Structural and electrical properties of (Na0.85K0.15)0.5Bi0.5TiO3 thin films deposited on LaNiO3 and Pt bottom electrodes

(Na_0.85K_0.15)_0.5Bi_0.5TiO₃ thin films were deposited on LaNiO₃(LNO)/SiO₂/Si(1 0 0) and Pt/Ti/SiO₂/Si(1 0 0) substrates by metal-organic decomposition, and the effects of bottom electrodes LNO and Pt on the ferroelectric, dielectric and piezoelectric properties were investigated by ferroelectric tester, impedance analyzer and scanning probe microscopy, respectively. For the thin films deposited on LNO and Pt electrodes, the remnant polarization 2P_r are about 22.6 and 8.8 μC/cm² under 375 kV/cm, the dielectric constants 238 and 579 at 10 kHz, the dielectric losses 0.06 and 0.30 at 10 kHz, the statistic d_33eff values 95 and 81 pm/V. The improved piezoelectric properties could make (Na_1−xK_x)_0.5Bi_0.5TiO₃ thin film as a promising candidate for piezoelectric thin film devices.     

Second-harmonic generation in the thermal/electrical poling (100−x)GeS2·x(0.5Ga2S3·0.5CdS) chalcogenide glasses

Utilizing Maker fringe (MF) method, second-harmonic generation (SHG) has been observed within the GeS₂-Ga₂S₃-CdS pseudo-ternary glasses through thermal/electrical poling technique. The SHG phenomenon was considered to be the result of breakage of the glassy macroscopic isotropy originated from the reorientations of dipoles during the thermal/electrical poling process. Under the same poling condition conducted with 5 kV and 280 °C for 30 min, the maximum value of second-order nonlinear susceptibility χ⁽²⁾ of the poled (100−x)GeS₂·x(0.5Ga₂S₃·0.5CdS) glasses was obtained to be ≈4.36 pm/V when the value of x is equal to 30. Nonlinear dependence of χ⁽²⁾ on compositions of these glasses can be well explained according to the theory related to the reorientation of dipoles.     

Structural, electrical and piezoelectric properties of LiNbO3 thin films for surface acoustic wave resonators applications

In this work, 0.30 μm thick LiNbO₃ layers have been deposited by sputtering on nanocrystalline diamond/Si and platinised Si substrates. The films were then analyzed in terms of their structural and optical properties. Crystalline orientations along the (0 1 2), (1 0 4) and (1 1 0) axes have been detected after thermal treatment at 500 °C in air. The films were near-stoichiometric and did not reveal strong losses or diffusion in lithium during deposition or after thermal annealing. Pronounced decrease of the roughness on top of the LiNbO₃ layer and at the interface between LiNbO₃ and diamond was also observed after annealing, compared to the bare nanocrystalline diamond on Si substrate. Furthermore, ellipsometry analysis showed a better density and a reduced thickness of the surface layer after post-deposition annealing. The dielectric constant and losses have been measured to 50 and less than 3.5%, respectively, for metal/insulator/metal structures with 0.30 μm thick LiNbO₃ layer. The piezoelectric coefficient d₃₃ was found to be 7.1 pm/V. Finally, we succeeded in switching local domain under various positive and negative voltages.     

Na0.5K0.5NbO3-BiFeO3 lead-free piezoelectric ceramics

Lead-free (Na_0.5K_0.5)NbO₃-based piezoelectric ceramics were successfully fabricated by substituting with a small amount of BiFeO₃ (BF). Difficulty in sintering of pure NKN ceramics can be eased by adding a few molar percent of BF, and the crystalline structure is also changed, leading to a morphotropic phase boundary (MPB) between ferroelectric orthorhombic and rhombohedral phases. The MPB exists near the 1-2 mol% BF-substituted NKN compositions, exhibiting enhanced ferroelectric, piezoelectric, and electromechanical properties of P_r=23.3 μC/cm², d₃₃=185 pC/N, and k_p=46%, compared to an ordinarily sintered pure NKN ceramics. The MPB composition has a Curie temperature of ∼370 °C, comparable to that of some commercial PZT materials.     

