Assembly of Alternated Multivalent Ion/Polyelectrolyte Layers on Colloidal Particles. Stability of the Multilayers and Encapsulation of Macromolecules into Polyelectrolyte Capsules

Alternating adsorption of multivalent ions and oppositely charged polyelectrolytes on colloid particles has been investigated. Multilayer films composed of Tb³⁺/polysterene sulfonate (PSS) and 4-pyrene sulfate/polyallylamine (PAH) were successfully assembled on polysterene sulfonate (PS) and melamine formaldehyde (MF) latex particles. The amount of assembled material was estimated by fluorescence and the linear growth of the film versus the number of layers was demonstrated. These multilayers are not stable and can be decomposed by salt and temperature. Dissolution of MF particles leads to formation of hollow capsules consisting of multivalent ion/polyelectrolyte multilayers. Comparative analysis of the capsules was done by confocal and scanning force microscopy. Complex hollow spheres consisting of Tb³⁺/PSS or 4-PS/PAH as an inner shell and stable PSS/PAH as an outer shell were produced. Due to selective permeability of the outer shell after degradation of the inner shell the multivalent ions are released out of the capsule while the polyelectrolytes fill the capsule interior. This is indicative of swelling of the capsule by osmotic pressure. The filled capsules were studied by confocal and scanning electron microscopy. Possibilities of encapsulating macromolecules in defined amounts per capsule are discussed.     

Microparticles of poly(methacrylic acid)–gadolinium ion complex and their magnetic force microscopic images

Modified poly(methacrylic acid) microparticles complexed with gadolinium(III) (Gd³⁺) ions were prepared in 100 nm. The emulsion terpolymerization of methacrylic acid, ethyl acrylate, and allyl methacrylate and the following complexation with Gd³⁺ ions yielded the polymer particles with different Gd³⁺ ion contents. Potentiometric titration of the complexation of the particle with Gd³⁺ ions indicated the formation of a very stable tris‐carboxylate coordinate complex with the Gd³⁺ ion. Electron spin resonance and IR spectra of the complexed particles were dependent on the Gd³⁺ ion content and the coordination environment in each particle. The microparticles dispersed on a mica substrate were subjected to atomic force microscopy (AFM), followed by magnetic force microscopy (MFM). AFM showed 100‐nm‐sized and monodispersed spherical images. The following MFM clearly provided strong magnetic responses exactly on the same particle positions, of which the images were also dependent on the Gd³⁺ ion content in the particle. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1912–1918, 2004     

Site percolation model for latex film formation in soft polymer matrix

The UV-visible (UVV) technique was used to monitor latex film formation in a soft polymer matrix. Various film samples were prepared by increasing the amount of poly(methyl methacrylate) (PMMA) particles in a poly(isobutylene) (PIB) matrix. These samples were then annealed above the glass transition temperature to promote latex film formation. Transmitted photon intensities, Itr, were measured for each film. It is observed that Itr decrease as the latex content is increased, which was explained by the increase in scattered light intensity, Isc. The drastic increase in Isc above a certain latex content is attributed to the site percolation of latex particles in the PIB matrix. The percolation threshold and the critical exponent were measured and found to be 0.3 and 0.4, respectively. The increase in Itr by annealing of film samples above Tg was explained with the void closure process below 0.8 occupation probability. When the film is occupied completely with the latex particles, interdiffusion of polymer chains was observed. Viscous flow and chain diffusion activation energies were determined and found to be 8 and 51 kcal/mol, respectively.     

Simple test system for single molecule recognition force microscopy

We have established an easy-to-use test system for detecting receptor-ligand interactions on the single molecule level using atomic force microscopy (AFM). For this, avidin-biotin, probably the best characterized receptor-ligand pair, was chosen. AFM sensors were prepared containing tethered biotin molecules at sufficiently low surface concentrations appropriate for single molecule studies. A biotin tether, consisting of a 6 nm poly(ethylene glycol) (PEG) chain and a functional succinimide group at the other end, was newly synthesized and covalently coupled to amine-functionalized AFM tips. In particular, PEG₈₀₀ diamine was glutarylated, the mono-adduct NH₂-PEG-COOH was isolated by ion exchange chromatography and reacted with biotin succinimidylester to give biotin-PEG-COOH which was then activated as N-hydroxysuccinimide (NHS) ester to give the biotin-PEG-NHS conjugate which was coupled to the aminofunctionalized AFM tip. The motional freedom provided by PEG allows for free rotation of the biotin molecule on the AFM sensor and for specific binding to avidin which had been adsorbed to mica surfaces via electrostatic interactions. Specific avidin-biotin recognition events were discriminated from nonspecific tip-mica adhesion by their typical unbinding force (∼40 pN at 1.4 nN/s loading rate), unbinding length (<13 nm), the characteristic nonlinear force-distance relation of the PEG linker, and by specific block with excess of free d-biotin. The convenience of the test system allowed to evaluate, and compare, different methods and conditions of tip aminofunctionalization with respect to specific binding and nonspecific adhesion. It is concluded that this system is well suited as calibration or start-up kit for single molecule recognition force microscopy.     

