分光光度法研究膨润土负载型 光催化剂降解亚甲基蓝

以Zn(NO3)2、SnCl4和膨润土为原料,采用沉淀法制备膨润土负载ZnO/SnO2光降解催化剂,用XRD对其结构进行了表征.在可见光下对亚甲基蓝染料废水进行降解实验,讨论了影响亚甲基蓝降解的主要因素.结果表明,光降解催化剂具有优良的光催化活性,在可见光下对浓度为10mg/L亚甲基蓝,30min降解率达到99.5%.     

分光光度法研究插层膨润土对有机染料的脱色性能

以钠基膨润土为原料制备o-羧甲基壳聚糖插层膨润土,通过XRD、IR及SEM表征插层膨润土的表面性质及组织构造;用分光光度法分析插层膨润土对有机染料的脱色性能;同时探讨表面活性剂和o-羧甲基壳聚糖加料顺序、配比对脱色性能的影响。结果表明:当表面活性剂和o-羧甲基壳聚糖为2:1时,先加入表面活性剂反应一定时间再加入羧甲基壳聚糖所得的插层膨润土对亚甲基蓝和酸性蓝脱色性能最优,脱色率可达98.5%。     

铁掺杂TiO2/膨润土光催化剂的制备及表征

以溶胶-凝胶法制备了过渡金属铁掺杂的Fe-TiO2/膨润土复合光催化剂,通过XRD、FTIR技术对该系列催化剂的结构进行了表征,并以亚甲基蓝染料废水为模型,考察了紫外光和日光下铁掺杂量对催化剂性能的影响。结果表明,催化剂中有锐钛矿型TiO2生成,铁掺杂TiO2进入了膨润土的蒙脱石层间,改变了蒙脱石层间的有序性,生成了Ti—O—Si键,实现了TiO2粒子与膨润土的复合;适量Fe3+的掺杂降低了TiO2粒子的粒径,并且部分Fe3+还可能进入了TiO2的晶格,形成了缺陷位,拓宽了TiO2的光谱利用范围,提高了光催化活性。     

超声场中sol-gel法制备纳米TiO2光催化剂的研究

本文在频率分别为20kHz、30kHz、40kHz(电功率均为500W)的超声场中制备溶胶。用光散射法测得溶胶粒子粒径分别为29．4nm、18．3nm、13．2nm，对无超声场和超声场(40kHz)制备的凝胶进行超临界乙醇干燥。用XRD、BET、TEM、DRS对上述干燥的TiO2粒子进行表征，以光催化降解罗丹明B为模型反应。结果表明，在实验范围内溶胶粒径随超声波频率的升高而减小，加超声场制备的纳米TiO2粒子光催化活性比无超声场下制备的粒子高。     

插层化合物LiV2O4的制备与实验研究

用化学方法从层状化合物LiVO₂中引出0.5个Li后得到Li_0.5VO₂,再经过低温真空热处理制备出尖晶石结构化合物LiV₂O₄,类似地处理Li_0.465VO₂,得到缺Li的Li_0.93V₂O₄,LiV₂O₄和Li_0.93V 关键词：     

插层化合物LiVO2的合成及物理性能的研究

本文用固态反应方法成功地合成了插层化合物LiVO₂。进行了成分配比实验、元素定量化学分析和X射线粉末衍射分析。最后对结果进行了讨论。 关键词：     

TiO2/SnO2复合光催化剂的制备及性能

采用特殊液相沉淀法制备纳米级的TiO2/SnO2复合粒子,对制备的纳米TiO2/SnO2采用XRD、TEM等手段进行了表征。用它做催化剂在日光下对甲基橙溶液进行了光催化实验。结果表明,纳米级TiO2/SnO2复合催化剂比纯TiO2的催化活性好,当SnO2摩尔百分数为20%时效果最佳,在60min内对10mg/L的甲基橙水溶液的降解率高达90.2%,具有较好的光催化活性。     

有机膨润土负载ZnO/TiO2光降解催化剂的研制及性能

以六水硝酸锌、酞酸丁酯和有机膨润土为原料,采用沉淀法制备ZnO/TiO2膨润土复合光催化材料,用IR和XRD对光催化剂的组织构造和微观结构进行表征,实验了光催化剂对亚甲基蓝废水的降解性能。结果表明：ZnO/TiO2成功负载于膨润土片层表面,ZnO的含量为有机膨润土的8%,反应温度为70℃,焙烧温度为420℃,催化剂用量为12mg/L时,亚甲基蓝废水的降解率可达97%以上。     

