Magnesium doped ZnO nanoparticles embedded ZnO nanorod hybrid electrodes for dye sensitized solar cells

We report a novel type of Mg doped ZnO nanoparticles (ZMP) embedded on hydrothermally grown ZnO nanorod (ZR) based photoanode dye sensitized solar cells. The crystallinity, composition and morphology of the photoanodes were characterized by using X-ray diffraction analysis, X-ray photoelectron spectroscopy and scanning electron microscopy. The amount of dye absorbed in the photoanode was observed using UV visible spectral analysis. The improved internal resistance and charge-transfer kinetics of the fabricated cells were analyzed using electrochemical impedance spectroscopy. The ZMP embedded electrode of low thickness (~2.5 μm) gained an enhanced short-circuit current density of 8.56 mA/cm², open-circuit photo voltage of 0.71 V, fill factor of 0.51, and overall conversion efficiency of 2.91 % under 1 sun illumination. This shows high conversion efficiency and performance than that of ZnO nanorod (η ~ 0.22 %) and bare ZnO nanoparticles (ZP) embedded ZnO nanorod (η ~ 1.04 %) based cells. The presence of Mg ions in the ZnO nanoparticle hinders the interfacial recombination of the photo-excited electrons with the electrolyte and also shows better dye absorption than that of ZR. These factors can significantly enhance solar-cell performance and increase the efficiency of the ZMP based dye sensitized solar cells.     

Photochemical performance of ZnO nanostructures in dye sensitized solar cells

In this work, the photoconversion efficiencies of ZnO having diverse microstructures and structural defects have been investigated. A conversion efficiency of 1.38% was achieved for the DSSCs fabricated with as prepared ZnO nanorods having minimum vacancy defects and a favourable one dimensional directional pathway for electron conduction. The DSSCs fabricated with ZnO nanoparticles exhibited relatively low conversion efficiency of 1.004% probably due to multiple trapping/detrapping phenomena within the grain boundaries and ZnO flowers though exhibited a high dye adsorption capability exhibited the lowest conversion efficiency of 0.59% due to a high concentration of structural defects. Based on the experimental evidences, we believe that the type of defects and their concentrations are more important than shape in controlling the overall performance of ZnO based DSSCs.     

Improved efficiency of TiO2 nanotubes in dye sensitized solar cells by decoration with TiO2 nanoparticles

In the present work we investigate the effect of TiCl₄ treatments on the photoconversion efficiency of TiO₂ arrays used in dye sensitized solar cell. The results clearly show that by an appropriate treatment the decoration of the TiO₂ nanotube arrays with TiO₂ nanocrystallites of a typical size of 3 nm can be achieved. These particles can be converted to mixture of anatase and rutile phase by annealing in air. This decoration of the TiO₂ nanotubes leads to a significantly higher specific dye loading and, for certain annealing treatments, to a doubling of the solar cell efficiency (in our case from 1.9% to 3.8% of AM 1.5 conditions) can be achieved.     

Barrier effect of dendrons on TiO2 particles in dye sensitized solar cells

The short circuit current of dye sensitised solar cells increased significantly by the simple addition of polyester hydroxyl acetylene bis(hydroxymethyl)propanoic acid dendrons on TiO(2) nanoparticles, resulting in a very high overall energy conversion efficiency.     

Detailed investigations of ZnO photoelectrodes preparation for dye sensitized solar cells

Wurtzite ZnO hexagonal nanopyramids were successfully synthesized in the liquid phase from homogeneous methanolic solutions of zinc acetate and tetramethylammonium hydroxide at an excess of zinc ions. The formation and properties of the nanocrystals were examined as a function of synthesis conditions. No significant influence of the [Zn(2+)]/[OH(-)] ratio was noticed on the final particle size, in spite of increased amounts of OH(-) ions, which tend to accelerate the particle nucleation and growth. Nevertheless, the reactant concentration ratio influences the surface properties of the ZnO nanocrystals. Mesoporous ZnO films were prepared by doctor blading ethanolic pastes containing ZnO nanoparticles and ethyl cellulose onto FTO conductive glass substrate followed by calcination. Additionally, the influence of a plasticizer (triacetin)-used during the paste preparation-on the film quality was investigated. A higher content of ZnO nanoparticles and plasticizer in the pastes improved the film quality. Four different temperatures (i.e., 400, 425, 450, and 475 °C) were used for the film calcination and their influence on the structural properties of the films was characterized. In principle, increasing the calcination temperature goes hand in hand with an increase of particle size, as well as the pore diameter and reduction of the surface area. Suitable mesoporous films were employed as photoanodes in dye sensitized solar cells (DSSCs). In order to assess the effect of the varied parameters on complete DSSC devices-using cis-diisothiocyanato-bis(2,2'-bipyridyl-4,4'-dicarboxylato) ruthenium(II)bis(tetrabutylammonium (N719) as a sensitizer-incident photon to current efficiency (IPCE) and current voltage measurements were carried out. The IPCE measurements confirmed photoinduced electron injection from the dye, reaching IPCE values up to 76%. Furthermore, current-voltage characteristics of complete cells emphasized the importance of the proper preparation methods and temperatures. These features are important assets for the preparation of nanocrystalline ZnO based photoelectrodes and for improving the DSSC performance.     

