Photoluminescence of new red phosphor SrZnO2:Eu

SrZnO₂:Eu³⁺ has been synthesized by solid-state reaction and its photoluminescence in ultraviolet (UV)-vacuum ultraviolet (VUV) range was investigated. The broad bands around 254 nm are assigned to CT band of Eu³⁺-O²⁻. With the increasing of Eu³⁺ concentration, Eu³⁺ could occupy different sites, which leads to the broadening of CT band. A sharp band is observed in the region of 110-130 nm, which is related to the host absorption. The phosphors emit red luminescence centered at about 616 nm due to Eu³⁺⁵D₀→⁷F₂ both under 254 and 147 nm, but none of Eu²⁺ blue emission can be observed.     

A novel blue-emitting phosphor LiSrPO4:Eu for white LEDs

A novel blue-emitting phosphor, LiSrPO₄:Eu²⁺, was prepared by the solid-state reaction and X-ray powder diffraction (XRD) analysis confirmed the formation of LiSrPO₄:Eu²⁺. Photoluminescence (PL) results showed that the phosphor can be efficiently excited by UV-visible light from 250 to 440 nm, and exhibited bright blue emission. The effects of the doped-Eu²⁺ concentration in LiSrPO₄:Eu²⁺ on the PL were investigated in detail. The results showed that the relative PL intensity increases with Eu²⁺-concentration increasing until a maximum intensity is reached, and then it decreases due to concentration quenching and a red-shift appears, which are explained satisfactorily with the luminescent theory. Upon excited with 396 nm light, the present synthesized phosphor has higher emission intensity than that from the commercial blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺. Bright blue light-emitting diodes were fabricated by the combination of the synthesized LiSrPO₄:Eu²⁺ with ∼397 nm emitting InGaN-based chips.     

Preparation, crystal structure, and photoluminescence of Ca2SnO4:Eu, Y

Eu³⁺-doped Ca₂SnO₄ (solid solutions of Ca_2−xEu_2xSn_1−xO₄, 0?x?0.3) and Eu³⁺ and Y³⁺-codoped Ca₂SnO₄ (Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄) were prepared by solid-state reaction at 1400 °C in air. Rietveld analysis of the X-ray powder diffraction patterns revealed that Eu³⁺ replaced Ca²⁺ and Sn⁴⁺ in Eu³⁺-doped Ca₂SnO₄, and that Eu³⁺ replaced Ca²⁺ and Y³⁺ replaced Sn⁴⁺ in Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄. Red luminescence at 616 nm due to the electric dipole transition ⁵D_o→⁷F₂ was observed in the photoluminescence (PL) spectra of Ca_2−xEu_2xSn_1−xO₄ and Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ at room temperature. The maximum PL intensity in the solid solutions of Ca_2−xEu_2xSn_1−xO₄ was obtained for x=0.1. The PL intensity of Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ was 1.26 times greater than that of Ca_2−xEu_2xSn_1−xO₄ with x=0.1.     

Role of crystallite size on the photoluminescence properties of SrIn2O4:Eu phosphor synthesized by different methods

Photoluminescence (PL) of Eu³⁺ was studied in SrIn₂O₄ host lattice. A complete solid solubility of Eu³⁺ has been found in the series SrIn_2−xEu_xO₄ [x=0-2.0]. The phase formation at a relatively low temperature and in a very short duration was achieved by combustion synthesis (CS). Concentration quenching of luminescence has been observed in SrIn_2−xEu_xO₄ [x=0.1-2.0] and the critical concentration for maximum emission was found to be with x=0.3. In order to find the role of crystallite size on the PL properties of SrIn₂O₄:Eu³⁺, the results obtained with phosphors synthesized by solid state reaction (SSR) and CS methods were compared.     

