碲化铋红外透明导电薄膜的制备与光电性能（特邀）

采用射频磁控溅射法在石英衬底和硒化锌衬底上制备了碲化铋薄膜,分别研究了薄膜厚度、退火温度对薄膜微观结构和光电性能的影响。利用X射线衍射仪、X射线光电子能谱仪和冷场发射扫描电子显微镜,分析了薄膜结构、成分和形貌。结果表明,退火有利于薄膜的结晶,且不改变晶体的择优取向。傅里叶变换红外光谱测试结果表明,在石英衬底和硒化锌衬底上沉积的薄膜,光学透过率随着薄膜厚度和退火温度的增加而减小,在硒化锌衬底上沉积的薄膜透过波段比石英长,且光学透过率更加稳定。霍尔效应测试结果表明,随着薄膜厚度和退火温度的增加,薄膜的电阻率逐渐减小,最小为1.448×10^-3Ω·cm,迁移率为27.400 cm²·V^-1·s^-1,载流子浓度为1.573×10²⁰ cm^-3。在石英衬底上沉积的15 nm厚的Bi₂Te₃薄膜,在1～5μm波段的透过率达到80%,退火200℃后透过率达到60%,电阻率为5.663×10^-3Ω·cm。在...     

生长温度对Ga掺杂ZnO薄膜光电性能的影响

在不同衬底温度(室温~750 ℃)条件下,采用脉冲激光沉积(PLD)方法在石英玻璃和单晶硅(111)衬底上制备了Ga掺杂ZnO(GZO)薄膜。结果显示:衬底温度的变化导致衬底表面吸附原子扩散速率和脱附速率的不同,从而导致合成薄膜结晶质量的差异,衬底温度450 ℃时制备的GZO薄膜具有最好的结晶特性;GZO薄膜中载流子浓度随衬底温度升高而单调减小的现象与GZO薄膜中的本征缺陷密切相关,晶界散射强度的变化导致迁移率出现先增大后减小的趋势,衬底温度450 ℃时制备的GZO薄膜具有最小的电阻率~0.02 Ω·cm;随着衬底温度的升高,薄膜载流子浓度的单调减小导致了薄膜光学带隙变窄,所有合成样品的平均可见光透过率均达到85%以上。采用PLD方法制备GZO薄膜,衬底温度的改变可以对薄膜的光电性能起到调制作用。     

衬底温度对反应磁控溅射W掺杂ZnO薄膜的微观结构及光电性能的影响

采用直流脉冲反应磁控溅射方法生长W掺杂ZnO（WZO）透明导电氧化物薄膜并研究了衬底温度对薄膜微观结构、组分、表面形貌以及光电性能的影响.实验结果表明,WZO薄膜具有良好的（002）晶面择优取向,且适当的衬底温度是制备优质WZO薄膜的关键因素.随着衬底温度升高,薄膜表面粗糙度先增大后减小;衬底温度较高时,薄膜的结构致密,结晶质量好,电子迁移率高.当衬底温度为325℃时,WZO薄膜获得最低电阻率9.25×10^-3Ω·cm,方块电阻为56.24Ω/□,迁移率为11.8 cm² V^-1·s^-1,其在可见光及近红外区域（400—1500 nm）范围的平均透过率达到85.7%.     

射频磁控溅射法制备ZnS多晶薄膜及其性质

实验采用射频磁控溅射法在玻璃衬底上沉积了ZnS多晶薄膜,研究了沉积气压、退火温度和衬底温度对ZnS薄膜质量的影响.利用X射线衍射(XRD)分析了薄膜的微结构,并计算了内应力值.通过紫外-可见光分光光度计测量了薄膜的透过谱,计算了Urbach能量和禁带宽度.利用扫描电子显微镜(SEM)观察了薄膜的表面形貌.结果表明: 衬底温度为室温时沉积的ZnS薄膜具有较大的压应力,并且内应力值随着工作气压增大而增大,在300 ℃下进行退火处理后内应力松弛,衬底温度为350 ℃时制备的ZnS薄膜内应力小,透过率高,经300 ℃退火处理后结晶质量有所提高. 关键词： ZnS薄膜 射频磁控溅射 内应力     

