Molecular‐Level Understanding of the Photocatalytic Activity Difference between Anatase and Rutile Nanoparticles

The generation of oxidants on illuminated photocatalysts and their participation in subsequent reactions are the main basis of the widely investigated photocatalytic processes for environmental remediation and selective oxidation. Here, the generation and the subsequent diffusion of ^.OH from the illuminated TiO₂ surface to the solution bulk were directly observed using a single‐molecule detection method and this molecular phenomenon could explain the different macroscopic behavior of anatase and rutile in photocatalysis. The mobile ^.OH is generated on anatase but not on rutile. Therefore, the photocatalytic oxidation on rutile is limited to adsorbed substrates whereas that on anatase is more facile and versatile owing to the presence of mobile ^.OH. The ability of anatase to generate mobile ^.OH is proposed as a previously unrecognized key factor that explains the common observations that anatase has higher activity than rutile for many photooxidative reactions.     

Preparation of nanocrystalline TiO<Subscript>2</Subscript> powders for photocatalytic oxidation of phenol

Nanocrystalline TiO₂ powders in the anatase, rutile, and mixed phases prepared by hydrolysis of TiCl₄ solution were of ultrafine size (<7.2 nm) with high specific surface areas in the range 167 to 388 m²/g. In the photocatalytic degradation of phenol as model reaction, the photocatalytic properties of TiO₂ nanoparticles were evaluated by use of UV–vis absorption spectroscopy and total organic carbon (TOC) content. The synthetic mixed-phase TiO₂ powder calcined at 400 °C had higher activity than pure anatase or rutile; it degraded more than 90% phenol to CO₂ (evaluated by TOC) after irradiation with near UV light for 90 min at a catalyst loading of 0.4 g/L. The TOC results indicated that rutile TiO₂ crystallites of particle size 7.2 nm resulted in much better photocatalytic performance than particles of larger size. This result suggested that some intermediates, not determined by UV–vis absorption spectroscopy, existed in the solution after the photocatalytic process over the rutile TiO₂ photocatalysts of larger crystallite size.     

Degradation of ofloxacin by UVA-LED/TiO<Subscript>2</Subscript> nanotube arrays photocatalytic fuel cells

The degradation of ofloxacin (OFX) at low concentration in aqueous solution by UVA-LED/TiO₂ nanotube arrays photocatalytic fuel cells (UVA-LED/TiO₂ NTs PFCs) was investigated. TiO₂ nanotube arrays (TiO₂ NTs) photoanode prepared by anodization-constituted anatase–rutile bicrystalline framework. The results indicated that the degradation efficiency of OFX by UVA-LED/TiO₂ NTs PFC was significantly enhanced by 14.3% compared with UVA-LED/TiO₂ NTs photocatalysis. The pH affected the degradation efficiency markedly; the highest degradation efficiency (95.0%) and the pseudo-first-order reaction rate constant k value (0.049 min^?1) were achieved in neutral condition (pH 7.0). The degradation efficiency increased with the increasing concentration of dissolved oxygen (DO) in the UVA-LED/TiO₂ NTs PFC. The main reactive species of OFX degradation are positive holes (h⁺) and superoxide ion radicals (O ₂ ^·? ) in a DO sufficient condition. Furthermore, the possible pathways of OFX degradation were proposed.     

Preparation of TiO2 nano-particle photocatalysts by a multi-gelation method: the effect of pH change

TiO₂ photocatalysts were prepared by a multi-gelation method and the effect of the changes in the pH during the pH swing times, i.e., by a controlled pH swing, on the morphology of the TiO₂ particles was investigated. The photocatalytic properties of the TiO₂ catalysts prepared by controlled pH swing were compared with TiO₂ particles prepared without adjusting the pH during the swing times. The photocatalytic degradation reaction of these TiO₂ catalysts was investigated by comparing their effectiveness in 2-propanol oxidation. The experimental results showed that the TiO₂ photocatalysts prepared without adjusting the pH performed better in controlling the important parameters of the catalysts such as particle size, surface area, anatase/rutile phase ratio and pore size, as well as pore volume than the TiO₂ photocatalysts prepared by a controlled pH swing method. Deceased.     