A new type of charge compensating mechanism in Ca5(PO4)3F:Eu phosphor

The X-ray powder diffraction, reflectance, photoluminescence, photoluminescence excitation and ESR spectra of Ca₅(PO₄)₃F:Eu³⁺ phosphor have been studied. Three distinct variants of calcium substitutional Eu³⁺-sites have been observed in this host and the charge compensating species related to each of these sites has been identified. It is noted that the host related trace impurities those have prospects of acting as charge compensator, and the reaction environment that exists during the preparation of the material, greatly influence the preferential substitution of different Ca²⁺-sites by the Eu³⁺ ions. It is also noted that the charge compensating species in a suitable case, takes part in the photophysical process of luminescence of the Eu³⁺.     

Preparation and optical properties of SrF2:Eu nanospheres

SrF₂:Eu³⁺ nanospheres with homogeneous diameter have been synthesized by a microemulsion-mediated hydrothermal method for the first time, in which quaternary microemulsion of CTAB/water/cyclohexane/n-pentanol was used. The possible reaction mechanism and the luminescent properties of SrF₂:Eu³⁺ nanospheres were also investigated in this paper. The morphology and grain sizes of final products were characterized by field emission scanning electron microscopy and transmission electron microscopy, indicating that most of the products were nanospheres with an average diameter of ∼50 nm. Room-temperature emission spectra, recorded under 394-nm excitation, showed that the transition of ⁵D₀ → ⁷F₁ emission be dominating in SrF₂:Eu³⁺ nanospheres. From the dependence of the luminescence intensity on the concentration of Eu³⁺ ions, the optimal dopant concentration is 2 mol%.     

Preparation and photoluminescence property of a loose powder, Ca3Al2O6:Eu by calcination of a layered double hydroxide precursor

A novel red light-emitting material, Ca₃Al₂O₆:Eu³⁺, which is the first example found in the Ca₃Al₂O₆ host, was prepared by calcination of a layered double hydroxide precursor at 1350 °C. The precursor, [Ca_2.9−xAl₂Eu_x(OH)_9.8](NO₃)_2+x·2.5H₂O, was prepared by coprecipitation of metal nitrates with sodium hydroxide. The material is a loose powder composed of irregular particles formed from aggregation of particles of a few nanometers, as shown in scanning electron microscope (SEM) images. It was found that the photoluminescence intensity reached the maximum when the calcination temperature was 1350 °C and the concentration of Eu³⁺ was 1.0%. The material emits bright red emission at 614 nm under a radiation of λ=250 nm.     

Fabrication and optical properties of core-shell structured spherical SiO2@GdVO4:Eu phosphors via sol-gel process

Europium-doped nanocrystalline GdVO₄ phosphor layers were coated on the surface of preformed submicron silica spheres by sol-gel method. The resulted SiO₂@Gd_0.95Eu_0.05VO₄ core-shell particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, low voltage cathodoluminescence (CL), time resolved PL spectra and kinetic decays. The XRD results demonstrate that the Gd_0.95Eu_0.05VO₄ layers begin to crystallize on the SiO₂ spheres after annealing at 600 ^°C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have spherical shape, narrow size distribution (average size ca. 600 nm), non-agglomeration. The thickness of the Gd_0.95Eu_0.05VO₄ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). PL and CL show that the emissions are dominated by ⁵D₀-⁷F₂ transition of Eu³⁺ (618 nm, red). The PL and CL intensities of Eu³⁺ increase with increasing the annealing temperature and the number of coating cycles. The optimum concentration for Eu³⁺ was determined to be 5 mol% of Gd³⁺ in GdVO₄ host.     

