基于金属钴配合物的均相光催化还原二氧化碳研究进展

本文综述了自20世纪80年代以来基于钴配合物的均相光催化二氧化碳还原研究成果,以钴配合物催化剂的结构分类并结合时间顺序回顾了近四十年来该领域的发展轨迹,重点总结了用于光催化二氧化碳还原研究的金属钴配合物的结构、催化活性以及光催化体系的构成等特点,分析了该领域面临的挑战并展望了未来的发展方向。     

钴(Ⅱ)基分子配合物用于光催化二氧化碳还原

Nowadays, more than 85% of the energy is generated by fossil fuels. The excessive utilization of finite fossil fuels has resulted in the crises of energy shortage and global warming caused by greenhouse gas emissions. Researchers have conceived several means for trying to solve these problems, among which the sunlight-driven CO₂ reduction is viewed as a sustainable process that utilizes CO₂ as the raw material to produce chemical fuels, including CO, formate, and CH₄; this method not only realizes the conversion and storage of intermittent solar energy, but also decreases the CO₂ concentration in the atmosphere and alleviates global warming. However, photochemical CO₂ reduction usually undergoes a sluggish process due to the inertness of CO₂. Moreover, the selectivity of the CO₂ reduction reaction is also challenged by the hydrogen evolution reaction, which exhibits faster reaction kinetics. In this context, the rational design and synthesis of efficient and selective catalysts for photochemical CO₂ reduction are major challenges.     

手性双提蓝钴卟啉配合物催化二氧化碳对环氧的不对称环加成（英文）

绿色化学是当今化学科学研究的前沿领域.仿生催化是绿色合成技术和方法学研究的一个重要方面.生物质和酶分子在酶催化转化过程中的"构-效"关系可以通过仿生催化进行模拟研究.CO_2作为温室气体的主要成分是造成全球气候变暖的主要因素,但它同时也是C1化学的重要原料.利用CO_2与有机环氧化合物通过偶联反应制备有机环碳酸酯或聚碳酸酯则是CO_2化学研究的热点之一,并已经取得了长足的进步.但是运用手性催化剂对此反应进行不对称环加成得到手性环碳酸酯的研究不多.本文首次设计并合成了具有双提篮结构的手性钴卟啉螯合物.其中的提篮部分由手性联萘酚(S或R)和L-苯丙氨酸组成,从卟啉骨架的meso位引入,首先制备了两种手性结构的自由卟啉配体(6a,7a);然后与醋酸钴反应得到两种二价钴卟啉手性配合物(6b,7b),加入醋酸后,通过空气氧化得到三价钴卟啉手性催化剂(6c,7c).采用紫外、红外光谱、质谱和核磁共振(包括二维NMR)等技术对得到的卟啉中间化合物、配合物和催化剂进行了详细的表征,确定了化合物的结构.将得到的三价钴卟啉配合物作为手性催化剂用于CO_2和环氧化合物的不对称环加成反应.结果表明,提篮的手性基团对小分子的环氧化合物环氧丙烷具有手性选择性,在低温-20°C下,可以得到大于50%的ee值.同时由于提篮与卟啉平面空间的有限性,导致分子体积较大的环氧化合物与CO_2的反应很慢,也没有发现其对环碳酸酯的对映选择性.我们相信本工作对于合成手性卟啉分子及其在不对称催化中的应用具有一定的意义.     

