Preparation of carbon encapsulated Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript> anode material for lithium ion battery through pre-coating method

Carbon encapsulated Li₄Ti₅O₁₂ (C/Li₄Ti₅O₁₂) anode material for lithium ion battery was prepared by using the pre-coat method of two steps, and the TiO₂ was pre coated before the reaction with Li₂CO₃. The structure and morphology of the resultant C/Li₄Ti₅O₁₂ materials were characterized by X-ray diffraction (XRD) and scanning microscopy (SEM). Electrochemical tests showed that at 0.1 C, the initial discharge capacity was 169.9 mAh g^?1, and the discharge capacity was 80 mAh g^?1 at 5 C. After 100 cycles at 2 C, the discharge specific capacity was 108.5 mAh g^?1. Compare with one step coating method, results showed the C/Li₄Ti₅O₁₂ prepared by pre-coat method can reduce the particle’s size and effectively improve the electrochemical performance.     

Nanocrystalline Li<Subscript>2</Subscript>TiO<Subscript>3</Subscript> electrodes for supercapattery application

Nanocrystalline Li₂TiO₃ was successfully synthesized using solid-state reaction method. The microstructural and electrochemical properties of the prepared material are systematically characterized. The X-ray diffraction pattern of the prepared material exhibits predominant (002) orientation related to the monoclinic structure with C2/c space group. HRTEM images and SAED analysis reveal the well-developed nanostructured particles with average size of ～40 nm. The electrochemical properties of the prepared sample are carried out using cyclic voltammetry (CV) and chronopotentiometry (CP) using Pt//Li₂TiO₃ cell in 1 mol L^?1 Li₂SO₄ aqueous electrolyte. The Li₂TiO₃ electrode exhibits a specific discharge capacity of 122 mAh g^?1; it can be used as anode in Li battery within the potential window 0.0–1.0 V, while investigated as a supercapacitor electrode, it delivers a specific capacitance of 317 F g^?1 at a current density of 1 mA g^?1 within the potential range ?0.4 to +0.4 V. The demonstration of both anodic and supercapacitor behavior concludes that the nanocrystalline Li₂TiO₃ is a suitable electrode material for supercapattery application.     

Pr-modified Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript> nanofibers as an anode material for lithium-ion batteries with outstanding cycling performance and rate performance

Pr-doped Li₄Ti₅O₁₂ in the form of Li_4?x/3Ti_5?2x/3Pr_xO₁₂ (x = 0, 0.01, 0.03, 0.05, and 0.07) was synthesized successfully by an electrospinning technique. ICP shows that the doped samples are closed to the targeted samples. XRD analysis demonstrates that traces of Pr³⁺ can enlarge the lattice parameter of Li₄Ti₅O₁₂ from 8.3403 to 8.3765 Å without changing the spinel structure. The increase of lattice parameter is beneficial to the intercalation and de-intercalation of lithium-ion. XPS results identify the existence form of Ti is mainly Ti⁴⁺ and Ti³⁺ in minor quantity in Li_4?x/3Ti_5?2x/3Pr_xO₁₂ (x = 0.05) samples due to the small amount of Pr³⁺. The transition from Ti⁴⁺ to Ti³⁺ is conducive to the electronic conductivity of Li₄Ti₅O₁₂. FESEM images show that all the nanofibers are well crystallized with a diameter of about 200 nm and distributed uniformly. The results of electrochemical measurement reveal that the 1D Li_4?x/3Ti_5?2x/3Pr_xO₁₂ (x = 0.05) nanofibers display enhanced high-rate capability and cycling stability compared with that of undoped nanofibers. The high-rate discharge capacity of the Li_4?x/3Ti_5?2x/3Pr_xO₁₂ (x = 0.05) samples is excellent (101.6 mAh g^?1 at 50 °C), which is about 58.48 % of the discharge capacity at 0.2 °C and 4.3 times than that of the bare Li₄Ti₅O₁₂ (23.5 mA g^?1). Even at 10 °C (1750 mA g^?1), the specific discharge capacity is still 112.8 mAh g^?1 after 1000 cycles (87.9 % of the initial discharge capacity). The results of cyclic voltammograms (CV) and electrochemical impedance spectroscopy (EIS) illustrate that the Pr-doped Li₄Ti₅O₁₂ electrodes possess better dynamic performance than the pure Li₄Ti₅O₁₂, further confirming the excellent electrochemical properties above.     

