Self-assembled InAs island formation on GaAs (1 1 0) by metalorganic vapor phase epitaxy

Formation of self-assembled InAs 3D islands on GaAs (1 1 0) substrate by metal organic vapor phase epitaxy has been investigated. Relatively uniform InAs islands with an average areal density of 10⁹ cm⁻²are formed at 400 ° C using a thin InGaAs strain reducing (SR) layer. No island formation is observed without the SR layer. Island growth on GaAs (1 1 0) is found to require a significantly lower growth temperature compared to the more conventional growth on GaAs (1 0 0) substrates. In addition, the island height is observed to depend only weakly on the growth temperature and to be almost independent of the V/III ratio and growth rate. Low-temperature photoluminescence at 1.22 eV is obtained from the overgrown islands.     

Preparation of five-layered Si/SixGe1−x nano-films by RF helicon magnetron sputtering

Five-layered Si/Si_xGe_1−x films on Si(1 0 0) substrate with single-layer thickness of 30 nm, 10 nm and 5 nm, respectively were prepared by RF helicon magnetron sputtering with dual targets of Si and Ge to investigate the feasibility of an industrial fabrication method on multi-stacked superlattice structure for thin-film thermoelectric applications. The fine periodic structure is confirmed in the samples except for the case of 5 nm in single-layer thickness. Fine crystalline Si_xGe_1−x layer is obtained from 700 °C in substrate temperature, while higher than 700 °C is required for Si good layer. The composition ratio (x) in Si_xGe_1−x is varied depending on the applied power to Si and Ge targets. Typical power ratio to obtain x = 0.83 was 7:3, Hall coefficient, p-type carrier concentration, sheet carrier concentration and mobility measured for the sample composed of five layers of Si (10 nm)/Si_0.82Ge_0.18 (10 nm) are 2.55 × 10⁶ /°C, 2.56 × 10¹² cm⁻³, 1.28 × 10⁷ cm⁻², and 15.8 cm⁻²/(V s), respectively.     

Photoluminescence scanning on InAs/InGaAs quantum dot structures

The photoluminescence spectra of InAs quantum dots (QDs) embedded into four types of In_xGa_1−xAs/GaAs (x = 0.10, 0.15, 0.20 and 0.25) multi quantum well MBE structures have been investigated at 300 K in dependence on the QD position on the wafer. PL mapping was performed with 325 nm HeCd laser (35 mW) focused down to 200 μm (110 W/cm²) as the excitation source. The structures with x = 0.15 In/Ga composition in the In_xGa_1−xAs capping layer exhibited the maximum photoluminescence intensity. Strong inhomogeneity of the PL intensity is observed by mapping samples with the In/Ga composition of x ≥ 0.20-0.25. The reduction of the PL intensity is accompanied by a gradual “blue” shift of the luminescence maximum at 300 K as follows from the quantum dot PL mapping. The mechanism of this effect has been analyzed. PL peak shifts versus capping layer composition are discussed as well.     

Sb-mediated growth of high-density InAs quantum dots and GaAsSb embedding growth by MBE

Self-assembled InAs quantum dots (QDs) with high-density were grown on GaAs(0 0 1) substrates by antimony (Sb)-mediated molecular beam epitaxy technique using GaAsSb/GaAs buffer layer and InAsSb wetting layer (WL). In this Sb-mediated growth, many two-dimensional (2D) small islands were formed on those WL surfaces. These 2D islands provide high step density and suppress surface migration. As the results, high-density InAs QDs were achieved, and photoluminescence (PL) intensity increased. Furthermore, by introducing GaAsSb capping layer (CL), higher PL intensity at room temperature was obtained as compared with that InGaAs CL.     

Synthesis and nonlinear optical characterization of SnO2 quantum dots

The present paper demonstrates the preparation and characterization of SnO₂ semiconductor quantum dots. Extremely small ∼1.1 and ∼1.4 nm SnO₂ samples were prepared by microwave assisted technique with a frequency of 2450 MHz. Based on XRD analysis, the phase, crystal structure and purity of the SnO₂ samples are determined. UV-vis measurements showed that, for the both size of SnO₂ samples, excitonic peaks are obtained at ∼238 and ∼245 nm corresponding to ∼1.1 nm (sample 1) and ∼1.4 nm (sample 2) sizes, respectively. STM analysis showed that, the quantum dots are spherical shaped and highly monodispersed. At first, the linear absorption coefficients for two different sizes of SnO₂ quantum dots were measured by employing a CW He-Ne laser at 632.8 nm and were obtained about 1.385 and 4.175 cm⁻¹, respectively. Furthermore, the nonlinear refractive index, n₂, and nonlinear absorption coefficient, β, were measured using close and open aperture Z-scan respectively using the same laser. As quantum dots have strong absorption coefficient to obtain purely effective n₂, we divided the closed aperture transmittance by the corresponding open aperture in the same incident beam intensity. The nonlinear refraction indices of these quantum dots were measured in order of 10⁻⁷ (cm²/W) with negative sign and the nonlinear absorption coefficients were obtained for both in order of 10⁻³ (cm/W) with positive sign.     