SnO2/TiO2纳米管复合光催化剂的性能及失活再生

基于微波水热法和微乳液法合成SnO₂/TiO₂纳米管复合光催化剂. 通过X射线衍射（XRD）、配有能量色散X射线光谱仪（EDX）的透射电镜（TEM）和电化学手段对光催化剂进行表征. 以甲苯为模型污染物,考察光催化剂在紫外光（UV）和真空远紫外光（VUV）下的性能及失活再生. 结果表明,SnO₂/TiO₂纳米管复合光催化剂形成三元异质结（锐钛矿相TiO₂（A-TiO₂）/金红石相TiO₂（R-TiO₂）、A-TiO₂/SnO₂和R-TiO₂/SnO₂异质结）,促使光生电子-空穴对的有效分离,提高光催化活性. SnO₂/TiO₂表现出最佳的光催化性能,UV和VUV条件下的甲苯降解率均达100%,CO₂生成速率（k₂）均为P25的3倍左右. 但由于UV光照矿化能力不足,中间产物易在催化剂表面累积. 随着UV光照时间的增加,SnO₂/TiO₂逐渐失活,20 h 后k₂由138.5 mg·m^-3·h^-1下降到76.1 mg·m^-3·h^-1. 利用VUV再生失活的SnO₂/TiO₂,过程中产生的·OH、O₂^-·、O（¹D）、O（³P）、O₃等活性物质可氧化吸附于催化剂活性位的难降解中间产物,使催化剂得以再生,12 h后k₂恢复到143.6 mg·m^-3·h^-1. UV和VUV的协同效应使UV降解耦合VUV再生成为一种可持续的光催化降解污染物模式.     

Selective dissolution of TiO2 crystalline phases: Physicochemical characterization and photocatalytic activity

In this study, different commercially available TiO₂ powders (Degussa P25, pure anatase, and rutile) were submitted to selective dissolution treatments, with H₂O₂/NH₄OH and 10% HF, known to remove rutile and anatase from physical mixtures. The aim was to check whether a particular separation method designed to remove a specific crystalline phase influences the properties of the other phase from the mixture or not. More precisely, we have studied how the HF dissolution method designed to selectively remove the anatase affected the physicochemical and photocatalytic properties of rutile. In a similar way, the changes in the anatase properties were studied, after the H₂O₂/NH₄OH treatment, initially used to remove rutile from the mixture. All the samples were characterized by X-ray diffraction, nitrogen adsorption–desorption, transmission electron microscopy, diffuse reflectance (DR) ultraviolet–visible, and Raman spectroscopy. The photocatalytic activity of these powders was tested in the oxidation of p-chlorophenol from water. The selective treatment methods not only dissolved the target phase but also changed some physicochemical and the photocatalytic performances of the other TiO₂ crystalline phase in a considerable manner. These aspects should be taken into account in the studies regarding the synergistic effects of anatase and rutile, especially in reconstructed TiO₂ photocatalysts.     

High temperature stability and photocatalytic activity of nanocrystalline anatase powders with Zr and Si co-dopants

TiO₂ nanopowders doped by Si and Zr were prepared by sol–gel method. The effects of Si and Zr doping on the structural, optical, and photo-catalytic properties of titania nanopowders have been studied by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy, and UV–Vis absorption spectroscopy. XRD results suggest that adding impurities has a significant effect on anatase phase stability, crystallinity, and particle size of TiO₂. Titania rutile phase formation in ternary system (Ti–Si–Zr) was inhibited by Zr⁴⁺ and Si⁴⁺ co-doped TiO₂ in high temperatures (500–900 °C) and 36 mol% anatase composition is retained even after calcination at 1,000 °C. The photocatalyst activity was evaluated by photocatalytic degradation kinetics of aqueous methylen orange under visible radiation. The results show that the photocatalytic activity of the 20 %Si and 15 %Zr co-doped TiO₂ nanopowders have a larger degradation efficiency than pure TiO₂ under visible light.     

