Electrical resistivity and superconductivity of amorphous La−Ag alloys

We report on measurements of the electrical resistivity and the superconducting transition temperature of amorphous La–Ag alloys (60–74 at % La) obtained by liquid quenching. The temperature coefficient of the resistivity is always slightly negativ, its value cannot be described well by existing theories.T _c depends linearly on the La content and seems to be not very sensitive to the second alloy constituent.Dedicated to Prof. Dr. W. Buckel on the occasion of his 60th birthday     

Measurement of the Electric Quadrupole Moment of the 9/2− and 21/2− Isomers in 173Ta

The electric quadrupole moments of the 9/2⁻ and 21/2⁻ isomeric states of ¹⁷³Ta at 165.8 keV and 1713.2 keV, respectively, were measured as Q(9/2⁻)=2.92(15) b and Q(21/2⁻)=6.23(18) b for the first time using the TDPAD technique. A 66 MeV pulsed ¹²C ion beam from the 15UD pelletron accelerator facility of the Nuclear Science Centre at New Delhi was used in the reaction ¹⁶⁵Ho(¹²C, 4nγ)¹⁷³Ta. The experimental values of equilibrium deformations β₂(9/2⁻)=0.251(7) and β₂(21/2⁻)=0.391(7) were extracted. This revised version was published online in July 2006 with corrections to the Cover Date.     

Evidence for a double charge transfer contribution to SERS in the Ag/Ag (CN)2− system

Using a square wave potential perturbation and monitoring the Raman intensity in parallel, the potential dependence of Ag(CN)₂⁻ spectra was studied with different exciting wavelengths. A double peak structure was found for the C-N stretch frequency both peaks having different excitation characteristics. In addition, the quenching rate of ad-complexes was measured at negative potentials together with the activation energy. From E_A = 75 kJ mol⁻, the energy of an acceptor level can be estimated located about 3 eV above E_F. This level presumably corresponds to the Ag 5s orbital which is shifted upwards due to the interaction with the ligands of the ad-complex. Since the CN⁻ 5σ or 1π orbitals form a donor level, the possibility of a double charge transfer contribution to the SERS enhancement exists.     

Percolation and electrical resistivity in the YBa2Cu3O7−Ag composite system

We have measured the resistivity of the YBa₂Cu₃O₇–Ag composite system with Ag volume fraction,p _Ag ranging from 0–100%. The percolation behavior and the normal-state resistivity are studied. We find a three-dimensional threshold for the Ag matrix occurring atp _Ag 20% and a threshold for the superconducting matrix occurring at 1–p _Ag30%. The electrical resistivity is interpreted in terms of a resistivity model for granular YBa₂Cu₃O₇ proposed by Halbritter et al. [Z. Phys. B —Condensed Matter71, 411 (1988)]. Based on this model, we show that the resistivities between the YBa₂Cu₃O₇ grains and flaws in the grains are greatly diminished in the samples, indicating significantly improved grain growth behavior of the YBa₂Cu₃O₇ phase resulting from the addition of Ag. With the diminishing of the grain boundary resistivities, an intrinsic value for the temperature coefficient of resistivity, (1/gr)(d/dT), can be inferred, which is 3.3×10^–3/K at 300 K. This value is very close to that observed in the Cu–O₂ planes in single crystals and epitaxial films of YBa₂Cu₃O₇.     

Synthesis of Ag metallic nanoparticles by 120 keV Ag− ion implantation in TiO2 matrix

TiO₂ thin film synthesized by the RF sputtering method has been implanted by 120 keV Ag^? ion with different doses (3?×?10¹⁴, 1?×?10¹⁵, 3?×?10¹⁵, 1?×?10¹⁶ and 3?×?10¹⁶ ions/cm²). Further, these were characterized by Rutherford back Scattering, XRD, X-ray photoelectron spectroscopy (XPS), UV–visible and fluorescence spectroscopy. Here we reported that after implantation, localized surface Plasmon resonance has been observed for the fluence 3?×?10¹⁶ ions/cm², which was due to the formation of silver nanoparticles. Ag is in metallic form in the matrix of TiO₂, which is very interestingly as oxidation of Ag was reported after implantation. Also, we have observed the interaction between nanoparticles of Ag and TiO₂, which results in an increasing intensity in lower charge states (Ti³⁺) of Ti. This interaction is supported by XPS and fluorescence spectroscopy, which can help improve photo catalysis and antibacterial properties.     

