多壁碳纳米管的制备及改性处理

用自制的镍 硅二元气凝胶作催化剂,合成了多壁碳纳米管.甲烷在680℃催化裂解120min,再升温至800℃继续裂解20min,得到多壁碳纳米管.TEM、HRTEM和Raman光谱分析表明,所得多壁碳纳米管与高定向石墨具有相似的层状结构,其管径分布均匀,约15～30nm左右,长径比大,管端封闭,并含有金属催化剂粒子;采用不同方法改性处理,发现经过稀硝酸浸泡和空气氧化处理后,能去除碳管中金属催化剂,同时碳纳米管管长变短,端帽开口,能有效利用内表面,比表面积增大.     

不同结构碳纳米管的电磁波吸收性能研究

研究了单壁、多壁碳纳米管(聚团状、阵列状)以及未纯化与纯化后碳纳米管在2～18 GHz范围内的电磁波吸收性能. 通过测定不同结构碳纳米管粉体的介电常数以及磁导率, 得到损耗因子及衰减常数大小顺序为: 阵列状多壁碳纳米管>原生聚团状多壁碳纳米管>纯化聚团状多壁碳纳米管>原生单壁碳纳米管>纯化后单壁碳纳米管. 相比多壁碳纳米管, 单壁碳纳米管衰减常数随频率变化较小, 且具有较宽的吸收峰. 模拟计算和实验测试结果都表明, 碳纳米管/聚合物复合材料具有优良的电磁吸波性能.     

焙烧法纯化多壁碳纳米管

自碳纳米管[1 ] 发现以来 ,已在世界范围内掀起了碳纳米管研究和应用的热潮 .其中一些文献报道了纯化单壁碳纳米管的方法 ,如超声波助滤法 [2 ] ,酸洗法 [3,4] ,微孔膜过滤法 [5,6] ,离心法[5] ,氧化法[5,7] ;另有少量文献报道了纯化多壁碳纳米管的方法 ,如氧化法 [5,8] ,石墨插层化合物纯化法 [9] 等 .本文使用焙烧法纯化实验室自制的多壁碳纳米管 .通过 TEM、XRD和比表面积等的测定 ,考察了不同焙烧时间的纯化效果 .采用催化甲烷裂解方法 ,在 6 0 0℃反应 4h制得多壁碳纳米管 ,粗产物收率接近 2 0 % .于干燥、洁净的坩埚中 ,分别称取 6…     

Ni/MWCNT及镧改性Ni/MWCNT催化CO2甲烷化反应的性能

以多壁碳纳米管(MWCNT)为载体, 通过浸渍法制备了负载型镍催化剂和稀土镧改性的镍催化剂, 并对其二氧化碳甲烷化的催化性能进行了研究. 借助比表面积测试、程序升温还原(TPR)、X射线衍射(XRD)和X射线光电子能谱(XPS)等表征手段研究了稀土镧的添加对Ni/MWCNT催化剂结构和表面组成、催化剂还原性能以及CO₂甲烷化反应性能的影响. 结果表明: 稀土镧改性的Ni/MWCNT较Ni/MWCNT催化剂具有更好的CO₂甲烷化活性, 镧组分的加入提高了催化剂表面的镍物种浓度和分散度, 弱化了氧化镍与载体MWCNT之间的相互作用, 促进了氧化镍的还原, 同时提高了表面镍物种的电子密度, 增加了对反应物的吸附能力, 从而提高了其CO₂甲烷化活性. 制备过程中稀土镧的添加次序对催化性能有较明显的影响, 其活性顺序为先浸渍镧后浸渍镍制备的催化剂活性明显好于先浸渍镍后浸渍镧制备的催化剂.     

催化裂解CH4制备不同形貌的碳纳米管

通过甲烷于较低温度(500～700℃)下在镍催化剂上催化裂解制备了各种形貌的碳纳米管.透射电镜测试结果表明,碳纳米管的外径和内径明显地受催化剂的大小和形貌的影响.本文考察了催化剂前驱体的种类、反应温度和原料气流速对镍催化剂和碳纳米管形貌的影响.     