Nano Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript> as sulfur host for high-performance Li-S battery

S/Li₄Ti₅O₁₂ cathode with high lithium ionic conductivity was prepared for Li-S battery. Herein, nano Li₄Ti₅O₁₂ is used as sulfur host and fast Li⁺ conductor, which can adsorb effectively polysulfides and improve remarkably Li⁺ diffusion coefficient in sulfur cathode. At 0.5 C, S/Li₄Ti₅O₁₂ cathode has a stable discharge capacity of 616 mAh g^?1 at the 700th cycle and a capacity loss per cycle of 0.0196% from the second to the 700th cycle, but the corresponding values of S/C cathode are 437 mAh g^?1 and 0.0598%. Even at 2 C, the capacity loss per cycle of S/Li₄Ti₅O₁₂ cathode is only 0.0273% from the second to the 700th cycle. The results indicate that Li₄Ti₅O₁₂ as the sulfur host plays a key role on the high performance of Li-S battery due to reducing the shuttle effect and enhancing lithium ionic conductivity.     

Urea-assisted solvothermal synthesis of monodisperse multiporous hierarchical micro/nanostructured ZnCo<Subscript>2</Subscript>O<Subscript>4</Subscript> microspheres and their lithium storage properties

High-quality monodisperse multiporous hierarchical micro/nanostructured ZnCo₂O₄ microspheres have been fabricated by calcinating the Zn_1/3Co_2/3CO₃ precursor prepared by urea-assisted solvothermal method. The as-prepared products are characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), high-resolution transmission electron microscopy (HRTEM), and Brunauer-Emmett-Teller (BET) measurement to study the crystal phase and morphology. When tested as anode material for lithium ion batteries, the multiporous ZnCo₂O₄ microspheres exhibit an initial discharge capacity of 1,369 mAh g^?1 (3,244.5 F cm^?3) and retain stable capacity of 800 mAh g^?1 (1,896 F cm^?3) after 30 cycles. It should be noted that the good electrochemical performances can be attributed to the porous structure composed of interconnected nanoscale particles, which can promote electrolyte diffusion and reduce volume change during discharge/charge processes. More importantly, this ZnCo₂O₄ 3D hierarchical structures provide a large number of active surface position for Li⁺ diffusion, which may contribute to the improved electrochemical performance towards lithium storage.     

Synthesis and electrochemical properties of Li<Subscript>1.2</Subscript>Mn<Subscript>0.54</Subscript>Ni<Subscript>0.13</Subscript>Co<Subscript>0.13</Subscript>O<Subscript>2</Subscript> cathode material for lithium-ion battery

The layered Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ lithium-rich manganese-based solid solution cathode material has been synthesized by a simple solid-state method. The as-prepared material has a typical layered structure with R-3m and C2/m space group. The synthesized Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ has an irregular shape with the size range from 200 to 500 nm, and the primary particle of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ has regular sphere morphology with a diameter of 320 nm. Electrochemical performances also have been investigated. The results show that the cathode material Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ prepared at 900 °C for 12 h has a good electrochemical performance, which can deliver a high initial discharge capacity of 233.5, 214.2, 199.3, and 168.1 mAh g^?1 at 0.1, 0.2, 0.5, and 1 C, respectively. After 50 cycles, the capacity retains 178.0, 166.3, 162.1, and 155.9 mAh g^?1 at 0.1, 0.2, 0.5, and 1 C, respectively. The results indicate that the simple method has a great potential in synthesizing manganese-based cathode materials for Li-ion batteries.     

