Effect of Sodium Alginate on the Properties of Thermosensitive Hydrogels

Sodium alginate (SA ) was combined with poly(N ‐isopropylacrylamide) (PNIPAAm ) to prepare thermosensitive hydrogels through semi‐interpenetrating polymer network (semi‐IPN ) and fully interpenetrating polymer network (full‐IPN ). The thermosensitive, swelling, mechanical, and thermal properties of pure PNIPAAm , SA /PNIPAAm semi‐IPN , and Ca‐alginate/PNIPAAm full‐IPN hydrogels were investigated. The formation of semi‐IPN and full‐IPN significantly improved the hydrogels’ swelling capability and mechanical properties without altering their thermosensitivity. 5‐Fluorouracil (5‐Fu) was selected as a model drug to study the release behaviors of the hydrogels. It was found that in vitro controlled drug release from semi‐IPN hydrogels showed an initial release burst, followed by a slower and sustained release, before reaching equilibrium. Full‐IPN hydrogels showed slow and sustained release during the whole process. Temperature and pH were found to affect the rate of drug release. Ca‐alginate/PNIPAAm full‐IPN hydrogels have potential application as drug delivery matrices in controlled drug release.     

Interpenetrating thermophobic and thermophilic dual responsive networks

Poly(N‐acryloyl glycinamide) (PNAGA)/poly(N‐isopropyl acrylamide) (PNIPAAm) interpenetrating network (IPN) hydrogels were made by UV‐light initiated radical polymerization in two‐steps. The IPN hydrogels showed a double thermoresponsive behavior due to the combination of PNIPAAm (thermophobic) and PNAGA (thermophilic) networks. Increasing the content of the thermophobic PNIPAAm network leads to a change from a broad thermophilic volume phase transition temperature of PNAGA to a thermophilic–thermophobic‐type dual transition for the prepared IPN. Due to the double thermoresponsive character of the IPN gels, the mechanical properties are dependent upon temperature as demonstrated by performing tensile tests in water at 15 and 50 °C. Furthermore, the IPN hydrogels were characterized using turbidity measurements, SEM, and the determination of the equilibrium swelling ratio. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019 , 57, 539–544     

Investigation of swelling,drug release and diffusion behaviors of poly(N‐isopropylacrylamide)/poly (N‐vinylpyrrolidone) full‐IPN hydrogels

The synthesis of sequential full interpenetrating polymer networks (IPNs) based on poly (N‐isopropylacrylamide) (PNIPAAm) and negatively charged poly(N‐vinyl‐2‐pyrrolidone) (PNVP) was described and their swelling, drug release, and diffusion studies were investigated. PNIPAAm was used as a host network. According to swelling experiments, IPNs gave relatively lower swelling ratios compared to PNIPAAm hydrogel due to the higher cross‐linking density. Lidocaine (LD) was used as a model drug for the investigation of drug release behavior of IPNs. LD uptake of the IPNs were found to increase from 24 to 166 (mg LD / g dry gel) with increasing amount of PNIPAAm and AMPS contents in the IPN structure. It was observed that the specific interaction between drug and AMPS co‐monomer influenced the drug release profile. In the diffusion transport mechanism study in water, the results indicated that the swelling exponents n for all IPNs are in the range from 0.50 to 0.72. This implies that the swelling transport mechanism was transferred from Fickian to non‐Fickian transport, with increasing AMPS content and NIPAAm character in the IPN structure. In addition, diffusion of LD within the IPNs showed similar trend. The incorporation of AMPS leads to an increase in electrostatic interaction between charge sites on carboxylate ions and cationic LD molecules. Therefore, the highest diffusion coefficient (D) of drug was found for IPN2 sample. Copyright © 2007 John Wiley & Sons, Ltd.     

From poly(N‐isopropylacrylamide)‐block‐poly(ethylene oxide)‐block‐poly(N‐isopropylacrylamide) triblock copolymer to poly(N‐isopropylacrylamide)‐block‐poly(ethylene oxide) hydrogels: Synthesis and rapid deswelling and reswelling behavior of hydrogels