Effect of structural stress on the intercalation rate of kaolinite

Particle size in kaolinite intercalation showed an inverse reactivity trend compared with most chemical reactions: finer particles had lower reactivity and some of the fine particles cannot be intercalated. Although this phenomenon was noted in the early 1960s and several hypotheses have been reported, there is no widely accepted theory about the unusual particle size response in the intercalation. We propose that structural stress is a controlling factor in the intercalation and the stress contributes to the higher reactivity of the coarser particles. In this study, we checked the structural deformation spectroscopically and indirectly proved the structural stress hypothesis. A Georgia kaolinite was separated into nine size fractions and their intercalations by hydrazine monohydrate and potassium acetate were investigated with X-ray diffraction (XRD) and Fourier-transform infrared (FTIR) analyses. The apical Si-O band of kaolinite at 1115 cm(-1) shifted to 1124 cm(-1) when the mineral was intercalated to 1.03 nm by hydrazine monohydrate, and its strong pleochroic properties became much weaker. Similar reduction in pleochroism was observed on the surface OH bands of kaolinite after intercalation. Both the bending vibrations of the inner OH group at 914 cm(-1) and of the surface OH group at 937 cm(-1) shifted to 903 cm(-1) after intercalation by hydrazine. A new band for the inner OH group appeared at 3611 cm(-1) during the deintercalation of the 1.03 nm hydrazine kaolinite complex. Pleochroism change in the apical Si-O band suggested the tetrahedra had increased tilt with respect to the (001) plane. The tilt of the Si-O apical bond could occur only if the octahedra had also undergone structural rearrangement during intercalation. These changes in the octahedral and tetrahedral sheets represent some change in the manner of compensation for the structural misfit of the tetrahedral sheet and octahedral sheet. As the lateral dimensions of a kaolinite particle increases, the cumulative degree of misfit increases. Intercalation breaks the hydrogen bonds between layers and allows for the structure to reduce the accumulated stress in some other manner. The reversed size effect on intercalation probably was not caused by crystallinity differences as reported in the literature, because the Hinckley and Lietard crystallinity indices of the four clay fractions were very close to each other. Impurities, such as dickite- or nacrite-like phases are not significant in the studied sample as suggested by the XRD and IR results, they are not the main reasons for the lower reactivity of the finer particles.     

Dielectrophoretic behavior of latex nanospheres: low-frequency dispersion

The electrostatic manipulation of nanoparticles using nonuniform electric fields (dielectrophoresis) has proved a useful method of investigating the movement of charge around colloidal particles. While previous work has explained many of the ways in which particle behavior deviates from that predicted by classical Maxwell-Wagner interfacial polarization theory, there exists an additional, anomalous polarization mechanism observed in media of high conductivity, causing an unexpected observation of positive dielectrophoresis. Here this is suggested that this may be explained in terms of the polarization of the Stern layer.     

Influence of electrical double-layer interaction on coal flotation

In the early 1930s it was first reported that inorganic electrolytes enhance the floatability of coal and naturally hydrophobic minerals. To date, explanations of coal flotation in electrolytes have not been entirely clear. This research investigated the floatability of coal in NaCl and MgCl2 solutions using a modified Hallimond tube to examine the role of the electrical double-layer interaction between bubbles and particles. Flotation of coal was highly dependent on changes in solution pH, type of electrolyte, and electrolyte concentration. Floatability of coal in electrolyte solutions was seen not to be entirely controlled by the electrical double-layer interaction. Coal flotation in low electrolyte concentration solutions decreases with increase in concentration, not expected from the theory since the electrical double layer is compressed, resulting in diminishing the (electrical double layer) repulsion between the bubble and the coal particles. Unlike in low electrolyte concentration solutions, coal flotation in high electrolyte concentration solutions increases with increase in electrolyte concentration. Again, this behavior of coal flotation in high electrolyte concentration solutions cannot be quantitatively explained using the electrical double-layer interaction. Possible mechanisms are discussed in terms of the bubston (i.e., bubble stabilized by ions) phenomenon, which explains the existence of the submicron gas bubbles on the hydrophobic coal surface.     

