Synthesis of silver nanoparticles for remote opening of polyelectrolyte microcapsules

Silver nanoparticles of 10, 18, and 23 nm were synthesized in aqueous medium by chemical reduction of silver nitrate in excess of sodium borohydride. Modification of polyelectrolyte shells with synthesized silver nanoparticles was performed using the layer-by-layer approach. Remote opening of the polyelectrolyte/silver capsules was performed with a CW Nd:YAG FD laser with an average incident power output up to 70 mW. Capsules with a mixture of 10 and 18 nm silver nanoparticles in its polyelectrolyte shell were ruptured after less than 7 s of laser irradiation, while microcapsules with 23 nm silver nanoparticles in the shell were broken after 11 s of laser treatment and 10 nm silver nanoparticles were broken after 26 s.     

Dual‐fluorophore Raspberry‐like Nanohybrids for Ratiometric pH Sensing

We report on the development of raspberry‐like silica structures formed by the adsorption of 8‐hydroxypyrene‐1,3,6‐trisulfonate (HPTS)@silica nanoparticles (NPs) on rhodamine B isothiocyanate (RBTIC)@silica NPs for ratiometric fluorescence‐based pH sensing. To overcome the well‐known problem of dye leaching which occurs during encapsulation of anionic HPTS dye in silica NPs, we utilized a polyelectrolyte‐assisted incorporation of the anionic HPTS. The morphological and optical characterization of the as‐synthesized dye‐doped NPs and the resulting nanohybrids were carried out. The pH‐sensitive dye, HPTS, incorporated in the HPTS‐doped silica NPs provided a pH‐dependent fluorescence response while the RBITC‐doped silica provided the reference signal for ratiometric sensing. We evaluated the effectiveness of the nanohybrids for pH sensing; the ratio of the fluorescence emission intensity at 510 nm and 583 nm at excitation wavelengths of 454 nm and 555 nm, respectively. The results showed a dynamic response in the acidic pH range. With this approach, nanohybrids containing different dyes or receptors could be developed for multifunctioning and multiplexing applications.     

Silver nanocube-enhanced far-red/near-infrared fluorescence of conjugated polyelectrolyte for cellular imaging

We present the study of silver nanocube (Ag NC)-enhanced fluorescence of a cationic conjugated polyelectrolyte (CPE) for far-red/near-infrared fluorescence cell imaging. Layer-by-layer self-assembly of polyelectrolytes on 78 nm Ag NCs is used to control CPE-metal distance and its effect on CPE fluorescence. The highest fluorescence enhancement factor (FEF) is obtained for Ag NCs with two bilayers, corresponding to a CPE-metal spacer thickness of ～6 nm. At the optimal excitation wavelength, the FEF is 13.8 with respect to the control silica nanoparticles (NPs). The fluorescent NPs are further used for cellular imaging studies. The CPE-loaded Ag NCs with two bilayers exhibit excellent image contrast, superior to the control of CPE-silica NP at a similar uptake efficiency. The viability test indicates low cytotoxicity of the CPE-loaded Ag NCs, rendering them as promising cell imaging agents.     

Antibacterial activity of silver bionanocomposites synthesized by chemical reduction route

ABSTRACT: BACKGROUND: The aim of this study is to investigate the functions of polymers and size of nanoparticles on the antibacterial activity of silver bionanocomposites (Ag BNCs). In this research, silver nanoparticles (Ag NPs) were incorporated into biodegradable polymers that are chitosan, gelatin and both polymers via chemical reduction method in solvent in order to produce Ag BNCs. Silver nitrate and sodium borohydride were employed as a metal precursor and reducing agent respectively. On the other hand, chitosan and gelatin were added as a polymeric matrix and stabilizer. The antibacterial activity of different sizes of silver nanoparticles was investigated against Gram-positive and Gram-negative bacteria by the disk diffusion method using Mueller-Hinton Agar. RESULTS: The properties of Ag BNCs were studied as a function of the polymer weight ratio in relation to the use of chitosan and gelatin. The morphology of the Ag BNCs films and the distribution of the Ag NPs were also characterized. The diameters of the Ag NPs were measured and their size is less than 20 nm. The antibacterial trait of silver/chitosan/gelatin bionanocomposites was investigated. The silver ions released from the Ag BNCs and their antibacterial activities were scrutinized. The antibacterial activities of the Ag BNC films were examined against Gram-negative bacteria (E. coli and P. aeruginosa) and Gram-positive (S. aureus and M. luteus) by diffusion method using Muller-Hinton agar. CONCLUSIONS: The antibacterial activity of Ag NPs with size less than 20 nm was demonstrated and showed positive results against Gram-negative and Gram-positive bacteria. The Ag NPs stabilized well in the polymers matrix.     

