luminescence of BaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript> crystals activated by Eu<Superscript>2+</Superscript> and Ce<Superscript>3+</Superscript> ions

We have studied the effect of doping with Eu²⁺ and Ce³⁺ ions on the photoluminescence (PL) of BaGa₂Se₄ crystals in the temperature range 77–300 K. We have established that the broad bands with maxima at wavelengths 456 nm and 506 nm observed in the photoluminescence spectra of BaGa₂Se₄:Ce³⁺ crystals are due to intracenter transitions 5d → ²F_7/2 and 5d →²F_5/2 of the Ce³⁺ ions, while the broad photoluminescence band with maximum at 521 nm in the spectrum of BaGa₂Se₄:Eu²⁺ is associated with 4f⁶ 5d → 4f⁷ (⁸S_7/2) transitions of the Eu²⁺ ion. We show that in BaGa₂Se₄:Eu²⁺,Ce³⁺ crystals, excitation energy is transferred from the Ce³⁺ ions to the Eu²⁺ ions.     

Synthesis and luminescent properties of Eu<Superscript>3+</Superscript>- and Eu<Superscript>2+</Superscript>-activated sodium pyrophosphate Na<Subscript>4</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

The luminescent properties of Eu³⁺ and Eu²⁺ ions in sodium pyrophosphate, Na₄P₂O₇, have been studied. The excitation spectrum of the Eu³⁺ emission in Na₄P₂O₇ consists of several sets of bands in the range 280–535 nm due to 4f–4f transitions of Eu³⁺ ions and a broad band with a maximum at about 240 nm interpreted to be due to a charge transfer (CT) transition from oxygen 2p states to empty states of the Eu³⁺ 4f⁶-configuration. Although the CT band energy is large enough, the quantum efficiency (η) of the Eu³⁺ emission in Na₄P₂O₇ under CT excitation was estimated to be very low (η ≤ 0.01). In terms of a configurational coordinate model, this fact is interpreted as a result of the high efficiency of a radiationless relaxation from the CT state to the ⁷F₀ ground state of Eu³⁺ ions occupying sodium sites in Na₄P₂O₇. A strong reducing agent is required in order to stabilize Eu²⁺ ions in Na₄P₂O₇ during the synthesis. Several nonequivalent Eu²⁺ luminescence centers in Na₄P₂O₇ were found.     

Spectral properties of neodymium in POCl<Subscript>3</Subscript>-BCl<Subscript>3</Subscript>-Nd<Superscript>3+</Superscript>

We measured the absorption and luminescence spectra of Nd³⁺ ions in an inorganic solvent POCl₃-BCl₃. The spectra were analyzed in terms of the Judd-Ofelt theory. We calculated the Judd-Ofelt parameters, oscillator strengths, spontaneous emission probabilities, luminescence quantum yield, and the stimulated emission cross section for the laser transition ⁴ F _3/2 → ⁴ I _11/2 of the neodymium ion in a POCl₃-BCl₃-Nd³⁺ solution.     

Luminescence of Eu<Superscript>3+</Superscript> rare-earth ions in Lu<Subscript>2</Subscript>O<Subscript>3</Subscript> nanospheres

The kinetics of luminescence of Eu³⁺ ions in Lu₂O₃:Eu nanospheres with diameters of 100–270 nm and a small standard deviation of the size distribution <15% has been studied. A sharp decrease in the decay time of luminescence of Eu³⁺ ions in the red range with an increase in the diameter of nanospheres has been attributed to the appearance of a photon mode accelerating spontaneous luminescence, which is confirmed by the calculation of ranges of existence of whispering-gallery modes in studied nanospheres.     

Spectral properties of neodymium in POCl<Subscript>3</Subscript>-SbCl<Subscript>5</Subscript>-Nd<Superscript>3+</Superscript>

The absorption and luminescence spectra of neodymium in a binary inorganic solvent—phosphorus oxychloride-antimony pentachloride—are measured. The spectra are analyzed in terms of the Judd-Ofelt theory. The Judd-Ofelt parameters Ω_λ, the oscillator strengths of the main absorption bands, the spontaneous emission probabilities, the radiative lifetime, the luminescence quantum yields, and the stimulated emission cross sections for the ⁴ F _3/2 → ⁴ I _11/2 laser transition are calculated.     