Experimental and theoretical investigations of the Knight shift of Pd and Ag in the alloy system Ag x Pd1−x

The Knight shift of Pd in Ag _x Pd_1–x has been determined for concentrationsx0.2. In full accordance with the expectations based on the behaviour of the magnetic susceptibility, it was found that the Knight shift of Pd is rapidly reduced in magnitude by adding Ag to Pd. To allow for a detailed interpretation of this finding, we have performed Korringa-Kohn-Rostoker coherent potential approximation (KKR-CPA) band structure calculations for Ag _x Pd_1–x . These calculations clearly demonstrate that the decrease in spin susceptibility with increasingx is accompanied with a decrease in core polarization. In contrast to Pd, the negative Knight shift of Ag on the Pd-rich side of the system is caused by the valence band contribution, as it is demonstrated by our calculations. This is caused by an intersite effect in analogy to the transferred hyperfine field found for non-magnetic elements dissolved in a magnetic host.     

Vibrational-electronic coupling in IrF6, OsCl6 2− and IrCl6 2−

The results obtained in a previous paper [1] for an unsymmetric regular model are applied to solid hydrogen at low temperatures when the lattice structure and the quadrupole-quadrupole interaction make the interaction energies non-isotropic. It is shown that, as for the lattice structures with isotropic interactions, no second-order transition is likely to occur through a cooperative rotational effect. The possible occurrence of spatial ordering on sub-lattices is discussed. It is found that such ordering is unlikely to occur at low temperatures on the face-centred cubic lattice, but that on the hexagonal close-packed lattice (which is the probable crystal structure) there is a second-order transition to an ordered state. Using a zeroth-order approximation the temperature at which this transition occurs in pure ortho-hydrogen is found to be 5·8°k.     

Doublet and quartet states of Li 2 −

Electronic states of the molecular lithium anion are investigated by configuration-interaction calculations. Comparison with the analogously computed potential energy curves for the lowest singlet and triplet states of the neutral Li₂ shows that in addition to the well-known stable ground state X there also exist metastable excited states of Li ₂ ^- . Within the quartet sector, two candidates for such long-lived states are identified and their spectroscopic properties studied. Received 23 March 1999     

Electrical properties and electronic structure of Cu1−xZnxInSe2 and Cu1−xZnxInS2 single crystals

Temperature dependence of the electrical conductivity of CuInS₂–ZnIn₂S₄ and CuInSe₂–ZnIn₂Se₄ solid solutions possessing n-type conductivity has been studied. It has been established that when the temperature decreases down to ~100 to 27 K, the hopping mechanism of electrical conductivity with a variable jumping length between localized states positioned in a narrow energy band near the Fermi level becomes dominant. The main parameters of the hopping conductivity have been determined. At higher temperatures (150–300 K), in the CuInSe₂–ZnIn₂Se₄ single crystals containing 15 and 20 mol% ZnIn₂Se₄ the thermally activated conductivity with activation energy of 0.018 and 0.04 eV, respectively, is detected. Among the CuInSe₂–ZnIn₂Se₄ single crystals, samples with 5 and 10 mol% ZnIn₂Se₄ were found to be close to degenerate semiconductors. Temperature dependences of the electrical conductivity of CuInS₂–ZnIn₂S₄ single crystals are described by a more complicated function that may indicate a competition of several conduction mechanisms in these compounds. For the CuInS₂–ZnIn₂S₄ solid solutions, X-ray photoelectron core-level and valence-band spectra have been measured for both pristine and Ar⁺ ion-bombarded surfaces. Our results indicate that the Cu_1−xZn_xInS₂ single-crystal surfaces are sensitive to Ar⁺ ion-bombardment. Additionally, for the Cu_1−xZn_xInS₂ crystal with the highest ZnIn₂S₄ content, namely 12 mol% ZnIn₂S₄, the X-ray emission bands representing the energy distribution of the Cu 3d, Zn 3d and S 3p states have been measured and compared on a common energy scale with the X-ray photoelectron valence-band spectrum.     

Comparative study of aerogels nanostructured catalysts: Ni/ZrO2–SO4 2− and Ni/ZrO2–Al2O3–SO4 2−

Ionics - A series of Ni/ZrO2–SO4 2− and Ni/ZrO2–Al2O3–SO4 2− catalysts were prepared in one step by the sol–gel method and dried in hypercritical conditions of...     