Enhancement of L10 ordered FePt by Pt buffer layer

L₁₀-ordered FePt thin films prepared by molecular-beam epitaxy on MgO (0 0 1) substrate at 320 °C with different thickness of Pt buffer layer have been investigated. The out-of-plane coercivity increases with increasing thickness of Pt buffer. The maximum values of the long-range order parameter and uniaxial magnetic anisotropy energy are 0.72 and 1.78×10⁷ erg/cm³, respectively, for films with 12 nm thick Pt buffer layer, where the c/a ratio (0.976) shows the minimum value. The reason for the enhancement in ordering is due to the proper lattice strains Pt buffer bestows on FePt layer, these strains are equal to the contraction in lattice parameter c and the expansion in a. Studies of angular-dependent coercivity revealed that the magnetization reversal behaviour shifts from a domain-wall motion dominated case towards a near rotational mode with increasing thickness of Pt buffer layer.     

The emission wavelength tuning of InAs/InP quantum dots with thin GaAs, InGaAs, InP capping layers by MOCVD

InAs quantum dots (QDs) were grown on InP substrates by metalorganic chemical vapor deposition. The width and height of the dots were 50 and 5.8 nm, respectively on the average and an areal density of 3.0×10¹⁰ cm⁻² was observed by atomic force microscopy before the capping process. The influences of GaAs, In_0.53Ga_0.47As, and InP capping layers (5–10 ML thickness) on the InAs/InP QDs were studied. Insertion of a thin GaAs capping layer on the QDs led to a blue shift of up to 146 meV of the photoluminescence (PL) peak and an InGaAs capping layer on the QDs led to a red shift of 64 meV relative to the case when a conventional InP capping layer was used. We were able to tune the emission wavelength of the InAs QDs from 1.43 to 1.89 μm by using the GaAs and InGaAs capping layers. In addition, the full-width at half-maximum of the PL peak decreased from 79 to 26 meV by inserting a 7.5 ML GaAs layer. It is believed that this technique is useful in tailoring the optical properties of the InAs QDs at mid-infrared regime.     

Influence of AlN interfacial layer on electrical properties of high-Al-content Al0.45Ga0.55N/GaN HEMT structure

Unintentionally doped high-Al-content Al_0.45Ga_0.55N/GaN high electron mobility transistor (HEMT) structures with and without AlN interfacial layer were grown by metal-organic chemical vapor deposition (MOCVD) on two-inch sapphire substrates. The effects of AlN interfacial layer on the electrical properties were investigated. At 300 K, high two-dimensional electron gas (2DEG) density of 1.66 × 10¹³ cm⁻² and high electron mobility of 1346 cm² V⁻¹ s⁻¹ were obtained for the high Al content HEMT structure with a 1 nm AlN interfacial layer, consistent with the low average sheet resistance of 287 Ω/sq. The comparison of HEMT wafers with and without AlN interfacial layer shows that high Al content AlGaN/AlN/GaN heterostructures are potential in improving the electrical properties of HEMT structures and the device performances.     

Characterization of crystal lattice constant and dislocation density of crack-free GaN films grown on Si(1 1 1)

GaN have sphalerite structure (Cubic-GaN) and wurtzite structure (hexagonal GaN). We report the H-GaN epilayer with a LT-AlN buffer layer has been grown on Si(1 1 1) substrate by metal-organic chemical vapor deposition (MOCVD). According to the FWHM values of 0.166° and 14.01 cm⁻¹ of HDXRD curve and E₂ (high) phonon of Raman spectrum respectively, we found that the crystal quality is perfect. And based on the XRD spectrum, the crystal lattice constants of Si (a = 5.3354 ?) and H-GaN (a_epi = 3.214 ?, c_epi = 5.119 ?) have been calculated for researching the tetragonal distortion of the sample. These results indicate that the GaN epilayer is in tensile strain and Si substrate is in compressive strain which were good agreement with the analysis of Raman peaks shift. Comparing with typical values of screw-type (D_screw = 7 × 10⁸ cm⁻²) and edge-type (D_edge = 2.9 × 10⁹ cm⁻²) dislocation density, which is larger than that in GaN epilayers growth on SiC or sapphire substrates. But our finding is important for the understanding and application of nitride semiconductors.     