Post-sintering annealing effect on the diffuse phase transition in (Pb1−xBax)(Yb0.5Ta0.5)O3 ceramics

The effect of post sintering annealing on the dielectric response of (Pb_1−xBa_x)(Yb_0.5Ta_0.5)O₃ ceramics in the diffuse phase transition range (x=0.2) has been investigated. The samples are prepared by conventional solid-state reaction method. The samples are sintered at 1300 °C for 2 h and annealed at different temperatures (800, 900 and 1000 °C) for 8 h and at 800 °C for different time durations (8, 12 and 24 h). A significant change in the dielectric response has been observed in all the samples. The dielectric constant increases remarkably and the dielectric loss tangent decreases. The dielectric peaks of the annealed samples are observed to be more diffused with noticeable frequency dispersion compared to the as sintered sample.     

Electrical behavior of BaZr0.1Ti0.9O3 and BaZr0.2Ti0.8O3 thin films

BaZr_0.1Ti_0.9O₃ and BaZr_0.2Ti_0.8O₃ (BZT) thin films were deposited on Pt/Ti/LaAlO₃ (1 0 0) substrates by radio-frequency magnetron sputtering, respectively. The films were further annealed at 800 °C for 30 min in oxygen. X-ray diffraction θ-2θ and Φ-scans showed that BaZr_0.1Ti_0.9O₃ films displayed a highly (h 0 0) preferred orientation and a good cube-on-cube epitaxial growth on the LaAlO₃ (1 0 0) substrate, while there are no obvious preferential orientation in BaZr_0.2Ti_0.8O₃ thin films. The BaZr_0.1Ti_0.9O₃ films possess larger grain size, higher dielectric constant, larger tunability, larger remanent polarization and coercive electric field than that of BaZr_0.2Ti_0.8O₃ films. Whereas, BaZr_0.1Ti_0.9O₃ films have larger dielectric losses and leakage current density. The results suggest that Zr⁴⁺ ion can decrease dielectric constant and restrain non-linearity. Moreover, the enhancement in dielectric properties of BaZr_0.1Ti_0.9O₃ films may be attributed to (1 0 0) preferred orientation.     

Properties of K0.5Bi0.5TiO3 thin films deposited on different substrates

K_0.5Bi_0.5TiO₃ thin films were deposited on fused quartz, n-type Si(100) and Pt/TiO₂/SiO₂/Si substrates by repeated coating/dying cycles. X-ray diffraction analysis shows that the films annealed at 700 °C for 10 min present perovskite phase. Atomic force microscopy reveals that the surface morphology is smooth, the grain sizes of the films on Si(100) are quite larger than on fused quartz. The capacitance-voltage hysteresis loops at various sweeping speed are collected as are polarization types. The films in the ON and OFF states are relatively stable. The films also exhibit a hysteresis loop at an applied voltage of 4 V, with a remanent polarization of 9.3 μC/cm² and a coercive voltage of 2 V. The insulating property of negative bias voltage is better than that of positive bias voltage. The transmittance of the films is between 74 and 82% in the wavelength range of 200-2000 nm.     

Thermal, electrical, and electrochemical properties of Lanthanum-doped Ba0.5Sr0.5 Co0.8Fe0.2O3-δ

