Study on the bias-dependent effects of proton-induced damage in CdZnTe radiation detectors using ion beam induced charge microscopy

The influence of damage induced by 2 MeV protons on CdZnTe radiation detectors is investigated using ion beam induced charge (IBIC) microscopy. Charge collection efficiency (CCE) in irradiated region is found to be degraded above a fluence of 3.3 × 10¹¹ p/cm² and the energy spectrum is severely deteriorated with increasing fluence. Moreover, CCE maps obtained under the applied biases from 50 V to 400 V suggests that local radiation damage results in significant degradation of CCE uniformity, especially under low bias, i. e., 50 V and 100 V. The CCE nonuniformity induced by local radiation damage, however, can be greatly improved by increasing the detector applied bias. This bias-dependent effect of 2 MeV proton-induced radiation damage in CdZnTe detectors is attributed to the interaction of electron cloud and radiation-induced displacement defects.     

Segments of a commercial Ge-doped optical fiber as a thermoluminescent dosimeter in radiotherapy

Optical fibers have been proposed as dosimeters in both diagnostic and radiotherapy applications. A commercial germanium (Ge)-doped silica fiber with a 50 μm core diameter which showed good thermoluminescence (TL) properties was selected for this study. The radiation sources used were a high dose rate brachytherapy iridium-192, MV photon and MeV electron beams from a linear accelerator. The coating of the fiber was chemically removed and then annealed at 400 °C for 1 h prior to irradiation. After irradiation, the fiber was read on a Harshaw Model 3500 TLD reader. The optical fiber had one well-defined glow peak at 327 ± 2 °C at all the radiotherapy energies. The dose response was linear within the clinical relevant dose for all these energies. Reproducibility was mainly within 4–6% (one standard deviation) for high energy photons and electrons. The fiber was found to be energy independent within the MV photon energy range. At room temperature the fading up until 1 month was around 6% which was within the 6% uncertainty of the sensitivity calibration of the fiber. Re-using the fiber four times did not significantly alter the sensitivity factor. The optical fiber was found to be dose rate as well as angular independent. Central axis depth dose curves of both 10 MV photons and 12 MeV electrons using the fiber showed relatively good agreement to standard depth dose curves in water within 4%. The Ge-doped fiber is a promising TL dosimeter but improvements have to be made to reduce the reproducibility within 3% for high energy photons and electrons.     

Wide-field imaging using a tunable terahertz free electron laser and a thermal image plate

The appearance of intense terahertz sources such as quantum cascade laser and free electron laser opens up new opportunities for 2D imaging. Though microbolometer and pyroelectric arrays are promising recorders, they are of small size and cannot be used when wide-field imaging in the longwave region is required. We applied for terahertz imaging 3″ × 3″ and 6″ × 6″ Macken Instruments Inc. “thermal image plates”, a set of thermal sensitive phosphor screens operating in a room temperature environment. The Novosibirsk free electron laser was used as a source of radiation. We have found that the response of thermal image plate is linear until the relative quenching is less than 60% of the initial luminescence intensity. The response curve follows the Seitz–Mott law. The threshold sensitivity was found to be 100 mW/cm² at 1.5 THz and 40 mW/cm² at 2.3 THz. Interferograms, holograms, and terahertz beam spatial distributions recorded in the spectral range of 1.2–2.5 THz are given as examples.     

Electron penetration depth in amorphous AlN exploiting the luminescence of AlN:Tm/AlN:Ho bilayers

The penetration depth of electron in amorphous aluminum nitride (AlN) is determined in terms of energy loss per unit length using electron beam in a cathodoluminescence (CL) apparatus. Thin films bilayers of holmium doped aluminum nitride (AlN:Ho) and thulium doped aluminum nitride (AlN:Tm) are deposited on silicon substrates by rf magnetron sputtering method at liquid nitrogen temperatures. The bilayers structure consisted of a 37.8 nm thick AlN:Tm film on the top of a 15.3 nm thick AlN:Ho film. Electron beam of different energies are allowed to penetrate the AlN:Tm/AlN:Ho bilayers film. The spectroscopic properties of AlN:Ho and AlN:Tm, the thickness of the film and the energies of electron beam are used to calculate the penetration depth of electron in amorphous AlN. Electron beam of 2.5 keV energy was able to pass through the 37.8 nm thick AlN:Tm film. The electron penetration depth for AlN is found to be 661.4 MeV/cm.     

