Self-assembled one-pot synthesis of red luminescent CdS:Mn/Mn(OH)2 nanoparticles

We report a novel method of growing red luminescent (635 nm) Mn-doped CdS (CdS:Mn) nanoparticles capped by an inorganic shell of Mn(OH)₂. CdSO₄, Na₂S₂O₃ and Mn(NO₃)₂ were used as the precursors, and thioglycerol (C₃H₈O₂S) was employed as the capping agent and also the catalyst of the reaction. Using these materials resulted in very slow rate of the reaction and particles growth. The self-assembled one-pot process was performed at pH of 8 and Mn:Cd ratio of 10, and took about 10 days for completion. CdS:Mn nanoparticles are slowly formed in the first day of the process; however, the luminescence is weak. After 7 days, the solution turns white turbid through the formation of additional particles, which precipitate on the walls on the next day. At this stage, a relatively strong red luminescence at 635 nm appears from transparent solution of the CdS:Mn nanoparticles. The white deposit on the walls turns to dark-brown color and luminescence increases on the 9th day. Finally, the CdS:Mn nanoparticles agglomerate and precipitate out of the solution on 10th day. X-ray diffraction and optical spectroscopy showed crystalline phase CdS nanoparticles with an average size of 3.6 nm. We explain the luminescence enhancement based on the formation of a Mn(OH)₂ shell on the surface of the CdS:Mn nanoparticles during the precipitation stage. This can passivate the S dangling bonds located on the particles surface. As the surface Cd sites are previously capped with thioglycerol molecules, a complete surface passivation is achieved and results in emergence of high-intensity luminescence.     

Porous ZnO nanobelts evolved from layered basic zinc acetate nanobelts

Novel porous ZnO nanobelts were successfully synthesized by heating layered basic zinc acetate (LBZA) nanobelts in the air. The precursor of LBZA nanobelts consisted of a lamellar structure with two interlayer distances of 1.325 and 0.99 nm were prepared using a low-temperature, solution-based method. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and infrared spectroscopy are used to characterize the as-products. PL measurements show that the porous ZnO nanobelts have strong ultraviolet emission properties at 380 nm, while no defect-related visible emission is detected. The good performance for photoluminescence emission makes the porous ZnO nanobelts promising candidates for photonic and electronic device applications.     

Abnormal blueshift of UV emission in single-crystalline ZnO nanowires

Single-crystalline ZnO nanowires (NWs) were synthesized by a facile vapor transport method. The good orientation and high crystal quality were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and high-resolution transmission electron microscope (HRTEM) measurements. Excitation-power-dependence photoluminescence spectra of ZnO NWs show that the UV emission displayed an evident blueshift with increasing excitation power and the corresponding energy shift might be as large as 10 meV. This anomalous phenomenon correlates to the band bending level caused by the surface built-in electric field due to the existence of substantial oxygen vacancies. By increasing the excitation power, the enhanced neutralization effect near the surface will reduce the built-in electric field and lead to a reduction of band bending which triggers the blueshift of the UV emission.     

Effects of thermal annealing temperature and duration on hydrothermally grown ZnO nanorod arrays

In this study, the effects of thermal annealing temperature and duration on ZnO nanorod arrays fabricated by hydrothermal method were investigated. The annealed ZnO/Si(1 1 1) substrate was used for ZnO nanorod array growth. The effects of annealing treatment on the structural and optical properties were investigated by scanning electron microscopy, X-ray diffraction, and room-temperature photoluminescence measurements. With the annealing temperature of 750 °C and the annealing duration of 10 min, both the structural and optical properties of the ZnO nanorod arrays improved significantly, as indicated in the X-ray diffraction and photoluminescence measurement.     

Band-edge photoluminescence in nanocrystalline ZnO:In films prepared by electrostatic spray deposition

ZnO:In films are successfully prepared by using the electrostatic spray deposition technique. X-ray diffraction indicates that the ZnO:In films have a polycrystalline hexagonal wurtzite structure with lattice parameters a=3.267 Å and c=5.209 Å. Photoluminescence properties of the films are investigated in the temperature range of 11.6-300 K, showing strong luminescence in the whole range of temperature. The temperature dependence of the photoluminescence are carried out with full profile fitting of spectra, which clearly shows that the ultraviolet (UV) emission in In-doped ZnO films at low temperature are attributed to emission of a neutral donor-bound exciton (D^°X) and recombination of donor-acceptor pairs (DAP), while the UV emission at room temperature originates from radiative transition of an electron bound on a donor to the valence band.     