Crystal structure, thermogravimetry (TG), thermal expansion coefficient (TEC), electrical conductivity and AC impedance of (Ba_0.5Sr_0.5)_1-xLa_xCo_0.8Fe_0.2O_3-δ (BSLCF; 0.05?x?0.20) were studied in relation to their potential use as intermediate temperature solid oxide fuel cell (IT-SOFC) cathode. A single cubic pervoskite was observed by X-ray diffraction (XRD). The TEC of BSLCF was increasing slightly with the increasing content of La, and all the compounds showed abnormal expansion at high temperature. Proved by the TG result, it was associated with the loss of lattice oxygen. The electrical conductivity, which is the main defect of Ba_0.5Sr_0.5 Co_0.8Fe_0.2O_3-δ (BSCF), was improved by La doping, e.g., the compound of x=0.20 demonstrated a conductivity of σ=376 S cm⁻¹ at 392 °C. The increase of electrical conductivity resulted from the increased concentration of charge carrier induced by La doping. In addition, the AC impedance revealed the better electrochemical performance of BSLCF. For example, at 500 °C, the sample with composition x=0.15 yielded the resistance values of 2.12 Ω cm², which was only 46% of BSCF.     

Room temperature fabrication Oxide TFT with Y2O3 as a gate oxide and Mo contact

In this investigation, an operating voltage as low as 5 V has been achieved for Oxide TFT with Y₂O₃ as a gate oxide and a-IGZO as an active layer. The OTFT has been fabricated at room temperature using RF sputter. The mobility and threshold voltages are 11.3 cm²/V s and 3.4 V for the device with W/L = 0.8, respectively. The annealing at 400 °C in N₂ containing 5% H₂ ambient has been utilized to improve the electrical performance of TFT. The on-off current which is determined by gate dielectric has been observed to be 10⁴. It has also been observed that the dielectric properties of gate oxide deteriorate on annealing. The dielectric constant of Y₂O₃ is observed in the range between 5.1 and 5.4 measured on various devices.     

Lead-free ferroelectric BaTiO3 doped-(Na0.5Bi0.5)TiO3 thin films processed by pulsed laser deposition technique

The difficulties in synthesizing phase pure BaTiO₃ doped-(Na_0.5Bi_0.5)TiO₃ are known. In this work, we reporting the optimized pulsed laser deposition (PLD) conditions for obtaining pure phase 0.92(Na_0.5Bi_0.5)TiO₃-0.08BaTiO₃, (BNT-BT_0.08), thin films. Dielectric, ferroelectric and piezoelectric properties of BNT-BT_0.08, thin films deposited by PLD on Pt/TiO₂/SiO₂/Si substrates are investigated in this paper. Perovskite structure of BNT-BT_0.08 thin films with random orientation of nanocrystallites has been obtained by deposition at 600 °C. The relative dielectric constant and loss tangent at 100 kHz, of BNT-BT_0.08 thin film with 530 nm thickness, were 820 and 0.13, respectively. Ferroelectric hysteresis measurements indicated a remnant polarization value of 22 μC/cm² and a coercive field of 120 kV/cm. The piezoresponse force microscopy (PFM) data showed that most of the grains seem to be constituted of single ferroelectric domain. The as-deposited BNT-BT_0.08 thin film is ferroelectric at the nanoscale level and piezoelectric.     

Electrical properties of SrBi2(Nb0.5Ta0.5)2O9 ceramics

Aurivillius SrBi₂(Nb_0.5Ta_0.5)₂O₉ (SBNT 50/50) ceramics were prepared using the conventional solid-state reaction method. Scanning electron microscopy was applied to investigate the grain structure. The XRD studies revealed an orthorhombic structure in the SBNT 50/50 with lattice parameters a=5.522 Å, b=5.511 Å and c=25.114 Å. The dielectric properties were determined by impedance spectroscopy measurements. A strong low frequency dielectric dispersion was found to exist in this material. Its occurrence was ascribed to the presence of ionized space charge carriers such as oxygen vacancies. The dielectric relaxation was defined on the basis of an equivalent circuit. The temperature dependence of various electrical properties was determined and discussed. The thermal activation energy for the grain electric conductivity was lower in the high temperature region (T>303.6 °C, E_a−ht=0.47 eV) and higher in the low temperature region (T<303.6 °C, E_a−lt=1.18 eV).     