高效二氧化碳电催化还原反应花状钴催化剂的制备及性能（英文）

随着工业的不断发展,化石燃料的大量使用导致全球大气二氧化碳浓度逐年升高.通过电还原将二氧化碳转化为燃料是实现碳循环经济最有前景的途径之一.目前,还原二氧化碳常用的方法包括热化学法,光化学法和电化学法.与另外两种方法相比,电催化还原二氧化碳具有条件简便,易于控制,转化率较高,材料易得,易于放大生产等优点,具备潜在的实际应用价值.电还原二氧化碳的催化材料主要分为金属材料,金属氧化物,有机分子,生物分子等.其中,以过渡金属催化剂的研究与应用最为普遍.我们发展了一种新型金属钴催化剂的制备方法,采用快捷,绿色的溶剂热方法,以正丁胺为保护剂,合成了具有花状形貌的金属钴催化剂.这种特殊形貌的金属钴催化剂相比体相的金属钴催化剂与层状的氢氧化钴材料,能够暴露更多的活性位点,在二氧化碳电还原反应中表现出极高的催化活性与选择性.我们采用循环伏安法和线性扫描伏安法(LSV)等电化学表征手段,进一步证明了先前其他课题组已报道过的通过溶剂热法制备得到的钴/钴氧化物二维材料在二氧化碳电催化还原过程中,金属钴/氧化钴界面的存在对二氧化碳还原反应具有决定性作用的观点.X射线衍射表明这种新型金属钴催化剂具有六方密堆积的晶体相,晶粒平均直径为17.3 nm.扫描电子显微镜直观地展示了其不同于体相的金属钴催化剂与层状的氢氧化钴材料,具有特殊的形貌.电化学表征结果显示花状金属钴催化剂比另外两种材料具有更正的起始电位(-0.7 V vs.SCE).不同扫描速度LSV研究表明,甲酸等其他还原产物的形成受二氧化碳传质控制影响.采用核磁共振分析不同电位下10 h恒电位电解产物,发现当电极电势为-0.85 V(vs.SCE)时,还原产物甲酸的法拉第效率达63.4%.另外,循环伏安曲线表明该催化剂不仅对二氧化碳还原反应具有极高的活性,同时,对还原产物的氧化也表现出极低的过电位与极高的反应活性,因此所开发催化剂可视为一类双效电催化剂.     

“一体化”共价有机框架光催化二氧化碳还原研究（英文）

自工业革命以来,温室气体CO₂大量排放使得环境问题日益突出,严重制约了人类的生存和发展.人工光合作用可利用取之不尽的阳光作为驱动力,将CO₂还原为可实际应用的化学燃料(CO、HCOOH等).人工光合作用体系通常包括两部分:光敏剂和催化剂.光敏剂吸收入射光的能量,电子由基态(价带)跃迁至激发态(导带);处于激发态的光敏剂将电子转移到催化剂上;最终由催化剂实现CO₂还原.对光敏剂和催化剂进行合理的调变可以构建更加高效、稳定的人工光合作用体系.共价有机框架(COFs)材料是由轻元素(C, H, O, N, B等)组成的有机小分子构筑单元通过动态共价键组装,所形成的具有预先设计的拓扑结构的一维、二维或三维的晶态有机多孔骨架材料.自从2005年首次报道COFs材料的成功合成以来,COFs逐渐地发展成为了一种具有高潜力和广泛的功能化应用前景的多孔骨架聚合物.特别是二维共价有机框架(2D-COFs).2D-COFs独特的平面扩展共轭π-π结构,使其具有较好的光吸收性能,轴向的π堆叠结构,有利于光生电荷的分离和转移, 2D-COFs材料...     

钴(Ⅱ)配合物与卟啉在超临界二氧化碳中的反应动力学研究

用紫外-可见光谱研究了1,1,1,5,5,5-六氟-2,4-戊二酮-钴(Ⅱ)二水[Co(hfac)2(H2O)2]与5,10,15,20-四(五氟苯基)卟啉(H2tpfpp)在超临界二氧化碳中反应生成钴卟啉[Co(tpfpp)]的反应动力学.在钴(II)配合物大大过量时,此反应对卟啉为一级,且其表观一级速率常数随钴(Ⅱ)配合物的浓度增加先增加、而后趋于稳定.根据实验事实,讨论了此反应的机理,得到了相应的热力学和动力学参数.     

