Ba1—x—yEuxGdyMgF4＋y复合氟化物中Eu^2＋离子的f—f跃迁线谱发射

报道了Ｇｄ＾３＋与Ｅｕ＾２＋共掺杂的钡镁复合氟化物在室温下的发射光谱中，不仅存在Ｅｕ＾２＋的带状发射，而且还出现了Ｅｕ＾２＋的４ｆ（＾６Ｐ７／２）－４ｆ（＾８Ｓ７／２）线谱发射，在该体系中，由于Ｇｄ＾３＋掺入后，诱导出一另一种Ｅｕ＾２＋的线谱发射中心，两种Ｅｕ＾２＋发射中心的激发光谱明显不同，ｆ－ｆ跃迁线谱发射的强度与Ｇｄ＾３＋及Ｅｕ＾２＋的浓度密切相关。     

Eu^2＋：Sr9Ca（PO4）6Cl2中的新型色心及其光激励发光

本文报道了Ｅｕ＾２＋：Ｓｒ９Ｃａ（ＰＯ４）６Ｃｌ２的新型色心。它的吸收带主峰分别位于７０８，７８５，８４５及９９０ｎｍ。用对应于Ｆ心吸收带和这些吸收带波长的光束分别激励样品时得到相同的光激励发光。通过对比研究表明，这些吸收带是由Ｆ心的缔合中心，即由ＦＡ心产生的。由于这些色心的吸收带偏离Ｅｕ＾２＋的发射波长（４５０ｎｍ）更远，故更适应于Ｅｕ＾２＋：Ｓｒ９Ｃａ（ＰＯ４）６Ｃｌ２光波励发光的研究和开发。     

Synthesis and characterization of Ca2Sn1-xCexO4 with blue luminescence originating from Ce^4＋ charge transfer transition

Ce^4＋-doped Ca2SnO4 with a one-dimensional structure, which emits bright blue light, is prepared by using a solid-state reaction method. The x-ray diffraction results show that the Ce^4＋ ions doped in Ca2SnO4 occupy the Sn^4＋ sites. The excitation and emission spectra of Ca2Sn1-xCexO4 appear to have broad bands with peaks at - 268nm and -442nm, respectively. A long excited-state lifetime （-83μs） for the emission from Ca2Sn1-xCexO4 suggests that the luminescence originates from a ligand-to-metal Ce^4＋ charge transfer （CT）. The luminescent properties of Ca2Snl_xCexO4 have been compared with those of Sr2CeO4, which is the only material reported so far to show Ce^4＋ CT luminescence. More interestingly, it is observed that the emission intensity of Ca2Sn1-xCexO4 with a small doping concentration （x - 0.03） is comparable to that of Sr2CeO4 in which the concentration of active centre is 100%.     

Luminescence Properties of Ca4GdO（BO3）3：RE （RE=Eu^3＋,Tb^3＋） under VUV Excitation

We experimentally investigated the VUV excitation luminescence properties of Ca4 GdO(B03)3 :RE (RE=Eu^3 , Tb^3 )Ca4GdO(BO3)3:Eu3 and Ca4GdO(BO3)3:Tb^3 emitted bright red and green colour light, respectively, under 172 nm excitation, resulting from the favorable position of the host absorption band (186 nm) and efficient energy transfer from Gd^3 to activators (e.g. Eu^3 or Tb^3 ) by means of secondary absorption in the Ca4GdO(BO3)3 matrix. The f-d transitions of Eu^3 and Tb^3 in the host lattice are depicted.     

Luminescence and Energy Transfer of Eu^2＋, Mn^2＋ in SrZnP2O7

The SrZnP2OT：Eu^2＋, Mn^2＋ phosphor is synthesized by high temperature solid state reaction. The luminescence properties and the energy transfer between Eu^2＋ and Mn^2＋ are investigated. The emission bands of this phosphor peaked at 42Ohm and 67Ohm are originated from the 5d → 4f transition of Eu^2＋ and from the 4T1 （4G） --〉 6A1 （6S） transit/on of Mn^2＋, respectively. With the increasing Mn^2＋ concentration, the intensity of fixed concentra- tion Eu^2＋ decreases and the intensity of Mn^2＋ also increases. It is suggested that there is an energy transfer from Eu^2＋ to Mn^2＋ in SrZnP2O7 host. According to Dexter＇s energy transfer formula of multipolar interaction, the energy transfer between Eu^2＋ and Mn^2＋ is due to the electric dipole-quadrupole interaction of the resonance transfer.     

