High-pressure synthesis and structural characterization of three new polyphosphides, α-SrP3, BaP8, and LaP5

Three novel metal polyphosphides, α-SrP₃, BaP₈, and LaP₅, were prepared in BN crucibles by the reaction of the respective stoichiometric mixtures under a high pressure of 3 GPa at 950-1000°C. Their crystal structures were determined from single-crystal X-ray data (α-SrP₃: space group C2/m, a=9.199(6) Å, b=7.288(3) Å, c=5.690(3) Å, β=113.45(4)°, Z=4, R₁/wR₂=0.0684/0.1180 for 471 observed reflections and 22 variables; BaP₈: space group P−1, a=6.762(2) Å, b=7.233(2) Å, c=8.567(2) Å, α=86.32(2)°, β=84.31(2)°, γ=70.40(2)°, Z=2, R₁/wR₂=0.0476/0.1255 for 2702 observed reflections and 82 variables; LaP₅: space group P2₁/m, a=4.885(1) Å, b=9.673(3) Å, c=5.577(2) Å, β=105.32(2)°, Z=2, R₁/wR₂=0.0391/0.1034 for 1272 observed reflections and 31 variables). α-SrP₃ is isostructural with SrAs₃ and the crystal structure consists of two-dimensional puckered polyanionic layers _∞²[P₃]²⁻ that stack along the c-axis yielding channels occupied by Sr²⁺ counterions. BaP₈ crystallizes in a new structure type which contains a three-dimensional infinite polyanionic framework _∞³[P₃]²⁻, with large channels hosting the barium cations. LaP₅ is a layered compound containing _∞²[P₅]³⁻ polyanionic layers separated by La³⁺ ions. All three compounds exhibit expected diamagnetic behaviors.     

Ab initio structure determination of new compound Li4CaB2O6

A new compound, Li₄CaB₂O₆, has been synthesized by solid-state reaction and its structure has been determined from powder X-ray diffraction data by direct methods. The refinement was carried out using the Rietveld methods and the final refinement converged with R_p=10.4%, R_wp=14.2%, R_exp=4.97%. This compound belongs to the orthorhombic space group Pnnm, with lattice parameters a=9.24036(9) Å, b=8.09482(7) Å, and c=3.48162(4) Å. Fundamental building units are isolated [BO₃]³⁻ anionic groups, which are all parallel to the a-b plane stacked along the c-axis. The Ca atoms are six-coordinated by the O atoms to form octahedral coordination polyhedra, which are joined together through edges along the c-axis, forming infinitely long three-dimensional chains. The Li atoms have a four-fold and a five-fold coordination with O atoms that lead to complex Li-O-Li chains that also extend along the c-axis. The infrared spectrum of Li₄CaB₂O₆ was also studied, which is consistent with the crystallographic study.     

The study of Bi3B5O12: synthesis, crystal structure and thermal expansion of oxoborate Bi3B5O12

The paper presents a new data on the crystal structure, thermal expansion and IR spectra of Bi₃B₅O₁₂. The Bi₃B₅O₁₂ single crystals were grown from the melt of the same stoichiometry by Czochralski technique. The crystal structure of Bi₃B₅O₁₂ was refined in anisotropic approximation using single-crystal X-ray diffraction data. It is orthorhombic, Pnma, a=6.530(4), b=7.726(5), c=18.578(5) Å, V=937.2(5) Å³, Z=4, R=3.45%. Bi³⁺ atoms have irregular coordination polyhedra, Bi(1)O₆ (d(B-O)=2.09-2.75 Å) and Bi(2)O₇ (d(B-O)=2.108-2.804 Å). Taking into account the shortest bonds only, these polyhedra are considered here as trigonal Bi(1)O₃ (2.09-2.20 Å) and tetragonal Bi(2)O₄ (2.108-2.331 Å) irregular pyramids with Bi atoms in the tops of both pyramids. The BiO₄ polyhedra form zigzag chains along b-axis. These chains alternate with isolated anions [B₂^IVB₃^IIIO₁₁]⁷⁻ through the common oxygen atoms to form thick layers extended in ab plane. A perfect cleavage of the compound corresponds to these layers and an imperfect one is parallel to the Bi-O chains. The Bi₃B₅O₁₂ thermal expansion is sharply anisotropic (α₁₁≈α₂₂=12, α₃₃=3×10⁻⁶ °C⁻¹) likely due to a straightening of the flexible zigzag chains along b-axis and decreasing of their zigzag along c-axis. Thus the properties like cleavage and thermal expansion correlate to these chains.     

Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

Contrasting oxide crystal chemistry of Nb and Ta:: The structures of the hexagonal bronzes BaTa2O6 and Ba0.93Nb2.03O6

The high-temperature hexagonal forms of BaTa₂O₆ and Ba_0.93Nb_2.03O₆ have P6/mmm symmetry with unit-cell parameters a=21.116(1) Å, c=3.9157(2) Å and a=21.0174(3) Å, c=3.9732(1) Å, respectively. Single crystal X-ray structure refinements for both phases are generally consistent with a previously proposed model, except for displacements of some Ba atoms from high-symmetry positions. The structures are based on a framework of corner- and edge-connected Nb/Ta-centred octahedra, with barium atoms occupying sites in four different types of [0 0 1] channels with hexagonal, triangular, rectangular and pentagonal cross-sections. The refinements showed that the non-stoichiometry in the niobate phase is due to barium atom vacancies in the pentagonal channels and to extra niobium atoms occupying interstitial sites with tri-capped trigonal prismatic coordination. The origin of the non-stoichiometry is attributed to minimisation of non-bonded Ba-Ba repulsions. The hexagonal structure is related to the structures of the low-temperature forms of BaNb₂O₆ and BaTa₂O₆, through a 30° rotation of the hexagonal rings of octahedra centred at the origin.     

Superstructure of a phosphor material Ba3MgSi2O8 determined by neutron diffraction data

Ba₃MgSi₂O₈, a phosphor host examined for use in white-light devices and plant-growth lamps, was synthesized at 1225 °C in air. Its crystal structure has been determined and refined by a combined powder X-ray and neutron Rietveld method (, Z=3, a=9.72411(3) Å, c=7.27647(3) Å, V=595.870(5) Å³; R_p/R_wp=3.79%/5.03%, χ²=4.20). Superstructure reflections, observed only in the neutron diffraction data, provided the means to establish the true unit cell and a chemically reasonable structure. The structure contains three crystallographically distinct Ba atoms—Ba1 resides in a distorted octahedral site with S₆ () symmetry, Ba2 in a nine-coordinate site with C₃ (3) symmetry, and Ba3 in a ten-coordinate site with C₁ (1) symmetry. The Mg atoms occupy distorted octahedral sites, and the Si atom occupies a distorted tetrahedral site.     

Temperature-dependent crystallographic studies and electronic structure of Ba2Cd3Bi4

The ternary compound Ba₂Cd₃Bi₄ crystallizes in the C-centered orthorhombic space group Cmce (No. 64) with its own type (Pearson's symbol oC36; a=7.019(3) Å, b=17.389(7) Å and c=9.246(3) Å determined at -23 °C). Although the structure of this intermetallic compound with transition metal in d¹⁰ configuration has already been established, details such as the rather unusual coordination of the Cd-atoms and the elongation in specific direction of their anisotropic displacement parameters had not been explained. These facts, along with the higher than 12% R-values from the original structure determination prompted the systematic structural studies by single-crystal X-ray diffraction at several different temperatures. The results from these studies confirm strong temperature dependence of the cadmiums’ anisotropic displacement parameters, concomitant rather large thermal expansion along the crystallographic b-axis. Electronic band structure calculations performed by the TB-LMTO-ASA method are also reported.     

