Hyperbranched and thermally cross‐linkable oligomer from a new 2,5,7‐tri‐functional fluorene monomer

New hyperbranched (HOFV) and linear oligomers (LOFV) were prepared from 2‐bromo‐5,7‐divinyl‐9,9‐dihexylfluorene (AB₂) and 2‐bromo‐7‐vinyl‐9,9‐dihexylfluorene, respectively, by the Heck reaction to study the effect of hyperbranched structure. The oligomers were readily soluble in common organic solvents. The weight‐average molecular weights (M_w) of HOFV and LOFV, determined by gel permeation chromatography using polystyrene as standard, were 2350 and 3950, respectively. Optical properties, both in solution and film state, were investigated using absorption and photoluminescence (PL) spectra. In film state, the absorption and PL spectra peaked at 416 ～ 425 nm and 473 ～ 503 nm, respectively. The HOFV showed energy funnel effect and enhanced fluorescence efficiency owing to the hyperbranched structure. The HOMO and LUMO levels of HOFV (LOFV), estimated from their cyclic voltammograms, were ?5.25 (?5.34) eV and ?2.66 (?2.75) eV, respectively. Thermal curing of HOFV to form cross‐linked HPFV (hyperbranched poly(fluorenevinylene)) was studied by IR, DSC, UV–visible spectra, NMR, AFM and SEM. The terminal vinyl groups in HOFV film almost disappeared to provide smooth, homogeneous and solvent‐resistant films of HPFV. Two‐layer PLED devices (ITO/PEDOT/HPFV/Ca/Al) exhibited maximal luminance and luminous efficiency of 1480 cd/m² and 0.18 cd/A, respectively, which were superior to its linear counterpart LPFV (352 cd/m², 0.06 cd/A). © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 70–84, 2008     

Vinyl copolymers containing pendant 1,4‐distyrylbenzene and 1,3,4‐oxadiazole chromophores: Preparation and optoelectronic properties

We prepared two vinyl copolymers P1 and P2 containing pendant distyrylbenzene and aromatic 1,3,4‐oxadiazole derivatives, respectively, from their precursor poly(styrene‐ran‐4‐vinylbenzyl chloride) (M_w = 11,400, PDI = 1.18), which had been prepared by the controlled radical polymerization (RAFT). Two main chain polymers containing similar isolated distyrylbenzene ( P3) and aromatic 1,3,4‐oxadiazole ( P4 ) chromophores were also synthesized for comparative study. The resulted copolymers ( P1 – P4 ) are soluble in common organic solvents and are basically amorphous materials with 5% weight‐loss temperature higher than 360 °C. The PL spectral results reveal that the architecture of P1 prevents the formation of inter‐ or intramolecular interaction. The HOMO and LUMO levels of P2 , estimated from cyclic voltammetric data, are ?5.96 and ?3.81 eV, respectively, which are much lower than those of P1 (?5.12 and ?3.11 eV). The emission of blend from P1 and P2 are contributed mainly from distyrylbenzene fluorophore (～450 nm) owing to efficient energy transfer. Moreover, the blend exhibits three kinds of redox behavior depending on their weight ratios. The luminance and current efficiency of the EL device lpar;ITO/PEDOT/ MEH ‐ PPV + P2 /Al) are 503 cd/m² and 0.11 cd/A, which can be improved to 1285 cd/m² and 0.44 cd/A, respectively, as the weight ratio of P2 increases from 0 to 20%. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5362–5377, 2006     

Synthesis and optoelectronic properties of luminescent poly(p‐phenylenevinylene) derivatives containing electron‐transporting 1,3,4‐oxadiazole groups

