Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体,制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1,0.75,0.5,0.25,0).应用Brunauer-Emmet-Teller(BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征,并系统研究了催化剂在饮食油烟催化燃烧中的催化活性.BET结果表叫催化剂的比表面积随Ce/Zr摩尔比的减小而减小.XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上.H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好.催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧,降低了反应温度.随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化,催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2＞Pt/γ-Al2O3/Ce0.25Zr0.75O2＞Pt/γ-Al2O3/Ce0.75Zr0.25O2＞Pt/γ-Al2O3/CeO2＞Pt/γ-Al2O3/ZrO2.     

不同载体负载的铂催化剂在丙酮酸乙酯不对称氢化反应中的活性及其铂流失率比较

以介孔树脂材料FDU-14和介孔碳材料CMK-3为载体制备了两种负载型铂催化剂, 用N₂气吸附、X射线衍射及CO化学吸附等手段对这两种催化剂进行了表征, 并将这两种不同的负载型铂催化剂在丙酮酸乙酯不对称氢化反应中的催化性能及其铂流失率与商品化Pt/Al₂O₃催化剂进行了比较. 研究结果表明, 尽管Pt/Al₂O₃催化剂的初始活性和光学选择性均较高, 然而相同反应条件下乙酸溶剂中Pt/FDU-14和Pt/CMK-3催化剂的铂流失率比Pt/Al₂O₃催化剂的低. 通过对催化剂进行CO吸附原位傅里叶变换红外漫反射光谱(DRIFTS)表征, 从载体的不同表面电子性质角度解释了不同载体负载的铂催化剂在丙酮酸乙酯不对称氢化反应中的活性和铂流失率的差异.     

铂基催化剂用于柴油烃氧化

The catalytic performance of Pt-based catalysts for the total oxidation of hydrocarbons was investigated.The activity of supported Pt catalysts(Pt/Al2O3,Pt/ZrO2,Pt/TiO2,and Pt/H-ZSM-5)depends on the metal oxide support.Pt/Al2O3 showed the highest catalytic activity when the catalysts were aged at 750°C for 50 h in air.The activity of Pt/Al2O3 was dependent on the valence state of the Pt surface.Pt/Al2O3 with the Pt surface in the metallic state was more active than with the surface in the cationic state.The surface density of acid and basic sites on the Al2O3 support controlled the valence state of the Pt surface and stability of the Pt particles in the highly dispersed state,respectively.     

PtSn/Al2O3/MCM-41催化剂的丙烷脱氢催化性能

用微型催化反应装置评价, 并结合X射线粉末衍射(XRD)、表面积和孔结构测试、程序升温还原(TPR)、氢化学吸附和热重分析等方法研究了负载型PtSn/γ-Al2O3, PtSn/MCM-41和PtSn/Al2O3/MCM-41催化剂的丙烷脱氢反应催化性能. 发现PtSn/Al2O3/MCM-41催化剂具有较PtSn/MCM-41催化剂高的丙烷脱氢反应活性和较PtSn/γ-Al2O3催化剂高的反应稳定性. 实验结果表明, 纯硅MCM-41载体表面的锡物种因与载体相互作用较弱故易被还原, 导致铂金属分散度和催化剂的丙烷脱氢活性较低. 用Al2O3修饰MCM-41可以增强Sn物种与Al2O3/MCM-41载体之间的相互作用, 提高PtSn/Al2O3/MCM-41催化剂铂金属分散度和丙烷脱氢催化活性. 并且, 积炭后的PtSn/Al2O3/MCM-41催化剂具有较高的铂金属表面裸露度, 故具有较高的丙烷脱氢反应稳定性. PtSn/Al2O3/MCM-41催化剂优良的丙烷脱氢催化性能可能不仅与Sn-载体Al2O3/MCM-41较强的相互作用有关, 而且与Al2O3/MCM-41载体的介孔结构有关.     