NaGdF4：Eu^3＋和GdBaB9O16的VUV荧光性质

在真空紫外光激发下，六方结构的NaGdF4:Eu^3 中的Gd^3 离子吸收一个光子，将能量分两步传递给Eu^3 离子，发生红色双光子发射。立方结构的NaGdF4:Eu^3 中存在一定量的氧离子取代缺陷，使Gd^3 离子4f-5d跃迁移到177nm附近，这与惰性气体放电产生的VUV光波长一致，并且其荧光色纯度较高。在VUV激发下，GdBaB9O16中的Gd^3 离子发生双光子（紫外和红色或远红外）发射。     

BaFBr：Eu2＋的发光及电特性研究

采用高温固相反应方法制备的BaFBr：Eu2 粉末样品，未经X射线、真空紫外或紫外光辐照，用波长大于400nm的光激发样品，可观测到Eu2 的390nm发光。样品的电子自旋共振(ESR)谱证实在BaFBr：Eu2 粉末样品的制备过程中，会产生大量的晶格缺陷，分别为电子和空穴陷阱，它们在光激励发光过程中充当不可缺少的角色。本工作将BaFBr：Eu2 粉末制成压片，在其一侧制作两个电极，以研究电阻-电压关系、剩余申压随时间的变化以及与电极材料的关系等电学特性。电特性研究结果也表明，样品中有电子和空穴陷阱两类缺陷，BaFBr：Eu2 的发光，源自激发能通过这两类缺陷向Eu2 的能量传递。     

Luminescence characteristics of Eu2+ activated Ca2SiO4 Sr2SiO4 and Ba2SiO4 phosphorsfor white LEDs

<正>This paper investigates the luminescence characteristics of Eu²⁺ activated Ca₂SiO₄,Sr₂SiO₄ and Ba₂SiO₄ phosphors. Two emission bands are assigned to the f-d transitions of Eu²⁺ ions doped into two different cation sites in host lattices,and show different emission colour variation caused by substituting M²⁺ cations for smaller cations.This behaviour is discussed in terms of two competing factors of the crystal field strength and covalence.These phosphors with maximum excitation of around 370 nm can be applied as a colour-tunable phosphor for light-emitting diodes（LEDs） based on ultraviolet chip/phosphor technology.     

Eu^2＋：BaFCl光激励发光衰减的研究

制备了系列材料Ｅｕ＾２＋：ＢａＦＣｌ，测量了其光激励发光的衰减曲线，基于隧穿模型，建立了描述隧穿过程的数学模型，得出了光激励发光衰减规律，并将结果与实验进行了比较。     

Luminescence of high-pressure phases of Eu2+-activated SrB2O4

The luminescence properties of the high-pressure phases of SrB₂O₄ : Eu²⁺ were studied. Their quantum efficiencies drastically increased with transforming into a high-pressure phase, which was found to be an efficient photoluminescent material. Its emission peak position (395 nm) also shifted to longer wavelength compared with that of other phases (367 nm).     

铈铕共掺高钆氧化物玻璃的发光性能及能量传递效应

在还原气氛下, 采用高温熔融法制备了Eu²⁺/Ce³⁺共掺的高钆氧化物玻璃. 荧光性能测试显示, Ce³⁺能够有效地敏化Eu²⁺的发光, 使Eu²⁺的发光强度增强了2.3倍; 测试对比了Ce³⁺ 发光的荧光寿命随Eu²⁺的掺入前后的变化情况, 计算得出Ce³⁺→Eu²⁺ 的能量传递效率可达61.5%, 并进一步探讨了其能量传递机理. 研究表明: 在高钆氧化物玻璃中, 采用Eu²⁺ 和Ce³⁺ 共掺的方法可有效地增强Eu²⁺ 的发光性能和闪烁性能. 关键词： 发光玻璃 能量传递 荧光寿命     

白光LED用LiBaBO3:Eu2+材料发光特性研究

采用高温固相法制备了LiBaBO₃:Eu²⁺绿色发光材料.测量了Eu²⁺浓度为1mol%时样品的激发与发射光谱,其发射光谱为双峰宽谱,主峰分别为482和507nm,与理论计算值符合很好;监测482nm发射峰时,对应激发光谱的峰值为287和365nm,监测507nm发射峰时,对应的激发峰为365和405nm.研究了Eu²⁺浓度对材料发射光谱的影响,结果显示,随Eu²⁺浓度的增大,蓝、绿发射峰均发生了     

