Porous/magnetic molecularly imprinted polymers (PM‐MIPs) were prepared by Pickering emulsion polymerization. The reaction was carried out in an oil/water emulsion using magnetic halloysite nanotubes as the stabilizer instead of a toxic surfactant. In the oil phase, the imprinting process was conducted by radical polymerization of functional and cross‐linked monomers, and porogen chloroform generated steam under the high reaction temperature, which resulted in some pores decorated with easily accessible molecular binding sites within the as‐made PM‐MIPs. The characterization demonstrated that the PM‐MIPs were porous and magnetic inorganic–polymer composite microparticles with magnetic sensitivity (Ms = 0.7448 emu/g), thermal stability (below 473 K) and magnetic stability (over the pH range of 2.0–8.0). The PM‐MIPs were used as a sorbent for the selective binding of lambdacyhalothrin (LC) and rapidly separated under an external magnetic field. The Freundlich isotherm model gave a good fit to the experimental data. The adsorption kinetics of the PM‐MIPs was well described by pseudo‐second‐order kinetics, indicating that the chemical process could be the rate‐limiting step in the adsorption of LC. The selective recognition experiments exhibited the outstanding selective adsorption effect of the PM‐MIPs for target LC. Moreover, the PM‐MIPs regeneration without significant loss in adsorption capacity was demonstrated by at least four repeated cycles. 相似文献
Molecularly imprinted polymer (MIP) films of melamine were prepared by photopolymerization of vinylic monomers on diazonium‐modified gold electrodes. The gold‐grafted MIPs are specific and selective for melamine in either organic or aqueous media. The interferent molecules cyromazine and cyanuric acid were not recognized by the MIPs. The limit of detection was as low as 1.75×10?12 mol L?1 at S/N=3. Efficiency of melamine rebinding is related to the solubility parameter of the organic solvent or pH and ionic strength of the aqueous medium. It is concluded that diazonium salts permit to design robust electrochemical MIP sensors. 相似文献
Ibuprofen and ketoprofen are chemically similar non‐steroidal anti‐inflammatory drugs widely used in the treatment of arthritis. Using a molecular imprinting technique, a simple and rapid method was developed for the simultaneous separation and determination of ibuprofen and ketoprofen. Molecular imprinting introduces artificial binding sites into a synthetic polymer matrix, allowing it to exhibit selective rebinding of template molecules. Imprinted polymers can be regarded as an HPLC stationary phase, important for pharmaceutical analysis. Most molecularly imprinted polymers (MIPs) are synthesized by free radical polymerization of functional monomers, resulting in an excess of crosslinking monomers. In this study, MIPs have been prepared with a ibuprofen template, which can form intramolecular hydrogen bonds. Methacrylic acid (MAA) and ethyleneglycol dimethacrylate (EGDMA) were used as the functional monomer and cross‐linker, respectively. Bulk polymerization was carried out at 4 °C under UV radiation. The resulting MIP was ground into 25?44 μm particles, which were slurry‐packed into analytical columns. Template molecules were removed by methanol‐acetic acid (9:1, v/v). We evaluated the template binding performance of the MIP using HPLC, with ultraviolet (UV) detection at 234 nm. Chromatographic resolution of ibuprofen and ketoprofen on the MIPs were appraised using buffer/acetonitrile (45/55, v/v) as the mobile phase. Results show that the MIPs prepared using ibuprofen as the template had a significant molecular imprinting effect. The method was successfully applied to the separation and analysis of ibuprofen and ketoprofen in pharmaceuticals. 相似文献
Development of photocatalysts (PCs) with diverse properties has been essential in the advancement of organocatalyzed atom transfer radical polymerization (O‐ATRP). Dimethyl dihydroacridines are presented here as a new family of organic PCs, for the first time enabling controlled polymerization of challenging acrylate monomers by O‐ATRP. Structure–property relationships for seven PCs are established, demonstrating tunable photochemical and electrochemical properties, and accessing a strongly oxidizing 2PC.+ intermediate for efficient deactivation. In O‐ATRP, the combination of PC, implementation of continuous‐flow reactors, and promotion of deactivation through addition of LiBr are critical to producing well‐defined acrylate polymers with dispersities as low as 1.12. The utility of this approach is established through demonstration of the oxygen‐tolerance of the system and application to diverse acrylate monomers, including the synthesis of well‐defined di‐ and triblock copolymers. 相似文献
The organocatalyzed photo‐atom transfer radical polymerization (photoATRP) using 10‐phenylphenothiazine as catalyst is studied toward its use in methacrylic acid (MAA) polymerization and surface grafting. The organocatalyzed photoATRP of methyl methacrylate (MMA) is first optimized for continuous flow synthesis in order to assess the livingness of the polymerization. MMA can be polymerized in batch and in flow; however, conversions are limited by the loss of bromine functionality and hence high conversions have to be traded in with increasing dispersities. Also, MAA is polymerized successfully in continuous flow with similar limitations. Flow conditions are transferred to surface grafting from silanized silicon wafers. The presence of ATRP initiators after silanization is confirmed by secondary ion mass spectrometry and X‐ray photoelectron spectroscopy. Dense polymethacrylic acid brush films are successfully produced, which is not directly accessible via classical copper‐mediated ATRP techniques. 相似文献
