Selective Catalytic Reduction of NO with Propene over Au/Fe2O3/Al2O3 Catalysts

A series of Au/Fe₂O₃/Al₂O₃ catalysts were prepared by the homogeneous deposition-precipitation method. The catalytic activity of the catalyst samples for selective catalytic reduction of NO by propene under oxygen-rich atmosphere was evaluated. The results showed that 2%Au/10%Fe₂O₃/Al₂O₃ exhibited good low-temperature activity. The maximum of NO conversion reached 43% at 300 °C, while it was only 21% over the 2%Au/Al₂O₃ catalyst at the same temperature. The addition of 2% steam to the feed gas had little effect on the catalytic activity. X-ray diffraction results indicated that both Au and Fe₂O₃ particles were highly dispersed over Al₂O₃. H₂-temperature-programmed reduction results indicated that there was strong interaction between Au and Fe₂O₃, which made the reduction of Fe₂O₃ easy. The synergistic effect between Au and Fe₂O₃ was probably responsible for the good catalytic performance of the Au/Fe₂O₃/Al₂O₃ catalyst at low temperature.     

V2O5/赤铁矿催化剂结构及其NH3选择性催化还原NOx性能

以水热合成针铁矿为前驱体浸渍偏钒酸铵,分别于300,400和500℃空气中焙烧,制备了不同活性组分负载量的V₂O₅/赤铁矿（V/H）催化剂,用于氨选择性催化还原（SCR）脱硝。采用X射线衍射、透射电子显微镜、比表面积分析仪、程序升温还原及程序升温脱附等方法对催化剂结构进行了表征,并用标气配制模拟烟气进行了脱硝实验。结果表明,300℃煅烧3%V/H催化剂当烟气温度为250-300℃时NO转化率均可达95%以上;当配气中单独加入水蒸气或低浓度SO₂（0.01%）时,V/H催化脱硝的活性不受影响;当系统加入高浓度的SO₂（0.03%与0.05%）或同时添加H₂O与SO₂时,SCR脱硝效率下降,其机制可能是SO₂在催化剂表面竞争吸附所致,停止添加后,催化活性迅速恢复。     

Cu/La2O3-ZrO2-Al2O3催化剂的制备及其对NO选择性还原的催化性能

采用将Al(NO3)3、La(NO3)3和ZrOCl2的混合液滴入沉淀剂(NH4)2CO3中的共沉淀法制备La2O3-ZrO2-Al2O3复合载体,然后负载上Cu2+,制成Cu/La2O3-ZrO2-Al2O3催化剂。考察了该催化剂在富氧条件下对C3H6选择还原NO的催化性能,并借助扫描电子显微镜（SEM）、X射线衍射（XRD）、比表面积测定（BET）、吡啶吸附红外光谱（Py-IR）、程序升温还原（TPR）和热重分析（TG）等方法研究催化剂制备方法与结构、性能的关系。实验结果表明,采用将Al(NO3)3滴入(NH4)2CO3制得的γ-Al2O3能有效地增大催化剂的比表面积,加入La2O3能提高催化剂的热稳定性,加入ZrO2能大幅度增加催化剂表面L酸和B酸的酸量。因此,采用共沉淀法制备的La2O3-ZrO2-Al2O3复合载体能够使Cu/La2O3-ZrO2-Al2O3催化剂具有良好的催化性能,最佳催化活性温度为300℃,NO最大转化率高达88.9%,在有10%水蒸气存在的情况下,仍可达81.9%。     

Enhancing effect of water vapor on the reduction of lean NOx by ethanol over an Ag/Al2O3 catalyst supported on cordierite honeycomb

The Ag/Al₂O₃ catalyst supported on cordierite honeycomb (Ag/Al₂O₃/ cordierite) is highly active forthe reduction of lean NOx by ethanol. Addition of H₂O enhances the NOx reduction to CO₂ and N₂, and suppresses the formation of by-products such as CO, CH₃CHO and C₂H₄.     

