Syntheses and electroluminescence properties of conjugated poly(p‐phenylene vinylene) derivatives bearing dendritic pendants

A series of new poly(p‐phenylene vinylene) derivatives with different dendritic pendants—poly{2‐[3′,5′‐bis(2″‐ethylhexyloxy)benzyloxy]‐1,4‐phenylenevinylene} (BE–PPV), poly{2‐[3′,5′‐bis(3″,7″‐dimethyl)octyloxy]‐1,4‐phenylenevinylene} (BD–PPV), poly(2‐{3′,5′‐bis[3″,5″‐bis(2?‐ethylhexyloxy)benzyloxy]benzyloxy}‐1,4‐phenylenevinylene) (BBE–PPV), poly(2‐{3′,5′‐bis[3″,5″‐bis(3?,7?‐dimethyloctyloxy)benzyloxy]benzyloxy}‐1,4‐phenylenevinylene) (BBD–PPV), and poly[(2‐{3′,5′‐bis[3″,5″‐bis(2?‐ethylhexyloxy)benzyloxy]benzyloxy}‐1,4‐phenylenevinylene)‐co‐(2‐{3′,5′‐bis[3″,5″‐bis(3?,7?‐dimethyloctyloxy)benzyloxy]benzyloxy}‐1,4‐phenylenevinylene)] (BBE‐co‐BBD–PPV; 1:1)—were successfully synthesized according to the Gilch route. The structures and properties of the monomers and the resulting conjugated polymers were characterized with ¹H and ¹³C NMR, elemental analysis, gel permeation chromatography, thermogravimetric analysis, ultraviolet–visible absorption spectroscopy, photoluminescence, and electroluminescence spectroscopy. The obtained polymers possessed excellent solubility in common solvents and good thermal stability, with a 5% weight loss temperature of more than 328 °C. The weight‐average molecular weights and polydispersity indices of BE–PPV, BD–PPV, BBE–PPV, BBD–PPV, and BBE‐co‐BBD–PPV (1:1) were in the range of 1.33–2.28 × 10⁵ and 1.35–1.53, respectively. Double‐layer light‐emitting diodes (LEDs) with the configuration of indium tin oxide/polymer/tris(8‐hydroxyquinoline) aluminum/Mg:Ag/Ag devices were fabricated, and they emitted green‐yellow light. The turn‐on voltages of BE–PPV, BD–PPV, BBE–PPV, BBD–PPV, and BBE‐co‐BBD–PPV (1:1) were approximately 5.6, 5.9, 5.5, 5.2, and 4.8 V, respectively. The LED devices of BE–PPV and BD–PPV possessed the highest electroluminescent performance; they exhibited maximum luminance with about 860 cd/m² at 12.8 V and 651 cd/m² at 13 V, respectively. The maximum luminescence efficiency of BE–PPV and BD–PPV was in the range of 0.37–0.40 cd/A. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3126–3140, 2005     

Electroluminescent properties of a partially‐conjugated hyperbranched poly(p‐phenylene vinylene)

In this paper, the electroluminescent properties of a new partially‐conjugated hyperbranched poly (p‐phenylene vinylene) (HPPV) were studied. The single layer light‐emitting device with HPPV as the emitting layer emits blue‐green light at 496 nm, with a luminance of 160 cd/m² at 9 V, a turn‐on voltage of 4.3 V and an electroluminescent efficiency of 0.028 cd/A. By doping an electron‐transport material [2‐(4‐biphenylyl)‐5‐phenyl‐1,3,4‐oxadiazole, PBD] into the emitting layer and inserting a thin layer of tris(8‐hydroxy‐quinoline)aluminum (Alq₃) as electron transporting/hole blocking layer for the devices, the electroluminescent efficiency of 1.42 cd/A and luminance of 1700 cd/m² were achieved. The results demonstrate that the devices with the hyperbranched polymers as emitting material can achieve high efficiency through optimization of device structures. Copyright © 2006 John Wiley & Sons, Ltd.     

