Side‐Chain‐Functionalized Polyacetylenes, 2. Photovoltaic Properties

Polymerization of a functionalized acetylene was successfully performed using a Rh complex as the catalyst and triethylamine as a base yielding poly{(E,E,E)‐4‐[4‐[4‐(3,4,5‐tridodecyloxystyryl)‐2,5‐bis((S)‐2‐methylbutoxy)styryl]‐2,5‐bis((S)‐2‐methylbutoxy)styryl]phenylacetylene} ( PAOPV ). Films of PAOPV mixed with a fullerene derivative showed electron transfer from the OPV oligomer donor to the fullerene acceptor. The films could be furthermore used in photovoltaic devices.     

Photovoltaic activity of Ti/MCM‐41

Ti/MCM‐41 is a well‐known heterogeneous catalyst for alkene epoxidation with organic peroxides. This titanosilicate contains isolated titanium atoms forming part of a framework of mesoporous silica whose structure is formed by parallel hexagonal channels 3.2 nm in diameter. The surface area and porosity of Ti/MCM‐41 are about 880 m² g^?1 and 0.70 cm³ g^?1, respectively. These values are among the highest for any material. Herein, we show that Ti/MCM‐41 exhibits photovoltaic activity. Dye‐sensitized solar cells using mesoporous Ti/MCM‐41 (2.8–5.7 % Ti content) as active layer, black dye N3 as photosensitizer and I₃^?/I^? in methoxyacetonitrile as electrolyte exhibit a V_OC, J_SC and FF of 0.44 V, 0.045 mA cm^?2 and 0.33, respectively. These values compare well against 0.75 V, 4.1 mA cm^?2 and 0.64, respectively, measured for analogous solar cells using conventional P‐25 TiO₂. However, the specific current density (J_SC/Ti atom) for the Ti/MCM‐41 is very similar to that of P25 TiO₂.     

Alkylthio‐Substituted Polythiophene: Absorption and Photovoltaic Properties

Two polythiophene derivatives with electron‐donating alkylthio side chains, poly[(3‐hexylthio)thiophene] (P3HST) and poly[(3‐hexylthio)thiophene‐alt‐thiophene] (P3HST‐co‐Th) have been synthesized and characterized. Both P3HST and P3HST‐co‐Th show broader absorption peaks than poly(3‐hexylthiophene). Meanwhile, the alkylthio side chains decrease the HOMO energy level of the polymers, which benefits the higher open circuit voltage of the polymer solar cells (PSCs) based on the polymer as donor. PSCs have been fabricated with the polymers as donor and [6,6]‐phenyl C61 butyric acid methyl ester as acceptor (1: 1, w/w). The devices based on P3HST and P3HST‐co‐Th show an open circuit voltage of 0.63 V, and a power conversion efficiency of 0.34% and 0.5%, respectively, under the illumination of AM1.5, 80 mW · cm⁻².

     

Thienopyrazine‐Based Low‐Bandgap Poly(heteroaryleneethynylene)s for Photovoltaic Devices

Summary: Low‐bandgap π‐conjugated polymers that consist of alkyl thiophene/alkoxy phenylene and 2,3‐diphenylthieno[3,4‐b]pyrazine units have been prepared in high yields by a Sonogashira polycondensation. The copolymers are characterized by NMR, IR, UV, GPC, and elemental analysis. Thin films of the polymers P1 , P2 , and P3 exhibit an optical bandgap of ≈1.57–1.60 eV. Under simulated AM 1.5 conditions P2/PCBM devices on polyester foil provide a short circuit current of I_SC = 10.72 mA · cm⁻², an open circuit voltage of V_oc = 0.67 V, and a power conversion efficiency of 2.37%.

Schematic of the photovoltaic device made from the polymers synthesized here.     

