Ionoluminescence and photoluminescence studies of Ag ion irradiated kyanite

Ionoluminescence (IL) of kyanite single crystals bombarded with 100 MeV swift Ag⁸⁺ ions with fluences in the range 1.87-7.5×10¹¹ ions/cm² has been studied. A pair of sharp IL peaks at ∼689 and 706 nm along with broad emission in the region 710-800 nm are recorded in both crystalline and pelletized samples. Similar results are recorded in Photoluminescence (PL) of pelletized kyanite bombarded with same ions and energy with fluences in the range 1×10¹¹-5×10¹³ ions/cm² with an excitation of 442 nm laser beam. The characteristic pair of sharp emission peaks at 689 and 706 nm in both IL and PL is attributed to luminescence centers activated by Fe²⁺ and Fe³⁺ ions. The reduction in IL and PL bands intensity with increase of ion fluence might be attributed to degradation of Si-O (2ν₃) bonds, present on the surface of the sample.     

Luminescence and defect studies of YAlO3:Dy3+, Sm3+ single crystals exposed to 100 MeV Si7+ ion beam

Ionoluminescence (IL) and photoluminescence (PL) spectra for different rare earth ions (Sm³⁺ and Dy³⁺) activated YAlO₃ single crystals have been induced with 100 MeV Si⁷⁺ ions with fluence of 7.81×10¹² ions cm^?2. Prominent IL and PL emission peaks in the range 550–725 nm in Sm³⁺ and 482–574 nm in Dy³⁺ were recorded. Variation of IL intensity in Dy³⁺ doped YAlO₃ single crystals was studied in the fluence range 7.81×10¹²–11.71×10¹² ions cm^?2. IL intensity is found to be high in lower ion fluences and it decreases with increase in ion fluence due to thermal quenching as a result of an increase in the sample temperature caused by ion beam irradiation. Thermoluminescence (TL) spectra were recorded for fluence of 5.2×10¹² ions cm^?2 on pure and doped crystals at a warming rate of 5 °C s^?1 at room temperature. Pure crystals show two glow peaks at 232 (Tg₁) and 328 °C (Tg₂). However, in Sm³⁺ doped crystals three glow peaks at 278 (Tg₁), 332 (Tg₂) and 384 °C (Tg₃) and two glow peaks at 278 (Tg₁) and 331 °C (Tg₂) in Dy³⁺ was recorded. The kinetic parameters (E, b s) were estimated using glow peak shape method. The decay of IL intensity was explained by excitation spike model.     

SrAl_2B_2O_7:Dy~(3+)材料的制备及其发光性能

采用高温固相法制备了SrAl2B2O7:Dy3+发光材料.在350nm紫外光激发下,测得SrAl2B2O7:Dy3+材料的发射光谱为一个多峰宽谱,主峰分别为480,573和678nm;分别和Dy3+的4F9/2→6H15/2,4F9/2→6H13/2,4F9/2→6H11/2的跃迁发射相对应;监测573nm的发射峰,得到材料的激发光谱为一个多峰宽谱,主峰分别为295,325,350,365,400nm.研究了Dy3+掺杂浓度对SrAl2B2O7:Dy3+材料发射光谱的影响,随着Dy3+掺杂浓度的增大,SrAl2B2O7:Dy3+材料的Iy/Ib逐渐增大,根据Judd-Ofelt理论解释了其原因.随着Dy3+掺杂浓度的增大,Dy3+的4F9/2→6H13/2跃迁产生的573nm发射峰强度先增大,在4%时达到最大值,之后减小,其自身的浓度猝灭机理为电偶极-电偶极相互作用.不同的电荷补偿剂Li+,Na+,K+的引入均使发光强度得到提高,尤其以Li+最佳,发光强度提高了大约33%.     