Properties of ZnO thin films grown on Si substrates in vacuum and oxygen ambient by pulsed laser deposition

Epitaxial ZnO thin films have been synthesized directly on Si(1 1 1) substrates by pulsed laser deposition (PLD) in vacuum. The reflection high-energy electron diffraction (RHEED) indicates that streaky patterns can be clearly observed from the ZnO epilayers prepared at 600 and 650 °C, revealing a two-dimensional (2D) growth mode. While the ZnO thin film deposited in oxygen ambient shows ring RHEED pattern. There is a compressive in-plane stress existing in the ZnO epitaxial film, but a tensile one in the polycrystalline film. Compared with the ZnO epilayer, the ZnO polycrystalline film shows more intense ultraviolet emission (UVE) with a small full width at half maximum (FWHM) of 89 meV. It is suggested that the atomically flat epilayers may be powerfully used as transitive stratums to grow high-quality ZnO films suitable for the fabrication of optoelectronic devices.     

Synthesis and optical properties of Co-doped ZnO nanofibers prepared by electrospinning

In this work, Co-doped ZnO nanofibers have been fabricated successfully by an electrospinning technique. The as-prepared nanofibers are characterized by themogravimetric analysis (TG), scanning electron microscopy (SEM), transmission electron microscopy (TEM), powder X-ray diffraction (XRD), Raman spectra and photoluminescence spectroscopy (PL). Results have showed that a wurtzite ZnO nanofibers were obtained and the PL spectrum showed a red-shift by 10 nm due to narrowing of the ZnO band gap (∼3.29 eV) as a result of Co doping. Meanwhile, Raman scattering spectra exhibited an unusual peak at 540 cm⁻¹.     

Effects of buffer layer annealing temperature on the structural and optical properties of hydrothermal grown ZnO

ZnO was deposited on bare Si(1 0 0), as-deposited, and annealed ZnO/Si(1 0 0) substrates by hydrothermal synthesis. The effects of a ZnO buffer layer and its thermal annealing on the properties of the ZnO deposited by hydrothermal synthesis were studied. The grain size and root mean square (RMS) roughness values of the ZnO buffer layer increased after thermal annealing of the buffer layer. The effect of buffer layer annealing temperature on the structural and optical properties was investigated by photoluminescence, X-ray diffraction, atomic force microscopy, and scanning electron microscopy. Hydrothermal grown ZnO deposited on ZnO/Si(1 0 0) annealed at 750 °C with the concentration of 0.3 M exhibits the best structural and optical properties.     

Effects of annealing atmosphere on the luminescent efficiency of ZnTe:O phosphors

The effect of the annealing atmosphere on the luminescent efficiency of ZnTe:O phosphors for X-ray imaging applications was studied. The phosphors were doped by ball-milling bulk ZnTe crystals in an O₂ atmosphere and annealed in various atmospheres: vacuum, N₂ or forming gas (95%N₂/5%H₂). All samples exhibited a deep red emission centered at 680 nm.The samples annealed in forming gas atmosphere exhibited an X-ray luminescent efficiency five times higher than the samples annealed in vacuum or N₂ atmospheres, which was attributed to the removal of surface tellurium oxides.     

Photoluminescence characteristics of ZnO doped with Eu powders

In this work, we have investigated the photoluminescence spectra of europium-doped zinc oxide crystallites prepared by a vibrating milled solid-state reaction method. X-ray diffraction, scanning electron microscopy, luminescence spectra and time-resolved spectra analysis were used to characterize the synthetic ZnO:Eu³⁺ powders. XRD results of the powders showed a typical wurtzite hexagonal crystal structure. A second phase occurred at 5 mol% Eu₂O₃-doped ZnO. The ⁵D₀-⁷F₁ (590 nm) and ⁵D₀-⁷F₂ (609 nm) emission characteristics of Eu³⁺ appeared after quenching with more than 1.5 mol% Eu₂O₃ doping. The Commission Internationale d’Eclairage (CIE) chromaticity coordinates of a ZnO:Eu³⁺ host excited at λ_ex=467 nm revealed a red-shift phenomenon with increase in Eu³⁺ ion doping. The lifetime of the Eu³⁺ ion decreased as the doping concentration was increased from 1.5 to 10 mol%, and the time-resolved ⁵D₀→⁷F₂ transition presents a single-exponential decay behavior.     