Tailoring Component Interaction for Air‐Processed Efficient and Stable All‐Inorganic Perovskite Photovoltaic

All‐inorganic lead halide perovskites are promising candidates for optoelectronic applications. However, fundamental questions remain over the component interaction in the perovskite precursor solution due to the limitation of the most commonly used solvents of N,N‐dimethylformamide (DMF) and dimethyl sulfoxide (DMSO). Here, we report an interaction tailoring strategy for all‐inorganic CsPbI_3?xBr_x perovskites by involving the ionic liquid solvent methylammonium acetate (MAAc). C=O shows strong interaction with lead (Pb²⁺) and N?H???I hydrogen bond formation is observed. The interactions stabilize the perovskite precursor solution and allow production of the high‐quality perovskite films by retarding the crystallization. Without the necessity for antisolvent treatment, the one‐step air‐processing approach delivers photovoltaic cells regardless of humidity, with a high efficiency of 17.10 % along with long operation stability over 1500 h under continuous light illumination.     

Fluorinated Photovoltaic Materials for High‐Performance Organic Solar Cells

Over the past decade, organic solar cells (OSCs) have achieved a dramatic boost in their power conversion efficiencies from about 6 % to over 16 %. In addition to developments in device engineering, innovative photovoltaic materials, especially fluorinated donors and acceptors, have become the dominant factor for improved device performance. This minireview highlights fluorinated photovoltaic materials that enable efficient OSCs. Impressive OSCs have been obtained by developing some important molds of fluorinated donor and acceptor systems. The molecular design strategy and the matching principle of fluorinated donors and acceptors in OSCs are discussed. Finally, a concise summary and outlook are presented for advances in fluorinated materials to realize the practical application of OSCs.     

Synthesis and Photovoltaic Properties of Cyclopentadithiophene‐Based Low‐Bandgap Copolymers That Contain Electron‐Withdrawing Thiazole Derivatives

We have synthesized four types of cyclopentadithiophene (CDT)‐based low‐bandgap copolymers, poly[{4,4‐bis(2‐ethylhexyl)‐4H‐cyclopenta[2,1‐b:3,4‐b′]dithiophene‐2,6‐diyl}‐alt‐(2,2′‐bithiazole‐5,5′‐diyl)] ( PehCDT‐BT ), poly[(4,4‐dioctyl‐4H‐cyclopenta[2,1‐b:3,4‐b′]dithiophene‐2,6‐diyl)‐alt‐(2,2′‐bithiazole‐5,5′‐diyl)] ( PocCDT‐BT ), poly[{4,4‐bis(2‐ethylhexyl)‐4H‐cyclopenta[2,1‐b:3,4‐b′]dithiophene‐2,6‐diyl}‐alt‐{2,5‐di(thiophen‐2‐yl)thiazolo[5,4‐d]thiazole‐5,5′‐diyl}] ( PehCDT‐TZ ), and poly[(4,4‐dioctyl‐4H‐cyclopenta[2,1‐b:3,4‐b′]dithiophene‐2,6‐diyl)‐alt‐{2,5‐di(thiophen‐2‐yl)thiazolo[5,4‐d]thiazole‐5,5′‐diyl}] ( PocCDT‐TZ ), for use in photovoltaic applications. The intramolecular charge‐transfer interaction between the electron‐sufficient CDT unit and electron‐deficient bithiazole (BT) or thiazolothiazole (TZ) units in the polymeric backbone induced a low bandgap and broad absorption that covered 300 nm to 700–800 nm. The optical bandgap was measured to be around 1.9 eV for PehCDT‐BT and PocCDT‐BT , and around 1.8 eV for PehCDT‐TZ and PocCDT‐TZ . Gel permeation chromatography showed that number‐average molecular weights ranged from 8000 to 14 000 g mol^?1. Field‐effect mobility measurements showed hole mobility of 10^?6–10^?4 cm² V^?1 s^?1 for the copolymers. The film morphology of the bulk heterojunction mixtures with [6,6]phenyl‐C₆₁‐butyric acid methyl ester (PCBM) was also examined by atomic force microscopy before and after heat treatment. When the polymers were blended with PCBM, PehCDT‐TZ exhibited the best performance with an open circuit voltage of 0.69 V, short‐circuit current of 7.14 mA cm^?2, and power conversion efficiency of 2.23 % under air mass (AM) 1.5 global (1.5 G) illumination conditions (100 mW cm^?2).     