Yellow‐light‐emitting cyano‐substituted poly[(1,3‐phenylene vinylene)‐alt‐(1,4‐phenylene vinylene)] derivative: Its synthesis and optical properties

A soluble cyano‐substituted poly[(1,3‐phenylene vinylene)‐alt‐(1,4‐phenylene vinylene)] derivative ( 9 ) was synthesized and characterized. Comparison between 9 and its model compound ( 10 ) showed that the chromophore in 9 remained to be well defined as a result of a π‐conjugation interruption at adjacent m‐phenylene units. The attachment of a cyano substituent only at the β position of the vinylene allowed the maximum electronic impact of the cyano group on the optical properties of the poly(p‐phenylene vinylene) material. At a low temperature (?108 or ?198 °C), the vibronic structures of 9 and 10 were partially resolved. The absorption and emission spectra of a film of 9 were less temperature‐dependent than those of a film of 10 , indicating that the former had a lower tendency to aggregate. A light‐emitting diode (LED) based on 9 emitted yellow light (λ_max ≈ 578 nm) with an external quantum efficiency of 0.03%. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3149–3158, 2003     

Direct Observation of α‐Chloro‐p‐quinodimethane as the Real Monomer in the Gilch Polymerization Leading to Poly(p‐phenylene vinylene)s

It is the general consensus that in Gilch polymerizations the 1,4‐bis(chloromethylene)benzene starting material first changes into p‐quinodimethane intermediates which then act as the real monomers. However, direct observation of these intermediates has not been possible so far. This is because usually the p‐quinodimethane auto‐initiates its rapid radical polymerization instantaneously, keeping its concentration extremely low throughout the whole process. Here it is shown that, when the reaction is carried out at very low temperatures, the formation of p‐quinodimethane still proceeds but chain growth is suppressed. Hence, the concentration of the active monomer reaches a level sufficient for NMR analysis.

     

Synthesis of poly(p‐phenylene vinylene)‐ and poly(phenylene ethynylene)‐based polymers containing p‐terphenyl in the main chain with alkoxyphenyl side groups

Starting from the pyrylium salt and following a facile synthetic route, we synthesized and polymerized 4,4″‐diiodo‐2′,6′‐di[4‐(2′‐ethylhexyl)oxy]phenyl‐p‐terphenyl with p‐divinylbenzene or p‐diethynylbenzene. The resulting polymers had moderate molecular weights, were amorphous, and dissolved in tetrahydrofuran and chloroform, with glass‐transition temperatures of 120–131 °C. The polymers behaved as violet‐blue‐emitting materials with photoluminescence maxima around 420 and 450 nm in solution and in thin films, respectively. They possessed well‐defined chromophores resulting from steric interactions in the polymer chain. The photoluminescence quantum yields were up to 0.29. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2591–2600, 2002     

Water‐soluble poly(ethylene oxide)‐block‐poly(p‐phenylene vinylene) copolymer: Synthesis and characterization

Water‐soluble and photoluminescent block copolymers [poly(ethylene oxide)‐block‐poly(p‐phenylene vinylene) (PEO‐b‐PPV)] were synthesized, in two steps, by the addition of α‐halo‐α′‐alkylsulfinyl‐p‐xylene from activated poly(ethylene oxide) (PEO) chains in tetrahydrofuran at 25 °C. This copolymerization, which was derived from the Vanderzande poly(p‐phenylene vinylene) (PPV) synthesis, led to partly converted PEO‐b‐PPV block copolymers mixed with unreacted PEO chains. The yield, length, and composition of these added sequences depended on the experimental conditions, namely, the order of reagent addition, the nature of the monomers, and the addition of an extra base. The addition of lithium tert‐butoxide increased the length of the PPV precursor sequence and reduced spontaneous conversion. The conversion into PPV could be achieved in a second step by a thermal treatment. A spectral analysis of the reactive medium and the composition of the resulting polymers revealed new evidence for an anionic mechanism of the copolymerization process under our experimental conditions. Moreover, the photoluminescence yields were strongly dependant on the conjugation length and on the solvent, with a maximum (70%) in tetrahydrofuran and a minimum (<1%) in water. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4337–4350, 2005     