Evolution of crystal structure and electrochemical performance of layered Li<Subscript>1.20</Subscript>Ti<Subscript>0.44</Subscript>Cr<Subscript>0.36</Subscript>O<Subscript>2</Subscript>/C cathode materials with cycling

Carbon-coated layered Li_1.20Ti_0.44Cr_0.36O₂/C and pristine Li_1.20Ti_0.44Cr_0.36O₂ cathode materials have been synthesized through a sol–gel method followed by high-temperature calcination. Their electrochemical performances have been evaluated, which indicate that the Li_1.20Ti_0.44Cr_0.36O₂/C exhibits much higher cyclic stability and capacity than the pristine one. The initial delithiation capacity of the Li_1.20Ti_0.44Cr_0.36O₂/C can reach 217.1 mAh g^?1. The reversible capacity retention is 94 % after 100 cycles at current density of 23 mA g^?1. Ex situ X-ray diffraction and electrochemistry impedance spectroscopy coupled with impedance fitting have been employed to reveal evolution of the crystal structure and the electrochemical kinetics of the Li_1.20Ti_0.44Cr_0.36O₂/C with delithiation/lithiation cycling. The results indicate that the cation layers of the Li_1.20Ti_0.44Cr_0.36O₂/C experience order to disorder transition. The abrupt delithiation capacity fading and potential drop after the initial cycle are resulted from the order to disorder transition accompanying with steep increase of the charge transfer resistance and decrease of the exchange current density and the Li-ion diffusion coefficient simultaneously.     

Thermoeletrochemical study on LiNi<Subscript>0.8</Subscript>Co<Subscript>0.1</Subscript>Mn<Subscript>0.1</Subscript>O<Subscript>2</Subscript> with in situ modification of Li<Subscript>2</Subscript>ZrO<Subscript>3</Subscript>

To improve the electrochemical performance of Nickel-rich cathode material LiNi_0.8Co_0.1Mn_0.1O₂, an in situ coating technique with Li₂ZrO₃ is successfully applied through wet chemical method, and the thermoelectrochemical properties of the coated material at different ambient temperatures and charge-discharge rates are investigated by electrochemical-calorimetric method. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) tests demonstrate that the Li₂ZrO₃ coating decreases the electrode polarizatoin and reduces the charge transfer resistance of the material during cycling. Moreover, it is found that with the ambient temperatures and charge-discharge rates increase, the specific capacity decreases, the amount of heat increases, and the enthalpy change (ΔH) increases. The specific capacity of the cells at 30 °C are 203.8, 197.4, 184.0, and 174.5 mAh g^?1 at 0.2, 0.5, 1.0, and 2.0 C, respectively. Under the same rate (2.0 C), the amounts of heat of the cells are 381.64, 645.32, and 710.34 mJ at 30, 40, and 50 °C. These results indicate that Li₂ZrO₃ coating plays an important role to enhance the electrochemical performance of LiNi_0.8Co_0.1Mn_0.1O₂ and reveal that choosing suitable temperature and current is critical for solving battery safety problem.     

CeO<Subscript>2</Subscript> coating to improve the performance of Li[Li<Subscript>0.2</Subscript>Mn<Subscript>0.54</Subscript>Ni<Subscript>0.13</Subscript>Co<Subscript>0.13</Subscript>]O<Subscript>2</Subscript>

The Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂ coated with CeO₂ has been fabricated by an ionic interfusion method. Both the bare and the CeO₂-coated samples have a typical layered structure with R-3m and C2/m space group. The results of XRD and TEM images display that the CeO₂ coating layer on the precursor could enhance the growth of electrochemically active surface planes ((010), (110), and (100) planes) in the following ionic interfusion process. The results of galvanostatic cycling tests demonstrate that the CeO₂-coated sample has a discharge capacity of 261.81 mAh g^?1 with an increased initial Coulombic efficiency from 62.4 to 69.1% at 0.05 °C compared with that of bare sample and delivers an improved capacity retention from 71.7 to 83.4% after 100 cycles at 1 °C (1 °C?=?250 mA g^?1). The results of electrochemical performances confirm that the surface modification sample exhibits less capacity fading, lower voltage decay, and less polarization.     

