基于透射光谱确定溶胶凝胶ZrO2薄膜的光学常数

基于溶胶凝胶ZrO₂薄膜的紫外/可见/近红外透射实验光谱,采用Swanepoel方法结合Wemple-DiDomenico色散模型,方便地导出了ZrO₂薄膜在200—1200nm波长范围内的光学常数,包括折射率、色散常数、膜层厚度、吸收系数及能量带隙.研究发现,溶胶凝胶ZrO₂薄膜具有高折射率(1.63—1.93,测试波长为632.8nm)、低吸收和直接能量带隙(4.97—5.63eV) 等光学特性,而且其光学常数对薄膜制备过程中的重要工艺 关键词： 光学常数 Swanepoel方法 2薄膜')" href="#">ZrO₂薄膜 热处理     

基于透射光谱确定溶胶凝胶ZrO2薄膜的光学常数

基于溶胶凝胶ZrO2薄膜的紫外/可见/近红外透射实验光谱,采用Swanepoel方法结合Wemple-DiDomenico色散模型,方便地导出了ZrO2薄膜在200-1200 nm波长范围内的光学常数,包括折射率、色散常数、膜层厚度、吸收系数及能量带隙.研究发现,溶胶凝胶ZrO2薄膜具有高折射率(1.63-1.93,测试波长为632.8 nm)、低吸收和直接能量带隙(4.97-5.63 eV) 等光学特性,而且其光学常数对薄膜制备过程中的重要工艺参数--膜层后处理温度表现出强烈的依赖性.此外,在膜层的弱吸收和中等吸收光谱区域内,计算得到的折射率色散曲线与分光光度法的测试结果基本符合,说明本实验中所建立的计算方法在确定溶胶凝胶ZrO2薄膜光学常数方面的可靠性.     

强冲击压缩下LiF，Al2O3和LiTaO3单晶的透光性

在二级轻气炮上，用高速电子相机扫描照相技术和改进的Mallory实验装置，对z切LiF，Al₂O₃(蓝宝石)和LiTaO₃单晶材料的冲击透光性进行了对比测量，并用黑密度计提取出动态图像定量化的光强对比度变化曲线.结果表明，LiF单晶在102 GPa压强下能够保持长时间的初始透光性不变，与公认的LiF具有优良的高压下透明性的认识一致.LiTaO₃单晶在实验压力(139GPa)下变成基本不透明.而Al_{关键词： 2}O₃')" href="#">Al₂O₃ LiF 3')" href="#">LiTaO₃ 光学透明性     

Si-Al2O3复合薄膜的室温铁磁性

在Si-Al₂O₃复合薄膜中观察到室温铁磁性.Si的体积百分比为15 %的Si-Al₂O₃复合薄膜的磁性最强.Si的含量影响样品的磁有序,在样品中观察到了明显的磁畴.在不同气氛下,对样品进行快速热退火.退火样品的磁性测试结果的差别表明氧空位不是样品铁磁性的主要来源.我们认为铁磁性来源于Si与Al₂O₃基质界面之间的缺陷的磁耦合.改变Si的含量可以改变缺陷密度,从而控制铁磁耦合强度. 关键词： 2O₃薄膜')" href="#">Al₂O₃薄膜 室温铁磁性 掺杂 交换相互作用     

Fe离子注入多晶Al2O3的光电子能谱研究

本文应用光电子能谱(XPS)方法分析Fe离子注入多晶Al₂O₃样品中各离子的存在状态。通过微机对谱峰进行高斯拟合处理,得出注入离子Fe不同价态的相对含量。 关键词：     

关于MgB2/Al2O3超导薄膜电阻转变和各向异性的研究

利用电子束蒸发方法将MgB₂超导薄膜沉积到Al₂O₃(001)衬底上.采用标准的四引线法研究了磁场平行和垂直超导薄膜ab平面下的电阻转变.一个激活能模型 U(T,H)=U₀(1-T/(T_c+δ))ⁿ(1-H/H 关键词： 2/Al₂O₃')" href="#">MgB₂/Al₂O₃ 超导体 电阻转变 各向异性     

12CaO·7Al2O3/5CaO·3Al2O3：Sm3+新型红色荧光粉的制备及发光性质

采用自蔓延燃烧法制备了不同Sm³⁺掺杂浓度的12CaO·7Al₂O₃（C12A7：x%Sm³⁺）荧光粉。在404 nm近紫外光激发下,观察到了位于565,599,648 nm附近的3个光发射峰,分别归属于Sm³⁺的⁴G_5/2→⁶H_J/2（J=5,7,9）能级跃迁。随着Sm³⁺掺杂浓度增加,红光发射强度呈现了先增大后减小的规律,优化的Sm³⁺掺杂摩尔分数为1.5%,发光的浓度猝灭效应可归因于Sm³⁺之间发生了交叉弛豫过程。采取混相策略,通过降低初始粉体的煅烧温度至900℃获得了12CaO·7Al₂O₃/5CaO·3Al₂O₃：1.5%Sm³⁺（C12A7/C5A3：Sm³⁺）混相荧光粉,进一步提高了红光发射强度。利用变温光致发光谱计算得到混相样品的热激活能约为200 meV,结果表明该混相荧光粉具有良好的热稳定性。     