Poly(N‐isopropylacrylamide)‐block‐poly(ethylene oxide)‐block‐poly(N‐isopropylacrylamide) (PNIPAAm‐b‐PEO‐b‐PNIPAAm) triblock copolymer was synthesized via the reversible addition‐fragmentation chain transfer/macromolecular design via the interchange of xanthate (RAFT/MADIX) process with xanthate‐terminated poly(ethylene oxide) (PEO) as the macromolecular chain transfer agent. The successful synthesis of the ABA triblock copolymer inspired the preparation of poly(N‐isopropylacrylamide)‐block‐poly(ethylene oxide) (PNIPAAm‐b‐PEO) copolymer networks with N,N′‐methylenebisacrylamide as the crosslinking agent with the similar approach. With the RAFT/MADIX process, PEO chains were successfully blocked into poly(N‐isopropylacrylamide) (PNIPAAm) networks. The unique architecture of PNIPAAm‐b‐PEO networks allows investigating the effect of the blocked PEO chains on the deswelling and reswelling behavior of PNIPAAm hydrogels. It was found that with the inclusion of PEO chains into the PNIPAAm networks as midblocks, the swelling ratios of the hydrogels were significantly enhanced. Furthermore, the PNIPAAm‐b‐PEO hydrogels displayed faster response to the external temperature changes than the control PNIPAAm hydrogel. The accelerated deswelling and reswelling behaviors have been interpreted based on the formation of PEO microdomains in the PNIPAAm networks, which could act as the hydrophilic tunnels to facilitate the diffusion of water molecules in the PNIPAAm networks. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

New silicone hydrogels based on interpenetrating polymer networks comprising polysiloxane and poly(vinyl alcohol) networks

A method for the synthesis of a new silicone hydrogel as a biphase material for soft contact lenses is considered. The method is based on the synthesis of sequential interpenetrating polymer networks (IPN) and includes the following stages: (1) cross‐linked silicone synthesis by the reaction of vinyl‐ and hydride‐containing oligosiloxanes; (2) silicone network saturation with vinyl acetate and cross‐linking monomer followed by UV‐initiated polymerization to form an IPN comprising the silicone and cross‐linked poly(vinyl acetate) (PVAc) network; (3) PVAc network alcoholysis with methanol to obtain silicone hydrogels comprising the silicone and cross‐linked poly(vinyl alcohol) (PVAl). A study of hydrophilic, optical, mechanical, and structural features of the silicone hydrogels showed that optical transparency is achieved for materials with the highest density of silicone network cross‐linking where the size of IPN structural units does not exceed 100 nm. The water content in hydrophilic networks of silicone hydrogel is found to be below the values typical of cross‐linked PVAl, leading to non‐additivity of IPN mechanical properties. Indeed, the elasticity moduli (E) of the hydrophilic and silicone networks are 0.4–0.7 and 0.7–1.8 MPa, respectively, whereas for some IPN this value reaches 3.0 MPa. The optimal parameters of synthesis providing the reduction of E to 0.8–1.6 MPa without deterioration of the required performance characteristics (optical transparency 90–92%, water content 20–39 wt%) are determined. Copyright © 2009 John Wiley & Sons, Ltd.     

Novel poly(N‐isopropylacrylamide)/clay/poly(acrylamide) IPN hydrogels with the response rate and drug release controlled by clay content

Novel interpenetrating network (IPN) hydrogels (PNIPAAm/clay/PAAm hydrogels) based on poly(N‐isopropylacrylamide) (PNIPAAm) crosslinked by inorganic clay and poly(acrylamide) (PAAm) crosslinked by organic crosslinker were prepared in situ by ultraviolet (UV) irradiation polymerization. The effects of clay content on temperature dependence of equilibrium swelling ratio, deswelling behavior, thermal behavior, and the interior morphology of resultant IPN hydrogels were investigated with the help of Fourier transform infrared spectroscopy, differential scanning calorimeter (DSC), scanning electron microscope (SEM). Study on temperature dependence of equilibrium swelling ratio showed that all IPN hydrogels exhibited temperature‐sensitivity. DSC further revealed that the temperature‐sensitivity was weakened with increasing amount of clay. Study on deswelling behavior revealed that IPN hydrogels had much faster response rate when comparing with PNIPAAm/clay hydrogels, and the response rate of IPN hydrogels could be controlled by clay content. SEM revealed that there existed difference in the interior morphology of IPN hydrogels between 20 [below lower critical solution temperature (LCST)] and 50 °C (above LCST), and this difference would become obvious with a decrease in clay content. For the standpoint of applications, oscillating swelling/deswelling behavior was investigated to determine whether properties of IPN hydrogels would be stable for potential applications. Bovine serum albumin (BSA) was used as model drug for in vitro experiment, the release data suggested that the controlled drug release could be achieved by modulating clay content. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 96–106, 2009     

