可能是易于还原的高度分散于催化剂表面的微晶N iO和表面尖晶石N iA l2O4物相;高分散的微晶N iO,类似于纯N iO,有利于ODE反应低温选择氧化生成目的产物C2H4,而易还原的表面尖晶石N iA l2O4物相的存在则可能是在高温下获得高选择氧化活性和选择性的主要原因之一.     

反相微乳法制备Ni/CeO2纳米复合催化剂催化乙醇水蒸气重整制氢

采用W/O反相微乳法制备了Ni/CeO2纳米复合催化剂,对比了加热和真空冷冻两种不同干燥方法处理的催化剂以及传统浸渍法制备的催化剂上乙醇水蒸气重整反应性能。由X射线衍射(XRD)、透射电子显微镜(TEM)、程序升温还原(TPR)和程序升温脱附(TPD)等技术对催化剂进行了表征。实验结果表明,采用反相微乳法制备的Ni/CeO2纳米复合催化剂显示了良好的催化活性和选择性;其中采用真空冷冻干燥处理的催化剂表现出最好的活性,H2产率最高达到42%,CO选择性低至0.35%,并且具有较好的稳定性和抗积炭能力,优于传统浸渍法制备的催化剂。     

Cu/Zn比对微波辐射老化制备CuO/ZnO/Al2O3催化剂结构和活性的影响

在微波辐射条件下, 对共沉淀法制备合成甲醇CuO/ZnO/Al₂O₃催化剂前驱体的母液进行老化, 通过改变Cu/Zn比, 研究了微波辐射对催化剂性能的影响, 并结合XRD, FTIR, DTG, H₂-TPR, XPS等表征手段, 探讨了微波辐射对前驱体物相组成及催化剂微观结构的影响. 结果表明: 在微波辐射老化条件下, Cu/Zn比对催化剂前驱体物相组成影响较大, 微波辐射有利于绿铜锌矿(Cu, Zn)₅(CO₃)₂(OH)₆晶相选择生成. 当Cu/Zn比为2.0时, 前驱体中含有较多的绿铜锌矿物相, 且结晶较好, 焙烧后形成的催化剂中CuO-ZnO协同作用较强, CuO分散性好, 导致H₂还原温度低, 在浆态床合成甲醇过程中表现出良好的催化活性和稳定性, 甲醇时空收率(STY)达到309.0 g•kg^－1•h^－1, 失活率仅为0.11%/d, 远优于常规水浴加热制备的催化剂.     

Activity of Mono-, Bi-, and Trimetallic Catalysts Pt-Ni-Cr/C in the Bicyclohexyl Dehydrogenation Reaction

The influence of metals with different redox properties and a carbon carrier on the activity of mono-, bi- and trimetallic Pt-Ni-Cr/C catalysts has been studied in the bicyclohexyl dehydrogenation reaction as the hydrogen release stage in hydrogen storage. An increase in the conversion (X > 62%) of bicyclohexyl and selectivity for biphenyl (S > 84%) was observed on trimetallic catalysts Pt-Ni-Cr/C compared with the monometallic catalyst Rt/C (X > 55%; S > 68%). It has been established that the increase in the conversion of bicyclohexyl and selectivity for biphenyl in the dehydrogenation reaction on trimetallic catalysts is due to an increase in the activity of Pt nanoparticles in the vicinity of local Cr-Ni clusters of solid substitution solutions.     

Cu含量对以水滑石为前驱体的Cu/Co/Mn/Al催化剂高级醇合成性能的影响

A series of Cu/Co/Mn/Al catalysts derived from hydrotalcite precursors with different Cu/Co molar ratios (0, 0.1, 0.5, 1.0, and 2.0) were prepared and used for the synthesis of higher alcohols from syngas. N₂ physical adsorption desorption, inductively coupled plasma atomic emission spectrometry (ICP-AES), X-ray diffraction (XRD), scanning electron microscopy (SEM), hydrogen temperature-programmed reduction (H₂-TPR), thermogravimetry (TG), and high-resolution transmission electron microscopy (HRTEM) techniques were employed to investigate the physical and chemical properties of the Cu/Co/Mn/Al catalysts. The results show that the optimum Cu content can increase specific surface area, improve reducibility, and form regular layered structure to provide more uniform distribution of active sites, thereby enhancing catalytic activity and alcohol selectivity. When the Cu/Co molar ratio was 0.5, the yield of alcohol and the alcohol selectivity reached the maximum values of 0.071 g·g^-1·h^-1 and 35.9%, respectively.     