Effects of different precipitants on LiNi<Subscript>0.5</Subscript>Mn<Subscript>1.5</Subscript>O<Subscript>4</Subscript> for lithium ion batteries prepared by modified co-precipitation method

Effects of two different precipitants of Na₂CO₃ and Na₂C₂O₄ on LiNi_0.5Mn_1.5O₄ (LNMO) cathode materials, which are prepared by a modified co-precipitation method, have been investigated. Various measurements have been applied to characterize the physical and electrochemical performances of LNMO. Compared with the LNMO prepared by the oxalate co-precipitation (LNMO2), the material synthesized by the carbonate co-precipitation (LNMO1) not only shows more uniform porosity and smaller particles but also has a better rate capability and cycling performance. In addition, the sample prepared by carbonate has a stable spherical structure, due to the fact that carbonate co-precipitation with less gas release during calcination can prevent the destruction of the as-prepared LNMO material structure and promote the formation of regular particle and aperture. Based on the electrochemical test results, LNMO1 shows greatly enhanced electrochemical performance of a high initial discharge capacity of 125.6 mAh g^?1 at 0.25 °C, as well as a preferably capacity retention of 96.5% after 100 cycles at 0.5 °C. And even at a high rate of 10 °C, the discharge capacity of LNMO1-based cell still approaches 83.1 mAh g^?1.     

Improved electrochemical performance of Li<Subscript>1.2</Subscript>Ni<Subscript>0.2</Subscript>Mn<Subscript>0.6</Subscript>O<Subscript>2</Subscript> cathode material with fast ionic conductor Li<Subscript>3</Subscript>VO<Subscript>4</Subscript> coating

Layered lithium-enriched nickel manganese oxides Li_1.2Ni_0.2Mn_0.6O₂ have been synthesized and coated by fast ionic conductor Li₃VO₄ with varying amounts (1, 3, and 5 wt%) in this paper. The effect of Li₃VO₄ on the physical and electrochemical properties of Li_1.2Ni_0.2Mn_0.6O₂ has been discussed through the characterizations of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM), discharge, cyclic performance, rate capability, and electrochemical impedance spectroscopy (EIS). The discharge capacity and coulomb efficiency of Li_1.2Ni_0.2Mn_0.6O₂ in the first cycle have been improved after Li₃VO₄ coating. And, the 3 wt% Li₃VO₄-coated Li_1.2Ni_0.2Mn_0.6O₂ shows the best discharge capacity (246.8 mAh g^?1), capacity retention (97.3 % for 50 cycles), and rate capability (90.4 mAh g^?1 at 10 C). Electrochemical impedance spectroscopy (EIS) results show that the R _ct of Li_1.2Ni_0.2Mn_0.6O₂ electrode decreases after Li₃VO₄ coating, which is due to high lithium ion diffusion coefficient of Li₃VO₄, is responsible for superior rate capability.     

Elevated electrochemical property of LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> originated from nano-sized Mn<Subscript>3</Subscript>O<Subscript>4</Subscript>

By employment of nano-sized pre-prepared Mn₃O₄ as precursor, LiMn₂O₄ particles have been successfully prepared by facile solid state method and sol-gel route, respectively. And the reaction mechanism of the used precursors of Mn₃O₄ is studied. The structure, morphology, and element distribution of the as-synthesized LiMn₂O₄ samples are characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Compared with LiMn₂O₄ synthesized by facile solid state method (SS-LMO), LiMn₂O₄ synthesized by modified sol-gel route (SG-LMO) possesses higher crystallinity, smaller average particle size (~175 nm), higher lithium chemical diffusion coefficient (1.17 × 10^?11 cm² s^?1), as well as superior electrochemical performance. For example, the cell based on SG-LMO can deliver a capacity of 85.5 mAh g^?1 at a high rate of 5 °C, and manifests 88.3% capacity retention after 100 cycles at 0.5 °C when cycling at 45 °C. The good electrochemical performance of the cell based on SG-LMO is ascribed mainly to its small particle size, high degree of dispersion, and uniform element distribution in bulk material. In addition, the lower polarization potential accelerates Li⁺ ion migration, and the lower atom location confused degree maintains integrity of crystal structure, both of which can effectively improve the rate capability and cyclability of SG-LMO.     