New poly(p‐phenylene vinylene) derivatives with two oxadiazole rings per repeat unit: Synthesis,photophysical properties,electroluminescence, and metal ion recognition

Two new poly(p‐phenylene vinylene) derivatives OX1‐PPV and OX2‐PPV bearing two 1,3,4‐oxadiazole rings per repeat unit and a fully conjugated backbone with solubilizing dodecyloxy side groups were synthesized and investigated. The amorphous conjugated polymers had glass‐transition temperature values of 60–75 °C and emitted intense blue or greenish‐blue light in solution with photoluminescence (PL) emission maxima at 379–492 nm and PL quantum yields of 0.41–0.52. In the solid state they emitted yellowish‐green light with PL emission maxima at 533–555 nm. Cyclic voltammetry showed that both conjugated polymers had reversible reduction and irreversible oxidation, making them n‐type materials. The electron affinity of OX2‐PPV was estimated as 2.85 eV whereas that of OX1‐PPV was 2.75 eV. Yellow electroluminescence (EL) was achieved from single‐layer light‐emitting diodes of OX2‐PPV with an EL emission maximum at 555 nm and a brightness of 70 cd/m². Polymer OX2‐PPV, which was functionalized with 2,6‐bis(1,3,4‐oxadiazole‐2‐yl)pyridine, demonstrated sensitivity to various metal ions as a fluorescence‐mode chemosensor. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2112–2123, 2004     

Synthesis,characterization, and electroluminescence of new conjugated PPV derivatives bearing triphenylamine side‐chain through a vinylene bridge

Three new conjugated poly(p‐phenylene vinylene) (PPV) derivatives bearing triphenylamine side‐chain through a vinylene bridge, poly(2‐(4′‐(diphenylamino)phenylenevinyl)‐1,4‐phenylene‐vinylene) (DP‐PPV), poly(2‐(3′‐(3″,7″‐dimethyloctyloxy)phenyl)‐1,4‐phenylenevinylene‐alt‐2‐(4′‐ (diphenylamino)phenylenevinyl)‐1,4‐phenylenevinylene) (DODP‐PPV), and poly(2‐(4′‐(diphenylamino)phenylenevinyl)‐1,4‐phenylenevinylene‐co‐2‐(3′,5′‐bis(3″,7″‐dimethyloctyloxy)‐1,4‐phenylenevinylene) (DP‐co‐BD‐PPV), were synthesized according to the Gilch or Wittig method. Among the three polymers, the copolymer DP‐co‐BD‐PPV is soluble in common solvents with good thermal stability with 5% weight loss at temperatures higher than 386°C. The weight‐average molecular weight (M_w) and polydispersity index (PDI) of DP‐co‐BD‐PPV were 1.83 × 10⁵ and 2.33, respectively. The single‐layer polymer light‐emitting diodes (PLEDs) with the configuration of Indium tin oxide (ITO)/poly (3,4‐ethylenedioxythiophene): poly(4‐styrene sulfonate)(PEDOT:PSS)/DP‐co‐BD‐PPV/Ca/Al were fabricated. The PLED emitted yellow‐green light with the turn‐on voltage of ca. 4.9 V, the maximum luminance of ca. 990 cd/m² at 15.8 V, and the maximum electroluminescence (EL) efficiency of 0.22 cd/A. Copyright © 2007 John Wiley & Sons, Ltd.     