Surface-guided self-assembly of silver nanoparticles on edges of heterogeneous surfaces

A general method for the generation of two-dimensional (2D) ordered silver nanoparticles (av 45 nm) ring array has been demonstrated via controllable self-assembly. The selective self-assembly is conducted on the edges of a gold coated polyelectrolyte film. This film is fabricated using the monolayer polystyrene (PS) spheres (av 600 nm) on a substrate as template, followed by depositing a positively charged polyelectrolyte and gold colloids (av 17 nm) via the layer-by-layer (LbL) self-assembly technique, and finally by eliminating the PS monolayer. This gold coated polyelectrolyte film has a regular pattern of sharp edges, and those edges are composed of abundant polyelectrolyte. This heterogeneous surface is easily prepared and universal for site-selective absorption of nanoparticles (silver nanoparticles in this paper, av 45 nm). This surface-guided self-assembly is powerful for fabricating micro/nanostructures on the edges of prepatterns. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to characterize the products.     

银纳米颗粒负载阶层多孔二氧化硅块体的制备及表征

以溶胶-凝胶伴随相分离法制备的阶层多孔二氧化硅作为载体,3-氨丙基三乙氧基硅烷(APTES)为改性剂,乙醇为还原剂,在阶层多孔二氧化硅固体骨架上进行银纳米颗粒均匀负载.利用扫描电镜(SEM)、透射电镜(TEM)、X射线衍射(XRD)、汞压、N2吸附/脱附、X射线光电子能谱(XPS)等测试技术对银纳米颗粒负载阶层多孔二氧化硅进行了表征,探讨了APTES表面改性、乙醇还原机理以及银纳米颗粒负载块体的孔结构特征变化规律.结果表明:APTES表面改性将氨基接枝于阶层骨架上,氨基与银离子形成银氨离子,银氨离子经乙醇还原后将平均粒径约16 nm的银纳米颗粒成功负载于二氧化硅的大孔及介孔内部;负载后的阶层多孔块体的大孔骨架未受到破坏,但其比表面积由418 m2·g-1下降到254m2·g-1,两次还原负载能提高银纳米颗粒的负载量.     

Electrochemical solid-state phase transformations of silver nanoparticles

Adenosine triphosphate (ATP)-capped silver nanoparticles (ATP-Ag NPs) were synthesized by reduction of AgNO(3) with borohydride in water with ATP as a capping ligand. The NPs obtained were characterized using transmission electron microscopy (TEM), UV-vis absorption spectroscopy, X-ray diffraction, and energy-dispersive X-ray analysis. A typical preparation produced ATP-Ag NPs with diameters of 4.5 ± 1.1 nm containing ~2800 Ag atoms and capped with 250 ATP capping ligands. The negatively charged ATP caps allow NP incorporation into layer-by-layer (LbL) films with poly(diallyldimethylammonium) chloride at thiol-modified Au electrode surfaces. Cyclic voltammetry in a single-layer LbL film of NPs showed a chemically reversible oxidation of Ag NPs to silver halide NPs in aqueous halide solutions and to Ag(2)O NPs in aqueous hydroxide solutions. TEM confirmed that this takes place via a redox-driven solid-state phase transformation. The charge for these nontopotactic phase transformations corresponded to a one-electron redox process per Ag atom in the NP, indicating complete oxidation and reduction of all Ag atoms in each NP during the electrochemical phase transformation.     

