Curing of linear and crosslinked epoxy systems: A fluorescence study with dansyl derivatives

The curing of diglycidyl ether of bisphenol A (DGEBA) with N,N′-dimethylethylenediamine (N,N′-DMEDA) or ethylenediamine (EDA) was monitored by fluorescence spectroscopy and Fourier transform infrared (in the near-infrared region). 5-Dimethylamino-naphthalene-1-sulfonamide (DNS) derivatives were used as probes (fluorophores added to the reaction mixture) and labels (fluorophores attached by covalent bonds to diglycidyl reactants). The term containing the ratio of the reaction rate constants for the addition of the secondary and primary amine hydrogens to the epoxide was included in the reduced reaction rate term for the autocatalyzed and catalyzed epoxide curing reactions. The changes in the integrated fluorescence intensities of the labels during the epoxy group conversion indicated, in some cases, the most important changes in the chemical transformations of the reaction mixture: the epoxy group conversion, during which a rapid increase in the tertiary amino group concentration was first observed; the gel point (for EDA); and the entry of the system into the glassy state (for N,N′-DMEDA and EDA). The fluorescence probes monitored neither the gel point nor the threshold of the glassy state. For the DGEBA–N,N′-DMEDA system, a wavy dependence of the integrated fluorescence intensities of the DNS labels on the epoxy group conversion might reflect the molar concentrations of polymer homologues (referred to the initial number of moles in the system) in the reaction mixtures of the diepoxide and secondary diamine. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 64–78, 2004     

Synthesis and characterization of fluoropolymers by the polyaddition of bis(epoxide)s with dicarboxylic acids and diols

The synthesis and characterization of the fluoropolymers poly 1a – 1d and poly 2a – 2d with pendant hydroxyl groups were examined. The polyaddition of bis(epoxide)s [2,2′‐bis(4‐glycidyletherphenyl)hexafluoropropane and bisphenol A diglycidyl ether] with dicarboxylic acids (tetrafluoroterephthalic acid and terephthalic acid) and diols [2,2′‐bis(4‐hydroxyphenyl)hexafluoropropane, 2,2′,3,3′,5,5′,6,6′‐octafluoro‐4,4′‐biphenol, 1,4‐bis(hexafluorohydroxyisopropyl)benzene, and 1,3‐bis(hexafluorohydroxyisopropyl)benzene] was carried out at 50–100 °C for 6–48 h in the presence of quaternary onium salts (tetrabutylammonium bromide, tetrabutylammonium chloride, tetrabutylphosphonium bromide, and tetrabutylphosphonium chloride; 2.5 mol %) as catalysts in dimethyl sulfoxide, N‐methylpyrrolidone, dimethylformamide, dimethylacetamide, dioxane, diglyme, o‐dichlorobenzene, chlorobenzene, and toluene to afford the corresponding polymers, poly 1a – 1d and poly 2a – 2d , with number‐average molecular weights of 11,000–59,400 in 45–97% yields. The solubility of the obtained polymers was good, and their thermal stability might be assumed from their structures. A linear relationship was observed between the contents of the fluorine atoms and the refractive indices. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1395–1404, 2002     

Synthesis and characterization of aromatic cyclolinear phosphazene polyetherketones containing bis‐Spiro‐substituted cyclotriphosphazene unit

A novel monomer, 2,2‐bis‐(4′‐fluorobenzoylphenoxy)‐4,4,6,6‐bis[spiro‐(2′,2″‐dioxy‐1′, 1′‐biphenylyl)] cyclotriphosphazene, was synthesized and polymerized with 4,4′‐difluorobenzophenone as a comonomer and 4,4′‐isopropylidenediphenol or 4,4′‐(hexafluoroisopropylidene) diphenol in N,N‐dimethylacetamide at 162 °C for 4 h to give two series of aromatic cyclolinear phosphazene polyetherketones containing bis‐spiro‐substituted cyclotriphosphazene groups. The structure of the monomer was confirmed by ¹H, ¹³C, and ³¹P NMR. The effect of the incorporation of the bis‐spiro‐substituted cyclotriphosphazene group on the thermal properties of these polymers was investigated by DSC and thermogravimetric analysis. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 2993–2997, 2001     

Epoxy resin/poly(ϵ‐caprolactone) blends cured with 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane. I. Miscibility and crystallization kinetics

