A review on flame retardant technology in China. Part I: development of flame retardants

This paper provides an insight into some developments in flame retardants for different polymeric materials in China, primarily based on the publications that have appeared in the last 15 years. It focuses on the following aspects: halogen‐containing flame retardants, inorganic flame retardants (e.g. metal oxides and hydroxides, silicon‐containing materials, ammonium polyphosphate, red phosphorus, and expandable graphite), and organic flame retardants (e.g. aliphatic and aromatic phosphonates, nitrogen‐containing organics, and multi‐element organics). The inherently flame‐retardant polymer systems are also reviewed. The exploration of the novel flame retardants and flame‐retardant systems provides a powerful basis for the construction of flame‐retardant technologies and industrial applications in China. Copyright © 2009 John Wiley & Sons, Ltd.     

A review on potential development of flame retardant kenaf fibers reinforced polymer composites

Kenaf fibers have been extensively explored from the past few decades in polymer composites industries owing to its extensive adaptations, excellent properties together with its comparable mechanical properties to traditional glass fibers polymer composites. The combustibility or lowered flame retardancy hampered the diverse applications of kenaf fibers reinforced polymer composites, as it affects the mechanical strength and stiffness of composites during fire. Current review article intended to be a comprehensive source of published literature involving the flame retardants (FRs), types and applications of FRs and the fabrication of kenaf fibers reinforced polymer composites. This article will also provide a perfect data on the recent development of the FR kenaf fibers polymer composites with different FRs and explored its structural and semi‐structural industrial application for performing further research in this topic. Copyright © 2016 John Wiley & Sons, Ltd.     

A novel phosphazene cyclomatrix network polymer: Design, synthesis and application in flame retardant polylactide

A novel phosphazene cyclomatrix network polymer poly(cyclotriphosphazene-co- pentaerythritol) (PCPP) was synthesized and characterized based on an attempt to look for a high efficient and green intumescent flame retardant. A series of flame retardant polylactide (FR-PLA) composites containing PCPP were prepared by melt blending method. Thermal degradation behavior and combustion properties of FR-PLA composites were evaluated through thermogravimetric analysis, UL-94 experiments, limiting oxygen index and cone calorimeter tests. It is found that the weight of residues for FR-PLA composites improved greatly with the addition of PCPP. Additionally, PCPP show a high flame retardant efficiency for PLA, UL-94 V-0 could be passed only containing 5 wt% PCPP. Fourier transform infrared spectra and scanning electronic microscopy investigations reveal that the residual chars are compact and foaming containing P-O-C structure, which restrains the development of fire and increases the flame retardant properties.     

Vegetable oil-based flame retardant epoxy/clay nanocomposites

Flammability of epoxy appears to be one of the greatest threats and hence limits its advanced applications. The present investigation, therefore, reports on vegetable oil-based self-extinguishing epoxy/clay nanocomposites for the first time. These nanocomposites were prepared by the ex-situ technique using mechanical shearing and ultrasonication at different loadings (1, 2.5 and 5 wt%) of nano-clay. Monoglyceride of Mesua ferrea L. seed oil, bisphenol-A and tetrabromobisphenol-A based epoxy resin was used as the matrix. XRD, TEM, SEM, FTIR and rheological studies confirmed partially exfoliated nanocomposites formation. The study demonstrates two fold improvements of tensile strength and scratch hardness, three-fold increase in adhesive strength and 20 units increase in gloss value without any change in impact resistance through nanocomposite formation. TG studied confirmed the enhancement of thermal stability of the nanocomposite by 25 °C. The limiting oxygen index values and UL 94 test indicated the self-extinguishing characteristic of the nanocomposites.     

Transparent and flame retardant PMMA/clay nanocomposites prepared with dual modified organoclay

In this study, the dual modified organoclay (DMC), was successfully prepared by the successive cationic exchange reactions of the sodium montomorillonite clay (MMT) with two intercalating reagents, hexadecyl‐triphenyl‐phosphonium bromide and 2‐methacryloxy‐ethyl‐hexadecyl‐dimethyl‐ammonium bromide. A series of the PMMA/DMC nanocomposite membranes (PDCM) were then prepared with the PMMA matrix and various amounts of DMC via the solution cast method. The results of XRD, TEM, SEM, and UV–VIS measurements of the PDCMs prepared showed that the DMC particles were well dispersed in the PMMA matrix with a highly exfoliated structure. The TGA thermograms indicated that the thermal stabilities of the PDCM membranes are higher than that of the PMMA. Furthermore, the tensile mechanical property and glass transition temperature of the nanocomposites were dramatically increased with increasing the DMC content. The limiting oxygen index of PDCM membranes also indicated that the flame retardancy was significantly enhanced due to the presence of DMC. Moreover, more than 90% of the PMMA's transparency was remained in the nanocomposites. Copyright © 2011 John Wiley & Sons, Ltd.     