Application of the JKR Method to the Measurement of Adhesion to Langmuir-Blodgett Cellulose Surfaces

The JKR method has been applied for studying adhesion between poly(dimethylsiloxane) (PDMS) caps and Langmuir–Blodgett cellulose surfaces including the substrate, hydrophobized mica, and two flat mineral surfaces, bare mica and glass. The self-adhesion of PDMS caps and oxidized PDMS caps are included as a reference to compare with literature data. The results of the measurements have been compared with previous studies using the surface force apparatus and similar systems. A satisfactory agreement is obtained for simple systems showing no, or very limited, hysteresis between loading and unloading curves. In several cases, however, a large hysteresis is found between loading and unloading curves, with a larger adhesion measured from the pull-off force than from the JKR-curve determined on loading. This is, for instance, the case for PDMS against cellulose. The situation is analogous to that found in wetting studies showing a large hysteresis between advancing and receding contact angles.     

Volume Fraction Effects in Electroacoustic Measurements

We measured the dynamic mobility of a polystyrene latex at 1 MHz as a function of volume fraction using the ESA-8000. The volume fraction dependence is compared with a semiempirical equation as well as with some theoretical predictions. It turns out that our polystyrene latex exhibits a volume fraction dependence much weaker than that predicted by any of the theories. This suggests that (polystyrene) latices may not be the ideal model system and that the centrifugation process may influence the surface structure of the particles. We also measured the dynamic mobility spectrum of a silica sol as a function of volume fraction using the Acoustosizer. The experimental spectrum of the silica sol was found to agree reasonably well with the semiempirical and theoretical spectra, especially below φ=0.144. At higher volume fractions we observed positive phase angles that were not predicted by the semiempirical method nor the cell model.     

Novel sintering behavior of polystyrene nanolatex particles in the filming process

The filming process of polystyrene nanolatex (NPS) particles was studied by a combination of various methods. For a constant annealing time of 1 h, the AFM images showed that the deformation and interdiffusion temperatures of NPS particles were ca. 90 and 100-110 degrees C, respectively. In spin-lattice relaxation measurements of solid state NMR, it is found that T1L, T1S, and PL increased significantly after annealing at 90 and 100 degrees C for 1 h. DSC results showed that there was a exothermic peak near Tg after annealing for 1 h at the elected temperatures below 95 degrees C; otherwise, the exothermic peak disappeared after annealing at 100 degrees C or above. The apparent density of NPS increased suddenly in the temperature range of 90-110 degrees C. The results indicated that the macromolecules are highly constrained in NPS particles, leading to higher conformational energy, with more free volume and segments less restricted, which are the driving forces for the particles sintering at a lower temperature compared to the micro-PS particles with larger diameter.     

Comparative observation of the recombinant adeno-associated virus 2 using transmission electron microscopy and atomic force microscopy.

Adeno-associated virus (AAV) is a defective, nonpathogenic human parvovirus, which coinfects with a helper adenovirus or herpes virus. AAV's unique characteristics have made it an appealing vector system for gene delivery. AAV or recombinant AAV (rAAV) has been widely detected using negative stain transmission electron microscopy (TEM) but little has been detected using atomic force microscopy (AFM). In this article, we used AFM and TEM to observe the recombinant AAV-2 (rAAV-2) virus particles and applied statistical analysis to the AFM and TEM images. The results indicated that the rAAV-2 particle was a slightly elliptic particle close to round when it was detected by TEM (the mean length of major and minor axes of rAAV-2 particles was 24.77 +/- 1.78 nm and 21.84 +/- 1.57 nm, respectively), whereas when detected by AFM, the rAAV-2 particle was almost round. Even though the dimensions of the rAAV-2 particle exhibited a polymorphous distribution via off-line particle analysis of AFM, most of the rAAV-2 particles had a mean diameter of approximate 22.04 nm, which was similar to the results obtained by TEM. The results above suggested that AFM was important for accurately determining the average dimensions and distributions of virus particles.     