溶胶-凝胶法合成Sr3MgSi2O8:Eu3+ 红色荧光粉及其发光性能

采用溶胶-凝胶法合成了Sr_3MgSi_2O_8∶Eu~(3+)红色荧光粉,并通过X射线衍射(XRD)、傅立叶变换红外光谱(FTIR)、扫描电镜(SEM)以及荧光光谱(PL)、X射线光电子能谱(XPS)等分析方法,对不同烧结温度(950,1 050,1 150,1 250℃)热处理4 h后得到的粉体的物相、形貌及发光性能进行了表征分析。由XRD表征结果可知,制备出的样品为正交晶系的Sr_3MgSi_2O_8;由扫描电镜及比表面积的测试结果可知,经过1 150℃热处理得到的荧光粉具有最大比表面积,可达到90.213 1 m~2/g,且粒径大小均一;由红外光谱图可知:样品中含有Si—O—Si、Mg—O和Sr—O化学键;在394 nm的激发波长下,所有样品在614 nm和702 nm处出现了强发射峰,分别对应于Eu~(3+)的~5D_0→~7F_2和~5D_0→~7F_4跃迁,属红光发射。随着热处理温度的升高,样品所对应的发射峰强度呈现出先增大后减小的变化趋势,即出现温度猝灭效应;经1 150℃热处理合成的Sr_3MgSi_2O_8∶Eu~(3+)红色荧光粉的发光性能最好,即最佳的热处理温度为1 150℃。     

近红外光诱导下NaYbF4:Tm3+,Eu3+ 体系中Eu3+的上转换发光

利用水热法制备得到NaYbF₄:0.01%Tm³⁺,20%Eu³⁺上转换材料,利用X射线衍射分析、扫描电子显微镜及光谱测试技术分别对其进行了结构、形貌以及光谱性质的表征。在980 nm近红外激光激发下,得到了Eu³⁺的可见到紫外范围的上转换荧光发射。分析表明:共掺杂NaYbF₄纳米材料中Tm³⁺到Eu³⁺离子的能量传递对布居Eu³⁺离子的激发态能级,获得Eu³⁺的上转换发光起着至关重要的作用。另外,在实验中首次获得了Eu³⁺对应于³P₀→⁷F_j (j=0,1,2)能级跃迁的上转换光发射。     

Ba3WO6:Eu3+红色荧光粉的结构及其发光特性

以高温固相法成功合成了一系列Eu³⁺离子激活Ba₃WO₆红色荧光粉。分别采用X射线衍射（XRD）和荧光光谱（FL）对样品的晶体结构和发光性能进行了表征。结果表明,样品均具有立方晶系的双钙钛矿结构;Eu³⁺离子的激发谱由一个宽带（包括Eu³⁺-O^2-和W⁶⁺-O^2-电荷转移带）和若干个窄峰（4f-4f电子跃迁）组成,而跃迁⁵D₀→⁷F₁和⁵D₀→⁷F₂则构成了发射谱的主要部分。调整原材料中BaCO₃和WO₃的量的比,XRD的主衍射峰位发生红移至与标准谱完全吻合,发光强度有所提升并分析了原因。Eu³⁺离子的临界摩尔分数为0.05,临界距离（R_c）为1.263 4 nm。在314 nm或394 nm激发光下,样品发出红光（λ_max=596 nm）,色坐标为（0.618,0.342）,在LED照明、显示等领域具备一定潜力。     

助熔剂对绿色荧光粉Ba2 SiO4∶Eu2+ 颗粒形貌及发光性能的影响

采用高温固相法在弱还原气氛下合成了Ba₂SiO₄∶Eu²⁺绿色荧光粉,利用X射线衍射、扫描电子显微镜和荧光分光光度计考察了不同助熔剂对Ba₂SiO₄∶Eu²⁺荧光粉的结晶度、物相纯度、颗粒形貌和发光强度的影响,并详细讨论了不同助熔剂在荧光粉制备过程中的作用机理。结果表明:不加助熔剂时样品存在BaSi₂和SiO₂杂相;利用NH₄F、Na₂CO₃或H₃BO₃作为助熔剂时会抑制BaSi₂杂相的形成,而BaF₂作助熔剂可以得到纯的斜方晶系。与未加助熔剂合成的荧光粉相比,添加质量分数为2% 的BaF₂、NH₄F或Na₂CO₃后合成样品的发光强度分别提高了138%,81%和34%;而质量分数为2%的H₃BO₃作助熔剂时,荧光粉的发光强度反而降低了14%。BaF₂作助熔剂合成的荧光粉颗粒形貌接近球形,以NH₄F、Na₂CO₃或H₃BO₃作助熔剂合成的荧光粉颗粒形貌分别为不规则片状、纺锤体形和不规则多边形大颗粒。