Three random copolymers ( P1–P3 ) comprising phenylenevinylene and electron‐transporting aromatic 1,3,4‐oxadiazole segments (11, 18, 28 mol %, respectively) were prepared by Gilch polymerization to investigate the influence of oxadiazole content on their photophysical, electrochemical, and electroluminescent properties. For comparative study, homopolymer poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐p‐phenylenevinylene] ( P0 ) was also prepared by the same process. The polymers ( P0–P3 ) are soluble in common organic solvents and thermally stable up to 410 °C under a nitrogen atmosphere. Their optical properties were investigated by absorption and photoluminescence spectroscopy. The optical results reveal that the aromatic 1,3,4‐oxadiazole chromophores in P1–P3 suppress the intermolecular interactions. The HOMO and LUMO levels of these polymers were estimated from their cyclic voltammograms. The HOMO levels of P0–P3 are very similar (?5.02 to ?5.03 eV), whereas their LUMO levels decrease readily with increasing oxadiazole content (?2.7, ?3.08, ?3.11, and ?3.19 eV, respectively). Therefore, the electron affinity of the poly(p‐phenylenevinylene) chain can be gradually enhanced by incorporating 1,3,4‐oxadiazole segments. Among the polymers, P1 (11 mol % 1,3,4‐oxadiazole) shows the best EL performance (maximal luminance: 3490 cd/m², maximal current efficiency: 0.1 cd/A). Further increase in oxadiazole content results in micro‐phase separation that leads to performance deterioration. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4377–4388, 2007     

Hyperbranched luminescent polyfluorenes containing aromatic triazole branching units

Using a new aromatic 1,2,4‐triazole branching monomer (4.8–13.3 mol %), three hyperbranched polyfluorenes ( P2 – P4 ) were synthesized by the Suzuki coupling reaction to investigate the structural effect on optoelectronic properties. Poly(9,9‐dihexylfluorene) ( P1 ) was also prepared for comparative investigation. Their weight‐average molecular weights and polydispersity indices are in the range of 1.16 × 10⁴ to 5.9 × 10⁴ and 1.49–2.25, respectively. Optical properties, both in solution and film state, were investigated using absorption and photoluminescence (PL) spectra. In film state, the absorption and PL spectra peaked at 377–392 and 424–425 nm, respectively, blue‐shift with increasing triazole concentration. Furthermore, a linear relationship between 1/λ_max,abs and 1/(1 ? n_triazole) is correlated (n: molar fraction), indicating a smooth decrease in conjugation length by incorporation of the branch unit. The P4 containing 13.3 mol % triazole reveals stable blue emission even at 150 °C (in air). The HOMO and LUMO levels of P2 – P4 , estimated from cyclic voltammograms, are ?5.69, ?5.73, ?5.78 eV and ?2.63, ?2.64, ?2.63 eV, respectively. The maximal brightness (current efficiency) of the electroluminescent devices (ITO/PEDOT:PSS/ P2 – P4 /Ca/Al) improves from 828 cd/m² (0.19 cd/A) to 2054 cd/m² (0.46 cd/A) with increasing triazole concentration. The results suggest that incorporation of aromatic 1,2,4‐triazole branch units is an effective way to improve annealing stability and EL performance of polyfluorenes. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4465–4476, 2007     

Design,synthesis, photophysical,and electrochemical properties of DCM‐based conjugated polymers for light‐emitting devices

A series of conjugated hyperbranched polymers, hyperbranched copolymers, and linear polymers containing 2‐pyran‐4‐ylidenemalononitrile (acceptor) and triphenylamine/fluorene (donor) units were synthesized and characterized by FTIR, ¹H NMR, thermogravimetric analyses, differential scanning calorimetry, gel permeation chromatography, UV–visible, photoluminescence, and cyclic voltammetry measurements. All the polymers show red‐light emission in the range of 566–656 nm both in solution and in solid state. The quantum efficiency of the polymers was in the range of 56–82%. Among the six polymers synthesized, only polymers containing fluorene units show T_g and polymers based on triphenylamine not exhibit T_g. The band gap of these polymers were found to be reasonably low; hyperbranched copolymer containing fluorene unit shows lowest band gap of 2.18 eV due to the stabilization of LUMO energy level by the electron withdrawing ? CN groups. The thermal and solubility behavior of the polymers were found to be good. All the EL spectra of the devices (indium‐tin oxide/poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate)/polymer/2,9‐dimethyl‐4,7‐diphenyl‐1,10‐phenanthroline/tris(8‐hydroxyquinoline)aluminum)/LiF/Al) show red‐light emission, and the device fabricated with P3 and P4 shows maximum luminance and luminous efficiency of 4104 cd m^?2 and 0.55 cd Å^?1 and 3696 cd m^?2 and 0.47 cd Å^?1, respectively, indicates that they had the best carrier balance. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Thermally stable red electroluminescent hybrid polymers derived from functionalized silsesquioxane and 4,7‐bis(3‐ethylhexyl‐2‐thienyl)‐2,1,3‐benzothiadiazole