CdS and CdSe quantum dots subsectionally sensitized solar cells using a novel double-layer ZnO nanorod arrays

We report a novel approach for synthesizing CdS and CdSe quantum dots subsectionally sensitized double-layer ZnO nanorods for solar cells, which are comprised of CdS QDs-sensitized bottom-layer ZnO NRs and CdSe QDs-sensitized top-layer ZnO NRs. X-ray diffraction study and scanning electron microscopy analysis indicate that the solar cells of subsectionally sensitized double-layer ZnO NRs, which are the hexagonal wurtzite crystal structure, have been successfully achieved. The novel structure enlarged the range of absorbed light and enhanced the absorption intensity of light. The I-V characteristics show that the double-layer structure improved both the current density (J_sc) and fill factor (FF) by 50%, respectively, and power conversion efficiency (η) was increased to twice in comparison with the CdS QDs-sensitized structure.     

Improved conversion efficiency in dye-sensitized solar cells based on electrospun Al-doped ZnO nanofiber electrodes prepared by seed layer treatment

The application of electrospun nanofibers in electronic devices is limited due to their poor adhesion to conductive substrates. To improve this, a seed layer (SD) is introduced on the FTO substrate before the deposition of the electrospun composite nanofibers. This facilitates the release of interfacial tensile stress during calcination and enhances the interfacial adhesion of the AZO nanofiber films with the FTO substrate. Dye-sensitized solar cells (DSSC) based on these AZO nanofiber photoelectrodes have been fabricated and investigated. An energy conversion efficiency (η) of 0.54-0.55% has been obtained under irradiation of AM 1.5 simulated sunlight (100 mW/cm²), indicating a massive improvement of η in the AZO nanofiber film DSSCs after SD-treatment of the FTO substrate as compared to those with no treatment. The SD-treatment has been demonstrated to be a simple and facile method to solve the problem of poor adhesion between electrospun nanofibers and the conductive substrate.     

水热法可控合成二氧化钛纳米晶及其在染料敏化太阳能电池中的应用

本文报道了水热法可控合成二氧化钛纳米晶及其在染料敏化太阳能电池中的应用.选择合适的有机碱胶化剂,能很好地控制二氧化钛纳米晶的生长,形成不同形貌和粒径的锐钛矿型二氧化钛纳米晶颗粒.染料敏化太阳能电池光电性能测试结果表明,以四乙基氢氧化铵为胶化剂合成的边长为8～13nm的正方形二氧化钛纳米晶构成的光阳极光电性能优于以四丁基氢氧化铵为胶化剂合成的边长为7～10nm的正方形二氧化钛纳米晶以及长18～35nm,宽10～18nm的长方形二氧化钛纳米晶构成的光阳极.用较高浓度的四甲基氢氧化铵胶化剂能合成球形或椭球形亚微米级二氧化钛颗粒,以其为散射中心在光阳极中构建散射层,染料敏化太阳能电池的光电转换效率能由6.77%提高到8.18%.     

Improved photoelectric performance of DSSCs based on TiO2 nanorod array/Ni-doped TiO2 compact layer composites film

Journal of Solid State Electrochemistry - In spite of the TiO2 compact layer (TCL) being widely used, it still needs more study. This paper took Ni-doped TCLs as the research target, using an...     