Polydispersity and Functional Group Distribution of Dispersant Polymer: Adsorption Properties and Magnetic Paint Dispersion

The quantitative analysis examining the functional group distribution of a dispersant polymer for magnetic paints is conducted by statistical estimation and adsorption experiments. The dispersant polymer contains averagely one or two functional groups on the chain, and has generally large polydispersity. By the calculation based on the random distribution of the functional group and the molecular weight, a typical design of the dispersant polymer is found to contain a significant amount of nonfunctionalized chains and highly functionalized ones. In adsorption experiments, the adsorbed amount of the polymer mass and the functional group are separately measured to determine the functional group distribution. The distribution is also evaluated by a sequential adsorption experiment, in which the chains are fractionated by the adsorption strength. Obtained experimental results agree with the calculated results. A practical method for increasing the effective chains in the paint is to make use of a preferential adsorption of the functionalized chain.     

Influence of Surface Hydrophobic Groups on the Adsorption of Proteins onto Nonporous Polymeric Particles with Immobilized Metal Ions

Iminodiacetic acid (IDA) and octyl moieties were covalently bound on nonporous particles, which were prepared from dispersion polymerization of methyl methacrylate and glycidyl methacrylate. After being charged with copper ions, the IDA-bound particles could specifically adsorb deoxyribonuclease I (DNase I) through the affinity interaction between protein and immobilized metal ion. A mixed-ligand (metal–chelate and octyl–bound) support was obtained after hydrophobic (octyl) groups were also introduced to the particle surface. The affinity adsorption of DNase I on the copper–IDA chelate was influenced by interaction between the protein and the bound octyl group. Both the affinity and the hydrophobic interactions could be well described by the Langmuir isotherms. The equilibrium adsorption constants were estimated separately to be 0.96 and 0.50 liter g⁻¹ for affinity and hydrophobic bindings, respectively. For binding on mixed-ligand support, the adsorption constant was 0.45 liter g⁻¹. It was evident that both affinity and hydrophobic interactions are involved in the adsorption of proteins onto mixed-ligand particles. Desorption of the inactive proteins from the support was possible by increasing the hydrophobicity of the solution.     

Multiple emulsion stability: pressure balance and interfacial film strength

The objective of this study was to investigate the significance of inner and outer phase pressure, as well as interfacial film strength on W/O/W multiple emulsion stability using microscopy and long-term stability tests. It was observed that immediately upon applying a coverslip to samples the multiple droplets deformed and there was coalescence of the inner aqueous droplets. Under certain conditions (such as lipophilic surfactant concentration and internal phase osmotic pressure) the destabilized multiple emulsions formed unique metastable structures that had a "dimpled" appearance. The formation of these metastable structures correlated with the real-time instability of the W/O/W multiple emulsions investigated. Multiple emulsion stability also correlated with the interfacial film strength (measured by interfacial elasticity) of the hydrophobic surfactant at the mineral oil/external continuous aqueous phase interface. The formation of the metastable dimpled structures and the long-term stability of the multiple emulsions were dependent on the osmotic pressure of the inner droplets and the Laplace curvature pressure as described by the Walstra Equation (P. Walstra, "Encyclopedia of Emulsion Technology" (P. Becher, Ed.), Vol. 4. Dekker, New York, 1996). It appears that the effect of coverslip pressure on multiple emulsions may be useful as an accelerated stability testing method or for initial formulation screening.     

Dynamic and static interactions between bitumen droplets in water

In the commercial bitumen extraction operation, dynamic and static interaction forces between bitumen drops in water determine the likelihood of desirable bitumen coalescence at different process stages. These dynamic and static forces were measured using colloidal particle scattering and hydrodynamic force balance techniques, respectively. In the former technique, dynamic interactions are studied through droplet-droplet collision trajectory measurement. In the latter technique, the static attractive forces between droplets are determined when a doublet is separated with a known and adjustable hydrodynamic force. The dynamic force measurement implies the presence of rigid chains on bitumen surfaces. The mean chain lengths for deasphalted bitumen at pH 7, whole bitumen at pH 7, and whole bitumen at pH 8.5 are 50, 78, and 41 nm, respectively. However, the static force measurement indicates much shorter mean chain lengths (<9 nm) in these three bitumen systems. Shorter chain length indicates weaker repulsive force. This finding of a much weaker repulsion between bitumen droplets under static conditions has important implications on the commercial bitumen extraction operation.     