多巴胺为前驱体过渡金属与N共同掺杂的碳纳米管催化剂ORR性能研究

采用多巴胺的自氧化聚合在多壁碳纳米管表面进行聚合沉积修饰,经热处理可得到氮掺杂的碳纳米管催化剂,通过调整沉积次数可控制表面聚多巴胺C-N膜的厚度,从而调控N的掺杂量.研究沉积次数对多壁碳纳米管催化剂表面形貌、化学组成及原子结合形态的影响,并考察N掺杂的多壁碳纳米管催化剂的氧还原反应活性.在此基础上,用多巴胺配合Mn、Fe离子进行共同聚合沉积,热处理后得到Mn(Fe)、N共同掺杂的多壁碳纳米管催化剂,对催化剂进行了多种测试和电化学表征.循环伏安和线性扫描的电化学表征表明,N掺杂可有效提高催化剂的氧还原反应(ORR)活性,C-N膜的厚度会影响催化剂性能,Mn(Fe)-N@MWCNTs催化剂的氧还原活性高于只有N掺杂的催化剂,两种催化剂氧还原反应均为4电子反应路径,可直接将氧气还原成H_2O,且F e-N@MWCNTs催化剂表现出较好的抗甲醇能力.SEM照片可以看到聚多巴胺在碳纳米管表面形成C-N膜;R aman分析表明聚多巴胺沉积后提高了催化剂表面的无序性,缺陷增多;XPS表征显示过渡金属的掺杂改变了CN_x的结合状态.     

碳纳米管负载金属卟啉电催化剂制备及其催化活性

采用微波合成法制备了多壁碳纳米管负载钴卟啉(CoTMPP/MWNT)电催化剂,利用透射电子显微镜对催化剂微观结构进行了表征,并通过旋转圆盘和旋转环盘技术对电催化剂的氧还原活性进行了评价.结果表明,与有机回流合成法制备的催化剂相比,微波法合成的CoTMPP/MWNT催化剂具有更好的氧还原性能,半波电位正向移动110mV;与多孔碳为载体的CoTMPP/BP2000催化剂相比,多壁碳纳米管为载体的CoTMPP/MWNT电催化剂的起始电位高10mV,还原电流损失低21%,表现出更好的氧还原活性和稳定性.在CoTMPP/MWNT电催化剂表面进行的氧还原过程中电子转移数为3·6,H2O2生成量为18%.MWNT独特的电子特性、强抗腐蚀能力及其与活性钴离子之间的相互作用有助于改善催化剂的氧化还原性能.     

合成甲醇的催化剂Rh-ZnO/MWNTs的研究

研究新型的由多壁碳纳米管(MWNTs)负载的， ZnO助催的铑基甲醇合成催化剂. 当铑含量达到4％(w)时，催化剂具有较高的比表面积(99.6 m2•g－1), 催化剂的反应活化能为68.8 kJ•mol－1.在563 K, 1 MPa下，催化剂的最高催化活性和甲醇选择性分别为411.4 mg/gcat.•h和96.7％. TEM、TPR和TPD等表征结果显示，碳纳米管能增加Rh在催化剂表面的分散度，提高催化剂的还原温度并能增加氢物种的吸附量，这些结果将有助于更好地了解催化剂中各组分间的协同作用和催化活性中心本质.     

多壁碳纳米管修饰玻碳电极测定乙炔雌二醇

多壁碳纳米管修饰玻碳电极测定乙炔雌二醇;多壁碳纳米管;乙炔雌二醇;化学修饰电极;电化学测定     

改性多壁碳纳米管/聚乳酸复合材料的研究

制备了改性多壁碳纳米管/聚乳酸复合材料,研究了改性多壁碳纳米管对聚乳酸的增强作用.通过拉曼光谱分析、热重分析证实了多壁碳纳米管酸化酯化反应的发生.通过溶液法制备了聚乳酸/改性多壁碳纳米管复合物.考察了聚乳酸和改性多壁碳纳米管复合体系的相容性.扫描电镜分析结果说明了聚乳酸和改性多壁碳纳米管复合物相容性的变化.随着改性多壁碳纳米管在复合物中含量的增加,体系的分散效果也越好,相容性也有提高.实验结果表明,在聚乳酸材料中添加改性碳纳米管材料到一定值对,可以提高材料的力学性能,且当改性碳纳米管添加量达到1.5％的时候材料力学性能达到了一个最大值,拉伸强度可达120.4MPa.     

Dichroism of absorption and polarization of phosphorescence of molecules of the closed form of nitrobenzospirothiopyran

The spectral-polarization characteristics of absorption and phosphorescence of molecules of the initial form of nitro-substituted indolinospirobenzothiopyran were studied in oriented polyethylene films and in solutions with different polarity. An oscillator model of the electron transitions responsible for the formation of absorption and luminescence spectra was suggested. It was established that the principal differences in the spectral and photophysical properties of the compound studied and its oxygen-containing analog are associated with the fact that the electronegativity of the S atom is lower than that of the O atom. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 6, pp. 1143–1146, June, 1997.     