Ion beam as a probe to study the behavior of hydrogen on silicon surfaces

Hydrogen adsorption and its behavior on Si surfaces is studied by ion beam techniques in the energy range of MeV–keV. Elastic recoil detection analysis employing MeV ion beams is one of the most reliable experimental techniques for direct determination of absolute hydrogen coverages on Si surfaces. Results of its application to Si(1 0 0) and Si(1 1 1) clean surfaces are described. Important new results of the role of adsorbed hydrogen on the growth process or structures of metallic thin films on Si(1 1 1) surfaces also are described. Characterization of the growth process or structure of the thin films, as well as the characterization of hydrogen, is performed by ion beam techniques.     

Hydrogen analysis in diamond like carbon by elastic recoil detection

Among the available surface analytic instruments, elastic recoil detection (ERD) is known as a reliable method for hydrogen analysis. Since conventional fluence determination i.e. beam current integration is incredible at a large tilt angle, ion fluence is determined by the scattering spectrum that is simultaneously measured with recoil spectrum. However scattering cross sections deviate Rutherford values in the ERD energy of 1–3 MeV. Carbon scattering cross section is different from Rutherford value for higher beam energies over 1.8 MeV. As a result hydrogen content is exaggerated when fluence is determined by carbon matrix because of fluence underestimation due to lower value of scattering cross section than Rutherford’s. Therefore in order to quantify hydrogen in diamond like carbon (DLC) incident beam energy lower than 1.6 MeV should be used where carbon scattering cross sections are well agreed with Rutherford’s.     

Optimization considerations for a SASE free electron laser based on a superconducting undulator

A self amplified spontaneous emission (SASE) free electron laser (FEL) based on a new generation superconducting planar undulator, is optimized. It is shown that the laser wavelength should be down to soft X-rays range (～2–3 nm) of the spectrum via a dedicated undulator driven by a 1 GeV electron linear accelerator (linac). Numerical calculations and simulation results of the three main performance parameters for SASE operation, namely 1D gain length (L_G,1D), saturation power (P_sat) and saturation length (L_sat), are compared and discussed.     

Optimal ablation of fluorine-doped tin oxide (FTO) thin film layers adopting a simple pulsed Nd:YAG laser with TEM00 mode

In material processing, a laser system with optimal laser parameters has been considered to be significant. Especially, the laser ablation technology is thought to be very important for fabricating a dye-sensitized solar cell (DSSC) module with good quality. Moreover, the TEM₀₀ mode laser beam is the most dominant factor to decide the incident photon to current conversion efficiency (IPCE) characteristics. In order to get the TEM₀₀ mode, a pin-hole is inserted within a simple pulsed Nd:YAG laser resonator. And the spatial field distribution is measured by using three pin-hole diameters of 1.6, 2.0 and 4.0 mm, respectively. At that moment, each case has the same laser beam energy by adjusting the discharge voltage and pulse per second (pps). From those results, it is known that the pin-hole size of 1.6 mm has the perfect TEM₀₀ mode. In addition, at the charging voltage of 1000 V, 10 pps, the feeding speed of 6.08 mm/s and the overlapping rate (OL) of 62%, the scanning electron microscope (SEM) photograph of fluorine-doped tin oxide (FTO) thin film layers shows the best ablation trace.     

Picosecond molecular switch based on the influence of photogenerated electric fields on optical charge transfer transitions

A concept for a picosecond molecular switch is demonstrated using a photoinduced electron transfer reaction in a covalently linked, fixed distance donor–acceptor molecule D–A linked to a perylene-3,4-dicarboximide chromophore, C. The chromophore C possesses a strong charge transfer transition in its optical spectrum. Selective excitation of C within D–A–C using 530 nm, 130 fs laser pulses produces^1 * C, which undergoes singlet–singlet energy transfer to produce^1 * D, which in turn transfers an electron to A. If the D–A–C system is selectively excited with 416 nm, 130 fs laser pulses to produce D ⁺ – A ⁻ –C prior to excitation of C with 530 nm, 130 fs laser pulses, a 25% lower yield of^1 * C is generated. The intense local electric field produced by D ⁺ – A ⁻ causes a 15 nm electrochromic red shift of the charge transfer absorption of C. Thus, the absorption of C at 530 nm is significantly diminished by the presence of D ⁺ – A ⁻ . The need to use two laser pulses with different wavelengths to observe these effects, and the resulting picosecond time response makes it possible to consider applications of this concept in the design of molecular switches.     