Formation of Al-N co-doped p-ZnO/n-Si (1 0 0) heterojunction structure by RF co-sputtering technique

Al-N co-doped ZnO (ZnO:Al-N) thin films were grown on n-Si (1 0 0) substrate by RF co-sputtering technique. As-grown ZnO:Al-N film exhibited n-type conductivity whereas on annealing in Ar ambient the conduction of ZnO:Al-N film changes to p-type, typically at 600 °C the high hole concentration of ZnO:Al-N co-doped film was found to be 2.86 × 10¹⁹ cm⁻³ and a low resistivity of 1.85 × 10⁻² Ω-cm. The current-voltage characteristics of the obtained p-ZnO:Al-N/n-Si heterojunction showed good diode like rectifying behavior. Room temperature photoluminescence spectra of annealed co-doped films revealed a dominant peak at 3.24 eV.     

Formation of hexagonal shaped wurtzite zinc sulphide nano rods

Zinc sulfide nanorods with good photoluminescence have been successfully fabricated using a simple sol-gel process via ultrasonication, with mercaptoethanol as capping agent. The formation of ZnS nucleation, followed by subsequent growth, is significant in obtaining highly oriented ZnS nanorods. Temperature, time, and capping agent also proved to be significant factors in the growth of ZnS nanorods and greatly affect their photo luminescent properties. X-ray diffraction (XRD) analysis, low and high-resolution transmission electron microscopy (TEM & HRTEM), selected-area electron diffraction (SAED) pattern, and scanning electron microscopy (SEM) indicated that the ZnS nanorods were single crystal in nature and that they had grown up preferentially along the [0001] direction. This simple method of nucleation, followed by their successive growth, resulted in the development of an effective and low-cost fabrication process for high-quality ZnS nanorods with good photo luminescent properties that can be applied to luminescent sensors and optoelectronic devices.     

Effect of Mn doping on the microstructures and photoluminescence properties of CBD derived ZnO nanorods

Mn-doped ZnO nanorods were synthesized from aqueous solutions of zinc nitrate hexahydrate, manganese nitrate and methenamine by the chemical solution deposition method (CBD). Their microstructures, morphologies and optical properties were studied in detail. X-ray diffraction (XRD) results illustrated that all the diffraction peaks can be indexed to ZnO with the hexagonal wurtzite structure. Scanning electron microscope (SEM) results showed that the average diameter of Mn-doped ZnO nanorods was larger than that of the undoped one. Photoluminescence (PL) spectra indicated that manganese doping suppressed the emission intensity and caused the blue shift of UV emission position compared with the undoped ZnO nanorods. In the Raman spectrum of Mn-doped ZnO nanorods, an additional mode at about 525 cm⁻¹ appeared which was significantly enhanced and broadened with the increase of Mn doping concentration.     

Effects of crystalline quality on the ultraviolet emission and electrical properties of the ZnO films deposited by magnetron sputtering

The ZnO films were deposited on c-plane sapphire, Si (0 0 1) and MgAl₂O₄ (1 1 1) substrates in pure Ar ambient at different substrate temperatures ranging from 400 to 750 °C by radio frequency magnetron sputtering. X-ray diffraction, photoluminescence and Hall measurements were used to evaluate the growth temperature and the substrate effects on the properties of ZnO films. The results show that the crystalline quality of the ZnO films improves with increasing the temperature up to 600 °C, the crystallinity of the films is degraded as the growth temperature increasing further, and the ZnO film with the best crystalline quality is obtained on sapphire at 600 °C. The intensity of the photoluminescence and the electrical properties strongly depend on the crystalline quality of the ZnO films. The ZnO films with the better crystallinity have the stronger ultraviolet emission, the higher mobility and the lower residual carrier concentration. The effects of crystallinity on light emission and electrical properties, and the possible origin of the n-type conductivity of the undoped ZnO films are also discussed.     

Influence of annealing atmosphere on ZnO thin films grown by MOCVD

ZnO films were deposited on c-plane sapphire substrates by metal-organic chemical vapor deposition (MOCVD). Annealing treatments for as-deposited samples were performed in different atmosphere under various pressures in the same chamber just after growth. The effect of annealing atmosphere on the electrical, structural, and optical properties of the deposited films has been investigated by means of X-ray diffraction (XRD), atomic force microscope (AFM), Hall effect, and optical absorption measurements. The results indicated that the electrical and structural properties of the films were highly influenced by annealing atmosphere, which was more pronounced for the films annealed in oxygen ambient. The most significant improvements for structural and electrical properties were obtained for the film annealed in oxygen under the pressure of 60 Pa. Under the optimum annealing condition, the lowest resistivity of 0.28 Ω cm and the highest mobility of 19.6 cm² v⁻¹ s⁻¹ were obtained. Meanwhile, the absorbance spectra turned steeper and the optical band gap red shifted back to the single-crystal value.     