Al2O3-Y2O3-ZrO2三相复合陶瓷的介电谱研究

采用传统的固相反应法,在1400–1500 ℃下烧结,制备得到Al₂O₃-Y₂O₃-ZrO₂三相复合陶瓷.样品的结构、形貌和电性能分别用X射线衍射(XRD)、扫描电子显微镜(SEM)及介电谱表征.XRD表明此三相复合体系无其他杂相,加入Y₂O₃及ZrO₂后使得Al₂O₃成瓷温度降低;SEM表明此体系晶粒直径为200–500 nm,并且样品随烧结温度的升高而变得更加致密,晶界更加清晰;介电损耗谱中出现峰值弛豫现象,根据Cole-Cole复阻抗谱得出其为非德拜弛豫. 关键词： 2O₃-Y₂O₃-ZrO₂三相陶瓷')" href="#">Al₂O₃-Y₂O₃-ZrO₂三相陶瓷 介电弛豫 阻抗谱 热导率     

镱铒共掺Al2O3薄膜上转换机理及其温度特性

采用中频磁控溅射法制备了镱铒共掺Al₂O₃薄膜,铒镱掺杂浓度分别为0.3%,3.6%(摩尔分数,全文同).讨论了三价铒离子529nm和549nm光致发光的上转换机理.在291.8—573.3K温度区间测量了两绿上转换光谱荧光强度比的温度特性,拟合表达式为R=5.37exp(-738/T).366 K温度时灵敏度最大,为0.0039 K^-1.结果表明镱铒共掺Al₂O₃薄膜适合作为小型、高温和高灵敏的光学温度传感材料. 关键词： 2O₃薄膜')" href="#">镱铒共掺Al₂O₃薄膜 中频磁控溅射 上转换 荧光强度比     

PuO2和α-Pu2O3光学性质的经验势模拟

用GULP程序拟合出α-Pu₂O₃的Pu-O作用BMH经验势参数.结合氧离子壳模型势,运用分子静力学和动力学计算出PuO₂和α-Pu₂O₃理想晶体的结构参数和光学性质.结果显示：它们的空间群、晶胞参数、密度和熵等,与文献报道值接近,相对误差均小于1.2%;并计算出PuO₂和α-Pu₂O₃的高频和静态介电张量、红外介电函数谱、晶格振动 关键词： 2')" href="#">PuO₂ 2O₃')" href="#">α-Pu₂O₃ 光学性质     

多孔阳极氧化铝薄膜光学常数的确定

根据多孔阳极氧化铝(AAO)薄膜的实验透射谱(200—2500nm)，采用极值包络线算法确定其光学常数，并由此较精确地计算出AAO薄膜样品在该波段的光学常数.结果表明，多孔氧化铝薄膜表现出直接带隙(能隙约4．5eV)半导体的光学特性，且其光学常数与制样中的重要工艺参数阳极氧化电压有显著的相关性，即随阳极氧化电压的增加，AAO薄膜的厚度、折射率和光学能隙变大，消光系数减小．同时，计算得到的薄膜厚度与实测值相吻合，则说明计算结果和实验值是自洽的. 关键词： 薄膜光学 光学常数 多孔阳极氧化铝 阳极氧化电压     

磁控溅射不同厚度银膜的微结构及其光学常数

用直流溅射法在室温K9玻璃基底上制备了8.2nm—107.2nm范围内不同厚度的Ag薄膜，并用X射线衍射及计算机辅助优化程序对薄膜的微结构和光学常数进行了测试分析. 结构分析表明：制备的Ag薄膜均呈多晶状态，晶体结构均呈面心立方；随着膜厚的增加，薄膜的平均晶粒尺寸逐渐增大，晶面间距逐渐减小. 计算机辅助优化编程计算的薄膜光学常数分析表明：在波长550nm处，当膜厚小于17.5nm时，随着膜厚的增加，折射率n快速减小，消光系数k则快速增大；当膜厚大于17.5nm时，n和k逐渐趋于稳定. 关键词： 直流溅射镀膜 银膜 微结构 光学常数     

Determination of the optical constants of selenium films

The optical constants of evaporated Se films are calculated following Valeev’s method and applied to Se in the visible region. The calculated values are in good agreement with published data.     