非那雄胺合成工艺改进

非那雄胺能抑制5α-还原酶的活性,明显降低二氢睾酮水平,是一种治疗良性前列腺增生的有效药品。该合成工艺以甾烯酮酸为原料,将其与氯化亚砜反应,无须分离即与叔丁胺反应得17β-酰胺化合物,再氧化开环,环合,氢化,脱氢合成了非那雄胺。经元素分析、IR、1HNMR、13CNMR、MS分析表征了其结构。该法无须使用昂贵的2,2-二吡啶二硫化物和剧毒药品苯亚硒酸酐,且以乙酸铵代替氨气,降低了对设备的要求和腐蚀,更适用于工业生产。     

Determination of heats of detonation and influence of components of composite explosives on heats of detonation of high explosives

The heats of detonation of 20 simple high explosives and explosive mixtures were determined by means of an adiabatic detonation calorimeter designed by the authors. The results indicated that the performance of the instrument was reliable and the experimental data were very accurate. For explosive mixtures, there was a linear accumulative relationship between the heats of detonation of the explosive mixture and its components. Accordingly, the heats of detonation of explosive mixtures could be calculated directly from the heats of detonation of simple explosives and the characteristic heats of other components. The experiments showed that the gold or brass shell of the cylindrical charge could be substituted by a thick-walled porcelain shell, which had the advantage of cheapness.

     

Synthesis of phenolic components of Grains of Paradise

Two vanilloids, (5E)-8-(4-hydroxy-3-methoxyphenyl)oct-5-en-4-one (1) and 4-[3-hydroxydecyl]-2-methoxyphenol (2), isolated from the dried seeds of Grains of Paradise (Aframomum melegueta), were synthesized; the latter compound was made as the S-enantiomer and the material derived from the seeds was found to be a 1:1.7 mixture of the R and S isomers. The synthetic route used should allow the preparation of analogs having extended alkyl chains and consequently different lipophilicity, and 3, a homolog of 2, was also prepared.     

Summary of development of the theory of stability of colloids and thin films

In this review, the research of the author in the field of colloidal systems is summarized. The factors influencing colloidal stability are systematized and analyzed. Examples are presented to illustrate the practical utilization of the theory of stability of colloids and thin films.This review was prepared on the basis of the works of the author, which were awarded the State Premium for 1991 in the field of science and technology, chemistry section.Institute of Physical Chemistry, Russian Academy of Sciences, 117915 Moscow. Translated from Izvestiya Akademii Nauk, Seriya Khimicheskaya, No. 8, pp. 1708–1717, August, 1992.     

Study of hydration of two cements of different strengths

Main hydration products of two cement pastes, i.e. CSH-gel, portlandite (P) (and specific surface S) were studied by static heating, and by SEM, TEM and XRD, as a function of cement strength (C-33 and C-43) hydration time (th) and subsequent hydration in water vapour.Total change in mass on hydration and air drying, M_o, increased with strength of cement paste and with hydration time. Content of water escaping at 110 to 220°C, defined as water bound with low energy, mainly interlayer and hydrate water, was independent on cement strength but its content increased with (th). Content of chemically bound (zeolitic) water in CSH-gel, escaping at 220-400°C, was slightly dependent on strength and increased with (th). It was possibly derived from the dehydroxylation of CSH-gel and AFm phase. Portlandite water, escaping at 400-500°C, was independent on cement strength and was higher on longer hydration. Large P crystals were formed in the weaker cement paste C-33. Smaller crystals were formed in C-43 but they increased with (th). Carbonate formated on contact with air (calcite, vaterite and aragonite), decomposed in cement at 600-700^oC. It was high in pastes C-33(1 month) and C-43(1 month), i.e. 5.7 and 3.3%, respectively; it was less than 1% after 6 hydration months (low sensitivity to carbonation) in agreement with the XRD study showing carbonates in the air dry paste (1month), and its absence on prolonged hydration (6 months) and on acetone treatment. Water vapour treatment of (6 months) pastes or wetting-drying increased this sensitivity.Nanosized P-crystals, detected by TEM, could contribute to the cement strength; carbonate was observed on the rims of gel clusters.This revised version was published online in November 2005 with corrections to the Cover Date.     

氯氧化镁生成热的研究

用氧化镁氯化镁水溶液制备了8水合氯氧化镁[nMg(OH)2·MgCl2·8H2O], 并测定了其在盐酸中的溶解热, 实验结果表明, 氯氧化镁溶解热与n值呈线性关系, 根据溶解热求出5Mg(OH)2·MgCl2·8H2O和3Mg(OH)2·MgCl2·8H2O的生成热分别为-7727.1和5888.1kJ·mol^1^-。     

Thermodynamics of the formation of oxosulfides of rare-earth elements

The enthalpies of solution of several oxosulfides of rare-earth elements and the high-temperature enthalpies of oxosulfides and oxosulfates of lanthanum and yttrium were measured using solution calorimetry and high-temperature microcalorimetry techniques. Standard enthalpies of formation and some thermodynamic properties of oxosulfides and oxosulfates were calculated. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 2 pp. 294–297, February, 1997.     

恶臭嗅辨实验室建设探讨

针对恶臭测试的环境影响问题,提出了解决的实例方案,并对方案的要点及优缺点进行讨论,此方案在实际操作中具有较好的效果。