Pt/MOx-SiO2 (M=Ce,Zr, Al)催化剂对CO和C3H8氧化性能的影响

采用共沉淀法制备质量比为1:1的MOx-SiO2(M=Ce,Zr,Al)复合氧化物,以此为载体采用浸渍法制备了铂基氧化型催化剂.考察了该系列催化剂在模拟柴油车尾气条件下,经SO2硫化前后对C3H8和CO的氧化性能.用X射线衍射(XRD)、低温N2吸附-脱附、氨气/氧气/二氧化碳程序升温脱附(NH3/O2/CO2-TPD)和X射线光电子能谱(XPS)等手段进行了表征.NH3-TPD证实催化剂表面存在多种酸中心,硫化后催化剂表面中强酸中心增多.O2-TPD证实催化剂表面存在α和β氧物种,硫化后催化剂表面氧脱附量减少.其中Pt/Al2O3-SiO2表面酸性最弱和表面氧脱附量最大.XPS结果表明新鲜催化剂经硫化后会使催化剂表面Pt的结合能降低.活性测试结果表明,三种催化剂对CO和C3H8的催化氧化活性均较好,其中Pt/ZrO2-SiO2抗SO2中毒性能最佳,具有良好的应用前景.     

金属羰基络合物制备的Pt-Re/Al_2O_3催化剂的性能 Ⅱ 不同方法制备的Pt-Re/Al_2O_3催化剂的物化性质表征

采用TPR,H_2化学吸附,TPD,TEM和DRS等方法对一组组成相同制法不同的Pt-Re/Al_2O_3催化剂进行了表征。TPR,H_2化学吸附等结果表明,Pt-Re/Al_2O_3催化剂中Re是通过与Pt的相互作用形成有高温吸附H_2中心及抗积炭能力的Pt-Re集团,从而提高了重整催化剂的活性和稳定性。制备方法的不同对催化剂活性表面的形成及铂铼相互作用有重要影响。以羰基金属原子簇化合物制备的Pt_5Re_2催化剂的Pt和Re的相互作用程度最大,这种相互作用从TPR和DRS测定中得到验证。电镜观察发现Pt_5Re_2催化剂表面的金属晶粒分布比常规Pt-Re小且均匀。由于担载羰基化合物在脱羰过程中CO发生歧化生成的微量碳物类使Pt_5Re_2具有较好的活性、芳构化选择性和稳定性。     

CeO2纳米层对多层载体x-CeO2/3DOM Al2O3负载纳米Au催化剂催化柴油炭烟燃烧活性的影响

与汽油车相比,柴油车具有CO2排放低、寿命长和经济性好等优点,所以近年来受到广泛关注并被大量使用.但是,柴油车在使用过程中会产生大量炭烟颗粒物(PM),对大气环境和人类健康造成很大威胁.因此,开展这方面的基础研究具有重要的科学意义及环境保护意义.催化柴油炭烟燃烧反应是一个气-固-固多相深度氧化反应,由于PM的粒径远大于传统催化剂,导致PM不能进入催化剂孔道内部,造成催化剂活性比表面积利用率较低.设计并制备大孔径的三维有序大孔结构(3DOM)的催化剂,能够减小反应扩散阻力,增加催化剂与炭烟颗粒物的有效接触,加快反应进行.另外,可以通过在3DOM氧化物表面担载其它活性组分,提高催化剂的氧化还原性能,进而提高其活性.CeO2有很好的储放氧性能,在柴油车尾气净化催化剂中较为常见,但是单一的CeO2热稳定性较差,高温下容易烧结,使得比表面积减小,并且失去储氧能力,造成催化剂失活.文献中较常见的解决办法是在CeO2中掺杂其它阳离子,如Zr4+,Pr3+,Al3+,La3+及Y3+等离子,以提高CeO2的抗高温烧结能力.此外,研究报道的催化剂对催化柴油炭烟颗粒物燃烧的峰值温度已经远低于炭烟颗粒物的自燃温度,但是对颗粒物的起燃温度仍普遍较高.我们前期研究结果表明,担载纳米Au颗粒催化剂能够显著降低炭烟燃烧的起燃温度.本文采用胶体晶体模板法制备了3DOM Al2O3载体,利用微孔膜-氨沉淀法担载不同量的活性组分CeO2,制备出一种负载型x-CeO2/3DOM Al2O3催化剂,它既可减少稀土元素用量,降低成本,又因为Al2O3的机械强度较高,还能保证催化剂的机械强度足够好.为了进一步降低催化剂催化炭烟燃烧的起燃温度,利用还原沉积法在多层载体x-CeO2/3DOM Al2O3上负载纳米Au催化剂,制备出不同厚度的CeO2纳米层负载Au催化剂(Au/x-CeO2/3DOM Al2O3).利用X射线衍射、扫描电镜、透射电镜、H2程序升温还原和O2程序升温脱附等方法研究了催化剂的结构及物化性质与催化剂活性之间的关系,提出了消除PM反应的可能机理.结果表明,Al3+离子能够部分进入到CeO2中,形成Al-Ce固溶体.由于Al离子半径小于Ce离子,Al3+掺杂后能引起CeO2晶格发生畸变,产生大量缺陷,形成大量氧空位,促进晶格氧的移动,从而使催化剂具有更大的储放氧能力.在Au/x-CeO2/3DOM Al2O3催化剂中,CeO2担载量过高时,氧化铈纳米层较厚,活性组分容易烧结,不利于催化剂活性提高;而CeO2担载量过低,则CeO2纳米层较稀薄,催化剂的氧化还原性能受限,催化剂活性也不高.因此,CeO2的担载量应适当.此外,Au和CeO2之间的强相互作用能够增加Au纳米颗粒表面活性氧物种的数量,从而促进柴油炭烟燃烧反应.活性测试结果表明,担载纳米Au颗粒后,催化剂催化柴油炭烟燃烧的起燃温度均明显降低,在所制备的系列催化剂中Au/20％CeO2/3DOM Al2O3催化剂展示了最高的催化活性,T10,T50和T90分别为267,372和426 oC.     