Studying the mechanism of ordered growth of InAs quantum dots on GaAs/InP

We study the mechanism of ordered growth of InAs quantum dots (islands) on a GaAs/InP substrate in theory and point out that the tensile strain can be used to control InAs/InP self-assembled quantum dots arrangement. Photoluminescence spectrum, and atomic force microscopy images have been investigated. In the experiment, ordered InAs islands have been obtained and the maximum density of quantum dots is 1.6×10¹⁰ cm⁻² at 4 monolayers InAs layer.     

Pulsed Nd:YAG laser depositions of ITO and DLC films for OLED applications

Indium-tin oxide (ITO) films deposited on heated and non-heated glass substrates by a pulsed Nd:YAG laser at 355 nm and ∼2.5 J/cm² were used in the fabrication of simple organic light-emitting diodes (OLEDs), ITO/(PVK + Alq₃ + TPD)/Al. The ITO was deposited on heated glass substrates which possessed resistivity as low as ∼3 × 10⁻⁴ Ω cm, optical transmission as high as ∼92% and carrier concentration of about ∼5 × 10²⁰ cm⁻³, were comparable to the commercial ITO. Substrate heating transformed the ITO microstructure from amorphous to polycrystalline, as revealed by the XRD spectrum. While the polycrystalline ITO produced higher OLED brightness, it was still lower than that on the commercial ITO due to surface roughness. A DLC layer of ∼1.5 nm deposited on this ITO at laser fluence of >12.5 J/cm² improved its device brightness by suppressing the surface roughness effect.     

Wetting layers effect on InAs/GaAs quantum dots

FEM combining with the K·P theory is adopted to systematically investigate the effect of wetting layers on the strain-stress profiles and electronic structures of self-organized InAs quantum dot. Four different kinds of quantum dots are introduced at the same height and aspect ratio. We found that 0.5 nm wetting layer is an appropriate thickness for InAs/GaAs quantum dots. Strain shift down about 3%∼4.5% for the cases with WL (0.5 nm) and without WL in four shapes of quantum dots. For band edge energy, wetting layers expand the potential energy gap width. When WL thickness is more than 0.8 nm, the band edge energy profiles cannot vary regularly. The electron energy is affected while for heavy hole this impact on the energy is limited. Wetting layers for the influence of the electronic structure is obviously than the heavy hole. Consequently, the electron probability density function spread from buffer to wetting layer while the center of hole's function moves from QDs internal to wetting layer when introduce WLs. When WLs thickness is larger than 0.8 nm, the electronic structures of quantum dots have changed obviously. This will affect the instrument's performance which relies on the quantum dots' optical properties.     

Microstructure and dielectric properties of La2O3 doped amorphous SiO2 films as gate dielectric material

As a potential gate dielectric material, the La₂O₃ doped SiO₂ (LSO, the mole ratio is about 1:5) films were fabricated on n-Si (0 0 1) substrates by using pulsed laser deposition technique. By virtue of several measurements, the microstructure and electrical properties of the LSO films were characterized. The LSO films keep the amorphous state up to a high annealing temperature of 800 °C. From HRTEM and XPS results, these La atoms of the LSO films do not react with silicon substrate to form any La-compound at interfacial layer. However, these O atoms of the LSO films diffuse from the film toward the silicon substrate so as to form a SiO₂ interfacial layer. The thickness of SiO₂ layer is only about two atomic layers. A possible explanation for interfacial reaction has been proposed. The scanning electron microscope image shows the surface of the amorphous LSO film very flat. The LSO film shows a dielectric constant of 12.8 at 1 MHz. For the LSO film with thickness of 3 nm, a small equivalent oxide thickness of 1.2 nm is obtained. The leakage current density of the LSO film is 1.54 × 10⁻⁴ A/cm² at a gate bias voltage of 1 V.     

The effect of the excitation and of the temperature on the photoluminescence circular polarization of AlInAs/AlGaAs quantum dots

In this paper, we present a study of photoluminescence (PL) from AlInAs/AlGaAs quantum dots (QDs) structures grown by molecular beam epitaxy. Specifically, we describe the effects of the temperature and of the excitation density on the photoluminescence circular polarization. We have found that the circular polarization degree depends on temperature. On the other hand, the study of the excitation density dependent circular polarization PL degree shows that the last increases in the case of the sample of weak dot density. However, in the case of large dot density, it is almost constant in the excitation density range from 0.116 W cm⁻² to 9 W cm⁻².     

Effect of CeO2 buffer layer thickness on the structures and properties of YBCO coated conductors

Biaxially textured YBa₂Cu₃O_7−x (YBCO) films were grown on inclined-substrate-deposited (ISD) MgO-textured metal substrates by pulsed laser deposition. CeO₂ was deposited as a buffer layer prior to YBCO growth. CeO₂ layers of different thickness were prepared to evaluate the thickness dependence of the YBCO films. The biaxial alignment features of the films were examined by X-ray diffraction 2θ-scans, pole-figure, ?-scans and rocking curves of Ω angles. The significant influence of the CeO₂ thickness on the structure and properties of the YBCO films were demonstrated and the optimal thickness was found to be about 10 nm. High values of T_c = 91 K and J_c = 5.5 × 10⁵ A/cm² were obtained on YBCO films with optimal CeO₂ thickness at 77 K in zero field. The possible mechanisms responsible for the dependence of the structure and the properties of the YBCO films on the thickness of the CeO₂ buffer layers are discussed.     