Poly[(2‐alkoxy‐5‐methyl‐1,3‐phenylene vinylene)‐alt‐(phenylene vinylene)] derivatives with different contents of cis‐ and trans‐olefins: The effect of the olefin bond geometry and conjugation length on luminescence

Poly[(2‐alkyloxy‐5‐methyl‐1,3‐phenylenevinylene)‐alt‐(1,3‐phenylenevinylene)]s ( 8 ) and poly[(2‐alkyloxy‐5‐methyl‐1,3‐phenylenevinylene)‐alt‐(1,4‐phenylenevinylene)]s ( 10 ) were synthesized by the Wittig reaction to provide materials containing 45–62% cis‐vinylene bonds. The optical characteristics of 8 and 10 were compared with those of their respective isomers, 3 and 4 , the cis‐vinylene contents of which were significantly lower (9–16%). Although a greater fraction of cis‐CH?CH linkages caused the absorption maximum (λ_max) of 8 and 10 to be slightly blueshifted (by ～3–6 nm) from that of 3 and 4 , the impact of the vinylene bond geometry appeared to be negligible on their fluorescence spectra. The fluorescence quantum efficiencies of 8 and 10 were estimated to be approximately 0.25 and 0.72, respectively. Both 8 (λ_max ≈ 445 or 462 nm) and 10 (λ_max ≈ 480 or 506 nm) were electroluminescent, showing effective color tuning by the controlled insertion of m‐phenylene moieties. The external electroluminescence quantum efficiencies were determined to be 4.26 × 10^?3% for 8 and 0.63% for 10 . The cis/trans‐vinylene bond ratio had a great impact on the electroluminescence device performance of 8 but a much smaller impact on the performance of 10 . © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 303–316, 2004     

Structural anisotropy in unstretched and uniaxially stretched poly(p‐phenylene vinylene)

Poly(p‐phenylene vinylene) or PPV is gaining increasing importance because of its superior electroluminescent efficiency and electrical conductivity. The most widely followed synthetic route for PPV involves synthesis of a precursor polymer using a sulfonium monomer salt. Previous studies have proven that the monomer salt which contains cyclic sulfonium groups yields better quality PPV than when the monomer containing dialkyl sulfonium groups is used. The structure of PPV synthesized using cyclic sulfonium precursor has not been as widely reported as that synthesized using dialkyl sulfonium monomer. In the current work, the structure of PPV, synthesized using a cyclic viz. tetrahydrothiophenium monomer salt, has been studied in detail using the wide angle X‐ray diffraction (WAXD) technique. The study reveals that even in the cast (unstretched) form, PPV shows considerable biaxial orientation in the plane of the film. This preferred orientation is found to occur during the casting process and is independent of the solvent used and casting substrate. On stretching these films to a final draw ratio of 7 : 1, this biaxial orientation is transformed into uniaxial orientation with nematic ordering of PPV chains along the stretch direction and PPV chains assuming three preferred orientations in the plane of the film. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 605–614, 1999     

Synthesis and optical properties of novel blue‐light‐emitting poly(p‐phenylene vinylene) derivatives with pendant oxadiazole or cyano groups

Two novel poly(p‐phenylene vinylene) polymers, which carried side substituents with cyano groups or 1,3,4‐oxadiazole, were synthesized by Heck coupling. They consisted of alternating conjugated segments and nonconjugated aliphatic spacers. The polymers had moderate molecular weights, were amorphous, and dissolved readily in tetrahydrofuran and halogenated organic solvents. They were stable up to approximately 340 °C in N₂ and 290 °C in air, and the anaerobic char yield was around 60% at 800 °C. The polymer with cyano side groups emitted blue light in solutions and thin films with identical photoluminescence (PL) maximum at 450 nm; this supported the idea that chain interactions were hindered even in the solid state. The PL maximum of this polymer in thin films was blueshifted upon annealing at 120 °C, indicating a thermochromic effect as a result of conformational changes in the polymer backbone. The polymer containing side substituents with oxadiazole rings emitted blue light in solutions with a PL maximum at 474 nm and blue‐greenish light in thin films with a PL maximum at 511 nm. The PL quantum yields of the polymers in tetrahydrofuran were 0.13–0.24. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1768–1778, 2004     