Synergistic effects of layered double hydroxide with phosphorus-nitrogen intumescent flame retardant in PP/EPDM/IFR/LDH nanocomposites

<正>Synergistic effects of layered double hydroxide(LDH) with intumescent flame retardanct(IFR) of phosphorus-nitrogen (NP) compound in the polypropylene/ethylene-propylene-diene/IFR/LDH(PP/EPDM/IFR/LDH) nanocomposites and related properties were studied by X-ray diffraction(XRD),transmission electron microscopy(TEM),scanning electron microscopy(SEM),limiting oxygen index(LOI),UL-94 test,cone calorimeter test(CCT) and thermo-gravimetric analysis (TGA).The XRD and TEM results show that the intercalated and/or exfoliated nanocomposites can be obtained by direct melt-intercalation of PP/EPDM into modified LDH and that LDH can promote the IFR additive NP to disperse more homogeneously in the polymer matrix.The SEM results provide positive evidence that more compact charred layers can be obtained from the PP/EPDM/NP/LDH sample than those from the PP/EPDM/LDH and PP/EPDM/NP samples during burning.The LOI and UL-94 rating tests show that the synergetic effects of LDH with NP can effectively increase the flame retardant properties of the PP/EPDM/NP/LDH samples.The data from the CCT and TGA tests indicate that the PP/EPDM/NP/LDH samples apparently decrease the HRR and MLR values and thus enhance the flame retardant properties and have better thermal stability than the PP/EPDM/LDH and PP/EPDM/NP samples.     

The determination of the gases released during heating of a flame retardant for polymers

The oxidative degradation of HET-acid (1,4,5,6,7,7-hexachlorobicyclo [2.2.1] hept-5-en-2, 3-dicarboxylic acid) is studied by the combination of TG, FTIR, MS and GC-MS. The gases evolved during the decomposition of this flame retardant are investigated on-line by FTIR and by MS. Simultaneously the evolved gases are collected by an adsorbent and, after the thermal experiment, desorbed to release the volatile products for identification using GC-MS. The combination of these techniques offers the unambiguous identification of the evolved products as a function of temperature. The main identified products are CO₂, H₂O, Cl₂, HCl, C₂Cl₄, maleic acid anhydride, HET-acid anhydride, chlorinated cyclic hydrocarbons and chlorinated unsaturated linear hydrocarbons.     

软质聚氨酯泡沫塑料用无卤阻燃剂的研究

本文以羟基苯氧膦丙烯酸(CEPP)和三聚氰胺(MA)为原料合成了一种含磷、氮无卤阻燃剂(CMA),采用FT-IR表征了阻燃剂的化学结构,并将该阻燃剂用于软质聚氨酯泡沫(FPUF)的阻燃。用扫描电镜(SEM)研究了阻燃剂的加入对FPUF的形态的影响,通过LO I和垂直燃烧(Cal.117A)测试研究了该阻燃剂对FPUF的阻燃效果。结果表明,CMA可以有效提高FPUF的阻燃性:当CMA的添加量为10%时,FPUF即可通过Cal.117A测试,其LO I值也从17.3提高到23.0;随阻燃剂添加量的增加,FPUF的阻燃性能也逐渐提高。TG测试结果表明CMA的加入对FPUF的热稳定性没有多大影响。     

Effect of a novel charring-foaming agent on flame retardancy and thermal degradation of intumescent flame retardant polypropylene