Synthesis and spectral characteristics of Sr2Y8(SiO4)6O2: Eu polycrystals

Spectral-luminescent characteristics of Sr₂Y₈(SiO₄)₆O₂: Eu powder crystal phosphor with the apatite structure and high-intensity luminescence of Eu³⁺ ions have been studied. The charge state of europium in the samples has been characterized by means of X-ray L₃-adsorption spectroscopy. It was established that Eu³⁺ forms two types of optical centers. Besides, luminescence of Eu²⁺ions was found. Reduction Eu³⁺→Eu²⁺ was considered, which may be due to vacancy formation in the 4f crystal lattice position and to negative charge transfer by this vacancy to two ions. Thus, in the silicate lattice there exist inhomogeneously distributed oxygen-deficient centers, which are responsible for nonradiative transfer of excitation energy to Eu³⁺ and Eu²⁺ ions. To study electron-vibrational interactions in the crystal phosphor samples, their IR and Raman spectra were examined. In the luminescence spectrum of Eu²⁺, a series of low-intensity bands caused by interaction of the 4f⁶5d state of Eu²⁺ with silicate lattice vibrations was observed.     

Synthesis and luminescence properties of nanocrystalline YVO4:Eu

Nanocrystalline YVO₄:Eu³⁺ was synthesized by direct precipitation reaction, which was then annealed at different temperatures. The results of XRD showed that nanocrystalline YVO₄:Eu³⁺ could be obtained in solution at 60 °C, and the mean particle sizes of samples are increased as annealing temperature is increased. The results of TEM exhibit that the sizes of samples are around 5-30 nm. Studies on the excitation spectra show that there are a large number of the structural distortions in smaller particles. By analyzing line splitting patterns and peaks broadening in the emission spectra, we consider that the deviations in intensity patterns of ⁵D₀-⁷F₂ are affected by distortions of crystal lattice. Some abnormal behaviors can be attributed to higher ratio of surface to volume, which lead to the different local symmetry environment of Eu³⁺ ions on the surface.     

铝热反应法制备双股类螺旋Zn2SnO4单晶纳米带

综合利用化学气相沉积、铝热反应法、汽-液-固生长法、极性面融合和稳态湍流动力学控制来大量制备双股类螺旋Zn₂SnO₄单晶纳米带. 该材料属于面心立方尖晶石型透明半导体, 在光伏器件和湿度与可燃气体传感器中有着广泛的应用. 扫描电镜、透射电镜、电子衍射、X射线衍射、拉曼光谱以及光发射等技术分析表明所得的双股类螺旋纳米带是由两个独立的Zn₂SnO₄纳米带通过扭曲纠缠和融合而成. 该双股类螺旋纳米带实际上是在轴向具有周期性的超晶格材料. 光致发光测量表明该纳米带在326.1 nm处出现强发射峰, 线宽约为1.5nm. 本研究所采用的综合制备法中的铝热反应法和稳态湍流微扰法可能有助于类似材料的控制制备.     

Sonochemical synthesis and luminescence properties of single-crystalline BaF2:Eu nanospheres

BaF₂ nanocrystals doped with 5.0 mol% Eu³⁺ has been successfully synthesized via a facile, quick and efficient ultrasonic solution route employing the reactions between Ba(NO₃)₂, Eu(NO₃)₃ and KBF₄ under ambient conditions. The product was characterized via X-ray powder diffraction (XRD), scanning electron micrographs (SEM), transmission electron microscopy (TEM), high-resolution transmission electron micrographs (HRTEM), selected area electron diffraction (SAED) and photoluminescence (PL) spectra. The ultrasonic irradiation has a strong effect on the morphology of the BaF₂:Eu³⁺ particles. The caddice-sphere-like particles with an average diameter of 250 nm could be obtained with ultrasonic irradiation, whereas only olive-like particles were produced without ultrasonic irradiation. The results of XRD indicate that the obtained BaF₂:Eu³⁺ nanospheres crystallized well with a cubic structure. The PL spectrum shows that the BaF₂:Eu³⁺ nanospheres has the characteristic emission of Eu^{3+ 5}D₀-⁷F_J (J=1-4) transitions, with the magnetic dipole ⁵D₀-⁷F₁ allowed transition (590 nm) being the most prominent emission line.     