Synthesis of Mixed-Phase TiO<Subscript>2</Subscript> Nanopowders Using Atmospheric Pressure Plasma Jet Driven by Dual-Frequency Power Sources

Mixed-phase TiO₂ nanopowders with different ratios of anatase and rutile have been successfully synthesized using atmospheric pressure plasma jet driven by dual-frequency power sources. The crystal structures of the TiO₂ nanopowders were characterized by X-ray diffraction, SAED, HRTEM, and Raman shift spectroscopy. These results indicated that samples possessed anatase and rutile structure, in addition, the crystallinity of the TiO₂ nanopowders increased and the chlorine contamination decreased with discharge RF power increasing. The photocatalytic activity of the TiO₂ nanopowders was evaluated by decomposition methylene blue solution. The TiO₂ nanopowders which were produced at the discharge RF power of 110 W had the highest photocatalytic activity. Optical emission spectroscopy (OES) was used to detect various excited species in the plasma jet. The results indicate that the various RF power significantly changes the intensities of emission lines (Ar, Ar⁺, Ti, Ti⁺, Ti²⁺, Ti³⁺ and O), which results in the TiO₂ nanopowders a mixture of anatase and rutile phases. The nonequilibrium chemical composition could be formed in one step without anneal. It may have potential applications for synthesizing nanosized particles of high crystallinity by reactive nonthermal plasma processing.     

An ambient temperature aqueous sol–gel processing of efficient nanocrystalline doped TiO2-based photocatalysts for the degradation of organic pollutants

An environmentally-friendly aqueous sol–gel process for producing undoped and Cu²⁺, Ni²⁺, Zn²⁺ or Pb²⁺-doped TiO₂ photocatalysts exhibiting a remarkably high photocatalytic activity without requiring any calcination step has been developed. The physicochemical properties of the catalysts were characterized by ICP-AES, XRD, UV–Vis spectroscopy and nitrogen adsorption–desorption. It has been found that the catalysts are composed of nanocrystallites of anatase with a size of 6–7 nm and a specific surface area varying from 184 to 275 m² g^?1. A screening of the photocatalytic activity of the undoped and doped photocatalysts has been performed by evaluating the degradation of 4-nitrophenol under artificial light (330 nm < λ < 800 nm) after 7 h of illumination using a custom-designed multisample photoreactor. The activity measured for the TiO₂-Undoped catalyst was found to be five times higher than the activity measured for uncalcined TiO₂ catalysts produced by other sol–gel methods. We propose that this interesting result is due to the particular morphology of the xerogels obtained. It has also been demonstrated that the presence of the dopant leads to an enhancement of the photocatalytic activity in all cases. The role of particular dopants in modulating the photocatalytic activity will be discussed. Finally, the possibility of producing undoped and Zn²⁺-doped films presenting a higher activity than the commercial photocatalytic coating (Saint Gobain Glass Bioclean^®) without requiring any calcination step has been demonstrated. These preliminary results constitute an important step forward in the development of photocatalytic films using a sol–gel process compatible with the constraints associated with large-scale industrial processing.     