Effect of phosphorus irradiation on the structural,electrical, and optical characteristics of ZnO thin films

Phosphorus irradiation at a low energy (50 keV) and at a dosage of 8×10¹⁴ ions/cm² was carried out on 〈002〉 ZnO films grown by using a pulsed laser deposition technique (Sample A). Subsequent rapid thermal annealing at 650 °C and 750 °C was performed to remove defects resulting from the irradiation (samples B and C, respectively). Atomic force microscopy was used to determine the root mean square roughness, which was 10.07, 8.66, and 9.31 nm for samples A, B, and C, respectively. Low-temperature photoluminescence measurements revealed increased deep-level defect peaks following irradiation; however, the subsequent annealing minimized the defects. Although the dominant donor-bound exciton peak verifies the n-type conductivity of the films, the free–electron–to–acceptor and donor-to-acceptor pair peaks in the irradiated samples confirm an increase in acceptor concentration.     

Photo-absorption studies on carbonyl sulphide in 30,000–91,000 cm−1 region using synchrotron radiation

Photo-absorption spectrum of carbonyl sulphide (OCS) is recorded in 30,000–91,000 cm^?1 (3300–1050 Å) region at an average resolution of 1.2 Å using Photo-physics beamline on the 450 MeV Indus-1 synchrotron radiation source at RRCAT Indore, India. Owing to significant absorption cross section dependence, spectra of OCS are recorded at various pressures (0.001–5 mbar) to optimize the S/N ratio for band systems appearing at different energy regions. The spectral region below 70,000 cm^?1 has contributions from dissociation mechanism of the ground state of OCS and three valence band systems arising from promotion of a 3π electron to 4π and 10σ orbital. Improved S/N ratio helped in unambiguous assignment of the valence band progressions at 42,000–48,000 cm^?1, 53,000–62,000 cm^?1 and 63,500–70,000 cm^?1 regions to the ¹Δ←X¹Σ⁺ transition, the relatively intense and sharp bands of ¹Π←X¹Σ⁺ transition and intense but broad bands of ¹Σ⁺←X¹Σ⁺ transition, respectively, and obtain the vibrational frequencies. Above 70,000 cm^?1 Rydberg series arising from s, p, d and f orbitals converging to the ionic ground state X²Π of OCS⁺ (90,121 cm^?1) are identified. Long progression in the first few members of the Rydberg series is suggestive of mixed valence character. Quantum defects are evaluated and used to discuss the nature of the molecular orbital. The present study provides a unifying picture of the VUV photo-absorption spectrum of OCS up to its first ionization limit.     

Laser diode end-pumped passively Q-switched Tm,Ho:YLF laser with Cr:ZnS as a saturable absorber

Output performance of a continuous-wave (CW) laser diode end-pumped passively Q-switched Tm,Ho:YLF laser is demonstrated with a Cr:ZnS crystal as the saturable absorber. We particularly investigate the influence of saturable absorber's position in the resonator when the Cr:ZnS crystal is placed close to and far from the laser beam waist. We compare the experimental results at the two different positions, and find that the laser shows unusual output characteristics when the Cr:ZnS saturable absorber is placed close to the beam waist. The pulse width and the pulse energy almost keep constant, measured about 1.25 μs and 4 μJ respectively, when the pump power is changed in the range of 1–1.9 W. Moreover, the pulse repetition frequency can be tuned between 1.3 kHz and 2.6 kHz by changing the pump power. The output wavelength of the passively Q-switched laser shifts to 2053 nm from 2067 nm in CW operation.     

Effect of laser incident energy on the structural,morphological and optical properties of Cu2ZnSnS4 (CZTS) thin films

The polycrystalline Cu₂ZnSnS₄ (CZTS) thin films have been prepared by pulsed laser deposition (PLD) method at room temperature. The laser incident energy was varied from 1.0 at the interval of 0.5–3.0 J/cm². The effect of laser incident energy on the structural, morphological and optical properties of CZTS thin films was studied by means of X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and optical absorption. The studies reveal that an improvement in the structural, morphological and optical properties of CZTS thin films with increasing laser incident energy up to 2.5 J/cm². However, when the laser incident energy was further increased to 3.0 J/cm², leads to degrade the structural, morphological and optical properties of the CZTS thin films.     

