The nuclear contribution to the specific heat of single crystals of YBa2Cu3O7 and Bi2Sr2CaCu2O8

Specific heat data below 1 K of Bi₂Sr₂CaCu₂O₈ and YBa₂Cu₃O₇ are analyzed. For YBa₂Cu₃O₇ the nuclear specific heat, C_N, amounts to 38T⁻² μJ/mol K. C_N for Bi₂Sr₂CaCu₂O₈ exceeds that of YBa₂Cu₃O₇ by a factor of 15. The nuclear quadrupolar specific heat contribution alone is insufficient to explain the data for YBa₂Cu₃O₇, while lack of NQR data does not allow such a comparison in Bi₂Sr₂CaCu₂O₈ to be made. The contribution to C_N from nuclear spins coupled via the contact hyperfine interaction with correlated magnetic spins (in the CuO₂ plane) is derived as a function of the correlation length. This contribution can be treated independently from the quadrupolar term. We show that the excess specific heat in YBa₂Cu₃O₇ likely originates in a few percentage of an impurity (oxygen deficient) phase with a strong hyperfine field on the Cu nuclei.     

Magnetic ordering in U4Cu4P7 single crystal

The magnetic ordering in the tetragonal ternary compound U₄Cu₄P₇ has been studied by neutron diffraction. It orders below T_N = 146 K with an antiferromagnetic structure of wave vector k = (001). The magnetic ordering corresponds to a stacking of ferromagnetic (001) uranium planes according to the sequences m₁, m₁, m₂, -m₂, -m₁, -m₁, -m₂, m₂ where m₁ and m₂ represent the magnetic moment, directed along the tetragonal axis of the two uranium sites U(1) (0,0,± z₁) and U(2) (0,0, ± z₂) respectively. The magnetic moments on these two sites have different temperature dependencies as well as well as they reach the different values of 1.1 and 2.2.μ_B for the U(1) and U(2) sites, respectively.     

Neutron diffraction study of magnetic ordering in ErMn2Si2, ErMn2Ge2 and ErFe2Si2

Neutron diffraction study of polycrystalline compounds ErMn₂Si₂, ErMn₂Ge₂ and ErFe₂Si₂ was performed in the temperature range between 1.8 and 293 K. All compounds have tetragonal, ThCr₂Si₂-type crystal structure. The antiferromagnetic collinear structure of ErMn₂Si₂ and ErMn₂Ge₂ at both RT and LNT, consists of a sequence + - + - of ferromagnetic layers of Mn atoms. The magnetic moment of an Mn atom (≈2μ_B) is parallel to the c-axist. At low temperatures (LHT and lower), the ferromagnetic ordering within the Er sublattice is observed. The magnetic moment (μ_Er ≈ 9μ_B) is perpendicular to the c-axis. From the temperature dependence of the intensities of the magnetic peaks, the following values for the Curie temperatures were obtained: (10±5) K for ErMn₂Si₂ and (8.5±3) K for ErMn₂Ge₂. For ErFe₂Si₂ a collinear antiferromagnetic structure of the + - - + type was found, the magnetic unit cell consisting of the chemical one, doubled along the c-axis.     

Lu2Ti2O7和Lu2TiO5陶瓷材料的Kr离子辐照损伤研究

钛酸盐因其优异的物理化学性能,可作为高放射性核废物（HLW）和锕系元素（钚）的重要候选固化材料之一。采用传统的陶瓷烧结工艺制备了多晶的Lu₂Ti₂O₇和Lu₂TiO₅陶瓷材料。在室温下,用800 keVKr2+对两种材料进行辐照,辐照后的样品采用GIXRD进行表征,观察到两种样品都经历了先肿胀、然后再发生非晶相变的过程。不同的是Lu₂Ti₂O₇的晶格肿胀程度大于Lu₂TiO₅。另外,Lu₂TiO₅样品的辐照到2×10₁₄ ions/cm₂时非晶含量达95.54%,而Lu₂Ti₂O₇样品在此剂量下非晶含量只有74.66%。通过第一性原理计算了Lu₂Ti₂O₇晶体的晶格肿胀随反位浓度的变化关系,结果表明,Lu₂Ti₂O₇出现非晶前的晶格肿胀主要由阳离子反位导致,而Lu₂TiO₅是无序的萤石结构,其辐照所导致的晶格肿胀不含阳离子反位的贡献,晶格肿胀程度较低。     