Spontaneous luminescence of Eu<Superscript>3+</Superscript> ions in porous Y<Subscript>2</Subscript>O<Subscript>3</Subscript> nanospheres

A study of the luminescence of Eu³⁺ ions in Y₂O₃ nanospheres indicates a significant influence of the porous structure of nanoparticles on the luminescence of dopant ions. It is shown that filling the nanopores of initially porous Y₂O₃ nanospheres shortens the decay time of the spontaneous luminescence of doping europium ions. The change in the decay time is associated with the change in the effective refractive index of the porous nanospheres.     

Formation of Eu<Superscript>2+</Superscript> and Eu<Superscript>3+</Superscript> centers in synthesis of CaF<Subscript>2</Subscript>:Eu luminophores

We have studied the effect of CaF₂:Eu luminophore synthesis methods on the charge state of europium. We have shown that Eu³⁺ predominates over Eu²⁺ in samples obtained by coprecipitation of europium with calcium fluoride, and the ratio Eu³⁺/Eu²⁺ grows as the total amount of europium increases. Partial charge conversion of the europium occurs during calcination of the samples, due to changes in the excess fluorine balance. We studied the luminescence, magnetic susceptibility, and EPR of the synthesized samples. We have shown that in a solid solution, europium forms large ordered clusters, determining both the luminescent and the magnetic properties of the material. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 74, No. 6, pp. 773–779, November–December, 2007.     

Luminescence in Dy<Superscript>3+</Superscript> and Eu<Superscript>3+</Superscript> Activated K<Subscript>3</Subscript>Al<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>

The Dy³⁺ and Eu³⁺ activated K₃Al₂ (PO₄)₃ phosphors were prepared by a combustion synthesis. From a powder X-ray diffraction (XRD) analysis the formation of K₃Al₂ (PO₄)₃ was confirmed. In the photoluminescence emission spectra, the K₃Al₂(PO₄)₃:Dy³⁺ phosphor emits two distinctive colors: blue and yellow whereas K₃Al₂(PO₄)₃:Eu³⁺ emits red color. Thus the combination of colors gives BYR (blue–yellow–red) emissions can produce white light. These phosphors exhibit a strong absorption between 340 and 400 nm which suggest that present phosphor is a promising candidate for producing white light-emitting diodes (LED).     

On the Luminescence of Ce<Superscript>3+</Superscript>, Eu<Superscript>3+</Superscript>, and Tb<Superscript>3+</Superscript> in Novel Borate LiSr<Subscript>4</Subscript>(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>

This paper reports on the photoluminescence (PL) and time-resolved properties of Ce³⁺, Eu³⁺, and Tb³⁺ in novel LiSr₄(BO₃)₃ powder phosphors. Ce³⁺ shows an emission band peaking at 420 nm under 350-nm UV excitation. Energy transfer from Ce³⁺ to Mn²⁺ takes place in the co-doped samples. Eu³⁺ shows red emission under near UV excitation. LiSr₄(BO₃)₃:Eu³⁺ phosphor could be a suitable candidate for phosphor-converted solid state lighting. The luminescence lifetime is 2.13 ms for Eu³⁺ in LiSr₄(BO₃)₃:0.001Eu³⁺. As Eu³⁺ concentration increasing, the decay curves deviate from exponential behavior. Tb³⁺ shows the strongest ⁵D₄→⁷ F₅ emission line at 540 nm. Decay curves of ⁵D₄→⁷ F₅ and ⁵D₃→⁷ F₅ emission with different Tb³⁺ concentrations were also measured. Cross-relaxation process is discussed based on the decay curves.     