Determination of the chemical states of impurities in natural kyanite by the ionoluminescence technique

Ionoluminescence (IL) of natural kyanite crystals was studied during 120 MeV Au⁹⁺ ion irradiation in the fluence range 1.50?12 × 10¹¹ ions/cm². The IL spectrum exhibits sharp peaks at ～689, 694, 705, 713 and 716 nm, along with a broad emission peak at 530 nm recorded for all samples investigated. The sharp emission peaks at 689 and 694 nm are attributed to R₂ and R₁ lines of Cr³⁺ impurities, and they are related to the transition ²E_g → ⁴A_2g. The peaks at 705–716 nm are attributed to Fe³⁺ impurities and are related to the transition ⁴T_1g → ⁶A_1g. It was observed that up to a given fluence, the IL peak intensity grows, reaches a maximum and gradually decreases with increase of Au⁹⁺ ion fluence. The decrease in IL intensity might be attributed to disorder produced by dense electronic excitation under swift heavy ion irradiation. The stability of the chemical species was studied both with and without irradiation by means of FTIR spectroscopy. The results confirm that the Si?O?Al, Al?O and Si?O (2ν₃) type species are destroyed due to amorphization.     

Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

Phosphorescent and thermoluminescent properties of SrAl2O4:Eu,Dy phosphors prepared by solid state reaction method

Long persistent SrAl₂O₄:Eu²⁺ phosphors co-doped with Dy³⁺ were prepared by the solid state reaction method. The main diffraction peaks of the monoclinic structure of SrAl₂O₄ were observed in all the samples. The broad band emission spectra at 497 nm for SrAl₂O₄:Eu²⁺, Dy³⁺ were observed and the emission is attributed to the 4f⁶5d¹ to 4f⁷ transition of Eu²⁺ ions. The samples annealed at 1100–1200 °C showed similar broad TL glow curves centered at 120 °C. The similar TL glow curves suggest that the traps responsible for them are similar. The long afterglow displayed by the phosphors annealed at different temperatures, may be attributed to the Dy³⁺ ions acting as the hole trap levels, which play an important role in prolonging the duration of luminescence.     

Enhanced luminescence of Dy in Y3Al5O12 by Bi co-doping

In the present paper, phosphors with the composition Y_3−x−yAl₅O₁₂:Bi³⁺_x, Dy³⁺_y were synthesized with solid state reactions. The luminescence properties of Bi³⁺ and Dy³⁺ in Y₃Al₅O₁₂(YAG) and the energy transfer from Bi³⁺ to Dy³⁺ were investigated in detail. Bi³⁺ in YAG emits one broad band peaking at 304 nm which can be ascribed to the transition from excited states ³P_{0, 1} to ground state ¹S₀. Dy³⁺ in YAG emits two groups of peaks around 484 and 583 nm, respectively, which can be ascribed to the transitions from excited state ⁴F_9/2 to ground states ⁶H_15/2 and ⁶H_13/2. The co-doping of Bi³⁺ enhances the luminescent intensity of Dy³⁺ by ∼7 times because Bi³⁺ can transfer the absorbed energy to Dy³⁺ efficiently. The mechanism of energy transfer was also discussed.     

Luminescence studies on swift heavy ion irradiated nanocrystalline aluminum oxide

Pellets of nanocrystalline aluminum oxide synthesized by a combustion technique are irradiated with 120 MeV Au⁹⁺ ions for fluence in the range 5×10¹¹-1×10¹³ ions cm⁻². Two photoluminescence (PL) emissions, a prominent one with peak at ∼525 nm and a shoulder at ∼465 nm are observed in heat treated and Au⁹⁺ ion irradiated aluminum oxide. The 525 nm emission is attributed to F₂²⁺-centers. The PL intensity at 525 nm is found to increase with increase in ion fluence up to 1×10¹² ions cm⁻² and decreases beyond this fluence. Thermoluminescence (TL) of heat-treated and swift heavy ion (SHI) irradiated aluminum oxide gives a strong and broad TL glow with peak at ∼610 K along with a weak shoulder at 500 K. The TL intensity is found to increase with Au⁹⁺ ion fluence up to 1×10¹³ ions cm⁻² and decreases beyond this fluence.     