银纳米颗粒负载阶层多孔二氧化硅块体的制备及表征

以溶胶-凝胶伴随相分离法制备的阶层多孔二氧化硅作为载体,3-氨丙基三乙氧基硅烷（APTES）为改性剂,乙醇为还原剂,在阶层多孔二氧化硅固体骨架上进行银纳米颗粒均匀负载. 利用扫描电镜（SEM）、透射电镜（TEM）、X射线衍射（XRD）、汞压、N₂吸附/脱附、X射线光电子能谱（XPS）等测试技术对银纳米颗粒负载阶层多孔二氧化硅进行了表征,探讨了APTES表面改性、乙醇还原机理以及银纳米颗粒负载块体的孔结构特征变化规律. 结果表明：APTES表面改性将氨基接枝于阶层骨架上,氨基与银离子形成银氨离子,银氨离子经乙醇还原后将平均粒径约16 nm的银纳米颗粒成功负载于二氧化硅的大孔及介孔内部;负载后的阶层多孔块体的大孔骨架未受到破坏,但其比表面积由418 m²·g^-1下降到254 m²·g^-1,两次还原负载能提高银纳米颗粒的负载量.     

Single step hybrid coating process to enhance the electrosteric stabilization of inorganic particles

We report on a single-step coating process and the resulting colloidal stability of silica-coated spindle-type hematite nanoparticles (NPs) decorated with a layer of poly(acrylic acid) (PAA) polyelectrolyte chains that are partially incorporated into the silica shell. The stability of PAA coated NPs as a function of pH and salt concentration in water was compared to bare hematite particles and simple silica-coated hematite NPs, studying their electrophoretic mobility and the hydrodynamic radius by dynamic light scattering. Particles coated with this method were found to be more stable upon the addition of salt at pH 7, and their aggregation at the pH of the isoelectric point is reversible. The hybrid coating appears to increase the colloidal stability in aqueous media due to the combination of the decrease of the isoelectric point and the electrosteric stabilization. This coating method is not limited to hematite particles but can easily be adapted to any silica-coatable particle.     

内部具有可移动金核的中空银纳米颗粒的制备、表征及其表面增强拉曼效应

采用振荡法和种子生长技术制备出核壳结构的Au@SiO2纳米颗粒及夹层结构的Au@SiO2@Ag纳米颗粒, 用HF将Au@SiO2@Ag NPs夹层的SiO2溶解, 得到内部带有粒径为30 nm的可移动金核、壳层厚度约为30 nm的中空银纳米颗粒(Au@air@Ag NPs). 用扫描电子显微镜和透射电子显微镜对所得到的纳米微球的形貌进行了表征, 并以罗丹明B为探针分子研究了Au@air@Ag 纳米颗粒的表面增强拉曼(SERS)效应, 发现Au@air@Ag 纳米颗粒是一种可应用于SERS的理想材料.     

Preparation and characterization of multi‐walled carbon nanotubes decorated with silver nanoparticles through ultraviolet irradiation reduction

A facile, green and efficient approach was applied to synthesize multi‐walled carbon nanotubes (MWNTs) decorated with silver nanoparticles (MWNT‐Ag) for further potential application. Oxidized MWNTs were decorated with silver nanoparticles (Ag NPs) via a method combining ultraviolet irradiation‐induced reduction and conventional silver mirror reaction without any reducing agent. The obtained product was characterized using various methods. X‐ray diffraction proved that the Ag NPs were synthesized successfully. Moreover, Ag NPs with a diameter of 80 nm, attached onto MWNTs, could be clearly observed in field emission scanning electron microscopy images, which also confirmed Ag NPs. Energy‐dispersive spectroscopy and transmission electron microscopy also indicated the presence of Ag NPs. Furthermore, thermogravimetric analysis was used to measure the content of Ag NPs in MWNT‐Ag, the result indicating that the weight content of Ag NPs was up to 31.88%. UV–visible absorption spectroscopy was adopted to evaluate the dispersion property of MWNT‐Ag. The result illustrated that MWNT‐Ag had a good dispersibility and stability in water. Characterization was also carried out through Fourier transform infrared spectroscopy, Raman spectroscopy and dynamic light scattering analysis.     