Crosslinkable poly(p‐phenylenevinylene) derivative

To simplify the fabrication of multilayer light‐emitting diodes, we prepared a p‐phenylenevinylene‐based polymer capped with crosslinkable styrene through a Wittig reaction. Insoluble poly(p‐phenylenevinylene) derivative (PPVD) films were prepared by a thermal treatment. The photoluminescence and ultraviolet–visible (UV–vis) absorbance of crosslinked films and noncrosslinked films were studied. We also studied the solvent resistance of crosslinked PPV films with UV–vis absorption spectra and atomic force microscopy. Double‐layer devices using crosslinked PPVD as an emitting layer, 2‐(4‐tert‐butylphenyl)‐5‐phenyl‐1,3,4‐oxadiazole (PBD) in poly(methyl methacrylate) as an electron‐transporting layer, and calcium as a cathode were fabricated. A maximum luminance efficiency of 0.70 cd/A and a maximum brightness of 740 cd/m² at 16 V were demonstrated. A 12‐fold improvement in the luminance efficiency with respect to that of single‐layer devices was realized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2124–2129, 2004     

Gel Formation during the Gilch Synthesis of Poly(p‐phenylene vinylenes): Evidence of an Unexpected Explanation

Gelation of the reaction mixture and insolubility of the poly(p‐phenylene vinylenes) (PPVs) when isolated at this stage, but complete redissolution of the gel and excellent solubility of the resulting PPVs after further stirring for hours or days, is a phenomenon in Gilch polymerizations that has not been explained so far. It is verified that, in agreement with the literature, specific additives prevent gelation. However, it is also shown that chemical crosslinking is certainly not the reason for gel formation. Instead, it seems to be the consequence of a very high entanglement density in the pristine PPVs, which requires time for relaxation. The mentioned additives seem to support this dis‐entanglement process.

     

Poly(p‐phenylene vinylene) derivatives containing triazole or oxadiazole segments: Connector effect in optical,electrochemical, and electroluminescent properties

To study the effect of connector structure between hole‐ and electron‐transporting segments, we synthesized and characterized new electroluminescent polymers P 1 – P 7 consisting of hole‐transporting 1,4‐bis(hexyloxy)‐2,5‐distyrylbenzene (DSB: P 1 and P 2 ) and electron‐transporting 4‐(4‐(hexyloxy)phenyl)‐3,5‐diphenyl‐4H‐1,2,4‐triazole (TAZ: P 3 and P 4 ) or 2‐(2,5‐bis(hexyloxy)‐4‐(5‐phenyl‐1,3,4‐oxadiazol)phenyl)‐5‐phenyl‐1,3,4‐oxadiazole (DIOXD: P 5 – P 7 ) segments linked by different connectors. The connectors between hole‐ and electron‐transporting segments are (1) 1,4‐phenylene in P 3 and P 5 , (2) 1,4‐divinylbenzene in P 4 and P 6 , and (3) 4,4′‐biphenyl in P 7 . Three corresponding end‐capped model polymers P 1‐M , P 2‐M , and P 3‐M were also synthesized to evaluate the effect of end groups. From optimized semiempirical MNDO calculations, the adjacent benzene rings between DSB and TAZ or DIOXD chromophores in P 3 , P 5 , and P 7 twist about 81°–89°. The effect of twisted architectures and connectors in optical and electrochemical properties for P 1 – P 7 have been discussed by comparing with copolymers P 1 and P 2 , which possess single bond or ether spacer as connectors. From cyclic voltammograms, the torsion in P 3 , P 5 , and P 7 confines electron delocalization and leads to simultaneously enhanced hole and electron affinity as compared to those of P 1 and P 2 . Furthermore, double‐layer light‐emitting diodes with a configuration of ITO/PEDOT:PSS/ P 1 – P 7 /Al all reveal green–yellow electroluminescence with maximum luminance at 8–320 cd/m² and their performances are greatly influenced by the connector's structure. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4514–4531, 2006     

