Microwave behavior of ferrites prepared via sol–gel method

Ni-ferrites were prepared at different temperatures via sol–gel method. The electromagnetic properties of these materials, namely permittivity and permeability were measured in the 0.1–13 GHz frequency range. Following a mathematical procedure, microwave absorption diagrams were constructed including the dependence of the microwave absorption of ferrite layer on microwave frequency and layer thickness. The permeability spectra broaden and the microwave absorption improves at 9–10 GHz with increase of annealing temperature.     

Nanostructures and luminescence properties of porous ZnO thin films prepared by sol–gel process

ZnO thin films containing nano-sized pores were synthesized on solid substrates through a sol–gel process by accommodating cetyl-trimethyl-ammonium bromide (CTAB) as an organic template in the precursor solution. By X-ray diffraction the resultant ZnO films were found to possess ordered pore arrays forming lamellar structure with the spacing between two adjacent pores being ∼3.0 nm. Photoluminescence measurements indicated that the surfactants effectively passivated the surface defects of the ZnO films responsible for the green emission. Al doping was found to improve not only the lamellar structure of the pore arrays but also the near-band-gap emission intensity while the suppression effect of CTAB on the green emission remained undisturbed. With a proper control of doping level, the optical property as well as the structural integrity can be tailored to augment the potential of ZnO films for the optoelectronics and sensor applications.     

Effect of annealing temperature on the structural and optical properties of ZnO thin films prepared by sol–gel method

In this work, ZnO thin films were synthesized by sol–gel method on glass substrates followed by calcinations on different temperatures. The effect of annealing temperature on the structure and optical properties of the films was studied. The structural characteristics of the samples were analyzed by X-ray diffraction and atomic force microscope. The optical properties were studied by a UV-visible spectrophotometer. The results show that all the prepared ZnO thin films have a high preferential oriented c-axis orientation with compact hexagonal wurtzite structure. With the increasing annealing temperature (mse.ufl.edu), the intensity of (002) peak, particle size, surface RMS roughness, and absorbance of the ZnO thin films were increased as well. On the contrary, the transmittance and optical band gaps were decreased.     

Electrical and optical properties of Sb-doped ZnO thin films synthesized by sol–gel method

Sb-doped ZnO thin films with different values of Sb content （from 0 to 1.1 at.%） are deposited by the sol-gel dip- coating method under different sol concentrations. The effects of Sb-doping content, sol concentration, and annealing ambient on the structural, optical, and electrical properties of ZnO films are investigated. The results of the X-ray diffraction and ultraviolet-visible spectroscopy （UV-VIS） spectrophotometer indicate that each of all the films retains the wurtzite ZnO structure and possesses a preferred orientation along the c axis, with high transmittance （〉 90%） in the visible range. The Hall effect measurements show that the vacuum annealed thin films synthesized in the sol concentration of 0.75 mol/L each have an adjustable n-type electrical conductivity by varying Sb-doping density, and the photoluminescence （PL） spectra revealed that the defect emission （around 450 nm） is predominant. However, the thin films prepared by the sol with a concentration of 0.25 mol/L, despite their poor conductivity, have priority in ultraviolet emission, and the PL peak position shows first a blue-shift and then a red-shift with the increase of the Sb doping content.     

Influence of post-deposition annealing on the structural and optical properties of ZnO thin films prepared by sol–gel and spin-coating method

Thin films of zinc oxide have been deposited onto (0001) sapphire substrate by sol–gel and spin-coating methods. The XRD pattern showed that the crystallinity of the annealed ZnO films had improved in comparison with that of the as-grown films. Photoluminescence spectra revealed a two-line structure, which is identified in terms of UV emission and defect-related emission. The emission intensity was found to be greatly dependent on heat treatment. Host phonons of ZnO and a shift of the _E2$E_2$ (high) peak from its position have been observed from Raman spectra. The surface morphologies of the film had been improved after annealing was observed from AFM images.     

