Electrosynthesis and characterization of Fe doped CdSe thin films from ethylene glycol bath

The CdSe and Fe doped CdSe (Fe:CdSe) thin films have been electrodeposited potentiostatically onto the stainless steel and fluorine doped tin oxide (FTO) glass substrates, from ethylene glycol bath containing (CH₃COO)₂·Cd·2H₂O, SeO₂, and FeCl₃ at room temperature. The doping concentration of Fe is optimized by using (photo) electrochemical (PEC) characterization technique. The deposition mechanism and Fe incorporation are studied by cyclic voltammetry. The structural, surface morphological and optical properties of the deposited CdSe and Fe:CdSe thin films have been studied by X-ray diffraction, scanning electron microscopy (SEM) and optical absorption techniques respectively. The PEC study shows that Fe:CdSe thin films are more photosensitive than that of undoped CdSe thin films. The X-ray diffraction analysis shows that the films are polycrystalline with hexagonal crystal structure. SEM studies reveal that the films with uniformly distributed grains over the entire surface of the substrate. The complete surface morphology has been changed after doping. Optical absorption study shows the presence of direct transition and a considerable decrease in bandgap, E_g from 1.95 to 1.65 eV.     

Electrosynthesis and characterization of CdSe thin films: Optimization of preparative parameters by photoelectrochemical technique

CdSe thin films have been electrodeposited potentiostatically onto stainless-steel and fluorine-doped tin oxide-coated glass substrates from an aqueous acidic bath using cadmium acetate ((CH₃COO)₂Cd·2H₂O) as a Cd ion source. Preparative parameters such as deposition potential, solution concentration, bath temperature, pH of the electrolytic bath and deposition time have been optimized by using photoelectrochemical (PEC) technique to obtain well adherent and uniform thin films. The electrodeposits were dark brown in colour. The films have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical absorption techniques. XRD studies reveal that films are polycrystalline, with hexagonal crystal structure. SEM shows that the films are compact, with spherical grains. Optical absorption studies reveal that the material exhibits a direct optical transition having band gap energy ∼1.72 eV. PEC study shows that the films are photoactive.     

基底对光学薄膜弱吸收测量的影响

 对表面热透镜技术测量光学薄膜弱吸收低频调制时不同基底对测量的影响进行了理论分析。用Lambda—900分光光度计测量了K9和石英基底的Ti₃O₅单层膜的吸收值,将该组样品作为定标片;用表面热透镜装置分别测量了BK7和石英空白基底及HfO₂,ZnO两组不同基底不同厚度单层膜样品的吸收。通过分析比较同一工艺条件下镀制的不同基底薄膜样品用与其同种和不同种基底定标片定标测量的结果,表明在低频测量时需要用与测量样品同种基底的定标片定标;不同厚度样品的测量结果表明,在不能严格满足热薄条件时,测量结果需引入修正值。     

Electrical and optical properties of ZnO thin films prepared by magnetron rf sputtering—influence of Al, Er and H

The influence of Al, Er and H in ZnO thin films (ZnO:Al, ZnO:Er and ZnO:H) deposited by magnetron sputtering at different substrate temperatures, T_s, on their optical, structural and electrical properties was investigated. X-ray diffraction (XRD) analyses show an improvement of the crystalline structure with increasing T_s. The optical band gap, , of the films, from transmission and reflection spectra, ranged from 3.27 to 3.41 eV. The Urbach band tail width was also calculated. Incorporation of Al and Er resulted in a reduced and an increased resistivity, ρ, respectively, and an increase in the Urbach tail width in both cases. However, sputtering in an Ar+H₂ gas mixture led to an increase in ρ and an improvement in the structural order of the films. A discussion of the influence of T_s and of Al, Er and H on the properties is presented.     

Processing parameters and transport properties of vacuum evaporated CdSe thin films

Semiconducting thin films of cadmium selenide have been grown by conventional thermal evaporation technique on glass substrate. Films evaporated at substrate temperature equal 523 K are stoichiometric and homogeneous. Effect of various growth parameters like rate of deposition and substrate temperature on the electrical properties has been studied in details. Also, the annealed at 673 K under vacuum for 1 h films have been analyzed for resistivity and Hall effect.     