Photoelectrochemical Complexes of Fucoxanthin‐Chlorophyll Protein for Bio‐Photovoltaic Conversion with a High Open‐Circuit Photovoltage

Open‐circuit photovoltage (V_oc ) is among the critical parameters for achieving an efficient light‐to‐charge conversion in existing solar photovoltaic devices. Natural photosynthesis exploits light‐harvesting chlorophyll (Chl) protein complexes to transfer sunlight energy efficiently. We describe the exploitation of photosynthetic fucoxanthin‐chlorophyll protein (FCP) complexes for realizing photoelectrochemical cells with a high V_oc . An antenna‐dependent photocurrent response and a V_oc up to 0.72 V are observed and demonstrated in the bio‐photovoltaic devices fabricated with photosynthetic FCP complexes and TiO₂ nanostructures. Such high V_oc is determined by fucoxanthin in FCP complexes, and is rarely found in photoelectrochemical cells with other natural light‐harvesting antenna. We think that the FCP‐based bio‐photovoltaic conversion will provide an opportunity to fabricate environmental benign photoelectrochemical cells with high V_oc , and also help improve the understanding of the essential physics behind the light‐to‐charge conversion in photosynthetic complexes.     

Tuning the Donor–Acceptor Strength of Low‐Bandgap Platinum‐Acetylide Polymers for Near‐Infrared Photovoltaic Applications

Two near‐infrared (NIR) absorbing metallopolyynes of platinum ( P1 and P2 ) functionalized with a weakly electron‐donating fluorene unit and two strong electron acceptors (viz. benzo[1,2‐c:4,5‐c′]bis([1,2,5]thiadiazole) and [1,2,5]thiadiazolo[3,4‐i ]dibenzo[a,c]phenazine) were synthesized and applied for NIR photovoltaic applications. With these designed weak donor–strong acceptor electronic traits, these metallopolymers possess narrow bandgaps of 1.54 and 1.65 eV and a low HOMO level of about 5.50 eV, thus inducing a power conversion efficiency up to 1% for bulk heterojunction solar cells at the NIR wavelength.

     

Solution‐Processed Bulk‐Heterojunction Photovoltaic Cells Based on Dendritic and Star‐Shaped D‐π‐A Organic Dyes

A series of D ‐π‐A organic dendritic and star‐shaped molecules based on three various chromophores (i.e., the truxene nodes, triphenylamine moieties as the donor, and benzothiadiazole chromophore as the acceptor) and their corresponding model compounds are facilely developed. Their photophysical and electrochemical properties are investigated in detail by UV/Vis absorption and photoluminescent spectroscopy, and cyclic voltammetry. By changing the various conjugated spacers (i.e., single bond, double bond, and triple bond) among the three chromophores of dendritic series, their photophysical properties (that is, the one‐photon absorption range and two‐photon absorption cross‐section values) are effectively modulated. All D ‐π‐A conjugated oligomers show a broad and strong absorption band from 250 to 700 nm in thin films. Solution‐processed bulk‐heterojunction photovoltaic devices using our oligomer as donor and PCBM as acceptor are fabricated and measured. The power conversion efficiency of the devices based on our oligomers continuously increases from DBTTr to TRTD2A as a result of an increasing relative absorption intensity in longer wavelength region by changing the donor‐acceptor ratio and conjugated spacers between the donor and acceptor. The power conversion efficiency of the devices based on TRTD2A was 0.54 % under the illumination of AM 1.5 and 100 mW cm^?2, which is the highest value recorded based on D ‐π‐A conjugated oligomers containing triphenylamine moieties and benzothiadiazole chromophores with truxene to date.     