Optical and transport properties of Sn-doped ZnMn2O4 prepared by sol–gel method

The paper describes the effect of ZnMn₂O₄ doping with different Sn ratios. Sn_x–ZnMn₂O₄ is prepared with Sol–Gel route at 700 °C. The structural, optical and electrical properties were studied. The X-ray diffraction patterns indicate the formation of pure tetragonal phase for the ratios lower than 0.03%, while for other compositions, the secondary phases were observed. The attenuated total reflectance (ATR) analysis confirmed the localization of Sn in octahedral sites. The optical properties showed not only the increase of E_g, but also the improvement of the optical characteristics such as extinction coefficient (k), optical conductivity (σ_opt), dissipation factor (tan δ) and the relaxation time (τ). The latter has been improved by 50%. The Hall measurements confirmed the transition of the conductivity mode, i.e, from p to n-type. The formation of Sn_Mn¹⁺ point defects is evidenced; however, the transport properties indicate that the charge carriers are mainly localized.     

Structural,optical and photocatalytic properties of (Mg,Al)-codoped ZnO powders prepared by sol–gel method

Structural and optical properties of 1 at % Al-doped Zn_1−xMg_xO (x=0–8%) powders prepared by sol–gel method were systematically investigated by means of X-ray diffraction, scanning electron microscopy, ultraviolet–visible absorbance measurement, photoluminescence and Raman scattering spectra. All the powders retained the hexagonal wurtzite structure of ZnO. The band gap and near band emission energies determined from absorbance and photoluminescence spectra increased linearly with increasing Mg content, respectively, which implied that the Mg worked effectively on ZnO band gap engineering, irrespective of Al codoping. However, according to the PL and Raman scattering studies, for the sample of x=8%, the Al doping efficiency was decreased by higher Mg codoping. On the other hand, the effect of Mg codoping on photocatalytic degradation of methylene orange was explored experimentally. The substitution of Mg ions at Zn sites shifted the conduction band toward higher energies and then enhanced the photocatalytic activity, while the incorporation of interstitial Mg ions and decreased Al doping efficiency for higher Mg doping sample (x=8%) reduced the photocatalytic activity.     

Particle size effects on magnetic properties of yttrium iron garnets prepared by a sol–gel method

We present detailed measurements of field—and temperature—dependence of magnetization in nanocrystalline YIG (Y₃Fe₅O₁₂) particles. The fine powders were prepared using sol–gel method. Samples with particle sizes ranging from 45 to 450 nm were obtained. We observe that the saturation magnetization decreases as the particle size is reduced due to enhancement of the surface spin effects. Below a critical diameter D_s≅190 nm, the particles become single domains and the coercive forces reaches a maximum at diameters close to the critical value. As the particle size decreases the coercivity diminishes and at D_p≃35 nm diameters the upper limit of superparamagnetic behavior is reached. A quantitative comparison of temperature and particle size dependence of coercivity shows a satisfactory agreement that is expected for an assembly of randomly oriented particles.     

Microstructure and electro-optical properties of sol–gel derived Cd-doped ZnO films

The microstructure, and the electrical and optical properties of undoped zinc oxide (ZnO) and cadmium-doped ZnO (CZO) films deposited by a sol–gel method have been investigated. The films have a polycrystalline structure with hexagonal wurtzite ZnO. Scanning electron microscopy (SEM) images indicated that the films have a wrinkle network with uniform size distributions. The elemental analyses of the CZO films were carried out by energy dispersive X-ray analysis. The fundamental absorption edge changed with doping. The optical band gap of the films decreased with Cd dopant. The optical constants of the films such as refractive index, extinction coefficient and dielectric constants changed with Cd dopant. A two-probe method was used to investigate the electrical properties, and the effect of Cd content on the electrical properties was investigated. The electrical conductivity of the films was improved by incorporation of Cd in the ZnO film.     

Indium doping effect on properties of ZnO nanoparticles synthesized by sol–gel method

Pure ZnO and indium-doped ZnO(In–ZO) nanoparticles with concentrations of In ranging from 0 to 5% are synthesized by a sol–gel processing technique. The structural and optical properties of ZnO and In–ZO nanoparticles are characterized by different techniques. The structural study confirms the presence of hexagonal wurtzite phase and indicates the incorporation of In~(3+) ions at the Zn~(2+) sites. However, the optical study shows a high absorption in the UV range and an important reflectance in the visible range. The optical band gap of In–ZnO sample varies between 3.16 e V and 3.22 e V. The photoluminescence(PL) analysis reveals that two emission peaks appear: one is located at 381 nm corresponding to the near-band-edge(NBE) and the other is observed in the green region. The aim of this work is to study the effect of indium doping on the structural, morphological, and optical properties of ZnO nanoparticles.     