Porous alginate-Ca hydrogels interpenetrated with PNIPAAm networks: Interrelationship between compressive stress and pore morphology

Thermo-sensitive porous hydrogels composed of interpenetrated networks (IPN) of alginate-Ca²⁺ and PNIPAAm have been obtained. The hydrogels were prepared by cross-linking alginate-Na⁺ with Ca²⁺ ions inside PNIPAAm networks. Compressive tests and scanning electron microscopy were used to evaluate gel strength and pore morphology, respectively. IPN hydrogels displayed two distinct pore morphologies under thermal stimuli. Below 30-35 °C, the LCST of PNIPAAm in water, IPN hydrogels were highly porous. The pore size of hydrogel heated above LCST became progressively smaller. Alginate-Ca²⁺ and PNIPAAm hydrogels, used as references, did not present such behaviour, indicating that the porous effect is due to IPN hydrogel. It was verified that higher strength is achieved when the hydrogel presents small pore size and the temperature is increased. It is suggested that at temperatures above LCST, the PNIPAAm chains shrink and pull the alginate-Ca²⁺ networks back. During shrinking, the polymer chains occupy the open spaces (pores from which water is expelled), and therefore, the hydrogel becomes less deformable when subjected to compressive stress. The results presented in this work indicate that the mechanical properties as well as the pore morphologies of these IPN hydrogels can be tailored by thermal stimulus.     

Dual temperature‐ and pH‐sensitive hydrogels from interpenetrating networks and copolymerization of N‐isopropylacrylamide and sodium acrylate

Hydrogels responsive to both temperature and pH have been synthesized in the forms of sequential interpenetrating networks (IPNs) of N‐isopropylacrylamide (NIPAAm) and sodium acrylate (SA) and compared with the crosslinked random copolymers of N‐isopropylacrylamide and SA. Whereas the stimuli‐sensitive behaviors of copolymer hydrogels were strongly dependent on the ionic SA contents, the IPN hydrogels exhibited independent swelling and thermal behaviors of each network component. The sequences and media in the synthesis of IPNs influenced the swelling capacities of the IPNs, but not the temperature or pH ranges at which the swelling changes occurred. In IPNs, a more expanded primary gel network during the synthesis of the secondary network contributed to the better swelling of the final IPNs. Both the swelling and thermal behaviors of the IPNs suggest that poly(N‐isopropylacrylamide) and poly(sodium acrylate) are phase separated regardless of their synthesis conditions. The presence of the poly(sodium acrylate) network did not influence the temperature or the extent of phase transition of the poly(N‐isopropylacrylamide) network in the IPNs, but did improve the thermal stability of the IPNs. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3293–3301, 2004     

Preparation and properties of poly(N‐isopropylacrylamide)/poly(N‐isopropylacrylamide) interpenetrating polymer networks for drug delivery

A novel poly(N‐isopropylacrylamide) (PNIPA)/PNIPA interpenetrating polymer network (IPN) was synthesized and characterized. In comparison with conventional PNIPA hydrogels, the shrinking rate of the IPN hydrogel increased when gels, swollen at 20 °C, were immersed in 50 °C water. The phase‐transition temperature of the IPN gel remained unchangeable because of the same chemical constituent in the PNIPA gel. The reswelling kinetics were slower than those of the PNIPA hydrogel because of the higher crosslinking density of the IPN hydrogel. The IPN hydrogel had better mechanical strength because of its higher crosslinking density and polymer volume fraction. The release behavior of 5‐fluorouracil (5‐Fu) from the IPN hydrogel showed that, at a lower temperature, the release of 5‐Fu was controlled by the diffusion of water molecules in the gel network. At a higher temperature, 5‐Fu inside the gel could not diffuse into the medium after a burst release caused by the release of the drug on the surface of the gel. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1249–1254, 2004     

Cross‐Linking Density and Temperature Effects on the Self‐Assembly of SiO2—PNIPAAm Core–Shell Particles at Interfaces