Luminescence characteristics of energy transfer between Ce<Superscript>3+</Superscript> and Eu<Superscript>2+</Superscript> in NaMgPO<Subscript>4</Subscript> phosphor

Powder samples of NaMgPO₄ doped with Eu²⁺ and Ce³⁺ were prepared and their photoluminescence spectra were systemically studied. Energy transfer from Ce³⁺ to Eu²⁺ in NaMgPO₄ phosphor was observed by investigating the optical properties from photoluminescence spectra in Eu²⁺ or Ce³⁺ singly doped and Eu²⁺–Ce³⁺ codoped sodium magnesium orthophosphates, NaMgPO₄. The enhancement of UV excitation is attributed to energy transfer from Ce³⁺ to Eu²⁺, and Ce³⁺ plays a role as a sensitizer. Ce³⁺–Eu²⁺ codoped NaMgPO₄ phosphors in which Eu²⁺ can be efficiently excited by 390 nm are potential candidates for phosphor-converted LEDs.     

Luminescence and energy transfer mechanism in Eu<Superscript>3+</Superscript>/Tb<Superscript>3+</Superscript>-co-doped ZrO<Subscript>2</Subscript> nanocrystal rods

Nanocrystal rods of Eu³⁺/Tb³⁺-co-doped ZrO₂ were synthesized using a simple chemical precipitation technique. Both ions were successfully doped into the Zr⁴⁺ ion site in a mixed structure containing both monoclinic and tetragonal phases. The Eu³⁺ or Tb³⁺ singly doped zirconia produced red and green luminescence which are characteristics of Eu³⁺ and Tb³⁺ ions, respectively. The co-doped zirconia samples produced blue emission from defect states transitions in the host ZrO₂, red and green luminescence from dopant ions giving cool to warm white light emissions. The phosphors were efficiently excited by ultraviolet and near-ultraviolet/blue radiations giving white and red light, respectively. The decay lifetime was found to increase with increasing donor ion concentration contrary to conventional observations reported by previous researchers. Weak quadrupole–quatdrupole multipolar process was responsible for energy transfer from Tb³⁺ (donor) ion to Eu³⁺ ion. No energy back-transfer from Eu³⁺ to Tb³⁺ ion was observed from the excitation spectra. Temperature-dependent photoluminescence shows the presence of defects at low temperature, but these defects vanished at room temperature and beyond. The Eu³⁺/Tb³⁺-co-doped ZrO₂ nanocrystal rod is a potential phosphor for white light application using UV as an excitation source. Thermoluminescence measurements show that the inclusion of Tb³⁺ ion increases trap depths in the host zirconia.     

Possibility of adjusting photoluminescence spectra of Ca scheelites (CaMoO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript> and CaWO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript>) to the emission spectrum of incandescent lamps

The peculiarities of the photoluminescence of compounds CaMoO₄: Eu³⁺ and CaWO₄: Eu³⁺ with the scheelite structure associated with a change in the short- and long-range orders of the crystal lattice upon a change in the activator (Eu³⁺) of the photoluminescence range in the interval 1–4 mol %, in which the photoluminescence of the matrix is preserved in the range 484–557 nm, are investigated using X-ray phase analysis as well as photoluminescence, Raman, and diffuse reflection spectroscopies. The introduction of Eu³⁺ ions leads to the reconstruction of the lattice so that up to 10% of these ions stimulate the formation of centrosymmetric localization upon the substitution of Ca²⁺ ions in the noncentrosymmetric positions. It is found that the spectral radiant emittance of the more effective luminophore CaMoO₄: Eu³⁺ can be adjusted to this parameter for an incandescent lamp for the Eu³⁺ concentration of 1–2 mol %.     

Luminescent properties of SrMg<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>:Eu<Superscript>2+</Superscript>, and Mn<Superscript>2+</Superscript> as a potential phosphor for ultraviolet light-emitting diodes