Luminescent properties of Dy doped SrMoO4 phosphor

Trivalent dysprosium ions (Dy³⁺) doped strontium molybdate (SrMoO₄) phosphors were synthesized by solid-state reaction and their photoluminescence (PL) properties were investigated. X-ray powder diffraction (XRD) analysis confirmed the formation of SrMoO₄:Dy³⁺. PL measurements indicated that the phosphor exhibited intense emission at 482, 490 (⁴F_9/2→⁶H_15/2) and 575 nm (⁴F_9/2→⁶H_13/2) under UV excitation. The effect of the doping concentration of Dy³⁺in SrMoO₄:Dy³⁺ on the PL was investigated in detail. Na⁺ ion was a good charge compensator for SrMoO₄:Dy³⁺.     

Auger electron/X-ray photoelectron and cathodoluminescent spectroscopic studies of pulsed laser ablated SrAl2O4:Eu,Dy thin films

Auger electron/X-ray photoelectron and cathodoluminescent (CL) spectroscopic studies were conducted on pulsed laser deposited SrAl₂O₄:Eu²⁺,Dy³⁺ thin films and the correlation between the surface chemical reactions and the decrease in the CL intensity was determined. The Auger electron and the CL data were collected simultaneously in a vacuum chamber either maintained at base pressure or backfilled with oxygen gas. The data were collected when the films were irradiated for 14 h with 2 keV electrons. The CL emission peak attributed to the 4f⁶5d¹ → 4f⁷ transitions was observed at ∼521 nm and the CL intensity of the peaks degraded at different rates in different vacuum conditions. X-ray photoelectron spectroscopy (XPS) data collected from degraded films suggest that strontium oxide (SrO) and aliminium oxide (Al₂O₃) were formed on the surface of the film as a result of electron stimulated surface chemical reaction (ESSCR).     

Photoluminescence characterization of Ce and Dy doped Li2CaGeO4 phosphors

Ce³⁺ and Dy³⁺ activated Li₂CaGeO₄ phosphors were prepared by a solid-state reaction method, and characterized by XRD (X-ray diffraction) and photoluminescence techniques. The characteristic emission bands of Dy³⁺ due to ⁴F_9/2→⁶H_15/2 (blue) and ⁴F_9/2→⁶H_13/2 (yellow) transitions were detected in the emission spectra of Li₂CaGeO₄:Dy³⁺. Ce³⁺ broad band emission was observed in Li₂CaGeO₄:Ce³⁺ phosphors at 372 and 400 nm due to 5d→4f transition when excited at 353 nm. Co-doping of Ce³⁺ enhanced the luminescence of Dy³⁺ significantly and concentration quenching occurs when Dy³⁺ is beyond 0.04 mol%. White-light with different hues can be realized by tuning Dy³⁺ concentration in the phosphors.     

100 MeV Si8+ ion induced luminescence and thermoluminescence of nanocrystalline Mg2SiO4:Eu3+

Nanoparticles of Mg₂SiO₄:Eu³⁺ have been prepared by the solution combustion technique and the grain size estimated by PXRD is found to be in the range 40–50 nm. Ionoluminescence (IL) studies of Mg₂SiO₄:Eu³⁺ pellets bombarded with 100 MeV Si⁸⁺ ions with fluences in the range 1.124–22.48×10¹² ions cm^?2 are carried out at IUAC, New Delhi, India. Five prominent IL bands with peaks at 580 nm, 590 nm, 612 nm, 655 nm and 705 nm are recorded. These characteristic emissions are attributed to the luminescence centers activated by Eu³⁺ cations. It is found that IL intensity decreases rapidly in the beginning. Later on, the intensity decreases slowly with further increase of ion fluence. The reduction in the ionoluminescence intensity with increase of ion fluence might be attributed to degradation of Si–O (ν₃) and Si–O (2ν₃) bonds present on the surface of the sample. The red emission with peak at 612 nm is due to characteristic emission of ⁵D₀→⁷F₂ of the Eu³⁺ cations. Thermoluminescence (TL) studies of Mg₂SiO₄:Eu³⁺ pellets bombarded with 100 MeV Si⁸⁺ cations with fluences in the range 5×10¹¹ ions cm^?2 to 5×10¹³ ions cm^?2 are made at RT. Two prominent and well resolved TL glows with peaks at ～220 °C and ～370 °C are observed. It is observed that TL intensity increases with increase of ion fluence. This might be due to creation of new traps during swift heavy ion irradiation.     