Crystalline thermosetting blends composed of 2,2′‐bis[4‐(4‐aminophenoxy)phenyl]propane (BAPP)‐cured epoxy resin (ER) and poly(?‐caprolactone) (PCL) were prepared via the in situ curing reaction of epoxy monomers in the presence of PCL, which started from initially homogeneous mixtures of diglycidyl ether of bisphenol A (DGEBA), BAPP, and PCL. The miscibility of the blends after and before the curing reaction was established with differential scanning calorimetry and dynamic mechanical analysis. Single and composition‐dependent glass‐transition temperatures (T_g's) were observed in the entire blend composition after and before the crosslinking reaction. The experimental T_g's were in good agreement with the prediction by the Fox and Gordon–Taylor equations. The curing reaction caused a considerable increase in the overall crystallization rate and dramatically influenced the mechanism of nucleation and the growth of the PCL crystals. The equilibrium melting point depression was observed for the blends. An analysis of the kinetic data according to the Hoffman–Lauritzen crystallization kinetic theory showed that with an increasing amorphous content, the surface energy of the extremity surfaces increased dramatically for DGEBA/PCL blends but decreased for ER/PCL blends. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1085–1098, 2003     

Advanced flame‐retardant epoxy resins from phosphorus‐containing diol

Phosphorus‐containing epoxy systems were prepared from isobutylbis(hydroxypropyl)phosphine oxide (IHPO) and diglycidyl ether of bisphenol A (DGEBA). Diethyl‐N,N‐bis(2‐hydroxyethyl) aminomethyl phosphonate (Fyrol 6) could not be incorporated into the epoxy backbone by a reaction with either epichlorohydrin or DGEBA because intramolecular cyclization took place. The curing behavior of the IHPO–DGEBA prepolymer with two primary amines was studied, and materials with moderate glass‐transition temperatures were obtained. V‐0 materials were obtained when the resins were tested for ignition resistance with the UL‐94 test. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3510–3515, 2005     

Development of novel phosphorus‐containing epoxy resins from renewable resources

Novel biobased epoxy resins were prepared from two fatty acid derivatives; epoxidized 10‐undecenoyl triglyceride and epoxidized methyl 3,4,5‐tris(10‐undecenoyloxy)benzoate, with 4,4′‐diaminodiphenylmethane as a crosslinking agent. The flame retardancy of these epoxy resins was improved by the addition of 10‐[2′, 5′‐bis(9‐oxiranyl‐nonayloxy)phenyl]‐9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide and by crosslinking with a phosphorus‐containing curing agent, bis(m‐aminophenyl)methylphosphine oxide. The thermal, thermomechanical, and flame‐retardant properties of the cured materials were measured with differential scanning calorimetry, thermogravimetric analysis, dynamic mechanical analysis, and the limiting oxygen index. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6717–6727, 2006     

Studies on curing kinetics of a novel combined liquid crystalline epoxy containing tetramethylbiphenyl and aromatic ester‐type mesogenic group with diaminodiphenylsulfone

The curing kinetics of a novel liquid crystalline epoxy resin with combining biphenyl and aromatic ester‐type mesogenic unit, diglycidyl ether of 4,4′‐bis(4‐hydroxybenzoyloxy)‐3,3′,5,5′‐tetramethyl biphenyl (DGE‐BHBTMBP), and the curing agent diaminodiphenylsulfone (DDS) was studied using the advanced isoconvensional method (AICM). DGE‐BHBTMBP/DDS curing system was investigated the curing behavior by means of differential scanning calorimetry (DSC) during isothermal and nonisothermal processes. Only one exothermal peak appeared in isothermal DSC curves. A variation of the effective activation energy with the extent of conversion was obtained by AICM. Three different curing stages were confirmed. In the initial curing stage, the value of E_a is dramatically decreased from ～90 to ～20 kJ/mol in the conversion region 0–0.2 for the formation of LC phase. In the middle stage, the value of E_a keeps about ～80 kJ/mol for cooperative effect of reaction mechanism and diffusion control. In the final stage, a significant increase of E_a from 84 to 136 kJ/mol could be caused by the mobility of longer polymer chains. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3922–3928, 2007     

Cationic,water‐soluble,fluorene‐containing poly(arylene ethynylene)s: Effects of water solubility on aggregation,photoluminescence efficiency,and amplified fluorescence quenching in aqueous solutions