Hyperbranched organic–inorganic hybrid conjugated polymers P1 and P2 were prepared via FeCl₃‐oxiditive polymerization of 4,7‐bis(3‐ethylhexyl‐2‐thienyl)‐2,1,3‐benzothiadiazole ( A ) and octa(3‐ethylhexyl‐2‐thienyl‐phenyl)polyhedral oligomeric silsesquioxane (POSS) ( B ) at different POSS concentrations. Compared to linear polymer PM derived from A , P1 , and P2 exhibit much higher PL quantum efficiency (?_PL‐f) in condensed state with improved thermal stability. ?_PL‐f of P1 and P2 increased by 80% and 400%, and the thermal degradation temperatures of P1 and P2 are increased by 35 °C and 46 °C, respectively. Light‐emitting diodes were fabricated using P1 , P2 , and PM . While the electroluminescent spectra of both P1 and PM show λ_max at 660 nm, P1 exhibits a much narrower EL spectrum and higher electroluminescence (～500%) compared with PM at a same voltage and film thickness. The maximum current efficiency of P1 is more than seven times of that of PM . The turn‐on voltages of the LEDs are in the order of P2 > PM > P1 . LED prepared by blending P1 with MEH‐PPV shows a maximum luminescence of 2.6 × 10³ cd/m² and a current efficiency of 1.40 cd/A, which are more than twice (1.1 × 10³ cd/m²) and five times (0.27 cd/A) of LED of PM /MEH‐PPV blend, respectively. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5661–5670, 2009     

Copolyfluorenes containing phenothiazine or thiophene derivatives: Synthesis,characterization, and application in white‐light‐emitting diodes

Four copolyfluorenes chemically doped with 0.1 and 1 mol % 3,7‐bis[2‐thiophene‐2‐yl)‐2‐cyanovinyl]phenothiazine ( PFPhT ) or 2,5‐bis[2‐(thiophene‐2‐yl)‐2‐cyanovinyl]thiophene chromophores ( PFThT ) were synthesized using the Suzuki coupling reaction and applied in white‐light‐emitting devices. They were characterized by GPC, elemental analysis, DSC, TGA, optical spectra, and cyclic voltammetry. They exhibited good thermal stability (T_d > 420 °C) and moderate glass transition temperatures (>95 °C). The PhT‐Br and ThT‐Br showed PL peaks at 586 and 522 nm (with a shoulder at 550 nm). In film state, PL spectra of the copolymers comprised emissions from the fluorene segments and the chromophores due to incomplete energy transfer. Both monomers exhibited low LUMO levels around ?3.50 to ?3.59 eV, whereas the PhT‐Br owned the higher HOMO level (?5.16 eV) due to its electron‐donating phenothiazine core. Light‐emitting diodes with a structure of ITO/PEDOT:PSS/copolymer/Ca(50 nm)/Al(100 nm) showed broad emission depending on the chromophore contents. The maximum brightness and maximum current efficiency of PFPhT2 ( PFThT1 ) device were 8690 cd/m² and 1.43 cd/A (7060 cd/m² and 0.98 cd/A), respectively. White‐light emission was realized by further blending PFPhT2 with poly(9,9‐dihexylfluorene) (w/w = 10/1), with the maximum brightness and maximum current efficiency being 10,600 cd/m² and 1.85 cd/A. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 833–844, 2009     