Distribution-related luminescence of Eu sensitized by SnO2 nano-crystals embedding in oxide glassy matrix

Eu³⁺ doped transparent glass ceramics embedding SnO₂ nano-crystals were prepared by melt quenching and subsequent heating. Site selective excitation experiments revealed that some Eu³⁺ ions were incorporated in the SnO₂ lattices by substituting Sn⁴⁺ ions, whereas the rest located in the oxide glassy matrix. Interestingly, it is found that the Eu³⁺ ions residing in the SnO₂ lattices exhibited much longer luminescent decay lifetime than those in the glassy matrix. Measurements on the photoluminescence excitation and photoluminescence spectra demonstrated the occurrence of energy transfer from the SnO₂ nano-crystals to the Eu³⁺ ions. The influences of Eu³⁺ content, and furthermore, their location on the energy transfer process were discussed.     

MoS2/Cd2SnO4复合材料的制备及其气敏性能

采用水热-煅烧法制备Cd₂SnO₄,之后通过超声混合法得到一系列MoS₂/Cd₂SnO₄复合材料。采用X射线衍射、扫描电子显微镜、X射线光电子能谱对Cd₂SnO₄和一系列MoS₂/Cd₂SnO₄复合材料进行结构和形貌的表征。研究了MoS₂掺杂量对于MoS₂/Cd₂SnO₄复合材料的气敏性能影响。实验结果表明,当MoS₂与Cd₂SnO₄的质量比为2.5%,MoS₂/Cd₂SnO₄复合材料制备的气敏元件在170 ℃时对浓度为100 μL·L^-1的甲醛气体的灵敏度为40.0,最低检测限为0.1 μL·L^-1。     

白色荧光粉NaGd（MoO4）2:Dy3+,Eu3+的水热合成及发光性能

采用谷氨酸辅助水热法合成了八面体形NaGd(MoO4)2:Dy3+,Eu3+白色荧光粉.X射线衍射结果表明,合成的样品为四方晶系的NaGd(MoO4)2纯相.扫描电子显微镜照片显示所制备的粒子为八面体形,各边长约为2μm.荧光光谱结果表明,在NaGd(MoO4)2:4%Dy3+,yEu3+(y=0,0.5%,0.6%,0.7%,0.8%,0.9%,1.0%)样品中,随着Eu3+掺入量的增加,Dy3+的发射峰逐渐减弱,而Eu3+的发射峰逐渐增强,说明Dy3+-Eu3+之间存在能量传递.通过色坐标图可知,当Eu3+掺杂量y=0.9%时,荧光粉的色坐标(0.338,0.281)与标准的白光色坐标(0.33,0.33)接近,表明NaGd(MoO4)2:4%Dy3+,0.9%Eu3+是很好的近紫外光激发下的白色荧光粉.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.     

Cr3+掺杂Ca4HfGe3O12宽带近红外荧光粉的发光特性及应用

近红外荧光粉在生物活体成像领域展现出重要的应用前景。但活体成像用近红外荧光粉存在种类匮乏、耐温性差等瓶颈问题。采用固相法合成了宽带近红外Ca₄HfGe₃O₁₂∶ xCr³⁺(0≤x≤0.09)荧光粉。X射线衍射和能谱分析的结果表明Cr³⁺离子成功进入Ca₄HfGe₃O₁₂晶格。在469 nm蓝光激发下，Ca₄HfGe₃O₁₂∶xCr³⁺荧光粉发射出690~1 200 nm的宽带近红外光，峰值波长为825 nm (⁴T₂-⁴A₂)，半高宽达到141 nm，Cr³⁺掺杂最佳浓度为0.03。依据激发光谱峰形和寿命衰减行为，证实Cr³⁺仅占据基质中一种阳离子格位。Ca₄HfGe₃O₁₂∶0.03Cr³⁺荧光粉的荧光量子效率为33.63%，该荧光粉发射光谱在400 K下的积分面积为室温下的60.5%，表明该样品具有优良的热稳定性。采用自制近红外荧光粉转换器件照射人手掌和滤波片遮挡的水果，观察到清晰地静脉血管和遮挡水果的轮廓。     