Improvement in rate capability of lithium-rich cathode material Li[Li<Subscript>0.2</Subscript>Ni<Subscript>0.13</Subscript>Co<Subscript>0.13</Subscript>Mn<Subscript>0.54</Subscript>]O<Subscript>2</Subscript> by Mo substitution

Lithium-rich cathode material Li[Li_0.2Ni_0.13Co_0.13Mn_0.54]O₂ doped with trace Mo is successfully synthesized by a sol-gel method. The X-ray diffraction patterns show that trace Mo substitution increases the inter-layer space of the material, of which is benefiting to lithium ion insertion/extraction among the electrode materials. The (CV) tests demonstrate the decrease of polarization, and on the other hand, the lithium ion diffusion coefficient (D _Li) of the modified material turns out to be larger, which indicates a faster electrochemical process. As a result, the Mo doped material possesses high rate performance and good cycling stability, and the initial discharge capacity reaches 149.3 mAh g^?1 at a current density of 5.0 °C, and the residual capacity is 144.0 mAh g^?1 after 50 cycles with capacity retention of 96.5 % in the potential range of 2.0–4.8 V at room temperature.     

Fabrication and electrochemical investigation of Li<Subscript>0.5</Subscript>TiO<Subscript>2</Subscript> as anode materials for lithium ion batteries

Hexagonal and cubic Li_0.5TiO₂ particles have been fabricated through magnesiothermic reduction of Li₂TiO₃ particles in a temperature range of 600 to 640 °C. The prolonged reduction time results in lattice transition from hexagonal to cubic structure of Li_0.5TiO₂. Their microstructures, valance state, chemical composition, as well as electrochemical performance as anode candidates for lithium ion batteries have been characterized and evaluated. The hexagonal Li_0.5TiO₂ exhibits better electrochemical activity compared with the cubic one. Further, the carbon-coated hexagonal Li_0.5TiO₂ displays improved electrochemical performance with initial reversible capacity of 176.6 mAh g^?1 and excellent cyclic behavior except capacity fading in the initial 10 cycles, which demonstrate a novel anode candidate for long lifetime lithium ion batteries.     

Enhanced electrochemical performance of Cu<Subscript>2</Subscript>O-modified Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript> anode material for lithium-ion batteries

Li₄Ti₅O₁₂/Cu₂O composite was prepared by ball milling Li₄Ti₅O₁₂ and Cu₂O with further heat treatment. The structure and electrochemical performance of the composite were investigated via X-ray diffraction, scanning electron microscopy, energy-dispersive spectroscopy, cyclic voltammetry, electrochemical impedance spectroscopy, and galvanostatic charge–discharge tests. Li₄Ti₅O₁₂/Cu₂O composite exhibited much better rate capability and capacity performance than pristine Li₄Ti₅O₁₂. The discharge capacity of the composite at 2 C rate reached up to 122.4 mAh g^?1 after 300 cycles with capacity retention of 91.3 %, which was significantly higher than that of the pristine Li₄Ti₅O₁₂ (89.6 mAh g^?1). The improvement can be ascribed to the Cu₂O modification. In addition, Cu₂O modification plays an important role in reducing the total resistance of the cell, which has been demonstrated by the electrochemical impedance spectroscopy analysis.     