Photovoltaic devices using semiconducting polymers containing head‐to‐tail‐structured bithiophene,pyrene, and benzothiadiazole derivatives

An alternating copolymer composed of heal‐to‐tail‐structured 3,4′‐dihexyl‐2,2′‐bithiophene (DHBT) and pyrene units [poly(DHBT‐alt‐PYR)] was synthesized using a Stille coupling reaction for use in photovoltaic devices as a p‐type donor. For the reduction of the bandgap energy of poly(DHBT‐alt‐PYR), 4,7‐bis(3′‐hexyl‐2,2′‐bithiophen‐5‐yl)benzo[c][1,2,5]thiadiazole (BHBTBT) units were introduced into the polymer. Poly(DHBT‐co‐PYR‐co‐BHBTBT)s were synthesized using the same polymerization reaction. The synthesized polymers were soluble in common organic solvents and formed smooth thin films after spin casting. The optical bandgap energies of the polymers were obtained from the onset absorption wavelengths. The measured optical bandgap energy of poly(DHBT‐alt‐PYR) was 2.47 eV. As the BHBTBT content in the ter‐polymers increased, the optical bandgap energies of the resulting polymers decreased. The bandgap energies of poly(50DHBT‐co‐40PYR‐co‐10BHBTBT) and poly(50DHBT‐co‐20PYR‐co‐30BHBTBT) were 1.84 and 1.73 eV, respectively. Photovoltaic devices were fabricated with a typical sandwich structure of ITO/PEDOT:PSS/active layer/LiF/Al using the polymers as electron donors and [6,6]‐phenyl C₇₁‐butyric acid methyl ester as the electron acceptor. The device using poly(50DHBT‐co‐20PYR‐co‐30BHBTBT) showed the best performance among the fabricated devices, with an open‐circuit voltage, short‐circuit current, fill factor, and maximum power conversion efficiency of 0.68 V, 5.54 mA/cm², 0.35, and 1.31%, respectively. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis and Photovoltaic Properties of Thieno[3,4‐c]pyrrole‐4,6‐dione‐based donor–acceptor Copolymers

Three donor–acceptor (D–A) 1,3‐di(thien‐2‐yl)thieno [3,4‐c]pyrrole‐4,6‐dione‐based copolymers, poly{9,9‐dioctylfluorene‐2,7‐diyl‐alt‐1,3‐bis(4‐hexylthien‐2‐yl)‐5‐octylthieno[3,4‐c]pyrrole‐4,6‐dione}, poly{N‐(1‐octylnonyl)carbazole‐2,7‐diyl‐alt‐1,3‐bis(4‐hexylthien‐2‐yl)‐5‐octylthieno[3,4‐c]pyrrole‐4,6‐dione}, and poly {4,8‐bis(2‐ethylhexyloxyl) benzo[1,2‐b:3,4‐b′]dithiophene‐alt‐1,3‐bis(4‐hexylthien‐2‐yl)‐5‐octylthieno[3,4‐c] pyrrole‐4,6‐dione} were synthesized by Suzuki or Stille coupling reaction. By changing the donor segment, the bandgaps and energy levels of these copolymers could be finely tuned. Cyclic voltammetric study shows that the highest occupied molecular orbital (HOMO) energy levels of the three copolymers are deep‐lying, which implies that these copolymers have good stability in the air and the relatively low HOMO energy level assures a higher open‐circuit potential when they are used in photovoltaic cells. Bulk‐heterojunction photovoltaic cells were fabricated with these polymers as the donors and PC₇₁BM as the acceptor. The cells based on the three copolymers exhibited power conversion efficiencies of 0.22, 0.74, and 3.11% with large open‐circuit potential of 1.01, 0.99, and 0.90 V under one sun of AM 1.5 solar simulator illumination (100 mW/cm²). © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Phthalimide and Naphthalimide end‐Capped Diketopyrrolopyrrole for Organic Photovoltaic Applications

Two small molecules named PI‐DPP and NI‐DPP with a DPP core as the central strong acceptor unit and phthalimide/naphthalimide as the terminal weak acceptor were designed and synthesized. The effects of terminal phthalimide/naphthalimide units on the thermal behavior, optical and electrochemical properties, as well as the photovoltaic performance of these two materials were systematically studied. Cyclic voltammetry revealed that the lowest unoccupied molecular orbitals (LUMO) (~ ‐3.6 eV) of both molecules were intermediate to common electron donor (P3HT) and acceptor (PCBM). This indicated that PI‐DPP and NI‐DPP may uniquely serve as electron donor when blended with PCBM, and as electron acceptor when blended with P3HT, where sufficient driving forces between DPPs and PCBM, as well as between P3HT and DPPs should be created for exciton dissociation. Using as electron donor materials, PI‐DPP and NI‐DPP devices exhibited low power conversion efficiencies (PCEs) of 0.90% and 0.76% by blending with PCBM, respectively. And a preliminary evaluation of the potential of the NI‐DPP as electron acceptor material was carried out using P3HT as a donor material, and P3HT: NI‐DPP device showed a PCE of 0.6%, with an open circuit voltage (V _OC) of 0.7 V, a short circuit current density (J _SC) of 1.91 mA•cm^‐2, and a fill factor (FF) of 45%.     