Ge-Sb-Se硫系薄膜制备及光学特性研究

介绍了几种常见的硫系薄膜制备方法, 根据现有实验条件采用热蒸发法和磁控溅射法制备出Ge-Sb-Se三元体系硫系薄膜, 通过台阶仪测试薄膜的厚度和表面粗糙度, 计算出两种制备方法的成膜速率, 并通过X射线光电子能谱测试了两种制备方法所得薄膜与块体靶材组分的差别. 利用Z扫描技术和分光光度计测试了热蒸发法制备所得薄膜的三阶非线性性能和透过光谱, 计算出非线性折射率、非线性吸收系数和薄膜厚度等参数. 结果表明热蒸发法制备Ge-Sb-Se薄膜具有良好的物理结构和光学特性, 在集成光学器件方面很高的应用潜力.     

Preparation and characterization of ZnO thin films prepared by thermal oxidation of evaporated Zn thin films

In this paper, the experimental results regarding some structural, electrical and optical properties of ZnO thin films prepared by thermal oxidation of metallic Zn thin films are presented.Zn thin films (d=200–400 nm) were deposited by thermal evaporation under vacuum, onto unheated glass substrates, using the quasi-closed volume technique. In order to obtain ZnO films, zinc-coated glass substrates were isochronally heated in air in the 300–660 K temperature range, for thermal oxidation.X-ray diffraction (XRD) studies revealed that the ZnO films obtained present a randomly oriented hexagonal nanocrystalline structure. Depending on the heating temperature of the Zn films, the optical transmittance of the ZnO films in the visible wavelength range varied from 85% to 95%. The optical band gap of the ZnO films was found to be about 3.2 eV. By in situ studying of the temperature dependence of the electrical conductivity during the oxidation process, the value of about 2×10⁻² Ω⁻¹ m⁻¹ was found for the conductivity of completely oxidized ZnO films.     

Influence of thermal annealing on optical and structural properties change in Bi-doped Ge30Se70 thin films

The effect of annealing on the structural and optical properties of thermally evaporated Ge₃₀Se₇₀ and Ge₃₀Se₆₀Bi₁₀ thin films is reported in this paper. The prepared films were thermally annealed at 250°C to optimize the optical properties which can be used for the optical device fabrication. X-ray diffraction study revealed no structural transformation whereas the surface morphology changed as observed from scanning electron microscopy. The optical properties of the deposited and annealed films have been investigated by using a UV–VIS–NIR spectrophotometer in the wavelength range of 400–1100?nm. The optical band gap of the Ge₃₀Se₇₀ annealed film is found to be increased while the energy gap of the Bi-doped annealed Ge₃₀Se₆₀Bi₁₀ thin film decreased which is explained by the chemical disorderness, defect states and density of localized states in the mobility gap. The Tauc parameter and Urbach energy which measure the degree of disorder changed with the annealing process. The transmittivity increases and the absorption power decreases in the Ge₃₀Se₇₀ annealed film, whereas the reverse effect is noticed for the annealed Ge₃₀Se₆₀Bi₁₀ thin film. The irreversible nature of this change can be useful for optical recording purposes.     

Studies on the electrical conductivity, optical absorption and x-ray diffraction in bismuth thin film

Spectroscopically pure bismuth is evaporated onto glass substrates at different substrate temperature using a Hind Hivac coating plant. The electrical conductivity of bismuth thin films, prepared at different substrate temperatures is measured and thermal activation energy is evaluated. From the recorded optical absorption spectrum in the ultraviolet and visible regions optical band gapE _g is determined. X-ray diffractograms are recorded and lattice parameters are determined.     

Structural and optical properties of La-doped BaSnO3 thin films grown by PLD

In this study the structural and optical properties of lanthanum-doped BaSnO₃ powder samples and thin films deposited on fused silica were investigaed using laser ablation. Under an oxygen pressure of 5×10⁻⁴ mbar, phase pure BaSnO₃ films with a lattice constant of 0.417 nm and grain size of 21 nm were prepared at 630 °C. The band gap of BaSnO3 powder sample and thin films was calculated to be 3.36 eV and 3.67 eV, respectively. There was a progressive increase in conductivity for thin films of BaSnO₃ doped with 0~7 at% of La. The highest conductivity, 9 Scm⁻¹, was obtained for 7 at% La-doped BaSnO₃. Carrier concentration, obtained from Burstein-Moss (B-M) shift, nearly matches the measured values except for 3 at% and 10 at% La-doped BaSnO₃ thin films.     