热处理温度对ZnO∶Al薄膜性能的影响

利用溶胶-凝胶技术在玻璃衬底上制备了ZnO∶Al薄膜,表征了薄膜的结构、光透过和光致发光特性,探讨了热处理温度对薄膜晶体结构和光学性质的影响.结果表明,在热分解温度400 ℃和退火温度600 ℃时,ZnO∶Al薄膜的C轴择优取向明显,透过率较高.在热处理温度400 ℃情况下,激发波长340 nm的光致发光谱中有三个发光中心,紫外发光强度随退火温度的升高先升高后下降,500 ℃时发光强度最强.其它两个发光峰的强度随退火温度的升高而降低甚至消失.激发波长不同,ZnO∶Al薄膜的发光中心和强度均发生变化.     

热处理温度对ZnO：Al薄膜性能的影响

利用溶胶-凝胶技术在玻璃衬底上制备了ZnO:Al薄膜,表征了薄膜的结构、光透过和光致发光特性,探讨了热处理温度对薄膜晶体结构和光学性质的影响.结果表明,在热分解温度400 ℃和退火温度600 ℃时,ZnO:Al薄膜的C轴择优取向明显,透过率较高.在热处理温度400 ℃情况下,激发波长340 nm的光致发光谱中有三个发光中心,紫外发光强度随退火温度的升高先升高后下降,500 ℃时发光强度最强.其它两个发光峰的强度随退火温度的升高而降低甚至消失.激发波长不同,ZnO:Al薄膜的发光中心和强度均发生变化.     

AlN缓冲层对ZnO薄膜质量的影响

采用脉冲激光沉积法以AlN为缓冲层在Si(100)衬底上制备了ZnO薄膜,并测量了样品的XRD谱、SEM图和PL谱.结果表明,AlN缓冲层可以提高Si衬底上外延生长ZnO薄膜的晶体质量.改变缓冲层的生长温度(50～500 ℃)所制备样品的测量结果表明,较低温度下生长的AlN缓冲层有利于制备高质量的ZnO外延层薄膜,其中AlN缓冲层生长温度为100 ℃时外延生长ZnO薄膜晶体质量最好.     

退火对ZnO薄膜晶体结构和ZnO/p-Si异质结光电性质的影响

采用脉冲激光沉积方法在p-Si(100)衬底卜牛长ZnO薄膜,分别在500℃、600℃和700℃下真空退火,采用X射线衍射仪研究了退火对ZnO薄膜品体结构的影响,并测量了ZnO的面电阻和ZnO/p-Si异质结的、I-V特性曲线.研究表明,随着退火温度的升高,ZnO的(002)衍射峰强度逐渐增大,半峰全宽不断减小,同时薄膜内应力减小,ZnO晶粒尺寸变大.表明高温退火有助于ZnO薄膜结晶质量的提高.在没有光照的条件下,异质结的漏电流随退火温度的增加而增大;用650 nm光照射样品时,600℃退火的样品表现出最明显的光电效应,而过高的退火温度会破坏ZnO/p-Si异质结的界面结构,使其光电流变小.所以,要得到性能良好的光电器件,应选取适当的退火温度.     