Photovoltaic performance enhancement using fluorene‐based copolymers containing pyrene units

A set of novel conjugated polyfluorene co‐ polymers, poly[(9,9′‐didecylfluorene‐2,7‐diyl)‐co‐(4,7′‐di‐2‐thienyl‐ 2′,1′,3′‐benzothiadiazole‐5,5‐diyl)‐co‐(pyrene‐1,6‐diyl)], are synthesized via Pd(II)‐mediated polymerization from 2,7‐bis(4′,4′,5′, 5′‐tetramethyl‐1,3,2‐dioxaborolan‐2‐yl)‐9,9′‐di‐n‐decylfluorene, 4, 7‐di(2‐bromothien‐5‐yl)‐2,1,3‐benzothiadiazole, and 1,6‐dibromopyrene with a variety of monomer molar ratios. The field‐effect carrier mobilities and optical, electrochemical, and photovoltaic properties of the copolymers are systematically investigated. The hole mobilities of the copolymers are found to be in the range 7.0 × 10^?5 ? 8.0 × 10^?4 cm² V^?1 s^?1 and the on/off ratios were 8 × 10³ ? 7 × 10⁴. Conventional polymer solar cells (PSCs) with the configuration ITO/PEDOT:PSS/polymer:PC₇₁BM/LiF/Al are fabricated. Under optimized conditions, the polymers display power conversion efficiencies (PCEs) for the PSCs in the range 1.99–3.37% under AM 1.5 illumination (100 mW cm^?2). Among the four copolymers, P2, containing a 2.5 mol % pyrene component incorporated into poly[9,9′‐didecylfluorene‐alt‐5,5‐(4′,7′‐di‐2‐thienyl‐2′,1′,3′‐benzothiadiazole)] (PFDTBT) displays a PCE of 3.37% with a short circuit current of 9.15 mA cm^?2, an open circuit voltage of 0.86 V, and a fill factor of 0.43, under AM 1.5 illumination (100 mW cm^?2). © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Enhanced Performance of Organic Photovoltaic Cells Fabricated with a Methyl Thiophene‐3‐Carboxylate‐Containing Alternating Conjugated Copolymer

A new donor‐acceptor copolymer, containing benzodithiophene (BDT) and methyl thiophene‐3‐carboxylate (3MT) units, is designed and synthesized for polymer solar cells (PSCs). The 3MT unit is used as an electron acceptor unit in this copolymer to provide a lower highest occupied molecular orbital (HOMO) level for obtaining polymer solar cells with a higher open‐circuit voltage (V_OC). The resulting bulk heterojunction PSC made of the copolymer and [6,6]‐phenyl‐C71‐butyric acid methyl ester (PC₇₁BM) exhibits a power conversion efficiency (PCE) up to 4.52%, a short circuit current (J_SC) of 10.5 mA·cm‐², and a V_OC of 0.86 V.     

Photovoltaic properties and femtosecond time‐resolved fluorescence study of polyoxometalate‐containing rod–coil diblock copolymers