Investigation of the structural and electrochemical performance of Li<Subscript>1.2</Subscript>Ni<Subscript>0.2</Subscript>Mn<Subscript>0.6</Subscript>O<Subscript>2</Subscript> with Cr doping

Cr-doped layered oxides Li[Li_0.2Ni_0.2???x Mn_0.6???x Cr_2x ]O₂ (x?=?0, 0.02, 0.04, 0.06) were synthesized by co-precipitation and high-temperature solid-state reaction. The materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (TRTEM), X-ray photoelectron spectroscopy (XPS), and electrochemical impedance spectroscopy (EIS). XRD patterns and HRTEM results indicate that the pristine and Cr-doped Li_1.2Ni_0.2Mn_0.6O₂ show the layered phase. The Li_1.2Ni_0.16Mn_0.56Cr_0.08O₂ shows the best electrochemical properties. The first discharge specific capacity of Li_1.2Ni_0.16Mn_0.56Cr_0.08O₂ is 249.6 mA h g^?1 at 0.1 C, while that of Li_1.2Ni_0.2Mn_0.6O₂ is 230.4 mA h g^?1. The capacity retaining ratio of Li_1.2Ni_0.16Mn_0.56Cr_0.08O₂ is 97.9% compared with 93.9% for Li_1.2Ni_0.2Mn_0.6O₂ after 80 cycles at 0.2 C. The discharge capacity of Li_1.2Ni_0.16Mn_0.56Cr_0.08O₂ is 126.2 mA h g^?1 at 5.0 C, while that of the pristine Li_1.2Ni_0.2Mn_0.6O₂ is about 94.5 mA h g^?1. XPS results show that the content of Mn³⁺ in the Li_1.2Ni_0.2Mn_0.6O₂ can be restrained after Cr doping during the cycling, which results in restraining formation of spinel-like structure and better midpoint voltages. The lithium-ion diffusion coefficient and electronic conductivity of Li_1.2Ni_0.2Mn_0.6O₂ are enhanced after Cr doping, which is responsible for the improved rate performance of Li_1.2Ni_0.16Mn_0.56Cr_0.08O₂.     

Synthesis and electrochemical performance of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>/C by organic solvent replacement drying method

A series of Li₃V₂(PO₄)₃/C composite cathodes have been prepared by the organic solvent replacement drying method. Five kinds of organic solvent including ethyl alcohol, butyl alcohol, 2-methoxyethanol, 1,2-propylene glycol, and ethylene glycol were used in the drying process to replace the water respectively. Powder X-ray diffraction (XRD), scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS), and galvanostatic charge-discharge tests were employed to analyze the crystal structure, morphology, and electrochemical properties of the as-prepared materials. The results show that the organic solvent has a great influence on the secondary particle size of the as-synthesized materials. Special emphasis is placed on the sample prepared with 1,2-propylene glycol, which has the smallest average particle size and uniform distribution, thus leading to the best high rate performance and long-term cycling stability. The electrode exhibits average specific discharge capacities of 127.6, 128.3, 127.7, 126.7, 125.5, 124.4, 121.9, and 117.0 mAh g^?1 at 0.1, 0.2, 0.5, 1, 3, 5, 10, and 20C, respectively. More encouragingly, this sample delivers an outstanding cycle life with capacity retention of up to 94.68% even after 1000 cycles at 20C. Moreover, EIS results demonstrate that this sample has the minimum resistance and the largest apparent lithium ion diffusion coefficient (1.569 × 10^?7 cm² s^?1) which can facilitate to the Li⁺ diffusion during the charge/discharge process. Our results indicate that this preparation strategy can be facile and versatile for the synthesis of other high-rate and high-capacity intercalation materials.     

Investigation on lithium ion conductivity and structural stability of yttrium-substituted Li<Subscript>7</Subscript>La<Subscript>3</Subscript>Zr<Subscript>2</Subscript>O<Subscript>12</Subscript>