A new triazine polymer was synthesized by using cyanuric chloride, ethanolamine and ethylenediamine as raw materials. It is used both as a charring agent and as a foaming agent in intumescent flame retardants, designated as charring-foaming agent (CFA). Effect of CFA on flame retardancy, thermal degradation and mechanical properties of intumescent flame retardant polypropylene (PP) system (IFR-PP system) has been investigated. The results demonstrated that the intumescent flame retardant (IFR) consisting of CFA, APP and Zeolite 4A is very effective in flame retardancy of PP. It was found that when the weight ratio of CFA to APP is 1:2, that is, the components of the IFR are 64 wt% APP, 32 wt% CFA and 4 wt% Zeolite 4A, the IFR presents the most effective flame retardancy in PP systems. LOI value of IFR-PP reaches 37.0, when the IFR loading is 25 wt% in PP. It was also found that when the IFR loading is only 18 wt% in PP, the flame retardancy of IFR-PP can still pass V-0 rating, and its LOI value reaches 30.2. TGA data obtained in pure nitrogen demonstrated that CFA has a good ability of char formation itself, and CFA shows a high initial temperature of the thermal degradation. The char residue of CFA can reach 35.7 wt% at 700 °C. APP could effectively promote the char formation of the APP-CFA system. The char residue reaches 39.7 wt% at 700 °C, while it is 19.5% based on calculation. The IFR can change the thermal degradation behaviour of PP, enhance T_max of the decomposition peak of PP, and promote PP to form char, based upon the results of the calculation and the experiment. This is attributed to the fact that endothermic reactions took place in IFR charring process and the char layer formed by IFR prevented heat from transferring into inside of IFR-PP system. TGA results further explained the effective flame retardancy of the IFR containing CFA.     

Intrinsically flame retardant epoxy resin - Fire performance and background - Part II

The flame retardant mechanism of a newly synthesized phosphorus-containing reactive amine, which can be used both as crosslinking agent in epoxy resins and as flame retardant, was investigated. The mode of action and degradation pathway were investigated by in situ analysis of the gases evolved during the degradation by thermogravimetric measurements coupled online with infrared (TG-EGA-FTIR) and mass spectroscopy (TG/DTA-EGA-MS) and by solid residue analysis by infrared (ATR) spectroscopic methods and X-ray photoelectron spectroscopy (XPS). It was observed that the main difference in the degradation of the reference and the flame retardant system is that the degradation of the latter begins at lower temperature mainly with the emission of degradation products of the phosphorus amine, which act as flame retardants in the gas phase slowing down the further degradation steps. At the high temperature degradation stage the solid phase effect of the phosphorus prevails: the formation of phosphorocarbonaceous intumescent char results in a mass residue of 23.4%. The ratio of phosphorus acting in gas phase and solid phase, respectively, was determined on the basis of thermogravimetric and XPS measurements.     

Synergistic effect of zeolite 4A on thermal,mechanical and flame retardant properties of intumescent flame retardant HDPE composites

The combination of synergistic agent with intumescent flame retardant (IFR) systems provides a promising way to prepare high performance IFR composites. In this study, the effects of the synthetic zeolite 4 A in combination with the IFR system consisting of ammonium polyphosphate (APP) and tris (2-hydroxyethyl) isocynurate (THEIC) on thermal degradation, mechanical properties, flame retardancy and char formation of high-density polyethylene composites were investigated by limiting oxygen index (LOI) measurement, cone calorimetry, scanning electron microscopy and laser Raman spectroscopy. The LOI value of HD/FR/Z-0.5 composite with an optimum content of 0.5 wt. % zeolite 4 A and 25 wt. % of total flame retardant reaches 26.3 %. A low loading of zeolite 4 A can improve the bench-scale combustion performance as determined by cone calorimetry, and promote the formation of more compact char residue with a highly graphitic structure. However, a low loading of zeolite in combination with the IFR system consisting of APP and THEIC produces no significant changes in mechanical performance.     

含季戊四醇磷酸酯阻燃剂的合成与表征

采用1-氧代-4-羟甲基-2,6,7-三氧杂-1-磷杂双环[2.2.2]辛烷(PEPA)、三氯氧磷、双酚A和双酚S为反应物,合成了两个新型添加型阻燃剂:双酚A双[二(1-氧代-1-磷杂-2,6,7-三氧杂双环辛烷-4-亚甲基)]磷酸酯(BAPP)和双酚S双[二(1-氧代-1-磷杂-2,6,7-三氧杂双环辛烷-4-亚甲基)]磷酸酯(BSPP),通过元素分析、FT-IR和1H NMR等表征了标题化合物的结构,结果表明,所合成的标题化合物的结构与预期一致。热失重分析结果证明,BAPP和BSPP质量损失5%(wt)时的温度分别为343.6℃和352.3℃,600℃残余量分别达46.6%和55.5%,具有较高的热稳定性和结炭性能。阻燃性能实验证明,E-51环氧树脂中分别添加质量分数为18.2%(wt)的BAPP和BSPP时,极限氧指数分别为32.2%和31.8%,均能达到UL 94 V-0级。     