(1-x)Sr_3Sn_2O_7+xCa_3Mn_2O_7陶瓷合成及其光电性能

为了寻求新的非常规多铁性材料,采用固相合成方法制备具有Ruddlesden-Popper结构的(1-x)Sr_3Sn_2O_7+x Ca_3Mn_2O_7(SSO+CMO)(x=0,0.05,0.10,0.15,0.20)系列陶瓷.通过X射线衍射、紫外可见光谱和磁性测量,发现SSO+CMO陶瓷为单一正交相结构,空间群为A21am.随着掺杂量x的增加,样品的晶胞参数和体积相应地减小;在室温不同频率下,样品的介电常数和介电损耗随着频率增加而减小,且在x=0.1时有弱的铁磁性.     

Magnetic properties of xFe2O3(1−x)[B2O3 · PbO] glasses

The magnetic measurements performed on xFe₂O₃(1-x)[B₂O₃ · PbO] glasses show that for x 5 mol.% Fe₂O₃ the thermal variation of reciprocal susceptibility obeys a Curie behaviour. For higher iron content, at T 50 K, a nonlinear variation, typical for systems with random distribution of exchange interactions is observed. At greater temperatures than 50 K a Curie-Weiss behaviour is shown. The composition dependence of the Curie constants is analysed in correlation with the number of Fe³⁺ and Fe²⁺ ions as determined from Mössbauer effect measurements. A comparison with the data obtained in case of xFe₂O₃(1-x)[3B₂O₃ · PbO] glasses is made.     

铯原子7S1/2态磁偶极超精细常数的测量

在室温下的原子气室中, 基于铯原子6S_1/2-6P_3/2-7S_1/2(852.3 nm+1469.9 nm) 阶梯型能级系统, 利用电光调制器的主频和±1级边带分别产生的三套双共振吸收光谱, 当驱动电光调制器的信号源频率严格等于7S_1/2态超精细分裂的能级间隔时, 三套谱线中的一些超精细跃迁谱线重叠且线宽最窄, 利用这一现象很好地避免了激光器频率扫描时非线性效应的影响, 测量出了7S_1/2 态超精细分裂能级间隔: 2183.72 MHz±0.23 MHz, 并计算出该态的磁偶极超精细常数: A_hfs= 545.93 m MHz±0.06 MHz, 与文献中报道的测量结果一致.     

Ionic conductivity of crystalline and glassy Mg4.5Na7(P2O7)4

In our work single crystals of Mg_4.5Na₇(P₂O₇)₄ were prepared, pulverized, pressed into pellets and sintered in order to measure the electrical conductivity of polycrystalline specimens. The conductivity was also measured on glassy specimens obtained by the melting of previously prepared crystals. The electrical conductivities at 25°C with values of the order of 10⁻¹⁶ Ω⁻¹ cm⁻¹ for polycrystalline samples and a value of the order of 10⁻¹⁴ Ω⁻¹ cm⁻¹ for glass, show that the glassy phase of Mg_4.5Na₇(P₂ because of its greater molar volume and loosely packed structure, is a better matrix for ionic motion.     

Pb掺杂对Cd_2Ru_2O_7反常金属态的调控

具有烧绿石结构的Cd_2Ru_2O_7在形成长程反铁磁序的同时进入反常的金属态.采用高压高温方法制备了一系列Pb掺杂的Cd_(2-x)Pb_xRu_2O_7(0≤x≤2)多晶样品,并系统研究了其晶体结构和电阻率、磁化率、热电势等物理性质.尽管Pb_2Ru_2O_7是泡利顺磁金属,但少量Pb~(2+)掺杂的样品Cd1.8Pb0.2Ru2O7却呈现出明显的金属-绝缘体转变,与施加静水压和少量Ca~(2+)掺杂的效果类似.通过与类似的烧绿石Ru~(5+)氧化物进行对比,提出Cd_2Ru_2O_7中的Ru~(5+)-4d~3电子态恰好处于巡游到局域过渡的区域,少量Pb~(2+)掺杂造成的晶格无序增强了电子的局域性,使得形成反铁磁序的同时伴随出现了金属-绝缘体转变.这表明具有烧绿石结构的Ru~(5+)氧化物是研究巡游-局域电子转变的理想材料体系.     