New poly(p‐phenylene vinylene) derivatives with two oxadiazole rings per repeat unit: Synthesis,photophysical properties,electroluminescence, and metal ion recognition

Two new poly(p‐phenylene vinylene) derivatives OX1‐PPV and OX2‐PPV bearing two 1,3,4‐oxadiazole rings per repeat unit and a fully conjugated backbone with solubilizing dodecyloxy side groups were synthesized and investigated. The amorphous conjugated polymers had glass‐transition temperature values of 60–75 °C and emitted intense blue or greenish‐blue light in solution with photoluminescence (PL) emission maxima at 379–492 nm and PL quantum yields of 0.41–0.52. In the solid state they emitted yellowish‐green light with PL emission maxima at 533–555 nm. Cyclic voltammetry showed that both conjugated polymers had reversible reduction and irreversible oxidation, making them n‐type materials. The electron affinity of OX2‐PPV was estimated as 2.85 eV whereas that of OX1‐PPV was 2.75 eV. Yellow electroluminescence (EL) was achieved from single‐layer light‐emitting diodes of OX2‐PPV with an EL emission maximum at 555 nm and a brightness of 70 cd/m². Polymer OX2‐PPV, which was functionalized with 2,6‐bis(1,3,4‐oxadiazole‐2‐yl)pyridine, demonstrated sensitivity to various metal ions as a fluorescence‐mode chemosensor. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2112–2123, 2004     

Novel mesogen‐jacketed poly(p‐phenylenevinylene) derivatives bearing oxadiazole pendants: Design,synthesis, and optoelectronic properties

1,3,4‐oxadiazole moieties were laterally linked to the phenyl rings via a short ? OCH₂ spacer and a series of novel poly(p‐phenylenevinylene) derivatives have been successfully synthesized through Horner–Witting–Emmons coupling reaction. The structures and properties of the monomers and the resulting conjugated polymers were characterized by nuclear magnetic resonance spectroscope, Fourier transform infrared, elemental analysis, gel permeation chromatography, thermogravimetric analysis, UV–vis absorption (UV) spectroscopy, photoluminescence spectroscopy and cyclic voltammetry. The UV spectra at solution state was similar to what's observed at film state while the PL spectra at film state had a red shift from 19 to 28 nm compared with the results at solution state, which implied that the unique bulky jacketed structure containing oxadiazole unit of these copolymers could effectively suppress π‐stacking/aggregation. LUMO levels of these polymers varied from ?3.44 to ?3.63 eV with increasing content of oxadiazole units, which facilitated electron injection. PLEDs with the configuration of ITO/PEDOT/Polymer/TPBI (15 nm)/LiF (1 nm)/Al (100 nm) were fabricated, which emit a yellowish green light around 540 and 570 nm with a maximum brightness of 1074.7 cd/m² and luminous efficiency of 0.108 cd/A. The introduction of the unique bulky OXD unit into PPVs at a low molar content largely improved the electroluminescence properties of PPV. © Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7173–7186, 2008     

Synthesis,characterization, and electroluminescence of novel copolyfluorenes and their applications in white light emission

