Structure, ferroelectric and piezoelectric properties of (Bi1−x−yNa0.925−x−yLi0.075)0.5BaxSryTiO3 lead-free piezoelectric ceramics

Lead-free multi-component ceramics (Bi_1−x−yNa_{0.925−x−y}Li_0.075)_0.5Ba_xSr_yTiO₃ have been prepared by an ordinary sintering technique and their structure and electrical properties have been studied. All the ceramics can be well-sintered at 1100 °C. X-ray diffraction patterns shows that Li⁺, Ba²⁺ and Sr²⁺ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a new solid solution with a pure perovskite structure, and a morphotropic phase boundary (MPB) is formed at 0.04 < x < 0.08. As compared to pure Bi_0.5Na_0.5TiO₃ ceramic, the coercive field E_C of the ceramics decreases greatly and the remanent polarization P_r of the ceramics increases significantly after the formation of the multi-component solid solution. Due to the MPB, lower E_C and higher P_r, the piezoelectricity of the ceramics is greatly improved. For the ceramics with the compositions near the MPB (x = 0.04–0.08 and y = 0.02–0.04), piezoelectric coefficient d₃₃ = 133–193 pC/N and planar electromechanical coupling factor k_P = 16.2–32.1%. The depolarization temperature T_d reaches a minimum value near the MPB. The temperature dependences of the ferroelectric and dielectric properties suggest that the ceramics may contain both the polar and non-polar regions at temperatures near/above T_d.     

Lithium ion conductive glass–ceramics with Li3Fe2(PO4)3 and YAG laser-induced local crystallization in lithium iron phosphate glasses

The glasses with the composition of 37.5Li₂O–(25 − x)Fe₂O₃–xNb₂O₅–37.5P₂O₅ (mol%) (x = 5,10,15) are prepared, and it is found that the addition of Nb₂O₅ is effective for the glass formation in the lithium iron phosphate system. The glass–ceramics consisting of Nasicon-type Li₃Fe₂(PO₄)₃ crystals with an orthorhombic structure are developed through conventional crystallization in an electric furnace, showing electrical conductivities of 3 × 10^− 6 Scm^− 1 at room temperature and the activation energies of 0.48 eV (x = 5) and 0.51 eV (x = 10) for Li⁺ ion conduction in the temperature range of 30–200 °C. A continuous wave Nd:YAG laser (wavelength: 1064 nm) with powers of 0.14–0.30 W and a scanning speed of 10 μm/s is irradiated onto the surface of the glasses, and the formation of Li₃Fe₂(PO₄)₃ crystals is confirmed from XRD analyses and micro-Raman scattering spectra. The crystallization of the precursor glasses is considered as new route for the fabrication of Li₃Fe₂(PO₄)₃ crystals being candidates for use as electrolyte materials in lithium ion secondary batteries.     

Structure and electrical properties of Bi0.5(Na, K)0.5TiO3−BiGaO3 lead-free piezoelectric ceramics

Lead-free piezoelectric ceramics (1 − x − y)Bi_0.5Na_0.5TiO₃−xBi_0.5K_0.5TiO₃− yBiGaO₃ have been fabricated by an ordinary sintering technique, and their structure and electrical properties and depolarization temperature have been studied. The results of X-ray diffraction reveal that Bi_0.5K_0.5TiO₃ and BiGaO₃ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a new solid solution with a pure perovskite structure. An obvious change in microstructure with increasing concentration of Bi_0.5K_0.5TiO₃ and BiGaO₃ was observed. The piezoelectric constant d₃₃ and the electromechanical coupling factor k_p of the ceramics attain maximum values of 165 pC/N and 0.346 at y = 0.01(x = 0.18) and x = 0.21(y = 0.01), respectively. The temperature dependence of dielectric constant indicates an obvious relaxor characteristic with strong frequency dependence of dielectric constant. The depolarization temperature decreased with increasing content of BiGaO₃ and first decreases and then increases with increasing amount of Bi_0.5K_0.5TiO₃.     