钙钛矿型锰氧化物(La$lt;sub$gt;0.8$lt;/sub$gt;Eu$lt;sub$gt;0.2$lt;/sub$gt;)$lt;sub$gt;4/3$lt;/sub$gt;Sr$lt;sub$gt;5/3$lt;/sub$gt;Mn$lt;sub$gt;2$lt;/sub$gt;O$lt;sub$gt;7$lt;/sub$gt;的磁性和电性研究

采用传统固相反应法制备钙钛矿型锰氧化物 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇多晶样品, X-射线衍射分析表明, 样品(La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇结构呈现良好的单相. 通过磁化强度随温度的变化曲线(M-T)、不同温度下磁化强度随磁场的变化曲线(M-H)和电子自旋共振谱发现: 在300 K以下, 随着温度的降低, 样品先后经历了二维短程铁磁有序转变 (T_C^2D ≈ 282 K)、三维长程铁磁有序转变(T_C^3D ≈ 259 K)、奈尔转变(T_N ≈ 208K)和电荷有序转变(T_CO ≈ 35 K); 样品 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇在T_N以下, 主要处于反铁磁态; 在T_C^3D达到370 K时, 样品处于铁磁-顺磁共存态, 在370 K以上时样品进入顺磁态. 此外, 分析电阻率随温度的变化曲线(ρ-T)得到: 样品在金属-绝缘转变温度(T_P ≈ 80 K)附近出现最大磁电阻值, 其位置远离T_C^3D, 表现出非本征磁电阻现象, 其磁电阻值约为61%. 在T_CO以下, 电阻率出现明显增长, 这是由于温度下降使原本在高温部分巡游的e_g电子开始自发局域化增强所致. 通过对 (La_0.8Eu_0.2)_4/3Sr_5/3Mn₂O₇的ρ-T 曲线拟合, 发现样品在高温部分的导电方式基本遵循小极化子的导电方式. 关键词： 磁性 电性 金属-绝缘转变温度 电子自旋共振     

The crystal structure of (Pb0.5Cd0.5)Sr2 (Y1−xCax)Cu2O7

The crystal structures of (Pb_0.5Cd_0.5)Sr₂YCu₂O₇, (Pb_0.5Cd_0.5)Sr₂(Y_0.6Ca_0.4)Cu₂O₇ and (Pb_0.5Cd _0.5)Sr₂(Y_0.5Ca_0.5)Cu₂O₇ have been refined by the Rietveld method for the X-ray diffraction data. The refinement results indicate that both Pb and Cd atoms in the (Pb, Cd)O layers and O(3) atoms are displaced from their ideal sites, and that there is a complicated occupation in the (Pb, Cd)O layers, i.e., other cations, such as Sr²⁺, Cu²⁺ and Ca²⁺, can occupy the (Pb, Cd) site for these samples. This may be the reason why the lattice constants do not vary monotanically with the calcium content, and why there exist broad superconducting transitions in the system (Pb_0.5Cd_0.5)Sr₂(Y_1−xCa_x)Cu₂O₇. The refinement results also indicate that, as the calcium content increases, the O(2) atoms move close to the CuO₂ planes and far from the (Pb, Cd)O layers. Thus, the increase of calcium content results in charge transfer from the charge reservoir layer (Pb, Cd)O to the CuO₂ planes. This result is consistent with the bond valence sums of the Cu ions in the CuO₂ planes.     