Copoly(p‐phenylene)s containing bipolar triphenylamine and 1,2,4‐triazole groups: Synthesis,optoelectronic properties,and applications

Two novel copoly(p‐phenylene)s ( P1 – P2 ) containing bipolar groups (12.8 and 6.8 mol %, respectively), directly linked hole transporting triphenylamine and electron transporting aromatic 1,2,4‐triazole, were synthesized to enhance electroluminescence (EL) of poly(p‐phenylene vinylene) (PPV) derivatives. The bipolar groups not only enhance thermal stability but also promote electron affinity and hole affinity of the resulting copoly(p‐phenylene)s. Blending the bipolar copoly‐(p‐phenylene)s ( P1 – P2 ) with PPV derivatives ( d6‐PPV ) as an emitting layer effectively improve the emission efficiency of its electroluminescent devices [indium tin oxide (ITO)/poly(3,4‐ethylenedioxythiophene) (PEDOT):poly(styrenesulfonate) (PSS)/polymer blend/Ca (50 nm)/Al (100 nm)]. The maximum luminance and maximum luminance efficiency were significantly enhanced from 310 cd m^?2 and 0.03 cd A^?1 ( d6‐PPV ‐based device) to 1450 cd m^?2 and 0.20 cd A^?1 (blend device with d6‐PPV / P1 = 96/4 containing ～0.5 wt % of bipolar groups), respectively. Our results demonstrate the efficacy of the copoly(p‐phenylene)s with bipolar groups in enhancing EL of PPV derivatives. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Bipolar poly(p‐phenylene vinylene)s bearing electron‐donating triphenylamine or carbazole and electron‐accepting quinoxaline moieties

Two new poly(phenylene vinylene)s (PPVs) carrying electron‐donating triphenylamine or carbazole and electron‐deficient quinoxaline units were synthesized and characterized. Their properties were compared with those of PPV containing only quinoxaline unit. The two polymers showed PL maximum at 501–510 in solution and 533–540 in thin film. Because of the presence of electron donor and acceptor units they displayed strong intramolecular charge transfer (ICT) effects; hence, low‐photoluminescence quantum yields. The polymers showed reversible electrochemical reduction with electron affinity of 2.75 eV and irreversible oxidation with ionization potential of 5.10–5.24 eV. Single‐layer LED of configuration ITO/PEDOT/polymer/Al showed low turn‐on voltage at 5 V, but limited brightness of 50–60 cdm^?2. The electroluminescence maximum was voltage‐tunable varying from 500 to 542 nm. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2367–2378, 2008     

Novel route to poly(p‐phenylene vinylene) polymers

Poly(p‐phenylene vinylene) (PPV), poly(2,5‐dioctyl‐p‐phenylene vinylene) (PDOPPV), and poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐p‐phenylene vinylene] (MEHPPV) were synthesized by a liquid–solid two‐phase reaction. The liquid phase was tetrahydrofuran containing 1,4‐bis(bromomethyl)benzene, 1,4‐bis(chloromethyl)‐2,5‐dioctylbenzene, or 1,4‐bis(chloromethyl)‐2‐methoxyl‐5‐(2′‐ethylhexyloxy)benzene as the monomer and a certain amount of tetrabutylammonium bromide as a phase‐transfer catalyst. The solid phase consisted of potassium hydroxide particles with diameters smaller than 2 mm. The experimental results demonstrated that the reaction conversions of PPV and PDOPPV were fairly high (～65%), but the conversion of MEHPPV was only 45%. Moreover, gelation was found in the polymerization processes. As a result, PPV was insoluble and PDOPPV and MEHPPV were partially soluble in the usual organic solvents, such as tetrahydrofuran and chloroform. Soluble PDOPPV and MEHPPV were obtained with chloromethylbenzene or bromomethylbenzene as a retardant regent. The molar mass of soluble PDOPPV was measured to be 2 × 10⁴ g mol^?1, and that of MEHPPV was 6 × 10⁴ g mol^?1. A thin, compact film of MEHPPV was formed via spin coating, and it emitted a yellow light. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 449–455, 2003     