Dissolution-accompanied aggregation kinetics of silver nanoparticles

Bare silver nanoparticles with diameters of 82 ± 1.3 nm were synthesized by the reduction of the Ag(NH(3))(2)(+) complex with D-maltose, and their morphology, crystalline structure, UV-vis spectrum, and electrophoretic mobilities were determined. Dynamic light scattering was employed to assess early stage aggregation kinetics by measuring the change in the average hydrodynamic diameter of the nanoparticles with time over a range of electrolyte types (NaCl, NaNO(3), and CaCl(2)) and concentrations. From this the critical coagulation concentration values were identified as 30, 40, and 2 mM for NaNO(3), NaCl, and CaCl(2), respectively. Although the silver nanoparticles were observed to dissolve in all three electrolyte solutions, the aggregation results were still consistent with classical Derjaguin-Landau-Verwey-Overbeek (DLVO) theory. The dissolution of the silver nanoparticles, which were coated with a layer of Ag(2)O, was highly dependent on the electrolyte type and concentration. In systems with Cl(-) a secondary precipitate, likely AgCl, also formed and produced a coating layer that incorporated the silver nanoparticles. Aggregation of the silver nanoparticles was also examined in the presence of Nordic aquatic fulvic acid and was little changed compared to that evaluated under identical fulvic acid-free conditions. These results provide a fundamental basis for further studies evaluating the environmental fate of silver nanoparticles in natural aquatic systems.     

Facile,single-pot preparation of nanoporous SiO2 particles (carrier) with AgNPs at core and crust for controlled disinfectant release

This study demonstrates a novel, facile and one-pot approach to synthesize silica nanoparticles with silver at core and crust (SiNP-AgCC). A modified Stöber method was used to make SiNP-AgCC. A significant reduction in the size of SiO₂ nanoparticles was seen, with 2–5 nm AgNPs being uniformly distributed on the surface and 10–20 nm AgNPs in the center. A typical mesoporous SiO₂ particle (SiNP) produced using the Stöber method was transformed to nanoporous SiO₂ by this modified Stöber method. Nanoporous SiO₂ particles with silver in the center are advantageous for slow and consistent Ag⁺ release, which was confirmed by Ag⁺ ion release test. Antibacterial activities of the samples were tested to evaluate the disinfection performance of the samples on gram-negative bacteria (Escherichia coli) using disk diffusion and the LB-agar method. SiNP-AgCC showed prolonged silver release for more than 20 days and improved antibacterial properties even after five days of incubation.     

Effects of surfactants and electrolytes on adsorbed layers and particle stability

Adsorbed polymer and polyelectrolyte layers on colloidal silica nanoparticles have been studied in the presence of various salts and surfactants using photon correlation spectroscopy and solvent relaxation NMR. Poly(ethylene oxide) (PEO; molar mass 103.6 kg mol (-1)) adsorbed with a relatively high affinity and gave a layer thickness of 4.2 +/- 0.2 nm. While the nonionic surfactant used only increased this thickness slightly, anionic surfactants had a much greater effect, mainly due to repulsions between adsorbed aggregates, leading to expansion of the layer. A nonionic/anionic surfactant mixture was also tested and resulted in a larger increase in layer thickness than any of the individual surfactants. The dominant factor on addition of salt was generally the reduced solvency of PEO, which resulted in a further increase in the layer thickness but in some cases caused flocculation. This was not the case when the surfactant was sodium dodecylbenzenesulfonate; instead screening of the intermicellar repulsions possibly combined with surfactant-cation binding resulted in a reduction in the layer thickness. In comparison the affinity between silica and sodium polystyrenesulfonate was very weak. Anionic surfactants and salts did not noticeably increase the strength of adsorption, but instead encouraged flocculation. The situation was different with a nonionic surfactant, which was able to adsorb to silica itself and apparently facilitated a degree of polyelectrolyte adsorption as well.     