New copolyfluorenes (PC8OF0–PC8OF50) comprised of 9,9‐dioctylfluorene and jacketed units 2,5‐bis[(5‐octyloxy‐phenyl)‐1,3,4‐ oxadiazole]‐1‐(3,5‐dibromophenyl)‐benzene (35C8) were synthesized by palladium‐catalyzed Suzuki coupling reaction. They were characterized by molecular weight determination, ¹H NMR, elemental analysis, DSC, TGA, absorption and emission spectroscopy, and cyclic voltammetry (CV). These copolymers were readily soluble in common organic solvents and exhibited high glass transition temperature and thermal stability.The copolymer films showed absorption peaks from 381 nm to 351 nm, and PL peaks from 432 nm to 421 nm with a blue shift originated from 35C8 units. Both the HOMO energy levels and LUMO levels changed little as the content of 35C8 units increased (?5.59 eV to ?5.48 eV and ?2.60 eV to ?2.49 eV). Electroluminescent devices: ITO/PEDOT:PSS[poly(ethylenedioxythiophene):polystyrenesulfonate]/polymer/Ca (25 nm)/Ag(80 nm) (a), ITO/PEDOT:PSS/polymer/TPBI [1,3,5‐ tris(N‐phenylbenzimidazol‐2‐yl)benzene](15 nm)/Mg:Ag(10:1, wt)/Ag (b), and ITO/ PEDOT:PSS/PVK[Poly(N‐vinylcarbazole)]/polymer/TPBI(15 nm)/Ca(25 nm)/Ag(80 nm) (c) were fabricated to investigate the influence of jacketed contents and device architectures on emission characteristics. The maximum brightness and current efficiency of the PC8OF25 device (5097.8 cd/m² and 0.484 cd/A) surpassed those of the PC8OF0 device (3122.8 cd/m² and 0.416 cd/A). The EL emissions of PC8OF0 – PC8OF50 were pure blue and low‐energy excimer emission bands were successfully suppressed, indicating that these copolymers could be good candidates for blue light‐emitting materials. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4555–4565, 2009     

Synthesis and properties of new orange red light‐emitting hyperbranched and linear polymers derived from 3,5‐dicyano‐2,4,6‐tristyrylpyridine

Two new orange red light‐emitting hyperbranched and linear polymers, poly(pyridine phenylene)s P1 and P2, were prepared by the Heck coupling reaction. In particular, an A₂ + B₃ approach was developed to synthesize conjugated hyperbranched polymer P2 via one‐pot polycondensation. The polymers were characterized by NMR, Fourier transform infrared, ultraviolet–visible, and elemental analysis. They showed excellent solubility in common solvents such as tetrahydrofuran, CH₂Cl₂, CHCl₃, and N,N‐dimethylformamide and had high molecular weights (up to 6.1 × 10⁵ and 5.8 × 10⁵). Cyclic voltammetry studies revealed that P2 had a low‐lying lowest unoccupied molecular orbital energy level of ?3.22 eV and a highest occupied molecular orbital energy level of ?5.43 eV. The thin film of P2 emitted strong orange‐red photoluminescence at 595 nm. A double‐layer light‐emitting diode fabricated with the configuration of indium tin oxide/P2/tris(8‐hydroxy‐quinoline)aluminum/Al emitted orange‐red light at 599 nm, with a brightness of 662 cd/m² at 7 V and a turn‐on voltage of 4.0 V; its external quantum efficiency was calculated to be 0.19% at 130.61 mA/cm². This indicated that this new electroluminescent polymer (P2) based on 3,5‐dicyano‐2,4,6‐tristyrylpyridine could possibly be used as an orange‐red emitter in polymer light‐emitting displays. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 493–504, 2005     

Copolyphenylenes with pendant benzimidazolyl and diethanolaminohexyloxy groups: Synthesis and electron‐transporting application in PLEDs

Two new electron‐transporting copolyphenylenes P1NH and P2NH possessing balanced charges crucial to emission efficiency of polymer light‐emitting diodes (PLEDs) have been synthesized and applied as an electron‐transporting layer (ETL). The main chain structure is all para‐linkage for P1NH and both para‐ and meta‐linkage for P2NH , with the same pendant electron‐withdrawing benzimidazolyl and polar diethanolaminohexyloxy groups. Both copolymers possess excellent thermal stability (T _d > 300 °C, T _g > 100 °C) due to their rigid backbones. In addition, the pendant groups effectively lower LUMO (～ ?2.70 eV) and HOMO (～ ?5.70 eV) levels, resulting in improved electron‐transporting and hole‐blocking capabilities. Multilayer yellow‐emitting PLEDs with a configuration of ITO/PEDOT:PSS/SY/ETL/LiF/Al were successfully fabricated by the spin‐coating process. The maximum luminance and maximum current efficiency of the P1NH ‐based device were 12,881 cd/m² and 10.94 cd/A, respectively, superior to the performance of P2NH ‐based device (4938 cd/m², 3.70 cd/A) and the device without ETL (8690 cd/m², 2.78 cd/A). Current results indicate that P1NH is highly effective in enhancing electron transport and device performance. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 2494–2505     