Co-Fe/SBA-15与过一硫酸盐联用非均相催化降解水中染料罗丹明B

由于硫酸根自由基(SO4?-)的强氧化性,基于SO4?-的高级氧化技术受到人们的高度关注.采用过渡金属活化过一硫酸盐(PMS)产生SO4?-用以分解有机物,反应体系简单,反应条件温和,且不需要额外的能量供给,因此,成为人们优先选用的方法,其中,采用高效、环境友好的非均相过渡金属催化剂活化PMS处理难降解有机物成为研究热点.本文研究了非均相CoFe/SBA-15-PMS体系对水中难降解染料罗丹明B(RhB)的降解.以SBA-15为载体, Co(NO3)2·6H2O和Fe(NO3)3·9H2O为前驱物,采用一步等体积浸渍法制备了CoFe/SBA-15,通过X射线衍射(XRD)、N2吸附-脱附、扫描电镜(SEM)、能谱(EDS)、透射电镜(TEM)和振动样品磁强计(VSM)等对其进行了表征.考察了焙烧温度、Co与Fe的负载量对CoFe/SBA-15催化性能的影响和该催化剂的重复使用性能,还考察了RhB降解动力学及催化剂CoFe/SBA-15投加量、氧化剂PMS投加量和反应物(RhB和PMS)初始浓度对其性能的影响,探讨了RhB的降解机理.结果表明：对于催化剂CoFe/SBA-15,合成焙烧后在SBA-15上负载的Fe、Co化合物主要是CoFe2O4复合物,它作为催化剂的活性中心负载在SBA-15的孔道内外.制备的焙烧温度对CoFe/SBA-15催化性能几乎无影响,但对Co浸出影响显著.与SBA-15相比,催化剂10Co9.5Fe/SBA-15-700(Co和Fe负载量分别为10 wt%和9.5 wt%,焙烧温度700 oC)的比表面积、孔体积和孔径均减小,分别为506.1 m2/g,0.669 cm3/g和7.4 nm,但仍然保持SBA-15的有序六方介孔结构.该催化剂以棒状体的聚集态存在,聚集体直径大于0.25μm,其磁化强度为8.3 emu/g,因此,可通过外磁铁容易地从水中分离.相比之下,10Co9.5Fe/SBA-15-700具有最佳的催化性能和稳定性,可使RhB的降解率达到96%以上, Co的浸出量小于32.4μg/L.在CoFe/SBA-15和PMS共存下, RhB的降解符合一级动力学方程, RhB降解速率随CoFe/SBA-15和PMS投加量的增加和初始反应物浓度的减小而提高.淬灭实验结果表明,在CoFe/SBA-15, PMS和RhB水溶液体系中,存在的主要活性自由基为SO4?-,它是由CoFe/SBA-15活化PMS产生的,对RhB的降解起决定性的作用. RhB降解过程的UV-vis结果表明, RhB的降解途径主要是蒽环打开, SO4?-优先攻击RhB的有色芳香烃环,然后RhB进一步分解为小分子有机物. CoFe/SBA-15循环使用10次仍能保持高催化活性和稳定性,在每次反应中RhB的降解率均大于84%, Co和Fe的浸出量均分别小于72.1和35μg/L. CoFe/SBA-15作为高效、环境友好的非均相催化剂可有效地活化PMS产生SO4?-降解水中RhB,具有实际应用的潜力.     