钴基非均相催化剂在光催化水分解、二氧化碳还原和氮还原的研究进展与展望（英文）

利用大自然丰富的太阳能驱动水、二氧化碳或氮气转化为高附加值燃料(如H₂, CO, CH₄, CH₃OH或NH₃等),实现人工光合成,将储量丰富的太阳能转化为可利用的清洁化学能源,被认为是解决能源短缺和环境问题的关键技术之一,能够有效缓解能源危机和全球变暖,极具应用前景.因此,各种类型的光催化剂相继被开发出来,以满足光催化的需求.其中钴基多相催化剂是最有前途的光催化剂之一,它可以通过扩大光吸收范围、促进电荷分离、提供活性位点和降低反应能垒等途径有效提高光催化效率,为太阳能燃料转化利用开辟广阔的前景.本文首先介绍了光催化水分解、CO₂还原和N₂还原的基本原理.然后,总结了基于钴基催化剂的改性策略,包括形貌、晶面、结晶度、掺杂和表面修饰,重点讨论了钴基多相材料在水分解(产氢、产氧和全解水)、二氧化碳还原以及氮还原领域的光催化进展.最后,对钴基光催化剂当前面临的挑战和未来的发展作了展望和总结.提出了钴基光催化剂未来的一些研究方向.包括:(1)基于材料光催化体系的设...     

分子氧在金属配合物担载磷铝分子筛修饰玻碳电极上的电催化还原反应

采用循环伏安法研究了负载金属配合物MnSALEN(SALEN=N,N-双水杨醛缩乙二胺)的磷铝分子筛APO-5复合催化剂修饰玻碳电极在水溶液中对分子氧的还原反应的电催化行为.结果表明,氧气的还原峰电位随扫描速率的增大负移,Ep~lnv呈线性关系;其还原峰电流随扫描速率的增大而增强,ip~v1/2呈直线关系.这说明分子氧在修饰电极PS/MnSALEN/APO-5/GCE上的还原是扩散控制的.根据Ep~lnv和ip~v1/2的线性关系计算出中性电解质溶液中分子氧在此修饰电极上的还原反应的电子转移数n接近4.即氧气在此修饰电极上被还原为水.     

简便方法制备氮掺杂的碳球用作高效非金属氧还原催化剂（英文）

随着人们环保意识的不断增强,社会对清洁能源的需求也日益增加.燃料电池具有效率高,燃料来源丰富,可直接将化学能转化成电能且污染小等优点,因而受到了广泛关注.然而,燃料电池的阴极氧还原反应(ORR)速率较慢,成为提高燃料电池整体效率的制约因素.因此,开发高性能的ORR催化剂,加快ORR反应速率具有非常重要的意义.目前,Pt基催化剂被认为是活性最好的商用ORR电催化剂.尽管此类催化剂具有较高的催化活性和良好的稳定性,但Pt的储量有限,价格高昂,抗燃料毒化性能差,限制了其大规模应用.近年来,为了减小Pt的用量,降低催化剂成本,人们除了致力于研究贵金属合金催化剂及非贵金属催化剂外,还把目光聚焦在了非金属催化剂,特别是碳及其复合材料的研究上.在众多碳材料中,碳球因具有良好的表面渗透性和较高的机械稳定性而被广泛应用于催化、吸附、药物输送和能量存储及转化等领域中.然而,碳球的表面化学惰性较强,比表面积较低,使其部分应用受到了限制.因此,人们采用了多种方法来调控碳球的物理化学性质.其中,向碳材料中掺入杂原子,尤其是氮原子的方法广受青睐.因为杂原子的掺入会显著增强作为主体的碳原子给电子的能力和表面吸附性质,从而对ORR表现出优异的催化活性和稳定性.本文以蔗糖作为碳源,三聚氰胺作为氮源,采用水热法及高温热解法制备了一系列氮掺杂的生物质碳球.并对氮掺杂量及热解温度进行了优化.结果表明,石墨化程度及石墨氮含量的提高,能有效地提高催化剂的活性.在优化了的条件下得到的催化剂N0.1C1.9S-900,表现出了比商业Pt/C催化剂更好的ORR催化性能.在0.1 mol/L KOH中,该催化剂催化ORR的起始电位和半波电位分别为–22.6和–133.6 mV(vs.Ag/AgCl),极限电流密度为4.6 mA/cm~2,分别比商业Pt/C高出7.2 mV,5.9 mV和0.2 mA/cm~2.同时,在经过30000 s的稳定性测试中,N0.1C1.9S-900催化剂的电流损失也远低于Pt/C,表明该催化剂具有良好的稳定性.此外,在抗甲醇毒化实验中,相比于商业Pt/C,N0.1C1.9S-900催化剂对甲醇有更好的耐受性.另外,该催化剂催化的ORR属于高效的4e~–途径.可见,该催化剂作为燃料电池的阴极氧还原反应催化剂具有广阔的前景.     