Ni对Cu/ZnO基甲醇裂解催化剂的促进机制

通过XRD,BET,In-situ XPS等表征技术对Cu/ZnO基甲醇裂解制氢催化剂进行 了详细的研究。XRD结果表明,Cu-Zn合金的生成是Cu/ZnO基催化剂在反应初期快速 失活的主要原因;XRD,BET和N_2O滴定实验结果表明,Ni助剂可能是通过提高 Cu~0活性物种的分散度并维持Cu~0活性物种在催化反应过程中的稳定性而使 Cu/Zn/Ni催化剂的活性及稳定性大幅度提高。In-situ XPS结果表明,Ni助剂的加 入可以诱导Cu/Zn/Ni催化剂表面在甲醇裂解反应过程中出现Cu~+,从而由 Cu~0/Cu~+共同构成催化剂的活性中心,并最终导致Cu/Zn/Ni催化剂的高活性。     

甲醇水蒸气重整制氢Cu/ZnO/Al2O3催化剂的研究

燃料电池作为一种无污染、高效率的能源引起世界各大汽车公司的广泛关注[1,2]。用于燃料电池的燃料目前研究较多的是氢气,用氢气作燃料存在储存、安全、运输等问题,寻求合适贮氢方法或替代燃料,实现车载制氢是解决问题的办法。甲醇作为液体燃料,因具有高能量密度,低碳含量,以及运输和贮存等优势成为车载制氢的理想燃料,甲醇水蒸气重整制氢反应也成为研究的热点[3～10]。车载制氢对甲醇水蒸气重整制氢反应体系中的产氢速率,氢气和CO的含量都有一定的要求。尤其对CO含量要求更为苛刻,因CO易引起燃料电池阳极催化剂中毒[11,12]。因此,开…     

Ni基乙烷脱氢催化剂的性能及其改进

过渡金属Ni是地球上储量丰富的金属元素, 在加氢脱硫、重整制氢等催化领域应用非常广泛, 但是关于Ni基催化剂在烷烃脱氢方面的研究较少; 因此, 本工作采用不同的方法, 制备了三种结构的Ni基负载催化剂, 即尖晶石分解型、浸渍型和钙钛矿析出型, 并在700 ℃、C₂H₆-N₂气氛中和50 mL•min^-1气体流速下, 探索了它们的乙烷脱氢性能. 结果表明: 尖晶石分解型催化剂Ni_1-xCu_xCr₂O₄还原后在Cr₂O₃表面形成Ni-Cu合金颗粒, 能有效钝化Ni的C—C键断裂活性, 提高乙烯的选择性. Ni含量过高时, Ni不能有效地分散而形成大的金属团簇, 造成乙烷过度裂解, 乙烯选择性较低. 浸渍负载型催化剂Ni_xM_y/Al₂O₃ (M为Cu或Ag) 比表面积大, 表面活性位点分散, 但活性金属与载体结合力弱, 在高温下不稳定; Cu或Ag与Ni形成合金, 可有效提高乙烯选择性, Ag较Cu的效果更佳. 钙钛矿析出型催化剂LaCr_1-xNi_xO₃(LCNi-100x)在还原气氛中析出均匀细小的Ni颗粒, 其与基体结合力强, 抗积碳性能和稳定性较高; 含15% Ni的LCNi-15还原后(R-LCNi-15)表现出最好的催化性能, 乙烯产率最高(24%), 同时具有较好的抗积碳性能和稳定性以及氧化再生性.     

CrOx/SiO2催化剂上丙烷在CO2气氛中脱氢反应的研究

采用ＸＲＤ、ＵＶ－ｖｉｓ　 ＤＲＳ、ＥＳＲ和微分吸附量热等技术,考察了铬担载量分别为２．５、５和 １０ｗｔ％的 ＣｒＯｘ／ＳｉＯ２催化剂的结构、表面性质和氧化还原性能。结果表明,催化剂表面上存在多种Ｃｒ的氧化态和聚集形式。随着Ｃｒ担载量从２．５ｗｔ％到１０ｗｔ％的逐渐增大,催化剂表面占主导地位的Ｃｒ物种由ＣｒＯ３单体转为多聚ＣｒＯ３和Ｃｒ２Ｏ３晶相。在 ＣＯ２气氛中催化剂对丙烷转化率和丙烯选择性的大小顺序为 ２． ５ｗｔ％ ＣｒＯｘ／ＳｉＯ２ ＞５ｗｔ％ ＣｒＯｘ／ＳｉＯ２＞１０ｗｔ％ ＣｒＯｘ／ＳｉＯ２,反应过程中的原位 ＥＳＲ和 ＵＶ－ｖｉｓＤＲＳ测定结果表明,催化剂表面的反应活性中心为Ｃｒ５＋, Ｃｒ５＋可由催化剂预处理过程中 Ｃｒ３＋的氧化及丙烷反应过程中 ＣｒＯ３单体的还原产生,在反应中 ＣＯ２可使Ｃｒ３＋重新氧化为Ｃｒ５＋。     

高效甲醇水蒸气重整制氢的SBA-15改性的Cu/ZnO/Al2O3催化剂

以介孔SBA-15为结构助剂, 制备出用于甲醇水蒸气重整制氢的新型高效氧化硅掺杂的Cu/ZnO/Al₂O₃催化剂, 并与传统Cu/ZnO/Al₂O₃催化剂在相同条件下的催化性能进行了比较. 结果表明, 添加适量介孔SBA-15可显著提高催化剂的催化活性和选择性, 在大幅度提高甲醇转化率的同时有效降低了重整产气中CO的含量. 原位XRD分析证实适量介孔SBA-15的添加对传统Cu/ZnO/Al₂O₃催化剂的微结构性质可产生重要的调控作用, 从而大大改善其催化活性和制氢选择性.