Eu²⁺ and Mn²⁺ co-doped SrMg₂(PO₄)₂ phosphors with blue and red two emission bands were prepared by the high temperature solid state method and their luminescent properties have been investigated as a function of activator and co-activator concentrations. Resonance-type energy transfers from Eu²⁺ to Mn²⁺ were discovered by directly overlapping the Eu²⁺ emission spectrum and the excitation spectrum of Mn²⁺. Efficiencies of energy transfer were also calculated according to the changes of relative intensities of Eu²⁺ and Mn²⁺ emission. According to the principle of energy transfer, we demonstrated that the phosphor SrMg₂(PO₄)₂:Eu²⁺,Mn²⁺ with double emission bands exhibited a great potential as a phosphor for ultraviolet light-emitting diodes and the relative intensities of blue and red emission could be tuned by adjusting the contents of Eu²⁺ and Mn²⁺. PACS 78.55.-m     

Polarized spectral properties of Er<Superscript>3+</Superscript> ions in NaGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

Polarized spectral properties of Er³⁺:NaGd(WO₄)₂ single crystal are reported. The crystal was grown by the Czochralski method. The Judd–Ofelt theory was applied to analyze the polarized absorption spectra and then calculate the spontaneous emission probabilities, radiative lifetimes, and branching ratios. Fluorescence decay curves of the ⁴ I _13/2, ⁴ I _11/2, and ⁴ S _3/2 multiplets for the Er³⁺ ions were measured. Stimulated emission cross-sections of the ⁴ I _13/2→⁴ I _15/2 transition obtained by the Fuchtbauer–Ladenberg formula and the reciprocity method were compared. Multi-phonon relaxation rates of the crystal were estimated. Green up-conversion fluorescence around 531 and 552 nm was observed, and the possible up-conversion mechanisms were proposed. PACS 78.20.-e; 42.70.Hj     

Local structure of Gd<Superscript>3+</Superscript> and Eu<Superscript>2+</Superscript> impurity centers in a CdF<Subscript>2</Subscript> crystal

The local crystal structure of Gd³⁺ and Eu²⁺ cubic impurity centers in cadmium fluoride is calculated within the shell model in the pair potential approximation. The local compressibility of the cationic and anionic sublattices of the host lattice is determined in the vicinity of the Gd³⁺ (Eu²⁺) impurity ion.     

PL Properties of Sr<Subscript>2</Subscript>CeO<Subscript>4</Subscript> With Eu<Superscript>3+</Superscript> and Dy<Superscript>3+</Superscript> for Solid State Lighting Prepared by Precipitation Method

Photoluminescence studies of pure and Dy³⁺, Eu³⁺ doped Sr₂CeO₄ compounds are presented by oxalate precipitation method for solid state lighting. The prepared samples also characterized by XRD, SEM (EDS) and FTIR spectroscopy. The pure Sr₂CeO₄ compound displays a broad band in its emission spectrum when excited with 280 nm wavelength, which peaks centered at 488 nm, which is due to the energy transfer between the molecular orbital of the ligand and charge transfer state of the Ce⁴⁺ ions. Emission spectra of Sr₂CeO₄ with different concentration of Dy³⁺ ions under near UV radiation excitation, shows that intensity of luminescence spectra is found to be affected by Dy³⁺ ions, and it increases with adding some percentages of Dy³⁺ ions. The maximum doping concentration for quenching is found to be Dy³⁺?=?0.2 mol % to Sr²⁺ions. The observed broad spectrum from 400 to 560 nm is mainly due to CT transitions in Sr₂CeO₄ matrix and some fractional contribution of transitions between ⁴F_9/2 → ⁶H_15/2 of Dy³⁺ ions. Secondly the effect of Eu³⁺ doping at the Sr²⁺ site in Sr₂CeO₄, have been studied. The results obtained by doping Eu³⁺ concentrations (0.2 mol% to 1.5 mol%), the observed excitation and emission spectra reveal excellent energy transfer between Ce⁴⁺ and Eu³⁺. The phenomena of concentration quenching are explained on the basis of electron phonon coupling and multipolar interaction. This energy transfer generates white light with a color tuning from blue to red, the tuning being dependent on the Eu³⁺ concentration. The results establish that the compound Sr₂CeO₄ with Eu³⁺?=?1 mol% is an efficient “single host lattice” for the generation of white lights under near UV-LED and blue LED irradiation. The commission internationale de I’Eclairage (CIE) coordinates were calculated by Spectrophotometric method using the spectral energy distribution of prepared phosphors.     