Bi3.15Eu0.85Ti3O12铁电薄膜的结构与光学性能

采用化学溶液沉积法在石英衬底上制备了Bi_3.15Eu_0.85Ti₃O₁₂ (BEuT) 铁电薄膜,研究了 BEuT薄膜的结构和光学性能。XRD结果表明,不同温度退火的BEuT皆形成铋层状钙钛矿型结构,其晶粒尺寸随着退火温度的升高而增大,与SEM观察结果一致。对BEuT薄膜的拉曼光谱研究表明,Eu³⁺主要取代钙钛矿层中的Bi³⁺位。光学透过率曲线显示,在大于500 nm的波段,各BEuT薄膜的透过率均比较高,其禁带宽度约为 3.69 eV。BEuT薄膜的发光随着退火温度的升高而增强,这可归因于其结晶状况的改善。     

ZnO薄膜的制备和结构特性及应变

在SiO₂/Si衬底上面,利用射频磁控溅射方法,在不同的工艺条件下生长ZnO薄膜,然后进行热处理(600～1000℃退火).研究了氩氧比和退火温度对薄膜结晶性能的影响.薄膜的表面结构和晶体特性通过扫描电子显微镜(SEM)、X射线衍射(XRD)来进行表征.结果表明:所制备的薄膜为多晶纤锌矿结构,具有垂直于衬底的c轴(002)方向的择优取向性.热处理可使ZnO(002)衍射峰相对强度增强,半峰全宽(FWHM)变小,即退火使c轴生长的薄膜取向性增强.未经退火的ZnO薄膜存在张应力,经过热处理后应力发生改变,最后变成压应力,并且随着退火温度的升高,压应力逐渐增大.     

Influence of substrate temperature on the optical and piezoelectric properties of ZnO thin films deposited by rf magnetron sputtering

In this study, ZnO thin films were fabricated using the rf magnetron sputtering method and their piezoelectrical and optical characteristics were investigated for various substrate temperatures. The ZnO thin film has the largest crystallization orientation for the (0 0 2) peak and the smallest FWHM value of 0.56° at a substrate temperature of 200 °C. The surface morphology shows a relatively dense surface structure at 200 °C compared to the other substrate temperatures. The surface roughness shows the smallest of 1.6 nm at a substrate temperature of 200 °C. The piezoelectric constant of the ZnO thin film measured using the pneumatic loading method (PLM) has a maximum value of 11.9 pC/N at a substrate temperature of 200 °C. The transmittance of the ZnO thin film measured using spectrophotometry with various substrate temperatures ranged from 75 to 93% in the visible light region. By fitting the refractive index from the transmittance to the Sellmeir dispersion relation, we can predict the refractive index of the ZnO thin film according to the wavelength. In the visible light range, the refraction index of the ZnO thin film deposited at a substrate temperature of 200 °C is the range of 1.88-2.08.     

Effect of annealing temperature on the optical constants of zinc oxide films

In this paper, the effect of annealing temperature on optical constants was studied. The ZnO films were deposited on microscopic glass substrates using the sol-gel method for various annealing temperatures. The deposited zinc oxide (ZnO) films were characterized by an X-ray diffractometer (XRD), a spectrophotometer and scanning electron microscopy (SEM). The transmittance spectra recorded through the spectrophotometer exhibits 90% transmittance. The XRD spectra showed polycrystalline nature of ZnO film. Optical constants were determined through transmittance spectra using an envelope method. It was found that there was a significant effect of annealing temperature on the refractive index and extinction coefficient of deposited ZnO films. In this experiment, the optimum refractive index value of 1.97 was obtained at 350 °C annealing temperature at visible (vis) wavelength. The optical energy gap was found to be of ∼3.2 eV for all the samples. The top view of SEM showed the ZnO grain growth on the glass substrates.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Enhanced blue emission of ZnO films deposited on AlN substrates

Taking into account the individual excellent optical properties of ZnO and AlN, the combination of ZnO with AlN may give the enhanced performances. Based on similar lattice constants between ZnO and AlN, considering that AlN is a promising high power integrated circuit substrate material, ZnO films are deposited on AlN substrates using magnetron sputtering. We find that AlN substrate shows an excellent transparency with an average transmittance of about 80%. As ZnO films are deposited on AlN substrate, average transmittance still maintain above 80% except for the UV absorption edge shifted to the longer wavelength. In addition, AlN substrate shows two emission peaks at 420 and 468 nm ascribed to Al vacancies with different charge states. As ZnO films are deposited on AlN substrates in pure Ar gas, the intensity of both peaks attain the maximum. After introducing O₂ gas, they conversely decreases and attains the minimum. PL emissions increase again as the sample is annealed in vacuum. Excellent blue emissions are obtained due to the synergistic effect between ZnO and AlN. This work may help the development of the practical optoelectronic devices based on ZnO and AlN materials.     