Structures and local ferroelectric polarization switching properties of orthorhombic YFeO_3 thin film prepared by a sol–gel method

Orthorhombic YFeO_3 thin film was prepared on La_(0.67)Sr_(0.33)MnO_3/LaAlO_3 substrate by a sol-gel spin-coating method. The structures of the YFeO_3/La_(0.67)Sr_(0.33)MnO_3/LaAlO_3(YFO/LSMO/LAO) sample were detected by x-ray diffraction pattern, Raman spectrometer, scanning electron microscopy, and atomic force microscope. The local ferroelectric polarization switching properties of the orthorhombic YFO film were confirmed by piezoresponse force microscopy(PFM) for the first time. The results show that the YFO film deposited on LSMO/LAO possesses orthorhombic structure,with ultra-fine crystal grains and flat surface. The leakage current of the YFO film is 8.39 × 10~(-4) A·cm~(-2) at 2 V,with its leakage mechanism found to be an ohmic behavior. PFM measurements indicate that the YFO film reveals weak ferroelectricity at room temperature and the local switching behavior of ferroelectric domains has been identified. By local poling experiment, polarization reversal in the orthorhombic YFO film at room temperature was further observed.     

Enhanced structural and magnetic properties of microwave sintered Li–Ni–Co ferrites prepared by sol–gel method

The properties of lithium ferrites are very sensitive to chemical composition, synthesis method, and sintering techniques. Li–Ni–Co ferrites with compositional formula Li_(0.45-0.5x)Ni_(0.1)Co_xFe_(2.45-0.5x)O_4, where 0.00 ≤ x ≤ 0.1 in steps of 0.02 were prepared by chemical sol–gel method and sintered by microwave sintering technique. The x-ray diffraction patterns confirmed the formation of single phase with spinel structure in all the samples. The structural parameter viz.lattice constant, crystallite size, and x-ray density for these samples were studied and compared with those measured from samples of similar composition prepared by the sol–gel method and sintered by conventional sintering technique. Enhancement in the magnetic properties like Curie temperature, hysteresis parameters was observed by employing sol–gel synthesis combined with microwave sintering. The results obtained and mechanisms involved are discussed in the paper.     

Capacitance–voltage and conductance–voltage characteristics of Ag/n-CdO/p-Si MIS structure prepared by sol–gel method

The frequency dependent electrical properties of Ag/n-CdO/p-Si structure has been investigated using capacitance–voltage (C–V) and conductance–voltage (G/ω–V) characteristics in the frequency range 10 kHz–1 MHz in the room temperature. The increase in capacitance at lower frequencies is observed as a signature of interface states. The presence of the interfaces states (N_SS) is also evidenced as a peak in the capacitance–frequency characteristics. Furthermore, the voltage and frequency dependence of series resistance were calculated from the C–V and G/ω–V measurements and plotted as functions of voltage and frequency. The distribution profile of R_S–V gives a peak in the depletion region at low frequencies and disappears with increasing frequencies. The values of interface state densities and series resistance from capacitance–voltage-frequency (C–V-f) and conductance–voltage-frequency (G/ω–V-f) measurements were obtained in the ranges of 1.44×10¹⁶–7.59×10¹² cm^?2 eV^?1 and 341.49–8.77 Ω, respectively. The obtained results show that the C–V-f and G/ω–V-f characteristics confirm that the interface states density (N_SS) and series resistance (R_S) of the diode are important parameters that strongly influence the electrical parameters in Ag/n-CdO/p-Si structures.     

Influence of acid catalysts on the structural and magnetic properties of nanocrystalline barium ferrite prepared by sol–gel method

BaFe₁₂O₁₉ powders with nanocrystalline size were prepared by sol–gel techniques. Nitric, hydrochloric, acetic and stearic acid were used to improve the magnetic properties. Amorphous gels were formed with Fe/Ba molar ratio of 10.5. Then powders were obtained by subsequent heat treatment at 800–1000 °C for 1 h. Barium ferrite powder was also synthesized by solid state reaction at 1210 °C. X-ray diffraction, scanning electron microscopy and transmission electron microscopy (TEM) experiments were conducted to evaluate structural properties of the samples. The value of the effective magnetic susceptibility was measured. The results show that the magnetoplumbite structure was formed in all of the powders. The TEM observation showed that the minimum particle size (20 nm) was produced with the stearic acid catalyst. The highest value of the effective magnetic susceptibility was achieved also using stearic acid.     