TiO2/SiO2多层膜的带隙结构及光催化性能

利用传输矩阵法设计了由SiO2、TiO2组成的多层膜高透射率光子晶体结构,并分析了其透射谱特性,根据等效层原理改变多层膜一维光子晶体的自身结构来提高通带内特征波长附近的透射率,获得了最佳结构参数。研究结果表明,当晶格参数为150nm,填充比为0.346,周期数为6时,400nm波长附近吸收带处的透射率最低也可达96.5%,并且不论是TM模式还是TE模式,入射角在0°～45°范围内仍保持高的透射率,该结构可望用于空气净化装置以提高SiO2、TiO2光催化剂的光催化效率。     

利用Li+插层调控WS2光电器件响应性能研究

过渡金属硫族化合物由于其具有独特的结构和性质,在光电子学、纳米电子学、储能器件、电催化等领域具有广泛的应用前景,是一类被持续关注的代表性二维层状材料.在材料应用过程中,对材料掺杂特性的调控会极大地改变器件的响应性能.因而,对利用掺杂手段调控过渡金属硫族化合物器件响应性能的研究具有重要的意义.电化学离子插层方法的发展为二维材料的掺杂调控提供了新的手段.本文以WS₂为例,采用电化学离子插层方法对厚层WS₂的掺杂特性进行优化,观察到离子插入后器件电导率的显著增强(约200倍),以及栅压对器件光电响应性能的有效且可逆的调控.本文通过栅压控制离子插层的方法实现对WS₂器件光电响应的可逆可循环调节,为利用离子插层方法调控二维材料光电器件响应性能研究提供了实验基础.     

膨润土负载掺铁氧化钛光降解苯酚

以钛酸四丁酯为原料,用溶胶-凝胶法制备了以膨润土为载体的负载型TiO2光催化剂;采用分光光度法测试其光降解性能;讨论了影响苯酚降解的主要因素。结果表明,在pH=8.0时,光催化剂的用量为15mg/L,苯酚溶液的浓度为5mg/L时,光照时间为120min,苯酚的降解率可达98.2%。     

铂颗粒粒径效应:负载铂纳米颗粒的TiO2薄膜性质研究

制备了负载不同大小Pt纳米颗粒的TiO薄膜。利用TEM测定了Pt粒子的大小,XRD,UV—Vis和测量光电流等方法对TiO2复合膜进行了表征,以亚甲基蓝降解反应评价了Pt／TiO2薄膜的光催化活性。结果表明,在负载相同物质的量的Pt情况下,Pt颗粒的大小直接影响TiO2薄膜的性能,显示较强的粒径效应,当负载平均粒径约5nm的Pt粒子后,薄膜具有最高的光电流和光催化活性。     

光催化剂SO2- 4/TiO2和TiO2 的光谱行为比较

用ＩＲ、Ｒａｍａｎ和ＤＲＳ光谱研究了ＳＯ＾２－４／ＴｉＯ２光催化剂和ＴｉＯ２光催化剂的光谱行为差别。结果表明,ＴｉＯ２光催化剂的表面只有Ｌ酸中心,而ＳＯ＾２－４／ＴｉＯ２光催化剂表面既有Ｌ酸中心也有Ｂ酸中心。ＴｉＯ２的硫酸化有效地抑制了晶相转变和晶粒度的增加。与ＴｉＯ２相比,ＳＯ＾２－４／ＴｉＯ２光催化剂的锐钛矿相含量较多、晶粒较小、光谱吸收边蓝移,从而增大了光吸收阈值,增强了光生空穴和电子的氧化     