The photovoltaic properties and exciton decay dynamics of three polyoxometalate (POM)‐containing hybrid rod–coil diblock copolymers (HDCPs), PS‐Mo6‐PT1–3 , are studied. Single‐component photovoltaic cells of PS‐Mo6‐PT2 and inverted solar cells based on ZnO nanorod arrays/ PS‐Mo6‐PT1–3 are fabricated showing power conversion efficiencies only up to 0.055%. To understand the poor photovoltaic performance, femtosecond fluorescence up‐conversion technique is used to study the exciton decay dynamics of all three HDCPs. Drastically different fluorescence dynamics of the three HDCPs are observed in dilute solutions, which is attributed to the different extent and different type of interpolymer association depending on the P3HT rod block length and the cluster loading ratio. While both cation‐mediated POM cluster association and P3HT‐P3HT π‐stacking contribute significantly to PS‐Mo6‐PT2 aggregation, the aggregation of PS‐Mo6‐PT1 and that of PS‐Mo6‐PT3 is driven predominantly by cluster association and π‐stacking, respectively. In conjunction with the high residual polarization anisotropy, it is concluded that charge transfer from P3HT excitons to POM clusters in all three HDCPs is inefficient. An improved system with direct π‐conjugation between the POM clusters and the rod block addressing this issue has been proposed. © 2013 Wiley Periodicals, 2014 , 52, 122–133     

Flexible Near‐Infrared Photovoltaic Devices Based on Plasmonic Hot‐Electron Injection into Silicon Nanowire Arrays

The development of flexible near‐infrared (NIR) photovoltaic (PV) devices containing silicon meets the strong demands for solar utilization, portability, and sustainable manufacture; however, improvements in the NIR light absorption and conversion efficiencies in ultrathin crystalline Si are required. We have developed an approach to improve the quantum efficiency of flexible PV devices in the NIR spectral region by integrating Si nanowire arrays with plasmonic Ag nanoplates. The Ag nanoplates can directly harvest and convert NIR light into plasmonic hot electrons for injection into Si, while the Si nanowire arrays offer light trapping. Taking the wavelength of 800 nm as an example, the external quantum efficiency has been improved by 59 % by the integration Ag nanoplates. This work provides an alternative strategy for the design and fabrication of flexible NIR PVs.     

Pd‐Catalysed Direct Arylation Polymerisation for Synthesis of Low‐Bandgap Conjugated Polymers and Photovoltaic Performance

Low‐bandgap conjugated copolymers based on a donor–acceptor structure have been synthesised via palladium‐complex catalysed direct arylation polymerisation. Initially, we report the optimisation of the synthesis of poly(cyclopentadithiophene‐alt‐benzothiadiazole) (PCPDTBT) formed between cyclopentadithiophene and dibromobenzothiadiazole units. The polymerisation condition has been optimised, which affords high‐molecular‐weight polymers of up to M _n = 70 k using N‐methylpyrrolidone as a solvent. The polymers are used to fabricate organic photovoltaic devices and the best performing PCPDTBT device exhibits a moderate improvement over devices fabricated using the related polymer via Suzuki coupling. Similar polymerisation conditions have also been applied for other monomer units.     

1‐Aryl‐4‐Silylmethyl[60]fullerenes: Synthesis,Properties, and Photovoltaic Performance

The efficient nucleophilic addition of aryl Grignard reagents (aryl=4‐MeOC₆H₄, 4‐Me₂NC₆H₄, Ph, 4‐CF₃C₆H₄, and thienyl) to C₆₀ in the presence of DMSO produced 1,2‐arylhydro[60]fullerenes after acid treatment. The reactions of the anions of these arylhydro[60]fullerenes with either dimethylphenylsilylmethyl iodide or dimethyl(2‐isopropoxyphenyl)silylmethyl iodide yielded the target compounds, 1‐aryl‐4‐silylmethyl[60]fullerenes. The properties and structures of these 1‐aryl‐4‐silylmethyl[60]fullerenes (aryl=4‐MeOC₆H₄, thienyl) were examined by electrochemical studies, X‐ray crystallography, flash‐photolysis time‐resolved microwave‐conductivity (FP‐TRMC) measurements, and electron‐mobility measurements by using a space‐charge‐limited current (SCLC) model. Organic photovoltaic devices with a polymer‐based bulk heterojunction structure and small‐molecule‐based p–n and p–i–n heterojunction configurations were fabricated by using 1‐aryl‐4‐silylmethyl[60]fullerenes as an electron acceptor. The most efficient device exhibited a power‐conversion efficiency of 3.4 % (short‐circuit current density: 8.1 mA/ cm², open‐circuit voltage: 0.69 V, fill factor: 0.59).