The accuracies of photometric, polarimetric and ellipsometric methods for the optical constants of thin films

The inherent accuracies of various techniques for determining the optical constants of thin films have been assessed by computing the errors produced in n and k by known experimental errors in the optical functions being measured. The results are presented as arrays of error parallelograms in the n–k plane covering d/λ from 0.001 to 0.20 and θ from 5° to 85°.The largest regions of accuracy, in the form of annular quadrants, were obtained using the mixed photometric and polarimetric functions at small angles of incidence. Ellipsometry gives similar results at large angles of incidence but for photometry and for polarimetry the accurate regions were in the form of two lobes.The effects of errors in x and θ were also considered.     

Structural and optical characterization of DC magnetron sputtered molybdenum oxide films

Thin films of molybdenum trioxide were deposited on glass substrates employing direct current (DC) magnetron sputtering by sputtering of molybdenum at different oxygen partial pressures in the range 8 × 10⁻⁵–1 × 10⁻³ mbar and at a substrate temperature of 473 K. The glow discharge characteristics of magnetron cathode target of molybdenum were studied. The influence of oxygen partial pressure on the structural and optical properties of molybdenum trioxide films was investigated. The films formed at an optimum oxygen partial pressure of 2 × 10⁻⁴ mbar were polycrystalline in nature with orthorhombic α- phase and an optical band gap of 3.16 eV. The refractive index of the films formed at an oxygen partial pressure of 2 × 10⁻⁴ mbar decreased from 2.08 to 1.89 with increase of wavelength from 450 to 1,000 nm, respectively. Paper presented at the Third International Conference on Ionic Devices (ICID 2006), Chennai, Tamilnadu, India, Dec. 7–9, 2006.     

铈掺杂氧化铝薄膜的蓝紫色发光特性

应用中频反应磁控溅射技术制备了Al₂O₃:Ce³⁺的非晶薄膜.X射线光电子谱(XPS)检测显示薄膜中有Ce³⁺生成.这些薄膜的光致发光峰是在374nm附近,它来自于Ce³⁺离子的5d¹激发态向基态4f¹的两个劈裂能级的跃迁.发光强度强烈地依赖于薄膜的掺杂浓度,但发光峰位置不随掺杂浓度而变化.Ce³⁺含量和薄膜的化学成分是通过X射线散 关键词： 光致发光 2O₃')" href="#">Al₂O₃ 薄膜 稀土元素     

The effects of post-thermal annealing on the optical parameters of indium-doped ZnO thin films

Indium-doped ZnO thin films are deposited on quartz glass slides by RF magnetron sputtering at ambient temper- ature. The as-deposited films are annealed at different temperatures from 400 C to 800 C in air for 1 h. Transmittance spectra are used to determine the optical parameters and the thicknesses of the films before and after annealing using a nonlinear programming method, and the effects of the annealing temperatures on the optical parameters and the thickness are investigated. The optical band gap is determined from the absorption coefficient. The calculated results show that the film thickness and optical parameters both increase first and then decrease with increasing annealing temperature from 400 C to 800 C. The band gap of the as-deposited ZnO:In thin film is 3.28 eV, and it decreases to 3.17 eV after annealing at 400 C. Then the band gap increases from 3.17 eV to 3.23 eV with increasing annealing temperature from 400 C to 800 C.     

多层高反膜光学常数和厚度的反演

基于精英保留策略的遗传算法具有良好的全局寻优能力和很强的鲁棒性,基于Levenberg-Marquardt 算法的非线性最小二乘法具有快速、高效的局部收敛能力.研究了将这两种算法结合起来求解多层膜光学常数和厚度的可行性和有效性.结果表明:基于两种算法的组合反演算法综合了这两种算法的优点,能以较大的概率、较高的精度找到在实际约束条件下多层膜的光学常数和厚度,特别是在寻找全局最优解方面表现出色.根据全光谱透射拟合法基本原理,应用组合反演算法分别在考虑测量误差与不考虑测量误差两种情况下反演 15 层规整高反膜的光学常数和厚度,得到了较为精确的薄膜参数.模拟实验表明:此组合反演算法可有效地求解多层膜反演问题,在反演多层膜光学常数和厚度方面具有实际的应用价值.     

椭偏与光度法联用精确测定吸收薄膜的光学常数与厚度

介绍了一种同时利用椭偏仪和分光光度计精确测量薄膜光学常数的方法, 并详细比较了该方法与使用单一椭偏仪拟合结果的可靠性.采用可变入射角光谱型椭偏仪（VASE）表征了250—1700 nm波段辉光放电法沉积的类金刚石薄膜,研究发现当仅用椭偏参数拟合时,由于厚度与折射率、消光系数的强烈相关性,无法得到吸收薄膜光学常数的准确解.如果加入分光光度计测得的透射率同时拟合,得到的结果具有很好的惟一性.该方法无需设定色散模型即可快速拟合出理想的结果,特别适合于确定透明衬底上较薄吸收膜的光学常数. 关键词： 光学常数 光谱型椭偏仪 吸收薄膜 透射率