Magnetic and structural transition of Ni50+xMn25−x/2Ga25−x/2 (x=2–5) alloys

Magnetic and structural transitions of non-stoichiometric Ni_50+xMn_25−x/2Ga_25−x/2 (x=2–5) alloys are systematically investigated. Differential scanning calorimetry and modified thermogravimetry (TG) are used to measure magnetic and structural transitions simultaneously. The structural transition temperatures increase monotonically with increasing Ni substitution for Mn and Ga. Different magnetic transition sequences on heating were observed from ferromagnetic martensite to ferromagnetic autensite, then to paramagnetic autensite, from ferromagnetic martensite to paramagnetic austensite or from ferromagnetic martensite to paramagnetic martensite, respectively. Three kinds of NiMnGa alloys were obtained according to the sequence of the structural and magnetic transition, whose structural transition temperatures are lower, equal to or higher than the magnetic transition temperatures.     

New pulse sequences for T1− and T1/T2−contrast enhancing in NMR imaging

Improved pulse sequences DIFN (abbreviation of the words: DIFferentiation by N pulses), 90° − τ₁ − 180° − τ₁ − … 180° − τ_n, with optimised time intervals τ₁ for T₁ measurement and contrast enhancing in NMR imaging are presented. The pulse sequences DIFN have a better sensitivity to T₁ than the well-known pulse sequence SR. In contrast to the IR pulse sequence, the information given by the DIFN pulse sequence is more reliable, because the NMR signal does not change its sign. For a given time interval τ₀ ≤ (0.1 − 0.3) T₁′ the DIFN pulse sequences serve as T₁-filters. They pass the signal components with relatively short T₁ < T₁′ and suppress the components with relatively long T₁ < T₁′. The effects of the radiofrequency field inhomogeneity and inaccurate adjusting of pulse lengths are also considered. It is also proposed in this work to use the joint T₁T₂-contrast in NMR imaging obtained as a result of applying the DIFN pulse sequences in combination with the well-known Carr-Purcell-Meiboom-Gill (CPMG) pulse sequence. The region of interest, where the contrast should be especially enhanced, is specified by the two times at which measurements are performed, which allow the amplitudes of pixels to reach some defined levels by spin-lattice and spin-spin relaxation.     

Two-photon transitions of Ag− centers in KBr

Abstract

Two-photon excitation spectra of Ag^? centers in KBr have been measured. The main excitation peak appears only with linearly polarized excitation and has been assigned to the ¹A_1g → ¹A_1g transition. Weaker structures have a polarization dependence corresponding to ¹A_1g → ¹E _g and ¹A_1g → ¹T_2g transitions.     

Red emitting centre in Ag1−xCuxI

Investigations of the red emission at 625 nm in Ag_1−xCu_xI for x from 0.6 to 0.95 have shown that the excitation spectra for this peak are significantly different from those of the other emission peaks. Substantially enhanced emission intensities are observed for the 625 nm peak excited by 395 nm radiation. The intensity of the 625 nm emission peak relative to those of the other emission peaks at 445–460, 485 and 525 nm is significantly increased. In the x=0.6 sample, the 625 nm emission displaces the 485 nm emission, dominant on excitation at 230 nm, as the major peak. A model is proposed to account for the red emission based on the coexistence of Cu²⁺ and Ag⁺ at the higher CuI concentrations, whilst its disappearance at higher AgI concentrations is attributed to Ag occupying interstitial sites.     

Structure and phase stability of nanocrystalline Ce1−x Ln x O2−x/2−δ (Ln = Yb, Lu) in oxidizing and reducing atmosphere

The structure and phase evolution of nanocrystalline Ce_{1− x} Ln _x O_{2− x/2−δ} (Ln = Yb, Lu, x = 0 − 1) oxides upon heating in H₂ was studied for the first time. Up to 950 °C the samples were single-phase, with structure changing smoothly with x from fluorite type (F) to bixbyite type (C). For the Lu-doped samples heated at 1100 °C in the air and H₂, phase separation into coexisting F- and C-type structures was observed for ~0.40 < x < ~0.70 and ~0.25 < x < ~0.70, respectively. It was found also that addition of Lu³⁺ and Yb³⁺ strongly hinders the crystallite growth of ceria during heat treatment at 800 and 950 °C in both atmospheres. Valency of Ce and Yb in Ce_0.1Lu_0.9O_1.55−δ and Ce_0.95Yb_0.05O_1.975−δ samples heated at 1100 °C was studied by XANES and magnetic measurements. In the former Ce was dominated by Ce⁴⁺, with small contribution of Ce³⁺ after heating in H₂. In the latter, Yb existed exclusively as 3+ in both O₂ and H₂.     