载体性质对Pt催化剂H2选择催化还原NOx活性和选择性的影响

研究了Pt/MgO, Pt/γ-Al2O3, Pt/ZrO2和Pt/HZSM-5催化剂上H2选择催化还原消除NOx(H2-SCR)反应。结果发现, H2-SCR活性和N2生成选择性受催化剂中Pt的金属性以及载体的氮氧化物吸附能力影响很大。 HZSM-5的表面酸性使载体对NOx吸附能力较小,使担载Pt以较高的金属性存在,从而导致Pt/HZSM-5催化剂的高活性和高选择性。相反, Pt/MgO和Pt/γ-Al2O3催化剂较差的活性和选择性可归因于其载体的碱性表面、催化剂中Pt较低的金属性以及载体对氮氧化物较大的吸附能力。结合反应的原位红外光谱结果可以认为,在Pt/载体界面处亚硝酸根/硝酸根物种被还原为N2或N2O,取决于该处参与反应的活性H与这些含氮物种的相对数目。     

铂（铂—铼）与氧化铝相互作用的研究：Ⅰ.氯的作用

采用PASCA、IR、化学分析及微反等技术,研究Pt/Al_2O_3和Pt-Re/Al_2O_3体系中金属与载体之间的相互作用。结果表明:氯在铂、铼与氧化铝之间的相互作用及对催化剂芳构化活性的影响方面起着十分重要的作用。在没有氯存在的情况下,铂(或铂-铼)与氧化铝之间是不存在相互作用的。当浸渍液中存在氯时,铂以[PtCl_6]~(2-)络离子形式取代氧化铝表面上某些活泼OH~-基,生成稳定的金属—载体相互作用复合物(MSIC)。而生成稳定MSIC的合适盐酸浓度为0.4 mol/L。这一结果与文献报导是一致的。 实验结果还表明,在探讨金属与载体之间的相互作用时,非金属元素(如氯等)是一个十分重要而不可忽视的因素。     

An efficient and reusable silica/dendrimer supported platinum catalyst for electron transfer reactions

A series of Pt nanoparticles (NPs) smaller than 3 nm were successfully encapsulated in dendrimer/SBA-15 organic and inorganic hybrid composite. The obtained catalysts were characterized by XPS, XRD and TEM. The results of XPS and XRD indicate the existence of Pt NPs in the hybrid matrix. TEM images display the Pt NPs with narrow size distribution are monodispersed in SBA-15 channels. Catalytic property of the supported Pt catalysts was investigated in inorganic (ferricyanide to ferrocyanide by thiosulfate) and organic (p-nitrophenol to p-aminophenol by sodium borohydride) electron transfer (redox) reactions. In both cases, the reduction reactions followed smoothly and the catalysts showed excellent catalytic activity. Moreover, the catalysts can be easily separated and reused several times preserving good catalytic performance.     

助剂对Cu-Mn复合氧化物整体式催化剂催化低浓度甲烷燃烧反应性能的影响

以堇青石蜂窝陶瓷(COR)为载体,采用浸渍法制备了Cu-Mn-O/A12O3/COR,Cu-Mn-Ce-O/Al2O3/COR,Cu-Mn-Zr-O/Al2O3/COR,Cu-Mn-La-O/A12O3/COR和Cu-Mn-Ce-Zr-O/Al2O3/COR5种Cu-Mn复合氧化物整体式催化剂,用于低浓度甲烷催化燃烧反...     