OMS-2/Al2O3/堇青石整体式催化剂的制备及其催化性能研究

以Al₂O₃/堇青石蜂窝陶瓷为载体,氧化锰八面体分子筛(OMS-2)为活性组分,采用涂覆法制备了系列整体式催化剂。考察了黏合剂种类和活性组分涂覆次数对二甲醚(DME)催化燃烧性能的影响,并对催化剂进行XRD、BET、SEM、H₂-TPR、O₂-TPD等表征。结果表明,以甲氧基聚乙二醇为黏合剂经一次涂覆制备的整体式催化剂的性能最佳,活性组分OMS-2以相互交织的簇体均匀分布在载体上,并与Al₂O₃之间存在较强的相互作用。涂层的添加有效增加了催化剂的比表面积,提高了催化剂的性能,最佳催化活性t₉₀为257 ℃。     

Two-stage catalytic system of Sn/Al2O3 and Pt/Al2O3for NO reduction by propene in lean conditions

The Pt/Al₂O₃, Sn/Al₂O₃catalysts were prepared by the single sol-gel method. The two-stage Sn/Al₂O₃and Pt/Al₂O₃catalyst in series for NO reduction with propene were investigated. The coexistance of water vapor enhanced the activity at medium temperature of 300-400^oC, and the NO conversion was above 50% at 225 to 500^oC even in the presence of water vapor and SO₂. This revised version was published online in August 2006 with corrections to the Cover Date.     

Mechanistic studies of methane partial oxidation to syngas over LiNiLaOx/Al2O3 catalyst

Reduction of vanadium-titanium oxide catalysts with hydrogen in the temperature range of 150–450°C results in the increase of the content of V⁴⁺ ions in substitution positions of TiO₂ with the anatase structure. The temperature increase up to 250°C results in the growth of the spectral intensity of V⁴⁺ associates in substitution positions of anatase. At higher treatment temperatures their intensity decreases due to the formation of VO₂ fragments in anatase. At 400°C and higher temperatures a solid solution of V⁴⁺ ions in rutile is formed.     

SO_2对甲烷在金属铁表面还原NO的反应影响

采用卧式程序控温电加热陶瓷管反应器,在N2和模拟烟气气氛中、300~1 100℃下,研究了SO2对甲烷在金属铁及其氧化物表面还原NO反应的影响。采用XRD等手段对反应前后铁催化剂样品的组成变化进行了表征,分析了SO2在甲烷-铁脱硝反应中的作用机理。结果表明,甲烷在金属铁及氧化铁表面能够高效率地还原NO,NO还原效率不受烟气中SO2的影响。在SO2体积分数为0.01%~0.04%的N2气氛中,温度高于700℃时,金属铁上NO还原率和SO2脱除率可同时达到100%。在SO2体积分数为0.01%~0.04%的模拟烟气中,当温度高于850℃时,NO还原效率达到90%以上;温度为950℃时,NO还原效率达到98%,SO2对NO还原效率的影响可忽略。当反应温度为1 000℃时,在含0.02%SO2的模拟烟气中,甲烷的体积分数为1.13%时,持续100 h金属铁表面上的NO还原效率都能保持95%以上。     

Ag对Pd/CeO2-ZrO2-La2O3-Al2O3催化氧化甲醇性能的影响

采用等体积共浸渍法制备了一系列Pd-Ag/CeO2-ZrO2-La2O3-Al2O3催化剂。运用N2吸附-脱附,X射线衍射(XRD),H2程序升温还原(H2-TPR),紫外-可见漫反射光谱(UV-Vis DRS),X射线光电子能谱(XPS)对催化剂进行表征,并考察其对甲醇的催化氧化性能。活性测试结果表明,Ag的添加可显著改善Pd催化剂对甲醇的催化氧化活性,T50、T90以及ΔT分别为125℃,150℃和25℃,具有较好的应用前景。H2-TPR表明,引入Ag可明显改善催化剂的还原性能,使表面易还原氧物种量增多,还原速率加快;UV-Vis DRS及XPS表明,Pd、Ag金属之间以及金属与载体之间存在电子效应,这种效应促使金属与载体界面产生大量具有活性的氧物种,不仅提高了催化剂的低温活性,还提高了催化剂的氧化速率。     