Kinetics of electron recombination of dye-sensitized solar cells based on TiO2 nanorod arrays sensitized with different dyes

The performance and electron recombination kinetics of dye-sensitized solar cells based on TiO(2) films consisting of one-dimensional nanorod arrays (NR-DSSCs) which are sensitized with dyes N719, C218 and D205, respectively, have been studied. It has been found that the best efficiency is obtained with the dye C218 based NR-DSSCs, benefiting from a 40% higher short-circuit photocurrent density. However, the open circuit photovoltage of the N719 based cell is 40 mV higher than that of the organic dye C218 and D205 based devices. Investigation of the electron recombination kinetics of the NR-DSSCs has revealed that the effective electron lifetime, τ(n), of the different dye based NR-DSSCs shows the sequence of C218 > D205 > N719. The higher V(oc) with the N719 based NR-DSSC is originated from the more negative energy level of the conduction band of the TiO(2) film. In addition, in comparison to the DSSCs with the conventional nanocrystalline particles based TiO(2) films, the NR-DSSCs have shown over two orders of magnitude higher τ(n) when employing N719 as the sensitizer. Nevertheless, the τ(n) of the DSSCs with the C218 based nanorod arrays is only ten-fold higher than that of the nanoparticles based devices. The remarkable characteristic of the dye C218 in suppressing the electron recombination of DSSCs is discussed.     

Fabrication and performance of nanoporous TiO2/SnO2 electrodes with a half hollow sphere structure for dye sensitized solar cells

The incorporation of nano-crystalline semiconductors with novel kinds of ordered microstructure is a very important area of research in the field of dye sensitized solar cells. A sol–gel method involving hydrolysis of titanium isopropoxide was used to form TiO₂ nanoparticles on the surface of SiO₂ spheres. In this process, 1, 5, or 10 wt% of SnCl₂.2H₂O was added to the sol–gel solution. To prepare TiO₂/SnO₂ nanoparticles with a half hollow sphere structure, SiO₂ was removed with NaOH solution. The crystal phase, crystal shape, and surface properties of the metal oxide nanocrystals were studied by x-ray diffraction and scanning electron microscopy. The photovoltaic performance of the TiO₂/SnO₂ nanoparticles with half hollow sphere structures was measured. The dye sensitized solar cell using nanoporous TiO₂ as electrode materials exhibits an overall conversion efficiency of 7.36% with a light intensity of 100 mW/cm². The short circuit photocurrent (I_sc), open circuit photovoltage (V_oc), and conversion efficiency (η) of these solar cells were improved over conventional materials.     

Improvement of the performance of dye sensitized solar cell using ZnO nanorods array deposited with Ag nanoparticles as photoanode

Well-aligned zinc oxide (ZnO) nanorods (NRs) arrays deposited with Ag nanoparticles (NPs) are prepared by a liquid phase epitaxial growth process followed by a reduction of Ag on the surface of the ZnO NRs. Transmission electron microscopy images show that most Ag NPs are deposited on the upper part of the ZnO NRs, and the overall optical absorption in the range of visible light can be enhanced due to the surface plasmon resonance of the Ag NPs. ZnO NRs with and without Ag NPs are used to assemble dye sensitized solar cells. Devices fabricated from the Ag NPs/ZnO NRs composite arrays exhibit a higher open voltage, short circuit current and fill factor than that fabricated from the bare ZnO NRs array, thus, the overall efficiency of the as-fabricated cell is increased from less than 0.5?% to 0.8?%. The main reason for the enhancement of the device performance may be ascribed to that the electron transfer back from ZnO to the dye and electrolyte is blocked by the Schottky barrier at the Ag/ZnO interface, resulting in a great increase of the electron density at the ZnO conduction band.     

Dual-functional ZnO nanorod aggregates as scattering layer in the photoanode for dye-sensitized solar cells

A bilayered ZnO photoanode was constructed for dye-sensitized solar cells with a high conversion efficiency of 4.0%. One layer made of ZnO nanocrystallites increases dye adsorption, and the other consisting of ZnO nanorod aggregates provides a directed electron pathway for the electron transport together with a prominent aggregation-induced light scattering.     

Fermi energy level tuning for high performance dye sensitized solar cells using sp2 selective nitrogen-doped carbon nanotube channels

Here, we find that doping sp(2) selective nitrogen, N sp(2), into carbon nanotube (CNT) channels induces a positive shift in the Fermi level of TiO(2) photoelectrodes. It is found that this results in the large diffusion coefficient of solar driven electrons for increasing the photocurrent as well as in the low recombination rate for improving open circuit voltage with 0.74 V, which could not be overcome by using pristine CNT channels with 0.66 V.     