Comparison of Glyphosate Detection by Surface-Enhanced Raman Spectroscopy Using Gold and Silver Nanoparticles at Different Laser Excitations

Glyphosate is one of the most widely used pesticides in the world, but it has been shown to persist in the environment and therefore needs to be detected in food. In this work, the detection of glyphosate by surface-enhanced Raman scattering (SERS) using gold and silver nanoparticles and three different commonly used laser excitations (532, 632, and 785 nm wavelengths) of a Raman microscope complemented with a portable Raman spectrometer with 785 nm excitation is compared. The silver and gold nanosphere SERS substrates were prepared by chemical synthesis. In addition, colorimetric detection of glyphosate using cysteamine-modified gold and silver nanoparticles was also tested. The best results were obtained with Ag NPs at 532 nm excitation with a detection limit of 1 mM and with Au nanoparticles at 785 nm excitation with a detection limit of 100 µM. The SERS spectra of glyphosate with cysteamine-modified silver NPs improved the detection limits by two orders of magnitude for 532 nm excitation, i.e., up to 10 µM, and by one order of magnitude for 632 and 785 nm excitation wavelengths.     

Electrochemistry and electrogenerated chemiluminescence of a spirobifluorene-based donor (triphenylamine)-acceptor (2,1,3-benzothiadiazole) molecule and its organic nanoparticles

A new D-A-π-A-D molecule (Spiro-BTA) containing two 2,1,3-benzothiadiazole (BTA) as the acceptor (A) and triphenylamine as the donor (D) bridged by a spirobifluorene moiety has been synthesized. The novel D-A molecule shows intense red emission (612 nm) with a high PL quantum yield (Φ(PL) = 0.51) in a solid film. A cyclic voltammogram of Spiro-BTA in 1:2 MeCN:benzene/0.1 M Bu(4)NPF(6) shows two reversible oxidation waves and one reversible reduction wave. The first oxidation wave and reduction wave were assigned as two successive electron transfer peaks separated by ～50 mV related to the oxidation of the two noninteracting donors and the reduction of the two noninteracting acceptors, respectively. Electrogenerated chemiluminescence (ECL) of Spiro-BTA upon cyclic oxidation and reduction in MeCN:benzene 1:2 shows a very bright and stable red emission that could be seen in a well-lit room. Using a reprecipitation method, well-dispersed organic nanoparticles (NPs) of the Spiro-BTA were prepared in aqueous solution. The nanoparticles were analyzed by dynamic light scattering (DLS) and scanning electron microscopy (SEM), yielding a NP size (without surfactant) of 130 ± 20 nm, while with surfactant, 100 ± 20 nm. Bathochromic shifts of absorption spectra (～16 ± 2 nm), as compared to that of the dissolved Spiro-BTA in THF, were observed for both NPs in water and as a thin film. While blue shifts (14 ± 2 nm) were observed for the photoluminescence (PL). The PL intensity of the Spiro-BTA nanoparticles was slightly enhanced (Φ(PL) of nanoparticles in water = 48%) over that of the dissolved Spiro-BTA in THF. The ECL of the organic Spiro-BTA nanoparticles in aqueous solution could be observed upon oxidation with tri-n-propylamine as a coreactant.     

Optimization of plasmonic enhancement of fluorescence on plastic substrates

In this work, we report on the uniform deposition of tailored plasmonic coatings on polymer substrates and on the distance dependence of the plasmonic enhancement of a fluorescent dye. Silver, gold, and silver/gold alloy nanoparticles (NPs) with a range of diameters were synthesized using chemical techniques and characterized using UV-vis absorption spectroscopy, transmission electron microscopy (TEM), and atomic force microscopy (AFM). Reproducible polyelectrolyte (PEL) layers, which were deposited on plastic microwell plates using a layer-by-layer technique, served as both a stable and uniform substrate for deposition of the NPs as well as providing spacer layers of known thickness between the NPs and the fluorescent dye. A maximum enhancement factor of approximately 11 was measured for 60 nm diameter pure silver NPs, for a dye-NP separation of approximately 3 nm. A shift in the localized surface plasmon resonance (LSPR) wavelength as a function of the effective refractive index of the PEL layers was also observed, and the measured shifts show a similar trend with theoretical predictions. This work will contribute toward the rational design of optical biochip platforms based on plasmon-enhanced fluorescence.     