钼掺杂氧化锌薄膜的结构、光学和表面等离子体特性研究

室温下,通过直流磁控反应溅射在石英衬底上制备一系列钼掺杂氧化锌薄膜。分别采用X射线衍射(XRD)、原子力显微镜(AFM)、分光光度计及拉曼光谱仪研究了钼掺杂浓度对氧化锌薄膜结构、表面形貌、光学性能和表面等离子体特性的影响。XRD测试结果表明,零掺杂氧化锌薄膜结晶良好,呈c轴择优取向,掺杂后薄膜缺陷增多,结晶质量下降,当掺杂浓度达到3.93 Wt%时,薄膜由c轴择优取向的晶态转变为非晶态。AFM测试结果表明非晶态掺钼氧化锌薄膜表面光滑,粗糙度最低可达489 pm。透射光谱表明所有薄膜样品在可见光范围(400～760 nm)平均透过率均达到80%,禁带宽度随着掺杂浓度的提高从3.28 eV单调增加至3.60 eV。吸收光谱表明氧化锌薄膜表面等离子体共振吸收峰随钼掺杂量的增大发生蓝移,而拉曼光谱表明Mo重掺杂时ZnO薄膜表面拉曼散射信号强度显著降低。通过Mo掺杂获得非晶态氧化锌薄膜,拓宽了氧化锌薄膜材料的应用领域,同时研究了Mo掺杂浓度对氧化锌薄膜表面等离子体的调控作用,这对制备氧化锌基光子器件具有重要参考价值。     

Effect of substrate and annealing on the structural and optical properties of ZnO:Al films

ZnO:Al thin films with c-axis preferred orientation were deposited on glass and Si substrates using RF magnetron sputtering technique. The effect of substrate on the structural and optical properties of ZnO:Al films were investigated. The results showed a strong blue peak from glass-substrate ZnO:Al film whose intensity became weak when deposited on Si substrate. However, the full width at half maxima (FWHM) of the Si-substrate ZnO:Al (0 0 2) peaks decreased evidently and the grain size increased. Finally, we discussed the influence of annealing temperature on the structural and optical properties of Si-substrate ZnO:Al films. After annealing, the crystal quality of Si-substrate ZnO:Al thin films was markedly improved and the intensity of blue peak (∼445 nm) increased noticeably. This observation may indicate that the visible emission properties of the ZnO:Al films are dependent more on the film crystallinity than on the film stoichiometry.     

Au层退火温度对ZnO/Au/ZnO多层膜的结构、光学及电学性质的影响

采用金属有机化学气相沉积(MOCVD)技术在蓝宝石衬底上制备出晶体质量较好的透明导电的ZnO/Au/ZnO(ZAZ)多层膜,其中,Au夹层是通过射频磁控溅射的方法获得。通过对Au夹层进行不同温度的退火处理,研究了Au层退火温度对ZAZ多层膜的结构特性、电学性能和光学特性的影响。利用原子力显微镜(AFM)、扫描电子显微镜(SEM)、X射线衍射(XRD)仪、霍尔效应测试和透射谱分析等测试手段对ZAZ多层膜的性质进行了分析。测试结果表明,在200 ℃下对Au夹层进行快速退火处理,多层膜的结构、电学和光学性质达到最优,表面等离子体效应也更明显。其中,XRD(002)衍射峰的半高宽为0.14°,电阻率为2.7×10^-3 Ω·cm,载流子浓度为1.07×10²⁰ cm^-3,可见光区平均透过率为75.3%。     