调节氧化镉-炭黑界面高效电催化CO2还原生成CO

通过调节氧化镉与炭黑之间的界面实现了高效电化学二氧化碳还原. 不同氧化镉和炭黑含量的 CdO/CB复合材料利用超声处理方法制备. 采用X射线衍射、 X射线光电子能谱和透射电子显微镜对所得复合材料进行表征, 揭示了其结构组成和形貌. 用H型电解池对CdO/CB复合材料电催化二氧化碳还原的性能进行测试发现, CdO质量分数为20%的CdO/CB 可在-1.0 V(vs. RHE)电位下获得高达92.7%的总法拉第效率, 而纯CdO在相同条件下的法拉第效率仅为69.5%. CO的法拉第效率最高可达87.4%. 进一步的对比实验和动力学研究结果表明, CdO/CB具有更高的电催化CO₂还原性能源于复合材料中氧化镉与炭黑之间的界面和高接触面积. 此外, CdO/CB可在至少10 h的二氧化碳电还原反应中保持稳定的CO法拉第效率.     

1,2-亚苯基二硫桥[FeFe]-氢化酶模拟物选择性光催化还原CO2至CO

利用基于非贵金属的分子催化剂通过光驱动催化CO2还原生成CO是将太阳能储存为化学能和缓解CO2温室效应的有效途径之一,具有重要的科学意义和潜在的应用前景.已报道的非贵金属分子催化剂,大多数对于光驱动CO2还原表现出缓慢的催化反应速率和/或对CO产物的低选择性,反应常常伴随着质子还原产氢反应,只有很少几种非贵金属分子催化剂对光催化CO2还原生成CO表现出高催化反应速率(>100 h?1)和高选择性.研究表明,双核过渡金属配合物由于分子中邻近的两个金属中心的协同催化作用,对于CO2还原生成CO的催化活性明显高于相应的单核配合物.因此,具有两个邻近的金属离子的非贵金属双核配合物有望作为CO2选择性还原的高效分子催化剂.我们最近的研究发现,具有刚性、共轭亚苯基二硫桥结构的[FeFe]-氢化酶模拟物[(μ-bdt)Fe2(CO)6](1,bdt=苯-1,2-二巯基)能够高活性、高选择性地光化学还原CO2至CO,而与其类似的模拟物[(μ-edt)Fe2(CO)6](2,edt=乙烷-1,2-巯基)则不具有光催化还原CO2活性,表明铁铁氢化酶模拟物中硫-硫桥的结构是影响模拟物的催化性能的重要结构因素之一.可见光照射1/[Ru(bpy)3]2+/BIH(BIH=1,3-二甲基-2-苯基-2,3-二氢-1H-苯并[d]-咪唑)体系4.5 h,1催化生成CO的循环数(TON)为710,在初始1 h的转化率(TOF)为7.12 min^-1,CO的选择性达到97%,内量子效率为2.8%.有趣的是,向体系中加入TEOA时可以调节1的催化选择性,光化学反应能够在CO2还原产生CO和质子还原产生H2之间进行切换.此外,采用稳态荧光和瞬态吸收光谱研究了光催化体系中的电子转移,提出可能的光催化反应机理.该研究结果揭示了刚性硫-硫桥结构的氢化酶模拟物对光化学CO2还原至CO的特殊催化活性,拓展了铁铁氢化酶模拟物的催化多功能性.     