Synthesis, phase and microstructure characteristics of Pb(Zr0.52Ti0.48)O3–(Bi3.25La0.75)Ti3O12 ceramics

Ceramics with formula (1 − x)Pb(Zr_0.52Ti_0.48)O₃–x(Bi_3.25La_0.75)Ti₃O₁₂ (when x = 0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1.0) were prepared by a solid-state mixed-oxide method and sintered at temperatures between 950 °C and 1250 °C. It was found that the optimum sintering temperature was 1150 °C at which all the samples had densities at least 95% of theoretical values. Phase analysis using X-ray diffraction indicated the existence of BLT- as well as PZT-based solid solutions with corresponding lattice distortion. Scanning electron micrographs of ceramic surfaces showed a plate-like structure in BLT-rich phase while the typical grain structure was observed for PZT-rich phase. The grain sizes of both pure BLT and PZT ceramics were found to decrease as the relative amount of the other phase increased. This study suggested that tailoring of properties of this PZT–BLT system was possible especially on the BLT-rich side due to its large solubility limit.     

Electrical characteristics and low-temperature sintering of BiFeO3-modified Pb(Zr,Ti)O3–Pb(Fe2/3W1/3)O3–Pb(Mn1/3Nb2/3)O3 ceramics with ZnO addition

Effects of ZnO addition on electrical properties and low-temperature sintering of BiFeO₃-modified Pb(Zr,Ti)O₃–Pb(Fe_2/3W_1/3)O₃–Pb(Mn_1/3Nb_2/3)O₃ were investigated. The investigations revealed that the sintering temperature can be decreased to 950 °C, and the favorable properties were obtained with 0.10 wt% ZnO added ceramics. The electrical properties were as follows: d₃₃ = 313 pC/N, K_p = 0.56, tan δ = 0.0053, ε_r = 1407 and T_c = 295 °C, which showed that this system was a promising material for the multilayer devices application.     

Luminescence and energy transfer in Eu, Mn co-doped Li4SrCa(SiO4)2 for white light-emitting-diodes

Li₄(Sr_0.96Eu_0.04)(Ca_1 − xMn_x)(SiO₄)₂ phosphors were synthesized by solid-state reactions and photoluminescence (PL) properties were investigated. These phosphors have intense absorption in n-UV region, which is suitable for excitation of UV LEDs. The orange-reddish emission of Mn²⁺ can be adjusted by changing the Mn²⁺/Eu²⁺ ratio. Energy transfer from Eu²⁺ to Mn²⁺ is observed. Li₄(Sr_0.96Eu_0.04)(Ca_1 − xMn_x)(SiO₄)₂ phosphors could be used in white LEDs.     

Study on nonlinear optical absorption properties of [(CH3)4N]2[Cu(dmit)2] by Z-scan technique

The third-order optical nonlinearities of an organo-metallic compound, [(CH₃)₄N]₂[Cu(dmit)₂] (dmit²⁻=4,5-dithiolate-1,3-dithiole-2-thione), abbreviated as MeCu, dissolved in acetone are characterized by Z-scan technique with picosecond and nanosecond laser pulses in the near-infrared region. Two-photon absorption has been found when the sample solution is irradiated by 40 ps pulse width at 1064 nm and the two-photon absorption (TPA) coefficient β_TPA is 4×10⁻¹³ m/W. While excited by 15 ns laser pulses at 1053 nm, the Z-scan spectra reveal strong reverse saturable absorption (RSA) and the nonlinear absorption coefficient β_RSA is estimated to be as high as 7.07×10⁻¹¹ m/W which is much larger than β_TPA. An explanation for this enhancement is given. All the results suggest that MeCu may be a promising candidate for the application to optical limiting in the near-infrared region.     

Spectral characterization and energy levels of Cr:Sc2(MoO4)3 crystal

This paper reports the spectral properties and energy levels of Cr³⁺:Sc₂(MoO₄)₃ crystal. The crystal field strength Dq, Racah parameter B and C were calculated to be 1408 cm⁻¹, 608 cm⁻¹ and 3054 cm⁻¹, respectively. The absorption cross sections σ_α of ⁴A₂→⁴T₁ and ⁴A₂→⁴T₂ transitions were 3.74×10⁻¹⁹ cm² at 499 nm and 3.21×10⁻¹⁹ cm² at 710 nm, respectively. The emission cross section σ_e was 375×10⁻²⁰ cm² at 880 nm. Cr³⁺:Sc₂(MoO₄)₃ crystal has a broad emission band with a broad FWHM of 176 nm (2179 cm⁻¹). Therefore, Cr³⁺:Sc₂(MoO₄)₃ crystal may be regarded as a potential tunable laser gain medium.     