SO_4~(2-)功能化处理对Fe_2O_3催化剂上氨选择性催化还原NO_x性能的促进机理研究

采用沉淀法制备了Fe(OH)_3和Fe_2O_3。通过硫酸化处理得到SO_4~(2-)/Fe(OH)_3和SO_4~(2-)/Fe_2O_3两种催化剂,并将其应用于氨选择性催化还原NO_x(NH_3-SCR)反应,研究了SO_4~(2-)功能化处理对Fe_2O_3催化剂上NH_3-SCR脱硝性能的促进机理。结果表明,与纯的Fe_2O_3相比,硫酸化处理得到的催化剂上SCR活性得到显著提升;其中,SO_4~(2-)/Fe(OH)_3表现出更加优异的催化性能,在250-450℃时NO_x转化率高于80%,且具有优异的稳定性和抗H_2O+SO_2性能。XRD、Raman、TG、FT-IR、H_2-TPR、NH_3-TPD和in situ DRIFTS等表征结果显示,硫酸功能化处理能抑制Fe_2O_3的晶粒生长,同时SO_4~(2-)与Fe~(3+)结合形成硫酸盐复合物,提高了催化剂表面酸性位点的数量和酸强度,抑制了Fe_2O_3上的氨氧化反应,从而提高了其脱硝催化性能。     

NO reduction with C3H8 on Co/Al2O3 catalyst. effect of O2 concentration

The selective catalytic reduction (SCR) of NO by propane in excess oxygen-containing gas mixture was studied on Co/Al₂O₃ catalyst. The oxygen concentration is very important for the reaction. The NO conversion to N₂ without oxygen is 3% at 800 K and when the O₂ concentration is raised up to 8% the NO conversion reaches its maximum value of 60% at 800 K. Characterization results by TPR and UV-Vis spectroscopy show that in the catalyst, species strongly interacting with tetrahedral and octahedral Co²⁺ ions in the support are present. This revised version was published online in June 2006 with corrections to the Cover Date.     

丙烷在Ce-Fe/Al2O3/cordierite上选择性催化还原NO

利用凝胶溶胶法和浸渍法制备了Ce-Fe/Al₂O₃/cordierite催化剂,实验研究了其催化丙烷选择性还原NO的特性。结果表明,当铈的负载量从1%增加至5%时,Ce-Fe/Al₂O₃/cordierite的C₃H₈-SCR性能先增强后减弱,3.5Ce-Fe/Al₂O₃/cordierite具有最佳的脱硝性能,在有氧条件下,600℃时可实现96.5%的脱硝效率。Ce的加入能够提升Fe/Al₂O₃/cordierite催化剂的抗硫性能。烟气中通入0.02%的SO₂后,3.5Ce-Fe/Al₂O₃/cordierite催化丙烷还原NO的转化率始终维持在93%,而没有经过Ce修饰的Fe/Al₂O₃/cordierite的NO转化率从88%下降为80%左右。利用XRD、N₂吸附-脱附、SEM、H₂-TPR、吡啶吸附红外光谱等手段研究了催化剂的物理化学性质。结果表明,加入助剂铈能与Fe形成了固溶体,增加催化剂表面Lewis酸浓度和氧化还原能力,从而提高了催化丙烷还原NO的性能。过多的铈引入会减少Fe₂O₃结晶体的形成,不利于在C₃H₈-SCR反应中形成NO₂/NO₃^-物种,从而导致NO还原效率下降。     

Cooperation of reducing species for NO reduction over Ag/Al2O3 under oxidizing conditions

Summary The cooperation effect of reducing species for selective reduction of NO over Ag/Al₂O₃ has been investigated in the presence of excess oxygen. When the combinations of propene or propane and ethanol or methanol were used as reducing agents, NO reduction took place over a wider temperature range, compared with a single hydrocarbon as reducing agent.     