SiO₂–PNIPAAm core–shell microgels (PNIPAAm=poly(N‐isopropylacrylamide)) with various internal cross‐linking densities and different degrees of polymerization were prepared in order to investigate the effects of stability, packing, and temperature responsiveness at polar–apolar interfaces. The effects were investigated using interfacial tensiometry, and the particles were visualized by cryo‐scanning electron microscopy (SEM) and scanning force microscopy (SFM). The core–shell particles display different interfacial behaviors depending on the polymer shell thickness and degree of internal cross‐linking. A thicker polymer shell and reduced internal cross‐linking density are more favorable for the stabilization and packing of the particles at oil–water (o/w) interfaces. This was shown qualitatively by SFM of deposited, stabilized emulsion droplets and quantitatively by SFM of particles adsorbed onto a hydrophobic planar silicon dioxide surface, which acted as a model interface system. The temperature responsiveness, which also influences particle–interface interactions, was investigated by dynamic temperature protocols with varied heating rates. These measurements not only showed that the particles had an unusual but very regular and reversible interface stabilization behavior, but also made it possible to assess the nonlinear response of PNIPAAm microgels to external thermal stimuli.     

Using hydrophobic additive as pore‐forming agent to prepare macroporous PNIPAAm hydrogels

Hydrophobic poly(lactic acid) nanospheres were fabricated and used as an additive during the polymerization and gelation process of temperature‐sensitive poly(N‐isopropylacrylamide) (PNIPAAm) hydrogels. The influence of hydrophobic additive on properties of PNIPAAm hydrogels was examined. The interior morphology studied by scanning electron microscopy revealed that the hydrophobic additive induced a macroporous structure in the resulting PNIPAAm hydrogels. Results demonstrate that the hydrophobic additive acts as a pore‐forming agent like conventionally used hydrophilic additive does during the gelation process. Because of the macroporous network and incorporated additives, the temperature‐sensitive characteristics, particularly the equilibrium swelling ratio at room temperature and shrinking rate upon temperature increase of modified PNIPAAm hydrogels, are significantly improved. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5490–5497, 2005     

Dextran Hydrogels Containing Poly(N‐isopropylacrylamide) as Grafts and Cross‐Linkers Exhibiting Enzymatic Regulation in a Specific Temperature Range

Summary: Specific temperature‐responsive biodegradable hydrogels were synthesized and characterized in terms of their regulation of enzymatic accessibility based on the physical properties of the temperature‐responsive polymers. The hydrogels consist of glycidyl methacrylate‐modified dextran grafted with the poly(N‐isopropylacrylamide) (PNIPAAm) homopolymer, and cross‐linked by co‐polymerization with NIPAAm and N,N‐dimethylacrylamide (DMAAm). The coil‐globule change in the grafted poly(NIPAAm) chains and only a slight dehydration of the poly(NIPAAm‐co‐DMAAm) cross‐linkers are effective in controlling the enzymatic degradation over a specific temperature range.

The thermo‐responses of the graft chains (steric hindrance) and the crosslinkers (slight deswelling of the hydrogel networks) control the enzymatic degradation of the hydrogel.     

Fabrication of Silver Nanoparticles in Hydrogel Networks

Summary: This paper describes a simple and facile approach to fabricate well dispersed silver nanoparticles (AgNPs) in poly[N‐isopropylacrylamide‐co‐(sodium acrylate)] hydrogels. The silver nanoparticles formed are spherical in shape with a narrow size distribution in the hydrogel networks in which the nanoparticles are stabilized by the polymer network. Uniformly dispersed silver nanoparticles were obtained with poly[N‐isopropylacrylamide‐co‐[sodium acrylate)] hydrogels, whereas a poly(N‐isopropylacrylamide)/poly(sodium acrylate) IPN gel showed aggregated nanoparticles. It is demonstrated that the hydrogel network structure determines the size and shape of the nanoparticles. These particles are more stable in the gel networks compared to other reduction methods. The hydrogel/silver nanohybrids were well characterized by XRD, UV‐vis spectrometry, scanning electron microscopy and transmission electron microscopy.

Schematic representation of the preparation of Ag nanoparticles in hydrogel networks.     