Preparation and electrical properties of a pyrochlore-related Ce2Zr2O8−x phase

A pyrochlore-related Ce₂Zr₂O_8−x phase has been prepared in a reduction reoxidation process from Ce_0.5Zr_0.5O₂ powders. Ce₂Zr₂O_8−x, based on a cubic symmetry with a=1.053 nm, decomposes in nitrogen at 800 °C, but remains stable up to 900 °C in air. It shows mixed oxygen ionic and electronic conductivity. The bulk conductivity at 700 °C is 4×10⁻⁴ S cm⁻¹ in air and 1×10⁻² S cm⁻¹ in nitrogen, and the activation energy is 1.27 eV in air. In nitrogen, the Arrhenius law is not obeyed, and a curved plot was obtained from 400 to 700 °C; then, the conductivity decreased rapidly due to the thermal decomposition of Ce₂Zr₂O_8−x.     

Cu掺杂La0.67Sr0.33CuxMn1-xO3薄膜的光诱导效应研究

分别采用溶胶-凝胶和射频磁控溅射的方法制备了La_0.67Sr_0.33Cu_xMn_1-xO₃（x=0.05, 0.10和0.15）系列块材和薄膜,研究了Cu部分替代对薄膜光诱导特性的影响.实验结果表明随着Cu掺杂量的增加,薄膜的金属-绝缘转变温度向低温方向移动,且导电性降低.在金属相激光作用诱导电阻增大.光致电阻相对变化极大值随着Cu含量的增加而增大,当 关键词： 锰氧化物 光诱导 Cu掺杂 晶格效应     

Magnetocaloric properties of (La0.67−xGdx)Sr0.33MnO3 polycrystalline nanoparticles

In this paper, magnetic property and magnetocaloric effect (MCE) in nanoparticles perovskite manganites of the type (La_0.67−xGd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) synthesized by using an amorphous molecular alloy as precursor have been reported. From the magnetic measurements as function of temperature and magnetic applied field, we have discovered that the Curie temperature (T_C) of the prepared samples is found to be strongly dependent on Gd content. The Curie temperature of samples is 358.4, 343.2, and 285.9 K for x=0.1, 0.15, and 0.2, respectively. A large magnetocaloric effect close to T_C has been observed with a maximum of magnetoentropy change in all the samples, ∣ΔS_M∣_max of 1.96 and 4.90 J/kg K at 2 and 5 T, respectively, for a substitution rate of 0.15. In addition, the maximum magnetic entropy change observed for samples with different concentration of Gd, exhibits a linear dependence with the applied high magnetic field. These results suggest that (La_0.67−x Gd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) compounds could be a suitable candidate as working substance in magnetic refrigeration near room temperature.     

Water incorporation into the Ba2(In1 − xMx)2O5‪ (M = Sc 0 ≤ x < 0.5 and M = Y 0 ≤ x < 0.35) system and protonic conduction

Ba₂(In_1 − xM_x)₂O_{5 − y / 2}(OH)_y‪□_{1 − y / 2} (y ≤ 2; M = Sc³⁺ 0 ≤ x < 0.5 and M = Y³⁺ 0 ≤ x < 0.35) compounds were prepared by reacting Ba₂(In_1 − xM_x)₂O₅‪ phases with water vapor. This reaction is reversible. Analyses of the hydration process by TG and XRD studies show that the thermal stability of hydrated phases increases when x increases and that the incorporation of water is not a single-phase reaction inducing either a crystal system or space group modification. Fully hydrated (y = 2) and dehydrated (y = 0) samples have been stabilized at room temperature and characterized for all compositions. In wet air, all phases show a proton contribution to the total conductivity at temperatures between 350 and 600 °C. At a given temperature, proton conductivity increases with the substitution ratio and reaches at 350 °C, 5.4 10^− 3 S cm^− 1 for Ba₂(In_0.65Sc_0.35)₂O_4.2□_0.2(OH)_1.6.     