Three novel fluorene‐containing poly(arylene ethynylene)s with amino‐functionalized side groups were synthesized through the Sonogashira reaction. They were poly{9,9‐bis[6′‐(N,N‐diethylamino)hexyl]‐2,7‐fluorenylene ethynylene}‐alt‐co‐{2,5‐bis[3′‐(N,N‐diethylamino)‐1′‐oxapropyl]‐1,4‐phenylene} ( P1 ), poly{9,9‐bis[6′‐(N,N‐diethylamino)hexyl]‐2,7‐fluorenylene ethynylene} ( P2 ), and poly({9,9‐bis[6′‐(N,N‐diethylamino)hexyl]‐2,7‐fluorenylene ethynylene}‐alt‐co‐(1,4‐phenylene)) ( P3 ). Through the postquaternization treatment of P1 – P3 with methyl iodide, we obtained their cationic water‐soluble conjugated polyelectrolytes (WSCPs): P1′ – P3′ . The water solubility was gradually improved from P3′ to P1′ with increasing contents of hydrophilic side chains. After examining the ultraviolet–visible absorption and photoluminescence (PL) spectra, fluorescence lifetimes, and dynamic light scattering data, we propose that with the reduction of the water solubility from P1′ to P3′ , they exhibited a gradually increased degree of aggregation in H₂O. The PL quantum yields of P1′ – P3′ in H₂O displayed a decreasing tendency consistent with the increased degree of aggregation, suggesting that the pronounced degree of aggregation was an important reason for the low PL quantum yields of WSCPs in H₂O. Two structurally analogous water‐soluble trimers of P2′ and P3′ , model compounds 2,7‐bis(9″,9″‐bis{6‴‐[(N,N‐diethyl)‐N‐methylammonium] hexyl}‐2″‐fluorenylethynyl)‐9,9‐bis{6′‐[(N,N‐diethyl)‐N‐methylammonium]hexyl}fluorene hexaiodide and 1,4‐bis(9′,9′‐bis{6″‐[(N,N‐diethyl)‐N‐methylammonium]hexyl}‐2′‐fluorenylethynyl)benzene tetraiodide, were synthesized. The amplified fluorescence quenching of these WSCPs by Fe(CN)₆⁴⁻ in H₂O was studied by comparison with a corresponding analogous trimer. The effects of aggregation on the fluorescence quenching may be two‐edged in these cases. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5778–5794, 2006     

Synthesis of New Ruthenium（Ⅱ）Bipyridyl Complexes and Studies on Their Photophysical and Photoelectrochemical Properties

Two new mixed-ligand ruthenium(Ⅱ） complexes,Ru(dcbpy)-(LL)NCS)2[where dcbpy=4,4‘-dicarboxyl-2,2‘‘-bipyridine,LL=4,4‘-bis(N-methyl-anilinomethyl)-2,2‘‘-bipyridine(2)],were synthesized,and the tphotophysical properties of these complexes were studied.The metal-to-ligand charge transfer (MLCT) transitions of these complexes exhibited solvatochromic effect due to the existence of NCS ligands.The MLCT energies also strongly depend on the pH values of the solutions because of protonation and deprotonation of the carboxyl groups.The pKa values of the ground state,4.0 for 1 and 3.8 for 2,were obtained from the titration curves.The photoelectrochemical properties of 1 and 2 as sensitizers in sandwich-type solar cells have been studied.Complex 1 exhibited better photoelectrochemical behavior than complex 2 as expected.It was proved that the design of mixed-ligand complex by introducing electron donating group in one of the ligands should be a promising approach.     

A New Luminescent Ruthenium(II) Polypyridine‐derived Dipicolylamine Complex as a Sensor for Cu2+ Ions

A chemo‐sensor [Ru(bpy)₂(bpy‐DPF)](PF₆)₂ ( 1 ) (bpy=2,2′‐bipyridine, bpy‐DPF=2,2′‐bipyridyl‐4,4′‐bis(N,N‐di(2‐picolyl))formylamide) for Cu²⁺ using di(2‐picolyl)amine (DPA) as the recognition group and a ruthenium(II) complex as the reporting group was synthesized and characterized successfully. It demonstrates a high selectivity and efficient signaling behavior only for Cu²⁺ with obvious red‐shifted MLCT (metal‐to‐ligand charge transfer transitions) absorptions and dramatic fluorescence quenching compared with Zn²⁺ and other metal ions.     