Synthesis and structure of a 1,6-hexyldiamine heptaborate, [H3N(CH2)6NH3][B7O10(OH)3]

A new 1,6-hexyldiamine heptaborate, [H₃N(CH₂)₆NH₃][B₇O₁₀(OH)₃] (1), has been solvothermally synthesized and characterized by single-crystal X-ray diffraction, FTIR, elemental analysis, and thermogravimetric analysis. Compound 1 crystallizes in monoclinic system, space group P2₁/n with a=8.042(2) Å, b=20.004(4) Å, c=10.103(2) Å, and β=90.42(3)°. The anionic [B₇O₁₀(OH)₃]_n²ⁿ⁻ layers are interlinked via hydrogen bonding to form a 3D supramolecular network containing large channels, in which the templated [H₃N(CH₂)₆NH₃]²⁺ cations are located.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Synthesis, structural characterization and optical properties of a new cesium aluminum borate, Cs2Al2B2O7

A new borate, Cs₂Al₂B₂O₇, was synthesized by solid-state reaction. It crystallizes in the monoclinic space group P2₁/c with a=6.719(1) Å, b=7.121(1) Å, c=9.626(3) Å, β=115.3(1)°, and Z=2. In the structure, two AlO₄ tetrahedra and two BO₃ planar triangles are connected alternately by corner-sharing to from nearly planar [Al₂B₂O₁₀] rings, which are further linked via common O1 atom to generate layers in the bc plane. These layers then share the O3 atoms lying on a center of inversion to form a three-dimensional framework with Cs atoms residing in the channels. The IR spectrum confirms the presence of both BO₃ and AlO₄ groups and the UV-vis-IR diffuse reflectance spectrum indicates a band gap of about 4.13(2) eV.     

Synthesis and structural investigation of the compounds containing HF2 anions: Ca(HF2)2, Ba4F4(HF2)(PF6)3 and Pb2F2(HF2)(PF6)

Three new compounds Ca(HF₂)₂, Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) were obtained in the system metal(II) fluoride and anhydrous HF (aHF) acidified with excessive PF₅. The obtained polymeric solids are slightly soluble in aHF and they crystallize out of their aHF solutions. Ca(HF₂)₂ was prepared by simply dissolving CaF₂ in a neutral aHF. It represents the second known compound with homoleptic HF environment of the central atom besides Ba(H₃F₄)₂. The compounds Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) represent two additional examples of the formation of a polymeric zigzag ladder or ribbon composed of metal cation and fluoride anion (MF⁺)_n besides PbF(AsF₆), the first isolated compound with such zigzag ladder. The obtained new compounds were characterized by X-ray single crystal diffraction method and partly by Raman spectroscopy. Ba₄F₄(HF₂)(PF₆)₃ crystallizes in a triclinic space group P1¯ with a=4.5870(2) Å, b=8.8327(3) Å, c=11.2489(3) Å, α=67.758(9)°, β=84.722(12), γ=78.283(12)°, V=413.00(3) Å³ at 200 K, Z=1 and R=0.0588. Pb₂F₂(HF₂)(PF₆) at 200 K: space group P1¯, a=4.5722(19) Å, b=4.763(2) Å, c=8.818(4) Å, α=86.967(10)°, β=76.774(10)°, γ=83.230(12)°, V=185.55(14) ų, Z=1 and R=0.0937. Pb₂F₂(HF₂)(PF₆) at 293 K: space group P1¯, a=4.586(2) Å, b=4.781(3) Å, c=8.831(5) Å, α=87.106(13)°, β=76.830(13)°, γ=83.531(11)°, V=187.27(18) Å³, Z=1 and R=0.072. Ca(HF₂)₂ crystallizes in an orthorhombic Fddd space group with a=5.5709(6) Å, b=10.1111(9) Å, c=10.5945(10) Å, V=596.77(10) Å³ at 200 K, Z=8 and R=0.028.     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