Crystal structure and ferroelectric properties of Mn-doped ((Ka0.5Na0.5)0.935Li0.065)NbO3 lead-free ceramics

In this study, ceramics in Mn-doped ((Ka_0.5Na_0.5)_0.935Li_0.065)NbO₃ ceramics (Mn content = 0.25, 0.50, 1.00 and 1.50 mol%) were successfully prepared by the conventional mixed-oxide technique. The crystal structure was identified by XRD as a single-phase perovskite structure with tetragonal symmetry. The valence of Mn ions, characterized by the synchrotron XAS technique, was seen to change from Mn⁴⁺ to Mn³⁺ during the formation of the crystal. The valence state of Mn strongly affected the crystal structure and ferroelectric properties of the ceramics. The ferroelectric parameters show the decrease of remnant polarization and the increase of the coercive field with increasing MnO₂ content. The results confirm the Mn³⁺ in KNNL perovskite lattices, leading to the formation of oxygen vacancies and hardening effects.     

Dielectric, ferroelectric and pyroelectric properties of Pb[(Ni1/3Sb2/3)xTiyZrz]O3 ceramics

In the present study, various Pb[(Ni_1/3Sb_2/3)_xTi_yZr_z]O₃ where x+y+z=1, x=0.08 and y=0.44-0.49, ceramics in the morphotropic phase boundary (MPB) range were studied by dielectric and pyroelectric methods. The results of the investigations revealed an MPB composition range of y≅0.46. The study of the dielectric properties of these compounds as a function of temperature suggests that with increase in y the permittivity maximum increases and transition temperature shifts towards higher temperature. Well-saturated polarization versus electric field (P-E) hysteresis loops were obtained and values of P_r were calculated. The samples revealed good pyroelectric properties for y=0.44 and y=0.45 at room temperature with large figures of merit F_v=0.019 m²/C and F_D=1.34×10^-5Pa^1/2.     

Microwave dielectric properties of (1 − x)(Mg0.95Co0.05)TiO3–x(Na0.5La0.5)TiO3 ceramic system

The microstructures and the microwave dielectric properties of the (1 − x)(Mg_0.95Co_0.05)TiO₃–x(Na_0.5La_0.5)TiO₃ ceramic system were investigated. Two-phase system was confirmed by the XRD patterns and the EDX analysis. A co-existed second phase (Mg_0.95Co_0.05)Ti₂O₅ was also detected. The microwave dielectric properties are strongly related to the density and the matrix of the specimen. A new microwave dielectric material 0.88(Mg_0.95Co_0.05)TiO₃–0.12(Na_0.5La_0.5)TiO₃, possessing an excellent combination of dielectric properties: ε_r  22.36, Q × f  110,000 GHz (at 9 GHz), τ_f  2.9 ppm/°C), is proposed as a candidate dielectric for GPS patch antennas.     

Effect of Sn-doping on the structural,magnetic and magnetocaloric properties of La0.67Ba0.33Mn1−xSnxO3 compounds

Magnetocaloric effect (MCE) in fine-grained perovskite manganites of the type La_0.67Ba_0.33Mn_1−xSn_xO₃ (x=0.05, 0.1 and 0.15) were prepared by the solid-state method. The prepared samples remain single phase and exhibit paramagnetic to ferromagnetic phase transition (T_C) at 340, 325 and 288 K for x=0.05, 0.1 and 0.15, respectively. From the measured magnetization data of La_0.67Ba_0.33Mn_1−xSn_xO₃ compounds as a function of field (2 T), the associated magnetic entropy change close to their respective Curie temperatures and the relative cooling power (RCP) have been determined. Large MCE has been obtained in all samples and |ΔS_M|_max reached the highest value of 2.49 J/kg K at T_C (288 K) for the sample x=0.15, with H=2 T.     