Effective synthesis of nanoscale anatase TiO2 single crystals using activated carbon template to enhance the photodegradation of crystal violet

Nanoscale anatase TiO₂ single crystals were successfully synthesized using three kinds of activated carbon (AC) templates through a simple sol–gel method. The optimal photocatalyst (T‐WOAC) was obtained using wood‐based AC template. X‐ray diffraction, transmission electron microscopy and Brunauer–Emmett–Teller analyses revealed that T‐WOAC possessed a small crystallite size of 8.7 nm and a clear mesoporous structure. The photocatalytic properties of samples were then evaluated through photodegradation of crystal violet (CV). Results implied that the photocatalysts prepared using the AC templates exhibited superior photocatalytic activity to that of the original TiO₂. This enhancement may be due to the small crystallite size, large specific surface area and pore volume of the catalysts prepared with ACs. T‐WOAC showed high photocatalytic activity, CV degradation of 99.01% after 120 min of irradiation and k = 0.03914 min^?1, which is 3.9 times higher than that of the original TiO₂ (k = 0.00994 min^?1). This result can be mainly attributed to the application of WOAC with moderate specific surface area and pore volume to produce T‐WOAC. Alkaline conditions benefitted the photodegradation of CV over photocatalysts. This work proposes a possible degradation mechanism of CV and indicates that the fabricated photocatalysts can be used to effectively remove CV from aqueous solutions.     

Synthesis of iron-containing nitrogen-doped titania by hydrothermal method and its photocatalytic activity

By a hydrothermal method, iron and nitrogen co-doped TiO₂ and iron oxide impregnated nitrogen-doped TiO₂ were prepared. The obtained Fe and N co-doped TiO₂ showed mixed anatase, rutile, and brookite phases, and high specific surface areas above 160 m²/g. The Fe co-doping was proved to be effective to enhance the visible light absorption ability; however, the photocatalytic activity in deNO _x experiment decreased due to the increase in the amount of lattice vacancy. On the other hand, the photocatalytic activity of N-doped TiO₂ was improved by the impregnation of iron oxide.     

Synthesis of anatase TiO2 in a vinyl-containing ionic liquid and its enhanced photocatalytic activity

TiO₂ microspheres were synthesized by the sol–gel method using the ionic liquid (IL) 1-vinyl-3-propylimidazolium iodide (VPIM⁺I^?) as a reaction medium, then calcined at 500 °C. The samples were characterized by X-ray diffraction, scanning electron microscopy, and ultraviolet–visible (UV–Vis) diffuse reflectance spectroscopy. The phase of TiO₂ microspheres is anatase, and VPIM⁺I^? is able to favor the growth of anatase phase and prevents the collapse of small pores. The photocatalytic activity of TiO₂-IL was tested by degradation of 2-nitrophenol under UV light illumination. The photocatalytic activity of TiO₂-IL was higher than that of samples prepared in the reaction medium without VPIM⁺I^?.     

Structural characterization of Fe/Ti oxide photocatalysts by X-ray,ESR, and Mössbauer methods

The polycrystalline solids TiO₂Fe₂O₃, with iron contents in the range 0–10 at.%, prepared by coprecipitation and by impregnation, and treated in air at temperatures in the range 500–1000°C, have been studied by X-ray, ESR, and Mössbauer methods. The TiO₂ in the samples treated at 800 and 1000°C always forms the rutile phase and the Fe³⁺ has a rather low solubility in it (～0.1 at.%). The Fe³⁺ in excess forms the antiferromagnetic pseudobrookite phase (Fe₂TiO₅). The samples treated at 500 and 650°C show a dependence on the preparation method. Those prepared by coprecipitation give at 500°C the pure anatase phase in which the Fe³⁺ has a higher solubility (≥ 1%); those prepared by impregnation give the anatase phase accompanied by a variable amount of rutile. The treatment at 650°C provokes the partial transformation of anatase to rutile and the complete development of the Fe₂TiO₅ phase. The relevance of these results to the photocatalytic properties shown by these solids for the photoreduction of dinitrogen to ammonia is discussed.     