Effect of sol-gel derived Al2O3-ZrO2 and Al2O3-TiO2 oxides on the selectivity of NO reduction by CO under oxidizing conditions

The role of Al₂O₃-ZrO₂ and Al₂O₃-TiO₂ sol-gel prepared supports in the activity of platinum for the NO reduction by CO under oxidizing conditions has been studied. ²⁷Al MAS-NMR spectra have shown the formation of pentacoordinate Al^V in alumina-zirconia support. ZrO₂ or TiO₂ crystalline phases cannot be identified by XRD diffraction, suggesting the formation of nanosized structures supported on alumina. When the reaction was carried out in presence of oxygen, large amounts of NO₂ were observed on Pt/Al₂O₃-ZrO₂catalyst, while the formation of N₂O is more prononced on Pt/Al₂O₃-TiO₂ catalyst. The effect of water during NO reduction is discussed. This revised version was published online in June 2006 with corrections to the Cover Date.     

Artificial neural network modelling applied on NOx reduction with octane in excess oxygen over Ag/Al2O3

A silver/alumina catalyst was tested for its NO_x reduction activity during oxygen-rich conditions and during variation in the input parameters, which were nitric oxide, octane and oxygen. The experimental data were investigated by means of artificial neural networks. This revised version was published online in August 2006 with corrections to the Cover Date.     

Kinetics of Co?Mo/Al2O3 catalyst reduction

According to kinetic studies on the reduction of commercial Co–Mo/Al₂O₃ and model catalysts in H₂ at 523–773 K, the kinetic curves for the reduction process have been determined. The reduction rate is shown to be higher for the commercial catalyst. Activation energies E_act for the reduction of several forms of Mo and Co in Co–Mo/Al₂O₃ catalysts are presented.

---

H₂ 523–773 . , : Mo Co .

     

Promoting effect of sol-gel method and pre-treatment on the activity of SnO2/Al2O3 catalyst for NO reduction by propene

SnO₂/Al₂O₃ catalyst prepared by sol-gel method showed higher activity than those prepared by impregnation method, and their activity was significantly improved by pre-treatment in the reaction gas. The increased activity is closely related to the agglomeration of SnO₂ species and the re-exposure of Al₂O₃, which was previously covered by dispersed SnO₂ species. This revised version was published online in June 2006 with corrections to the Cover Date.     

Kinetics of catalytic combustion in air over Pt/Al2O3/Al catalyst

Summary Catalytic combustion of toluene, propylene and CO over Pt/Al₂O₃ /Al catalyst was investigated. Strong inhibition effects are observed when the mixture of toluene, propylene and CO is oxidized. A reaction mechanism of catalytic combustion over Pt/Al₂O/Al is proposed. The results from kinetic models are in good agreement with the experimental data.     

原位漫反射红外光谱法研究SO2对Ag/Al2O3选择性催化丙烯还原NOx反应的影响

 以Ag/Al2O3为催化剂,采用原位漫反射傅里叶变换红外光谱法研究了SO2对C3H6选择性还原NOx反应的影响. 结果表明, SO2在催化剂表面转化为硫酸盐,并且随着硫酸盐累积量的增加,其主要红外特征吸收峰由低波数向高波数漂移. 高浓度表面硫酸盐的存在不仅抑制了催化剂表面硝酸盐的生成,而且抑制了硝酸盐与表面烯醇式物种(RCH=CH-O-)或乙酸盐物种进一步反应,生成活泼的反应中间体异氰酸酯(-NCO), 这是导致Ag/Al2O3催化剂上C3H6选择性还原NOx活性降低的主要原因.     

纳米Fe_3O_4催化剂在稠油水热裂解降黏中的应用

通过高温热解法和低温双相回流法制备了四种不同尺寸的纳米Fe_3O_4催化剂,并将其应用于辽河油田稠油水热裂解降黏实验中。结果表明,制备过程中加入重烷基苯磺酸钠(HABS)表面活性剂能够有效提高Fe_3O_4催化剂在稠油水热裂解体系中的分散性,以高温热解法制备出的HABS修饰的9 nm Fe_3O_4催化剂降黏效果最佳。当稠油量为250 g时,按m(稠油)∶m(催化剂)∶m(油层水)质量比为100∶0.3∶30加入催化剂和油层水,加入0.75 g正作为己烷供氢体,在240℃下反应24 h,辽河油田稠油黏度从86200 mPa·s下降到2065 mPa·s,降黏率高达到97.6%。反应机理分析显示,纳米Fe_3O_4催化剂攻击稠油长链上键能最低C-S键,使其断键,重组分转化为轻组分。