Large piezoresponse of lead-free Bi0.5(Na0.85K0.15)0.5TiO3 thin film

0.85Bi_0.5Na_0.5TiO₃-0.15Bi_0.5K_0.5TiO₃ (BNKT15) lead-free thin films were prepared on Pt(111)/TiO₂/SiO₂/Si(100) substrates by the chemical solution deposition method. BNKT15 are MPB composition in the Bi_0.5Na_0.5TiO₃-Bi_0.5K_0.5TiO₃ (BNT-BKT) system. The maximum piezoelectric coefficient (d_33,f) value of BNKT15 thin film is approximately 75 pm/V, which is comparable to that of polycrystalline PZT thin films. These results suggest that BNKT15 thin film can be used as an alternative for PZT films in piezoelectric micro-electromechanical systems.     

Orientation-dependent dielectric properties of Ba(Sn0.15Ti0.85)O3 thin films prepared by sol-gel method

The orientation-dependent dielectric properties of barium stannate titanate (Ba(Sn_0.15Ti_0.85)O₃, BTS) thin films grown on (1 0 0) LaAlO₃ single-crystal substrates through sol-gel process were investigated. The nonlinear dielectric properties of the BTS films were measured using an inter-digital capacitor (IDC). The results show that the in-plane dielectric properties of BTS films exhibited a strong sensitivity to orientation. The upward shift of Curie temperature (T_c) of the highly (1 0 0)-oriented BTS thin films is believed to be attributing to a tensile stress along the in-plane direction inside the film. A high tunability of 47.03% was obtained for the highly (1 0 0)-oriented BTS films, which is about three times larger than that of the BTS films with random orientation, measured at a frequency of 1 MHz and an applied electric field of 80 kV/cm. This work clearly reveals the highly promising potential of BTS films for application in tunable microwave devices.     

Enhanced dielectric and ferroelectric properties of Pb1−3x/2Lax(Zr0.5Ti0.5)O3 thin films with low lanthanum substitution

Effects of lanthanum (La) substitution (0.003 ≤ x ≤ 0.015) on the dielectric and ferroelectric properties of Pb(Zr_0.5Ti_0.5)O₃ thin films have been investigated. The films were synthesized on the Pt (1 1 1)/Ti/SiO₂/Si (1 0 0) substrates by a sol-gel method. Large dielectric constants of the films are obtained within range of 800-1600 which are almost comparable to those observed in bulk ceramics. The films also show improved remnant polarization values and reduced coercive field values with the increasing addition of La substitution. Our results suggest that low La substitution contributes to enhance film electric properties due to the improvement of non-180° domain wall mobility as well as the stabilization of tetragonal phase.     

Third-order optical nonlinearities of lead-free (Na1−xKx)0.5Bi0.5TiO3 thin films

(Na_1−xK_x)_0.5Bi_0.5TiO₃ (NKBT) (x = 0.1, 0.2, and 0.3) thin films with good surface morphology and rhombohedral perovskite structure were fabricated on quartz substrates by a sol-gel process. The fundamental optical constants (the band gaps, linear refractive indices and absorption coefficients) of the films were obtained through optical transmittance measurements. The nonlinear optical properties were investigated by Z-scan technique performed at 532 nm with a picosecond laser. A two-photon absorption effect closely related with potassium-doping content was found in thin films, and the nonlinear refractive index n₂ increases evidently with potassium-doping. The real part of the third-order nonlinear susceptibility χ⁽³⁾ is much larger than its imaginary part, indicating that the third-order optical nonlinear response of the NKBT films is dominated by the optical nonlinear refractive behavior. These results show that NKBT thin films have potential applications in nonlinear optics.     