A novel efficient halogen-free flame retardant system for polycarbonate

A novel silicon- and phosphorus-containing flame retardant, poly (9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide siloxane), P(DOPO-VTES) was synthesized from 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide(DOPO) and vinyltriethoxy silane(VTES). Its chemical structure was confirmed by FTIR. The thermal gravimetrical analysis (TGA) showed that P(DOPO-VTES) had good thermal stability and a high of char yield (86.31%) at 700 °C in nitrogen atmosphere. Its XRD patterns showed that this compound had a certain ordered structure. P(DOPO-VTES) was blended with polycarbonate (PC) together with montmorillonite(MMT) to prepare a series of organic-inorganic hybrids of flame retardant (PC)/P(DOPO-VTES)/MMT via melt blending. The thermal degradation behavior and flame retardancy of those hybrids were investigated with TGA, limiting oxygen index (LOI), vertical burning test (UL-94), and cone calorimeter. The LOI value of the flame-retardant PC systems could reach a maximal value of 32.8 when the content of P(DOPO-VTES) was 5 wt%. When 2 wt% MMT was added into the PC/5%P(DOPO-VTES) system, the UL-94 rating reached V-0. The possible flame retardant mode of MMT was studied via the dynamic rheological properties of the systems and the morphology of the chars remaining after the LOI test and the cone calorimeter test.     

Intrinsically flame retardant epoxy resin - Fire performance and background - Part I

The flame retardant effect of newly synthesized phosphorus-containing reactive amine, which can be used both as crosslinking agent in epoxy resins and as a flame retardant, was investigated. The effect of montmorillonite and sepiolite additives on the fire induced degradation was compared to pristine epoxy resin. The effect of combining the organophosphorous amine with clay minerals was also studied. It could be concluded that the synthesized phosphorus-containing amine, TEDAP can substitute the traditional epoxy resin curing agents providing additionally excellent flame retardancy: the epoxy resins flame retarded this way reach 960 °C GWFI value, 33 LOI value and V-0 UL-94 rating - compared to the 550 °C GWFI value, 21 LOI value and “no rate” UL-94 classification of the reference epoxy resin. The peak of heat release was reduced to 1/10 compared to non-flame retarded resin, furthermore a shift in time was observed, which increases the time to escape in case of fire. The flame retardant performance can be further improved by incorporating clay additives: the LOI and the HRR results showed that the optimum of flame retardant effect of clay additives is around 1 mass% filler level in AH-16-TEDAP system. Applying a complex method for mechanical and structural characterization of the intumescent char it was determined that the flame retarded system forms significantly more and stronger char of better uniformity with smaller average bubble size. Incorporation of clay additives (owing to their bubble nucleating activity) results in further decrease in average bubble diameter.     

Comparison of different reactive organophosphorus flame retardant agents for cotton. Part II: Fabric flame resistant performance and physical properties

N-Methylol dimethylphosphonopropionamide (MDPA) is one of the most commonly used durable flame retardant agents for cotton. In our previous research, we developed a new flame retardant finishing system based on a hydroxy-functional organophosphorus oligomer (HFPO) and bonding agents, such as dimethyloldihydroxyethyleneurea (DMDHEU) and trimethylolmelamine (TMM). In this research, we compared the flame resistant performance as well as physical properties of the cotton fabric treated with these two flame retardant finishing systems. The cotton fabric treated with MDPA/TMM has a higher initial limiting oxygen index (LOI) than that of the fabric treated with HFPO/TMM due to higher nitrogen content in the system. The LOI of the cotton fabric treated with the HFPO and MDPA systems becomes identical when the treated fabric contains equal amount of phosphorus and nitrogen. The MDPA/TMM shows higher laundering durability on cotton than HFPO/TMM system. The fabric treated with HFPO/TMM and MDPA/TMM has low wrinkle resistance and low strength loss whereas the fabric stiffness significantly increases when the TMM concentration is increased.     

Thermal degradation and flame retardancy of epoxy resins containing intumescent flame retardant

Pentaerythritol diphosphonate melamine-urea-formaldehyde resin salt, a novel cheap macromolecular intumescent flame retardants (IFR), was synthesized, and its structure was a caged bicyclic macromolecule containing phosphorus characterized by IR. Epoxy resins (EP) were modified with IFR to get the flame retardant EP, whose flammability and burning behavior were characterized by UL 94 and limiting oxygen index (LOI). 25 mass% of IFR were doped into EP to get 27.2 of LOI and UL 94 V-0. The thermal properties of epoxy resins containing IFR were investigated with thermogravimetry (TG) and differential thermogravimetry (DTG). Activation energy for the decomposition of samples was obtained using Kissinger equation. The resultant data show that for EP containing IFR, compared with EP, IFR decreased mass loss, thermal stability and R _max, increased the char yield. The activation energy for the decomposition of EP is 230.4 kJ mol⁻¹ while it becomes 193.8 kJ mol⁻¹ for EP containing IFR, decreased by 36.6 kJ mol⁻¹, which shows that IFR can catalyze decomposition and carbonization of EP.     