LiB3O5 crystal structure at 20, 227 and 377 °C

Crystal structure of LiB₃O₅ (a framework of [B₃O₅]⁻ rings and Li atoms located in interspaces) was refined at high temperatures using single-crystal X-ray diffraction, MoKα-radiation, anharmonic approximation, orthorhombic; Pna2₁; Z=4; 20 °C (a=8.444, b=7.378, c=5.146 Å, 1411 F(hkl), R=0.022); 227 °C (a=8.616, b=7.433, c=5.063 Å, 1336 F(hkl), R=0.026), 377 °C (a=8.746, b=7.480, c=5.013 Å, 1193 F(hkl), R=0.035). A high mobility of Li atoms and their highly asymmetric vibrations are revealed. Ellipsoid of Li thermal vibrations is oviform. Li is shifted on heating to 0.26 Å mainly along a-axis causing high thermal expansion in this direction; Li temperature factors are multiplied by 4 on heating. Rigid boron-oxygen groups in LiB₃O₅ remain practically stable on heating similar to α-Na₂B₈O₁₃ and α-CsB₅O₈. At the same time these groups rotate relative to each other like hinges leading to extremely anisotropic thermal expansion (α_a=101, α_b=31, α_c=−71, α_v=60×10⁻⁶ °C⁻¹, 20-530 °C, HTXRPD data).     

Thermal stability and crystal structure of β-Ba3YB3O9

A new compound, β-Ba₃YB₃O₉, has been attained through solid phase transition from α-Ba₃YB₃O₉ at high temperatures. Differential thermal analysis (DTA) revealed the phase transition at about 1120°C, the melting temperature at about 1253°C. Its crystal structure has been determined from powder X-ray diffraction data. The refinement was carried out using the Rietveld method and the final refinement converged with R_p=10.5% and R_wp=13.7%. This compound belongs to the hexagonal space group R-3, with lattice parameters a=13.0441(1) Å and c=9.5291(1) Å. There are 6 formulas per unit cell and 7 atoms in the asymmetric unit. The structure of β-Ba₃YB₃O₉ is built up from Ba(Y)O₈, BaO₆ and YB₆O₁₈ units formed by one YO₆ octahedron and six BO₃ triangles with shared O atoms.     

High-pressure high-temperature synthesis and crystal structure of the isotypic rare earth (RE)-thioborate-sulfides RE9[BS3]2[BS4]3S3, (RE=Dy-Lu)

Application of high-pressure high-temperature conditions (3.5 GPa at 1673 K for 5 h) to mixtures of the elements (RE:B:S=1:3:6) yielded crystalline samples of the isotypic rare earth-thioborate-sulfides RE₉[BS₃]₂[BS₄]₃S₃, (RE=Dy-Lu), which crystallize in space group P6₃ (Z=2/3) and adopt the Ce₆Al_3.33S₁₄ structure type. The crystal structures were refined from X-ray powder diffraction data by applying the Rietveld method. Dy: a=9.4044(2) Å, c=5.8855(3) Å; Ho: a=9.3703(1) Å, c=5.8826(1) Å; Er: a=9.3279(12) Å, c=5.8793(8) Å; Tm: a=9.2869(3) Å, c=5.8781(3) Å; Yb: a=9.2514(5) Å, c=5.8805(6) Å; Lu: a=9.2162(3) Å, c=5.8911(3) Å. The crystal structure is characterized by the presence of two isolated complex ions [BS₃]^3- and [BS₄]^5- as well as [□(S^2-)₃] units.     

Crystal growth of a novel oxygen-deficient layered perovskite: Ba7Li3Ru4O20

Single crystals of both Ba₇Li₃Ru₄O₂₀ and Ba₄NaRu₃O₁₂ were grown from reactive molten hydroxide fluxes. Ba₇Li₃Ru₄O₂₀ is a 7L-layer perovskite-related phase resulting from the stacking of six [AO₃] layers and one oxygen deficient [AO₂] layer, thereby creating LiO₄ tetrahedra in addition to the LiO₆ octahedra and face-sharing Ru₂O₉ bi-octahedra formed from the [AO₃] layers. The compound crystallizes in the space group with a=5.7927(1) Å and c=50.336(2) Å, Z=3. Ba₄NaRu₃O₁₂ crystallizes in the space group P6₃mc with lattice parameters of a=5.8014(2) Å and c=19.2050(9) Å, Z=2. Ba₄NaRu₃O₁₂ is identical to a previously reported neutron refinement structure. The magnetic properties of Ba₇Li₃Ru₄O₂₀ are also reported.     