Electrochemical reduction of CO2 with high current density in a CO2 + methanol medium II. CO formation promoted by tetrabutylammonium cation

The cation of the supporting electrolyte was found to play an important role in the electrochemical reduction of highly concentrated CO₂ in a CO₂ + methanol medium. Electroreduction of CO₂ with tetrabutylammonium (TBA) salts yielded CO as the main product, while methyl formate was predominantly formed when lithium salts were used as supporting electrolytes. The latter supporting electrolytes showed a higher overvoltage than the former. When TBA salt was used, the reduction of CO₂ was catalysed by TBA ion to yield CO^−.₂. This intermediate may be stabilized by forming an ion pair, {TBA⁺---CO^−.₂}, or by being adsorbed on the electrode surface as CO^−._2ad. Then CO^−.₂ reacts with CO₂ to produce CO. The hydrophobic atmosphere at the electrode provided by TBA ion may be adequate for CO production. Lithium ion, on the other hand, suppressed the reduction of CO₂.     

Cloride-derived copper electrode for efficient electrochemical reduction of CO2 to ethylene

Transformation of CuCl into cubic structure of bi-phasic Cu₂O-Cu (CB-Cu) enhanced production of ethylene from electrochemical reduction of CO₂.     

A new polypyridyl-based Ru (II) complex as a highly efficient electrocatalyst for CO2 reduction

A new polypyridyl Ru (II) complex, cis-[Ru (Me₄phen)₂(CH₃CN)₂](NO₃)₂ (Me₄phen = 3,4,7,8-tetramethyl-1,10-phenanthroline) has been prepared and fully characterized by elemental analysis, X-ray crystallography, cyclic voltammetry and spectroscopic techniques. The solid-state structure of the complex indicated that the Ru (II) center is sitting in an N₄N′₂ coordination environment with a distorted octahedral geometry. Cyclic voltammetry technique was used to investigate the catalytic activity of the Ru (II) complex on the electrocatalytic reduction of CO₂ to CO in acetonitrile. The effect of the different reaction parameters, including the scan rate, concentration of the electrocatalyst [complex Ru (II)] and reaction temperature, on the catalytic activity was also investigated. The results showed that the electrocatalytic activity of the complex increases with increasing electrocatalyst concentration and scan rate. Further, the CO₂ reduction peak current decreases at lower temperatures owing to the inverse relationship between the temperature and activation energy. The theoretical calculations confirmed the proposed electrocatalytic mechanism comprising seven steps.     

钯基纳米材料电化学还原二氧化碳研究进展

电化学二氧化碳还原是利用电能驱动将CO_2高效转化为小分子碳基燃料的新方法,被认为是目前最具应用潜力的碳资源转化技术之一。然而,CO_2还原反应仍面临着诸多挑战,如反应过电位高,产物选择性低以及析氢反应的竞争等。因此,开发高效的电催化剂是发展CO_2还原技术的核心关键。近年来,Pd基材料在CO_2还原反应中表现出独特的催化性能优势:它不仅可以在接近平衡电位下高选择性地还原CO_2生成甲酸/甲酸盐,还能够在一定的负电位区间高效地还原CO_2生成CO。尽管如此,Pd基材料目前仍存在着成本较高、活性不理想以及稳定性差等问题,严重制约了其进一步应用与发展。对此,本文首先简单介绍了CO_2RR的基本原理,并综述了近年来Pd基催化剂电还原CO_2的应用研究及发展现状。重点探讨了尺寸效应、形貌效应、合金效应、核壳效应及载体效应等对Pd基催化剂性能的影响。最后针对这类材料的问题挑战及其未来发展方向进行了探讨与展望。     