A vanillin-derived flame retardant based on 2-aminopyrimidine for enhanced flame retardancy and mechanical properties of epoxy resin

In order to give epoxy resin good flame retardance, a novel bio-based flame retardant based on 2-aminopyrimidine (referred to as VAD) was synthesized from renewable vanillin as one of the starting materials. Its structure was confirmed by NMR and mass spectra. The epoxy resins containing VAD were prepared by utilizing 4,4-diaminodiphenylmethane (DDM) as a co-curing agent, and their flame-retardant, mechanical and thermal properties and corresponding mechanisms were studied. VAD accelerated the cross-linking reaction of DDM and E51 (diglycidyl ether of bisphenol A). 12.5 wt% VAD made the epoxy resin achieve UL-94 V-0 rating and its limited oxygen index (LOI) value increase from 22.4% to 32.3%. The cone calorimetric testing results revealed the decline in the values of total heat release (THR) and peak of heat release rate (pk-HRR) and the obvious enhancement of residue yield. A certain amount of VAD enhanced the flame inhibition, charring and barrier effects, resulting in good flame retardance of the epoxy resin. Furthermore, the tensile strength, flexural strength and flexural modulus of the epoxy resin with 12.5 wt% loading of VAD were 6.5%, 14.9%, 15.2% higher than those of EP, indicating the strengthening effect of VAD. This work guarantees VAD to be a promising flame retardant for enhancing the fire retardancy of epoxy resin without compromising its mechanical properties.     

Flame retardant effects of organic inorganic hybrid intumescent flame retardant based on expandable graphite in silicone rubber composites

In this work, an organic inorganic hybrid intumescent flame retardant (functionalized expandable graphite, FEG) was synthesized and characterized by Fourier transform infrared spectrometry (FTIR). The flame retardant effects of FEG in silicone rubber (SR) composites were investigated by cone calorimeter test (CCT), and the thermal stability of SR composites was studied using TGA. The CCT results showed that FEG can effectively reduce the flammable properties including peak heat release rate (PHRR), total heat release (THR), smoke production rate (SPR), total smoke release (TSR), and smoke factor (SF). An improvement of thermal stability of SR/FEG was also observed. Compared with EG, FEG can further reduce THR, SPR, and TSR of SR/FEG composites in combustion process. Moreover, there is a more obvious intumescent char layer formed from the sample with FEG than the sample with EG at the same loading in SR composites. Copyright © 2014 John Wiley & Sons, Ltd.     

A bio‐safe cyclophosphazene derivative flame retardant for polylactic acid composites: Flammability and cytotoxicity

An efficient bio‐safe cyclophosphazene flame retardant, 1,5,9,13,16,20‐Hexaoxa‐7,14,21‐triaza‐6λ⁴,8λ⁴,5λ⁴‐triphosphatrispiro[5.1.5.1.5.1]heneicosa‐6,8(14),15(21)‐triene (HCPO), was synthesized, and then was incorporated into polylactic acid (PLA) to improve the fire safety. The chemical structure of HCPO was confirmed by Fourier‐transformed infrared spectroscopy, mass spectrometry, and nuclear magnetic resonance spectroscopy. The thermal stability of the compound was characterized by thermogravimetric (TG) analyzer. The cytotoxic effects of HCPO to cells were evaluated. Fire behavior and thermal stability of PLA composites were investigated by vertical burning, limiting oxygen index (LOI), TG analysis, and cone calorimeter. The morphology of residual charring was observed by scanning electron microscope. The results showed HCPO was bio‐safe, and highly effective to enhance the flame retardancy of PLA composites. The LOI value was increased from 18.4 to 27.5 and UL‐94 grade achieved V‐0 for the PLA composite containing only 2% HCPO and 2% pentaerythrotol. It was demonstrated that intermolecular cross‐linking reaction between pentaerythrotol and HCPO in high temperature range could accelerate the formation of compact char layers.