Synthesis and electro‐optical properties of light‐emitting polymers containing oxadiazole derivatives for light‐emitting diodes applications

Two PPV‐based bipolar polymers containing 1,3,4‐oxadiazole pendant groups were synthesized via the Gilch polymerization reaction for use in light‐emitting diodes (LEDs). The resulting polymers were characterized using ¹H and ¹³C NMR, elemental analysis, DSC, and TGA. These polymers were found to be soluble in common organic solvents and are easily spin‐coated onto glass substrates, producing high optical quality thin films without defects. The electro‐optical properties of ITO/PEDOT/polymer/Al devices based on these polymers were investigated using UV‐visible, PL, and EL spectroscopy. The turn‐on voltages of the OC₁Oxa‐PPV and OC₁₀Oxa‐PPV devices were found to be 8.0 V. The maximum brightness and luminescence efficiency of the OC₁Oxa‐PPV device were found to be 544 cd/m² at 19 V and 0.15 cd/A, respectively. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1098–1110, 2008     

Synthesis and optoelectronic properties of alternating benzofuran/terfluorene copolymer with stable blue emission

The solution processable alternating benzofuran/terfluorene copolymer bearing side oxadiazole groups ( PBF‐OXD ) was synthesized and its optoelectronic properties and color stability were investigated. Electron‐deficient and stereohindered oxadiazole units were used as pendent groups to compensate for the poor electron‐transporting ability of a p‐type polymer backbone, to depress the intermolecular π‐stacking, and to improve solubility while retaining polymer blue emission. PBF‐OXD showed a glass transition at 135 °C and an onset decomposition temperature of ～345 °C. A simple EL device, with the configuration of ITO/PEDOT:PSS/ PBF‐OXD /Ba/Al, displayed a stable blue emission (λ_max = 434 nm), good color purity (full width half‐maximum = 59 nm), maximum brightness of 1400 cd/m², and a maximum luminance efficiency of 0.95 cd/A. The PL and EL spectra changed slightly on annealing and on increasing the applied voltage. These results show that the as‐synthesized copolymer PBF‐OXD had integrated respective functions of its different building blocks and exhibited good thermal and color stability with improved EL performance. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5488–5497, 2009     

Synthesis and characterization of novel poly(p‐phenylenevinylene) derivatives containing phenothiazine‐5‐oxide and phenothiazine‐5, 5‐dioxide moieties

PPV‐based copolymers containing phenothiazine‐5‐oxide and phenothiazine‐5, 5‐dioxide moieties have been successfully synthesized by Wittig‐Horner reaction and characterized by means of UV‐vis, photoluminescence, electroluminescence spectra, and cyclic voltammetry. All of these copolymers can be dissolved in common organic solvents such as chloroform, tetrahydrofuran, and toluene. The PL maxima in the film state are located at 582, 556, and 552 nm for P1, P2, and P3, respectively. The HOMO and LUMO levels of P2 are found to be ?5.21 and ?2.68 eV, respectively; whereas those of P3 are found to be ?5.26 and ?2.71 eV, respectively. The cyclic voltammetry result indicates that the conversion of electron‐donating sulfide to electron‐withdrawing sulfoxide or sulfone group in polymers plays a dominating role in increasing its oxidation potential. Yellowish‐green light ranging from 568 to 540 nm was observed for the single layer device with the configuration of ITO/Polymer/Ca/Al. Double layer devices with Zn (BTZ)₂ as a hole blocking layer exhibited enhanced EL performance compared to the single layer devices. The maximum brightness of the double layer devices of P1, P2, and P3 is 278, 400, and 796 cd/m², respectively. The results of EL and electrochemical analyses revealed that they are promising candidate materials for organic, light‐emitting diodes with hole‐transporting ability. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4291–4299, 2007     