高选择性和稳定性SnO2纳米催化剂上 CO2电化学还原为甲酸

作为最重要的还原产品,甲酸是 CO2还原中非常有价值的液体燃料.已有研究报道, Sn类金属电极对甲酸生成有很好的催化活性,所用电解液均为 KHCO3溶液(0.5 mol/L),但多数研究没有对其电解液条件的影响给出清晰解释.一般而言,电解液 pH值会影响 H2O和 CO2还原的电极电势,酸性环境有利于氢析出,碱性环境则不利于甲酸形成.在中性偏碱性环境, CO2电解可以提供维持氧化物稳定性的可能性.同时,电解质浓度也极大地影响甲酸形成.研究表明,当在固定床反应器中使用 Sn颗粒电极,在 KHCO3溶液(0.5 mol/L)中甲酸的法拉第效率比 K2CO3溶液(0.1 mol/L)的法拉第效率更大.我们研究组通过简单的水热自组装法成功制备了一种纳米结构 SnO2催化剂.其中 SnO2-50纳米催化剂由三维多级结构组成,为纳米颗粒和微米球的聚集体,其中含有直径为500 nm?1μm的高度多孔结构.该催化剂负载气体扩散电极用于 CO2电化学还原,表现出优异的 CO2还原催化活性和甲酸选择性.与其他文献报道相比,该电极具有明显的低过电位(?0.56 V vs. SHE).经研究发现,这与甲酸形成由传质和电荷传递过程控制有关,同时 CO2还原强烈依赖于电解液条件.此外,催化剂的电化学性能和甲酸选择性强烈依赖于电解液浓度.在0.5 mol/L KHCO3电解液中,当电解液浓度为0.1?0.5 mol/L时,催化性能随电解液浓度增加而提高,同时在电解液浓度为0.5 mol/L时催化性能达到最佳,获得56%的甲酸法拉第效率,这主要是由于 HCO3?直接参与反应的结果.在电解液浓度较低时,甲酸的形成由传质控制,而在电解液浓度较高时,甲酸的形成则由电荷传递控制.
　　同时我们发现在形成甲酸过程中,电解液 pH值对 CO2电化学还原过程有很大影响.为了研究电解液pH值影响,重点考察了pH值分别为6,7,8.3和9时的电位值,其原因是酸性过高有利于氢气形成,碱度过高不利于甲酸形成.结果表明,pH =8.3的电解液为 CO2还原的最佳电解液条件.此外,在最负的电势下,电解液pH=8.3时,阴极电流密度比其他电解液都大,几乎是pH=6的电解液的2倍.此时在中性偏碱性环境下, CO2还原可以提供维持氧化物稳定性的可能性.当电解液 pH增加到9.0时,甲酸产量及法拉第效率略有下降,可能是碱性环境不利于甲酸形成.
　　同时,对 SnO2-50纳米催化剂经28 h电解后的甲酸法拉第效率的衰减机制进行了深入研究.结果表明,随着电解时间延长,甲酸法拉第效率衰减.电解时间为1?28 h时,法拉第效率和甲酸产量均保持平稳下降趋势,28 h后法拉第效率由初始的56%降至24%.有文献报道,甲酸法拉第效率随电解时间的改变主要是由于阳极上甲酸的氧化或阴极上杂质的污染.为了证明阴极电解后的状态,我们对 SnO2-50/GDL阴极电解前后的 XPS谱进行了分析.结果发现,法拉第效率的下降是由于痕量氟离子沉积到 SnO2-50/GDL电极表面,这些痕量氟离子可能来自反应槽,阻碍电极表面 CO2电化学还原为甲酸.     