Thermophoresis-assisted vapour phase synthesis of CeO2 and CexY1−xO2−δ nanoparticles

Thermophoresis-assisted chemical vapour deposition (CVD) was used to produce nano-sized particles of ceria and yttria-doped ceria. The solid precursors cerium trichloride and yttrium trichloride were used with oxygen. After homogeneous nucleation, condensation and coagulation, thermophoresis-assisted particle collection was achieved in two different ways. Particle dimensions were studied by transmission electron microscopy (TEM) and X-ray diffraction (XRD)-line broadening. Crystallite and particle dimensions varied from 9 to 30 nm and from 30 to 80 nm, respectively. The influence of process conditions is discussed.     

TiO_2/石墨烯/Ag复合结构SERS实验

基于氧化物半导体的光催化特性,能够降解有机物分子,使表面增强拉曼散射基底得以重复使用。提出了银纳米颗粒有效修饰覆盖有石墨烯的二氧化钛纳米棒阵列(TiO_2/石墨烯/Ag)复合结构作为表面增强拉曼散射基底,并对其进行了实验研究。利用水热法制备了二氧化钛纳米棒阵列;采用湿法转移石墨烯和光照还原方法制备了TiO_2/石墨烯/Ag复合结构。用罗丹明6G(R6G)分子作为探测分子,结果表明:随着紫外光照沉积时间增加,探针分子的拉曼信号先增强后减弱;计算得到最大增强因子值约为2.6×106。此外,还对TiO_2/石墨烯/Ag复合结构的紫外自清洁特性进行了初步实验,结果表明,紫外光照射20min后,其拉曼强度下降到42.3%,具有一定的紫外清洁效果。     

基于Ag/Ge/Ag阳极的as

通过在Ag层中引入一层Ge薄膜, 获得了具有低反射率和高反射相移的Ag/Ge/Ag复合阳极, 并制备了基于该阳极的蓝光顶发射有机电致发光器件.阳极高的反射相移使得器件在有机层厚度为100 nm时获得了顶发射蓝光发射, 且阳极较低的反射率减弱了器件内的微腔效应, 使得其电致发光光谱在不同视角下具有良好的稳定性.当Ge的厚度为20 nm时, 器件性能表现最为优良, 最高亮度和最大电流效率分别可达3 612 cd/m²和5.4 cd/A, 且色坐标在视角从0°变化到60°时仅移动了(0.007, 0.006).     

Diffusion and point defects in TiO2−x

The self-diffusion of ⁴⁴Ti has been measured both parallel to and perpendicular to the c axis in rutile single crystals by a serial-sectioning technique as a function of temperature (1000–1500°C) and oxygen partial pressure (10^?14 ? 1 atm). The oxygen-partial-pressure dependence of. D¹_Ti indicates that cation selfdiffusion occurs by an interstitial-type mechanism and that both trivalent and tetravalent interstitial titanium ions may contribute to cation self-diffusion. At p_o2 = 1.50 × 10^?7 atm where impurity-induced defects are unimportant,

$\text{D}{}^1{}_{\mathrm{<mtext>Ti</mtext>}}\text{(∥c)=}\text{6.50}\text{+1.33}\text{?1.11}\text{exp}\text{?}\text{(66.11±0.56}\text{kcal}\text{mole}\text{RT}\text{cm}{}^2\text{S}$

and

$\text{D}{}^1{}_{\mathrm{<mtext>Ti</mtext>}}\text{(⊥c)=}\text{4.55}\text{+1.78}\text{?1.28}\text{exp}\text{?}\text{(64.08±0.99)}\text{kcal}\text{mole}\text{RT}\text{cm}{}^2\text{S}\text{.}$

In the intrinsic region, the ratio D¹_Ti (⊥c)/D¹_Ti(∥c) was found to increase from 1.2 to 1.6 as the temperature decreased from 1500 to 1000°C. Computations based upon the defect model of Kofstad (involving the atomic defects Ti^..._iTi^...._iand V^.._o), of Marucco etal. (Ti^...._i and V^.._o), and of Blumenthal etal. (Ti^..._i and Ti^...._i) are compared with the experimental data on deviation from stoichiometry, electrical conductivity, cation self-diffusion and chemical diffusion in TiO_2?x. These comparisons provide values of the defect concentrations, cation-defect diffusivities, electron mobility and reasonable values of the correlation factor for cation diffusion by the interstitialcy mechanism. Only the model of Kofstad is inconsistent with the data.