纳米膜组装介孔Al2O3：合成及Pt/Al2O3的硝基苯催化加氢性能

以"乙酸乙酯(EA)-偏铝酸钠-水"体系在室温下合成了纳米膜组装介孔Al2O3。研究发现:合成反应时间、静置前搅拌时间、NaAlO2用量、EA用量及反应温度等对合成产物的形貌有影响;另外,与用商品γ-Al2O3制备的Pt/γ-Al2O3催化剂相比,纳米膜组装介孔Al2O3制备的Pt/Al2O3催化剂含有部分易被还原的PtOx物种。在硝基苯催化加氢反应中,用合成Al2O3为载体制备的Pt/Al2O3催化剂,比用商品γ-Al2O3制备的Pt/γ-Al2O3催化剂具有更好的催化活性。     

甲烷部分氧化制合成气Pt-Ni/Al~2O~3催化剂的研究

研究了Ni/Al~2O~3,Pt/Al~2O~3和一系列Pt-Ni/Al~2O~3催化剂对甲烷部分氧化制合成气的催化作用,发现Pt-Ni/Al~2O~3催化剂显示了比Ni/Al~2O~3和Pt/Al~2O~3更高的活性和稳定性。H~2-TPR,CO-TPD,CO~2-TPD,SEM,XPS和XRD等结果证明:Pt和Ni之间存在较强的相互作用,Pt和部分Ni形成固溶体合金并且Pt在催化剂表面富集。Pt和Ni之间的相互作用提高了催化剂的活性和稳定性,甲烷在Pt-Ni/Al~2O~3上的催化部分氧化具有不同于在Pt/Al~2O~3和Ni/Al~2O~3上的反应性能。     

Al-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以磷酸氢二铵为磷源,硝酸镍为镍源,硝酸铝为助剂铝源,制备了n_P/n_Ni=0.8,Al含量为1.06wt%~6.35wt%的一系列Al-Ni₂P/SBA-15催化剂。采用XRD、TEM和N₂吸脱附等技术对催化剂的结构进行了表征研究,以二苯并噻吩(DBT)作为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,Al修饰的Al-Ni₂P/SBA-15催化剂仍然保持介孔结构,当Al含量低于5.29wt%时,催化剂的物相主要是Ni₂P,当Al含量在5.29wt%-6.35wt%之间时,催化剂的物相为Ni₂P和Ni₁₂P₅。Al含量为4.24wt%的3-Al-Ni₂P/SBA-15催化剂具有最好的二苯并噻吩加氢脱硫催化活性,在反应温度为360 ℃,反应压力为3.0 MP的条件下,3-Al-Ni₂P/SBA-15催化剂对二苯并噻吩的转化率可达99.0%。     

Experimental and DFT studies of the conversion of ethanol and acetic acid on PtSn-based catalysts

Reaction kinetics studies were conducted for the conversions of ethanol and acetic acid over silica-supported Pt and Pt/Sn catalysts at temperatures from 500 to 600 K. Addition of Sn to Pt catalysts inhibits the decomposition of ethanol to CO, CH4, and C2H6, such that PtSn-based catalysts are active for dehydrogenation of ethanol to acetaldehyde. Furthermore, PtSn-based catalysts are selective for the conversion of acetic acid to ethanol, acetaldehyde, and ethyl acetate, whereas Pt catalysts lead mainly to decomposition products such as CH4 and CO. These results are interpreted using density functional theory (DFT) calculations for various adsorbed species and transition states on Pt(111) and Pt3Sn(111) surfaces. The Pt3Sn alloy slab was selected for DFT studies because results from in situ (119)Sn M?ssbauer spectroscopy and CO adsorption microcalorimetry of silica-supported Pt/Sn catalysts indicate that Pt-Sn alloy is the major phase present. Accordingly, results from DFT calculations show that transition-state energies for C-O and C-C bond cleavage in ethanol-derived species increase by 25-60 kJ/mol on Pt3Sn(111) compared to Pt(111), whereas energies of transition states for dehydrogenation reactions increase by only 5-10 kJ/mol. Results from DFT calculations show that transition-state energies for CH3CO-OH bond cleavage increase by only 12 kJ/mol on Pt3Sn(111) compared to Pt(111). The suppression of C-C bond cleavage in ethanol and acetic acid upon addition of Sn to Pt is also confirmed by microcalorimetric and infrared spectroscopic measurements at 300 K of the interactions of ethanol and acetic acid with Pt and PtSn on a silica support that had been silylated to remove silanol groups.     