Growth of ordered silver nanoparticles in silica film mesostructured with a triblock copolymer PEO-PPO-PEO

Elaboration of mesostructured silica films with a triblock copolymer polyethylene oxide-polypropylene oxide-polyethylene oxide, (PEO-PPO-PEO) and controlled growth of silver nanoparticles in the mesostructure are described. The films are characterized using UV-visible optical absorption spectroscopy, TEM, AFM, SEM, X-ray diffraction (XRD) and Rutherford backscattering spectrometry (RBS). Organized arrays of spherical silver nanoparticles with diameter between 5 and 8 nm have been obtained by NaBH₄ reduction. The size and the repartition of silver nanoparticles are controlled by the film mesostructure. The localization of silver nanoparticles exclusively in the upper-side part of the silica-block copolymer film is evidenced by RBS experiment. On the other hand, by using a thermal method, 40 nm long silver sticks can be obtained, by diffusion and coalescence of spherical particles in the silica-block copolymer layer. In this case, migration of silver particles toward the glass substrate-film interface is shown by the RBS experiment.     

XPS study of silver and copper nanoparticles demonstrated selective anticancer,proapoptotic, and antibacterial properties

Silver and copper nanoparticles were produced by an ecologically safe metal vapor synthesis (MVS) method using acetone as an organic dispersion medium. Transmission electron microscopy (TEM) showed that the specimens are spherical and polydisperse, and their average size is 2.5 nm for silver nanoparticles (Ag NPs) and 2.6 nm for copper nanoparticles (Cu NPs). X-ray photoelectron spectroscopy analyses showed that the state of silver in the nanoparticles is close to that of silver in the Ag⁰ state, whereas copper black contains two oxidized states of the metal—Cu⁺ and Cu²⁺. Biological in vitro studies demonstrated that the nanoparticles have antibacterial activity against Gram-positive and Gram-negative bacterial species. Cu NPs exhibited more prominent antibacterial effects and induced significant growth inhibition of Bacillus cereus and Escherichia coli. Both types of nanoparticles showed anticancer properties in vitro. Cu NPs induced intense cytotoxicity in cancer and normal fibroblasts in vitro cultures, but their inhibitory effect against noncancerous cells was milder compared with cancer cell lines. Ag NPs demonstrated selective cytotoxicity against human lung and cervical adenocarcinoma cell lines. Further in vitro studies indicated that the mechanism of Ag NPs and Cu NPs anticancer effects involves induction of apoptosis. The present study describes a green synthesis approach for production of biologically active silver and copper nanoparticles and highlights their potential for medical application.     

Circular dichroism and UV-Vis absorption spectroscopic monitoring of production of chiral silver nanoparticles templated by guanosine 5'-monophosphate

Herein we report the chemical reduction of silver ions incorporated into chiral supramolecular nanostructures by NaBH(4) in buffered (basic) and unbuffered conditions. In situ self-assembly of guanosine 5'-monophosphate (5'-GMP) templated by Ag(I) and generation of silver nanoparticles (NPs) were continuously monitored by CD and UV-Vis spectroscopy measurements. 5'-GMP has been identified as an efficient chiral organic ligand to complex silver ions into a hierarchical helical nanostructure and is a useful capping agent for stabilizing silver NPs with a size diameter lower than 20 nm. The observation of opposite signed bands in the CD spectra of Ag(I)/5'-GMP complexes at different pH has suggested the existence of opposite-handed supramolecular helical structures depending on pH. Both helical supramolecular structures induce chirality in the silver NPs during their growth of the same handedness as shown by the CD signals in the plasmon resonance band.