C-V studies on metal-ferroelectric bismuth vanadate (Bi2VO5.5)-semiconductor structure

Ferroelectric bismuth vanadate Bi₂VO_5.5 (BVO) thin films have been successfully grown on p-type Si(100) substrate by using chemical solution decomposition (CSD) technique followed by rapid thermal annealing (RTA). The crystalline nature of the films has been studied by X-ray diffraction (XRD). Atomic force microscopy (AFM) was used to study the microstructure of the films. The dielectric properties of the films were studied. The capacitance-voltage characteristics have been studied in metal-ferroelectric-insulator-semiconductor (MFIS) configuration. The dielectric constant of BVO thin films formed on Si(100) is about 146 measured at a frequency of 100 kHz at room temperature. The capacitance-voltage plot of a Bi₂VO_5.5 MFIS capacitor subjected to a dc polarizing voltages shows a memory window of 1.42 V during a sweep of ±5 V gate bias. The flatband voltage (V_f) shifts towards the positive direction rather than negative direction. This leads to the asymmetric behavior of the C-V curve and decrease in memory window. The oxide trap density at a ramp rate of 0.2 V/s was estimated to be as high as 1.45×10¹² cm⁻².     

Microstructure and piezoelectric properties of Bi0.5(Na0.82K0.18)0.5TiO3−NaSbO3 ceramics

Lead-free piezoelectric ceramics (1−x)Bi_0.5(Na_0.82K_0.18)_0.5TiO₃−xNaSbO₃ have been prepared by a conventional ceramics technique, and their microstructure and electrical properties have been investigated. The addition of NaSbO₃ has no remarkable effect on the crystal structure within the studied doping content; however, an obvious change in microstructure took place. With increase in NaSbO₃ content, the temperature from a ferroelectric to antiferroelectric phase transition increases, and the temperature for a transition from antiferroelectric phases to paraelectric phases changes insignificantly. Simultaneously, the temperature range between the rhombohedral phase transition point and the Curie temperature point becomes smaller. The piezoelectric properties significantly increase with increase in NaSbO₃ content and the piezoelectric constant and electromechanical coupling factor attain maximum values of d₃₃=160 pC/N and k_p=0.333 at x=0.01. The results indicate that (1−x)Bi_0.5(Na_0.82K_0.18)_0.5TiO₃−xNaSbO₃ ceramic is a promising lead-free piezoelectric candidate material.     

Maxwell-Wagner characterization of dielectric relaxation in Ni0.8Zn0.2Fe2O4/Sr0.5Ba0.5Nb2O6 composite

Dense composites were prepared through incorporating the dispersed Ni_0.8Zn_0.2Fe₂O₄ ferromagnetic particles into Sr_0.5Ba_0.5Nb₂O₆ ferroelectric matrix. Extrinsic dielectric relaxation and associated high permittivities of the materials are reported in the composites. We used an ideal equivalent circuit to explain electrical responses in impedance formalism. A Debye-like relaxation in the permittivity formalism was also found. Interestingly, real permittivity (ε′) of the sample containing 30% Ni_0.8Zn_0.2Fe₂O₄ shows obvious independence of the temperature at 100 kHz. Dielectric relaxation and high-ε′ properties of the composites are explained in terms of the Maxwell-Wagner (MW) polarization model.     

Dielectric properties and magnetoelectric effect of (x)NiFe2O4+(1−x)Ba0.8Sr0.2TiO3 composites

Magnetoelectric composites of NiFe₂O₄ and Ba_0.8Sr_0.2TiO₃ were prepared using conventional double-sintering ceramic method. The phase formation of magnetoelectric composites was confirmed by XRD technique. Variation of dielectric constant and loss tangent at room temperature with frequency in the range 100 Hz-1 MHz has been studied. Also the variation of dielectric constant and loss tangent with temperature and composition at fixed frequencies of 1 kHz, 10 kHz, 100 kHz and 1 MHz is reported. The static value of the magnetoelectric conversion factor was measured as a function of intensity of the magnetic field. The ME voltage coefficient of about 430 μV/cm Oe was observed for 15% NiFe₂O₄+85% Ba_0.8Sr_0.2TiO₃ composite. All the samples show linear variation of magnetoelectric conversion in the presence of static magnetic field.