GaN/AlN quantum dot photodetectors at 1.3–1.5 μm

We have demonstrated GaN/AlN quantum dots (QD) photodetectors, relying on intraband absorption and in-plane carrier transport in the wetting layer. The devices operate at room temperature in the wavelength range 1.3–1.5 μm. Samples with 20 periods of Si-doped GaN QD layers, separated by 3 nm-thick AlN barriers, have been grown by plasma-assisted molecular-beam epitaxy on an AlN buffer on a c-sapphire substrate. Self-organized dots are formed by the deposition of 5 monolayers of GaN under nitrogen-rich conditions. The dot height is 1.2±0.6 to 1.3±0.6 nm and the dot density is in the range 10¹¹–10¹² cm⁻². Two ohmic contacts were deposited on the sample surface and annealed in order to contact the buried QD layers. The dots exhibit TM polarized absorption linked to the s–p_z transition. The photocurrent at 300 K is slightly blue-shifted with respect to the s–p_z intraband absorption. The responsivity increases exponentially with temperature and reaches a record value of 10 mA/W at 300 K for detectors with interdigitated contacts.     

Dependence of surface distribution of self-assembled InSb nanodots on surface morphology and spacer layer thickness

Self-assembled InSb nanodots (NDs) were grown on a GaSb (1 0 0) substrate using metal-organic vapour phase epitaxy (MOVPE). The effects of etching depth of the substrate and thickness of the GaSb buffer layer on the density and size distribution of single and double layer dots were studied for detector applications. The etch depth of the substrate was varied up to 30 μm. In this particular study, the dots were grown at 450 °C and the GaSb spacer thickness was varied between 50 nm and 200 nm. The optimum substrate etch depth was found to be 30 μm while the best spacer thickness was found to be 200 nm.     

Strain and optical transitions in InAs quantum dots on (001) GaAs

To investigate the strain characteristics of InAs quantum dots grown on (001) GaAs by solid source molecular beam epitaxy we have compared calculated transition energies with those obtained from photoluminescence measurements. Atomic force microscopy shows the typical lateral size of the quantum dots as 20–22 nm with a height of 10–12 nm, and photoluminescence spectra show strong emission at 1.26 μ m when the sample is capped with a GaAs layer. The luminescence peak wavelength is red-shifted to 1.33 μ m when the dots are capped by an In_0.4Ga_0.6As layer. Excluding the strain it is shown that the theoretical expectation of the ground-state optical transition energy is only 0.566 eV (2.19 μ m), whereas a model with three-dimensionally-distributed strain results in a transition energy of 0.989 eV (1.25 μ m). It has thus been concluded that the InAs quantum dot is spatially strained. The InGaAs capping layer reduces the effective barrier height so that the transition energy becomes red-shifted.     

Densely packed Ge quantum dots grown on SiO2/Si substrate

We studied the growing process of Ge dots on silicon substrates covered with an ultrathin silicon dioxide buffer layer which was formed with simple chemical procedure. Uniform and densely packed (10¹¹ cm⁻²) quantum dots (QDs) were obtained by optimizing the growth parameter with the MBE method. The influence of temperature, coverage, as well as the post-annealing process, on the epitaxial and non-epitaxial nanodots formation was evaluated. Nano-sized high density quantum dots were also realized with different growing conditions, whose structural and growing mechanism were discussed under the help of SEM and RHEED results.     

Optical transitions of InAs/In0.36Ga0.64As/GaAs(311B) surface quantum dots clearly identified by the piezoreflectance technique

The bilayer InAs/In_0.36Ga_0.64As/GaAs(311B) quantum dots (QDs), including one InAs buried quantum dot (BQD) layer and the other InAs surface quantum dot (SQD) layer, have been grown by molecular beam epitaxy (MBE). The optical properties of these three samples have been studied by the piezoreflectance (PzR) spectroscopy. The PzR spectra do not exhibit only the optical transitions originated from the InAs BQDs, but the features originated from the InAs SQDs. After the InAs SQDs have been removed chemically, those optical transitions from InAs SQDs have been demonstrated clearly by investigating the PzR spectra of the residual InAs BQDs in these samples. The great redshift of these interband transitions of InAs SQDs has been well discussed. Due to the suitable InAs SQD sizes and the thickness of In_0.36Ga_0.64As layer, the interband transition of InAs SQDs has been shifted to ∼1.55 μm at 77 K.