MgF2对Mn4+掺杂锗酸盐红色荧光粉发光的影响

3.5MgO·0.5MgF₂·GeO₂∶Mn⁴⁺作为优异热稳定性和良好发光性能的红色荧光粉而被市场应用,然而,该粉体中MgF₂的作用影响机理尚不明晰,阻碍其性能进一步优化和发展。采用高温固相法制备了系列Mn⁴⁺激活的锗酸盐荧光粉,通过对比加入MgF₂、H₃BO₃(助熔剂),研究了该粉体的结构、形貌、发光性能等变化规律,阐明了MgF₂的发光影响作用。研究表明,加入MgF₂、H₃BO₃和不加任何助熔剂时的样品,其最佳烧结温度分别为1 150、1 250和1 350 ℃,上述温度下发光强度均为最佳值,其中加入MgF₂、H₃BO₃的样品在最佳温度处生成了纯相。MgF₂的添加,一方面同H₃BO₃一样作为助熔剂对生成纯相、提高样品结晶度起了积极的作用;另一方面,通过研究分析,确认F^-离子成功掺杂进入晶格,促使样品生成的晶体结构为Mg₁₄Ge₅(O,F)₂₄。加入MgF₂、H₃BO₃在最佳烧结温度的样品的荧光寿命分别为0.93和0.75 ms。     

The synthesis and structural characterization of the new ternary nitrides: Ca4TiN4 and Ca5NbN5

The ternary nitrides, Ca₄TiN₄ and Ca₅NbN₅, were synthesized in sealed niobium tubes using lithium nitride as a flux at 900 and 1050 °C, respectively. The structures of both compounds were solved from single-crystal X-ray diffraction data. Ca₄TiN₄ is the first example of a calcium group IV nitride; it crystallizes in the triclinic space group (No. 2) with cell parameters a=5.9757(5) Å, b=6.0129(5) Å, c=6.0116(12) Å, α=71.565(4)°, β=79.471(4)°, γ=68.258(4)° and Z=2. Ca₄TiN₄ is isostructural with Na₄TiO₄ and contains tetrahedral TiN₄ units connected through edges and corners to CaN₄ tetrahedra and CaN₅ square pyramids. Ca₅NbN₅ crystallizes in the monoclinic space group C2/m (No. 12) with cell parameters a=11.922(7) Å, b=6.878(5) Å, c=8.936(7) Å, β=101.22(3)° and Z=4. Ca₅NbN₅ is isostructural with Ba₅NbN₅; the structure contains NbN₄ tetrahedra that share vertices with CaN₅ trigonal bipyramids.     

Ca9Y(PO4)7:Ce3+,Tb3+纳米荧光粉的制备及发光性能

采用水热法制备出Ca₉Y（PO₄）₇：Ce³⁺,Tb³⁺纳米荧光粉,通过XRD、SEM和荧光光谱等对样品进行了分析,研究在Ca₉Y（PO₄）₇基质中引入Ce³⁺,Tb³⁺离子对发光性能的影响规律。研究发现因Tb³⁺离子自身能量交叉驰豫的存在,使得单掺Tb³⁺时,通过调节Tb³⁺离子的浓度可以实现对发光颜色的控制。同时研究了Ce³⁺-Tb³⁺之间的能量传递为电多极相互作用的偶极-四极机制,Ce³⁺-Tb³⁺之间最大的能量传递效率为55.6%。Ca₉Y（PO₄）₇：Ce³⁺,Tb³⁺的发光颜色可以通过激活离子之间的能量传递和共发射得到可控调节。SEM分析表明荧光粉颗粒尺寸在100 nm左右,分散性好。