The effects of post-thermal annealing on the optical parameters of indium-doped ZnO thin films

Indium-doped ZnO thin films are deposited on quartz glass slides by RF magnetron sputtering at ambient temper- ature. The as-deposited films are annealed at different temperatures from 400 C to 800 C in air for 1 h. Transmittance spectra are used to determine the optical parameters and the thicknesses of the films before and after annealing using a nonlinear programming method, and the effects of the annealing temperatures on the optical parameters and the thickness are investigated. The optical band gap is determined from the absorption coefficient. The calculated results show that the film thickness and optical parameters both increase first and then decrease with increasing annealing temperature from 400 C to 800 C. The band gap of the as-deposited ZnO:In thin film is 3.28 eV, and it decreases to 3.17 eV after annealing at 400 C. Then the band gap increases from 3.17 eV to 3.23 eV with increasing annealing temperature from 400 C to 800 C.     

基底对光学薄膜弱吸收测量的影响

对表面热透镜技术测量光学薄膜弱吸收低频调制时不同基底对测量的影响进行了理论分析。用Lambda—900分光光度计测量了K9和石英基底的Ti3O5单层膜的吸收值,将该组样品作为定标片;用表面热透镜装置分别测量了BK7和石英空白基底及HfO2,ZnO两组不同基底不同厚度单层膜样品的吸收。通过分析比较同一工艺条件下镀制的不同基底薄膜样品用与其同种和不同种基底定标片定标测量的结果,表明在低频测量时需要用与测量样品同种基底的定标片定标;不同厚度样品的测量结果表明,在不能严格满足热薄条件时,测量结果需引入修正值。     

Thickness effect on the structural and optical constants of stibnite thin films prepared by sulfidation annealing of antimony films

This paper deals with some physical properties of antimony sulphide Sb₂S₃ thin films obtained by an annealing process in sulphur vapors at 300 °C of Sb thermal evaporated thin films deposited on glass substrate. The crystal structure and surface morphology were investigated by both XRD and AFM techniques. This structural study shows that Sb₂S₃ thin films were well crystallized in orthorhombic structure and some parameters such as the lattice parameter, crystallite size, microstrain and degree of preferred orientation have been reported and correlated with the effect of crystallite size. On the other hand, the refractive index and the extinction coefficient were discussed in terms of the Forouhi–Bloomer model. The optical band gap was found to range from 1.75 to 2.23 eV. Finally, the analysis of the optical parameters extracted from the Urbach–Martienssen and Forouhi–Bloomer models lead to some explanations of the correlations between the structural properties in terms of the crystallite size and optical ones.     

Electronic and optical properties in ZnO:Ga thin films induced by substrate stress

The effects of biaxial stress in ZnO:Ga thin films on different substrates, e.g., sapphire(0001), quartz, Si(001), and glass have been investigated by X-ray diffraction, atomic force microscopy, and electrical transport and ellipsometric measurements. A strong dependence of orientation, crystallite size, transport, and electronic properties upon the substrate-induced stress has been found. The structural properties indicate that a tensile stress exists in epitaxial ZnO:Ga films grown on sapphire, Si, and quartz, while a compressive stress appears in films grown on glass. The resistivity of the films decreased with increasing biaxial stress, which is inversely proportional to the product of the carrier concentration and Hall mobility. The refractive index n was found to decrease with increasing biaxial stress, while the optical band gap E₀ increased with stress. These behaviors are attributed to lattice contraction and the increase in the carrier concentration that is induced by the stress. Our experimental data suggest that the mechanism of substrate-induced stress is important for understanding the properties of ZnO:Ga thin films and for the fabrication of devices which use these materials.     

Baking impact on photoelectrochemical cells performance of electrodeposited CdSe films

Cadmium selenide (CdSe) nanocrystalline thin films in the form of upright nanocones, perpendicular to substrate surface, are grown electrochemically onto a conducting and transparent indium-tin-oxide substrate at room temperature and impact of baking under oxygen flow on their structure, morphology, optical absorbance and dark-light photoelectrochemical cell performance is explored. Crystallinity improvement followed by enhancement in the surface roughness 11-19 nm and reduction in water contact angle from 60° to 22° (±0.2)° due to baking impact showed increase in crystallite size from 25 to 100 Å. Increase in current density from 0.07 to 5.61 mA/cm² after baking under oxygen flow has promoted the conversion efficiency to 0.5% from 0.007%.     