Polyfluorenes minimally doped with 1,4‐bis(2‐thienyl‐2‐cyanovinyl)benzene chromophore: Their synthesis,characterization, and application to white‐light‐emitting materials

Copolyfluorenes ( PFR1 and PFR2 ), chemically doped with 0.1 and 0.025 mol % 2,5‐dihexyloxy‐1,4‐bis(2‐thienyl‐2‐cyanovinyl)benzene (MR chromophere) were synthesized by the Suzuki coupling reaction. The PFR s were used to fabricate white‐light‐emitting devices through incomplete energy transfer. Because of the low content of the MR chromophore, the optical, thermal, and electrochemical properties of the PFR s were almost identical to those of polyfluorene, except for their photoluminescent (PL) and electroluminescent (EL) properties. The copolymer films showed PL peaks at about 428 and 570 nm originating from fluorene segments and MR chromophores, respectively. Compared with the model compound ( MR ), the polymer chains extended the conjugation length of the MR chromophores and exhibited a 20–48 nm red‐shift in the emission band. In addition, the lower LUMO level of the MR (?3.27 eV) was expected to improve the electron injection. The EL devices [ITO/PEDOT:PSS/ PFR s/Ca (50 nm)/Al (100 nm)] showed a broad emission band, covering the entire visible region, with chromaticity coordinates of (0.36, 0.35) and (0.32, 0.30) for PFR1 and PFR2 devices, respectively. The emission color of the PFR2 device was very similar to that of a pure white light (0.33, 0.33); and the maximal brightness and current efficiency were 3011 cd/m² and 1.98 cd/A, respectively, which surpass those found for polyfluorene devices (1005 cd/m², 0.28 cd/A). A). © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3703–3713, 2008     

Carbazolevinylene‐based polymers and model compounds with oxadiazole and triphenylamine segments: Synthesis,photophysics, and electroluminescence

Two new soluble alternating carbazolevinylene‐based polymers POXD and PTPA as well as the corresponding model compounds MOXD and MTPA were synthesized by Heck coupling. POXD and MOXD contained 2,5‐diphenyloxadiazole segments, while PTPA and MTPA contained triphenylamine segments. All samples displayed high thermal stability. The polymers had higher glass transition temperature (T_g) than their corresponding model compounds. The samples showed absorption maximum at 364–403 nm with optical band gap of 2.62–2.82 eV. They emitted blue‐green light with photoluminescence (PL) emission maximum at 450–501 nm and PL quantum yields in THF solution of 0.15–0.36. The absorption and the PL emission maxima of PTPA and MTPA were blue‐shifted as compared to those of POXD and MOXD . The electroluminescence (EL) spectra of multilayered devices made using four materials exhibited bluish green emissions, which is well consistent with PL spectra. The EL devices made using poly(vinyl carbazole) doped with MOXD and MTPA as emitting materials showed luminances of 12.1 and 4.8 cd m^?2. POXD and PTPA exhibited 25.4, and 96.3 cd m^?2, respectively. The polymer containing the corresponding molecules in the repeating group showed much higher device performances. Additionally, POXD and MOXD exhibited better stability of external quantum efficiency (EQE) and luminous efficiency with current density resulting from enhancing the electron transporting properties. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5592–5603, 2008     

Copolyfluorenes containing bridged triphenylamine or triphenylamine: Synthesis,characterization, and optoelectronic properties