Synchrotron radiation assistant MOCVD deposition of ZnO films on Si substrate

The growth of ZnO film on Si(1 0 0) substrate has been studied with synchrotron radiation (SR) assisted MOCVD method. The diethylzinc (DEZn) and CO₂ are used as source materials, while Nitrogen is employed as a carrier gas for DEZn. With the assistance of SR the ZnO film can be deposited even at room temperature. XRD, SEM and photoluminescence (PL) studies show that the crystal quality of ZnO films grown with the assistance of SR is higher than that of those without SR assistance. The growth mechanism of ZnO film with the SR assistant MOCVD system is primarily discussed.     

Properties of ZnO thin films grown on Si substrates by photo-assisted MOCVD

ZnO thin films were grown on (1 0 0) p-Si substrates by Photo-assisted Metal Organic Chemical Vapor Deposition (PA-MOCVD) using diethylzinc (DEZn) and O₂ as source materials and tungsten-halogen lamp as a light source. The effects of tungsten-halogen lamp irradiation on the surface morphology, structural and optical properties of the deposited ZnO films have been investigated by means of atomic force microscope (AFM), X-ray diffraction and photoluminescence (PL) spectra measurements. Compared with the samples without irradiation, the several characteristics of ZnO films with irradiation are improved, including an improvement in the crystallinity of c-axis orientation, an increase in the grain size and an improvement in optical quality of ZnO films. These results indicated that light irradiation played an important role in the growth of ZnO films by PA-MOCVD.     

Room temperature electroluminescence from ZnO/Si heterojunction devices grown by metal-organic chemical vapor deposition

Heterojunction light-emitting diodes with ZnO/Si structure were fabricated on both high-resistivity (p) and low-resistivity (p⁺) Si substrates by metal-organic chemical vapor deposition technology. Fairly good rectifications were observed from the current-voltage curves of both heterojunctions. Ultraviolet (UV) and blue-white electroluminescence (EL) from ZnO layer were observed only from ZnO/p⁺-Si heterojunction under forward bias at room temperature (RT), while strong infrared (IR) EL emissions from Si substrates were detected from both ZnO/p-Si and ZnO/p⁺-Si heterojunctions. The UV and IR EL mechanisms have been explained by energy band structures. The realization of RT EL in UV-visible and IR region on Si substrate has great applicable potential for Si-based optoelectronic integrated circuits.     

Fabrication of ZnO nanostructures of various dimensions using patterned substrates

ZnO nanostructures were grown on silicon, porous silicon, ZnO/Si and AlN/Si substrates by low-temperature aqueous synthesis method. The shape of nanostructures greatly depends on the underlying surface. Scattered ZnO nanorods were observed on silicon substrate, whereas aligned ZnO nanowires were obtained by introducing sputtered ZnO film as a seed layer. Furthermore, both the combination of nanorods and the bunch of nanowires were found on porous silicon substrates, whereas platelet-like morphology was observed on AlN/Si substrates. XRD patterns suggest the crystalline nature of aqueous-grown ZnO nanostructures and high-resolution transmission electron microscopy images confirm the single-crystalline growth of the ZnO nanorods along [0 0 1] direction. Room-temperature photoluminescence characterization clearly shows a band-edge luminescence along with a visible luminescence in the yellow spectral range.     

Microemulsion-mediated synthesis of cadmium zinc sulfide nanocrystals with composition-modulated optical properties

Cadmium zinc sulfide nanocrystals were synthesized by a microemulsion-mediated process, which involving two steps: the preparation of CdS (or ZnS) seeds and the succedent hydrothermal growth of ZnS (or CdS) component. The XRD results show that the cadmium zinc sulfide nanocrystals with CdS seeds present a hexagonally homogeneous alloyed structure, while the ones with ZnS seeds mainly take on the characteristic of hexagonal CdS nanocrystals. The intrinsic factors influencing the crystal structures were discussed. The UV-vis and photoluminescence (PL) spectra indicate that the optical properties of the obtained nanocrystals with CdS seeds can be continuously modulated by tuning their compositions, although their sizes and size distributions are not under a strict control. The composition-modulated strategy, along with the hydrothermal microemulsion process, will be an effective route to achieve semiconductor nanocrystals with tunable optical properties under more manageable conditions.