Measurement of mobility of adsorbed colloids by lateral force microscopy

The surface mobility of colloidal latex particles adsorbed on mica was measured by moving the particles with an AFM tip in the lateral force microscopy mode. The same particle was repeatedly scanned while the normal force was gradually increased, until the particle was displaced from its location on the substrate. The lateral (friction) force curve obtained for that scan was then used to determine the force needed to displace the particle. The data accumulated for approximately 100 particles indicate a wide distribution in the lateral force required. However, the data show that the mean lateral force is proportional to the particle diameter, with the effect of electrostatic interactions on the mobility of adsorbed particles seen to be weak. These results are consistent with classical theories of friction in macroscopic systems.     

有机HTDIOO分子LB膜结构的AFM研究

利用原子力显微镜（ＡＦＭ）对有机分子ＨＴＤＩＯＯ单层和多层ＬＢ膜结构进行了观察。实验结果表明，针尖与ＬＢ膜表面分子间的相互作用力会对成像的膜结构有影响。当悬臂针尖与ＬＢ膜表面分子的相互作用力较大时，针尖会扰动ＨＴＤＩＯＯ分子在单层ＬＢ膜中的有序排列。ＨＴＤＩＯＯ单层ＬＢ膜具有有序结构；而在多层ＬＢ膜中，ＨＴＤＩＯＯ分子则聚集在一起形成了一定的畴结构。     

Investigation of Calcium Carbonate Scaling Inhibition and Scale Morphology by AFM

The calcium carbonate scale inhibition by two inhibitors, polyacrylic acid (PAA) and 2-phosphonobutane-1,2,4-tricarboxylic acid (PBTCA), has been studied in two heat transfer systems: recirculating cooling water and pool boiling systems. It is found that PBTCA has a better inhibition effect than PAA under identical conditions. The inhibition effect increases with increasing fluid velocity for the cooling water system, whereas in the presence of inhibitors, the fluid velocity has less effect on the scaling behavior. When the initial surface temperature increases, the inhibition efficiency decreases. In the presence of inhibitors, the scaling behavior is insensitive to the change of surface temperature. The relationship between the inhibition effect and the fractal dimension has also been investigated. The results show that the fractal dimension is higher in the presence of inhibitors. The better the inhibition effect, the higher the fractal dimension. XRD and FTIR analyses demonstrate that for the CaCO₃ formed in the pool boiling system, the content of vaterite increases with the increase of inhibition effects. The metastable crystal forms of vaterite and aragonite are stabilized kinetically in the presence of inhibitors. The step morphology has been observed by atomic force microscopy. It is shown that the step space on the CaCO₃ surface increases in the presence of inhibitors. Moreover, with the increase in inhibition effect, both the step space and the fractal dimension increase. Step bunching is also found and discussed in this paper.     

Genetic Algorithm Approach to the Determination of Particle Size Distributions from Static Light-Scattering Data

The application of genetic algorithms to the inversion of static light-scattering (SLS) measurements is investigated. The approach is illustrated using simulated data on samples with unimodal, bimodal, and trimodal distributions of spherical particles. Particles having diameters in the range from 100 to 4000 nm are treated. Results are compared with other inversion procedures. It is found that genetic algorithms yield very good results in this situation.     

壳核型磁性纳米纤维素微球的超声制备及表征

A kind of cellulose magnetic nanoparticle with a core / shell structure has been prepared by ultrasonic irradiation. Cellulose acts as the shell while Fe3O4 magnetic nanoparticles take the role as the core. Magnetic force microscopy（MFM）with atomic force microscopy（AFM）measurement showed that the size of the magnetic nanoparticles is about 30-50 nm in diameter,while the Fe3O4 core is about 20-30 nm. FT-IR,XRD and MFM was used to provide the chemical and magnetic information of the nanoparticles. The MFM image showed that the nanoparticles separate very well with each other,indicating the cellulose shell produces a good prevention from the aggregation of the Fe3O4 particles. MFM studies also showed two magnetic nanoparticles can form particle-pairs,indicating a weak magneto-dipole interaction between magnetic nanoparticles. It is also found that the average sizes of magnetic nanoparticles have relation to the power of ultrasonic irradiation,and the possible mechanism is discussed.