A simple FTIR spectroscopic method for the determination of the lower critical solution temperature of N‐isopropylacrylamide copolymers and related hydrogels

Linear and crosslinked polymers based on N‐isopropylacrylamide (NIPAAm) exhibit unusual thermal properties. Aqueous solutions of poly(N‐isopropylacrylamide) (PNIPAAm) phase‐separate upon heating above a lower critical solution temperature (LCST), whereas related hydrogels undergo a swelling–shrinking transition at an LCST. A linear copolymer made of NIPAAm/acryloxysuccinimide (98/2 mol/mol) and two hydrogels with different hydrophilicities were prepared. Fourier transform infrared (FTIR) spectroscopy was employed to determine the transition temperature and provide insights into the molecular details of the transition via probing of characteristic bands as a function of temperature. The FTIR spectroscopy method described here allowed the determination of the transition temperature for both the linear and crosslinked polymers. The transition temperatures for PNIPAAm and the gel resulting from the crosslinking with polylysine or N,N′‐methylenebisacrylamide (MBA) were in the same range, 30–35 °C. For the gels, the transition temperature increased with the hydrophilicity of the polymer matrix. The spectral changes observed at the LCST were similar for the free chains and the hydrogels, implying a similar molecular reorganization during the transition. The C H stretching region suggests that the N‐isopropyl groups and the backbone both underwent conformational changes and became more ordered upon heating above the LCST. An analysis of the amide I band suggests that the amide groups of the linear polymer were mainly involved in hydrogen bonding with water molecules below the LCST, the chain being flexible and disordered in a water solution. During the transition, around 20% of these intermolecular hydrogen bonds between the polymer and water were broken and replaced by intramolecular hydrogen bonds. Similar changes were also observed at the LCST of a gel crosslinked with MBA. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 907–915, 2000     

Thermoresponsive Double Network Hydrogels with Exceptional Compressive Mechanical Properties

The utility of thermoresponsive hydrogels, such as those based on poly(N‐isopropylacrylamide) (PNIPAAm), is severely limited by their deficient mechanical properties. In particular, the simultaneous achievement of high strength and stiffness remains unreported. In this work, a thermoresponsive hydrogel is prepared having the unique combination of ultrahigh compressive strength (≈23 MPa) and excellent compressive modulus (≈1.5 MPa). This is accomplished by employing a double network (DN) design comprised of a tightly crosslinked, highly negatively charged 1st network based on poly(2‐acrylamido‐2‐methylpropane sulfonic acid (PAMPS) and a loosely crosslinked, zwitterionic 2nd network based on a copolymer of thermoresponsive NIPAAm and zwitterionic 2‐(methacryloyloxy)ethyl]dimethyl‐(3‐sulfopropyl)ammonium hydroxide (MEDSAH). Comparison to other DN designs reveals that this PAMPS/P(NIPAAm‐co‐MEDSAH) DN hydrogel's remarkable properties stem from the intra‐ and internetwork ionic interactions of the two networks. Finally, this mechanically robust hydrogel retains the desirable thermosensitivity of PNIPAAm hydrogels, exhibiting a volume phase transition temperature of ≈35 °C.     

Dual responsive poly(N‐isopropylacrylamide) hydrogels having spironaphthoxazines as pendant groups

Stimuli responsive hydrogels (PNIPAAm‐MSp) with a thermoresponsive backbone and photochromic pendant groups were synthesized via free radical polymerization using N‐isopropylacrylamide, modified spironaphthoxazines with a polymerizable double bond (MSp) as photochromic monomer, the crosslinker N,N′‐methylenebis(acrylamide) and the initiator 2,2′‐azobis(isobutyronitrile) in dimethylsulfoxide. The polymers are dual responsive, in that poly(N‐isopropylacrylamide) (PNIPAAm) responds to temperature changes whereas the pendant spironaphthoxazines respond to light. Irradiation enhanced the water absorption of the polymers while increases in temperature decreased it. The irradiated PNIPAAm‐MSp showed best water absorption at 0 °C (Q = 3.25) while water desorbed at higher temperatures (35 °C; Q = 0.30); where Q is the amount of water absorbed by a gram of dry polymer. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3318–3325, 2009     

Synthesis and characterization of stimuli‐responsive porous/hollow nanoparticles by self‐assembly of chitosan‐based graft copolymers and application in drug release