Influence of Ag doping on structural and optical properties of ZnO thin films synthesized by the sol–gel technique

Thin films of Ag–ZnO samples deposited on glass substrates with a different percentage of Ag content (1, 2, and 3 at%) were synthesized, at room temperature, by a dip-coating sol-gel method. The obtained samples are hexagonal wurtzite structure. The average grain size of deposits is about 5 nm. Up to 3 at%, c-axis lattice parameter shifts toward a higher value, which indicates that silver atoms replace Zn atoms in the crystal lattice. As shown by the DRX spectra, growth rate in the (101) direction is favored by the presence of silver ions in the ZnO. The layers present a homogeneous crystallites distribution, as we can remark it on SEM micrographs and exhibit a very low roughness according to AFM images. The entire samples exhibit a transmission value greater than 80 %, in the visible region, while the maximum is obtained for those doped at 2 at%. Energy band varies between 3.15 eV and 3.25 eV. The wider gap obtained is that of the ZnO layer doped with 2 at%. It is worth noting a strong UV emission observed on PL spectrum, performed at very low temperature (liquid nitrogen temperature), for silver doped ZnO compared to that of pure ZnO.     

Study of NiCuZn ferrite powders and films prepared by sol gel method

This paper reports that a series of NiCuZn ferrite powders and films are prepared by using sol-gel method.The effects of raw material composition and the calcinate temperature on magnetic properties of them are investigated.The NiCuZn ferrite powders are prepared by the self-propagating high-temperature synthesis method and subsequently heated at 700 C～1000 C.The results show that NiCuZn ferrite powders with single spinel phase can be formed after heat-treating at 750 C.Powders obtained from Ni 0.4 Cu 0.2 Zn 0.4 Fe 1.9 O 4 gel have better magnetic properties than those from gels with other composition.After heat-treating at 900 C for 3 h,coercivity H c and saturation magnetization M s are 9.7 Oe (1 Oe=80 A/m) and 72.4 emu/g,respectively.Different from the powders,NiCuZn films produced on Si (100) from the Ni 0.4 Cu 0.2 Zn 0.4 Fe 2 O 4 gel formed at room temperature possess high properties.When heat-treating condition is around 600 C for 6 min,samples with low H c and high M s will be obtained.The minimal H c is 16.7 Oe and M s is about 300 emu/cm 3.In comparison with the films prepared through long-time heat treating,the films prepared through short heat-treating time exhibits better soft magnetic properties.     

Synthesis and magnetic properties of barium–calcium hexaferrite particles prepared by sol–gel and microemulsion techniques

The preparation of W-type hexaferrite particles with the composition BaCa₂Fe₁₆O₂₇ by microemulsion and a stearic acid sol–gel method with and without surfactant has been investigated at various sintering temperatures. The structural and magnetic characteristics have been studied by X-ray diffraction (XRD), a vibrating sample magnetometer (VSM), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), differential scanning calorimetric (DSC) and Fourier transform infrared (FTIR) techniques. The effect of sintering temperature on the properties of BaCa₂Fe₁₆O₂₇ hexaferrites has been studied. The value of saturation magnetization (M_s) depends on types of surfactant used. The sample prepared in the presence of polyoxyethylene (20) sorbitan monooleat (Tween 80) shows low saturation magnetization (M_s=15.10 emu/g), whereas the other sample prepared in the presence of a surfactant cetyltrimethylammonium bromide (CTAB) exhibits high saturation magnetization (M_s=24.60 emu/g) compared to the normal sample.     

Structural and thermoluminescence properties of undoped and Fe-doped-TiO<Subscript>2</Subscript> nanopowders processed by sol–gel method

In this study, we report on the nanocrystalline powders of TiO₂ and Fe-doped TiO₂ (anatase and rutile phases) prepared by sol–gel method. The X-ray diffraction and Raman spectroscopy measurements indicated the presence of anatase or rutile phase in nanopowders. TEM micrographs showed 10 and 112 nm average particle sizes for anatase and rutile, respectively. Furthermore, their thermoluminescence properties were analyzed.