Structural and optical properties of electrodeposited molybdenum oxide thin films

Electrosynthesis of Mo(IV) oxide thin films on F-doped SnO₂ conducting glass (10-20/Ω/□) substrates were carried from aqueous alkaline solution of ammonium molybdate at room temperature. The physical characterization of as-deposited films carried by thermogravimetric/differential thermogravimetric analysis (TGA/DTA), infrared spectroscopy and X-ray diffraction (XRD) showed the formation of hydrous and amorphous MoO₂. Scanning electron microscopy (SEM) revealed a smooth but cracked surface with multi-layered growth. Annealing of these films in dry argon at 450 °C for 1 h resulted into polycrystalline MoO₂ with crystallites aligned perpendicular to the substrate. Optical absorption study indicated a direct band gap of 2.83 eV. The band gap variation consistent with Moss rule and band gap narrowing upon crystallization was observed.Structure tailoring of as-deposited thin films by thermal oxidation in ambient air to obtain electrochromic Mo(VI) oxide thin films was exploited for the first time by this novel route. The results of this study will be reported elsewhere.     

Impact of thermal annealing on physical properties of vacuum evaporated polycrystalline CdTe thin films for solar cell applications

A study on impact of post-deposition thermal annealing on the physical properties of CdTe thin films is undertaken in this paper. The thin films of thickness 500 nm were grown on ITO and glass substrates employing thermal vacuum evaporation followed by post-deposition thermal annealing in air atmosphere within low temperature range 150–350 °C. These films were subjected to the XRD, UV‐Vis NIR spectrophotometer, source meter, SEM coupled with EDS and AFM for structural, optical, electrical and surface topographical analysis respectively. The diffraction patterns reveal that the films are having zinc-blende cubic structure with preferred orientation along (111) and polycrystalline in nature. The crystallographic parameters are calculated and discussed in detail. The optical band gap is found in the range 1.48–1.64 eV and observed to decrease with thermal annealing. The current–voltage characteristics show that the CdTe films exhibit linear ohmic behavior. The SEM studies show that the as-grown films are homogeneous, uniform and free from defects. The AFM studies reveal that the surface roughness of films is observed to increase with annealing. The experimental results reveal that the thermal annealing has significant impact on the physical properties of CdTe thin films and may be used as absorber layer to the CdTe/CdS thin films solar cells.     

Growth and annealing of zinc-blende CdSe thin films on GaAs (0 0 1) by molecular beam epitaxy

CdSe thin films have been grown on GaAs (0 0 1) substrates by molecular beam epitaxy (MBE). The effects of substrate temperature and annealing treatment on the structural properties of CdSe layers were investigated. The growth rate slightly decreases due to the accelerated desorption of Cd from CdSe surface with an increase in the temperature. The sample grown at 260 °C shows a polycrystalline structure with rough surface. As the temperature increases over 300 °C, crystalline CdSe (0 0 1) epilayers with zinc-blende structure are achieved and the structural quality is improved remarkably. The epilayer grown at 340 °C displays the narrowest full-width at half-maximum (FWHM) from (0 0 4) reflection in double-crystal X-ray rocking curve (DCXRC) and the smallest root-mean-square (RMS) roughness of 0.816 nm. Additionally, samples fabricated at 320 °C were annealed in air for 30 min to study the films’ thermal stability. X-ray diffraction (XRD) results indicate that the zinc-blende structure remains unchanged when the annealing temperature is elevated to 460 °C, meaning a good thermal stability of the cubic CdSe epilayers.     

Photoelectrochemical properties of electrochemically deposited CdIn2S4 thin films

Thin films of CdIn₂S₄ have been deposited on to stainless steel and fluorine-doped tin oxide (FTO)-coated glass substrates from aqueous acidic bath using an electrodeposition technique. Ethylene diamine tetra-acetic acid (EDTA) disodium salt is used as complexing agent to obtain good-quality deposits by controlling the rate of the reaction. The different preparative parameters like concentration of bath, deposition time, bath temperature, pH of the bath have been optimized by the photoelectrochemical (PEC) technique in order to get good-quality photosensitive material. Different techniques have been used to characterize CdIn₂S₄ thin films. Optical absorption shows the presence of direct transition with band gap energy 2.17 eV. The X-ray diffraction (XRD) analysis of the as-deposited and annealed films showed the presence of polycrystalline nature. Energy-dispersive analysis by X-ray (EDAX) study for the sample deposited at optimized preparative parameters shows that the In-to-Cd ratio is almost 2 and S-to-Cd ratio is almost 4. Scanning electron microscopy (SEM) for samples deposited at optimized preparative parameters reveals that spherical grains are uniformly distributed over the surface of the substrate indicates the well-defined growth of polycrystalline CdIn₂S₄ thin film. PEC characterization of the films is carried out by studying photoresponse, spectral response and photovoltaic output characteristics. The fill factor (ff) and power conversion efficiency (η) of the cell are 69 and 2.94%, respectively.