铀在Nd_2Zr_2O_7烧绿石中的固溶量及重离子辐照效应

Nd_2Zr_2O_7烧绿石因其稳定的物理化学性质和辐照稳定性可以作为高放废物中锕系核素的固化基材.通过溶胶凝胶—喷雾热解—高温烧结方法制备了含铀的Nd_2Zr_2O_7烧绿石固化体;开展了Nd_2Zr_2O_7和Nd_(1.9)U_(0.1)Zr_2O_7固化体的重离子辐照实验,辐照剂量为1 dpa和3 dpa;利用X射线衍射和Raman光谱对固化体结构进行了分析.研究发现铀在Nd_2Zr_2O_7烧绿石体系的固溶量仅为10 at%,高价态铀掺杂导致固化体结构向无序化转变.重离子辐照实验表明, Nd_2Zr_2O_7烧绿石基材具有较高的抗辐照稳定性;而Nd_(1.9)U_(0.1)Zr_2O_7在较低辐照剂量下,固化体烧绿石体系结构破坏,重离子辐照诱导固化体结构转变为更加无序化的萤石结构.低固溶量和抗辐照能力减弱主要是由于锕系核素烧绿石固化体的结构无序化所致.     

Infrared optical response of YBa2Cu3O7 and PrBa2Cu3O7 An ellipsometric study

Ellipsometry was used to study (110) and (001) oriented films of YBa₂Cu₃O₇ and PrBa₂Cu₃O₇ in the mid-and near-infrared spectral regions. Below a photon energy of 0.1 eV, the in-plane component of the dielectric tensor of YBa₂Cu₃O₇ is dominated by a Drude term with a squared plasma energy of (3.0 ± 0.3) eV². This “oscillator strength”, and the Lorentzian broadening energy of (0.104 ± 0.005) eV at room temperature, are confirmed by the changes induced in Pr-substituted material, and by low-temperature measurements in the near-infrared. The deviation from the Drude behavior observed above 0.1 eV is accounted for by a broad absorption band with an oscillator strength of (3.6 ± 0.1) eV² in YBa₂Cu₃O₇ which shifts to higher energies and takes over almost all of the oscillator strength of the Drude term when Y is substituted by Pr. The response to electric fields perpendicular to the planes is much weaker, with an upper bound of 0.63 eV² for the squared plasma energy. The in-plane loss function computed from the measured dielectric function follows the Drude-like lineshape, modified by the bound-state absorption band, down to the lowest energy reached in our measurements (0.058 eV).     

Tuning the multiferroic properties of Pb(Fe1/2Nb1/2)O3 by cationic substitution

A series of substituted lead iron niobate compounds with the general formula Pb²⁺_(1−x)A^Z_x(Fe_{{(1−(2−Z)x)/2}}Nb_{{(1+(2−Z)x)/2}})O₃ (0<x<0.6 and A=La³⁺, K⁺ or Sr²⁺) were prepared by a modified solid-state synthesis. The relative concentrations of Fe³⁺ and Nb⁵⁺ were adjusted to compensate the charge imbalance due to the aliovalent substitution. The dielectric constant and magnetic susceptibilities were studied as a function of temperature. The temperature of the dielectric maximum, T_M, of the substituted compounds decreased linearly with increasing concentration of the substituent ions. The magnetic measurements showed an antiferromagnetic transition at temperatures T_N1 due to the superexchange interactions mediated by Fe–O–Fe and an additional antiferromagnetic-type transition at T_N2. T_N1 linearly increased with the increasing concentration of Fe³⁺ ion at the B-site of ABO₃-type substituted compounds. T_M is shown to be directly dependent on the concentration of the ferroactive Nb⁵⁺ ions at the B-site and Pb²⁺ ions at the A-site.     

Magnetic ordering temperature of [(CH3)3ND] CoCl3·2D2O

Deuteration of the readily-exchangeable protons in [(CH₃)₃NH]-CoCl₃·2H₂O causes little or no change in the long-range magnetic ordering temperature. This is consistent with the strong two-dimensional anisotropy of exchange interactions in this chained compound.     