TiO2花状纳米结构的制备及光催化性能

用Ti片和H2O2在较低的温度下通过控制反应时间制备了不同形貌的纳米TiO2.在80℃下反应10 min得到了和Ti片黏附较好的多孔纳米结构,延长反应时间先后得到了类花状和类棒状纳米结构．在80℃下反应4 h得到的纳米结构样品为非晶态,而反应10 h制备出以锐钛矿相为主的结晶态纳米结构．通过300℃退火得到的几乎是纯锐钛矿相的纳米TiO2．用紫外光照射降解RhB溶液的方法研究了纳米TiO2的光催化性能．结果表明7 cm2的退火后的类花状纳米TiO2降解染料分子的光催化效率是仅用紫外光降解的29．8倍．     

Preparation of S-TiO2 photocatalyst and photodegradation of L-acid under visible light

S-doped TiO₂ (S-TiO₂) photocatalyst was synthesized by sol–gel method with tetrabutyl titanate and thiourea as precursor. S-TiO₂ was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV–vis absorption spectroscopy, transmission electron microscopy (TEM) and the photocatalytic activity was evaluated by 1-naphthol-5-sulfonic acid (L-acid) under UV, visible light and solar light radiation. The results showed that doped S could improve photoabsorption property of TiO₂ in the visible region, leading the increase in the photocatalytical activity of TiO₂.

The average particle size of the S-TiO₂ photocatalyst is about 10 nm. The S-TiO₂-4 photocatalyst contains 100% anatase crystalline phase of TiO₂. In the S-TiO₂-4 photocatalyst, S does not exist independently, but is incorporated into the crystal lattice of TiO₂. In the inner crystal lattice of the S-TiO₂-4 photocatalyst, S as S²⁻ replaces O in TiO₂, while on the surface of crystal lattice, S exists as S⁴⁺ and S⁶⁺.

The photocatalytical activity of S-TiO₂-4 photocatalyst for the photodegradation of L-acid is better than that of pure TiO₂. Under the same conditions, the photodegradation efficiency of L-acid for the S-TiO₂-4 photocatalyst and the solar light irradiation is 85.1%, while it is only 26.4% for pure TiO₂. In addition, the final products of the photocatalysis of L-acid using the S-TiO₂-4 photocatalyst are not organic compounds with low molecular weight, but the inorganic compounds.     

One-step synthesis of black TiO2-x microspheres by ultrasonic spray pyrolysis process and their visible-light-driven photocatalytic activities

Black TiO_2-x has recently emerged as one of the most promising visible-light-driven photocatalysts, but current synthesis routes that require a reduction step are not compatible with cost-effective mass production and a relatively large particle such as microspheres. Herein, we demonstrate a simple, fast, cost-effective and scalable one-step process based on an ultrasonic spray pyrolysis for the synthesis of black TiO_2-x microspheres. The process utilizes an oxygen-deficient environment during the pyrolysis of titanium precursors to directly introduce oxygen vacancies into synthesized TiO₂ products, and thus a reduction step is not required. Droplets of a titanium precursor solution were generated by ultrasound energy and dragged with continuous N₂ flow into a furnace for the decomposition of the precursor and crystallization to TiO₂ and through such a process spherical black TiO_2-x microspheres were obtained at 900 °C. The synthesized black TiO_2-x microsphere with trivalent titanium/oxygen vacancy clearly showed the variation of physicochemical properties compared with those of white TiO₂. In addition, the synthesized microspheres presented the superior photocatalytic activity for degradation of methylene blue under visible light irradiation. This work presents a new methodology for a simple one-step synthesis of black metal oxides microspheres with oxygen vacancies for visible-light-driven photocatalysts with a higher efficiency.     

碳量子点负载TiO_2纳米棒阵列的光电化学性能

研究了碳量子点负载的Ti O2纳米棒阵列光阳极的光电化学过程和光催化行为。实验发现碳量子点的引入使Ti O2纳米棒阵列在可见光区域的吸收强度增强,对可见光的响应电流提高3倍,光照下的开路电位增加了2.5%,光生载流子的转移和传输能力得到相应提高。光阳极对亚甲基蓝的降解特性显示,碳量子点的引入使Ti O2纳米棒在可见光照射下的催化效率由25%提高到33%。利用电化学交流阻抗谱(EIS)、MottSchottky曲线讨论了光影响下的电荷运动过程,表明Ti O2纳米棒阵列负载碳量子点后的电荷转移电阻减小,电子寿命增加;碳量子点的负载使Ti O2纳米棒的平带电位负移,导带位置提高,电子的还原能力增强。