Effect of electron beam on structural,linear and nonlinear properties of nanostructured Fluorine doped ZnO thin films

Electron beam induced effects on Fluorine doped ZnO thin films (FZO) grown by chemical spray pyrolysis deposition technique were studied. The samples were exposed to 8 MeV electron beam at different dose rate ranging from 1 kGy to 4 kGy. All films exhibit a polycrystalline nature which shows an increase in crystallanity with irradiation dosages. The electron beam irradiation effectively controls the films surface morphology and its linear optical characteristics. Z-Scan technique was employed to evaluate the sign and magnitude of nonlinear refractive index and nonlinear absorption coefficient using a continuous wave laser at 632.8 nm as light source. Enhancement in the third order nonlinear optical properties was were noted due to electron beam irradiation. Tailoring the physical and NLO properties by electron beam, the FZO thin films becomes a promising candidate for various optoelectronic applications such as phase change memory devices, optical pulse compression, optical switching and laser pulse narrowing.     

All fiber passively mode locked zirconium-based erbium-doped fiber laser

All passively mode locked erbium-doped fiber laser with a zirconium host is demonstrated. The fiber laser utilizes the Non-Linear Polarization Rotation (NPR) technique with an inexpensive fiber-based Polarization Beam Splitter (PBS) as the mode-locking element. A 2 m crystalline Zirconia–Yttria–Alumino-silicate fiber doped with erbium ions (Zr–Y–Al-EDF) acts as the gain medium and generates an Amplified Spontaneous Emission (ASE) spectrum from 1500 nm to 1650 nm. The generated mode-locked pulses have a spectrum ranging from 1548 nm to more than 1605 nm, as well as a 3-dB bandwidth of 12 nm. The mode-locked pulse train has an average output power level of 17 mW with a calculated peak power of 1.24 kW and energy per pulse of approximately 730 pJ. The spectrum also exhibits a Signal-to-Noise Ratio (SNR) of 50 dB as well as a repetition rate of 23.2 MHz. The system is very stable and shows little power fluctuation, in addition to being repeatable.     

Template-free sonochemical synthesis of hierarchically porous NiO microsphere

A novel template-free sonochemical synthesis technique was used to prepare NiO microspheres combined with calcination of NiO_2.45C_0.74N_0.25H_2.90 precursor at 500 °C. The NiO microspheres samples were systematically investigated by the thermograviometric/differential scanning calorimetry (TG/DSC), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), fourier-transformed infrared spectroscopy (FT-IR), Brunnauer–Emmett–Teller (BET) nitrogen adsorption–desorption isotherms, laser particle size analyzer, and ultraviolet–visible spectroscopy (UV–Vis). The morphology of the precursor was retained even after the calcination process, and exhibited hierarchically porous sphericity. The morphology changed over the ultrasonic radiation time, and the shortest reaction time was 70 min, which was much less than 4 h for the mechanical stirring process. The mechanical stirring was difficult to form the complete hierarchically porous microsphere structure. The BET specific surface area and the median diameter of the hierarchically porous NiO microspheres were 103.20 m²/g and 3.436 μm, respectively. The synthesized NiO microspheres were mesoporous materials with a high fraction of macropores. The pores were resulted from the intergranular accumulation. The ultraviolet absorption spectrum showed a broad emission at the center of 475 nm, and the band gap energy was estimated to be 3.63 eV.     

Femtosecond laser ablation of cadmium tungstate for scintillator arrays

Ultrafast pulsed laser ablation has been investigated as a technique to machine CdWO₄ single crystal scintillator and segment it into small blocks with the aim of fabricating a 2D high energy X-ray imaging array. Cadmium tungstate (CdWO₄) is a brittle transparent scintillator used for the detection of high energy X-rays and γ-rays. A 6 W Yb:KGW Pharos-SP pulsed laser of wavelength 1028 nm was used with a tuneable pulse duration of 10 ps to 190 fs, repetition rate of up to 600 kHz and pulse energies of up to 1 mJ was employed. The effect of varying the pulse duration, pulse energy, pulse overlap and scan pattern on the laser induced damage to the crystals was investigated. A pulse duration of ≥500 fs was found to induce substantial cracking in the material. The laser induced damage was minimised using the following operating parameters: a pulse duration of 190 fs, fluence of 15.3 J cm⁻² and employing a serpentine scan pattern with a normalised pulse overlap of 0.8. The surface of the ablated surfaces was studied using scanning electron microscopy, energy dispersive X-ray spectroscopy, atomic force microscopy and X-ray photoelectron spectroscopy. Ablation products were found to contain cadmium tungstate together with different cadmium and tungsten oxides. These laser ablation products could be removed using an ammonium hydroxide treatment.     