Thermoluminescent and stuctural properties of BaAl2O4:Eu,Nd,Gdphosphors prepared by combustion method

BaAl₂O₄:Eu²⁺,Nd³⁺,Gd³⁺ phosphors were prepared by a combustion method at different initiating temperatures (400–1200 °C), using urea as a comburent. The powders were annealed at different temperatures in the range of 400–1100 °C for 3 h. X-ray diffraction data show that the crystallinity of the BaAl₂O₄ structure greatly improved with increasing annealing temperature. Blue-green photoluminescence, with persistent/long afterglow, was observed at 498 nm. This emission was attributed to the 4f⁶5d¹–4f⁷ transitions of Eu²⁺ ions. The phosphorescence decay curves were obtained by irradiating the samples with a 365 nm UV light. The glow curves of the as-prepared and the annealed samples were investigated in this study. The thermoluminescent (TL) glow peaks of the samples prepared at 600 °C and 1200 °C were both stable at ∼72 °C suggesting that the traps responsible for the bands were fixed at this position irrespective of annealing temperature. These bands are at a similar position, which suggests that the traps responsible for these bands are similar. The rate of decay of the sample annealed at 600 °C was faster than that of the sample prepared at 1200 °C.     

The effect of different gas atmospheres on luminescent properties of pulsed laser ablated SrAl2O4:Eu,Dy thinfilms

SrAl₂O₄:Eu²⁺,Dy³⁺ thin films were grown on Si (1 0 0) substrates using the pulsed laser deposition (PLD) technique to investigate the effect of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological, photoluminescence (PL) and cathodoluminescence (CL) properties of the films. The films were ablated using a 248 nm KrF excimer laser. Atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS) and fluorescence spectrophotometry were used to characterize the thin films. Auger electron spectroscopy (AES) combined with CL spectroscopy were employed for the surface characterization and electron-beam induced degradation of the films. Better PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres with respect to those prepared in vacuum. A stable green emission peak at 515 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions were obtained with less intense peaks at 619 nm, which were attributed to transitions in Eu³⁺. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The CL intensity increased under prolonged electron bombardment during the removal of C due to electron stimulated surface chemical reactions (ESSCRs) on the surface of the SrAl₂O₄:Eu²⁺, Dy³⁺ thin films. The CL stabilized and stayed constant thereafter.     

Dy3+掺杂Ge-Ga-S-CsI玻璃中红外发光特性研究

用熔融淬冷法制备了系列掺杂浓度的Dy³⁺:Ge-Ga-S-CsI硫卤玻璃样品,测试了样品拉曼光谱、折射率、吸收光谱、近红外及中红外荧光谱.应用Judd-Ofelt理论计算了Dy³⁺离子的强度参数 (Ω_i, i=2,4,6)、自发辐射跃迁概率(A)、荧光分支比(β)、以及辐射寿命(τ_rad)等光谱参数.研究了810 nm激光抽运下样品中红 关键词： 硫系玻璃 中红外发光 3+掺杂')" href="#">Dy³⁺掺杂 多声子弛豫     

Sol-gel synthesis, structural and optical properties of rare earth ions (Sm or Dy) activated Ca3Ga2Si3O12 powder phosphors

Structural, morphological and optical properties of rare earth ions (RE³⁺=Sm³⁺ or Dy³⁺) activated Ca₃Ga₂Si₃O₁₂ (CaGaSi) phosphors synthesized by the sol-gel method are reported. XRD results confirmed the cubic phase structure of RE³⁺:CaGaSi phosphors. From the SEM images of RE³⁺:CaGaSi phosphors, it is observed that the particles are agglomerated. Photoluminescence spectra of Sm³⁺:CaGaSi phosphors have shown bright orange red emission at 598 nm (⁴G_5/2→⁶H_7/2) with an excitation wavelength of λ_exci=401 nm. In the case of Dy³⁺:CaGaSi phosphors bright yellow emission has been observed at 574 nm (⁴F_9/2→ ⁶H_13/2) with λ_exci=451 nm. From the PL spectral results, the rare earth ion concentration of CaGaSi phosphors is optimized.     