Shape‐memory effect in hyperbranched poly(ethyleneimine)‐modified epoxy thermosets

A series of shape‐memory epoxy thermosets were synthesized by crosslinking diglycidyl ether of bisphenol A with mixtures of commercially available hyperbranched poly(ethyleneimine) and polyetheramine. Thermal, mechanical and shape‐memory properties were studied and the effect on them of the content and structure of the hyperbranched polymer was discussed. Measurements showed that the glass transition temperature can be tailored from 60 °C to 117 °C depending on the hyperbranched polymer content, and all formulations showed an appropriate glassy/rubbery storage modulus ratio. Shape‐memory programming was carried out at TgE′ given the excellent mechanical properties of the materials, with maximum stress and failure strain up to 15 MPa and 60%, respectively. The resulting shape‐memory behavior was excellent, with maximum shape recovery and shape fixity of 98% as well as a fast shape‐recovery rate of 22%/min. The results show that hyperbranched poly(ethyleneimine) as a crosslinking agent can be used to enhance mechanical and shape‐memory properties with different effects depending on the crosslinking density. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 924–933     

Synthesis and characterization of novel polyamide‐imides containing noncoplanar 2,2′‐dimethyl‐4,4′‐biphenylene unit

A new diimide‐dicarboxylic acid, 2,2′‐dimethyl‐4,4′‐bis(4‐trimellitimidophenoxy)biphenyl (DBTPB), containing a noncoplanar 2,2′‐dimethyl‐4,4′‐biphenylene unit was synthesized by the condensation reaction of 2,2′‐dimethyl‐4,4′‐bis(4‐minophenoxy)biphenyl (DBAPB) with trimellitic anhydride in glacial acetic acid. A series of new polyamide‐imides were prepared by direct polycondensation of DBAPB and various aromatic diamines in N‐methyl‐2‐pyrrolidinone (NMP), using triphenyl phosphite and pyridine as condensing agents. The polymers were produced with high yield and moderate to high inherent viscosities of 0.86–1.33 dL · g⁻¹. Wide‐angle X‐ray diffractograms revealed that the polymers were amorphous. Most of the polymers exhibited good solubility and could be readily dissolved in various solvents such as NMP, N,N‐dimethylacetamide (DMAc), N,N‐dimethylformamide (DMF), dimethyl sulfoxide, pyridine, cyclohexanone, and tetrahydrofuran. These polyamide‐imides had glass‐transition temperatures between 224–302 °C and 10% weight loss temperatures in the range of 501–563 °C in nitrogen atmosphere. The tough polymer films, obtained by casting from DMAc solution, had a tensile strength range of 93–115 MPa and a tensile modulus range of 2.0–2.3 GPa. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 63–70, 2001     

Double‐crosslinked reversible redox‐responsive hydrogels based on disulfide–thiol interchange

We present novel redox‐responsive hydrogels based on poly(N‐isopropylacrylamide) or poly(acrylamide), consisting of a reversible disulfide crosslinking agent N,N′‐bis(acryloyl)cystamine and a permanent crosslinking agent N,N′‐methylenebisacrylamide for microfluidic applications. The mechanism of swelling/deswelling behavior starts with the cleavage and reformation of disulfide bonds, leading to a change of crosslinking density and crosslinking points. Raman and ultraviolet‐visible spectroscopy confirm that conversion efficiency of thiol–disulfide interchange up to 99%. Rheological analysis reveals that the E modulus of hydrogel is dependent on the crosslinking density and can be repeatedly manipulated between high‐ and low‐stiffness states over at least 5 cycles without significant decrease. Kinetic studies showed that the mechanical strength of the gels changes as the redox reaction proceeds. This process is much faster than the autonomous diffusion in the hydrogel. Moreover, cooperative diffusion coefficient (D_coop) indicates that the swelling process of the hydrogel is affected by the reduction reaction. Finally, this reversibly switchable redox behavior of bulky hydrogel could be proven in microstructured hydrogel dots through short‐term photopatterning process. These hydrogel dots on glass substrates also showed the desired short response time on cyclic swelling and shrinking processes known from downsized hydrogel shapes. Such stimuli‐responsive hydrogels with redox‐sensitive crosslinkers open a new pathway in exchanging analytes for sensing and separating in microfluidics applications. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 2590–2601     

Synthesis and characterization of alt‐bipyridinylene‐phenylene copolymers containing ruthenium(II) complexes

Poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3a ), poly{bis(4,4′‐tert‐butyl‐2,2′‐bipyridine)–(2,2′‐bipyridine‐4,4′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3b ), and poly{bis(2,2′‐bipyridine)–(2,2′‐bipyridine‐5,5′‐diyl‐[1,4‐phenylene])–ruthenium(II)bishexafluorophosphate} ( 3c ) were synthesized by the Suzuki coupling reaction. The alternating structure of the copolymers was confirmed by ¹H and ¹³C NMR and elemental analysis. The polymers showed, by ultraviolet–visible, the π–π* absorption of the polymer backbone (320–380 nm) and at a lower energy attributed to the d–π* metal‐to‐ligand charge‐transfer absorption (450 nm for linear 3a and 480 nm for angular 3b ). The polymers were characterized by a monomodal molecular weight distribution. The degree of polymerization was approximately 8 for polymer 3b and 28 for polymer 3d . © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2911–2919, 2004     

Synthesis and micropatterning properties of a novel base‐soluble,positive‐working,photosensitive polyimide having an o‐nitrobenzyl ether group

A novel positive‐working, photosensitive polyimide, poly[1,4‐phenyleneoxy‐1,4‐phenylene‐2,2′‐di(2‐nitrobenzyloxy)benzophenone‐3,3′,4,4′‐tetracarboxdiimide] (OPI‐Nb), developable with an aqueous base was prepared by the o‐nitrobenzylation of a polyimide, poly(1,4‐phenyleneoxy‐1,4‐phenylene‐2,2′‐dihydroxybenzophenone‐3,3′,4,4′‐tetracarboxdiimide) (OPI), derived from 2,2′‐dihydroxy‐3,3′,4,4′‐benzophenonetetracarboxylic dianhydride (DHBA) and 4,4′‐oxydianiline, and it micropatterning properties were investigated. The o‐nitrobenzylation of OPI to OPI‐Nb was conducted with o‐nitrobenzyl bromide in N‐methyl‐2‐pyrrolidinone containing Et₃N. The DHBA monomer was synthesized by exhaustive KMnO₄ oxidation of bis(2‐dimethoxy‐3,4‐dimethylphenyl)methane obtained by etherification of bis(2‐hydroxy‐3,4‐dimethylphenyl)methane with iodomethane, followed by deprotection of the methoxy groups and cyclodehydration of the obtained 2,2′‐dihydroxy‐3,3′4,4′‐benzophenonetetracarboxylic acid. The intermediate bis(2‐hydroxy‐3,4‐dimethylphenyl)methane was prepared by the condensation of 2,3‐dimethylphenol with paraformaldehyde. The degree of o‐nitrobenzylation was determined to be over 94 mol % from ¹H NMR absorption of benzylic CH₂ protons. The aromatic OPI was perfectly soluble in a dilute aqueous NaOH solution and tetramethylammonium hydroxide (TMAH), whereas OPI‐Nb was not even swellable in them. In the micropatterning process, OPI‐Nb showed a line‐width resolution of 0.4‐μm and a sensitivity of 5.4 J/cm² when its thin films were irradiated with 365‐nm light and developed with a 2.38% aqueous TMAH solution at room temperature for 90 s. The thickness loss of OPI‐Nb films measured after postbaking at 350 °C was in the 8–9% range. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 776–788, 2007     

Polymer‐based fluorescence sensors incorporating chiral binaphthyl and benzo[2,1,3]thiadiazole moieties for Hg2+ detection

Three chiral polymers P‐1 , P‐2 , and P‐3 could be obtained by the polymerization of (R)‐6,6′‐dibutyl‐3,3′‐diiodo‐2, 2′‐binaphthol (R‐M‐1) , (R)‐6,6′‐dibutyl‐3,3′‐diiodo‐2,2′‐bisoctoxy‐1,1′‐binaphthyl ( R‐M‐2 ), and (R)‐6,6′‐dibutyl‐3,3′‐diiodo‐2,2′‐bis (diethylaminoethoxy)‐1,1′‐binaphthyl ( R‐M‐3 ) with 4,7‐diethynyl‐benzo[2,1,3]‐thiadiazole ( M‐1) via Pd‐catalyzed Sonogashira reaction, respectively. P‐1 , P‐2 , and P‐3 can show pale red, blue–green, and orange fluorescence. The responsive optical properties of these polymers on various metal ions were investigated by fluorescence spectra. Compared with other cations, such as Co²⁺, Ni²⁺, Ag⁺, Cd²⁺, Cu²⁺, and Zn²⁺, Hg²⁺ can exhibit the most pronounced fluorescence response of these polymers. P‐1 and P‐2 show obvious fluorescence quenching effect upon addition of Hg²⁺, on the contrary, P‐3 shows fluorescence enhancement. Three polymer‐based fluorescent sensors also show excellent fluorescence response for Hg²⁺ detection without interference from other metal ions. The results indicate that these kinds of tunable chiral polybinaphthyls can be used as fluorescence sensors for Hg²⁺ detection. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 997–1006, 2010     