Characterization of monoenergetic neutron reference fields with a high resolution diamond detector

A novel radiation detector based on an artificial single crystal diamond was used to characterize in detail the energy distribution of neutron reference fields at the Physikalisch-Technische Bundesanstalt (PTB) and their contamination with charged particles. The monoenergetic reference fields at PTB in the neutron energy range from 1.5 MeV up to 19 MeV are generated by proton and deuteron beams impinging on solid and gas targets of tritium and deuterium. The energy of the incoming particles and the variation of the angle under which the measurement is performed produce monoenergetic reference fields with different mean energies and line shapes. Well established simulation codes allow these parameters to be calculated in detail, provided the properties of the targets are known.In this paper we present high resolution neutron spectrometry measurements of different monoenergetic reference fields. The results are compared with calculated spectra taking into account the actual target parameters. The influence of deviations from the ideal case, e.g. a non homogeneous tritium distribution in a solid Ti/T-target, was investigated. Line structures in the order of 80 keV for a neutron energy of 9 MeV were resolved. The shift of the mean energy and the increasing of the width of the neutron peak with increasing pressure in the gas target in the order of 30 keV were measured.Another result is the determination of the contamination of the neutron field at 14 MeV with high energy charged particles (protons) from side reactions inside the T-target. This effect is due to the thin backing of the targets in use at PTB. It depends on the age of the target and it has to be taken into consideration for irradiations at small distances for some detectors, especially when very old targets are used.The experiments have shown that this detector is an easy to operate compact neutron spectrometer with extremely good energy resolution and that detailed structures in the line shapes of monoenergetic neutron fields can be resolved without using time-of-flight techniques.     

Experimental femtosecond laser photodisruption of rabbit sclera for minimally invasive laser sclerostomy: An in vitro study

Femtosecond laser technology, used as a minimally invasive tool in intrastromal refractive surgery, may also have potential as a useful instrument for glaucoma filtration surgery. The purpose of the present study was to evaluate the feasibility of minimally invasive laser sclerostomy by femtosecond laser photodisruption and seek the appropriate patterns of laser ablation and relevant laser parameters. A femtosecond laser (800 nm/50 fs/1 kHz), focused by a 0.1 numerical aperture (NA) objective lens, with different pulse energies and exposure times was applied to ablate hydrated rabbit sclera in vitro. The irradiated samples were examined by scanning electron microscopy (SEM). By moving a three-dimensional, computer-controlled translation stage to which the sample was attached, the femtosecond laser could produce three types of ablation patterns, including linear ablation, cylindrical aperture and rectangular cavity. With pulse energies ranging from 37.5 to 150 μJ, the linear lesions were consistently observed at the inner surface of sclera, whereas it failed to make any photodisruption if pulse energy was below the threshold value of 31.25 μJ, with the corresponding threshold intensity of 4.06×10¹⁴ W/cm². The depths of the linear lesions increased linearly with both pulse energy (37.5–150 μJ) and exposure time (0.1–0.4 s). Histological examination showed the incisions produced by femtosecond laser photodisruption had precise geometry and the edges were sharp and smooth, with no evidence of collateral damage to the surrounding tissue. Our results predict the potential application of femtosecond laser pulses in minimally invasive laser sclerostomy for glaucoma treatment.     

Wavelength tunable,high energy femtosecond laser pulses directly generated from large-mode-area photonic crystal fiber

Wavelength tunable high energy ultrashort laser pulses are generated from a large-mode-area photonic crystal fiber in anomalous dispersion (AD) regime. A simplified laser cavity design with one fine polished facet of the fiber as a cavity mirror is used. The intra-cavity dispersion compensation is achieved by a grating pair, the spatial dispersed light from which also have optical spectrum filtering effects combined with the limited aperture of the fiber core. The laser system is able to generate ultrashort pulses ranging from 494 fs (with 56 nJ pulse energy) to 1.24 ps (with 49 nJ pulse energy) at 55 MHz repetition rate. The filtering mechanism benefits the generation of high energy pulses with narrowing pulse duration in AD regime. An undulation in frequency and time domain is also observed with the increase of the pump power. Furthermore, this laser system is directly used as seed for supercontinuum generation.