A key issue in the synthesis of molecularly imprinted polymers (MIPs) is the identification and optimisation of the main factors that affect the material structure and its molecular recognition properties. This paper describes the application of an experimental design and multivariate analysis method for the synthesis of bisphenol A (BPA)-selective MIPs. Six factors with a large impact on the MIP synthesis and its analytical performance have been optimised: the amount of template, the type and the percentage of functional and cross-linking monomers, the polymerisation method (i.e. thermal or UV initiation) and the porogenic solvent. The polymers have been prepared in small-scale (mini-MIPs) and, after careful removal of the template, their BPA rebinding capacity has been evaluated and related to the MIP composition. Among the two functional monomers tested, namely 4-vinylpyridine (4-vpy) and methacrylic acid (MAA), the former rendered the best selectivity for BPA analysis. The partial least squares (PLS) models revealed that the photoinitiated polymers with a 1:1 ratio of 4-vinylpyridine to cross-linker (EDMA or TRIM) yield the highest specific binding. Such procedure is time and cost effective and can be used as a general tool in the preparation of MIPs for different analytes. 相似文献
A one‐pot procedure for the synthesis of hyperbranched polyethylenes tethered with ATRP initiating sites by chain walking ethylene copolymerization with an acrylate‐type ATRP inimer, 2‐(2‐bromoisobutyryloxy) ethyl acrylate (BIEA) is reported. Because of its ability to incorporate acrylate‐type comonomers and tolerance toward the α‐bromoester group, the chain walking Pd‐diimine catalyst, [(ArNC(Me) (Me)CNAr)Pd(CH3)(NCMe)]SbF6 (Ar = 2,6‐(iPr)2C6H3), allowed the successful synthesis of a series of hyperbranched copolymers tethered with 2‐bromoisobutyryl groups at different densities. These copolymers may serve as polyfunctional macroinitiators for the ATRP of functional monomers to further synthesize core‐shell structured functionalized copolymers with a hyperbranched polyethylene core grafted with side chains of the functional monomers.
How to simply and efficiently separate and recycle catalyst has still been a constraint for the wide application of atom transfer radical polymerization (ATRP), especially for the polymerization systems with hydrophilic monomers because the polar functional groups may coordinate with transition metal salts, resulting in abundant catalyst residual in the resultant water‐soluble polymers. In order to overcome this problem, a latent‐biphasic system is developed, which can be successfully used for ATRP catalyst separation and recycling in situ for various kinds of hydrophilic monomers for the first time, such as poly(ethylene glycol) monomethyl ether methacrylate (PEGMA), 2‐hydroxyethyl methacrylate (HEMA), 2‐(dimethylamino)ethyl methacrylate (DMAEMA), N,N‐dimethyl acrylamide (DMA), and N‐isopropylacrylamide (NIPAM). Herein, random copolymer of octadecyl acrylate (OA), MA‐Ln (2‐(bis(pyridin‐2‐ylmethyl)amino)ethyl acrylate), and POA‐ran‐P(MA‐Ln) is designed as the macroligand, and heptane/ethanol is selected as the biphasic solvent. Copper(II) bromide (CuBr2) is employed as the catalyst, PEG‐bound 2‐bromo‐2‐methylpropanoate (PEG350‐Br) as the water‐soluble ATRP initiator and 2,2′‐azobis(isobutyronitrile) (AIBN) as the azo‐initiator to establish an ICAR (initiators for continuous activator regeneration) ATRP system. Importantly, well‐defined water‐soluble polymers are obtained even though the recyclable catalyst is used for sixth times.
The novel hydrophobic coating material was received for the first time by a two‐step synthetic route. Firstly, the 15‐functional brominated macroinitiator was prepared by the esterification methodology. Next step covers synthesis of star‐like polymers by poly(n‐butyl acrylate) (PBA) arms polymerization via three low‐ppm atom transfer radical polymerization (ATRP) approaches including application of copper and silver wire in SARA and ARGET ATRP, respectively, as driving forces in redox cycle of catalyst, and an external stimulus in the form of electric current (seATRP) as the third approach in copper(II) regeneration system. As expected, the electrochemically mediated technique allows synthesis of tannic acid‐inspired coating polymers in precisely controlled manner during the entire polymerization process, proved by linear first‐order kinetics plot in contrast to above‐mentioned methods, low dispersity (Ð = 1.18) of star‐shaped polymers, and high efficiency of initiation (?i = 81%) determined after detaching of polymers side arms. Macromolecules received by all low‐ppm ATRP solutions were characterized by preserved chain‐end functionality (theoretical dead chain fraction; DCFtheo <1%). Adhesive and hydrophobic properties of received polymer materials were investigated by contact angles (θ) and free surface energy (FSE) calculations. Prepared polymer films besides excellent hydrophobic properties have great potential as a self‐healing solution. 相似文献
Low molecular weight linear poly(methyl acrylate), star and hyperbranched polymers were synthesized using atom transfer radical polymerization (ATRP) and end‐functionalized using radical addition reactions. By adding allyltri‐n‐butylstannane at the end of the polymerization of poly(methyl acrylate), the polymer was terminated by allyl groups. When at high conversions of the acrylate monomer, allyl alcohol or 1,2‐epoxy‐5‐hexene, monomers which are not polymerizable by ATRP, were added, alcohol and epoxy functionalities respectively were incorporated at the polymer chain end. Functionalization by radical addition reactions was demonstrated to be applicable to multi‐functional polymers such as hyperbranched and star polymers. 相似文献
A promising strategy for the controlled synthesis of inorganic/polymeric nanocomposites may be sustained by fabricating cross-linked PbS nanoparticles/polymer composite thin films through combining surface-initiated atom transfer radical polymerization (ATRP) and gas/solid reaction. The introduction of Pb ions through the extension of surface-initiated ATRP to the monomers containing metal ions provides an opportunity for generating nanoparticles on the substrate. 相似文献