Pt，Pd助剂对Ni基催化剂中Ni的分散度及抗积碳性能的影响

研究了添加少量贵金属(Pt,Pd)的Ni/Al2O3催化剂对甲烷水蒸汽重整反应抗积碳能力和催化性能的影响.催化活性实验表明,添加少量Pt的样品显著提高了Ni/Al2O3催化剂的活性,稳定性,抗积碳和抗氧化能力,而添加Pd的样品对Ni/Al2O3催化剂的催化性能提高并不明显.利用氢气程序升温还原(H2-TPR),X射线晶体衍射(XRD),热重-差热分析(TG-DTA)等手段对反应前后的催化剂进行了表征,研究发现在Ni-Pt/Al2O3催化剂中Ni与Pt之间存在较强的相互作用力,在主要由Ni覆盖的表面形成了Ni-Pt双金属簇,提高了Ni的分散度,在催化剂的表面易于形成较小的Ni颗粒,抑制了Ni的烧结,改善了Ni基催化剂的抗积碳能力;贵金属Pt通过H2的溢流效应促进了Ni的还原,抑制了催化剂的氧化.而在Ni-Pd/Al2O3中,Ni和Pd存在着一定的偏析效应,不能有效的形成Ni-Pd双金属簇,在还原过程中分别被还原.     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体, 制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1, 0.75, 0.5, 0.25, 0). 应用Brunauer-Emmet-Teller (BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征, 并系统研究了催化剂在饮食油烟催化燃烧中的催化活性. BET结果表明催化剂的比表面积随Ce/Zr摩尔比的减小而减小. XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上. H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好. 催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧, 降低了反应温度. 随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化, 催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2>Pt/γ-Al2O3/Ce0.25Zr0.75O2>Pt/γ-Al2O3/Ce0.75Zr0.25O2>Pt/γ-Al2O3/CeO2>Pt/γ-Al2O3/ZrO2.     

PtZn-Sn/SBA-15合成、表征及对丙烷催化脱氢性能

以SBA-15为载体,利用浸渍法制备了单、双和三金属Pt催化剂,并对催化剂进行了N2物理吸附(BET)、程序升温还原(H2-TPR)、H2-化学吸附、透射电子显微镜(TEM)和O2-脉冲等技术表征,研究了它们对丙烷催化脱氢(CDH)制丙烯反应的催化性能。研究结果表明,Pt在三金属催化剂中的分散性能最好,并且部分负载组分可以进入SBA-15的孔道,Pt的分散度达到29%,Pt粒子尺寸为3 nm左右。三金属催化剂表现出优越的脱氢性能,这主要归结于载体的弱酸性、活性组分和助剂、载体之间的相互作用及Zn对Pt的电子调控作用。这些因素使催化剂的积炭量较低,因而具有较高的脱氢稳定性和极高的选择性。     

Characterization and acidic properties of Al-SBA-15 materials prepared by post-synthesis alumination of a low-cost ordered mesoporous silica

A series of Al-containing SBA-15 type materials with different Si/Al ratio, were prepared by post-synthesis modification of a pure highly ordered mesoporous silica SBA-15 obtained by using sodium silicate as silica source, and amphiphilic block copolymer as structure-directing agent. A high level of aluminum incorporation was achieved, reaching an Si/Al ratio of up to 5.5, without any significant loss in the textural properties of SBA-15. These materials were fully characterized by powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), ²⁷Al NMR spectroscopy, and N₂ adsorption at 77 K. The acid properties of these materials have been evaluated by NH₃-TPD, adsorption of pyridine and deuterated acetonitrile coupled to FTIR spectroscopy. The effective acidity of these materials was evaluated using two catalytic reactions: 2-propanol dehydrogenation and 1-butene isomerization. The adsorption of basic probe molecules and the catalytic behavior revealed an evolution of the acid properties with the Al content. These studies have shown that the Al-SBA-15 materials contain Brønsted and Lewis acid sites with medium acidity which makes them appropriate to be used as acid catalysts in heterogeneous catalysis, catalytic supports, and adsorbents.