In this research, stimuli‐responsive porous/hollow nanoparticles were prepared by the self‐assembly method. First, chitosan‐graft‐poly(N‐isopropylacrylamide) (CS‐g‐PNIPAAm) copolymers were synthesized through polymerization of N‐isopropylacrylamide (NIPAAm) monomer in the presence of chitosan (CS) solution using ceric ammounium nitrate as the initiator. Then, the CS‐g‐PNIPAAm copolymers were dissolved in the acetic acid aqueous solution and heated to 40 °C to induce their self‐assembly. After CS‐g‐PNIPAAm assembled to form micelles, a cross‐linking agent was used to reinforce the structure to form nanoparticles. The molecular weight of grafted PNIPAAm on CS chains was changed to investigate its effect on the structure, morphology, thermo‐, and pH‐responsive properties of the nanoparticles. TEM images showed that a porous or hollow structure in the interior of nanoparticles was developed, depending on the medium temperature. The synthesized nanoparticles carried positive charges on the surface and exhibited stimuli‐responsive properties, and their mean diameter thus could be manipulated by changing the pH value and temperature of the environment. The nanoparticles showed a continuous release of the encapsulated doxycycline hyclate up to 10 days during an in vitro release experiment. These porous/hollow particles with environmentally sensitive properties are expected to be used in hydrophilic drug delivery system. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2377–2387, 2010     

聚丙烯酰胺/聚异丙基丙烯酰胺互穿网络水凝胶的制备与性能

采用分步法用电子加速器辐射合成了聚丙烯酰胺(PAAm)/聚异丙基丙烯酰胺(PNIPAAm)互穿网络水凝胶,并考察了温度、pH值、离子强度对其溶胀性能的影响.研究表明:互穿水凝胶具有温度敏感性,且其体积相变与互穿网络中PAAm和PNIPAAm含量有关,随着网络中PAAm含量的增加水凝胶的体积相变趋于平缓,可以通过改变PAAm和PNIPAAm的组成比来控制水凝胶的体积相变行为.此外,互穿水凝胶还具有pH敏感性和一定的抗盐性.     

Organic–inorganic hybrid hydrogels involving poly(N‐isopropylacrylamide) and polyhedral oligomeric silsesquioxane: Preparation and rapid thermoresponsive properties

3‐Acryloxypropylhepta(3,3,3‐trifluoropropyl) polyhedral oligomeric silsesquioxane (POSS) was synthesized and used as a modifier to improve the thermal response rates of poly(N‐isopropylacrylamide) (PNIPAM) hydrogel. The radical copolymerization among N‐isopropylacrylamide (NIPAM), the POSS macromer and N,N′‐methylenebisacrylamide was performed to prepare the POSS‐containing PNIPAM cross‐linked networks. Differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) showed that the POSS‐containing PNIPAM networks displayed the enhanced glass transition temperatures (T_g's) and improved thermal stability when compared with plain PNIPAM network. The POSS‐containing PNIPAM hydrogels exhibited temperature‐responsive behavior as the plain PNIPAM hydrogels. It is noted that with the moderate contents of POSS, the POSS‐containing PNIPAM hydrogels displayed much faster response rates in terms of swelling, deswelling, and re‐swelling experiments than plain PNIPAM hydrogel. The improved thermoresponsive properties of hydrogels have been interpreted on the basis of the formation of the specific microphase‐separated morphology in the hydrogels, that is, the POSS structural units in the hybrid hydrogels were self‐assembled into the highly hydrophobic nanodomains, which behave as the microporogens and promote the contact of PNIPAM chains and water. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 504–516, 2009     

Network parameters of poly(N‐isopropylacrylamide)/montmorillonite hydrogels: effects of accelerator and clay content

The results of network parameters of poly(N‐isopropylacrylamide)/montmorillonite (PNIPAAm/MMT) hydrogels prepared with two different types and concentrations of accelerators (tetramethylethylenediamine, TEMED and quaternary TEMED containing decyl bromide, QTEMED) using three different clay contents (1.0, 3.0, and 5.0 wt% of total monomer concentration) at two different polymerization temperatures (10 and 32°C) were presented and discussed. It was observed that when the reaction temperature of PNIPAAm crosslinked with MMT was chosen as 10°C both volume swelling ratios (i.e., thermodynamic interaction) and shear moduli, G increased. In hydrogels, thermodynamic interaction is reflected by polymer–water interaction parameter (χ). The lower is the value of χ, the stronger is the interaction between polymer and water, and the lower is the interaction between hydrophobic groups or between polymer chains. In addition, increase in MMT content was slightly affected on these intermolecular interactions. Therefore, this effect that combines high‐shear modulus with lower value of χ in the same molecular structure was defined as clay content‐independent diffusion behavior. On the other hand, in the case of the hydrogels synthesized with the higher concentration of TEMED and MMT, the values of χ and G decreased. These facts were interpreted that increase in both accelerator concentration and clay content, for fixed NIPAAm concentration made the number of effective crosslinks between MMT layers smaller. Copyright © 2010 John Wiley & Sons, Ltd.