A novel aryl‐bridged triphenylamine derivative, 7‐t‐butyl‐5,5,9,9‐tetraaryl‐13b‐aza‐naphtho[3,2,1‐de]anthracene (ABTPA) was designed and synthesized. The alternating copolymers of ABTPA/dihexylfluorene ( P1 ) and triphenylamine (TPA)/dihexylfluorene ( P2 ) were synthesized by Suzuki coupling reaction. P1 shows excellent thermal stability with a decomposition temperature of 440 °C and a glass‐transition temperature of 326 °C. The HOMO energy levels of the two polymers are very close (?5.15 eV for P1 and ?5.13 eV for P2 ). The maximum absorption peak of P1 is red shifted by 23 nm with respect to P2 , because the incorporation of ABTPA units into the PF backbone enhances the electronic conjugation degree compared with the case of TPA units. The rigidity and the steric hindrance of the ABTPA in P1 result in a small Stokes shift and almost the same emission spectra of P1 between its film and solution. A PLED with simple configurations of ITO/ P1 /TNS (tetranaphthalen‐2‐yl‐silane)/Alq₃ (tris(8‐hydroxyquinolinolato)aluminum)/Al emits a blue light with emission peak at 436 nm, and exhibits a maximum current efficiency of 1.89 cd/A and a maximum luminance of 4183 cd/m², which is superior to the device with P2 as emissive layer under the identical conditions. These results indicate that ABTPA unit could be a very promising candidate to replace TPA unit and find widely application in organic/polymeric optoelectronic materials. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3651–3661, 2009     

Synthesis and nonlinear optical properties of polyacetylenes containing oxadiazole and thiophene pendant groups with high thermal stability

A series of random copolymers poly(3‐ethynylthiophene)‐copoly(2‐(4‐decyloxyphenyl)‐5‐(4‐ethynylphenyl)‐1,3,4‐oxadiazole) with different oxadiazole content ( P2 – P4 ) and homopolymer poly(3‐ethynylthiophene) ( P1 ) as well as poly(2‐(4‐decyloxyphenyl)‐5‐(4‐ethynylphenyl)‐1,3,4‐oxadiazole) ( P5 ) were prepared. The copolymers ( P2 – P4 ) are completely soluble in common organic solvents. The structures and properties of all polymers were characterized and evaluated by FTIR, ¹H NMR, ¹³C NMR, TGA, UV, PL, GPC, and nonlinear optical (NLO) analyses. The incorporation of diaryl‐oxadiazole into polyacetylene‐containing thiophene significantly endows copolymers with higher thermal stability, which may origin from the synergetic effect of the “jacket effect” of diaryl‐oxadiazole units and the effect of retarding or eliminating a few 6π‐electrocycliaztion proceeds of oxadiazole‐containing polyacetylene due to the hindrance of thiophene units. When the copolymer ( P3 ) posses more regular alternating thiophene pendants and oxadiazole pendants arrangement along the polymer backbone, it shows good thermal stability (T_d up to 388 °C) and larger third‐order nonlinear optical susceptibility (χ(3) up to 11.0 × 10^?11 esu). © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Synthesis and characterization of bipolar copolymers containing oxadiazole and carbazole pendant groups and their application to electroluminescent devices

A series of random copolymers POC10{Poly(2,5‐bis[(5‐decyloxy‐phenyl)‐1,3,4‐oxadiazole]styrene)}‐co‐Poly(N‐vinylcarbazole) (PVK) with different nvk content were synthesized through common radical polymerization and were incorporated into light emitting diodes as emitting layers. The structures and properties of the copolymers were characterized and evaluated by GPC, TGA, DSC, UV, PL, CV, and EL analyses. All the polymers enjoy high thermal stability. Cyclic voltammetry revealed that, with the incorporation of N‐vinylcarbazole to the copolymer, these copolymers had high‐lying HOMO energy values, which facilitated hole injection. PL peaks in the film show blue‐shift compared with those in solutions and fluorescent quantum efficiency decreased with the nvk content increasing, which supported the efficient energy transfer from nvk units to the oxadiazole units. Single‐layer LEDs with the configuration of ITO/PEDOT/PC10‐nvk/Mg:Ag/Ag were fabricated, which emit a blue light around 440 and 490 nm with a maximum brightness of 675.3 cd/m² and luminous efficiency of 0.108 cd/A. Moreover, we fabricated electrophosphorescent device from bipolar transport copolymer PC10‐nvk4 as host material and an orange‐light‐emitting iridium phosphor IrMDPP as guest. The maximum luminous efficiency of 0.548 cd/A was obtained. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5452–5460, 2008