The itinerant electron metamagnetism for ScCo2, YCo2 and LuCo2

Electronic structure of d-electrons under external magnetic field is calculated for ScCo₂, YCo₂ and LuCo₂ in the self-consistent tight-binding approximation and the field dependence of the induced moment is estimated in the Hartree-Fock approximation. The critical field of the metamegnetic transition for these compounds is evaluated at 0 K.     

用穆斯堡尔效应研究YBa2Cu3O7-δ中的磁有序

以⁵⁷Fe作为探针,用穆斯堡尔效应研究YBa₂Cu₃O_7-δ的磁有序与超导电性的关系。实验结果可以用非声子超导机制进行定性解释。 关键词：     

Tb掺杂双层锰氧化物La_(4/3)Sr_(5/3)Mn_2O_7的磁熵变和电输运性质

研究了Tb掺杂对双层锰氧化物La_(4/3)Sr_(5/3)Mn_2O_7磁熵变和电输运性质的影响.样品采用传统固相反应法制备,两样品的名义组分可以表示为(La_(1-x)Tb_x)_(4/3)Sr_(5/3)Mn_2O_7(x=0,0.025),磁场为7 T时的最大磁熵变?S_M分别为-4.60 J/(kg·K)和-4.18 J/(kg·K).比较后发现,Tb元素的掺杂使得最大磁熵变值减小,但同时增大了相对制冷温区.电性测量结果表明,x=0.025的样品在高温区的导电机制可以用小极化子模型解释,与母体三维变程跳跃模型不同;当温度降低至三维长程铁磁有序温度(T_c~(3D))附近时,掺杂样品发生金属绝缘相变;掺杂后样品在T_c~(3D)附近,磁电阻取得极大值(约为56%),表明是本征磁电阻效应.     

钙钛矿锰氧化物(La_(1-x)Eu_x)_(4/3)Sr_(5/3)Mn_2O_7(x=0,0.15)的磁性和电性研究

通过传统固相反应法制备了钙钛矿锰氧化物(La1-xEux)4/3Sr5/3Mn2O7(x=0,0.15)多晶样品,并且对其磁性和电性进行了研究.磁性测量表明:随着温度的降低,样品经历了一个复杂的转变过程,在温度为T*时经历二维短程铁磁有序转变,在温度为TC时进入三维长程铁磁态.随着Eu的掺杂,T*和TC减小,并且样品(La0.85Eu0.15)4/3Sr5/3Mn2O7在低温区表现出自旋玻璃行为.电性质测量表明:在母体La4/3Sr5/3Mn2O7中La位掺杂Eu后电阻率明显变大,金属绝缘转变温度TMI降低,磁电阻峰值增大.这些影响归因于较小的Eu3+离子替代La3+离子导致平均离子半径减小,晶格发生畸变.此外,较小的Eu3+离子优先占据层间岩盐层的R-site,使La3+,Sr3+,Eu3+离子在(La0.85Eu0.15)4/3Sr5/3Mn2O7中的分布更加有序,所以x=0.15的样品的ρ-T曲线只有一个峰.     

Realization and properties of ramp-type YBa2Cu3O7−δ/Au/Nb junctions

All-thin-film ramp type Josephson junctions between YBa₂Cu₃O_7−δ and Nb have been fabricated. This procedure allows connections between high-T_c and low-T_c superconductors at different crystal sides of the high-T_c superconductor on one chip, which is of great interest for novel phase devices. A thin Au layer is incorporated as a chemical barrier to avoid oxygen transfer from the YBa₂Cu₃O_7−δ to the Nb. Critical current densities up to 600 A/cm² are obtained at T=4.2 K, with typical R_nA values of 0.8 μΩ cm². The variation of the magnetic field dependence of the critical current with the angle between the junction barrier and the YBa₂Cu₃O_7−δ crystal axes is explained by considering a predominant d_x²−y² order parameter symmetry of the YBa₂Cu₃O_7−δ. The successful fabrication of these junctions allows the implementation of novel superconducting electronics, such as complementary Josephson circuitry or proposed qubit concepts, using the unconventional order parameter symmetry of the high-T_c superconductor.