The thermal conversion of the tetrahydrothiophene‐precursor polymer to poly(p‐phenylene vinylene)

This paper reports the thermal conversion of the tetrahydrothiophene (THT)‐precursor to poly(p‐phenylene vinylene) (PPV). Detailed investigations of the conversion process show that the leaving groups THT and HCl do not eliminate simultaneously. Moderate temperatures (≤125 °C) are sufficient to eliminate the THT while a higher temperature of ≈150 °C is necessary for the leaving group HCl. Furthermore, the THT groups split off at two characteristic temperatures. Our investigations have shown that a consistent picture of the reaction mechanism can only be obtained if the configuration of the polymer chain is considered. For the total reaction of the THT‐precursor to PPV a reaction mechanism is suggested that consists of at least four steps. Copyright © 1999 John Wiley & Sons, Ltd.     

Blue‐emitting poly[(m‐phenylene vinylene)‐alt‐(o‐phenylene vinylene)]s: The effect of regioregularity on the optical properties

Poly[(m‐phenylene vinylene)‐alt‐(o‐phenylene vinylene)]s with different contents of cis‐/trans‐CH?CH ( 3 and 6 ) have been synthesized through Wittig condensation. The polymers exhibit good solubility in common organic solvents such as toluene and tetrahydrofuran. A comparison of the optical properties has been made between 3 and its phenyl regioisomers containing either p‐phenylene or m‐phenylene units. The results show that the regiochemistry of the phenyl ring can be a useful tool for tuning the emission color of π‐conjugated polymers because the extension of π conjugation can only partially be achieved through an o‐phenylene bridge. Although both polymers 3 and 6 exhibit comparable low fluorescence quantum efficiencies (≈0.18) in solution, their films are highly luminescent, showing a broad emission band near 456 nm (blue color). Electroluminescence results show that the device of polymer 3 , which has a higher content of trans‐CH?CH linkages, is about 20 times more efficient than that of 6 . © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2650–2658, 2003     

Novel mesogen‐jacketed poly(p‐phenylenevinylene) derivatives bearing oxadiazole pendants: Design,synthesis, and optoelectronic properties

1,3,4‐oxadiazole moieties were laterally linked to the phenyl rings via a short ? OCH₂ spacer and a series of novel poly(p‐phenylenevinylene) derivatives have been successfully synthesized through Horner–Witting–Emmons coupling reaction. The structures and properties of the monomers and the resulting conjugated polymers were characterized by nuclear magnetic resonance spectroscope, Fourier transform infrared, elemental analysis, gel permeation chromatography, thermogravimetric analysis, UV–vis absorption (UV) spectroscopy, photoluminescence spectroscopy and cyclic voltammetry. The UV spectra at solution state was similar to what's observed at film state while the PL spectra at film state had a red shift from 19 to 28 nm compared with the results at solution state, which implied that the unique bulky jacketed structure containing oxadiazole unit of these copolymers could effectively suppress π‐stacking/aggregation. LUMO levels of these polymers varied from ?3.44 to ?3.63 eV with increasing content of oxadiazole units, which facilitated electron injection. PLEDs with the configuration of ITO/PEDOT/Polymer/TPBI (15 nm)/LiF (1 nm)/Al (100 nm) were fabricated, which emit a yellowish green light around 540 and 570 nm with a maximum brightness of 1074.7 cd/m² and luminous efficiency of 0.108 cd/A. The introduction of the unique bulky OXD unit into PPVs at a low molar content largely improved the electroluminescence properties of PPV. © Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7173–7186, 2008