Luminescence studies of a combustion-synthesized blue–green BaAlxOy:Eu,Dy nanoparticles

Blue–green emitting BaAl_xO_y:Eu²⁺,Dy³⁺ phosphor was synthesized by the combustion method. The influence of various parameters on the structural, photoluminescence (PL) and thermoluminescence (TL) properties of the phosphor were investigated by various techniques. Phosphor nanocrystallites with high brightness were obtained without significantly changing the crystalline structure of the host. In the PL studies, broad-band excitation and emission spectra were observed with major peaks at 340 and 505 nm, respectively. The observed afterglow is ascribed to the generation of suitable traps due to the presence of the co-doped Dy³⁺ ions. Though generally broad, the peak structure of the TL glow curves obtained after irradiation with UV light was non-uniform with suggesting the contribution to afterglow from multiple events at the luminescent centers. Further insight on the afterglow behavior of the phosphor was deduced from TL decay results.     

Intense up-conversion emissions of Yb3+/Dy3+ co-doped Al2O3 nanopowders prepared by non-aqueous sol—gel method

Yb³⁺/Dy³⁺ co-doped Al₂O₃ nanopowders have been prepared by the non-aqueous sol-gel method and their up- conversion photoluminescence spectra are measured under excitation by 980-nm semiconductor laser. The results show that there are comparatively abundant spectra of up-conversion emissions centered at 378, 408, 527 and 543, and 663 nm, corresponding to ⁴G_9/2 → ⁶H_13/2, ⁴G_9/2 → ⁶H_11/2, ⁴I_15/2 → ⁶H_13/2, and ⁴F_9/2 → ⁶H_11/2 transitions of Dy³⁺, respectively. Two-photon and three-photon processes are involved in ultraviolet, violet, green, and red up-conversion emissions. The energy transition between Yb³⁺ and Dy³⁺ is discussed.     

Synthesis and photoluminescence properties of Sm-doped CaWO4 nanoparticles

The Sm³⁺-doped CaWO₄ nanoparticles were synthesized by hydrothermal method. The room temperature photoluminescence (PL) spectra of Sm³⁺-doped CaWO₄ nanoparticles doped with different Sm³⁺ concentrations under 405 nm excitation have been investigated. The PL spectra showed four strong emission peaks at 460, 571, 609, and 653 nm. The first emission peak at 460 nm could be due to a structural defect of the lattice, an oxygen-deficient WO₃ complex. The other three emissions at 571, 609, and 653 nm were due to the f-f forbidden transitions of the 4f electrons of Sm³⁺, corresponding to ⁴G_5/2→⁶H_5/2 (571 nm), ⁶H_7/2 (609 nm), and ⁶H_9/2 (653 nm), respectively. In addition, the optimum Sm³⁺ concentration in CaWO₄ nanoparticles for optical emission was determined to be 1.0%. The Sm³⁺⁴G_5/2→⁶H_7/2 (609 nm) emission intensity of Sm³⁺-doped CaWO₄ nanoparticles significantly increased with the increase of Sm³⁺ concentration, and showed a maximum when Sm³⁺ doping content was 1.0%. If Sm³⁺ concentration continued to increase, namely more than 1.0%, the Sm³⁺⁴G_5/2→⁶H_7/2 emission intensity would decrease. The present materials might be a promising phosphor for white-light LED applications.     

Dy含量对红色长余辉发光材料Sr3Al2Ｏ6:Eu2＋,Dy3＋性能的影响

采用溶胶凝胶法制备了Sr₃Al₂Ｏ₆:Eu^2＋,Dy^3＋红色长余辉发光材料,利用X射线衍射仪对材料的物相进行了分析,结果表明,1200℃下制备的样品的物相为Sr₃Al₂Ｏ₆,少量的Eu和Dy掺杂没有影响样品的相组成.采用荧光分光光度计、照度计测定了样品的发光特性.结果表明Sr₃Al₂Ｏ关键词： 红色长余辉 3Al₂Ｏ₆')" href="#">Sr₃Al₂Ｏ₆ 溶胶凝胶法