Study on the formation of H2O2 on TiO2 photocatalysts and their activity for the photocatalytic degradation of X-GL dye

Titanium dioxide (TiO₂) nanoparticles of both anatase and rutile phases were synthesized by hydrothermal treatment of microemulsions, and their photocatalytic activity for the degradation of X-GL dye was investigated. The only difference between the two methods used was that different acids were added to the microemulsions to make a direct comparison of the photocatalytic activity of the polymorphs possible. UV — Vis reflectance and XRD spectroscopic investigations of these titanium dioxides indicated that a rutile structure could be formed (PR) when hydrochloric acid was used, and anatase formed (PA) when nitric acid was used. The activity of the two polymorphs and P-25 for the photocatalytic degradation of dye in water was also examined. It was found that P-25 consisting of anatase and rutile has the highest activity, and PR consisting of rutile has the lowest. Photodegradation of X-GL in the presence of these different TiO₂ particles under air-equilibrated controlled conditions led to the formation of hydrogen peroxide. The formation rate of H₂O₂ depended on the difference in crystalloid phase. These results indicate that the observed differences in the photocatalytic activity for the three TiO₂ photocatalysts are directly related to the formation rate of H₂O₂.     

原位红外光谱法研究Gd3+掺杂TiO2光催化降解乙烯性能

随着环境污染的日益严重,寻求环境友好、节能、高效的污染治理技术已成为各国科学研究者致力的目标。以TiO2半导体为主的多相光催化氧化技术因与传统污染处理技术相比具有许多优点而倍受青睐,但是,目前以TiO2为基础的光催化技术还存在量子效率低、太阳能利用率低等技术难题[1,2     

Synthesis and characterization of TiO<Subscript>2</Subscript> doping with rare earths by sol–gel method: photocatalytic activity for phenol degradation

The enhancement of TiO₂ photocatalyst activity will lead to more practical applications of this technology. In this work we studied the effect of rare earth doping of sol–gel synthesized TiO₂ for phenol degradation and we compared the performance with commercial catalyst. Photocatalysts were characterized by nitrogen adsorption to determine textural properties, ultraviolet visible light diffuse reflectance spectrometry (UV-Vis DRS), X-ray diffraction, STEM-EDS (scanning transmission electronic microscopy-energy dispersive X-ray spectroscopy) and XPS (X-ray photoelectron spectroscopy). Main phase for materials calcined at 500 °C was anatase. Residual nitrogen from NH₄OH used in the sol–gel synthesis was identified by XPS analysis. Ti³⁺/Ti⁴⁺ ratio increased when TiO₂ was doped with 0.5 wt% of Ce. Anatase phase was stabilized in photocatalysts doped with La even after calcination at 800 °C, for Pr and Nd a mixture of anatase-rutile phases was obtained, whereas for Ce doping only rutile phase was found. For the photocatalytic oxidation of phenol, the best results were obtained for Ce doped TiO₂, which could be related to the ability of Ce^IV/Ce^III oxidation/reduction cycle.     

Polyacrylamide gel synthesis and photocatalytic properties of TiO2 nanoparticles

In this study, a polyacrylamide gel route was introduced to synthesize TiO₂ nanoparticles. The influence of synthesis conditions on the properties of products was investigated. It is found that the samples prepared at the calcination temperature of 400 °C crystallize majorly in the anatase phase with a minor rutile phase. The second rutile phase has a dependence on the chelating agent, which is formed more readily when using acetic acid as the chelating agent. The introduction of acrylamide and glucose to the precursor solution shows the capability of improving the particle morphology, and the resulted particles are uniformly shaped like spheres. The photocatalytic activity of the prepared TiO₂ samples was evaluated by the degradation of acid orange 7 under 254 nm ultraviolet irradiation, revealing that they exhibit a good photocatalytic activity. Ethanol was used as a ^·OH scavenger to investigate its effect on the photocatalytic efficiency as well as the ^·OH radical yields. Based on the experimental results, ^·OH radical is suggested to be the dominant active species responsible for the dye degradation.     