The amplified circularly polarized luminescence emission response of chiral 1,1′‐binaphthol‐based polymers via Zn(II)‐coordination fluorescence enhancement

Two kinds of chiral 1,1′‐binaphthol (BINOL)‐based polymer enantiomers were designed and synthesized by the polymerization of 5,5′‐((2,2′‐bis (octyloxy)‐[1,1′‐binaphthalene]‐3,3′‐diyl)bis(ethyne‐2,1‐diyl))bis(2‐hydroxybenzaldehyde) ( M1 ) with alkyl diamine ( M2 ) via nucleophilic addition–elimination reaction. The resulting chiral polymers can exhibit mirror image cotton effects either in the absence or in the presence of Zn²⁺ ion. Almost no fluorescence or circularly polarized luminescence (CPL) emission could be observed for two chiral BINOL‐based polymer enantiomers in the absence of Zn²⁺. Interestingly, the chiral polymers can show strong fluorescence and CPL response signals upon the addition of Zn²⁺, which can be attributed to Zn²⁺‐coordination fluorescence enhancement effect. This work can develop a new strategy on the design of the novel CPL materials via metal‐coordination reaction. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 1282–1288     

Tetrakis(μ‐2,3‐dimethoxybenzoato)bis[(2,2′‐bipyridine)(2,3‐dimethoxybenzoato)lanthanum(III)]

The title compound, tetrakis(μ‐2,3‐di­methoxy­benzoato)‐κ⁴O:O′;κ⁶O,O′:O′‐bis[(2,2′‐bi­pyridine‐N,N′)(2,3‐di­methoxy­benzoato‐O,O′)lanthanum(III)], [La₂(2,3‐DMOBA)₆(2,2′‐bpy)₂], where 2,3‐DMOBA is 2,3‐di­methoxy­benzoate (C₉H₉O₄) and 2,2′‐bpy is 2,2′‐bi­pyridine (C₁₀H₈N₂), is a dimer with a centre of inversion between the La atoms bridged by four carboxyl­ate ligands. The central La atom is ennea‐coordinated and has a distorted monocapped square‐antiprism geometry.     

Structure and property relationships in model diglycidyl ether of bisphenol‐a and diglycidyl ether of tetramethyl bisphenol‐a epoxy systems. I. Mechanical property characterizations

Model epoxy networks, with variations in crosslink density and in epoxy monomer rigidity, were prepared to study how the network structure affects modulus, T_g, and toughness/toughenability of epoxy resins. Diglycidyl ether of bisphenol‐A and diglycidyl ether of tetramethyl‐bisphenol‐A, along with the corresponding chain extenders, were chosen to study how monomer backbone rigidity and crosslink density affect physical and mechanical properties of epoxies. The present study indicates that, as expected, the backbone rigidity of the epoxy network, not the crosslink density alone, will strongly influence modulus and T_g of epoxy resins. Upon rubber toughening, it is found that the rigidity of the epoxy backbone and/or the nature of the crosslinking agent utilized are most critical to the toughenability of the epoxy. That is, the well‐known correlation between toughenability and the average molecular weight between crosslinks (M_c) does not necessarily hold true when the nature of epoxy backbone molecular mobility is altered. The potential significance of the present findings for a better design of toughened thermosets for structural applications is discussed. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2137–2149, 1999     

New soluble functional polymers by free‐radical copolymerization of methacrylates and bipyridine ruthenium complexes

The luminescent complex [4‐(3‐hydroxypropyl)‐4′‐methyl‐2,2′‐bipyridine]‐bis(2,2′‐bipyridine)‐ruthenium(II)‐bis(hexafluoroantimonate) and its methacrylate derivative were successfully synthesized and fully characterized by two‐dimensional ¹H and ¹³C{¹H} NMR techniques [correlation spectroscopy (COSY) and heteronuclear multiple‐quantum coherence experiment (HMQC)], as well as matrix‐assisted laser desorption ionization time‐of‐flight mass spectrometry. The respective labeled methyl methacrylate‐ruthenium(polypyridyl) copolymers were obtained by free‐radical copolymerization with methyl methacrylate and were characterized utilizing NMR, IR, and UV–visible spectroscopy and gel permeation chromatography. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3954–3964, 2003