Synthesis, structure characterization and optical properties of a new tripotassium cadmium pentaborate, K3CdB5O10

A new ternary borate oxide, K₃CdB₅O₁₀, has been synthesized by solid-state reaction at 580 °C. The compound crystallizes in the monoclinic space group P2₁/n with a=7.6707 (7) Å, b=19.1765 (17) Å, c=7.8784 (6) Å, β=115.6083 (49)°, and Z=4. The crystal structure consists of a two-dimensional infinite [CdB₅O₁₀] layer, which forms by connecting isolated double ring [B₅O₁₀] groups and CdO₄ tetrahedra. K atoms filling in the interlayer and intralayer link the layers together and balance charge. The IR spectrum has been studied and confirmed the presence of both BO₃ and BO₄ groups, and the UV-vis-IR diffuse reflectance spectrum exhibits a band gap of about 3.4 eV. The DSC analysis proves that K₃CdB₅O₁₀ is a congruent melting compound.     

Synthesis, crystal structure and optical properties of a novel sodium lead pentaborate, NaPbB5O9

A novel sodium lead pentaborate, NaPbB₅O₉, has been successfully synthesized by standard solid-state reaction. The single-crystal X-ray structural analysis showed that NaPbB₅O₉ crystallizes in the monoclinic space group P2₁/c with a=6.5324(10) Å, b=13.0234(2) Å, c=8.5838(10) Å, β=104.971(10)°, and Z=4. The crystal structure is composed of double ring [B₅O₉]³⁻ units, [PbO₇] and [NaO₇] polyhedra. [B₅O₉]³⁻ groups connect with each other forming two-dimensional infinite _∞[B₅O₉]³⁻ layers, while [PbO₇] and [NaO₇] polyhedra are located between the layers. [PbO₇] polyhedra linked together via corner-sharing O atom forming novel infinite _∞[PbO₆] chains along the c axis. The thermal behavior, IR spectrum and the optical diffuse reflectance spectrum of NaPbB₅O₉ were reported.     

Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

Subsolidus phase relations and crystal structures of the mixed-oxide phases in the In2O3-WO3 system

Subsolidus phase relationships in the In₂O₃-WO₃ system at 800-1400°C were investigated using X-ray diffraction. Two binary-oxide phases—In₆WO₁₂ and In₂(WO₄)₃—were found to be stable over the range 800-1200°C. Heating the binary-oxide phases above 1200°C resulted in the preferential volatilization of WO₃. Rietveld refinement was performed on three structures using X-ray diffraction data from nominally phase-pure In₆WO₁₂ at room temperature and from nominally phase-pure In₂(WO₄)₃ at 225°C and 310°C. The indium-rich phase, In₆WO₁₂, is rhombohedral, space group (rhombohedral), with Z=1, a=6.22390(4) Å, α=99.0338(2)° [hexagonal axes: a_H=9.48298(6) Å, c=8.94276(6) Å, a_H/c=0.9430(9)]. In₆WO₁₂ can be viewed as an anion-deficient fluorite structure in which 1/7 of the fluorite anion sites are vacant. Indium tungstate, In₂(WO₄)₃, undergoes a monoclinic-orthorhombic transition around 250°C. The high-temperature polymorph is orthorhombic, space group Pnca, with a=9.7126(5) Å, b=13.3824(7) Å, c=9.6141(5) Å, and Z=4. The low-temperature polymorph is monoclinic, space group P2₁/a, with a=16.406(2) Å, b=9.9663(1) Å, c=19.099(2) Å, β=125.411(2)°, and Z=8. The structures of the two In₂(WO₄)₃ polymorphs are similar, consisting of a network of corner sharing InO₆ octahedra and WO₄ tetrahedra.