不同衬底和CdCl2退火对磁控溅射CdS薄膜性能的影响

在科宁7059玻璃, FTO, ITO, AZO四种衬底上磁控溅射CdS薄膜, 并在CdCl₂+干燥空气380 ℃退火, 分别研究了不同衬底和退火工艺对CdS薄膜形貌、结构和光学性能的影响. 扫描电子显微镜形貌表明: 不同衬底原位溅射CdS薄膜的形貌不同, 退火后相应CdS薄膜的晶粒度和表面粗糙度明显增大. XRD衍射图谱表明: 不同衬底原位溅射和退火CdS薄膜均为六角相和立方相的混相结构, 退火前后科宁7059玻璃, FTO, AZO衬底上CdS薄膜有 H(002)/C(111) 最强衍射峰, ITO衬底原位溅射CdS薄膜没有明显的最强衍射峰, 退火后出现 H(002)/(111) 最强衍射峰. 紫外-可见分光光度计分析表明: AZO, FTO, ITO, 科宁7059玻璃衬底CdS薄膜的可见光平均透过率依次减小, 退火后相应衬底CdS薄膜的可见光平均透过率增大, 光学吸收系数降低; 退火显著增大了不同衬底CdS薄膜的光学带隙. 分析得出: 上述结果是由于不同衬底类型和退火工艺对CdS多晶薄膜的形貌、结构和带尾态掺杂浓度改变的结果. 关键词： CdS薄膜 磁控溅射 退火再结晶 带尾态     

Microstructures and optical properties of Cu-doped ZnO films prepared by radio frequency reactive magnetron sputtering

Pure and Cu-doped ZnO (ZnO:Cu) thin films were deposited on glass substrates using radio frequency (RF) reactive magnetron sputtering. The effect of substrate temperature on the crystallization behavior and optical properties of the ZnO:Cu films have been studied. The crystal structures, surface morphology and optical properties of the films were systematically investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and a fluorescence spectrophotometer, respectively. The results indicated that ZnO films showed a stronger preferred orientation toward the c-axis and a more uniform grain size after Cu-doping. As for ZnO:Cu films, the full width at half maxima (FWHM) of (0 0 2) diffraction peaks decreased first and then increased, reaching a minimum of about 0.42° at 350 °C and the compressive stress of ZnO:Cu decreased gradually with the increase of substrate temperature. The photoluminescence (PL) spectra measured at room temperature revealed two blue and two green emissions. Intense blue-green luminescence was obtained from the sample deposited at higher substrate temperature. Finally, we discussed the influence of annealing temperature on the structural and optical properties of ZnO:Cu films. The quality of ZnO:Cu film was markedly improved and the intensity of blue peak (∼485 nm) and green peak (∼527 nm) increased noticeably after annealing. The origin of these emissions was discussed.     

纳米ZnO-SiO2自清洁增透薄膜的制备及其性能

以乙酸锌醇热法ZnO纳米粒子为基料, 通过溶胶-凝胶浸渍提拉法制备纳米ZnO-SiO₂自清洁增透薄膜. 采用透射电镜, 光谱椭偏仪, 扫描电镜, X-射线衍射, 差热分析仪和UV-vis等技术对样品进行表征, 以亚甲基蓝的光催化降解为目标反应, 评价其光催化活性. 结果表明, ZnO纳米粒子为球粒状结构, 直径约12-20 nm, 特征紫外吸收波长位于375 nm 处; 与未涂覆纳米ZnO-SiO₂自清洁增透薄膜的石英玻璃基底相比, 涂覆后石英玻璃在400-800 nm波长范围内平均透光率提升达4.17%, 具有良好的宽光谱增透行为; 且在紫外光激发下对亚甲基蓝染料具有光催化降解特性, 进而具备良好的自清洁性能.