Cooperation among N,F and Fe in tri-doped TiO<Subscript>2</Subscript> photocatalyst

TiO₂ photocatalysts tri-doped with N, F and Fe were synthesized by a sol–gel method. The cooperation of N, F and Fe in tri-doped TiO₂ was verified by monitoring NH₃ decomposition, X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet–visible (UV–Vis) absorption spectroscopy, and by the simulation based on the density functional theory (DFT). The results from NH₃ decomposition revealed that the cooperation of N, F and Fe broadened the optical response of TiO₂ to the visible light range and also enhanced the photocatalytic activity of TiO₂ under UV light. The reusability of the tri-doped TiO₂ sample after three cycles under UV and visible light irradiation was very good. XRD patterns and SEM and HRTEM images indicated that the tri-doped sample was nanometric anatase with a small amount of rutile with an average particle size of 18 nm. Tri-doping with N, F and Fe suppressed the phase transition from anatase to rutile and also resulted in some more lattice defects. XPS analysis showed that the N, F and Fe atoms were doped into the TiO₂ lattice. UV–Vis absorption spectra of the tri-doped TiO₂ showed that its optical absorption edge was moved up to 640 nm and its UV absorption was also enhanced. The DFT results confirmed that the cooperation of Fe 3d and N 2p orbits narrowed the band gap of TiO₂ and the F 2p orbit broadened the upper valence bands. The synergistic electron density around N, F and Fe in tri-doped TiO₂ was capable of enhancing the photochemical stability and reusability of TiO₂.     

Preparation and characterization of sulfonated polyimide/TiO2 composite membrane for vanadium redox flow battery

A sulfonated polyimide (SPI)/TiO₂ composite membrane was fabricated by a blend way to improve its performance in vanadium redox flow battery (VRB). Both EDS and XRD results verify the successful preparation of the SPI/TiO₂ composite membrane. The surface SEM image shows its homogeneous structure. TG analysis identifies its thermal stability. The SPI/TiO₂ composite membrane possesses much lower permeability of VO²⁺ ions (2.02?×?10^?7 cm² min^?1) and favorable proton conductivity (3.12?×?10^?2 S cm^?1). The VRB single cell with SPI/TiO₂ composite membrane shows higher coulombic efficiency (93.80–98.00 %) and energy efficiency (83.20–67.61 %) at the current density ranged from 20 to 80 mA cm^?2 compared with that with Nafion 117 membrane. And the operational stability of the as-prepared composite membrane is good after 50 times of cycling tests. Therefore, the low-cost SPI/TiO₂ composite membrane with excellent battery performance exhibits a great potential for application in VRB.     

Three-phase junction for modulating electron–hole migration in anatase–rutile photocatalysts

The heterophase solid–solid junction as an important type of structure unit has wide applications for its special mechanics and electronic properties. Here we present a first three-phase atomic model for the anatase–rutile TiO₂ heterophase junction and determine its optical and electronic properties, which leads to resolution of the long-standing puzzles on the enhanced photocatalytic activity of anatase–rutile photocatalysts. By using a set of novel theoretical methods, including crystal phase transition pathway sampling, interfacial strain analysis and first principles thermodynamics evaluation of holes and electrons, we identify an unusual structurally ordered three-phase junction, a layer-by-layer “T-shaped” anatase/TiO₂-II/rutile junction, for linking anatase with rutile. The intermediate TiO₂-II phase, although predicted to be only a few atomic layers thick in contact with anatase, is critical to alleviate the interfacial strain and to modulate photoactivity. We demonstrate that the three-phase junction acts as a single-way valve allowing the photogenerated hole transfer from anatase to rutile but frustrating the photoelectron flow in the opposite direction, which otherwise cannot be achieved by an anatase–rutile direct junction. This new model clarifies the roles of anatase, rutile and the phase junction in achieving high photoactivity synergistically and provides the theoretical basis for the design of better photocatalysts by exploiting multi-phase junctions.