Dye-sensitized solar cells based on a single-crystalline TiO2 nanorod film

Highly crystalline TiO2 nanorods with lengths of 100-300 nm and diameters of 20-30 nm have been synthesized by a hydrothermal process in a cetyltrimethylammonium bromide surfactant solution. The microstructure measured by X-ray diffraction and high-resolution transmission electron microscopy was a pure highly crystalline anatase phase with a long nanorod shape. The addition of a triblock copolymer poly(ethylene oxide)100-poly(propylene oxide) 65-poly(ethylene oxide)100 (F127) decreased the length of the nanorods and kept the rod shape of the particles even after sintering at high temperatures. The rod shape kept under high calcination temperatures contributed to the achievement of the high conversion efficiency of light-to-electricity as discussed in the paper. A high conversion efficiency of light-to-electricity of 7.29% was obtained with the TiO2 single-crystalline anatase nanorod cell.     

A swift dye uptake procedure for dye sensitized solar cells

Solar cells based on swift self-assembled sensitizer bis(tetrabutylammonium)-cis-di(thiocyanato)-N,N'-bis(4-carboxylato-4'-carboxylic acid-2,2'-bipyridine)ruthenium(II) (N719) on double layers of 12 + 4 microm thick nanocrystalline TiO2 films exhibit the incident monochromatic photon-to-current conversion efficiency (IPCE) 90% and show a short circuit current density of 17 mA cm(-2), 750 mV open circuit potential and 0.72 fill factor yielding power conversion efficiencies over 9.18% under AM 1.5 sun. For the first time highest power conversion efficiencies are obtained for dye sensitized solar cells using a swift self-assembled procedure.     

Ultrafast fluorescence studies of dye sensitized solar cells

Time-resolved fluorescence spectra from the RuN719 dye exhibit very short lifetimes (<30 fs) in solutions, on non-injecting substrates and on injecting ones. This reveals <10 fs intramolecular energy redistribution competing with the injection. We conclude that injection proceeds on a sub-10 fs time scale from non-thermalized levels of the dye.     

Nanocrystalline TiO2 solar cells sensitized with InAs quantum dots

We report nanocrystalline TiO2 solar cells sensitized with InAs quantum dots. InAs quantum dots of different sizes were synthesized and incorporated in solar cell devices. Efficient charge transfer from InAs quantum dots to TiO2 particles was achieved without deliberate modification of the quantum dot capping layer. A power conversion efficiency of about 1.7% under 5 mW/cm2 was achieved; this is relatively high for a nanocrystalline metal oxide solar cell sensitized with presynthesized quantum dots, but this efficiency could only be achieved at low light intensity. At one sun, the efficiency decreased to 0.3%. The devices are stable for at least weeks under room light in air.     

Role of nanochemical environments in porous TiO2 in photocurrent efficiency and degradation in dye sensitized solar cells

Elongated dye sensitized solar cells with a thickness gradient of the nanoporous TiO2 front electrode were used to assess the impact of the layer thickness on photocurrent and degradation. The photocurrent efficiency passes through a maximum (in our case at about 12 microm). Interestingly, the degradation rate also strongly depends on the layer thickness and is about 3 times faster for a 15-microm cell (in comparison with a 1-microm cell). To explain these nonanticipated results, a model to describe the I3(-)/I- concentration within a typical dye sensitized solar cell under steady-state conditions was derived. It includes the nanoporous TiO2 layer and a bulk solution with their different mobilities for the electrolyte species. Using typical parameters from the literature, it turned out that, despite the fact that the initial I- concentration is about 1 order of magnitude larger and the assumed diffusion coefficient is 1.3 times higher, the depletion of the I- concentration at the TiO2/FTO front contact happens to be in the same range as the depletion of the I3(-) concentration at the back contact. This stresses the importance of iodide in nanoporous environments for both the maximum attainable photocurrent and its role in the regeneration of the oxidized dye. Enhanced degradation rates might be related to poor iodide supply, since the oxidized state cannot be regenerated efficiently.     

High efficiency solar cell based on dye sensitized plasma treated nano-structured TiO2 films

Radio frequency (RF) plasma treatment of nano-structured TiO₂ was carried out to enhance the efficiency of dye-sensitized solar cell. Relative change in surface chemistry and hydrophilic characteristics was investigated by X-ray photoelectron spectroscopy (XPS) and contact angle measurements. Increase in surface hydrophilic and carboxyl functionality had enhanced the dye molecule adsorption. Plasma treatment has also increased proportion of Ti³⁺ surface site which supported transport of electron and hole between dye molecules and photoelectrode. Plasma treated TiO₂ at optimum condition had increased efficiency by 40% relative to untreated TiO₂.