Advanced Li-air battery architecture demands a high Li⁺ conductive solid electrolyte membrane that is electrochemically stable against metallic lithium and aqueous electrolyte. In this work, an investigation has been carried out on the microstructure, Li⁺ conduction behaviour and structural stability of Li₇La_3-x Y _x Zr₂O₁₂ (x = 0.125, 0.25 and 0.50) prepared by conventional solid-state reaction technique. The phase analysis of Li₇La_3-x Y _x Zr₂O₁₂ (x = 0.125, 0.25 and 0.50) sintered at 1200 °C by powder X-ray diffraction (PXRD) and Raman confirms the formation of high Li⁺ conductive cubic phase (\( Ia\overline{3}d \)) lithium garnets. Among the investigated lithium garnets, Li₇La_2.75Y_0.25Zr₂O₁₂ sintered at 1200 °C exhibits a maximized room temperature total (bulk + grain boundary) Li⁺ conductivity of 3.21 × 10^?4 S cm^?1 along with improved relative density of 96 %. The preliminary investigation on the structural stability of Li₇La_2.75Y_0.25Zr₂O₁₂ in the solutions of 1 M LiCl, dist. H₂O and 1 M LiOH at 30 °C/50 °C indicates that the Li₇La_2.75Y_0.25Zr₂O₁₂ is relatively stable against 1 M LiCl and dist. H₂O. Further electrochemical investigation is essential for practical application of Li₇La_2.75Y_0.25Zr₂O₁₂ as protective solid electrolyte membrane in aqueous Li-air battery.     

Improving the electrochemical performance of Li-rich Li<Subscript>1.2</Subscript>Ni<Subscript>0.13</Subscript>Co<Subscript>0.13</Subscript>Mn<Subscript>0.54</Subscript>O<Subscript>2</Subscript> cathode material by LiF coating

To suppress the capacity fade of Li-rich Li_1.2Ni_0.13Co_0.13Mn_0.54O₂ material as cathode materials for lithium-ion battery, we introduce a LiF coating layer on the surface to improve the cycling performance of Li_1.2Ni_0.13Co_0.13Mn_0.54O₂ material. The modified sample shows a capacity of 163.2 mAh g^?1 with a capacity retention of 95% after 100 cycles at a current density of 250 mA g^?1, while the pristine sample only delivers a capacity of 129.9 mAh g^?1 with a capacity retention of 82%. Compared with the pristine material, the LiF-modified sample exhibits an obvious enhancement in the electrochemical performance, which will be very beneficial for this material to be commercialized on the new energy vehicles and other related areas.     

Electrochemical comparison of LiFe<Subscript>0.4</Subscript>Mn<Subscript>0.595</Subscript>Cr<Subscript>0.005</Subscript>PO<Subscript>4</Subscript>/C and LiMnPO<Subscript>4</Subscript>/C cathode materials

A comparison of electrochemical performance between LiFe_0.4Mn_0.595Cr_0.005PO₄/C and LiMnPO₄/C cathode materials was conducted in this paper. The cathode samples were synthesized by a nano-milling-assisted solid-state process using caramel as carbon sources. The prepared samples were investigated by XRD, SEM, TEM, energy-dispersive X-ray spectroscopy (EDAX), powder conductivity test (PCT), carbon-sulfur analysis, electrochemical impedance spectroscopy (EIS), and galvanostatic charge-discharge cycling. The results showed that LiFe_0.4Mn_0.595Cr_0.005PO₄/C exhibited high specific capacity and high energy density. The initial discharge capacity of LiFe_0.4Mn_0.595Cr_0.005PO₄/C was 163.6 mAh g^?1 at 0.1C (1C = 160 mA g^?1), compared to 112.3 mAh g^?1 for LiMnPO₄/C. Moreover, the Fe/Cr-substituted sample showed good cycle stability and rate performance. The capacity retention of LiFe_0.4Mn_0.595Cr_0.005PO₄/C was 98.84 % over 100 charge-discharge cycles, while it was only 86.64 % for the pristine LiMnPO₄/C. These results indicated that Fe/Cr substitution enhanced the electronic conductivity for the prepared sample and facilitated the Li⁺ diffusion in the structure. Furthermore, LiFe_0.4Mn_0.595Cr_0.005PO₄/C composite presented high energy density (606 Wh kg^?1) and high power density (574 W kg^?1), thus suggested great potential application in lithium ion batteries (LIBs).