利用光热耦合下的光电导研究TiO2光热催化还原CO2（英文）

利用太阳能缓解能源危机和解决环境污染,是当前和未来的全球性课题.其中,光催化技术的研究步伐日渐加快.这不仅体现在光催化材料种类的增加,更体现在以光催化为基础的多场协同催化,特别是光热耦合作用成为增强光催化性能的一种高效、可靠的方法.氧空位的引入不仅可以拓宽催化剂对可见光的吸收、抑制载流子的复合、促进反应物的吸附以及降低反应的活化能,而且对于光热协同催化效率的提升有着重要的贡献.然而,目前光热协同催化的表征多局限于常规的光催化手段.开展光热耦合下的测量技术对深刻理解光热催化是十分必要的.本文研究温度、气氛、氧空位浓度对TiO2光电导的影响,构建光电导与光热催化活性之间的关系.我们将商用的ST-01 TiO2制成浆料,利用丝网印刷法将浆料覆盖在刻有沟槽的FTO上,并通过N2/H2混合气不同温度退火,得到不同氧空位含量的TiO2薄膜(Ov-TiO2).采用紫外-可见光谱(UV-Vis),拉曼光谱(Raman),电子顺磁共振(ESR)等手段对样品进行了表征.结果表明,N2/H2退火温度越高,氧空位浓度越高.我们对不同浓度氧空位的样品进行了光催化及光热协同催化CO2还原实验.结果表明,适量氧空位的样品(H2-150)光催化还原CO2性能最差,但光热协同催化还原CO2的性能最佳.我们对其光电导值的衰减情况进行了分析,看到H2-150样品在CO2气氛、光热条件下,电导衰减加快.由于光电导的衰减是由电荷复合和电荷参与的表面反应共同决定的,为确定是哪一因素决定了电导的衰减,我们进一步测试了H2-150样品在N2气氛下的电导衰减情况.结果发现,H2-150样品在N2气氛、光热条件下电导衰减反而变慢.这表明,造成H2-150样品在CO2气氛、光热条件下的电导衰减加快是光热条件下CO2还原速率加快,也验证了H2-150具有较好的光热催化CO2活性.与H2-150样品不同的是,大量氧空位样品(H2-350)在CO2气氛、光热条件下电导衰减反而变慢,我们认为这是由于H2-350存在深能级缺陷,在热的作用下会将捕获的电子释放,因此延缓了光电导的衰减.但由于深能级电子的还原能力较弱,所以H2-350样品的光热CO2还原活性稍逊于H2-150.综上所述,在光热电导与光热催化相关的研究中,我们证实了在Ov-TiO2中被捕获的电子在热激发下可再次向导带弛豫,从而解释了Ov-TiO2优异的光热催化性能.因此,光热电导的研究在理解光热催化方面具有重要的前景.     

Iron Porphyrin Allows Fast and Selective Electrocatalytic Conversion of CO2 to CO in a Flow Cell

Molecular catalysts have been shown to have high selectivity for CO₂ electrochemical reduction to CO, but with current densities significantly below those obtained with solid-state materials. By depositing a simple Fe porphyrin mixed with carbon black onto a carbon paper support, it was possible to obtain a catalytic material that could be used in a flow cell for fast and selective conversion of CO₂ to CO. At neutral pH (7.3) a current density as high as 83.7 mA cm⁻² was obtained with a CO selectivity close to 98 %. In basic solution (pH 14), a current density of 27 mA cm⁻² was maintained for 24 h with 99.7 % selectivity for CO at only 50 mV overpotential, leading to a record energy efficiency of 71 %. In addition, a current density for CO production as high as 152 mA cm⁻² (>98 % selectivity) was obtained at a low overpotential of 470 mV, outperforming state-of-the-art noble metal based catalysts.     

吡咯氮配位单原子铜催化剂的电催化二氧化碳还原性能

采用温度控制的浸渍-热解法, 合成了以碳纳米管为载体的一系列铜单原子催化剂. 扩展X射线吸收精细结构(EXAFS)分析表明, 催化剂中的单原子铜位点分别由吡啶氮和吡咯氮配位. 电催化性能测试表明, 所制备催化剂可用于电催化二氧化碳生成一氧化碳, 由吡啶氮配位的铜单原子催化剂的反应选择性较差, 而由吡咯氮配位的铜单原子催化剂则具有更强的活性, CO法拉第效率在-0.70 V(vs. RHE)时可达到96.3%; 吡咯氮配位的铜单原子中心对于析氢反应具有更好的抑制效果.