Temperature dependence of the indirect band gap, steepness parameter and related optical constants of [Kx(NH4)1−x]2ZnCl4 mixed crystals

Optical transmittance measurements near the absorption edge of [K_x(NH₄)_1−x]₂ZnCl₄ mixed crystals, where x=0.00, 0.232, 0.522, 0.644, 0.859 and 1.00, are reported over 276–350 K range. Analysis reveals that the type of transition is the indirect allowed one. The absorption edge shifted towards lower energy with increasing temperature. It is shown that [K_x(NH₄)_1−x]₂ZnCl₄ mixed crystals with x0.644 reveal a phase transition at 319 K, this phase disappeared at high concentrations of K⁺ ions. The steepness parameter is given, its value is used to estimate the temperature dependence of the indirect energy gap. In the region of the absorption edge, the absorption coefficient obeys Urbach's rule. Urbach parameters are investigated as a function of temperature.     

Magnetic properties of FexCo1−x/CoyFe1−yFe2O4 composite under hydrothermal condition

The metal–ferrite composites Fe_xCo_1−x/Co_yFe_1−yFe₂O₄ are synthesized by using disproportion of Fe (II) and reduction of Co (II) by Fe⁰ under hydrothermal condition. The size of the particles of the composites decreases as the [KOH] decreasing. The composites are measured by TEM and it can be deduced that when [KOH] = 0.1, the size of the alloy body-centered cubic (BCC) in composites is 20 ± 7 nm, the size of the Cobalt ferrite (spinel) is 170 ± 50 nm. The maximal value of the saturation magnetization (Ms) of the composite is about 100.14 emu/g, which is synthesized under Co (II)/Fe (II) = 0.05, [KOH] = 1 N, T = 150 °C and t = 3 h. The value of Hc of the composite synthesized under Co (II)/Fe (II) = 0.5, t = 3 h, T = 150 °C and [KOH] = 10.2 mol/L is about 2878.19 Oe. The Fe–Co alloy is synthesized through a reduction reaction of the composites in a flowing gaseous mixture. There is a maximal value (302.9 emu/g) of the Ms for the alloys generated at 1000 °C, which is the Co_0.412Fe_0.588 alloy.     

Electrical properties of perovskite-type La(Cr1−xMnx)O3+δ

Perovskite-type La(Cr_1−xMn_x)O_3+δ (0.0x1.0) was synthesized using a sol–gel process. The crystal structure of La(Cr_1−xMn_x)O_3+δ changes from orthorhombic to rhombohedral at x=0.6. The Mn⁴⁺ ion content increases monotonically in the range 0.2x1.0. The magnetic measurement of La(Cr_1−xMn_x)O_3+δ indicates that a Mn³⁺ ion is a high-spin state with (d)³(dγ)¹. The variation of the average (Cr, Mn)-O distance is explained by ionic radii of the Cr³⁺, the Mn³⁺, the Mn⁴⁺ ions. Since the log σT–1/T curve is linear and the Seebeck coefficient (α) is independent of temperature, it is considered that La(Cr_1−xMn_x)O_3+δ is a p-type semiconductor and exhibits the hopping conductivity.     

Superprotonic solid solutions between CsHSO4 and CsH2PO4

Solid solutions of (CsHSO₄)_1 − x(CsH₂PO₄)_x (x = 0.25-0.75) were synthesized by mechanical milling method over a wide range of compositions. Superprotonic cubic phase was confirmed for all these samples between 293 and 420 K depending on its composition. These superprotonic phases have primitive cubic structure similar to that of CsH₂PO₄. The kinetic stability of the supercooled cubic phase depends both on the composition x and the humidity of surrounding atmosphere. The most stable composition of the cubic phase was found around x = 0.67 and could be maintained for several days even under ambient atmosphere. The ionic conductivities of these superprotonic phases reached 10^− 2–10^− 3 S∙cm^− 1 at 450 K. With increasing x the ionic conductivity at the superprotonic phase decreased continuously associated with the increase of the activation energy. These findings suggest that the average number of the hydrogen bonds between XO₄ (X = S, P) units plays an important role on the stability of the cubic phase and also on the conductivity.