Fabrication,structure, and properties of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@C encapsulated with YVO<Subscript>4</Subscript>:Eu<Superscript>3+</Superscript> composites

The use of carbon shells offers many advantages in surface coating or surface modification due to their surface with activated carboxyl and carbonyl groups. In this study, the Fe₃O₄@C@YVO₄:Eu³⁺ composites were prepared through a simple sol–gel process. Reactive carbon interlayer was introduced as a key component, which separates lanthanide-based luminescent component from the magnetite, more importantly, it effectively prevent oxidation of the Fe₃O₄ core during the whole preparation process. The morphology, structure, magnetic, and luminescent properties of the composites were characterized by transmission electron microscopy (TEM), high-resolution TEM, X-ray diffraction, X-ray photoelectron spectra, VSM, and photoluminescent spectrophotometer. As a result, the Fe₃O₄@C/YVO₄:Eu³⁺ composites with well-crystallized and core–shell structure were prepared and the YVO₄:Eu³⁺ luminescent layer decorating the Fe₃O₄@C core–shell microspheres are about 10 nm. In addition, the Fe₃O₄@C@YVO₄:Eu³⁺ composites have the excellent magnetic and luminescent properties, which allow them great potential for bioapplications such as magnetic bioseparation, magnetic resonance imaging, and drug/gene delivery.     

Photolumiscent Properties of Nanorods and Nanoplates Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Eu<Superscript>3+</Superscript>

Nanorods and nanoplates of Y₂O₃:Eu³⁺ powders were synthesized through the thermal decomposition of the Y(OH)₃ precursors using a microwave-hydrothermal method in a very short reaction time. These powders were analyzed by X-ray diffraction, field emission scanning electron microscopy, Fourrier transform Raman, as well as photoluminescence measurements. Based on these results, these materials presented nanoplates and nanorods morphologies. The broad emission band between 300 and 440 nm ascribed to the photoluminescence of Y₂O₃ matrix shifts as the procedure used in the microwave-hydrothermal assisted method changes in the Y₂O₃:Eu³⁺ samples. The presence of Eu³⁺ and the hydrothermal treatment time are responsible for the band shifts in Y₂O₃:Eu³⁺ powders, since in the pure Y₂O₃ matrix this behavior was not observed. Y₂O₃:Eu³⁺ powders also show the characteristic Eu³⁺ emission lines at 580, 591, 610, 651 and 695 nm, when excited at 393 nm. The most intense band at 610 nm is responsible for the Eu³⁺ red emission in these materials, and the Eu³⁺ lifetime for this transition presented a slight increase as the time used in the microwave-hydrothermal assisted method increases.     

Red,Yellow, Blue and Green Emission from Eu<Superscript>3+</Superscript>, Dy<Superscript>3+</Superscript> and Bi<Superscript>3+</Superscript> Doped Y<Subscript>2</Subscript>O<Subscript>3</Subscript>nano-Phosphors

Rare earth elements (RE = Eu³⁺& Dy³⁺)and Bi³⁺ doped Y₂O₃ nanoparticles were synthesized by urea hydrolysis method in ethylene glycol, which acts as reaction medium as well as a capping agent, at a low temperature of 140 °C,followed by calcination of the obtained product. Transmission electron microscope (TEM) images reveals that ovoid shaped Y₂O₃ nanoparticles of around 22–24 nm size range were obtained in this method. The respective RE and Bi³⁺ doped Y₂O₃ precursor nanoparticles when heated at 600 and 750 °C, retains the same shape as that of the as-synthesized Y₂O₃ precursor samples. From EDAX spectra, the incorporation of RE ions into the host has been studied. XRD pattern reveals the crystalline nature of the heated nanoparticles and indicate the absence of any impurity phase other than cubic Y₂O₃.However, the as-synthesized nanoparticles were highly amorphous without the presence of any sharp XRD peaks. Photoluminescence study suggests that the synthesized samples could be used as red (Eu³⁺), yellow (Dy³⁺), blue and green (Bi³⁺)emitting phosphors.